WO2007079806A1 - Versatz für ein feuerfestes keramisches produkt und daraus gebildetes feuerfestes keramisches produkt - Google Patents

Versatz für ein feuerfestes keramisches produkt und daraus gebildetes feuerfestes keramisches produkt Download PDF

Info

Publication number
WO2007079806A1
WO2007079806A1 PCT/EP2006/010582 EP2006010582W WO2007079806A1 WO 2007079806 A1 WO2007079806 A1 WO 2007079806A1 EP 2006010582 W EP2006010582 W EP 2006010582W WO 2007079806 A1 WO2007079806 A1 WO 2007079806A1
Authority
WO
WIPO (PCT)
Prior art keywords
ceramic product
offset according
offset
refractory
mass
Prior art date
Application number
PCT/EP2006/010582
Other languages
English (en)
French (fr)
Inventor
Christian Majcenovic
Dieter Pirkner
Original Assignee
Refractory Intellectual Property Gmbh & Co. Kg
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Refractory Intellectual Property Gmbh & Co. Kg filed Critical Refractory Intellectual Property Gmbh & Co. Kg
Priority to EP06806683A priority Critical patent/EP1966106A1/de
Publication of WO2007079806A1 publication Critical patent/WO2007079806A1/de

Abstract

Die Erfindung betrifft einen Versatz für ein bei bestimmungsgemäßer Anwendung feuerfestes keramisches Produkt, beispielsweise einen Formkörper oder eine Gießmasse.

Description

Versatz für ein feuerfestes keramisches Produkt und daraus gebildetes feuerfestes keramisches Produkt
B e s c h r e i b u n g
Die Erfindung betrifft einen Versatz für ein bei bestimmungsgemäßer Anwendung feuerfestes keramisches Produkt, beispielsweise einen Formkörper oder eine Gießmasse.
Feuerfeste keramische Produkte, und zwar sowohl Massen (wie Gießmassen, Spritzmassen, Stampfmassen, Mörtel) als auch Formteile (wie Ziegel, Quader, Kegel, Platten), finden zur Auskleidung metallurgischer Schmelzgefäße ebenso Anwendung wie zur Verwendung als Funktionalteile (wie Schieberplatten, Hülsen, Stopfen, Lanzen, Rohre), insbesondere im Rahmen sekundärmetallurgischer Verfahren. -I-
Dies gilt sowohl für bestimmungsgemäße Anwendungen in der Eisenmetall- Industrie wie für Anwendungen in der Nichteisenmetall-Industrie.
Das feuerfeste Material kommt nicht nur mit den metallurgischen Schmelzen, sondern auch mit korrespondierenden Schlacken in Berührung. Insoweit unterliegt das Feuerfestmaterial einem erheblichen Verschleiß, insbesondere einem Verschleiß durch einen chemischen/metallurgischen Korrosionsangriff, wobei eine Infiltration von Schmelze und/oder Schlacke in das Feuerfestmaterial eine Verschleißursache sein kann.
In diesem Zusammenhang ist die Verwendung von Additiven bekannt, die zu einer Verringerung des Verschleißes des Feuerfestmaterials führen können. Diese Additive (Versatz-Bestandteile), die das fertige Feuerfestmaterial korrosionsstabiler machen sollen und/oder die das Feuerfestmaterial besser vor Infiltrationen von Fremdstoffen schützen, werden nachstehend als „Korrosions-/Infiltrationsinhibitoren" bezeichnet. Bariumsulfat (BaSO4) und Calciumfluorid (CaF2) sind solche Stoffe.
Bariumsulfat zerfällt jedoch bei höheren Temperaturen. Zum Beispiel im Kontakt mit Bauxit aus dem Versatz des Feuerfest-Produkts reagiert BaSO4 zu Celsian (BaAl2Si2Oe) und die Schutzwirkung des Additivs geht verloren. Dies gilt insbesondere im Temperaturbereich > 900° C.
Beispielsweise durch Verwendung moderner Brenner kann eine feuerfeste Auskleidung in einem Schmelzgefäß beim Aufheizen zwischen 1 100 und 1250° C heiß werden. Sie ist dann oft heißer als die nachfolgend im Gefäß behandelte Schmelze. BaSO4 versagt dann als Verschleißschutz vollständig.
CaF2 ist zwar thermisch stabiler als BaSO4, die infiltrations-/korrosions- hemmende Wirkung ist jedoch schlechter als bei Verwendung von BaSO4. Der Erfindung liegt insofern die Aufgabe zugrunde, eine Möglichkeit aufzuzeigen, das Infiltrations-/Korrosionsverhalten feuerfester keramischer Produkte insbesondere auch im Hochtemperatur-Anwendungsbereich (> 1.200° Celsius) zu verbessern.
In Versuchen wurde festgestellt, dass durch Calciumsulfat im Versatz der Verschleiß eines zugehörigen gebrannten fertigen Produktes drastisch herabsetzt wird, und zwar ohne negative Auswirkungen auf das mechanische Verhalten der Produkte und ohne negative Auswirkungen auf die Temperaturbeständigkeit und Temperaturwechselbeständigkeit.
Das Calciumsulfat kann wasserfrei, also als Anhydrit (CaSO4), oder wasserhaltig, beispielsweise als Halbhydrat (CaSO4 • Vi H2O) oder Dihydrat (CaSO4 • 2 H2O) eingesetzt werden, als feines Pulver oder auch in verschiedenen gröberen Kornfraktionen.
Die spezifische Oberfläche nach Blaine kann beispielsweise > 2000 cm2/g betragen. Sie kann über 4000 cm2/g liegen und Werte > 7000 cm2/g erreichen. Der Rückstand auf einem Sieb gemäß DIN 4188 beträgt dann beispielsweise: R 0,02 mm: > 40 %, R 0,02 mm > 25 % oder R 0,02 mm: < 20 %. Üblicherweise ist die spezifische Oberfläche nach Blaine > 1000 cm2/g.
Die genannten korrosionshemmenden Substanzen (Additive) werden als Versatzkomponente eingesetzt, gegebenenfalls auch dem fertigen Produkt zugesetzt, zum Beispiel mittels Vakuumbehandlung infiltriert. Bei anschließender Temperaturbehandlung (beim Brand/Sintern der Produkte oder bei ihrer bestimmungsgemäßen Anwendung) zersetzt sich das CaSO4 zwar, bildet aber mit dem umgebenden Feuerfestmaterial neue Verbindungen, die ebenfalls infiltrations/-korrosionshemmend sind. Die Gründe/Phänomene dafür sind noch nicht abschließend vollständig geklärt. Es wurde aber unter anderem festgestellt, dass CaSO4 bei höheren Temperaturen mit Aluminiumoxid aus dem refraktären Produkt zu Yeelimit (Ca4AIoOi2SO4) reagiert. Yeelimit ist bis > 1200° C beständig und übernimmt offensichtlich bei höheren Temperaturen die Schutzfunktion des Calciumsulfat-Additivs.
In ihrer allgemeinsten Ausführungsform umfasst die Erfindung einen Versatz für ein bei bestimmungsgemäßer Anwendung feuerfestes keramisches Produkt, der
a) 75 - 99,5 Masse-% mindestens einer refraktären Grundkomponente und b) 0,5 - 25 Masse-% mindestens eines Additivs aus der Gruppe: Calciumsulfat, Calciumsulfathydrat
enthält.
Refraktäre Grundkomponenten sind Stoffe (Verbindungen, wie Oxide), die feuerfest sind oder bei höheren Temperaturen (> 900° C) feuerfest werden. Sie werden erfindungsgemäß in Korngrößen < 6 mm eingesetzt und können einen Feinkornanteil (< 250 μm) enthalten.
Verschiedene Weiterbildungen ergeben sich aus den Merkmalen der Unteransprüche und den sonstigen Beschreibungsunterlagen. Der Rohstoffversatz ist entsprechend einzustellen, sofern die korrosions- hemmende(n) Komponente(n) nicht erst durch Tränkung des fertigen gebrannten Produktes eingebracht wird (werden). Der Versatz enthält also entsprechende Additive (Zusatzmittel). Die Menge der infiltrations- hemmenden Komponente im Versatz kann auf < 15, < 10, < 7, < 5, bis < 3 M.-%, bezogen auf den Gesamtversatz aus refraktärer Grundkomponente und Zusatzmittel, eingestellt werden. Meist beträgt ihr Anteil > 1 , > 3 oder > 5 M.-%. Entsprechend erhöht beziehungsweise verringert sich der Anteil der refraktären Grundkomponente (Summe aus refraktären Grundkomponenten und Additiven jeweils auf 100 M.-% gerechnet).
Ebenso ist es möglich, weitere Komponenten dem Versatz zuzumischen, beispielsweise ein Bindemittel, z.B. auf Phosphat- oder Zementbasis, oder Antioxidantien (Gesamtsumme aller Versatzkomponenten dann wiederum auf 100 M.-% addiert).
Die Erfindung schließt die Verarbeitung des Versatzes zu keramisch gebundenen feuerfesten Produkten ebenso ein wie die Verarbeitung zu chemisch gebundenen Produkten. Die feuerfesten keramischen Produkte können monolithische Massen, Mörtel, Formteile, beispielsweise in Form von Steinen, Platten, Hülsen oder dergleichen sein.
Soweit Massen angesprochen sind schließt dies auch hydraulisch gebundene Massen ein.
Eine geeignete Grundkomponente kann zumindest anteilig eine nichtbasische Grundkomponente sein, beispielsweise aus der Gruppe: Tonerde, Korund, ZrO2, Zirkonsilikat (ZrO2 . SiO2), Mullit, TiO2, SiC, Andalusit, Chromoxid, Mikrosilika. Allerdings sind Cr2Ü3-freie Produkte bevorzugt. Auf BaSO4 und/oder CaF2 kann verzichtet werden. Ein entsprechender Versatz kann in üblicher Weise aufbereitet werden, beispielsweise durch Vermischen der refraktären Grundkomponente(n) mit dem Additiv (den Additiven) und einem Bindemittel, anschließender Formgebung (zum Beispiel durch Pressen) und Brand zur Sinterung, insbesondere bei Temperaturen > 1.200° Celsius.
Die Erfindung wird nachstehend anhand von vier Versätzen beispielhaft dargestellt:
Beispiel 1 : Versatz für eine Gießmasse
Figure imgf000007_0001
Beispiel 2: Versatz für eine Stampfmasse
Figure imgf000007_0002
Beispiel 3 : Versatz für einen zu pressenden Stein
Figure imgf000008_0001
Beispiel 4: Versatz für eine Spritzmasse
Figure imgf000008_0002
Aus dem Versatz gemäß Beispiel 1 wurden vier Prüfkörper der Größe 25x25x51 mm hergestellt. An diesen Probekörpern wurde der so genannte „füll immersion test" durchgeführt, wie er sich aus „Aluminium Transactions, Vol. 3, No. 1 , 2000, 105-120" ergibt, auf den Bezug genommen wird. Dabei wurden die Probekörper mit Abstand zueinander auf den Boden eines mit Siliziumcarbid-Gießmasse ausgekleideten Prüfgefäßes gestellt, welches mit 3,5 kg einer Aluminiumschmelze nachstehender Spezifierung so gefüllt war, dass die Prüfkörper komplett von der Schmelze überdeckt waren.
Die Oberfläche des Schmelzbades wurde mit einem Salz abgedeckt, um eine Oxidation zu vermeiden. Die Prüfkörper, die jeweils mindestens eine Oberfläche in Kontakt mit der Schmelze aufwiesen, die durch ein Schneidwerkzeug freigelegt wurde, blieben 4 Tage (96 Stunden) in der auf 850° C gehaltenen Schmelze, wobei die Schmelzzusammensetzung jeweils nach 24 Stunden nachreguliert wurde.
Zusammensetzung der Aluminiumschmelze:
Figure imgf000009_0001
An dem bei 1200° C vorgebrannten Prüfkörpern wurde keine durchgehende Anhaftung von Metall festgestellt. Es konnte keine makroskopisch sichtbare Infiltration festgestellt werden. Mikroskopisch ergab sich eine dünne, circa 500 μm starke Reaktionszone im Oberflächenbereich der Prüfkörper. Weitere Untersuchungen ergaben, dass Calziumsulfat als solches nicht mehr vorhanden war. Dagegen konnte in der Probe ein Anteil an Yeelimit (Ca4AIoOi2SO4) festgestellt werden. Yeelimit hatte sich dabei insbesondere im Grenzflächenbereich des zuvor von Calziumsulfat eingenommenen Raumes zum umgebenden Matrixmaterial gebildet.
Die aus einem Versatz der genannten Art gebildeten ungebrannten oder gebrannten Produkte, letztere mit einem Gehalt an Yeelimit, sind ebenfalls Gegenstand der Erfindung.

Claims

Versatz für ein feuerfestes keramisches Produkt und daraus gebildetes feuerfestes keramisches ProduktA n s p r ü c h e
1. Versatz für ein bei bestimmungsgemäßer Anwendung feuerfestes keramisches Produkt, der a) 75 - 99,5 Masse-% mindestens einer refraktären Grundkomponente und b) 0,5 - 25 Masse-% mindestens eines Additivs aus der Gruppe:
Calciumsulfat, Calciumsulfathydrat enthält.
2. Versatz nach Anspruch 1 , bei dem der Anteil des Additivs < 10 Masse-% beträgt.
3. Versatz nach Anspruch 1 , bei dem der Anteil des Additivs < 5 Masse-% beträgt.
4. Versatz nach Anspruch 1 , bei dem der Anteil des Additivs > 1 Masse-% beträgt.
5. Versatz nach Anspruch 1 , bei dem der Anteil des Additivs > 5 Masse-% beträgt.
6. Versatz nach Anspruch 1 , bei dem mindestens eine refraktäre Grundkomponente eine nicht-basische Grundkomponente ist.
7. Versatz nach Anspruch 6, bei dem die nicht-basische Grundkomponente zumindest anteilig aus der Gruppe: Tonerde, Bauxit, Korund, ZrO2, Siliziumcarbid, Andalusit, Chromoxid, Mikrosilika, Zirkonsilikat, Mullit, TiO2 stammt.
8. Versatz nach Anspruch 1 , bei dem das Additiv als feinteiliges Pulver mit einer spezifischen Oberfläche nach Blaine > 1000 cm2/g vorliegt.
9. Versatz nach Anspruch 1 , der bis auf etwaige Verunreinigungen frei von mindestens einer der folgenden Bestandteile ist: BaSO4, CaF2 Cr2O3.
10. Ungebranntes keramisches Produkt, hergestellt aus einem Versatz nach Anspruch 1.
1 1 . Gebranntes feuerfestes keramisches Produkt, hergestellt aus einem Versatz gemäß Anspruch 1 mit einem Anteil an Yeelimit (Ca4Al6Oi2SO4).
PCT/EP2006/010582 2005-12-23 2006-11-04 Versatz für ein feuerfestes keramisches produkt und daraus gebildetes feuerfestes keramisches produkt WO2007079806A1 (de)