SU316715A1 - - Google Patents
Info
- Publication number
- SU316715A1 SU316715A1 SU1464390A SU1464390A SU316715A1 SU 316715 A1 SU316715 A1 SU 316715A1 SU 1464390 A SU1464390 A SU 1464390A SU 1464390 A SU1464390 A SU 1464390A SU 316715 A1 SU316715 A1 SU 316715A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- composition
- polymer composition
- peroxide
- methacrylate
- solution
- Prior art date
Description
ПОЛИМЕРНАЯ Известна полимерна композици , состо ща из распвора ненасыщенного полиэфира в диметакриловом эфире триэтиленгликол и вспомогательных добавок, например перекиси, ускорител - б«с-(н- бутилфталата) кобальта . Предлагаетс в полимерную композицию вводить олигодиенуретандиметакрилат в количестве 1,0-15,0 вес. ч. Введение этого соединени позвол ет улучшить адгезионные свойства полимерной композиции. Полимерна композици содержит, вес. ч.: Ненасыщенный полиэфир100 Ди- или олигоэфир метакриловой 50-150 кислоты Олигодиенуретандиметакрилат 1 -15,0 Вспомогательные добавки (наполнитель, инициатор и ускоритель) берут :В обычных дл известных композиций количествах. Дл отверждени полимерной композиции иопользуют любые перекисные инициаторы (гипериз, перекись циклогексанона, перекись метилэтилкетона, перекись бензоила и др.). МПОЗИЦИЯ . -,-,-, г--, о U л Я ; , L,u,...;SBBi г.-:й-;.:;о: шА например быс-(н-бутилфталат) ко-бальта, бнс (н-бутилмалеинат) марганца, бмс-(н-бутилфталат ) ванадила, нафтенат кобальта и другие , или третичные амины, например диметиланилин , диэтилтолуидин и др. В качестве наполнителей употребл ют мел, маршалит, пылевидный молотый кварц, древесную муку и другие в количестве 0,0- 300 вес. ч. на 100 вес. ч. полиэфира. Пример 1. В состав полимерной композиции вход т раствор 54 г полпдиэтиленгликольмалеинатфталата , полученного поликонденсацией 1,5 люль малеинового и 1 моль фталевого ангидридов с 2,62 моль диэтиленгликол , 5 г полифункционального ненасыщенного олигомера - олигодиепуретандиметакрилата - и 150 г молотого пылевидного кварца. При введении в состав клеевой композиции 0,5 г быс-(н-бутилфталата) кобальта и 7 г перекиси циклогексанона клеева композици полностью отверждаетс при 55 ± 5°С за 2 час. Пример 2. В состав полимерной композиции вход т раствор 50 г полидиэтиленгликолъмалеинатфталата (рецептура состава из примера 1) в 25 г диметакрилового эфираPOLYMERIC A polymer composition is known, consisting of an unsaturated polyether solution in triethylene glycol dimethacrylic ether and auxiliary additives, for example, peroxide, an accelerator — cobalt (n-butyl phthalate). It is proposed to introduce oligodienurethanedimethacrylate in the polymer composition in an amount of 1.0-15.0 wt. Part of the introduction of this compound improves the adhesive properties of the polymer composition. The polymer composition contains, by weight. b .: Unsaturated polyether100 Di-or oligoether of methacrylic 50-150 acid Oligodiurethanes methacrylate 1 -15.0 Auxiliary additives (filler, initiator and accelerator) are taken: In the usual amounts of known compositions. In order to cure the polymer composition, any peroxide initiators (hyperies, cyclohexanone peroxide, methyl ethyl ketone peroxide, benzoyl peroxide, etc.) are used. OPTION. -, -, -, g--, about U l I; , L, u, ...; SBBi g .-: y -;.:; O: shA such as bys- (n-butyl phthalate) co-balt, bns (n-butyl maleate) manganese, bms- (n-butyl phthalate) vanadyl, cobalt naphthenate, and others, or tertiary amines, for example, dimethylaniline, diethyltoluidine, etc. The fillers used are chalk, marshallite, powdered ground quartz, wood flour, and others in an amount of 0.0 to 300 wt. hours per 100 weight. including polyester. Example 1. The composition of the polymer composition includes a solution of 54 g of polydiethylene glycol maleate naphthalate obtained by polycondensation of 1.5 lulles of maleic and 1 mol of phthalic anhydrides with 2.62 mol of diethylene glycol, 5 g of a polyfunctional unsaturated oligomer — oligodiapentane methacrylate — and 150 grams of a syrup and 150 grams of a syrup; When 0.5 g of bys- (n-butyl phthalate) cobalt and 7 g of cyclohexanone peroxide are added to the adhesive composition, the adhesive composition cures at 55 ± 5 ° C in 2 hours. Example 2. The composition of the polymer composition includes a solution of 50 g of polydiethylene glycol maleate phthalate (the formulation of the composition of Example 1) in 25 g of dimethacrylic ester
метакрилата и 15 г древесной муки. При введении в композицию I г бис-(н-бутилфатала) марганца и 3 г гидроперекиси изопропилбе зола оца отверждаотс за 4 час при 55 rt 5°С.methacrylate and 15 g wood flour. With the introduction of bis ((n-butylfatal) manganese and 3 g of isopropyl hydroperoxide Ig into the composition I, the ashes of octane hardened for 4 hours at 55 rt 5 ° C.
Пример 3. В состав полимерной композиции вход т раствор 50 г полиэтилеигликольмалеинатфталата (рецептура состава изи примера 1) в 75 г диметакрилового эфира триэтилецгликол , 7,5 г олигодиенуретаидиметакрилага и 300 г маршалита. При введении в композицию 0,8 г нафтеиата .кобальта и 6 г перекиси циклогексаноиа она отверждаетс за 2 час при 55 ± 5°(.Example 3. The composition of the polymer composition includes a solution of 50 g of polyethylene glycol maleate phthalate (formula 1) of Example 1) in 75 g of triethylglycol dimethacrylic ester, 7.5 g of oligodienuretadi-methacrylate and 300 g of marshalite. With the introduction of 0.8 g of naphthyate and cobalt and 6 g of cyclohexanoic peroxide into the composition, it hardens for 2 hours at 55 ± 5 ° (.
В таблице приведены результаты испытаний иа прочность склеивани трехслойных конструкций типа слоистый иластик - заполнитель - слоистый пластик предлагаемыми полимерпыми композици ми.The table shows the test results and the bonding strength of three-layer structures such as laminated plastic - aggregate - laminated plastic offered by polymer compositions.
Таким образом, предлагаемые полимерные композиции не ток1сичпы, имеют хорошую адгезию К склеиваемым материалам (дреБесине, слоистому пластику, неиопластам и др.) и при отверждении образуют прочные и долговечные клеевые соединени .Thus, the proposed polymer compositions are not current; they have good adhesion to the materials being glued (wood, laminated plastic, neioplast, etc.) and during curing they form strong and durable adhesive joints.
П р и.ч е ч а н ие. В числнте.че приведены минимальные и максимальные, а в зна.менателе-средние значени .N ote. The numbers show minimum and maximum numbers, and the mean values show average values.
Предмет изобретени Subject invention
Полимерна композици , состо ща из раствора ненасыщенного полиэфира в диметакриловом эфире триэтиленгликол и вспомогательных добавок, отличающа с тем, что, с целью улучщени адгезионных свойств композиции , в нее введен олигодиенуретандиметакрилат в количестве 1,0-15,0 вес. ч.Polymer composition consisting of a solution of unsaturated polyester in triethylene glycol dimethacrylic ether and auxiliary additives, characterized in that, in order to improve the adhesive properties of the composition, oligodienurethane methacrylate is introduced into it in an amount of 1.0-15.0 wt. h