WO2020218168A1 - Particules de resine absorbante, corps absorbant et article absorbant - Google Patents

Particules de resine absorbante, corps absorbant et article absorbant Download PDF

Info

Publication number
WO2020218168A1
WO2020218168A1 PCT/JP2020/016761 JP2020016761W WO2020218168A1 WO 2020218168 A1 WO2020218168 A1 WO 2020218168A1 JP 2020016761 W JP2020016761 W JP 2020016761W WO 2020218168 A1 WO2020218168 A1 WO 2020218168A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
resin particles
absorbent resin
absorbent
mass
Prior art date
Application number
PCT/JP2020/016761
Other languages
English (en)
Japanese (ja)
Inventor
崇志 居藤
Original Assignee
住友精化株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友精化株式会社 filed Critical 住友精化株式会社
Priority to JP2021516064A priority Critical patent/JPWO2020218168A1/ja
Publication of WO2020218168A1 publication Critical patent/WO2020218168A1/fr

Abstract

L'invention concerne des particules de résine absorbante, pour lesquelles la vitesse d'absorption d'un liquide accumulé, telle que mesurée selon le procédé suivant, est comprise entre 30 et 90 secondes. (1) Placer une couche absorbante de forme rectangulaire, de façon que le côté court soit situé sur une surface horizontale et que le côté long suive une surface inclinée. (2) En une seconde au maximum, introduire la totalité de 5mL d'une urine artificielle dont la température est 25±1℃, à partir d'un emplacement verticalement en amont d'1cm par rapport au point d'introduction, le point d'introduction étant un emplacement au centre dans la direction courte, et à 2cm dans la direction longue à partir de l'extrémité supérieure de la surface de la couche absorbante. (3) Mesurer en tant que vitesse d'absorption d'un liquide accumulé, la durée entre le moment où l'urine artificielle a été complètement introduite et le moment ou la totalité de l'urine artificielle introduite est absorbée dans la couche absorbante.
PCT/JP2020/016761 2019-04-23 2020-04-16 Particules de resine absorbante, corps absorbant et article absorbant WO2020218168A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021516064A JPWO2020218168A1 (ja) 2019-04-23 2020-04-16 吸水性樹脂粒子、吸収体及び吸収性物品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-082024 2019-04-23
JP2019082024 2019-04-23

Publications (1)

Publication Number Publication Date
WO2020218168A1 true WO2020218168A1 (fr) 2020-10-29

Family

ID=72942552

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/016761 WO2020218168A1 (fr) 2019-04-23 2020-04-16 Particules de resine absorbante, corps absorbant et article absorbant

Country Status (2)

Country Link
JP (1) JPWO2020218168A1 (fr)
WO (1) WO2020218168A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023189672A1 (fr) * 2022-03-29 2023-10-05 住友精化株式会社 Particules de résine absorbant l'eau et article absorbant

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001158802A (ja) * 1999-12-02 2001-06-12 Kao Corp 高吸水性樹脂の製造方法
JP2005132957A (ja) * 2003-10-30 2005-05-26 Dainippon Ink & Chem Inc 吸水性樹脂の製造方法
JP2005247931A (ja) * 2004-03-02 2005-09-15 San-Dia Polymer Ltd 吸水性樹脂粒子の製造方法
JP2007177153A (ja) * 2005-12-28 2007-07-12 Toagosei Co Ltd 逆相懸濁重合装置及び重合体の製造方法
WO2012033025A1 (fr) * 2010-09-06 2012-03-15 住友精化株式会社 Résine absorbant l'eau et son procédé de production
JP2012183175A (ja) * 2011-03-04 2012-09-27 Sumitomo Seika Chem Co Ltd 吸水シート構成体
WO2016182082A1 (fr) * 2015-05-14 2016-11-17 株式会社日本触媒 Procédé de dispersion d'une composition liquide polymérisable et procédé de production de particules polymères sphériques
WO2017169246A1 (fr) * 2016-03-31 2017-10-05 住友精化株式会社 Dispositif de production de particules de résine absorbant l'eau

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001158802A (ja) * 1999-12-02 2001-06-12 Kao Corp 高吸水性樹脂の製造方法
JP2005132957A (ja) * 2003-10-30 2005-05-26 Dainippon Ink & Chem Inc 吸水性樹脂の製造方法
JP2005247931A (ja) * 2004-03-02 2005-09-15 San-Dia Polymer Ltd 吸水性樹脂粒子の製造方法
JP2007177153A (ja) * 2005-12-28 2007-07-12 Toagosei Co Ltd 逆相懸濁重合装置及び重合体の製造方法
WO2012033025A1 (fr) * 2010-09-06 2012-03-15 住友精化株式会社 Résine absorbant l'eau et son procédé de production
JP2012183175A (ja) * 2011-03-04 2012-09-27 Sumitomo Seika Chem Co Ltd 吸水シート構成体
WO2016182082A1 (fr) * 2015-05-14 2016-11-17 株式会社日本触媒 Procédé de dispersion d'une composition liquide polymérisable et procédé de production de particules polymères sphériques
WO2017169246A1 (fr) * 2016-03-31 2017-10-05 住友精化株式会社 Dispositif de production de particules de résine absorbant l'eau

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023189672A1 (fr) * 2022-03-29 2023-10-05 住友精化株式会社 Particules de résine absorbant l'eau et article absorbant

Also Published As

Publication number Publication date
JPWO2020218168A1 (ja) 2021-12-02

Similar Documents

Publication Publication Date Title
EP3896097A1 (fr) Particules de résine absorbante, corps absorbant, et article absorbant
WO2019189445A1 (fr) Article absorbant
EP3896120B1 (fr) Particules de résine absorbantes, corps absorbant, et article absorbant
WO2021006178A1 (fr) Composition de résine absorbant l'eau particulaire
WO2020184386A1 (fr) Particules de résine absorbant l'eau, article absorbant, procédé de fabrication de particules de résine absorbant l'eau, procédé pour faciliter la perméation d'une solution saline physiologique dans un corps absorbant
JP7443330B2 (ja) 吸水性樹脂粒子及びその製造方法、吸収体、吸収性物品、並びに、浸透速度の調整方法
WO2020184387A1 (fr) Particules de resine hydro-absorbantes, procede de production de celles-ci, corps absorbant ainsi qu'article absorbant
WO2020184398A1 (fr) Particules de resine hydro-absorbantes, procede de production de celles-ci, corps absorbant ainsi qu'article absorbant
WO2020184393A1 (fr) Particules de résine absorbante, corps absorbant, et article absorbant
WO2020218158A1 (fr) Particules de resine absorbante
EP3896095A1 (fr) Particules de résine absorbantes, corps absorbant, et article absorbant
WO2020218168A1 (fr) Particules de resine absorbante, corps absorbant et article absorbant
WO2020218160A1 (fr) Particules de résine absorbant l'eau, absorbant et article absorbant
WO2020184391A1 (fr) Corps absorbant, article absorbant et procédé d'ajustement de vitesse de perméation
JP6780047B2 (ja) 吸水性樹脂粒子、吸収体及び吸収性物品
JP6752319B2 (ja) 吸水性樹脂粒子
WO2020184392A1 (fr) Particules de resine hydro-absorbantes et procede de production de celles-ci
WO2021049450A1 (fr) Particules de résine absorbant l'eau
EP3960792A1 (fr) Particules de résine absorbante
JP6775049B2 (ja) 吸水性樹脂粒子
WO2020218162A1 (fr) Particules de résine absorbant l'eau et procédé de production associé, corps absorbant et article absorbant
JP6775048B2 (ja) 吸水性樹脂粒子、吸水性樹脂粒子の液体漏れ性の評価方法、及び吸水性樹脂粒子の製造方法
JP6775051B2 (ja) 吸収性物品
JP6889811B2 (ja) 吸水性樹脂粒子、吸収性物品、吸水性樹脂粒子を製造する方法、及び吸収性物品の液漏れを抑制する方法
JP6780048B2 (ja) 吸水性樹脂粒子、吸収体及び吸収性物品

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20796022

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021516064

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20796022

Country of ref document: EP

Kind code of ref document: A1