RU2559336C1 - Method of micro-profiling of silicon structures - Google Patents
Method of micro-profiling of silicon structures Download PDFInfo
- Publication number
- RU2559336C1 RU2559336C1 RU2014119505/28A RU2014119505A RU2559336C1 RU 2559336 C1 RU2559336 C1 RU 2559336C1 RU 2014119505/28 A RU2014119505/28 A RU 2014119505/28A RU 2014119505 A RU2014119505 A RU 2014119505A RU 2559336 C1 RU2559336 C1 RU 2559336C1
- Authority
- RU
- Russia
- Prior art keywords
- protective film
- silicon
- etching
- anisotropic
- anisotropic etching
- Prior art date
Abstract
Description
Изобретение относится к приборостроению и может применяться для изготовления конструктивных элементов микромеханических приборов на кремниевых монокристаллических подложках, а именно упругих подвесов и всего чувствительного элемента в целом, например для микромеханических акселерометров и гироскопов.The invention relates to instrumentation and can be used for the manufacture of structural elements of micromechanical devices on silicon single-crystal substrates, namely, elastic suspensions and the entire sensitive element as a whole, for example, for micromechanical accelerometers and gyroscopes.
Известен способ изготовления глубокопрофилированных кремниевых структур путем изотропного травления исходной пластины монокристаллического кремния [1].A known method of manufacturing deeply profiled silicon structures by isotropic etching of the original plate of single-crystal silicon [1].
Недостатком известного способа является неточность изготовления конструктивных элементов для микроприборов, из-за зависимости скорости травления от температуры и концентрации травителя, а также сложность обеспечения локальной защиты от длительного воздействия травителя. Другим недостатком данного способа является значительное боковое расстравливание монокристаллического кремния, т.к. при изотропном травлении скорость во всех направлениях одинакова.The disadvantage of this method is the inaccuracy of the manufacture of structural elements for microdevices, due to the dependence of the etching rate on temperature and the concentration of the etchant, as well as the difficulty of providing local protection from prolonged exposure to the etchant. Another disadvantage of this method is the significant lateral melt single crystal silicon, because with isotropic etching, the speed in all directions is the same.
Известен способ изготовления чувствительного элемента микромеханического устройства, заключающийся в нанесении на пластину защитной маски, формировании окна и локальном анизотропном травлении кремния в окне этой маски [2].A known method of manufacturing a sensitive element of a micromechanical device, which consists in applying a protective mask to the plate, forming a window and local anisotropic etching of silicon in the window of this mask [2].
Однако известный способ имеет следующие недостатки. В результате анизотропного травления получается профиль в виде трапеции в сечении, на вершинах которой в местах резкого перехода возникают концентраторы механических напряжений и при наличии микротрещин при эксплуатации происходит его разрушение. Кроме того, в микромеханических приборах это также ведет к отказу всего прибора, следовательно, к снижению надежности. Кроме того, в микромеханических приборах изготовленный таким способом упругий подвес обладает низкой устойчивостью к продольному сжимающему воздействию. При воздействии измеряемой величины упругий элемент, полученный таким способом, испытывает распределенный изгиб, что снижает точность преобразователя.However, the known method has the following disadvantages. As a result of anisotropic etching, a profile is obtained in the form of a trapezoid in cross section, on the tops of which concentrators of mechanical stress arise at the points of abrupt transition and, in the presence of microcracks, it is destroyed during operation. In addition, in micromechanical devices, this also leads to a failure of the entire device, therefore, to a decrease in reliability. In addition, in micromechanical devices, an elastic suspension made in this way has a low resistance to longitudinal compressive action. When the measured value is exposed, the elastic element obtained in this way experiences distributed bending, which reduces the accuracy of the transducer.
Задачей, на решение которой направлено изобретение, является снижение трудоемкости изготовления и повышение качества структур. Для достижения этого способ микропрофилирования кремниевых структур включает нанесение защитной пленки на пластину из монокристаллического кремния, формирование из защитной пленки локальной маски в области формирования микропрофиля и дальнейшего анизотропного травления пластины монокристаллического кремния, после анизотропного травления пластины монокристаллического кремния наносят защитную пленку, наносят слой поликристаллического кремния, проводят анизотропное травление поликристаллического кремния, проводят окисление поликристаллического кремния, проводят травление диоксида кремния со вновь наносимой защитной пленки, проводят травление защитной пленки до поверхности пластины, проводят анизотропное травление в образовавшемся окне пластины монокристаллического кремния, затем снова наносят защитную пленку, слой поликристаллического кремния, проводят анизотропное травление поликристаллического кремния, окисление поликристаллического кремния, травление диоксида кремния, травление защитной пленки до поверхности пластины и анизотропное травление необходимое количество раз до получения требуемого микропрофиля с последующим сглаживанием в изотропном или анизотропном травителе или анизотропном и изотропном травителях полученной поверхности.The problem to which the invention is directed, is to reduce the complexity of manufacturing and improve the quality of structures. To achieve this, the method of microprofiling silicon structures includes applying a protective film to a single-crystal silicon wafer, forming a local mask from the protective film in the area of microprofile formation and further anisotropic etching of a single-crystal silicon wafer, after anisotropic etching of a single-crystal silicon wafer, a protective film is applied, a layer of polycrystalline silicon is applied, conduct anisotropic etching of polycrystalline silicon, conduct oxidation of the floor crystalline silicon, etch silicon dioxide from the newly applied protective film, etch the protective film to the wafer surface, conduct anisotropic etching in the resulting window of a single-crystal silicon wafer, then apply a protective film, a layer of polycrystalline silicon, conduct anisotropic etching of polycrystalline silicon, oxidize polycrystalline silicon , etching of silicon dioxide, etching of the protective film to the surface of the plate and anisotropic etching of neo the required number of times until the desired microprofile is obtained, followed by smoothing in the isotropic or anisotropic etch or anisotropic and isotropic etch of the resulting surface.
Отличительными признаками заявленного способа является то, что после анизотропного травления пластины монокристаллического кремния наносят защитную пленку, наносят слой поликристаллического кремния, проводят анизотропное травление поликристаллического кремния, проводят окисление поликристаллического кремния, проводят травление диоксида кремния со вновь наносимой защитной пленки, проводят травление защитной пленки до поверхности пластины, проводят анизотропное травление в образовавшемся окне пластины монокристаллического кремния, затем снова наносят защитную пленку, слой поликристаллического кремния, проводят анизотропное травление поликристаллического кремния, окисление поликристаллического кремния, травление диоксида кремния, травление защитной пленки до поверхности пластины и анизотропное травление необходимое количество раз до получения требуемого микропрофиля с последующим сглаживанием в изотропном или анизотропном травителе или анизотропном и изотропном травителях полученной поверхности. Повторение последовательности технологического цикла и технологических операций, а также количество циклов определяется сложностью проектируемого профиля и его назначением соответственно-конкретным применением конечного получаемого профиля, например, для чувствительных элементов датчиков давления, или датчиков линейных, угловых ускорений, или датчиков угловых скоростей, или датчиков силы, или датчиков перемещений. Таким образом, получение конкретного профиля определяется конкретным назначением приборов, в которых будет использоваться микропрофиль, например его упругих элементов, которые определяют его основные точностные и прочностные характеристики. Соответственно для каждого конкретного микропрофиля по назначению количество циклов определяется для каждого индивидуального микропрофиля отдельно по назначению. Предлагаемый способ позволяет изготавливать профиль упругих элементов микромеханических приборов плавным. Это увеличивает надежность по сравнению с прототипом, у которого на изгибах возникают концентраторы напряжений, ведущих к разрушению прибора.Distinctive features of the claimed method is that after anisotropic etching of a single-crystal silicon wafer, a protective film is applied, a layer of polycrystalline silicon is applied, anisotropic etching of polycrystalline silicon is carried out, polycrystalline silicon is oxidized, silicon dioxide is etched from the newly applied protective film, and the protective film is etched to the surface plates, conduct anisotropic etching in the resulting window of the plate of a single-crystal cream They then apply a protective film again, a layer of polycrystalline silicon, conduct anisotropic etching of polycrystalline silicon, oxidize polycrystalline silicon, etch silicon dioxide, etch the protective film to the wafer surface and anisotropic etch as many times as necessary to obtain the desired microprofile, followed by smoothing in an isotropic or anisotropic etch or anisotropic and isotropic etch the resulting surface. The repetition of the sequence of the technological cycle and technological operations, as well as the number of cycles is determined by the complexity of the designed profile and its purpose, respectively, by the specific application of the final obtained profile, for example, for sensitive elements of pressure sensors, or linear, angular acceleration sensors, or angular velocity sensors, or force sensors , or displacement sensors. Thus, obtaining a specific profile is determined by the specific purpose of the devices in which the microprofile will be used, for example, its elastic elements, which determine its basic accuracy and strength characteristics. Accordingly, for each specific microprofile as intended, the number of cycles is determined for each individual microprofile separately for its intended purpose. The proposed method allows to make the profile of the elastic elements of micromechanical devices smooth. This increases reliability compared to the prototype, in which stress concentrators appear on bends, leading to the destruction of the device.
Предлагаемое изобретение иллюстрируется чертежами фиг. 1, фиг. 2.The invention is illustrated by the drawings of FIG. 1, FIG. 2.
На фиг. 1 (а, б, в, г, д) и фиг. 2 (а, б, в) изображена последовательность микропрофилирования кремниевых структур,In FIG. 1 (a, b, c, d, e) and FIG. 2 (a, b, c) shows the sequence of microprofiling of silicon structures,
где:Where:
1 - монокристаллическая пластина кремния;1 - single crystal silicon wafer;
2 - защитная пленка двуокиси кремния;2 - a protective film of silicon dioxide;
3 - защитная пленка нитрида кремния;3 - a protective film of silicon nitride;
4 - слой поликристаллического кремния.4 - layer of polycrystalline silicon.
Способ реализуется следующим образом. На пластину монокристаллического кремния 1 наносят защитную пленку двуокиси кремния 2 (фиг. 1а), проводят экспонирование для вскрытия окон в защитной пленке двуокиси кремния 2 (фиг. 1б). Проводят анизотропное травление монокристаллической пластины кремния 1 в образовавшемся окне (фиг. 1в). Вновь наносят защитную пленку нитрида кремния 3 (фиг. 1г). Наносят поликристаллический кремний 4 (фиг.1г). Проводят анизотропное травление поликристаллического кремния 4 (фиг. 1д). Проводят окисление поликристаллического кремния 4 (фиг. 2а). Проводят травление защитной пленки нитрида кремния 3 до поверхности пластины 1 (фиг. 2б). Проводят анизотропное травление монокристаллической пластины кремния 1 в образовавшемся окне (фиг. 2в). Повторяют необходимое количество раз до получения требуемого микропрофиля с последующим сглаживанием в изотропном или анизотропном травителе или анизотропном и изотропном травителях полученной поверхности. Получение конкретного профиля определяется конкретным назначением приборов, в которых будет использоваться микропрофиль, например его упругих элементов, которые определяют его основные точностные и прочностные характеристики. Соответственно для каждого конкретного микропрофиля по назначению количество циклов определяется для каждого индивидуального микропрофиля отдельно по назначению.The method is implemented as follows. A protective film of
Пример.Example.
На пластине монокристаллического кремния ориентации (100) при термическом окислении, температуре 1100°C в течение 65 мин в водном паре образуется на поверхности монокристаллического кремния пленка диоксида кремния толщиной 0,4 мкм при нормальном атмосферном давлении. Затем наносят фоторезист ФП-383. Проводят фотолитографию. Проводят плазмохимическое травление (вертикальное) SiO2. Далее проводят плазмохимическое травление кремния на глубину 2 мкм. После этого проводят осаждение Si3N4 (100 нм). Процесс осаждения Si3N4 проводят из газовой фазы (моносилан и аммиак) в течение 60 мин, при температуре 850-870°C, рабочем давлении 30 Па. Затем проводят осаждение поликристаллического кремния (1 мкм = 2 раза по 60 мин) из газовой фазы (моносилан) в течение 120 мин, при температуре 850-870°C, рабочем давлении 30 Па. Проводят плазмохимическое травление (вертикальное) поликремния на глубину 1 мкм. Затем проводят окисление поликристаллического кремния при парциальном давлении H2O в 0,6 атм в течение 600 мин, температуре 1150°C, рабочем давлении 1 атм. Проводят плазмохимическое травление (вертикальное) Si3N4 до поверхности пластины. Проводят плазмохимическое травление кремния на глубину 2 мкм. Повторяют операции начиная с осаждения Si3N4 необходимое количество раз до получения требуемого микропрофиля с последующим сглаживанием в изотропном или анизотропном травителе или анизотропном и изотропном травителях полученной поверхности. Причем процесс микропрофилирования кремниевых структур проводится с одним фотошаблоном. При этом варьированием толщины осажденного поликристаллического кремния и глубины анизотропного травления в образовавшемся окне пластины монокристаллического кремния каждой стадии формирования получают требуемую форму микропрофиля. Обеспечивается получение различных форм профиля кремниевых структур: как овальных, так и ломаных.On a single-crystal silicon wafer of orientation (100), during thermal oxidation at a temperature of 1100 ° C for 65 min in water vapor, a silicon dioxide film 0.4 μm thick is formed on the surface of single-crystal silicon at normal atmospheric pressure. Then apply photoresist FP-383. Photolithography is carried out. Plasma-chemical etching (vertical) of SiO 2 is carried out. Next, plasma-chemical etching of silicon to a depth of 2 μm is carried out. After that, the deposition of Si 3 N 4 (100 nm). The deposition process of Si 3 N 4 is carried out from the gas phase (monosilane and ammonia) for 60 min, at a temperature of 850-870 ° C, operating pressure of 30 Pa. Then, polycrystalline silicon is deposited (1 μm = 2 times 60 min) from the gas phase (monosilane) for 120 min, at a temperature of 850-870 ° C, and a working pressure of 30 Pa. Plasma-chemical etching (vertical) of polysilicon to a depth of 1 μm is carried out. Then polycrystalline silicon is oxidized at a partial pressure of H 2 O of 0.6 atm for 600 min, a temperature of 1150 ° C, and a working pressure of 1 atm. Plasma-chemical etching (vertical) of Si 3 N 4 is carried out to the plate surface. Plasma-chemical etching of silicon to a depth of 2 μm is carried out. Operations are repeated starting from the deposition of Si 3 N 4 the required number of times until the desired microprofile is obtained, followed by smoothing in the isotropic or anisotropic etchant or anisotropic and isotropic etch of the resulting surface. Moreover, the process of microprofiling silicon structures is carried out with one photomask. In this case, by varying the thickness of the deposited polycrystalline silicon and the depth of anisotropic etching in the resulting window of the single-crystal silicon wafer of each formation stage, the desired microprofile shape is obtained. It is possible to obtain various profile shapes of silicon structures: both oval and broken.
Таким образом, предложенный способ обеспечивает снижение трудоемкости изготовления чувствительных элементов, повышение работоспособности преобразователя путем увеличения механической прочности подвеса. При этом существенно снижается концентрация механических напряжений в местах сопряжения упругих элементов.Thus, the proposed method reduces the complexity of manufacturing sensitive elements, increasing the efficiency of the Converter by increasing the mechanical strength of the suspension. In this case, the concentration of mechanical stresses at the junctions of the elastic elements is significantly reduced.
В случае наличия микротрещин в теле элемента подвеса по сравнению с прототипом уменьшается вероятность выхода из строя преобразователя.In the case of microcracks in the body of the suspension element in comparison with the prototype reduces the likelihood of failure of the Converter.
Источники информацииInformation sources
1. Травление полупроводников [сборник статей]. Пер. с англ. С.Н. Горина. М.: Мир, 1965.1. Etching of semiconductors [collection of articles]. Per. from English S.N. Gorina. M.: Mir, 1965.
2. Ваганов В.И. Интегральные тензопреобразователи. - М.: Энергоатомиздат, 1983. - прототип.2. Vaganov V.I. Integrated strain gauges. - M .: Energoatomizdat, 1983. - prototype.
Claims (1)