RU2470899C1

RU2470899C1 - Crude mixture for producing concrete

Info

Publication number: RU2470899C1
Application number: RU2011136217/03A
Authority: RU
Inventors: Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2011-08-31
Filing date: 2011-08-31
Publication date: 2012-12-27

Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to the industry of building materials, in particular to production of concrete which can be used in making wall blocks. The crude mixture for producing concrete contains the following, wt %: cement 25-27, thermal power plant flue ash with specific surface area of 2800-5000 cm²/g 10.0-12.0, carboxymethyl cellulose 0.01-0.02, superplasticiser S-3 1-1.4, expanded clay with particle size of 10-20 mm and/or azerit with particle size of 10-20 mm 34-37, water - the balance.

EFFECT: low cement consumption without loss of quality of concrete.

1 tbl

Description

Изобретение относится к промышленности строительных материалов, в частности к производству бетонов, которые могут быть использованы для изготовления стеновых блоков.The invention relates to the building materials industry, in particular to the production of concrete, which can be used for the manufacture of wall blocks.

Известна сырьевая смесь для изготовления бетона (пенобетона), содержащая, мас.%: цемент 35,0-39,0; золу-унос ТЭС с удельной поверхностью 2800-5000 см²/г 35,0-39,0; смолу воздухововлекающую экстракционно-канифольную 0,11-0,17; карбоксиметилцеллюлозу 0,05-0,07; суперпластификатор С-3 0,4-1,4; воду - остальное [1]. Такая сырьевая смесь содержит большое количество цемента.Known raw mix for the manufacture of concrete (foam), containing, wt.%: Cement 35,0-39,0; fly ash TPP with a specific surface area of 2800-5000 cm ² / g 35.0-39.0; extraction air rosin resin 0.11-0.17; carboxymethyl cellulose 0.05-0.07; superplasticizer C-3 0.4-1.4; water - the rest [1]. Such a raw material mixture contains a large amount of cement.

Задача изобретения состоит в снижении расхода цемента без потери качества бетона.The objective of the invention is to reduce cement consumption without loss of concrete quality.

Технический результат достигается тем, что сырьевая смесь для изготовления бетона, содержащая цемент, золу-унос ТЭС с удельной поверхностью 2800-5000 см²/г, карбоксиметилцеллюлозу, суперпластификатор C-3, воду, дополнительно содержит керамзит фракции 10-20 мм и/или азерит фракции 10-20 мм при следующем соотношении компонентов, мас.%: цемент 25-27; зола-унос ТЭС 10,0-12,0; карбоксиметилцеллюлоза 0,01-0,02; суперпластификатор C-3 1-1,4; керамзит фракции 10-20 мм и/или азерит фракции 10-20 мм 34-37; вода - остальное.The technical result is achieved by the fact that the raw material mixture for the manufacture of concrete containing cement, fly ash TPP with a specific surface area of 2800-5000 cm ² / g, carboxymethyl cellulose, superplasticizer C-3, water, additionally contains expanded clay fractions of 10-20 mm and / or Azerite fractions of 10-20 mm in the following ratio of components, wt.%: cement 25-27; fly ash TPP 10.0-12.0; carboxymethyl cellulose 0.01-0.02; superplasticizer C-3 1-1.4; expanded clay fraction of 10-20 mm and / or Azerite fraction of 10-20 mm 34-37; water is the rest.

Составы сырьевой смеси для изготовления бетона приведены в таблице.The compositions of the raw mix for the manufacture of concrete are given in the table.

ТаблицаTable Компоненты Components Содержание, мас.%Content, wt.% состав № 1composition number 1 состав № 2composition number 2 состав № 3composition No. 3 Портландцемент Portland cement 2525 -- -- ШлакопортландцементSlag Portland Cement -- 2626 -- Белый цементWhite cement -- -- 2727 Зола-унос ТЭСFly ash TPP 1212 11eleven 1010 КарбоксиметилцеллюлозаCarboxymethyl cellulose 0,020.02 0,0150.015 0,010.01 Суперпластификатор C-3Superplasticizer C-3 1one 1,21,2 1,41.4 Керамзит фракции 10-20 ммExpanded clay fraction 10-20 mm 3737 15,515,5 -- Азерит фракции 10-20 ммAzerite fractions 10-20 mm -- 20twenty 3434 ВодаWater (остальное) 24,98(rest) 24.98 (остальное) 26,285(rest) 26,285 (остальное) 27,59(rest) 27.59 Прочность бетона на сжатие в возрасте 28 сут, МПаThe compressive strength of concrete at the age of 28 days, MPa ~7~ 7 ~9~ 9 ~10~ 10

Цемент смешивают с золой-уносом ТЭС, керамзитом и/или азеритом, добавляют воду, карбоксиметилцеллюлозу, суперпластификатор C-3 и подготавливают сырьевую смесь, которой заполняют металлические формы, выдерживают ее в формах 12 ч при температуре 20-25°C, а затем изделия (стеновые блоки) подвергают автоклавной обработке при температуре 175°C и давлении 0,8 МПа в течение 12 ч.Cement is mixed with TPP fly ash, expanded clay and / or Azerite, water, carboxymethyl cellulose, C-3 superplasticizer are added and the raw material mixture is prepared, which is filled into metal molds, kept in molds for 12 hours at a temperature of 20-25 ° C, and then products (wall blocks) are autoclaved at a temperature of 175 ° C and a pressure of 0.8 MPa for 12 hours

Источники информацииInformation sources

1. Патент РФ № 2237041, C04B 38/10, 2003.1. RF patent No. 2237041, C04B 38/10, 2003.

Claims

Raw mix for the manufacture of concrete, containing cement, fly ash TPP with a specific surface area of 2800-5000 cm ² / g, carboxymethyl cellulose, superplasticizer C-3, water, characterized in that it additionally contains expanded clay fraction 10-20 mm and / or Azerite fraction 10-20 mm in the following ratio of components, wt.%:
cement 25-27 fly ash TPP 10.0-12.0 carboxymethyl cellulose 0.01-0.02 superplasticizer C-3 1-1,4 expanded clay fractions of 10-20 mm and / or Azerite fractions 10-20 mm 34-37 water rest