WO2017180468A1 - Article abrasif - Google Patents

Article abrasif Download PDF

Info

Publication number
WO2017180468A1
WO2017180468A1 PCT/US2017/026591 US2017026591W WO2017180468A1 WO 2017180468 A1 WO2017180468 A1 WO 2017180468A1 US 2017026591 W US2017026591 W US 2017026591W WO 2017180468 A1 WO2017180468 A1 WO 2017180468A1
Authority
WO
WIPO (PCT)
Prior art keywords
supersize
abrasive
percent
supersize composition
composition
Prior art date
Application number
PCT/US2017/026591
Other languages
English (en)
Inventor
Yugeun P. Yang
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Publication of WO2017180468A1 publication Critical patent/WO2017180468A1/fr

Abstract

La présente invention décrit des articles abrasifs, conjointement à des compositions et des procédés associés. La présente invention comprend des articles abrasifs comprenant un support, une couche abrasive, et un revêtement de surencollage qui comprend du stéarate de calcium et un sel de sodium d'un polymère modifié styrène acrylique. Les compositions de surencollage décrites permettent un niveau élevé de taux de coupe abrasif et de durée de vie de coupe par rapport aux compositions classiques de surencollage. Comme avantage supplémentaire, les compositions donnent des revêtements de surencollage qui fournissent un degré élevé de clarté optique, permettant d'imprimer des images graphiques sur le côté abrasif de l'article.
PCT/US2017/026591 2016-04-13 2017-04-07 Article abrasif WO2017180468A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201662321996P 2016-04-13 2016-04-13
US62/321,996 2016-04-13

Publications (1)

Publication Number Publication Date
WO2017180468A1 true WO2017180468A1 (fr) 2017-10-19

Family

ID=58699240

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/026591 WO2017180468A1 (fr) 2016-04-13 2017-04-07 Article abrasif

Country Status (1)

Country Link
WO (1) WO2017180468A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111251175A (zh) * 2020-03-13 2020-06-09 于洋 研磨垫及其制备方法和应用
US11660726B2 (en) 2019-09-05 2023-05-30 Saint-Gobain Abrasives, Inc. Coated abrasives having an improved supersize coating
WO2024069578A1 (fr) * 2022-09-29 2024-04-04 3M Innovative Properties Company Composition de revêtement de supertaille, article abrasif et procédé de fabrication d'article abrasif

Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2403821A (en) 1946-07-09 Polishing cloth
US3352695A (en) 1965-01-18 1967-11-14 Gorham Corp Silver polish containing di-n-hexadecyl disulfide
US4988554A (en) 1989-06-23 1991-01-29 Minnesota Mining And Manufacturing Company Abrasive article coated with a lithium salt of a fatty acid
US5164265A (en) * 1989-12-11 1992-11-17 Minnesota Mining And Manufacturing Company Abrasive elements
US5700302A (en) 1996-03-15 1997-12-23 Minnesota Mining And Manufacturing Company Radiation curable abrasive article with tie coat and method
US5704952A (en) * 1996-05-08 1998-01-06 Minnesota Mining And Manufacturing Company Abrasive article comprising an antiloading component
WO1999015315A1 (fr) * 1997-09-19 1999-04-01 Minnesota Mining And Manufacturing Company Articles abrasifs a additif de polymere
US6183677B1 (en) 1995-10-31 2001-02-06 Kovax Corporation Method of manufacturing abrasive sheet with thin resin film
US6372323B1 (en) 1998-10-05 2002-04-16 3M Innovative Properties Company Slip control article for wet and dry applications
US6682574B2 (en) 2001-09-13 2004-01-27 3M Innovative Properties Company Binder for abrasive articles, abrasive articles including the same and method of making same
US6773474B2 (en) 2002-04-19 2004-08-10 3M Innovative Properties Company Coated abrasive article
US7329175B2 (en) 2004-12-30 2008-02-12 3M Innovative Properties Company Abrasive article and methods of making same
US7381231B2 (en) 2004-01-29 2008-06-03 3M Innovative Properties Company Finishing compositions with reduced volatile organic compounds
WO2008109211A1 (fr) * 2007-03-05 2008-09-12 3M Innovative Properties Company Article abrasif avec revêtement surdimensionné et procédé de fabrication
US8025557B2 (en) 2009-02-27 2011-09-27 Illinois Tool Works Inc. Sanding clay

Patent Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2403821A (en) 1946-07-09 Polishing cloth
US3352695A (en) 1965-01-18 1967-11-14 Gorham Corp Silver polish containing di-n-hexadecyl disulfide
US4988554A (en) 1989-06-23 1991-01-29 Minnesota Mining And Manufacturing Company Abrasive article coated with a lithium salt of a fatty acid
US5164265A (en) * 1989-12-11 1992-11-17 Minnesota Mining And Manufacturing Company Abrasive elements
US6183677B1 (en) 1995-10-31 2001-02-06 Kovax Corporation Method of manufacturing abrasive sheet with thin resin film
US5700302A (en) 1996-03-15 1997-12-23 Minnesota Mining And Manufacturing Company Radiation curable abrasive article with tie coat and method
US5704952A (en) * 1996-05-08 1998-01-06 Minnesota Mining And Manufacturing Company Abrasive article comprising an antiloading component
WO1999015315A1 (fr) * 1997-09-19 1999-04-01 Minnesota Mining And Manufacturing Company Articles abrasifs a additif de polymere
US6372323B1 (en) 1998-10-05 2002-04-16 3M Innovative Properties Company Slip control article for wet and dry applications
US6682574B2 (en) 2001-09-13 2004-01-27 3M Innovative Properties Company Binder for abrasive articles, abrasive articles including the same and method of making same
US6773474B2 (en) 2002-04-19 2004-08-10 3M Innovative Properties Company Coated abrasive article
US7381231B2 (en) 2004-01-29 2008-06-03 3M Innovative Properties Company Finishing compositions with reduced volatile organic compounds
US7329175B2 (en) 2004-12-30 2008-02-12 3M Innovative Properties Company Abrasive article and methods of making same
WO2008109211A1 (fr) * 2007-03-05 2008-09-12 3M Innovative Properties Company Article abrasif avec revêtement surdimensionné et procédé de fabrication
US8025557B2 (en) 2009-02-27 2011-09-27 Illinois Tool Works Inc. Sanding clay

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11660726B2 (en) 2019-09-05 2023-05-30 Saint-Gobain Abrasives, Inc. Coated abrasives having an improved supersize coating
US12233511B2 (en) 2019-09-05 2025-02-25 Saint-Gobain Abrasives, Inc. Coated abrasives having an improved supersize coating
CN111251175A (zh) * 2020-03-13 2020-06-09 于洋 研磨垫及其制备方法和应用
WO2024069578A1 (fr) * 2022-09-29 2024-04-04 3M Innovative Properties Company Composition de revêtement de supertaille, article abrasif et procédé de fabrication d'article abrasif

Similar Documents

Publication Publication Date Title
EP3397426B1 (fr) Articles abrasifs et procédés associés
EP3759191B1 (fr) Aggloméré abrasif siliceux façonné comportant des particules abrasives façonnées, articles abrasifs, et procédés associés
EP3397425B1 (fr) Article abrasif
EP3532246B1 (fr) Agglomérat abrasif vitrifié façonné à particules abrasives façonnées, articles abrasifs et procédés associés
EP3519135B1 (fr) Article abrasif à couche ouverte et procédé d'abrasion
EP3442749B1 (fr) Article abrasif et procédé de réalisation d'un article abrasif
WO2017180468A1 (fr) Article abrasif
US11358254B2 (en) Abrasive article
US9221151B2 (en) Abrasive articles including a blend of abrasive grains and method of forming same
WO2024069578A1 (fr) Composition de revêtement de supertaille, article abrasif et procédé de fabrication d'article abrasif
US20230278170A1 (en) Abrasive article and method of making the same
KR20000010854A (ko) 안티로딩 성분을 포함하는 연마 용품

Legal Events

Date Code Title Description
NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17722907

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 17722907

Country of ref document: EP

Kind code of ref document: A1