RU2375031C2

RU2375031C2 - Adsorbing product

Info

Publication number: RU2375031C2
Application number: RU2008105602/14A
Authority: RU
Inventors: Керстин ЭДВАЛЛЬ (SE); Керстин ЭДВАЛЛЬ; Маргарета ВЕННЕРБОК (SE); Маргарета ВЕННЕРБОК; Элизабет ЛАКСО (SE); Элизабет ЛАКСО
Original assignee: Ска Хайджин Продактс Аб
Priority date: 2005-07-14
Filing date: 2005-07-14
Publication date: 2009-12-10
Also published as: RU2008105602A

Abstract

FIELD: medicine.

SUBSTANCE: invention relates to medicine, namely to adsorbing products of panties type, and is intended for application in case of enuresis. Adsorbing product contains at least one elastic roll material, which is welded by ultrasound to at least one second roll material at least along one welding seam. Second roll material differs from first elastic roll material, and second roll material has degree of elasticity, which differs from elasticity of first elastic roll material. According to invention ultrasound welding seam between first elastic roll material and second roll material is strengthened in such way, that it has welding seam strength in direction, transversal to welding sew, constituting at least 5 H/25.4 mm.

EFFECT: invention allows to combine for user properties of comfort and good fitting in such way, that product is comfortable for user, preserving its own integrity during putting on and during use.

25 cl, 7 dwg

Description

Область техникиTechnical field

Настоящее изобретение относится к адсорбирующему изделию, такому как подгузник, подгузник в виде трусов, гигиенические трусы или предмет одежды, используемый при недержании, причем указанное изделие содержит эластичный рулонный материал.The present invention relates to an absorbent article, such as a diaper, a diaper in the form of underpants, hygiene pants or an article of clothing used for incontinence, said article comprising an elastic web material.

Уровень техники изобретенияBACKGROUND OF THE INVENTION

Предполагается, что адсорбирующие изделия, подобные подгузникам, подгузникам в виде трусов, гигиеническим трусам или предметам одежды, используемым при недержании, имеют удобное прилегание на теле пользователя. Для адсорбирующих изделий типа трусов является также желательным, чтобы изделия были способны натягиваться вверх и стягиваться вниз по бедрам пользователя, чтобы позволить пользователю или обслуживающему персоналу легко надеть или удалить изделие после его загрязнения. Подобные изделия должны объединять для пользователя свойства удобства и хорошего прилегания с прочностью так, чтобы изделие было удобным для пользователя, все еще сохраняя свою целостность при надевании и в течение использования. Те области, которые наиболее подвергаются нагрузкам и где наиболее вероятен разрыв, являются такими областями, в которых элементы, составляющие адсорбирующее изделие, соединяются вместе (например, швы изделия).It is believed that absorbent articles like diapers, panty-shaped diapers, hygiene pants or incontinence garments have a snug fit on the wearer's body. For absorbent articles such as underpants, it is also desirable that the articles are capable of being pulled up and pulled down over the thighs of the wearer to allow the wearer or maintenance personnel to easily put on or remove the garment after being soiled. Such products should combine the features of comfort and good fit for the user with durability so that the product is comfortable for the user, while still maintaining its integrity when donning and during use. Those areas that are most exposed to stress and where rupture is most likely are areas in which the elements that make up the absorbent product are joined together (for example, product seams).

Международная заявка РСТ/SE05/000319 раскрывает одноразовые гигиенические трусы, содержащие эластичный рулонный материал, в которых боковые края (боковые швы), которые соединяют переднюю и заднюю части изделия, свариваются и усиливаются неткаными полосами.PCT / SE05 / 000319 discloses disposable hygiene pants containing elastic roll material in which the side edges (side seams) that connect the front and back of the product are welded and reinforced with non-woven strips.

US 2003/0120252 описывает подгузник в виде трусов, имеющий покрытие из лент, прикрепленное над боковыми сварными швами, которое предоставляет эстетически приятный внешний вид. Внешнее покрытие данного подгузника в виде трусов может быть эластичным материалом. Боковые швы могут связываться с помощью клея и/или ультразвука.US 2003/0120252 describes a diaper in the form of pants, having a coating of tapes attached above the side welds, which provides an aesthetically pleasing appearance. The outer cover of this diaper in the form of pants can be an elastic material. Side seams can be bonded using glue and / or ultrasound.

Остается потребность в адсорбирующем изделии, в котором компоненты прочно и надежно соединяются и которое не порвется вдоль швов или разъединится, когда изделие подвергается нагрузкам (например, при надевании или удалении изделия). Обнаружено, что это является особенно важным, когда соединяются вместе два компонента, имеющие различные эластичные свойства (различное сопротивление растяжению).There remains a need for an absorbent article in which the components are firmly and reliably connected and which will not tear along the seams or disconnect when the article is subjected to stresses (for example, when donning or removing the article). This has been found to be especially important when two components having different elastic properties (different tensile strength) are joined together.

Сущность изобретенияSUMMARY OF THE INVENTION

Настоящее изобретение касается проблем, связанных с известными изделиями данного типа. Более конкретно, настоящее изобретение предоставляет адсорбирующее изделие, такое как подгузник, подгузник в виде трусов, гигиенические трусы или предмет одежды, используемый при недержании. Изделие содержит, по меньшей мере, один первый эластичный рулонный материал, который с помощью ультразвука приваривается, по меньшей мере, к одному второму рулонному материалу, по меньшей мере, вдоль одного сварного шва. Второй рулонный материал отличается от первого эластичного рулонного материала, и второй рулонный материал является неэластичным или имеет степень эластичности, которая отличается от эластичности первого эластичного рулонного материала. В соответствии с изобретением ультразвуковой сварной шов между первым эластичным рулонным материалом и вторым рулонным материалом усиливается, чтобы иметь прочность сварного шва в направлении, поперечном к сварному шву, которая составляет, по меньшей мере, 5 Н/25,4 мм.The present invention relates to problems associated with known products of this type. More specifically, the present invention provides an absorbent article, such as a diaper, a diaper in the form of pants, hygiene pants or an article of clothing used for incontinence. The product comprises at least one first elastic web material that is ultrasonically welded to at least one second web material along at least one weld. The second roll material is different from the first elastic roll material, and the second roll material is inelastic or has a degree of elasticity that is different from the elasticity of the first elastic roll material. In accordance with the invention, the ultrasonic weld between the first elastic roll material and the second roll material is reinforced to have a weld strength in the direction transverse to the weld that is at least 5 N / 25.4 mm.

Адсорбирующее изделие в соответствии с одним воплощением изобретения является адсорбирующим изделием типа трусов, таким как подгузник в виде трусов, гигиенические трусы или трусы, используемые при недержании. Оно содержит переднюю часть и заднюю часть. Передняя и задняя части соединяются друг с другом вдоль двух противоположных продольных боковых краев для ограничения отверстия для талии и пары отверстий для ног. По меньшей мере, одна из передней и задней частей содержит первый эластичный рулонный материал. Изделие далее содержит ластовичную часть, расположенную между передней частью и задней частью в продольном направлении изделия, причем ластовичная часть содержит второй рулонный материал. Ластовичная часть приваривается к передней и задней частям с помощью ультразвуковых сварных швов. В одном воплощении адсорбирующего изделия типа трусов как передняя, так и задняя части содержат первый эластичный рулонный материал.The absorbent article in accordance with one embodiment of the invention is a panty type absorbent article, such as a diaper in the form of underpants, hygiene pants or incontinence pants. It contains the front and back. The front and rear parts are connected to each other along two opposite longitudinal side edges to limit the waist opening and the pair of leg openings. At least one of the front and back portions comprises a first elastic web material. The product further comprises a crotch portion located between the front part and the rear part in the longitudinal direction of the product, wherein the crotch portion contains a second web material. The gusset is welded to the front and back using ultrasonic welds. In one embodiment of an absorbent article such as underpants, both the front and rear parts comprise a first elastic web material.

В следующем воплощении изделие содержит переднюю часть талии, которая располагается на крае передней части, который является дистальным от ластовичной части в продольном направлении изделия. Передняя часть содержит первый эластичный рулонный материал, в то время как передняя часть талии содержит второй рулонный материал. Передняя часть талии приваривается к передней части с помощью ультразвукового сварного шва. Альтернативно или дополнительно адсорбирующее изделие изобретения типа трусов может содержать заднюю часть талии, которая располагается на крае задней части, который является дистальным от ластовичной части в продольном направлении изделия. Задняя часть содержит первый эластичный рулонный материал, в то время как задняя часть талии содержит второй рулонный материал. Задняя часть талии приваривается к задней части с помощью ультразвукового сварного шва.In a further embodiment, the article comprises a front part of the waist that is located at the edge of the front part which is distal from the crotch part in the longitudinal direction of the article. The front part contains the first elastic web material, while the front part of the waist contains the second web material. The front of the waist is welded to the front with an ultrasonic weld. Alternatively or additionally, the absorbent article of the invention, such as a panty type, may comprise a rear part of the waist that is located at the edge of the rear part which is distal from the crotch part in the longitudinal direction of the product. The back portion comprises a first elastic web material, while the back portion of the waist comprises a second web material. The back of the waist is welded to the back with an ultrasonic weld.

Желательно, чтобы первый эластичный рулонный материал адсорбирующего изделия типа трусов являлся многослойным материалом. Многослойный материал можно составить из первого и второго слоев волокнистого материала и слоя эластичной пленки, расположенного между первым и вторым волокнистыми слоями. Первый эластичный рулонный материал может быть единым компонентом первой и второй частей, по меньшей мере, на 20%, предпочтительно на 25%, более предпочтительно на 30%, наиболее предпочтительно на 40% общей площади поверхности адсорбирующего изделия и является предпочтительно воздухопроницаемым. Типично эластичный рулонный материал имеет скорость прохождения водяного пара в соответствии с методикой D ASTM Е96-00, по меньшей мере, 1500 г/м² 24 ч, предпочтительно, по меньшей мере, 3000 г/м² 24 ч.It is desirable that the first elastic web material of an absorbent article such as a panty is a multilayer material. The multilayer material can be composed of the first and second layers of fibrous material and a layer of elastic film located between the first and second fibrous layers. The first elastic web material may be a single component of the first and second parts, at least 20%, preferably 25%, more preferably 30%, most preferably 40% of the total surface area of the absorbent article and is preferably breathable. A typically elastic web material has a water vapor transmission rate of at least 1,500 g / m ² 24 hours, preferably at least 3,000 g / m ² 24 hours, in accordance with Method D ASTM E96-00.

Второй рулонный материал предпочтительно имеет эластичность, которая является более низкой, чем эластичность первого эластичного сетчатого материала. Нетканые материалы являются подходящими для второго сетчатого материала.The second web material preferably has an elasticity that is lower than the elasticity of the first elastic net material. Nonwovens are suitable for a second mesh material.

В дополнение к вышеизложенному ультразвуковой сварной шов между первым эластичным сетчатым материалом и вторым сетчатым материалом усиливают, чтобы иметь прочность сварки в направлении, поперечном сварному шву, которая составляет, по меньшей мере, 7 Н/25,4 мм, предпочтительно, по меньшей мере, 9 Н/25,4 мм. Усиление сварного шва можно обеспечить дополнительным слоем сетчатого материала, который присоединяется к сварному шву. Данный дополнительный слой сетчатого материала может проходить, по меньшей мере, вдоль 50%, предпочтительно, по меньшей мере, вдоль 75%, более предпочтительно, по меньшей мере, вдоль 100% длины сварного шва, к которому он присоединяется.In addition to the foregoing, an ultrasonic weld between the first elastic net material and the second net material is reinforced to have a weld strength in the direction transverse to the weld that is at least 7 N / 25.4 mm, preferably at least 9 N / 25.4 mm. The reinforcement of the weld can be provided with an additional layer of mesh material, which is attached to the weld. This additional layer of mesh material can extend at least along 50%, preferably at least along 75%, more preferably at least along 100% of the length of the weld to which it is attached.

В качестве альтернативы усиление сварного шва можно обеспечить клеем, который наносят вдоль 50-100%, предпочтительно вдоль 70-90% длины сварного шва.Alternatively, the reinforcement of the weld can be provided with glue, which is applied along 50-100%, preferably along 70-90% of the length of the weld.

В соответствии с настоящим изобретением адсорбирующее изделие типа трусов далее содержит адсорбирующий комплект, причем указанный адсорбирующий комплект содержит непроницаемый для жидкости защитный слой, проницаемый для жидкости верхний слой и адсорбирующую сердцевину, заключенную между ними.In accordance with the present invention, the panty-type absorbent article further comprises an absorbent kit, said absorbent kit comprising a liquid-impervious protective layer, a liquid-permeable upper layer and an absorbent core interposed therebetween.

Краткое описание чертежейBrief Description of the Drawings

Фиг. 1 показывает перспективный вид подгузника в виде трусов.FIG. 1 shows a perspective view of a panty diaper.

Фиг. 2 показывает вид сверху подгузника в виде трусов в его плоском полностью растянутом состоянии перед формированием, как видно с обращенной к телу стороны.FIG. 2 shows a top view of a panty-shaped diaper in its flat, fully stretched state before being formed, as seen from the side facing the body.

Фиг. 3 является соответствующим видом сверху с противоположной обращенной к предмету одежды стороны подгузника в виде трусов.FIG. 3 is a corresponding plan view from the opposite side of the diaper in the form of panties facing the garment.

Фиг. 4 является поперечным сечением по линии VI-VI Фиг. 3.FIG. 4 is a cross section along line VI-VI of FIG. 3.

Фиг. 5 является поперечным сечением эластичного ламината по линии VII-VII Фиг. 3.FIG. 5 is a cross-section of an elastic laminate along line VII-VII of FIG. 3.

Фиг. 6-7 схематично показывают способ измерения прочности сварного шва.FIG. 6-7 schematically show a method for measuring the strength of a weld.

Подробное описание предпочтительных воплощенийDETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Адсорбирующее изделиеAbsorbent product

Термин “адсорбирующее изделие” относится к изделиям, которые размещаются прямо напротив кожи пользователя для адсорбции и сохранения физиологических экссудатов, подобных моче, фекалиям и менструальной текучей среде. Изобретение относится главным образом к одноразовым адсорбирующим изделиям, которые подразумевают изделия, которые не предназначены для стирки, или для восстановления иным образом, или повторного использования в качестве адсорбирующего изделия после использования. Изобретение относится к “адсорбирующим изделиям типа трусов”. Примерами подобных адсорбирующих изделий типа трусов являются подгузники в виде трусов, гигиенические трусы и трусы, используемые при недержании.The term “absorbent article” refers to articles that are placed directly opposite the user's skin to adsorb and preserve physiological exudates, such as urine, feces and menstrual fluid. The invention mainly relates to disposable absorbent articles, which include articles that are not intended to be washed, or otherwise restored, or reused as an absorbent article after use. The invention relates to “coward-type absorbent articles”. Examples of such absorbent articles such as panties are diapers in the form of panties, hygiene pants and panties used for incontinence.

“Растянутое состояние” изделия в данном документе определяется как состояние, в котором изделие является растянутым во всех четырех направлениях до такой степени, что все эластичные материалы, содержащиеся в нем, такие как эластичный рулонный материал, резинки на талии, резинки на ногах, растягиваются так, что они не соберут в складки никакую часть изделия, т.е. изделие является совершенно плоским. Изделие растягивается только до такой степени, когда достигается данное плоское состояние.The “stretched state” of an article in this document is defined as the state in which the article is stretched in all four directions to such an extent that all the elastic materials contained therein, such as elastic web material, elastic at the waist, elastic at the feet, are stretched so that they will not fold any part of the product into folds, i.e. the product is completely flat. The product is stretched only to the extent that this flat state is achieved.

Фиг.1 показывает воплощение адсорбирующего изделия 1, которое является подгузником в виде трусов для детей или взрослых людей, страдающих недержанием. Изделие содержит, по меньшей мере, один первый эластичный рулонный материал 10. Далее данный эластичный рулонный материал 10 описывается подробно.Figure 1 shows an embodiment of an absorbent article 1, which is a diaper in the form of pants for children or adults with incontinence. The product contains at least one first elastic roll material 10. Next, this elastic roll material 10 is described in detail.

Эластичность в х-направлении эластичного сетчатого материала 10 должна составлять, по меньшей мере, 30%, предпочтительно, по меньшей мере, 50%, более предпочтительно, по меньшей мере, 70%, как измеряется тестом на эластичность, детально изложенном в данном документе. Предпочтительно эластичный рулонный материал 10 является также эластичным в у-направлении изделия. Однако эластичность в у-направлении предпочтительно является более низкой, чем в х-направлении. Эластичность в у-направлении должна составлять, по меньшей мере, 20%. Другой способ характеристики эластичности ламината заключается в определении основной массы эластичного сетчатого материала до и после растяжения. В данном случае подходящий рулонный материал имеет основную массу, равную приблизительно 80 г/м² в нерастянутом состоянии, и его можно растянуть до основной массы, равной 65 г/м².The x-direction elasticity of the elastic net material 10 should be at least 30%, preferably at least 50%, more preferably at least 70%, as measured by the elasticity test detailed in this document. Preferably, the elastic web material 10 is also elastic in the y-direction of the article. However, the elasticity in the y-direction is preferably lower than in the x-direction. Elasticity in the y-direction should be at least 20%. Another way to characterize the elasticity of a laminate is to determine the bulk of the elastic net material before and after stretching. In this case, a suitable web material has a bulk of approximately 80 g / m ² in an unstretched condition, and can be stretched to a bulk of 65 g / m ² .

Эластичный рулонный материал 10 является предпочтительно многослойным материалом 9. На воплощении, иллюстрированном на Фиг.5, эластичный рулонный материал 10 является эластичным ламинатом 9, состоящим из первого и второго внешних слоев волокнистого материала (т.е. нетканого) 11 и 12 и слоя 13 эластичной пленки, расположенного между указанными волокнистыми слоями. Однако понятно, что можно применять другие типы эластичных сетчатых материалов, такие как эластичные нетканые материалы, нетканые материалы, которые сами по себе являются не эластичными, но которые эластифицируются посредством эластичных нитей и т.д. Эластичные сетчатые материалы могут содержать один слой или два или более слоев, которые были ламинированы. Общая основная масса эластичного сетчатого материала 10 составляет предпочтительно 100 г/м² или менее, более предпочтительно не более, чем 90 г/м².The elastic roll material 10 is preferably a multilayer material 9. In the embodiment illustrated in FIG. 5, the elastic roll material 10 is an elastic laminate 9 consisting of the first and second outer layers of fibrous material (i.e. non-woven) 11 and 12 and layer 13 an elastic film located between these fibrous layers. However, it is understood that other types of elastic net materials can be used, such as elastic non-woven materials, non-woven materials which are not elastic in themselves, but which are elasticized by elastic threads, etc. Elastic mesh materials may contain one layer or two or more layers that have been laminated. The total bulk of the elastic net material 10 is preferably 100 g / m ² or less, more preferably not more than 90 g / m ² .

В эластичном ламинате, показанном и описанном в данном документе, предпочтительным является, чтобы внешние волокнистые слои 11 и 12 выбирались так, чтобы они в комбинации с внутренним слоем эластичной пленки 13 придавали материалу более высокое сопротивление проколу. Они также должны предоставить ламинату мягкое и подобное одежде ощущение. Примерами подходящих материалов являются кардные сетки и спряденные материалы. Основная масса слоев волокнистого материала должна составлять между 10 и 35 г/м², предпочтительно между 12 и 30 г/м², более предпочтительно между 15 и 25 г/м². Примерами подходящих полимеров, применяемых в волокнистых материалах, являются полиэтилен, сложные полиэфиры, полипропилен и другие полиолефиновые гомополимеры и сополимеры. Можно также применять натуральные волокна, например хлопчатобумажные, пока они обеспечивают требуемые свойства. Смесь полимеров может способствовать более высокой гибкости волокнистых слоев и благодаря этому придавать волокнистому материалу более высокое удлинение при максимальной нагрузке. Доказано, что смесь полимеров полиэтилена и полипропилена обеспечивает хорошие результаты в данном отношении. Также является возможным, чтобы волокнистые слои содержали смесь волокон различных полимеров.In the elastic laminate shown and described herein, it is preferable that the outer fibrous layers 11 and 12 be selected so that in combination with the inner layer of the elastic film 13 give the material a higher puncture resistance. They should also provide the laminate with a soft and clothing-like feel. Examples of suitable materials are carded meshes and spun materials. The bulk of the layers of fibrous material should be between 10 and 35 g / m ² , preferably between 12 and 30 g / m ² , more preferably between 15 and 25 g / m ² . Examples of suitable polymers used in fibrous materials are polyethylene, polyesters, polypropylene and other polyolefin homopolymers and copolymers. Natural fibers, such as cotton, can also be used as long as they provide the desired properties. A mixture of polymers can contribute to higher flexibility of the fibrous layers and thereby give the fibrous material a higher elongation at maximum load. It has been proven that a mixture of polymers of polyethylene and polypropylene provides good results in this regard. It is also possible that the fibrous layers contain a mixture of fibers of various polymers.

Слой 13 эластичной пленки в соответствии с одним воплощением изобретения является апертурной (перфорированной) эластичной пленкой, имеющей основную массу между 20 и 80 г/м², предпочтительно между 20 и 60 г/м². Пленка может быть из любого подходящего эластичного полимера, природного или синтетического. Некоторыми примерами подходящих материалов для эластичной пленки являются полиэтилены низкой кристалличности, полиэтилены низкой кристалличности на металлоценовом катализаторе, сополимеры этилена и винилацетата (EVA), полиуретан, полиизопрен, сополимеры бутадиена и стирола, блок-сополимеры стирола, такие как блок-сополимеры стирола, изопрена и стирола (SIS), стирола, бутадиена и стирола (SВS) или стирола, этилена-бутадиена и стирола. Можно также применять смеси этих полимеров, а также другие модифицированные эластомерные или неэластомерные материалы. Одним примером подходящей пленки является апертурная трехслойная эластомерная пленка PE-SEBS-PE.The elastic film layer 13 according to one embodiment of the invention is an aperture (perforated) elastic film having a bulk of between 20 and 80 g / m ² , preferably between 20 and 60 g / m ² . The film may be from any suitable flexible polymer, natural or synthetic. Some examples of suitable materials for an elastic film are low crystallinity polyethylene, low crystallinity polyethylene on a metallocene catalyst, ethylene vinyl acetate (EVA) copolymers, polyurethane, polyisoprene, butadiene and styrene copolymers, styrene block copolymers such as styrene, isoprene and block copolymers styrene (SIS), styrene, butadiene and styrene (SBS), or styrene, ethylene butadiene and styrene. Mixtures of these polymers can also be used, as well as other modified elastomeric or non-elastomeric materials. One example of a suitable film is the aperture three-layer elastomeric film PE-SEBS-PE.

Эластичный ламинат 9 можно изготовить в соответствии со способом, раскрытым в WO 03/047488, в котором один спряденный слой 11 наносится на пленку 13 в клейком состоянии и таким образом связывается со слоем пленки, в то время как другой спряденный слой 12 адгезивно ламинируется со слоем пленки 13 с использованием, например, термоплавкого адгезива, чувствительного к давлению. Альтернативно ламинат производят в соответствии с модифицированной версией данного известного способа, причем модификация заключается в том, что ламинат инкрементно растягивается (через чересстрочные устройства, IMG) до точки ниже удлинения при пиковой нагрузке, по меньшей мере, одного из неэластичных нетканых слоев для сохранения некоторой прочности, по меньшей мере, для одного из нетканых слоев. Другой слой можно также растянуть до точки ниже его удлинения при пиковой нагрузке или до точки, при которой он будет разрываться в ходе растяжения.The elastic laminate 9 can be made in accordance with the method disclosed in WO 03/047488, in which one spun layer 11 is applied to the film 13 in an adhesive state and thus bonded to the film layer, while the other spun layer 12 is adhesive laminated to the layer films 13 using, for example, a pressure sensitive hot melt adhesive. Alternatively, the laminate is produced in accordance with a modified version of this known method, the modification being that the laminate is incrementally stretched (through interlaced devices, IMG) to a point below elongation at peak load of at least one of the non-elastic non-woven layers to maintain some strength at least for one of the nonwoven layers. Another layer can also be stretched to a point below its elongation at peak load or to a point at which it will break during stretching.

Способ, раскрытый в WO 03/047488, включает растяжение ламината свыше точки разрушения волокнистого материала так, чтобы неэластичные слои разрушались совсем. Следовательно, как описано в WO 03/047488, удлинение ламината не ограничивается модулем растяжения неэластичного материала.The method disclosed in WO 03/047488 involves stretching the laminate over the fracture point of the fibrous material so that the inelastic layers break completely. Therefore, as described in WO 03/047488, the extension of the laminate is not limited to the tensile modulus of the inelastic material.

В предпочтительном воплощении, по меньшей мере, один, предпочтительно оба волокнистых слоя, которые связываются с эластичной пленкой (в отличие от способа, описанного в WO 03/047488), не полностью разрываются при образовании ламината в соответствии с настоящим изобретением. Выбор волокнистых материалов, которые имеют удлинение при максимальной нагрузке больше, чем эластичность эластичного ламината, позволяет эластичной пленке растягиваться без препятствий со стороны волокнистых слоев. Подобный выбор также гарантирует, что волокнистые слои вносят вклад в сопротивление проколу ламината, так как они не полностью расслаиваются или разрушаются в ходе изготовления. Предпочтительно оба волокнистых слоя или, по меньшей мере, один из волокнистых слоев имеют удлинение при максимальной нагрузке, которое, по меньшей мере, на 10% выше, чем эластичность ламината. Это описано более подробно в документе РСТ/SE2004/001005, который включен в данное описание в виде ссылки.In a preferred embodiment, at least one, preferably both of the fibrous layers that bind to the elastic film (in contrast to the method described in WO 03/047488) does not completely break when a laminate is formed in accordance with the present invention. The choice of fibrous materials that have an elongation at maximum load greater than the elasticity of the elastic laminate allows the elastic film to stretch without obstruction from the side of the fibrous layers. This selection also ensures that the fibrous layers contribute to the puncture resistance of the laminate, as they do not completely delaminate or break during manufacture. Preferably, both fibrous layers or at least one of the fibrous layers have an elongation at maximum load, which is at least 10% higher than the elasticity of the laminate. This is described in more detail in PCT / SE2004 / 001005, which is incorporated herein by reference.

Непрозрачность слоя материала является характеристической способностью слоя материала прятаться визуально со стороны нижележащего объекта или рисунка. Непрозрачность измеряется в процентах, где непрозрачность в 100% означает, что ничего нельзя увидеть через слой материала, и 0% означает, что слой материала является совершенно прозрачным. Непрозрачность измеряется с помощью теста на непрозрачность, раскрытого в РСТ/SE2004/001415, который основан на данных показателя отражения света.The opacity of the material layer is the characteristic ability of the material layer to hide visually from the side of the underlying object or pattern. Opacity is measured as a percentage, where 100% opacity means that nothing can be seen through the material layer, and 0% means that the material layer is completely transparent. Opacity is measured using the opacity test disclosed in PCT / SE2004 / 001415, which is based on light reflectance data.

Непрозрачность эластичного сетчатого материала 10 можно получить при введении непрозрачных наполнителей в ламинат 9, особенно в эластичную пленку 13. Подобные пигменты могут быть органическими или неорганическими красителями, красящими добавками или отбеливающими добавками. Неорганические материалы, такие как диоксид титана, неорганические карбонаты, синтетические карбонаты, тальк, сиенит нифелина, гидроксид магния, тригидрат алюминия сиатомитовой земли, слюда, природные или синтетические кремнекислоты, кальцинированные глины и их смеси, являются все примерами предпочтительных непрозрачных наполнителей. Наполнитель предпочтительно добавляют в качестве маточной смеси при экструзии пленки. Один пример приблизительной концентрации составляет около 5% наполнителя к массе пленки.The opacity of the elastic net material 10 can be obtained by introducing opaque fillers into the laminate 9, especially into the elastic film 13. Such pigments can be organic or inorganic dyes, coloring additives or bleaching additives. Inorganic materials such as titanium dioxide, inorganic carbonates, synthetic carbonates, talc, nypheline syenite, magnesium hydroxide, Siatomite earth aluminum trihydrate, mica, natural or synthetic silicic acids, calcined clays and mixtures thereof are all examples of preferred opaque fillers. Filler is preferably added as a masterbatch during film extrusion. One example of an approximate concentration is about 5% filler by weight of the film.

Предпочтительно, чтобы эластичный рулонный материал 10 имел воздухопроницаемость (скорость пропускания водяного пара) в соответствии с методикой D ASTM Е96-00, по меньшей мере, 1500 г/м² 24 ч, предпочтительно, по меньшей мере, 3000 г/м² 24 ч. Живое сечение (открытая область) слоя эластичной пленки составляет предпочтительно, по меньшей мере, 5%, более предпочтительно, по меньшей мере, 8%. Живое сечение измеряется способами анализа изображения и определяется как сумма площади отверстий, деленная на общую площадь образца пленки.Preferably, the elastic web material 10 has a breathability (water vapor transmission rate) in accordance with Method D of ASTM E96-00 of at least 1,500 g / m ² 24 h, preferably at least 3,000 g / m ² 24 h The living cross-section (open area) of the elastic film layer is preferably at least 5%, more preferably at least 8%. The live section is measured by image analysis methods and is defined as the sum of the area of the holes divided by the total area of the film sample.

Первый эластичный рулонный материал 10 сваривается с помощью ультразвука, по меньшей мере, с одним вторым сетчатым материалом 21, по меньшей мере, вдоль одного сварного шва 8. Данный второй рулонный материал 21 описывается далее подробно.The first elastic web material 10 is ultrasonically welded to at least one second mesh material 21 along at least one weld 8. This second web material 21 is described in further detail below.

Второй рулонный материал 21 должен также предоставлять мягкое и подобное одежде ощущение адсорбирующему изделию 1. Примерами подходящих материалов являются нетканые материалы, такие как кардные сетки и спряденные материалы. Основная масса второго сетчатого материала должна составлять между 10 и 35 г/м², предпочтительно между 12 и 30 г/м², более предпочтительно между 15 и 25 г/м². Примерами подходящих полимеров, применяемых во втором сетчатом материале, являются полиэтилен, сложные полиэфиры, полипропилен и другие полиолефиновые гомополимеры и сополимеры. Можно также применять натуральные волокна, например хлопчатобумажные, пока они обеспечивают требуемые свойства. Смесь полимеров может способствовать более высокой гибкости второго сетчатого материала и благодаря этому придавать второму сетчатому материалу 21 более высокое удлинение при максимальной нагрузке. Доказано, что смесь полимеров полиэтилена и полипропилена обеспечивает хорошие результаты в данном отношении. Также является возможным, чтобы второй рулонный материал 21 содержал смесь волокон различных полимеров. Предпочтительно второй рулонный материал 21 является воздухопроницаемым.The second web material 21 should also provide a soft and clothing-like feel to the absorbent article 1. Examples of suitable materials are non-woven materials such as carded meshes and spun materials. The bulk of the second mesh material should be between 10 and 35 g / m ² , preferably between 12 and 30 g / m ² , more preferably between 15 and 25 g / m ² . Examples of suitable polymers used in the second network material are polyethylene, polyesters, polypropylene and other polyolefin homopolymers and copolymers. Natural fibers, such as cotton, can also be used as long as they provide the desired properties. A mixture of polymers can contribute to higher flexibility of the second mesh material and thereby give the second mesh material 21 higher elongation at maximum load. It has been proven that a mixture of polymers of polyethylene and polypropylene provides good results in this regard. It is also possible that the second web material 21 contains a mixture of fibers of various polymers. Preferably, the second web material 21 is breathable.

Второй рулонный материал 21 отличается от первого эластичного сетчатого материала 10. Под этим подразумевается, что они различаются, по меньшей мере, одним свойством; например, структурой, составом, текстурой и т.д. Не требуется, чтобы второй рулонный материал 21 имел состав, отличающийся от первого эластичного сетчатого материала 10 (т.е. оба могут содержать одинаковые полимеры, тем не менее в различных формах). Однако второй рулонный материал 21 должен иметь степень эластичности, которая отличается от эластичности первого эластичного сетчатого материала 10, или второй рулонный материал может быть неэластичным. Эластичность сетчатых материалов можно определить при применении теста на эластичность, детально изложенного в данном документе. В одном воплощении второй рулонный материал 21 имеет эластичность, которая является более низкой, чем эластичность первого эластичного сетчатого материала 10.The second web material 21 is different from the first elastic net material 10. By this is meant that they differ in at least one property; for example, structure, composition, texture, etc. It is not required that the second web material 21 have a composition different from the first elastic net material 10 (i.e., both may contain the same polymers, however in different forms). However, the second web material 21 must have a degree of elasticity that is different from that of the first elastic net material 10, or the second web material may be inelastic. The elasticity of the mesh materials can be determined by applying the elasticity test detailed in this document. In one embodiment, the second web material 21 has an elasticity that is lower than the elasticity of the first elastic net material 10.

Ультразвуковой сварной шов 8, 17а, 18а между первым эластичным сетчатым материалом 10 и вторым сетчатым материалом 21 усиливается, чтобы иметь прочность сварки в направлении, поперечном сварному шву, которая составляет, по меньшей мере, 5 Н/25,4 мм. Обнаружено, что прочность сварного шва является достаточной, чтобы сварной шов не разрушился при нагрузках, которым адсорбирующее изделие 1 подвергается при надевании. Предпочтительно ультразвуковой сварной шов 8, 17а, 18а между первым эластичным сетчатым материалом 10 и вторым сетчатым материалом 21 усиливается, чтобы иметь прочность сварного шва в направлении, поперечном сварному шву, которая составляет, по меньшей мере, 7 Н/25,4 мм, предпочтительно, по меньшей мере, 9 Н/25,4 мм.The ultrasonic weld 8, 17a, 18a between the first elastic mesh material 10 and the second mesh material 21 is reinforced to have welding strength in the direction transverse to the weld, which is at least 5 N / 25.4 mm. It was found that the strength of the weld is sufficient so that the weld does not collapse under the loads that the absorbent article 1 is subjected to when donning. Preferably, the ultrasonic weld 8, 17a, 18a between the first elastic mesh material 10 and the second mesh material 21 is reinforced to have a weld strength in the direction transverse to the weld that is at least 7 N / 25.4 mm, preferably at least 9 N / 25.4 mm.

Подгузник в виде трусов, иллюстрированный на Фиг.1, 2 и 3, типично содержит переднюю часть 5 и заднюю часть 6. Изделие имеет продольное направление у и поперечное направление х. Как можно видеть на Фиг.1, передняя и задняя части соединяются друг с другом вдоль двух противоположных продольных боковых краев 4 для ограничения отверстия для талии 15 и пары отверстий для ног 16. По меньшей мере, одна из передней и задней частей 5, 6 содержит первый эластичный рулонный материал 10, как описано выше. Подгузник далее содержит ластовичную часть 7, расположенную между передней частью 5 и задней частью 6 в продольном направлении у изделия. Ластовичная часть 7 содержит второй рулонный материал 21, как описано выше. Ластовичная часть 7 приваривается к передней 5 и задней 6 частям с помощью ультразвуковых сварных швов 8. Эти ультразвуковые сварные швы имеют прочность сварного шва в направлении, поперечном сварному шву, как определено выше.The panty-shaped diaper illustrated in FIGS. 1, 2 and 3 typically comprises a front portion 5 and a rear portion 6. The article has a longitudinal direction y and a transverse direction x. As can be seen in FIG. 1, the front and rear parts are connected to each other along two opposite longitudinal side edges 4 to limit the openings for the waist 15 and the pair of openings for the legs 16. At least one of the front and rear parts 5, 6 contains the first elastic web material 10, as described above. The diaper further comprises a crotch portion 7 located between the front part 5 and the rear part 6 in the longitudinal direction of the product. The gusset portion 7 comprises a second web material 21, as described above. The shank portion 7 is welded to the front 5 and rear 6 parts using ultrasonic welds 8. These ultrasonic welds have a weld strength in the direction transverse to the weld as defined above.

Передняя часть 5 ограничивается сварным швом 17а, присоединяющим ее к передней части 17 талии, причем продольные боковые края 4 изделия и сварной шов 8 присоединяют ее к ластовичной части 7. При применении передняя часть 5 располагается на животе пользователя. Задняя часть ограничивается подобным образом: сварной шов 18а присоединяет ее к задней части 18 талии, продольные боковые края 4 изделия и сварной шов 8 присоединяют ее к ластовичной части 7. Ластовичная часть ограничивается на продольных краях краями отверстий 16 для ног изделия и на поперечных краях сварными швами 8, описанными выше.The front part 5 is limited by a weld seam 17a connecting it to the front part 17 of the waist, and the longitudinal side edges 4 of the product and the weld 8 connect it to the crotch part 7. In use, the front part 5 is located on the stomach of the user. The back part is limited in a similar way: the weld seam 18a connects it to the rear part 18 of the waist, the longitudinal side edges 4 of the product and the weld 8 connect it to the crotch part 7. The crotch part is limited on the longitudinal edges by the edges of the openings 16 for the legs of the product and welded on the transverse edges seams 8 described above.

Как упоминалось выше, по меньшей мере, одна из передней и задней частей 5 и 6 изделия 1 содержит эластичный рулонный материал 10. Предпочтительно как передняя, так и задняя части 5 и 6 содержат эластичный рулонный материал 10. Эластичный рулонный материал 10 является предпочтительно одинаковым как в передней 5, так и в задней 6 частях, однако эластичный рулонный материал 10 может быть различным в передней 5 и задней 6 частях. Эластичный рулонный материал может быть единым компонентом передней 5 и задней 6 частей, по меньшей мере, на 20%, предпочтительно на 25%, более предпочтительно на 30%, наиболее предпочтительно на 40% общей площади поверхности адсорбирующего изделия.As mentioned above, at least one of the front and rear parts 5 and 6 of the article 1 contains elastic roll material 10. Preferably, both the front and rear parts 5 and 6 contain elastic roll material 10. The elastic roll material 10 is preferably the same as in the front 5 and rear 6 parts, however, the elastic web material 10 may be different in the front 5 and rear 6 parts. The elastic web material may be a single component of the front 5 and rear 6 parts, at least 20%, preferably 25%, more preferably 30%, most preferably 40% of the total surface area of the absorbent article.

Адсорбирующее изделие 1 типа трусов в соответствии с изобретением может также содержать переднюю часть 17 талии, которая располагается на крае передней части 5, который является дистальным относительно ластовичной части 7 в продольном направлении у изделия. Как описано выше, передняя часть 5 содержит первый эластичный рулонный материал 10, в то время как передняя часть 17 талии содержит второй рулонный материал 21. Передняя часть 17 талии приваривается к передней части 5 с помощью ультразвукового сварного шва 17а. Эти ультразвуковые сварные швы имеют прочность сварного шва в направлении, поперечном сварному шву, как определяется выше.The panty type absorbent article 1 according to the invention may also comprise a front waist part 17 which is located at the edge of the front part 5, which is distal relative to the crotch part 7 in the longitudinal direction of the product. As described above, the front part 5 comprises a first elastic web material 10, while the front part 17 of the waist comprises a second web material 21. The front part 17 of the waist is welded to the front part 5 by means of an ultrasonic weld 17a. These ultrasonic welds have a weld strength in the direction transverse to the weld, as defined above.

Адсорбирующее изделие 1 типа трусов может альтернативно или дополнительно содержать заднюю часть 18 талии, которая располагается на крае задней части 6, который является дистальным относительно ластовичной части 7 в продольном направлении у изделия. Задняя часть 6 содержит первый эластичный рулонный материал 10, в то время как задняя часть 18 талии содержит второй рулонный материал 21. Задняя часть 18 талии приваривается к задней части 6 с помощью ультразвукового сварного шва 18а. Эти ультразвуковые сварные швы имеют прочность сварного шва в направлении, поперечном сварному шву, как определяется выше. Нет необходимости, чтобы материал задней части 18 талии был таким же, как и материал передней части 17 талии.The panty type absorbent article 1 may alternatively or additionally include a waist back 18 that is located at the edge of the back 6, which is distal relative to the crotch portion 7 in the longitudinal direction of the product. The rear portion 6 comprises a first elastic roll material 10, while the rear waist portion 18 comprises a second roll material 21. The rear waist portion 18 is welded to the rear portion 6 using an ultrasonic weld 18a. These ultrasonic welds have a weld strength in the direction transverse to the weld, as defined above. It is not necessary that the material of the rear part 18 of the waist is the same as the material of the front part 17 of the waist.

Усиление сварного шва можно обеспечить дополнительным слоем сетчатого материала 14, который присоединяется к сварному шву 8, 17а, 18а так, чтобы сварной шов получил необходимую прочность сварного шва. Дополнительный слой сетчатого материала 14 можно присоединить к сварному шву 8, 17а, 18а в то же самое время, когда присоединяется остальная часть шва - т.е. посредством ультразвуковой сварки. Альтернативно его можно добавить к сварному шву 8, 17а, 18а на более поздней стадии хотя одновременное присоединение является предпочтительным для облегчения изготовления. Дополнительный слой сетчатого материала 14 можно присоединить с помощью адгезии, ультразвуковой сварки, тепловой сварки или любого способа, известного специалистам для соединения двух материальных сеток. В предпочтительном воплощении дополнительный слой сетчатого материала 14 располагается между первым эластичным сетчатым материалом 10 и вторым сетчатым материалом 21 (т.е. вставляется между ними на участке сварного шва). Альтернативно его можно расположить на внешней поверхности первого эластичного сетчатого материала 10 или на внешней поверхности второго сетчатого материала 21 на участке сварного шва. Могут присутствовать два дополнительных слоя сетчатого материала 14 - каждый снаружи каждой стороны сварного шва. Дополнительный слой сетчатого материала 14 проходит, по меньшей мере, вдоль 50%, предпочтительно, по меньшей мере, вдоль 75%, более предпочтительно, по меньшей мере, вдоль 100% длины сварного шва 8, 17а, 18а, к которому он присоединяется. Дополнительный слой сетчатого материала 14 является предпочтительно нетканым материалом. Предпочтительно дополнительный слой сетчатого материала 14 является полосой материала.The reinforcement of the weld can be provided with an additional layer of mesh material 14, which is attached to the weld 8, 17a, 18a so that the weld obtains the necessary strength of the weld. An additional layer of mesh material 14 can be attached to the weld 8, 17a, 18a at the same time that the rest of the weld is attached — i.e. through ultrasonic welding. Alternatively, it can be added to the weld 8, 17a, 18a at a later stage although simultaneous joining is preferred to facilitate fabrication. An additional layer of mesh material 14 can be attached using adhesion, ultrasonic welding, heat welding, or any method known to those skilled in the art for joining two material grids. In a preferred embodiment, an additional layer of mesh material 14 is sandwiched between the first elastic mesh material 10 and the second mesh material 21 (i.e., inserted between them at the weld section). Alternatively, it may be located on the outer surface of the first elastic mesh material 10 or on the outer surface of the second mesh material 21 in the weld area. Two additional layers of mesh material 14 may be present - each on the outside of each side of the weld. An additional layer of mesh material 14 extends at least along 50%, preferably at least along 75%, more preferably at least along 100% of the length of the weld 8, 17a, 18a to which it is attached. The additional layer of net material 14 is preferably a nonwoven material. Preferably, the additional layer of net material 14 is a strip of material.

Нет необходимости, чтобы дополнительный слой сетчатого материала 14 являлся отдельным куском материала, который присоединяется к адсорбирующему изделию 1. При условии, что удовлетворяются требования прочности сварного шва, дополнительный слой сетчатого материала 14 может быть компонентом адсорбирующего изделия в сварке. Например, передняя и задняя части 17, 18 талии в большинстве случаев образуются более чем из одного слоя сетчатого материала. Слой нетканого материала можно согнуть так, чтобы линия сгиба образовала внешний край подгузника 1 в виде трусов в продольном направлении (у), в то время как два края сетчатого материала соприкасаются на сварном шве 17а, 18а. Если это так, то для целей настоящего изобретения является достаточным, чтобы оба слоя, которые содержат части 17, 18 талии приваривались к передней/задней частям 5, 6. До тех пор пока на участке сварного шва присутствует, по меньшей мере, один дополнительный слой сетчатого материала 14, требования изобретения выполняются.It is not necessary that the additional layer of mesh material 14 be a separate piece of material that is attached to the absorbent article 1. Provided that the strength requirements of the weld are satisfied, the additional layer of mesh material 14 may be a component of the absorbent article in welding. For example, the front and back of the waist 17, 18 in most cases are formed from more than one layer of mesh material. The nonwoven layer can be bent so that the fold line forms the outer edge of the diaper 1 in the form of pants in the longitudinal direction (y), while the two edges of the mesh material are in contact on the weld 17a, 18a. If this is the case, for the purposes of the present invention, it is sufficient that both layers that contain waist portions 17, 18 are welded to the front / rear portions 5, 6. As long as at least one additional layer is present in the weld section mesh material 14, the requirements of the invention are fulfilled.

Усиление можно также обеспечить с помощью клея, который наносится вдоль 50-100%, предпочтительно вдоль 70-90% длины сварного шва 8, 17а, 18а так, чтобы сварной шов получил необходимую прочность сварного шва. Клей можно нанести одновременно с ультразвуковой сваркой или на более поздней стадии. Если клей наносится одновременно с ультразвуковой сваркой, его можно нанести на поверхности первого эластичного сетчатого материала 10 и второго сетчатого материала 21, которые входят в контакт внутри сварного шва. Альтернативно их можно нанести на одну или обе поверхности первого эластичного сетчатого материала 10 и/или второго сетчатого материала 21, которые не контактируют в сварном шве. Если клей наносится на более поздней стадии, его можно нанести на одну или обе внешние поверхности сварного шва 8, 17а, 18а.Reinforcement can also be achieved with glue, which is applied along 50-100%, preferably along 70-90% of the length of the weld 8, 17a, 18a so that the weld obtains the necessary strength of the weld. The adhesive can be applied simultaneously with ultrasonic welding or at a later stage. If the adhesive is applied simultaneously with ultrasonic welding, it can be applied on the surface of the first elastic mesh material 10 and the second mesh material 21, which come into contact inside the weld. Alternatively, they can be applied to one or both surfaces of the first elastic mesh material 10 and / or the second mesh material 21 that are not in contact in the weld. If the adhesive is applied at a later stage, it can be applied to one or both outer surfaces of the weld 8, 17a, 18a.

Адсорбирующее изделие 1 типа трусов в соответствии с изобретением может далее содержать адсорбирующий комплект 3, причем адсорбирующий комплект 3 содержит непроницаемый для жидкости защитный слой 19, проницаемый для жидкости верхний слой 20 и адсорбирующую сердцевину 2, заключенную между ними (Фиг.4). Эти компоненты описываются далее.The panty type absorbent article 1 according to the invention may further comprise an absorbent kit 3, the absorbent kit 3 comprising a liquid impervious protective layer 19, a liquid permeable top layer 20, and an absorbent core 2 enclosed therebetween (FIG. 4). These components are described below.

Верхний слойUpper layer

Проницаемый для жидкости верхний слой 20 может состоять из нетканого материала, например спряденного, вспученного, кардного, гидроспутанного, влажно уложенного и т.д. Подходящие нетканые материалы могут состоять из натуральных волокон, таких как древесная масса или хлопчатобумажные волокна, искусственных волокон, таких как сложный полиэфир, полиэтилен, полипропилен, вискоза и т.д. или из смеси натуральных и искусственных волокон. Материал верхнего слоя может далее состоять из волокон пакли, которые могут быть связаны друг с другом в связанном рисунке, как, например раскрыто в ЕР-А-1035818. Дальнейшими примерами материалов верхнего слоя являются пористые пены, апертурные пластичные пленки и т.д. Материалы, подходящие в качестве материалов верхнего слоя, должны быть мягкими и не раздражающими кожу и предназначенными для легкого пропитывания физиологической текучей средой, например мочой или менструальной текучей средой. Верхний слой может быть различным в различных частях адсорбирующего изделия.The liquid-permeable topsheet 20 may consist of a non-woven material, for example spun, expanded, carded, hydro-tangled, wet laid, etc. Suitable non-woven materials may consist of natural fibers, such as wood pulp or cotton fibers, artificial fibers, such as polyester, polyethylene, polypropylene, rayon, etc. or from a mixture of natural and artificial fibers. The material of the top layer may further consist of tow fibers, which may be bonded to each other in a related pattern, as, for example, disclosed in EP-A-1035818. Further examples of topcoat materials are porous foams, aperture plastic films, etc. Materials suitable as topcoat materials should be soft and non-irritating to the skin and designed to be easily soaked with physiological fluid, such as urine or menstrual fluid. The top layer may be different in different parts of the absorbent article.

Защитный слойProtective layer

Непроницаемый для жидкости защитный слой 19, содержащийся в адсорбирующем комплекте 3 на обращенной к предмету одежды стороне адсорбирующей сердцевины 2, состоит из непроницаемого для жидкости материала, такого как тонкая пластичная пленка, например полиэтиленовая или полипропиленовая пленка, нетканого материала, покрытого не проницаемым для жидкости материалом, гидрофобного нетканого материала, который препятствует проникновению жидкости, или ламината, содержащего пластичные пленки и нетканые материалы. Защитный слой 19 может быть воздухопроницаемым так, чтобы позволить улетучиванию пара из адсорбирующей сердцевины, в то же время все еще предотвращая прохождение через него жидкостей. Примерами воздухопроницаемых материалов защитного слоя являются пористые полимерные пленки, нетканые ламинаты из спряденных и вспученных слоев, ламинаты из пористых полимерных пленок и нетканых материалов. Защитный слой 19 является предпочтительно не эластичным.The liquid impervious protective layer 19 contained in the absorbent assembly 3 on the clothing side of the absorbent core 2 consists of a liquid impermeable material, such as a thin plastic film, for example a polyethylene or polypropylene film, a non-woven material coated with a liquid impermeable material hydrophobic non-woven material that prevents the penetration of a liquid, or a laminate containing plastic films and non-woven materials. The protective layer 19 may be breathable so as to allow vapor to escape from the absorbent core, while still preventing liquids from passing through it. Examples of breathable materials of the protective layer are porous polymer films, non-woven laminates from spun and expanded layers, laminates from porous polymer films and non-woven materials. The protective layer 19 is preferably not elastic.

Адсорбирующая сердцевинаAbsorbent core

“Адсорбирующая сердцевина” является адсорбирующей структурой, расположенной в адсорбирующем комплекте адсорбирующего изделия. Адсорбирующая сердцевина 2 может быть любого традиционного вида. Примерами обычно встречающихся адсорбирующих материалов являются распушенная масса целлюлозы, тканевые слои, высоко адсорбирующие полимеры (так называемые сверхадсорбенты), адсорбирующие вспененные материалы, адсорбирующие нетканые материалы или подобные. Является общепринятым комбинировать распушенную массу целлюлозы со сверхадсорбирующими полимерами в адсорбирующей сердцевине. Сверхадсорбирующие полимеры являются набухаемыми в воде, не растворимыми в воде органическими или неорганическими материалами, способными адсорбировать, по меньшей мере, около 20 раз собственной массы и в водном растворе содержащими 0,9 массовых процентов хлорида натрия. Органические материалы, подходящие для применения в качестве сверхадсорбирующего материала, могут включать природные материалы, такие как полисахариды, полипептиды и подобные, наряду с синтетическими материалами, такими как синтетические гидрогелевые полимеры. Подобные гидрогелевые полимеры включают, например, соли щелочных металлов полиакриловых кислот, полиакриламиды, поливиниловый спирт, полиакрилаты, полиакриламиды, поливинилпиридины и подобные. Другие подходящие полимеры включают гидролизованный крахмал с привитым акрилонитрилом, крахмал с привитой акриловой кислотой и сополимеры изобутилена и малеинового ангидрида и их смеси. Гидрогелевые полимеры предпочтительно слегка сшиваются для превращения материала, по существу, в нерастворимую в воде форму. Предпочтительные сверхадсорбирующие материалы далее сшиваются на поверхности так, чтобы внешняя поверхность или оболочка сверхадсорбирующей частицы, волокна, чешуйки, сферы и т.д. обладала более высокой плотностью сшивания, чем внутренняя часть сверхадсорбента. Сверхадсорбирующие материалы могут находиться в любой форме, подходящей для применения в адсорбирующих композитах, включая частицы, волокна, чешуйки, сферы и подобные.An “absorbent core” is an absorbent structure located in an absorbent assembly of an absorbent article. The absorbent core 2 may be of any conventional kind. Examples of commonly occurring adsorbent materials are fluff pulp, tissue layers, highly absorbent polymers (so-called superabsorbents), absorbent foam materials, absorbent nonwoven materials, or the like. It is generally accepted to combine the fluff pulp with superabsorbent polymers in an absorbent core. Superabsorbent polymers are water-swellable, water-insoluble organic or inorganic materials, capable of adsorbing at least about 20 times their own weight and containing 0.9 weight percent sodium chloride in an aqueous solution. Organic materials suitable for use as a superabsorbent material may include natural materials such as polysaccharides, polypeptides and the like, along with synthetic materials such as synthetic hydrogel polymers. Such hydrogel polymers include, for example, alkali metal salts of polyacrylic acids, polyacrylamides, polyvinyl alcohol, polyacrylates, polyacrylamides, polyvinylpyridines and the like. Other suitable polymers include hydrolyzed starch grafted with acrylonitrile, starch grafted with acrylic acid and copolymers of isobutylene and maleic anhydride and mixtures thereof. The hydrogel polymers are preferably slightly crosslinked to convert the material substantially into a water-insoluble form. Preferred superabsorbent materials are further crosslinked so that the outer surface or shell of the superabsorbent particle, fiber, flake, sphere, etc. had a higher crosslink density than the inner part of the superabsorbent. Superabsorbent materials can be in any form suitable for use in adsorbent composites, including particles, fibers, flakes, spheres and the like.

Высокая адсорбционная способность обеспечивается применением большого количества сверхадсорбирующего материала. Для адсорбирующей сердцевины, содержащей матрицу гидрофильных волокон, таких как волокна целлюлозы, и сверхадсорбирующего материала доля сверхадсорбирующего материала составляет предпочтительно между 10 и 90 мас.%, более предпочтительно между 30 и 70 мас.%.High adsorption capacity is ensured by the use of a large amount of superabsorbent material. For an absorbent core containing a matrix of hydrophilic fibers, such as cellulose fibers, and a superabsorbent material, the proportion of superabsorbent material is preferably between 10 and 90 wt.%, More preferably between 30 and 70 wt.%.

Традиционно, чтобы адсорбирующие изделия имели адсорбирующие сердцевины, содержащие слои с различными свойствами по отношению к способности приема жидкости, способности распределения жидкости и способности сохранения. Тонкие адсорбирующие основные части, которые являются обычными, например, в детских подгузниках и защитных средствах при недержании, часто содержат сжатую смешанную или слоистую структуру распушенной массы целлюлозы и сверхадсорбирующих полимеров. Размер и адсорбционная способность адсорбирующей сердцевины может варьироваться, чтобы подходить для различных применений, таких как для детей или для взрослых людей с недержанием.Conventionally, absorbent articles have absorbent cores containing layers with different properties with respect to liquid receiving ability, liquid distribution ability, and storage ability. Thin adsorbent core parts that are common, for example, in baby diapers and incontinence protectors, often contain a compressed mixed or layered structure of the fluff pulp and superabsorbent polymers. The size and adsorption capacity of the absorbent core may vary to suit various applications, such as for children or for adults with incontinence.

Адсорбирующая сердцевина может далее включать слой распределения и сбора, расположенный наверху основной адсорбирующей основной части и который приспособлен для быстрого приема и временного сохранения выделенной жидкости до того, как она адсорбируется основной адсорбирующей сердцевиной. Подобные слои распределения и сбора хорошо известны в технике и могут состоять из пористых волокнистых подкладок или вспененных материалов.The absorbent core may further include a distribution and collection layer located at the top of the main absorbent core and which is adapted to quickly receive and temporarily store the recovered liquid before it is adsorbed by the main absorbent core. Such distribution and collection layers are well known in the art and may consist of porous fibrous linings or foam materials.

ОПИСАНИЕ СПОСОБОВ ИСПЫТАНИЙDESCRIPTION OF TEST METHODS

Тест на эластичностьElasticity test

Способ измеряет, как эластичный материал ведет себя при повторяющихся циклах нагрузки и разгрузки. Образец растягивается до предварительно определенного удлинения и совершается циклическое движение между 0 и указанным предварительно определенным удлинением. Регистрируются желательные усилия нагрузки и разгрузки. Измеряется постоянное, т.е. остающееся, удлинение расслабленного материала.The method measures how an elastic material behaves during repeated loading and unloading cycles. The sample is stretched to a predetermined elongation and a cyclic movement is made between 0 and the specified predefined elongation. The desired loading and unloading forces are recorded. The constant is measured, i.e. remaining, lengthening of relaxed material.

Используется динамометр Lloyd LRX, способный совершать циклические движения и оснащенный принтером/самописцем, или используется программное обеспечение. Образец получают при разрезании его до ширины 25 мм и длины, которая предпочтительно на 20 мм длиннее, чем расстояние между зажимами динамометра.A Lloyd LRX dynamometer capable of cycling and equipped with a printer / recorder is used, or software is used. The sample is obtained by cutting it to a width of 25 mm and a length that is preferably 20 mm longer than the distance between the clamps of the dynamometer.

Динамометр калибруется в соответствии с приборными инструкциями. Параметры, необходимые для испытания (усилия нагрузки и разгрузки), регулируются:The dynamometer is calibrated in accordance with the instrument instructions. The parameters required for the test (load and unloading forces) are regulated:

Скорость ползуна: 500 мм/минSlider Speed: 500mm / min

Расстояние между зажимами: 50 ммClamp distance: 50 mm

Предварительная нагрузка: 0,05 НPreload: 0.05 N

Образец помещают в зажимы в соответствии с отметками и следует удостовериться, что образец центрирован и прикреплен перпендикулярно к зажимам. Динамометр включают и совершают три цикла между 0 и предварительно определенным удлинением, равным самой высокой определенной 1-й нагрузке. Перед последним циклом образец релаксирует в течение 1 минуты, затем измеряется постоянное удлинение при растяжении образца до тех пор, пока не достигается усилие в 0,1 Н, и считывается удлинение.The sample is placed in the clamps in accordance with the marks and you should make sure that the sample is centered and attached perpendicular to the clamps. The dynamometer is turned on and performs three cycles between 0 and a predetermined extension equal to the highest defined 1st load. Before the last cycle, the sample relaxes for 1 minute, then the constant elongation is measured by stretching the sample until a force of 0.1 N is reached, and the elongation is read.

Постоянное удлинение после релаксации должно быть менее чем 10% и измеряется выше приведенным способом. Таким образом, эластичность в 30% определяется, как тот факт, что ламинат должен иметь постоянную релаксацию после удлинения менее чем 10% после воздействия до удлинения в 30% на приведенном выше динамометре. Удлинение в 30% означает удлинение до длины, которая на 30% длиннее, чем первоначальная длина образца.Permanent elongation after relaxation should be less than 10% and is measured by the above method. Thus, an elasticity of 30% is defined as the fact that the laminate must have permanent relaxation after elongation of less than 10% after exposure to elongation of 30% on the above dynamometer. Elongation of 30% means elongation to a length that is 30% longer than the original length of the sample.

Тестовый способ измерения прочности сварного шваTest method for measuring the strength of the weld

Условная прочность при растяжении сварных швов измеряется в соответствии со способом, описанном в патентной заявке РСТ 2004/001004 (ссылка на ASTM D 882). Прямоугольные образцы для испытаний вырезают из адсорбирующих изделий так, чтобы усиленный сварной шов вытягивался через образец, по существу, перпендикулярно краям образца. Ширина образцов для испытаний составляет 25,4 мм и длина - если возможно - на 50 мм длиннее, чем расстояние между зажимами разрывной машины Instron 4301. Фиг.6 и 7 иллюстрируют, как образцы для испытаний крепятся между зажимами машины.Conditional tensile strength of welds is measured in accordance with the method described in patent application PCT 2004/001004 (reference to ASTM D 882). Rectangular test specimens are cut out from the absorbent articles so that the reinforced weld is drawn through the specimen substantially perpendicular to the edges of the specimen. The width of the test specimens is 25.4 mm and the length — if possible — is 50 mm longer than the distance between the clamps of the Instron 4301 tensile testing machine. Figures 6 and 7 illustrate how the test specimens are attached between the clamps of the machine.

Следует понимать, что хотя изобретение описано со ссылкой на предпочтительные воплощения, модификации являются возможными в рамках объема формулы изобретения. В частности, изобретение описано со ссылкой на адсорбирующее изделие типа трусов, но особенности изобретения в равной степени применимы к другим адсорбирующим изделиям, таким как подгузники. Следовательно, изобретение предназначено для охватывания любых вариаций или эквивалентов, которые находятся в рамках известных или привычных осуществлений в рамках технической области, к которой оно принадлежит. Объем настоящего изобретения ограничивается исключительно приложенной формулой изобретения.It should be understood that although the invention has been described with reference to preferred embodiments, modifications are possible within the scope of the claims. In particular, the invention has been described with reference to an absorbent article such as underpants, but the features of the invention are equally applicable to other absorbent articles, such as diapers. Therefore, the invention is intended to cover any variations or equivalents that are within the scope of known or habitual implementations within the technical field to which it belongs. The scope of the present invention is limited solely by the appended claims.

Claims

1. An absorbent product (1), such as a diaper in the form of pants, hygiene pants or pants used for incontinence, said product containing at least one first elastic roll material (10), which is welded using ultrasound, at least to at least one second roll material (21) along at least one weld (8), the second roll material (21) being different from the first elastic roll material (10), the second roll material (21) being inelastic or has a degree of elasticity , which differs from the elasticity of the first elastic roll material (10), characterized in that the ultrasonic weld (8, 17a, 18a) between the first elastic roll material (10) and the second roll material (21) is reinforced so as to have a welding strength of a direction transverse to the weld, which is at least 5 N / 25.4 mm.

2. An absorbent article (1) according to claim 1, characterized in that the article comprises a front part (5) and a rear part (6), in which the front and rear parts are connected to each other along two opposite longitudinal side edges (4) for the restrictions of the holes (15) for the waist and a pair of holes (16) for the legs, and at least one of the front and rear parts (5, 6) contains the first elastic roll material (10), while the product (1) further comprises crotch part (7) located between the front part (5) and the rear part (6) in the longitudinal direction (y) of the product I, and the crotch part (7) contains the second roll material (21), and the crotch part (7) is welded to the front (5) and rear (6) parts using ultrasonic welds (8).

3. The absorbent product (1) according to claim 2, characterized in that both the front (5) and the rear (6) parts contain the first elastic roll material (10).

4. An absorbent product (1) according to any one of claims 1 to 3, characterized in that the product comprises a front part (5) and a rear part (6), in which the front and rear parts are connected to each other along two opposite longitudinal side edges (4) to limit the opening (15) for the waist and a pair of holes (16) for the legs, while the product (1) further comprises a crotch portion (7) located between the front part (5) and the rear part (6) in the longitudinal direction (y) the product, and the product further comprises a front part (17) of the waist, which is located on the edge of the front part (5), which is distal relative to the crotch part (7) in the longitudinal direction (y) of the product, and the front part (5) contains the first elastic roll material (10), and the front part (17) of the waist contains the second roll material (21 ), and the front part (17) of the waist is welded to the front part (5) using an ultrasonic weld (17a).

5. An absorbent product (1) according to any one of claims 1 to 3, characterized in that the product comprises a front part (5) and a rear part (6), in which the front and rear parts are connected to each other along two opposite longitudinal side edges (4) to limit the opening (15) for the waist and a pair of holes (16) for the legs, while the product (1) further comprises a crotch portion (7) located between the front part (5) and the rear part (6) in the longitudinal direction (y) the product, and the product further comprises a rear part (18) of the waist, which is located on the edge of the rear part and (6) which is distal relative to the crotch portion (7) in the longitudinal direction (y) of the product, the rear part (6) containing the first elastic roll material (10), and the rear part (18) of the waist contains the second roll material (21 ), and the rear part (18) of the waist is welded to the rear part (6) using an ultrasonic weld (18a).

6. An absorbent product (1) according to claim 1, characterized in that the first elastic roll material (10) is a multilayer material (9).

7. An absorbent article (1) according to claim 6, characterized in that the multilayer material (9) is formed from the first and second layers of fibrous material (11, 12) and a layer (13) of an elastic film located between the first and second fibrous layers.

8. The absorbent product (1) according to claim 2, characterized in that the first elastic roll material is a single component of the front (5) and rear (6) parts of at least 20% of the total surface area of the absorbent product.

9. An absorbent article (1) according to claim 2, characterized in that the first elastic roll material is a single component of the front (5) and rear (6) parts for 25% of the total surface area of the absorbent article.

10. The absorbent product (1) according to claim 2, characterized in that the first elastic roll material is a single component of the front (5) and rear (6) parts for 30% of the total surface area of the absorbent product.

11. The absorbent product (1) according to claim 2, characterized in that the first elastic roll material is a single component of the front (5) and rear (6) parts for 40% of the total surface area of the absorbent product.

12. The absorbent product (1) according to claim 1, characterized in that the first elastic roll material (10) is breathable.

13. The absorbent product (1) according to item 12, characterized in that the first elastic roll material (10) has a water vapor transmission rate of at least 1500 g / cm ² 24 hours

14. An absorbent product (1) according to claim 12, characterized in that the first elastic web material (10) has a water vapor transmission rate of at least 3000 g / m ^{2 for} 24 hours.

15. An absorbent article (1) according to claim 1, characterized in that the second roll material (21) has an elasticity that is lower than the elasticity of the first elastic roll material (10).

16. An absorbent product (1) according to claim 1, characterized in that the second roll material (21) is a nonwoven material.

17. An absorbent product (1) according to claim 1, characterized in that the ultrasonic weld (8, 17a, 18a) between the first elastic roll material (10) and the second roll material (21) is reinforced so as to have welding strength in the direction transverse to the weld, which is at least 7 N / 25.4 mm

18. An absorbent product (1) according to claim 1, characterized in that the ultrasonic weld (8, 17a, 18a) between the first elastic roll material (10) and the second roll material (21) is reinforced so as to have welding strength in the direction transverse to the weld, which is at least 9 N / 25.4 mm

19. An absorbent product (1) according to claim 1, characterized in that the reinforcement is provided by an additional layer of web material (14), which is attached to the weld (8, 17a, 18a).

20. An absorbent product (1) according to claim 19, characterized in that the additional layer of web material (14) extends along at least 50% of the length of the weld (8, 17a, 18a) to which it is attached.

21. An absorbent product (1) according to claim 19, characterized in that the additional layer of web material (14) extends along at least 75% of the length of the weld (8, 17a, 18a) to which it is attached.

22. An absorbent product (1) according to claim 19, characterized in that the additional layer of web material (14) extends at least along 100% of the length of the weld (8, 17a, 18a) to which it is attached.

23. An absorbent product (1) according to claim 1, characterized in that the reinforcement is provided by an adhesive that is applied along 50-100% of the length of the weld (8, 17a, 18a).

24. The absorbent product (1) according to claim 1, characterized in that the reinforcement is provided by glue, which is applied along 70-90% of the length of the weld (8, 17a, 18a).

25. An absorbent article (1) according to claim 1, characterized in that the article (1) further comprises an absorbent assembly (3), the absorbent assembly comprising a liquid impervious protective layer (19), a liquid permeable top layer (20), and an absorbent core (2) enclosed between them.