[go: up one dir, main page]

TWI655278B - Liquid crystal composition and display device thereof - Google Patents

Liquid crystal composition and display device thereof Download PDF

Info

Publication number
TWI655278B
TWI655278B TW105133551A TW105133551A TWI655278B TW I655278 B TWI655278 B TW I655278B TW 105133551 A TW105133551 A TW 105133551A TW 105133551 A TW105133551 A TW 105133551A TW I655278 B TWI655278 B TW I655278B
Authority
TW
Taiwan
Prior art keywords
liquid crystal
compound
crystal composition
weight
total weight
Prior art date
Application number
TW105133551A
Other languages
English (en)
Other versions
TW201718832A (zh
Inventor
徐海彬
韓文明
徐爽
王盼盼
王莉
Original Assignee
大陸商江蘇和成顯示科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大陸商江蘇和成顯示科技有限公司 filed Critical 大陸商江蘇和成顯示科技有限公司
Publication of TW201718832A publication Critical patent/TW201718832A/zh
Application granted granted Critical
Publication of TWI655278B publication Critical patent/TWI655278B/zh

Abstract

本發明提供一種液晶組合物，它包含一種或多種選自通式I的化合物組成的組；一種或多種選自通式II的化合物組成的組；一種或多種選自通式III的化合物組成的組。本發明的液晶組合物具有合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性好等優點，本發明所述的液晶組合物可適用於VA或IPS/FFS液晶顯示器件中。

Description

液晶組合物及其顯示器件
本發明涉及一種合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性的液晶組合物，以及包含所述液晶組合物的的液晶顯示器件。
液晶顯示器件用於資訊顯示的眾多領域，可用於直視顯示器也用於投影型顯示器。
根據顯示模式的類型分為PC(phase change，相變)、TN(twist nematic，扭曲向列)、STN(super twisted nematic，超扭曲向列)、ECB(electrically controlled birefringence，電控雙折射)、OCB(optically compensated bend，光學補償彎曲)、IPS(in-plane switching，共面轉變)、VA(vertical alignment，垂直配向)等類型。
工作在TN、STN模式的元件使用正介電各項異性液晶，而工作在VA模式的元件使用負介電各項異性液晶，IPS模式既可使用正介電各項異性液晶，也可使用負介電各項異性液晶。其中，IPS顯示模式具有良好的視角特性和改善的回應時間，被越來越多的用於多媒體應用(例如手機、平板電腦)，乃至用於TV及桌面監視器。
隨著技術的發展，人們對顯示器件的要求在不斷提高，如趨於完美的現實效果、低功耗、快回應、壽命長等，這也從側面要求液晶材 料不斷提升性能參數。
含有光學各向異性適當的液晶材料的液晶顯示器件能夠增大對比度。不同的液晶顯示模式對光學各項異性的要求是不一樣的，光學各項異性變小可獲得較寬的視角。
含有粘度小的液晶材料的液晶顯示器件能夠縮短回應時間。當液晶顯示器件的回應時間短時，可適用於動畫顯示。
含有介電各項異性大的液晶材料，可降低液晶的閾值電壓，進一步降低消耗電功率，但介電越大越容易被光熱電破壞造成離子析出，從而導致電阻率降低。
此外，液晶組合物對紫外線(UV)的穩定性及熱穩定性與液晶顯示器件的壽命相關聯。提高液晶組合物對紫外線(UV)的穩定性及熱穩定性可延長液晶顯示器件的壽命。
現有技術無法兼顧合適大的介電各項異性、快回應、抗UV及高溫穩定的性能均衡問題，不能同時滿足各方面指標。因此，為了獲得穩定的液晶顯示狀態，達到上述要求，通過液晶材料的優化來提供合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性，是本領域技術人員的努力方向。
從液晶材料的製備角度出發，液晶材料的各項性能是互相牽制影響的，某項性能指標的提升可能會使其它性能發生變化。因此，製備各方面性能都合適的液晶材料往往需要創造性勞動。
本發明的目的是提供一種合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性的液晶組合物。
發明目的：本發明的目的是提供一種具有合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性的液晶組合物。
本發明的另一目的是提供一種液晶顯示器件，其包含具有合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性的液晶組合物。
技術方案：為了實現上述發明目的，本發明提供一種液晶組合物，所述液晶組合物包含：一種或多種選自通式I的化合物組成的組 一種或多種選自通式II的化合物組成的組；以及一種或多種選自通式III的化合物組成的組 其中，R1和R2相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R3和R4相同或不同，各自獨立地表示碳原子數為1-10的直鏈烷基；R5和R6相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳 原子數為1-7的直鏈烷氧基；碳原子數為2-7的直鏈烯基；m和n相同或不同，各自獨立地表示1或2；環或相同或不同，各自獨立地表示或 當n表示2時，兩個環相同或不同，各自獨立地表示或
在本發明的實施方案中，優選地所述通式I的化合物選自由下列化合物組成的組：；以及 其中，R1表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R2表示碳原子數為1-7的直鏈烷氧基，優選地所述通式II的化合物選自由下列化合物組成的組： 其中， R3和R4相同或不同，各自獨立地表示碳原子數為2-8的直鏈烷基，優選地所述通式III的化合物選自由下列化合物組成的組： ；以及 其中，R5和R6相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；碳原子數為2-7的直鏈烯基。
在本發明的實施方案中，更優選地所述通式I的化合物選自由下列化合物組成的組： ；以及 更優選地所述通式II的化合物選自由下列化合物組成的組： ；以及 更優選地所述通式III的化合物選自由下列化合物組成的組： ；以及
在本發明的實施方案中，所述液晶組合物還包含：一種或多種通式IV和/或V的化合物 其中，R7、R8、R9和R10相同或不同，各自獨立地表示碳原子數為1-7的直鏈 烷基、碳原子數為1-7的直鏈烷氧基；p表示1或2；Z1表示單鍵、-CH2O-、-COO-。
在本發明的實施方案中，優選地所述通式IV的化合物選自由下列化合物組成的組： ；以及 其中，R7表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R8表示碳原子數為1-7的直鏈烷氧基，所述通式V的化合物選自由下列化合物組成的組： 其中，R9表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R10表示碳原子數為1-7的直鏈烷氧基。
在本發明的實施方案中，更優選地所述通式IV的化合物選自由下列化合物組成的組： ；以及 所述通式V的化合物選自由下列化合物組成的組： ；以及
在本發明的實施方案中，所述液晶組合物還包含：一種或更多種選自通式VI的化合物組成的組 其中，R11和R12相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；環或相同或不同，各自獨立地表示 Z2表示單鍵、-CH2O-或-COO-。
在本發明的實施方案中，優選地所述通式VI的化合物選自由下列化合物組成的組： ；以及 其中，R11和R12相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基。
在本發明的實施方案中，更優選地所述通式VI的化合物選自由下列化合物組成的組： ；以及
作為優選方案，本發明所述的液晶組合物中，通式I的化合物的重量百分含量為1-25%；通式II的化合物的重量百分含量為1-20%；通式III的化合物的重量百分含量為30-75%；通式IV和/或V的化合物的重量百分含量為10-50%；通式VI的化合物的重量百分含量為0-10%。
作為優選方案，本發明所述的液晶組合物中，通式I的化合物的重量百分含量為1-20%；通式II的化合物的重量百分含量為1-15%；通式III的化合物的重量百分含量為30-70%；通式IV和/或V的化合物的重量百分含量為10-45%；通式VI的化合物的重量百分含量為0-10%。
作為優選方案，本發明所述的液晶組合物中，通式I的化合物的重量百分含量為5-15%；通式II的化合物的重量百分含量為1-10%； 通式III的化合物的重量百分含量為40-70%；通式IV和/或V的化合物的重量百分含量為15-43%；通式VI的化合物的重量百分含量為0-5%。
作為優選方案，本發明所述的液晶組合物中，通式I的化合物的重量百分含量為5-15%；通式II的化合物的重量百分含量為1-10%；通式III的化合物的重量百分含量為40-70%；通式IV的化合物的重量百分含量為9-19%；通式V的化合物的重量百分含量為6-24%；通式VI的化合物的重量百分含量為1-5%。
作為優選方案，本發明所述的液晶組合物包括：占所述液晶組合物總重量4%的化合物I-1-1；占所述液晶組合物總重量4%的化合物I-1-2；占所述液晶組合物總重量4%的化合物I-1-3；占所述液晶組合物總重量4%的化合物II-1；占所述液晶組合物總重量7%的化合物III-3-3；占所述液晶組合物總重量35%的化合物III-1-4；占所述液晶組合物總重量7%的化合物III-5-1；占所述液晶組合物總重量5%的化合物IV-3-3；占所述液晶組合物總重量5%的化合物IV-3-2；占所述液晶組合物總重量4%的化合物IV-4-2；占所述液晶組合物總重量7%的化合物V-1；占所述液晶組合物總重量7%的化合物V-2；以及占所述液晶組合物總重量7%的化合物V-8，或者，所述液晶組合物包括： 占所述液晶組合物總重量5%的化合物I-1-1；占所述液晶組合物總重量4%的化合物I-1-2；占所述液晶組合物總重量4%的化合物I-1-3；占所述液晶組合物總重量6%的化合物II-1；占所述液晶組合物總重量6%的化合物III-3-3；占所述液晶組合物總重量31%的化合物III-1-4；占所述液晶組合物總重量3%的化合物III-5-1；占所述液晶組合物總重量6%的化合物IV-3-3；占所述液晶組合物總重量6%的化合物IV-4-1；占所述液晶組合物總重量6%的化合物IV-4-2；占所述液晶組合物總重量7%的化合物V-1；占所述液晶組合物總重量8%的化合物V-2；以及占所述液晶組合物總重量8%的化合物V-8，或者，所述液晶組合物包括：占所述液晶組合物總重量4%的化合物I-1-1；占所述液晶組合物總重量4%的化合物I-1-2；占所述液晶組合物總重量4%的化合物I-1-3；占所述液晶組合物總重量6%的化合物II-1；占所述液晶組合物總重量5%的化合物III-3-3；占所述液晶組合物總重量33%的化合物III-1-4；占所述液晶組合物總重量5%的化合物III-4-3；占所述液晶組合物總重量4%的化合物IV-1-1； 占所述液晶組合物總重量4%的化合物IV-1-3；占所述液晶組合物總重量4%的化合物IV-1-7；占所述液晶組合物總重量6%的化合物V-1；占所述液晶組合物總重量7%的化合物V-2；占所述液晶組合物總重量6%的化合物V-8；占所述液晶組合物總重量5%的化合物V-5；以及占所述液晶組合物總重量3%的化合物VI-3-1，或者，所述液晶組合物包括：占所述液晶組合物總重量5%的化合物I-1-1；占所述液晶組合物總重量5%的化合物I-1-2；占所述液晶組合物總重量4%的化合物I-1-3；占所述液晶組合物總重量7%的化合物II-1；占所述液晶組合物總重量4%的化合物III-3-3；占所述液晶組合物總重量30%的化合物III-1-4；占所述液晶組合物總重量5%的化合物IV-1-1；占所述液晶組合物總重量5%的化合物IV-1-3；占所述液晶組合物總重量5%的化合物IV-1-7；占所述液晶組合物總重量4%的化合物IV-2-1；占所述液晶組合物總重量6%的化合物V-I；占所述液晶組合物總重量6%的化合物V-2；占所述液晶組合物總重量6%的化合物V-8；占所述液晶組合物總重量6%的化合物V-5；以及 占所述液晶組合物總重量2%的化合物VI-3-1，或者，所述液晶組合物包括：占所述液晶組合物總重量4%的化合物I-1-1；占所述液晶組合物總重量3%的化合物I-1-2；占所述液晶組合物總重量4%的化合物II-1；占所述液晶組合物總重量3%的化合物II-2；占所述液晶組合物總重量21%的化合物III-1-1；占所述液晶組合物總重量12%的化合物III-1-2；占所述液晶組合物總重量7%的化合物III-3-3；占所述液晶組合物總重量8%的化合物III-2-1；占所述液晶組合物總重量8%的化合物III-4-3；占所述液晶組合物總重量5%的化合物III-4-4；占所述液晶組合物總重量9%的化合物III-5-1；占所述液晶組合物總重量4%的化合物IV-1-1；占所述液晶組合物總重量6%的化合物IV-2-1；以及占所述液晶組合物總重量6%的化合物V-2，或者，所述液晶組合物包括：占所述液晶組合物總重量4%的化合物I-1-1；占所述液晶組合物總重量4%的化合物I-1-2；占所述液晶組合物總重量4%的化合物I-2-1；占所述液晶組合物總重量3%的化合物II-1；占所述液晶組合物總重量20%的化合物III-1-1； 占所述液晶組合物總重量15%的化合物III-1-2；占所述液晶組合物總重量10%的化合物III-3-3；占所述液晶組合物總重量10%的化合物III-2-1；占所述液晶組合物總重量7%的化合物III-4-3；占所述液晶組合物總重量8%的化合物III-5-1；占所述液晶組合物總重量4%的化合物IV-1-1；占所述液晶組合物總重量5%的化合物IV-2-1；以及占所述液晶組合物總重量6%的化合物V-2。
本發明的另一個方面是提供一種包含合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性的液晶組合物的液晶顯示器件。
本發明通過大量實驗篩選，優選得到本發明的液晶組合物具有合適大的介電各項異性、快回應、對紫外線(UV)及高溫穩定性等特性，本發明所述的液晶組合物適用於VA或IPS/FFS液晶顯示器件中。
在本發明中如無特殊說明，所述的比例均為重量比，所有溫度均為攝氏度溫度，所述的回應時間資料的測試選用的盒厚為4μm。
以下將結合具體實施方案來說明本發明。需要說明的是，下面的實施例為本發明的示例，僅用來說明本發明，而不用來限制本發明。在不偏離本發明主旨或範圍的情況下，可進行本發明構思內的其他組合和各種改良。
為便於表達，以下各實施例中，液晶組合物的基團結構用表1所列的代碼表示：
以如下結構式的化合物為例：
該結構式如用表1所列代碼表示，則可表達為：mCPWn，代碼中的m表示左端烷基的碳原子數，例如m為“2”，即表示該烷基為-C2H5；代碼中的C代表“環己烷基”，代碼中的P代表“1,4-亞苯基”，代碼中的W代表“2,3-二氟-1,4-亞苯基”，代碼中的n表示左端烷基的碳原子數，例如n為“2”，即 表示該烷基為-C2H5。
以下實施例中測試專案的簡寫代號如下：
其中，光學各向異性使用阿貝折光儀在鈉光燈(589nm)光源下、25℃測試得；V10測試條件：DMS505/方波/1KHZ，4μm VA cell；△ε=ε｜｜-ε⊥，其中，ε｜｜為平行于分子軸的介電常數，ε⊥為垂直于分子軸的介電常數，測試條件：25℃、1KHz、6μm VA cell；VHR(初始)是使用TOY06254型液晶物性評價系統測試得；測試溫度為60℃，測試電壓為5V，測試頻率為6Hz；VHR(UV)是使用TOY06254型液晶物性評價系統測試得；使用波長為365nm、能量為6000mJ/cm2的光照射液晶後測試，測試溫度60℃，測試電壓為5V，測試頻率為6Hz； VHR(高溫)是使用TOY06254型液晶物性評價系統測試得；液晶在150℃下高溫保持1h後測試，測試溫度60℃，測試電壓為5V，測試頻率為6Hz；在以下的實施例中所採用的各成分，均可以通過公知的方法進行合成，或者通過商業途徑獲得。這些合成技術是常規的，所得到各液晶化合物經測試符合電子類化合物標準。
按照以下實施例規定的各液晶組合物的配比，製備液晶組合物。所述液晶組合物的製備是按照本領域的常規方法進行的，如採取加熱、超聲波、懸浮等方式按照規定比例混合制得。
製備並研究下列實施例中給出的液晶組合物。下面顯示了各液晶組合物的組成和其性能參數測試結果。
對比例1
以表2所列的各化合物及重量百分數配製成對比例1的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
對比例2
以表3所列的各化合物及重量百分數配製成對比例2的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例1
按表4中所列的各化合物及重量百分數配製成實施例1的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例2
按表5中所列的各化合物及重量百分數配製成實施例2的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例3
按表6中所列的各化合物及重量百分數配製成實施例3的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例4
按表7中所列的各化合物及重量百分數配製成實施例4的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例1、實施例3分別與對比例1、對比例2相比，該液晶組合物具有較小的旋轉粘度和回應時間，較好的穩定性，在合適的介電各項異性下能同時兼顧快回應和高可靠性的要求，適用於VA或IPS/FFS液晶顯示器件。
實施例2、實施例4分別與對比例1、對比例2相比，該液晶組合物在兼顧快回應和高可靠性的要求的同時具有大的介電各項異性， 適用於VA或IPS/FFS液晶顯示器件。
對比例3
以表8所列的各化合物及重量百分數配製成對比例3的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例5
按表9中所列的各化合物及重量百分數配製成實施例5的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下 表所示：
實施例6
按表10中所列的各化合物及重量百分數配製成實施例6的液晶組合物，其填充於液晶顯示器兩基板之間進行性能測試，測試資料如下表所示：
實施例5、實施例6分別與對比例3相比，該液晶組合物具有較小的旋轉粘度和回應時間，較好的穩定性，在合適的介電各項異性下能同時兼顧快回應和高可靠性的要求，適用於VA或IPS/FFS液晶顯示器件。
以上所述，僅是本發明的較佳實施例而已，並非對本發明作任何形式上的限制，雖然本發明已以較佳實施例揭露如上，然而並非用以限定本發明，任何熟悉本專業的技術人員，在不脫離本發明技術方案範圍內，當可利用上述揭示的技術內容作出些許更動或修飾為等同變化的等效實施例，但凡是未脫離本發明技術方案內容，依據本發明的技術實質對以上實施例所作的任何簡單修改、等同變化與修飾，均仍屬於本發明技術方案的範圍內。

Claims (9)

  1. 一種液晶組合物，包含：一種或多種選自通式I的化合物 一種或多種選自通式II的化合物；以及一種或多種選自通式III的化合物 其中，通式I的化合物的重量百分含量為1-25%；通式II的化合物的重量百分含量為1-20%；通式III的化合物的重量百分含量為30-75%；R1和R2相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R3和R4相同或不同，各自獨立地表示碳原子數為1-10的直鏈烷基；R5和R6相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；碳原子數為2-7的直鏈烯基；m和n相同或不同，各自獨立地表示1或2；環或相同或不同，各自獨立地表示或 當n表示2時，兩個環相同或不同，各自獨立地表示或該液晶組合物還包含：一種或多種選自通式IV和/或V的化合物 其中，通式IV和/或V的化合物的重量百分含量為10-50%；R7、R8、R9和R10相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；p表示1或2；Z1表示單鍵、-CH2O-、-COO-；以及一種或多種選自通式VI的化合物 其中，通式VI的化合物的重量百分含量為0-10%；R11和R12相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基或碳原子數為1-7的直鏈烷氧基；環或相同或不同，各自獨立地表示 Z2表示單鍵、-CH2O-或-COO-。
  2. 如申請專利範圍第1項所述之液晶組合物，其中，該通式I的化合物選自由下列化合物：；以及 其中，R1表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R2表示碳原子數為1-7的直鏈烷氧基，該通式II的化合物選自由下列化合物： 其中，R3和R4相同或不同，各自獨立地表示碳原子數為2-8的直鏈烷基；該通式III的化合物選自由下列化合物： ；以及 其中，R5和R6相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；碳原子數為2-7的直鏈烯基。
  3. 如申請專利範圍第2項所述之液晶組合物，其中，該通式I的化合物選自由下列化合物： ；以及 該通式II的化合物選自由下列化合物： ；以及 該通式III的化合物選自由下列化合物： ；以及
  4. 如申請專利範圍第1項所述之液晶組合物，其中，該通式IV的化合物選自由下列化合物： ；以及 其中，R7表示碳原子數為1-7的直鏈烷基或碳原子數為1-7的直鏈烷氧基；R8表示碳原子數為1-7的直鏈烷氧基；該通式V的化合物選自由下列化合物： 其中， R9表示碳原子數為1-7的直鏈烷基、碳原子數為1-7的直鏈烷氧基；R10表示碳原子數為1-7的直鏈烷氧基。
  5. 如申請專利範圍第4項所述之液晶組合物，其中，該通式IV的化合物選自由下列化合物： 以及 該通式V的化合物選自由下列化合物： ；以及
  6. 如申請專利範圍第1項所述之液晶組合物，其中，該通式VI的化合物選自由下列化合物： ；以及 其中，R11和R12相同或不同，各自獨立地表示碳原子數為1-7的直鏈烷基。
  7. 如申請專利範圍第6項所述之液晶組合物，其中，該通式VI的化合物選自由下列化合物： ；以及
  8. 如申請專利範圍第1至3項中之任一項所述之液晶組合物，其中，該液晶組合物包括：占該液晶組合物總重量4%的化合物I-1-1；占該液晶組合物總重量4%的化合物I-1-2；占該液晶組合物總重量4%的化合物I-1-3；占該液晶組合物總重量4%的化合物II-1；占該液晶組合物總重量7%的化合物III-3-3；占該液晶組合物總重量35%的化合物III-1-4；占該液晶組合物總重量7%的化合物III-5-1；占該液晶組合物總重量5%的化合物IV-3-3；占該液晶組合物總重量5%的化合物IV-3-2；占該液晶組合物總重量4%的化合物IV-4-2；占該液晶組合物總重量7%的化合物V-1；占該液晶組合物總重量7%的化合物V-2；以及占該液晶組合物總重量7%的化合物V-8，或者，該液晶組合物包括：占該液晶組合物總重量5%的化合物I-1-1；占該液晶組合物總重量4%的化合物I-1-2； 占該液晶組合物總重量4%的化合物I-1-3；占該液晶組合物總重量6%的化合物II-1；占該液晶組合物總重量6%的化合物III-3-3；占該液晶組合物總重量31%的化合物III-1-4；占該液晶組合物總重量3%的化合物III-5-1；占該液晶組合物總重量6%的化合物IV-3-3；占該液晶組合物總重量6%的化合物IV-4-1；占該液晶組合物總重量6%的化合物IV-4-2；占該液晶組合物總重量7%的化合物V-1；占該液晶組合物總重量8%的化合物V-2；以及占該液晶組合物總重量8%的化合物V-8，或者，該液晶組合物包括：占該液晶組合物總重量4%的化合物I-1-1；占該液晶組合物總重量4%的化合物I-1-2；占該液晶組合物總重量4%的化合物I-1-3；占該液晶組合物總重量6%的化合物II-1；占該液晶組合物總重量5%的化合物III-3-3；占該液晶組合物總重量33%的化合物III-1-4；占該液晶組合物總重量5%的化合物III-4-3；占該液晶組合物總重量4%的化合物IV-1-1；占該液晶組合物總重量4%的化合物IV-1-3；占該液晶組合物總重量4%的化合物IV-1-7； 占該液晶組合物總重量6%的化合物V-1；占該液晶組合物總重量7%的化合物V-2；占該液晶組合物總重量6%的化合物V-8；占該液晶組合物總重量5%的化合物V-5；以及占該液晶組合物總重量3%的化合物VI-3-1，或者，該液晶組合物包括：占該液晶組合物總重量5%的化合物I-1-1；占該液晶組合物總重量5%的化合物I-1-2；占該液晶組合物總重量4%的化合物I-1-3；占該液晶組合物總重量7%的化合物II-1；占該液晶組合物總重量4%的化合物III-3-3；占該液晶組合物總重量30%的化合物III-1-4；占該液晶組合物總重量5%的化合物IV-1-1；占該液晶組合物總重量5%的化合物IV-1-3；占該液晶組合物總重量5%的化合物IV-1-7；占該液晶組合物總重量4%的化合物IV-2-1；占該液晶組合物總重量6%的化合物V-1；占該液晶組合物總重量6%的化合物V-2；占該液晶組合物總重量6%的化合物V-8；占該液晶組合物總重量6%的化合物V-5；以及占該液晶組合物總重量2%的化合物VI-3-1，或者，該液晶組合物包括： 占該液晶組合物總重量4%的化合物I-1-1；占該液晶組合物總重量3%的化合物I-1-2；占該液晶組合物總重量4%的化合物II-1；占該液晶組合物總重量3%的化合物II-2；占該液晶組合物總重量21%的化合物III-1-1；占該液晶組合物總重量12%的化合物III-1-2；占該液晶組合物總重量7%的化合物III-3-3；占該液晶組合物總重量8%的化合物III-2-1；占該液晶組合物總重量8%的化合物III-4-3；占該液晶組合物總重量5%的化合物III-4-4；占該液晶組合物總重量9%的化合物III-5-1；占該液晶組合物總重量4%的化合物IV-1-1；占該液晶組合物總重量6%的化合物IV-2-1；以及占該液晶組合物總重量6%的化合物V-2，或者，該液晶組合物包括：占該液晶組合物總重量4%的化合物I-1-1；占該液晶組合物總重量4%的化合物I-1-2；占該液晶組合物總重量4%的化合物I-2-1；占該液晶組合物總重量3%的化合物II-1；占該液晶組合物總重量20%的化合物III-1-1；占該液晶組合物總重量15%的化合物III-1-2；占該液晶組合物總重量10%的化合物III-3-3； 占該液晶組合物總重量10%的化合物III-2-1；占該液晶組合物總重量7%的化合物III-4-3；占該液晶組合物總重量8%的化合物III-5-1；占該液晶組合物總重量4%的化合物IV-1-1；占該液晶組合物總重量5%的化合物IV-2-1；以及占該液晶組合物總重量6%的化合物V-2。
  9. 一種液晶顯示器件，該液晶顯示器件包含如申請專利範圍第1至3、4至5及6至8項中任一項所述之液晶組合物。
TW105133551A 2015-11-19 2016-10-18 Liquid crystal composition and display device thereof TWI655278B (zh)