SU1659376A1 - Putty compound - Google Patents
Putty compound Download PDFInfo
- Publication number
- SU1659376A1 SU1659376A1 SU894676942A SU4676942A SU1659376A1 SU 1659376 A1 SU1659376 A1 SU 1659376A1 SU 894676942 A SU894676942 A SU 894676942A SU 4676942 A SU4676942 A SU 4676942A SU 1659376 A1 SU1659376 A1 SU 1659376A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- titanium
- plasticizer
- thirty
- putty
- mineral filler
- Prior art date
Description
Изобретение относится к составам, предназначенным для шпаклевания бетонИзобретение относится к строительным материалам, в частности к составам, предназначенным для шпаклевания бетонных, кирпичных и деревянных поверхностей.The invention relates to compositions intended for puttying concrete. The invention relates to construction materials, in particular to compositions intended for puttying concrete, brick and wood surfaces.
Цель изобретения - повышение жизнеспособности при сокращении сроков высыхания, снижение усадки и улучшение декоративности.The purpose of the invention is to increase the viability while reducing drying time, reducing shrinkage and improving the decorative effect.
Изобретение иллюстрируется примерами конкретного выполнения и их физико-механическими показателями свойств, приведенными в табл.1 и 2.The invention is illustrated by examples of specific performance and their physico-mechanical properties shown in Tables 1 and 2.
Наполнителем в предлагаемой шпаклевке является кремнегель - отход комплексной переработки минерального сырья в производстве фосфатных удобрений. Источником для производства фосфатных удобрений служит апатит. При его переработке ' получается фосфорная кислота - основной продукт для получения фосфатных удобрений и побочный продукт - кремнефтористоных, кирпичных и деревянных поверхностей. Цель изобретения - повышение жизнеспособности при сокращении сроков высыхания, снижение усадки и улучшение декоративности. Состав для получения шпаклевки содержит, мас.%: клей на основе натриевой соли карбоксиметилцеллюлозы 8-10: пластификатор 0,5-1.0: кремнегель отход производства фосфатных удобрений на стадии гидролиза кремнефтористоводородной кислоты 45-75. титанокальциевый пигмент - (полупродукт лакокрасочного производства состава, мас.%: ТЮг 33-35. Са5О4 65-67)15-45. Жизнеспособность шпаклевки 10 мес.. время высыхания 2535 мин. 2 табл.The filler in the proposed putty is silica gel - waste complex processing of mineral raw materials in the production of phosphate fertilizers. The source for the production of phosphate fertilizers is apatite. When it is processed, phosphoric acid is obtained - the main product for the production of phosphate fertilizers and the by-product of silicon fluoride, brick and wood surfaces. The purpose of the invention is to increase the viability while reducing drying time, reducing shrinkage and improving the decorative effect. The composition for producing putty contains, in wt%: glue based on carboxymethylcellulose sodium salt 8-10: plasticizer 0.5-1.0: silica gel, production of phosphate fertilizers at the hydrolysis stage of hydrofluorosilicic acid 45-75. titanium-calcium pigment - (intermediate product of paint and varnish production of composition, wt.%: Tug 33-35. Ca5O4 65-67) 15-45. Viability of putty 10 months drying time 2535 min. 2 tab.
СПSP
сwith
водородная кислота, которая также подвергается дальнейшей переработке на фторидбифторид аммония. На стадии гидролиза кремнефтористоводородной кислоты наряду с фтористым аммонием образуется кремнегель, являющийся отходом производства. Его вещественный состав, мас.%, в пересчете на сухое вещество.’hydrogen acid, which is also further processed to ammonium fluoride bifluoride. At the hydrolysis stage of fluorosilicic acid, along with ammonium fluoride, silica gel is formed, which is a production waste. Its material composition, wt.%, In terms of dry substance. ’
5Ю-2 85-955U-2 85-95
ΝΗ4Ε 0,4-13,0ΝΗ4Ε 0.4-13.0
ΝΗ3 свобод 0,1 “1.5ΝΗ3 freedoms 0.1 “1.5
СаРг. №Р, МдЕг. РеРг. А!Рз ОстальноеSaRg. No. P, MDEg. Rerg. A! Rz Else
1659376 А11659376 A1
Титано-кальциевый пигмент выполняет в шпаклевке одновременно две функции: является собственно пигментом за счет наличия в его составе двуокиси титана и гипсовым вяжущим веществом за счет наличия сульфата кальция в ангидритной форме.' Титано-кальциевый пигмент не является отхо3The titanium-calcium pigment performs two functions simultaneously in the putty: it is the actual pigment due to the presence of titanium dioxide in its composition and the gypsum binder due to the presence of calcium sulfate in the anhydrite form. Titanium-calcium pigment is not waste
'1659376'1659376
4four
дом производства, а является промежуточным продуктом в лакокрасочном производстве, Сырьем для производства титано-кальциевого пигмента служат титановая соль (сульфат титанила и аммония (ΝΗ4)2ΤΙΟ(5Ο4)2·Η2Ο) и известь СаО. В состав сульфата титанила и аммония входят, мас.%; ТЮг 20-21; Η23Ο4 28-29; (ΝΗ4)2 5Од 38-39; Н2О 11 — 14. Титано-кальциевый пигмент получают в процессе прокаливания при х 700-750°С смеси титановой соли и извести, взятых в стехиометрическом соотношении. При прокаливании из шихты удаляются вода и сульфат аммония, а серная кислота связывается с известью, образуя Са50д - инертный носитель,. на .частицы которого осаждается ТЮг, т.е. образуется титано-кальциевый пигмент ТЮгл *Са5О4, имеющий показатель разбеливающей способности > 400 усл. ед., что на 100 уел. ед, выше, чем у простой физической смеси ТЮг и Са5О4 такого же соотношения.production house, and is an intermediate product in the paint and varnish production. The raw material for the production of titanium-calcium pigment are titanium salt (titanyl and ammonium sulfate (ΝΗ4) 2ΤΙΟ (5Ο4) 2 · Η2Ο) and lime CaO. The composition of titanyl sulfate and ammonium are, wt.%; South 20-21; Η 2 3Ο 4 28-29; (ΝΗ 4) 2 5Od 38-39; H 2 O 11 - 14. Titanium-calcium pigment is obtained in the process of calcination at x 700-750 ° C mixture of titanium salt and lime, taken in a stoichiometric ratio. When calcined, water and ammonium sulfate are removed from the mixture, and sulfuric acid is bound to lime, forming Ca50d, an inert carrier. on the particles of which TiOg is deposited, i.e. a titanium-calcium pigment Tüg l * Ca5O4 is formed, having a bleaching capacity index> 400 srvc. units, which is 100 uel. units, higher than that of a simple physical mixture of TiOg and Ca5O4 of the same ratio.
Титано-кальциевый пигмент содержит, мас.%: ТЮг 33-35; Сз5О4 65-67.Titanium-calcium pigment contains, wt%: Tyr 33-35; Sz5O4 65-67.
Состав готовят следующим образом.The composition is prepared as follows.
Исходные компоненты при определенном их процентном содержании загружают в смеситель и тщательно перемешивают до получения однородного состава. Готовый порошок подают на расфасовку. Расфасовку осуществляют в герметичные емкости, например в полиэтиленовые банки или мешки из прочной пленки, которые транспортируются в магазины или строительные организации к месту производства работ.The original components at a certain percentage of them are loaded into the mixer and mix thoroughly until a homogeneous composition is obtained. The finished powder is fed to the packaging. The packaging is carried out in sealed containers, for example, in plastic jars or bags of durable film, which are transported to stores or building organizations to the work site.
Сухую шпаклевочную массу замешивают в теплой воде (50-60°С) и оставляют на 2 ч для набухания, после чего тщательно перемешивают и приступают к шпаклеванию. Воду добавляют в количестве 35.50 мас.% в зависимости от требуемой вязкости, определяемой родом работ.Dry putty mass is kneaded in warm water (50-60 ° C) and left for 2 hours to swell, then mix thoroughly and proceed to puttying. Water is added in the amount of 35.50 wt.% Depending on the required viscosity, determined by the type of work.
Шпаклевку можно наносить на поверхность внутренних стен помещений с нормальным влажностным режимом. Естественный цвет шпаклевки - белый, поэтому она может применяться для заделывания трещин и щелей в потолках без дополнительного забеливания, может применяться под побелку и под покраску. Покраску стен можно производить красками световых пастельных тонов.Putty can be applied to the surface of the interior walls of rooms with normal humidity conditions. The natural color of the putty is white, so it can be used to seal cracks and crevices in ceilings without additional whitening, can be used for whitewashing and painting. Walls can be painted with light pastel colors.
Использование в составе для получения , шпаклевки титанокальцевого пигмента, выполняющего одновременно функции пигмента и гипсового вяжущего, обеспечивает быстрое высыхание шпаклевочного слоя,Use in the composition to obtain, putty titanokaltsevogo pigment, simultaneously performing the functions of the pigment and gypsum binder, provides quick drying of the putty layer,
придает покрытию твердость, а также улучшает декоративные свойства шпаклевки (обеспечивает чистую белизну).gives the coating hardness and also improves the decorative properties of putty (provides clean whiteness).
Исключительно белый цвет шпаклевки позволяет использовать ее для шпаклевания трещин и щелей в потолках без последующей их побелки.The extremely white color of the putty allows it to be used for filling cracks and crevices in the ceilings without subsequent whitewashing.
Использование в качестве наполнителя кремнесодержащего отхода комплексной переработки минеральных удобрений придает шпаклевке высокую пластичность, что снижает ее усадку (отсутствие усадочных трещин на толщине шпаклевочного слоя до 15 мм) и повышает жизнеспособность в 50 раз. Высокая жизнеспособность шпаклевки позволяет использовать шпаклевочный состав не только в сухом виде, но и допускает выпуск готовой к употреблению шпаклевки (т.е. замешанной на воде) в качестве товара народного потребления с расфасовкой в мелкую тару и большим гарантийным сроком хранения.Use as a filler of silicon-containing waste complex processing of mineral fertilizers gives the putty a high plasticity, which reduces its shrinkage (no shrinkage cracks in the thickness of the putty layer up to 15 mm) and increases viability 50 times. The high viability of the putty makes it possible to use the putty compound not only in dry form, but also allows the release of ready-to-use putty (ie, mixed with water) as consumer goods with packaging in small containers and a large warranty period of storage.
Кроме того, при изготовлении состава для получения шпаклевки с использованием в качестве наполнителя кремнесодержащего отхода комплексной переработки минеральных удобрений исключаются энергетические затраты на измельчение последнего,так как он представляет собой мелкодисперсный порошок (размер частиц менее 20 мкм). при этом полученные при шпаклевании покрытия имеют ровную гладкую поверхность, а утилизация отхода способствует охране окружающей среды.In addition, in the manufacture of a compound for the preparation of putty using silicon-containing waste of complex processing of mineral fertilizers as a filler, the energy costs of grinding the latter are excluded, since it is a fine powder (particle size less than 20 microns). at the same time, the coatings obtained by puttying have a smooth, smooth surface, and the utilization of waste contributes to environmental protection.
**
Claims (1)