WO2017176600A1 - Electrocatalytic process for carbon dioxide conversion - Google Patents

Electrocatalytic process for carbon dioxide conversion Download PDF

Info

Publication number
WO2017176600A1
WO2017176600A1 PCT/US2017/025630 US2017025630W WO2017176600A1 WO 2017176600 A1 WO2017176600 A1 WO 2017176600A1 US 2017025630 W US2017025630 W US 2017025630W WO 2017176600 A1 WO2017176600 A1 WO 2017176600A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
cell
active element
catalytically active
reaction
Prior art date
Application number
PCT/US2017/025630
Other languages
French (fr)
Inventor
Richard I. Masel
Amin Salehi-Khojin
Robert Kutz
Original Assignee
Dioxide Materials, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US15/090,477 external-priority patent/US9580824B2/en
Priority claimed from US15/158,227 external-priority patent/US9945040B2/en
Priority claimed from US15/400,712 external-priority patent/US9815021B2/en
Application filed by Dioxide Materials, Inc. filed Critical Dioxide Materials, Inc.
Publication of WO2017176600A1 publication Critical patent/WO2017176600A1/en

Abstract

An electrocatalytic process for carbon dioxide conversion includes combining a Catalytically Active Element and a Helper Polymer in the presence of carbon dioxide, allowing a reaction to proceed to produce a reaction product, and applying electrical energy to said reaction to achieve electrochemical conversion of said carbon dioxide reactant to said reaction product. The Catalytically Active Element can be a metal in the form of supported or unsupported particles or flakes with an average size between 0.6 nm and 100 nm. The reaction products comprise at least one of CO, HCO−, H2CO, (HCO2)−, H2CO2, CH3OH, CH4, C2H4, CH3CH2OH, CH3COO−, CH3COOH, C2H6, (COOH)2, (COO−)2, and CF3COOH.

Description

ELECTROCATALYTIC PROCESS FOR CARBON DIOXIDE CONVERSION
Field of the Invention
[0001] The field of the invention is electrocatalysis and electrocatalysts. The catalysts of this invention are applicable, for example, to the electrochemical conversion of carbon dioxide into useful products.
Background of the Invention
[0002] There is a present need to decrease carbon dioxide (CO2) emissions from industrial facilities. Over the years, a number of electrochemical processes have been suggested for the conversion of CO2 into useful products. Processes for CO2 conversion and the catalysts for them are discussed in U.S. patents 3,959,094, 4,240,882, 4,523,981, 4,545,872, 4,595,465, 4,608,132, 4,608,133, 4,609,440, 4,609,441, 4,609,451, 4,620,906, 4,668,349, 4,673,473, 4,711,708, 4,756,807, 4,818,353, 5,064,733, 5,284,563, 5,382,332, 5,457,079, 5,709,789, 5,928,806, 5,952,540, 6,024,855, 6,660,680, 6,987,134 (the Ί34 patent), 7,157,404,
7,378,561, 7,479,570, U.S. patent application 20080223727 (the '727 application) and papers reviewed by Hori (Modem Aspects of Electrochemistry, 42, 89-189, 2008) ("the Hori Review"), Gattrell, et al. (Journal of Electroanalytical Chemistry, 594, 1-19, 2006) ("the Gattrell review"), DuBois (Encyclopedia of Electrochemistry, 7a, 202-225, 2006) ("the DuBois review").
[0003] Generally, an electrochemical cell contains an anode 50, a cathode 51 and an electrolyte 53 as illustrated in FIG. 1. Catalysts are placed on the anode, and/or the cathode, and/or in the electrolyte to promote desired chemical reactions. During operation, reactants or a solution containing reactants is fed into the cell. Then a voltage is applied between the anode and the cathode, to promote an electrochemical reaction.
[0004] When an electrochemical cell is used as a CO2 conversion system, a reactant comprising CO2, carbonate or bicarbonate is fed into the cell. A voltage is applied to the cell, and the CO2 reacts to form new chemical compounds. Examples of cathode reactions in the Hori Review include:
Figure imgf000003_0001
CO2 + 2H2O + 4e"→ HCO" + 30H-
CO2 + 2H20 + 2e"→ H2CO + 20H-
CO2 + H2O + 2e"→ (HCO2)- + OH-
CO2 + 2H20 + 2e"→ H2CO2 + 20H-
CO2 + 5H2O + 6e"→ CH3OH + 60H-
CO2 + 6H2O + 8e"→ CH4 + 80H-
2CO2 + 8H2O + 12e"→ C2H4 + 120H-
2CO2 + 9H20 + 12e"→ CH3CH2OH + 120H-
2CO2 + 6H2O + 8e"→ CH3COOH + 80H-
2CO2 + 5H20 + 8e"→ CH3COO- + 70H-
2CO2 + IOH2O + 14e"→ C2H6 + 140H-
CO2 + 2H+ + 2e"→ CO + H2O, acetic acid, oxalic acid, oxylate
Figure imgf000004_0001
where e" is an electron. The examples given above are merely illustrative and are not meant to be an exhaustive list of all possible cathode reactions.
[0005] Examples of reactions on the anode mentioned in the Hori Review include:
Figure imgf000004_0002
The examples given above are merely illustrative and are not meant to be an exhaustive list of all possible anode reactions.
[0006] In the previous literature, catalysts comprising one or more of V, Cr, Mn, Fe, Co, Ni, Cu, Sn, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Hf, Ta, W, Re, Ir, Pt, Au, Hg, Al, Si, In, Tl, Pb, Bi, Sb, Te, U, Sm, Tb, La, Ce, and Nd have all shown activity for CO2 conversion. Reviews include Hori (Modern Aspects of Electrochemistry, 42, 89-189, 2008) ("the Hori Review"), Gattrell, et al. (Journal of Electroanalytical Chemistry, 594, 1-19, 2006) ("the Gattrell review"), DuBois (Encyclopedia of Electrochemistry, 7a, 202-225, 2006) ("the DuBois review"), and the papers Li, et al. (Joumal of Applied Electrochemistry, 36, 1105-1115, 2006, Li, et al. (Journal of Applied Electrochemistry, 37, 1107-1117, 2007, and Oloman, et al. (ChemSusChem, 1, 385-391, 2008) ("the Li and Oloman papers"), and references therein.
[0007] The results in the Hori Review show that the conversion of CO2 is only mildly affected by solvent unless the solvent also acts as a reactant. Water can act like a reactant, so reactions in water are different than reactions in non-aqueous solutions. But the reactions are the same in most non-aqueous solvents, and importantly, the overpotentials are almost the same in water and in the non-aqueous solvents.
[0008] The catalysts have been in the form of either bulk materials, supported particles, collections of particles, small metal ions or organometallics. Still, according to Bell (A. Bell. Ed, Basic Research Needs, Catalysis For Energy, U.S. Department of Energy Report PNNL17712, 2008) ("the Bell Report"), "The major obstacle preventing efficient conversion of carbon dioxide into energy -bearing products is the lack of catalyst" with sufficient activity at low overpotentials and high electron conversion efficiencies.
[0009] The overpotential is associated with lost energy of the process, so the overpotential should be as low as possible. Yet, according to The Bell Report "Electron conversion efficiencies of greater than 50 percent can be obtained, but at the expense of very high overpotentials". This limitation needs to be overcome before practical processes can be obtained.
[0010] A second disadvantage of many of the catalysts is that they also have low electron conversion efficiency. Catalyst systems are considered practical where electron conversion is over 50%.
[0011] U.S. patent application Serial Nos. 12/830,338 (published as US2011/0237830) and 13/174,365 (published as US2012/0308903), and International Application No.
PCT/US2011/030098 (published as WO2011/120021) and PCT/US2011/042809 (published as WO2012/006240) disclose that a catalyst mixture containing an active metal and a Helper Catalyst could catalyze CCh conversions with low overpotential and high electron conversion efficiency. However, the catalysts disclosed in these patent applications showed a lower activity than was desired.
[0012] The patent documents identified above consider applications for CCh conversion, but the present electrocatalysts overcome limitations of other systems. For example, some commercial CCh sensors use an electrochemical reaction to detect the presence of CCh. At present, these sensors require over 1-5 watts of power, which is too high for portable sensing applications.
Summary of the Invention
[0013] The present process employs a novel catalyst combination that can overcome one or more of the limitations of low rates, high overpotentials and low electron conversion efficiencies (namely, selectivities), low rates for catalytic reactions and high power requirements for sensors. The catalyst combination or mixture includes at least one Catalytically Active Element in the form of supported or unsupported particles wherein the particles have an average particle size (as defined below) between about 0.6 nm and 100 nm, preferably between 0.6 nm and 40 nm, and most preferable between 0.6 nm and 10 nm. The catalyst combination also includes a Helper Polymer that can contain, for example, positively charged cyclic amine groups, such as imidazoliums or pyridiniums. The catalyst combination of a Catalytically Active Element and a Helper Polymer are useful, for example, in the cathode catalyst layer of an electrochemical cell used for conversion of CO2 to various reaction products.
[0014] The present process is not limited to catalysts for CO2 conversion. In particular, catalysts that include Catalytically Active Elements and Helper Catalysts or Helper Polymers might enhance the rate of a wide variety of chemical reactions. Reaction types include:
homogeneously catalyzed reactions, heterogeneously catalyzed reactions, chemical reactions in chemical plants, chemical reactions in power plants, chemical reactions in pollution control equipment and devices, chemical reactions in fuel cells, and chemical reactions in sensors. The present process includes all of these examples.
Brief Description of the Drawings
[0015] FIG. 1 is a diagram of a typical electrochemical cell.
[0016] FIG. 2 illustrates how the cyclic voltammogram (CV) of electrochemical water reduction varies with the average particle size of the Catalytically Active Element silver on the cathode: (A) bare silver electrode, (B) electrode covered by nominally 200 nm silver particles, (C) electrode covered by nominally 100 nm silver particles, (D) electrode covered by nominally 20-40 nm silver particles, (E) electrode covered by 5 nm silver particles, and (F) electrode covered by 0.67 nm silver particles. The numeric designations 500-505 indicate the positions of the hydrogen peak in the figures. All of the CV's are reported as the current divided by the electrochemical surface area of the particles
[0017] FIG. 3 illustrates how the CV changes in FIG. 2 when CO2 is added to the reaction: (A) bare silver electrode, (B) electrode covered by nominally 200 nm silver particles, (C) electrode covered by nominally 100 nm silver particles, (D) electrode covered by nominally 20-40 nm silver particles, (E) electrode covered by 5 nm silver particles, and (F) electrode covered by 0.67 nm silver particles. The numeric designations 600-605 indicate the CO2 reduction peak in the figures. All of the CV's are reported as the current divided by the electrochemical surface area of the particles
[0018] FIG. 4 illustrates particle size distribution of the (A) nominally 20-40 nm silver particles, (B) nominally 100 nm silver particles, and (C) nominally 200 nm silver particles as measured by dynamic light scattering. The nominally 20-40 nm particles have an average size of 35 nm. The nominally 100 nm particles have an average size of 70 nm and the nominally 200 nm particles have an average size of 190 nm.
[0019] FIG. 5 shows how the voltammograms of a 5 cm2 cell change when 0% (plot 200), 1 % (plot 201), 5% (plot 202), and 10% (plot 203) of Helper Polymer PSMIMC1 are added to the CC electrolyzer cathode catalyst layer, where the percentage is calculated as the weight of the PSMIMC1 divided by the weight of the silver. "PSMIMC1" refers to the chloride form of a co-polymer of polystyrene and poly l-(p-vinylbenzyl)-3-methyl-imidazolium.
Detailed Description of Illustrative Embodiment(s)
[0020] The invention disclosed herein is not limited to the particular methodology, protocols, and reagents described herein, as these can vary as persons familiar with the technology involved here will recognize. The terminology employed herein is used for the purpose of describing particular embodiments only, and is not intended to limit the scope of the invention. As used herein and in the appended claims, the singular forms "a," "an," and "the" include the plural reference unless the context clearly dictates otherwise. Thus, for example, a reference to "a linker" is a reference to one or more linkers and equivalents thereof known to persons familiar with the technology involved here.
[0021] Unless defined otherwise, all technical and scientific terms used herein have the same meanings as commonly understood by persons familiar with the technology involved here. The embodiments of the invention and the various features and advantageous details thereof are explained more fully with reference to the non-limiting embodiments and/or illustrated in the accompanying drawings and detailed in the following description, where the term
"and/or" signifies either one or both of the options. It should be noted that the features illustrated in the drawings are not necessarily drawn to scale, and features of one embodiment can be employed with other embodiments as persons familiar with the technology involved here would recognize, even if not explicitly stated herein.
[0022] Any numerical value ranges recited herein include all values from the lower value to the upper value in increments of one unit provided that there is a separation of at least two units between any lower value and any higher value. As an example, if it is stated that the concentration of a component or value of a process variable such as, for example, size, angle size, pressure, time and the like, is, for example, from 1 to 90, specifically from 20 to 80, more specifically from 30 to 70, it is intended that values such as 15 to 85, 22 to 68, 43 to 51 , 30 to 32, and so on, are expressly enumerated in this specification. For values which are less than one, one unit is considered to be 0.0001, 0.001, 0.01 or 0.1 as appropriate. These are only examples of what is specifically intended and all possible combinations of numerical values between the lowest value and the highest value are to be treated in a similar manner.
[0023] Moreover, provided immediately below is a "Definitions" section, where certain terms related to the invention are defined specifically. Particular methods, devices, and materials are described, although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the invention. All references referred to herein are incorporated by reference herein in their entirety.
Definitions
[0024] The term "electrochemical conversion of CC " as used here refers to any
electrochemical process where carbon dioxide, carbonate, or bicarbonate is converted into another chemical substance in any step of the process.
[0025] The term "CV" as used here refers to a cyclic voltammogram or cyclic voltammetry.
[0026] The term "Overpotential" as used here refers to the potential difference (voltage) between a reaction's thermodynamically determined reduction or oxidation potential and the potential at which the event is experimentally observed.
[0027] The term "Cathode Overpotential" as used here refers to the overpotential on the cathode of an electrochemical cell.
[0028] The term "Anode Overpotential" as used here refers to the overpotential on the anode of an electrochemical cell.
[0029] The term "Electron Conversion Efficiency" refers to selectivity of an electrochemical reaction. More precisely, it is defined as the fraction of the current that is supplied to the cell that goes to the production of a desired product.
[0030] The term "Catalytically Active Element" as used here refers to any chemical element that can serve as a catalyst for the electrochemical conversion of CO2.
[0031] The term "Helper Catalyst" as used here refers to any organic molecule or ion, or a mixture of organic molecules and/or ions, that does at least one of the following:
(a) Speeds up a chemical reaction; or
(b) Lowers the overpotential of the reaction,
without being substantially consumed in the process.
[0032] The term "Helper Polymer" as used here refers to a polymer that does at least one of the following: (a) Speeds up a chemical reaction;
(b) Increases the current seen in an electrochemical reaction at a given potential;
(c) Increases the Faradaic efficiency of a given reaction; or
(d) Increases the selectivity of a reaction.
[0033] The term "MEA" as used here refers to a membrane electrode assembly.
[0034] The term "imidazolium" as used here refers to a positively charged ligand containing an imidazole group. This includes a bare imidazole or a substituted imidazole. Ligands of the form:
Figure imgf000009_0001
where Ri- R.5 are each independently selected from hydrogen, halogens, linear alkyls, branched alkyls, cyclic alkyls, heteroalkyls, aryls, cyclic aryls, heteroaryls, alkylaryls, heteroalkylaryls, and polymers thereof, such as the vinyl benzyl copolymers described herein, are specifically included.
[0035] The term "pyridinium" as used here refers to a positively charged ligand containing a pyridinium group. This includes a protonated bare pyridine or a substituted pyridine or pyridinium. Ligands of the form:
Figure imgf000009_0002
where R.6-R11 are each independently selected from hydrogen, halogens, linear alkyls, branched alkyls, cyclic alkyls, heteroalkyls, aryls, cyclic aryls, heteroaryls, alkylaryls, heteroalkylaryls, and polymers thereof, such as the vinyl benzyl copolymers described herein, are specifically included.
[0036] The term "pyrazoliums" as used here refers to a positively charged ligand containing a pyrazolium group. This includes a bare pyrazolium or a substituted pyrazolium. Ligands of the form:
Figure imgf000010_0001
where R16-R20 are each independently selected from hydrogen, halogens, linear alkyls, branched alkyls, cyclic alkyls, heteroalkyls, aryls, cyclic aryls, heteroaryls, alkylaryls, heteroalkylaryls, and polymers thereof, such as the vinyl benzyl copolymers described herein, are specifically included.
[0037] The term "phosphonium" as used here refers to a positively charged ligand containing phosphorous. This includes substituted phosphorous. Ligands of the form:
P+(Rl2Rl3Rl4Rl5)
where R12-R15 are each independently selected from hydrogen, halogens, linear alkyls, branched alkyls, cyclic alkyls, heteroalkyls, aryls, cyclic aryls, heteroaryls, alkylaryls, heteroalkylaryls, and polymers thereof, such as the vinyl benzyl copolymers described herein, are specifically included.
[0038] The term "positively charged cyclic amine" as used here refers to a positively charged ligand containing a cyclic amine. This specifically includes imidazoliums, pyridiniums, pyrazoliums, pyrrolidiniums, pyrroliums, pyrimidiums, piperidiniums, indoliums, triaziniums, and polymers thereof, such as the vinyl benzyl copolymers described herein.
Specific Description
[0039] The present process relates generally to Catalytically Active Element, Helper Polymer Mixtures where the mixture does at least one of the following:
(a) Speeds up a chemical reaction;
(b) Increases the current seen in an electrochemical reaction at a given potential;
(c) Increases the Faradaic efficiency of a given reaction; or
(d) Increases the selectivity of a reaction.
[0040] For example, such mixtures can increase the rate of CO2 conversion to a value that is higher than when the same Catalytically Active Element is used without the Helper Polymer.
[0041] U.S. patent application Serial Nos. 12/830,338 (published as US2011/0237830), and 13/174,365 (published as US2012/0308903), and International Application No.
PCT/US2011/030098 (published as WO2011/120021) and PCT/US2011/042809 (published as WO2012/006240) disclose that a catalyst mixture containing a Catalytically Active Metal and a Helper Catalyst catalyzes CO2 conversions with low overpotential and high electron conversion efficiency. Active Metals included one or more of V, Cr, Mn, Fe, Co, Ni, Cu, Sn, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Hf, Ta, W, Re, Ir, Pt, Au, Hg, Al, Si, In, Tl, Pb, Bi, Sb, Te, U, Sm, Tb, La, Ce, and Nd. Examples of Helper Polymers include polymers containing one or more of positively charged cyclic amines, phosphines, imidazoliums, pyridiniums, pyrrolidiniums, phosphoniums, sulfoniums, prolinates, methioninates, cholines,
acetylcholines, alanines, aminoacetonitriles, methylammoniums, arginines, aspartic acids, threonines, chloroformamidiniums, thiouroniums, quinoliniums, pyrrolidinols, serinols, benzamidines, sulfamates, acetates, carbamates, triflates, and cyanides.
[0042] Of course, the '338 U.S. application, the '365 U.S. application, the '098 international application and the '809 international application disclose that not every substance listed above will act as a Helper Polymer. In general, one can determine whether a polymer P is a Helper Catalyst for electrochemical conversion of CO2 catalyzed by a catalytically active element M by the following test:
(1) Prepare two different membrane electrode assemblies (MEAs) with 5 cm2 of active area: i) one having the polymer P in the cathode catalyst layer; and i) one otherwise identical but without the polymer P in the cathode catalyst layer, wherein the weight of the polymer is 4% of the weight of the catalytically active element M.
(2) Both membrane electrode assemblies are mounted in Fuel Cell Technologies (Albuquerque, NM) 5 cm2 fuel cell hardware assembly with serpentine flow fields.
(3) CO2 humidified at 50°C is fed into the cathode of both cells at a rate of 5 seem with the cell at room temperature and pressure, and the anode side is left open to the atmosphere at room temperature and pressure.
(4) A voltage of 1 V is applied to the cell without the polymer P, and then the voltage is raised to a voltage V such that the output current is as least 20 niA/cm2. The current output of the cell is recorded after running for 30 minutes.
(5) The same voltage V is applied to the cell with the polymer P and the current output of the cell is recorded after running for 30 minutes.
If the current is at least 20% higher in the cell with the polymer P in the catalyst layer than the cell without the polymer P in the catalyst layer, the polymer P is a Helper Polymer for that reaction.
[0043] Preferably the two MEA's are manufactured as follows:
(1) A solvent S is identified such that S can dissolve at least 5 mg of the polymer P in 3 mL of solution.
(2) A cathode for the MEA containing the polymer P is produced as follows:
(a) 100 mg of nanoparticles of Catalytically Active Element M are mixed with 4 mg of polymer P, and 3 mL of solvent S.
(b) The mixture is sonicated for 10 minutes to create a catalyst ink.
(c) The ink is painted onto a gas diffusion layer (Sigracet 35 BC GDL, Ion Power Inc., New Castle, DE) covering an area of 6 cm x 6 cm. The electrode was immersed in 1 M KOH for at least 1 hour for ion exchange, then the electrode is cut into 2.5 cm x 2.5 cm sections for cell testing.
(3) The anode for the MEA is produced prepared as follows:
(a) 100 mg of IrC (43396, Alfa Aesar, Ward Hill, MA) is dispersed in the mixture of 1 ml of deionized water, 2 ml of isopropanol (3032-16, Macron Fine Chemicals, Avantor Performance Materials, Center Valley, PA) and 0.1 ml of 5 wt.% poly-tetrafluoroethylene (PTFE) dispersion (665800, Sigma- Aldrich, St. Louis, MO).
(b) The mixture is sonicated for 10 min using a water bath sonicator.
(c) The ink is painted onto 6 cm x 6 cm of carbon fiber paper (Toray Paper 120, Fuel Cell Earth, Woburn, MA). The IrC loading is about 2 mg/cm2 The electrode is cut into 3 cm x 3 cm sections for cell testing.
(4) An anion exchange membrane is sandwiched between the anode and the cathode with the metal-containing layers on the anode and cathode facing the membrane to create the MEA. Preferably the anion exchange membrane is one of the helper membranes described in US9,370,773.
(5) The same procedure is used to create the MEA the does not contain the Polymer, except no polymer P is added in step 2a.
[0044] In the foregoing applications, new catalyst formulations are disclosed that maintain the ability to convert CC with a high electron conversion efficiency and low overpotential, but also show an improved specific catalytic activity. The catalyst of the present application was prepared by modifying the structure of the silver so it is more active. The catalyst can be in the form of supported or unsupported metal particles wherein the average particle size is below about 100 nm, preferably between 0.6 nm and 40 nm, more preferably between 0.6 nm and 20 nm, and most preferably between 0.6 nm and 10 nm.
[0045] In this context, the particle sizes can be determined by one or more of microscopy, x- ray line broadening, chemisorption, or small angle x-ray scattering. For example, one might measure the x-ray diffraction partem of the catalysts, determine β, the width of the diffraction line at some angle Θ, and then calculate the particle size, D, from the Scherrer equation:
0.9 λ
D ~ β cos(O)
where λ is the wavelength of the x-ray beam.
[0046] Chemisorption can alternately be used to measure the Sg, the surface area of the active element per unit mass, and then calculate the particle size from the formula:
5
D =—
Sgp
where p is the bulk density of the active element.
[0047] The present process specifically includes any catalyst with a particle size between 0.6 nm and 100 nm measured by any of x-ray line broadening, chemisorption, or small angle x- ray scattering.
Background Data; An illustration of the effects of particle size on CCh conversion on a silver/EMIM catalyst
Catalysts Tested
[0048] This example illustrates the effect of silver particle size on the rate of CCh conversion on an EMIM-BF4 (Sigma Aldrich, St. Louis, MO) coated silver catalyst.
Experimental Data
[0049] During the experiments, a silver ink was deposited onto a silver rotating disk electrode (Pine Instruments, Grove City, PA). In the first experiment, the silver electrode was polished, and a CV was run as described in the fourth paragraph below. Subsequent experiments were run by depositing one of: (i) 200 nm silver (Sigma Aldrich, St. Louis, MO); (ii) 100 nm silver (Sigma Aldrich); (iii) 20-40 nm silver (Sigma Aldrich); (iv) 5 nm (UT Dots, Champaign, IL); (v) 0.67 nm (Purest Colloids, Westampton, NJ) onto the silver electrode and running the CV as set forth in the fourth paragraph below.
[0050] In the case of 500-1000 nm, 100 nm, and 20-40 nm silver, a silver ink was prepared by mixing 5.6 mg of silver particles with 1 ml deoxygenated Millipore water. The catalyst was applied on the surface of a rotating electrode by adding 60 of the ink to the surface and allowing the water to evaporate under ambient temperature for 60 minutes. In order to ensure the quality of the measurements, special attention was paid to the material cleaning and solution purity.
[0051] The 10 nm Ag arrived suspended in an organic solution, so this solution was applied to the silver electrode, and subsequently heated in air at 85°C for 3 hours to remove residual organics. [0052] The 0.6 nm Ag particles arrived suspended in distilled water, so they were used as received.
[0053] The counter electrode was made by attaching a 25 mm x 25 mm platinum mesh (size 52) to a 5-inch platinum wire (99.9%, 0.004-inch diameter). A silver quasi-reference electrode (Ag-QRE) was used. The electrolytes were first loaded into the glass cell and then purged with dry argon (99.99%) for two hours in order to remove oxygen from the electrolytes. Prior to each experiment, a 20-40 linear sweep cyclic voltammogram at 75 mVs" 1 was taken with the range between -2 V and 0 vs. Ag-QRE in order to condition the electrodes and remove oxides from the surfaces. Then several cycles were performed at 10 mVs"1 before taking the final cycle to ensure that the CV had stabilized (that is, any "dirt" or other material was removed from the surfaces). Finally, cleaning and stabilizing CV cycles were performed at 10 mVs"1. Then CCh was bubbled in the solution at 1 atm pressure for 20 minutes. Cyclic voltammetry was conducted again at a sweep rate of 10 mV/s in the range from -2 V to 0 V vs. Ag-QRE.
Results; Water Electrolysis
[0054] FIG. 2 shows how the CV of water varies with particle size. One finds that there is very little variation in the catalytic activity of silver, in agreement with the literature reviewed in a recent paper, M.T.M. Koper, Structural sensitivity and nanostructure effects in electrocatalysis , Nanoscale 3, 2054 (2011) ("the Koper Paper").
Results; CO2 Electrolysis
[0055] FIG. 3 shows how the CV changes when CO2 is added to the electrochemical cell. Notice that CO2 conversion peaks, labeled 100, 101, 102, 103, 104, 105 and 106 are observed. The CCh conversion peaks grow as one decreases the particle size from 1000-10 nm, but then we observed the opposite effect, where the CCh peak shrinks moving from 10 nm to 0.6 nm. Evidently, there is an optimal particle size somewhere between 0.6 and 100 nm. The optimal size is probably between 0.6 and 40 nm, most probably between 0.6 and 20 nm.
[0056] The result above shows that unsupported silver catalysts have an optimal size between 0.6 and 100 nm. Those trained in the art know that if a reaction is structure sensitive on an unsupported catalyst, or single crystal, it will also show structure sensitivity on a supported catalyst. Further, the Korper Paper suggests that if a reaction is structure sensitive on one transition metal, it will also be structure sensitive on most other transition metals. In particular, the optimum particle size is very similar on most transition metals. Therefore, we conclude that V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd, W, Re, Ir, Pt, Au, Hg, Pb, Bi, electrocatalysts for CO2 conversion should have an optimal size between 0.6 and 100 nm.
Example 1; use of solid polymers as Helper Catalysts
[0057] The objective of this example is to show that polymers containing imidazoliums can be Helper Catalysts.
[0058] A copolymer, which is designated here as PSMIM (CI), was prepared following the synthetic route in U.S. Patent No. 9,370,773. "PSMIM" refers to a co-polymer of polystyrene and poly l-(p-vinylbenzyl)-3-meth l-imidazolium:
Figure imgf000015_0001
where X~ is an anion, m > 0 and n > 0.
[0059] The inhibitor-free styrene was prepared by passing styrene (Sigma- Aldrich) through the tert-butylcatechol (TBC) inhibitor remover (Sigma- Aldrich 311340). In general, 40 ml of remover is sufficient to yield 50 ml of clear, inhibitor free styrene. Inhibitor TBC in 4- vinylbenzyl chloride (4-VBC) was removed by the same inhibitor remover in a similar fashion.
[0060] Poly(4-vinylbenzyl chloride-co-styrene) was then synthesized by heating a solution of inhibitor-free styrene (Sigma- Aldrich) (36.139 g, 350 mmol) and 4-vinylbenzyl chloride (Sigma-Aldrich) (29.7272 g, 190 mmol) in chlorobenzene (Sigma-Aldrich) (45 ml) at 60- 65°C in an oil bath for approximately 20 hours under argon gas with AIBN (α,α'- Azoisobutyronitrile, Sigma-Aldrich) (0.5927 g, 0.90 wt% based on the total monomers' weight) as initiator. The copolymer was precipitated in CH3OH (methanol) and dried under vacuum.
[0061] "4-VBC-co-St" or "poly(4-vinylbenzyl chloride co-styrene)" as used here refers to a co-polymer of styrene and 4-vinylbenzyl chloride:
Figure imgf000016_0001
where m > 0 and n > 0.
[0062] "Polystyrene methyimidazolium chloride" (PSMIM-C1) was synthesized by adding 1-methylimidazole (Sigma-Aldrich) (2.8650 g, 034.9 mmol), which is an alkylimidazole, to the solution of the poly(4-VBC-co-St) (5.0034 g, 19.4 mmol) in anhydrous NN- Dimethylformamide (DMF) (Sigma-Aldrich) (30 mL). The mixture was then stirred at around 30°C for around 50 hours to form a PSMIM solution.
[0063] "4-VBC-co-St" or "poly(4-vinylbenzyl chloride co-styrene)" as used here refers to a co-polymer of styrene and 4-vinylbenzyl chloride:
Figure imgf000016_0002
where m > 0 and n > 0.
[0064] Anion exchange membrane polymer PSMIM-DVB was synthesized starting with poly(4-vinylbenzyl chloride co-styrene.) 1-methylimidazole (Sigma-Aldrich) (3.912 g, 47.7 mmol) was added in a 250 ml 3-neck round bottom flask to the solution of the poly(4-VBC- co-St) (15.358 g, 59.8mmol) in anhydrous Ν,Ν-Dimethylformamide (DMF) (Sigma-Aldrich) (105 ml). 0.22 ml of a divinylbenzene (DVB) in DMF solution (DVB concentration = 0.0083 g/ml) was carefully added through a pipette to the mixture with continual magnetic stirring. After this, 0.22 ml of AIBN-DMF solution (AIBN concentration = 0.0083 g/ml) was added to the mixture in a similar fashion. The reaction was then kept under nitrogen atmosphere at 50°C for about 60 hours. PSMIM-DVB was obtained as a white powder after purification by precipitation into diethyl ether.
[0065] Membranes were prepared by casting the PSMIM-DVB solution prepared above directly onto a flat glass surface. The thickness of the solution on the glass was controlled by a film applicator (MTI Corporation, Richmond, CA) with an adjustable doctor blade. The membranes were then dried in a vacuum oven in the following stepwise fashion. They were first kept at 80°C for 120 minutes, then at 100°C for 60 minutes, at 120°C for 30 minutes and finally at 150°C for 60 minutes. Chloride ions in the membranes were removed by soaking the membranes in 1 M KOH solution for 24 hours or longer.
[0066] The cathode layer in Example 1 was prepared as follows. Silver ink was made by mixing 100 mg of silver nanoparticles (20-40 nm, 45509, Alfa Aesar, Ward Hill, MA), 5 mg porous carbon (Vulcan XC-72R, Fuel Cell Earth, Woburn, MA) and different amounts of PSMIM-C1 in 3 ml of ethanol (459844, Sigma-Aldrich). The mixture was then sonicated for 10 minutes. The silver ink was painted onto a gas diffusion layer (Sigracet 35 BC GDL, Ion Power Inc., New Castle, DE) covering an area of 6 cm x 6 cm. The electrode was immersed in 1 M KOH for at least 1 hour so that PSMIM-C1 converted by ion exchange to PSMIM-OH. Then the electrode was cut into 2.5 cm x 2.5 cm sections for cell testing.
[0067] The anode in Example 1 was prepared as follows: 100 mg of IrCh (43396, Alfa Aesar) was dispersed in the mixture of 1 ml of deionized water, 2 ml of isopropanol (3032-16, Macron Fine Chemicals, Avantor Performance Materials, Center Valley, PA) and 0.1 ml of 5 wt.% poly-tetrafluoroethylene (PTFE) dispersion (665800, Sigma-Aldrich). The mixture was sonicated for 10 min using a water bath sonicator. The ink was painted onto 6 cm x 6 cm of carbon fiber paper (Toray Paper 120, Fuel Cell Earth). The actual IrCh loading was about 2 mg/cm2 The electrode was cut into 3 cm x 3 cm sections for cell testing.
[0068] The PSMIM-DVB membrane was sandwiched between the anode and the cathode with the metal-containing layers on the anode and cathode facing the membrane, and the whole assembly was mounted in a Fuel Cell Technologies 5 cm2 fuel cell hardware assembly with serpentine flow fields.
[0069] CCh humidified at 25°C was fed into the cathode flow field at a rate of 20 seem, and 10 mM KHCO3 was fed into the anode flow field. The cyclic voltammograms were collected by scanning the cell voltage from 1.2 to 3.0 V. All of the scans were made at room
temperature and atmospheric pressure.
[0070] FIG. 5 shows the results of the above scans. Plot 200 is a base case with no PSMIM in the cathode catalyst layer ink. It should be noted that the current increases when PSMIM is added to the catalyst layer in a later sample, such that the PSMIM weight is 1% of the weight of the silver (plot 201). Further increases in the current are seen as the PSMIM concentration is increased so that the PSMIM weight is 5% of the weight of the silver (plot 202). Then there is a small decrease when the weight of the PSMIM is increased to 10% of the weight of the silver (plot 203).
[0071] A run in which the PSMIM weight was 20% of the weight of the silver was also performed. The cell showed a small current, but analysis of the exit stream did not show significant CCh conversion.
[0072] These results demonstrate that the addition of an ionomer containing an imidazolium to the cathode catalyst layer enhances the performance of a CCh electrolyzer and the PSMIM polymer is therefore a Helper Polymer.
[0073] Co-pending U.S. patent application Serial No. 15/158,227 provides a number of other examples. The data in the '227 application indicates that polymers containing positively charged cyclic amines can also act as Helper Polymers.
[0074] The example given above is illustrative and is not meant to be an exhaustive list of all possible embodiments, applications or modifications of the invention. Thus, various modifications and variations of the described methods and systems of the invention will be apparent to those skilled in the art without departing from the scope and spirit of the invention. Although the invention has been described in connection with specific embodiments, it should be understood that the invention as claimed should not be unduly limited to such specific embodiments. Indeed, various modifications of the described modes for carrying out the invention which are obvious to those skilled in the chemical arts or in the relevant fields are intended to be within the scope of the appended claims.
[0075] The disclosures of all references and publications cited above are expressly incorporated by reference in their entireties to the same extent as if each were incorporated by reference individually.
[0076] While particular elements, embodiments and applications of the present invention have been shown and described, it will be understood that the invention is not limited thereto since modifications can be made by those skilled in the art without departing from the scope of the present disclosure, particularly in light of the foregoing teachings.

Claims

CLAIMS What is claimed is:
1. A process for making a chemical reaction product, comprising:
(a) combining a Catalytically Active Element and Helper Polymer in the presence of CO2, wherein the Catalytically Active Element is a metal in the form of supported or unsupported particles or flakes with an average size between 0.6 nm and 100 nm;
(b) allowing a reaction to proceed to produce a reaction product; and
(c) applying electrical energy to said reaction to achieve electrochemical conversion of at least a portion of said CO2 to said reaction product;
wherein a polymer P is identifiable as a Helper Polymer for an electrochemical reaction R that is catalyzed by a Catalytically Active Element M by applying a test comprising:
(i) preparing two different membrane electrode assemblies with 5 cm2 of active area: i) one having the polymer P in the cathode catalyst layer; and ii) one otherwise identical but without the polymer P in the cathode catalyst layer, wherein the weight of the polymer in the catalyst layer is 4% of the weight of the catalytically active element M in the catalyst layer;
(ii) mounting both membrane electrode assemblies in a Fuel Cell Technologies 5 cm2 fuel cell hardware assembly with serpentine flow fields;
(iii) providing CO2 humidified at 50°C to the cathode of both cells at a rate of 5 seem with the cell at room temperature and pressure, with the anode side left open to the atmosphere at room temperature and pressure;
(iv) applying a voltage of 1 V to the cell without the polymer P, and then raising the cell voltage to a voltage V such that the output current is as least 20 mA/cm2, then recording the current output of the cell after running for 30 minutes;
(v) applying the same voltage V to the cell with the polymer P and recording the current output of the cell after running for 30 minutes; and
(vi) designating the polymer P as a Helper Polymer if the current is at least 20% higher in the cell with the polymer P in the catalyst layer than the cell without the polymer P in the catalyst layer.
2. The process of claim 1 wherein said Catalytically Active Element is selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, Cu, Sn, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Hf, Ta, W, Re, Ir, Pt, Au, Hg, Al, Si, In, Tl, Pb, Bi, Sb, Te, U, Sm, Tb, La, Ce, and Nd.
3. The process of claim 2 wherein said Catalytically Active Element is selected from the group consisting of Pt, Pd, Au, Ag, Cu, Ni, Fe, Co, Ru and Rh.
4. The process of claim 1 wherein said Helper Polymer is selected from the group consisting of polymers containing positively charged cyclic amines, phosphines, imidazoliums, pyridiniums, pyrrolidiniums, phosphoniums, sulfoniums, prolinates, methioninates, and cholines.
5. The process of claim 1 wherein the reaction products comprise at least one of CO, HCO\ H2CO, (HCO2)-, H2CO2, CH3OH, CH4, C2H4, CH3CH2OH, CH3COO-,
CH3COOH, C2H6, (COOH)2, (COO )2, and CF3COOH.
6. The process of claim 5 wherein said reaction product is one of formic acid (H2CO2) and carbon monoxide (CO).
7. The process of claim 1, wherein the Catalytically Active Element is electrically connected to an electrode of an electrochemical device.
8. An electrochemical device adapted to carry out the process of claim 1.
PCT/US2017/025630 2016-04-04 2017-03-31 Electrocatalytic process for carbon dioxide conversion WO2017176600A1 (en)