(54) СПОСОБ ОТБЕЛКИ ЦЕЛЛЮЛОЗЫ(54) PULSE BLEACHING METHOD

.и;;Д :ii;; U.:rtyB.i ;; D: ii ;; U.:rtyB

33

теми же бел щими реагентами при том же их расходе, что и в предыдущих опытах. Кроме того, эта же целлюлоза была добелена до белизны, полученной в опыте 2, известнымthe same bleaching reagents with the same consumption as in previous experiments. In addition, the same pulp was added to the whiteness obtained in experiment 2, known

способом - в две ступени, in two steps,

гипохлоритом и двуокисью хлора.hypochlorite and chlorine dioxide.

Результаты всех отбелок приведены в табл. 1. Таблица 1The results of all bleaching are given in table. 1. Table 1

Полученные данные показывают, что кратковременна промежуточна обработка целлюлозы кислотой, не ухудша физико-механических показателей целлюлозы и не увеличива расхода бел щих реагентов, позвол ет получить белизну на 4-7% выше, чем при двухступенчатой отбелке известным способом (опыты 4-5), и такую же, как при трехступенчатой отбелке (опыт 6). При этом стабильность белизны целлюлозы, полученной предлагаемым способом, лучше. Пример 2. Небеленую сульфатную березовую целлюлозу с жесткостью 96 перманганатных единиц и белизной 36,1% подвергают кислородно-щелочной обработке, затем промывают , обрабатывают сернистой кислотой при концентрации массы 10% и рН 2,6 в течение 5 мин. После второй промывки целлюлозу добеливают одним из следующих реагентов: гипохлоритом натри при расходе активного хлора 1,2%; двуокисью хлора при расходе 0,8%; перекисью водорода при расходе 1,3%. Дл сравнени ту же целлюлозу после кислородно-щелочной обработки и промывки добеливали (без обработки Н250з) теми же бел щими реагентами (с тем же расходом ) ; кроме того, добелку целлюлозы осуществл ли и в две ступени - гипохлоритом и двуокисью хлора - до достижени такой же белизны, как и по предлагаемому способу . Результаты приведены в табл. 2. Таблица 2The obtained data show that short-term intermediate treatment of cellulose with acid, without deteriorating the physico-mechanical properties of cellulose and not increasing the consumption of protein reagents, allows to obtain a whiteness 4-7% higher than with two-stage bleaching in a known manner (experiments 4-5), and the same as with a three-stage bleaching (experiment 6). The stability of the white cellulose, obtained by the proposed method is better. Example 2. Unbleached sulphate birch cellulose with a hardness of 96 permanganate units and whiteness of 36.1% is subjected to oxygen-alkali treatment, then washed, treated with sulfuric acid at a mass concentration of 10% and a pH of 2.6 for 5 minutes. After the second washing, the cellulose is added with one of the following reagents: sodium hypochlorite at a flow rate of active chlorine of 1.2%; chlorine dioxide at a flow rate of 0.8%; hydrogen peroxide at a flow rate of 1.3%. For comparison, the same cellulose, after oxygen-alkali treatment and washing, was made (without treatment with H2503) with the same white-colored reagents (with the same consumption); In addition, the finishing of the pulp was carried out in two steps — hypochlorite and chlorine dioxide — to achieve the same whiteness as in the proposed method. The results are shown in Table. 2. Table 2

Эти данные также подтверждают, что белизна целлюлозы, нолучаемой нри отбелке с промежуточной обработкой кислотой, на 3-7% выше, чем при отбелке известным -способом , нри практически одинаковых физикомеханических показател х целлюлозы (опыты 1--3 и 4-5).These data also confirm that the whiteness of cellulose, which is obtained by bleaching with intermediate acid treatment, is 3–7% higher than in bleaching with the known method, and of almost identical physicomechanical indicators of cellulose (experiments 1--3 and 4-5).

Предмет изобретени Subject invention

Claims

1. A method of bleaching pulp with an oxy-alkaline treatment of the original pulp followed by finishing with bleaching agents, characterized in that, in order to increase the whiteness and its stability, the pulp is subjected to an oxygen-alkali treatment before finishing with an acid solution.

2. A method according to claim 1, characterized in that sulfurous acid is used as the acid.

3. Method according to paragraphs. 1 and 2, the difference is that the treatment with an acid solution is carried out at a pH of 2-4.