Abstract

FIELD: manufacture of coatings. SUBSTANCE: invention relates to objects with simulated finishing characterized by artificial reproduction of texture not intrinsic of surface to be treated. Method includes successively applying transparent pigmented lacquer materials possessing various color gamma pigments onto surface. Utilized are lacquer materials having the same makeup with no regard to material to be treated. Evaporation of liquid fractions and hardening of film-formation substance occurs after applying each layer of lacquer material at room temperature. Coating thus manufactured manifests high adhesion to substrate, mechanical strength, and wear resistance. Precise reproduction of rock structure pattern on any substrate is determined by independence of coating makeup, application and hardening conditions of chosen substrate material, which makes method versatile. Coating may be applied onto any substrate (wood, metal, glass, carbon plastic and so on) under the same conditions. EFFECT: improved performance characteristics and versatility of coating.

Description

Изобретение относится к способам получения покрытий и может быть использовано в производстве изделий с имитационной отделкой, характеризуемой искусственным воспроизведением текстуры, не свойственной отделываемой поверхности. The invention relates to methods for producing coatings and can be used in the manufacture of products with simulated finish, characterized by the artificial reproduction of a texture that is not characteristic of the surface being trimmed.

Известен способ покрытия погружением подложки в ванну с водой, на поверхности которой находится пленка красящего пигмента. Для получения рисунка, имитирующего горную породу, в ванну добавляют очищенный скипидар [1]
Известен способ получения покрытия путем нанесения красящего состава распылением [2] При этом способе распыление отделочных составов производят распылителями, пульверизаторами за счет высокого давления на струю распыляемого раствора красителя или распылением краски струей сжатого воздуха.A known method of coating by immersion of the substrate in a bath of water, on the surface of which is a film of coloring pigment. To obtain a pattern imitating a rock, add purified turpentine to the bath [1]
A known method of producing a coating by applying a coloring composition by spraying [2] With this method, the spraying of finishing compositions is carried out by spray guns, spray guns due to high pressure on the jet of the sprayed dye solution or by spraying paint with a stream of compressed air.

Известен способ получения покрытия, согласно которому нанесенные на поверхность полимерные связующие, содержащие красящие пигменты различной световой гаммы, обрабатывают струей сжатого воздуха при давлении 0,1-5 ати до отверждения. При этом составы полимерного связующего, содержащие красящие пигменты различной цветовой гаммы, наносят последовательно, не дав высохнуть предыдущему слою [3]
При данном способе покрытия состав покрытия не постоянен и выбирается в зависимости от подложки, например, для ДСП-эпоксидная основа плюс эпоксидная декоративная добавка; для стеклопрофилита оба слоя пентафталевые эмали различных цветов; для гипса оба слоя масляные краски различных цветов.There is a known method of producing a coating, according to which polymer binders, containing coloring pigments of various light gamut applied to the surface, are treated with a stream of compressed air at a pressure of 0.1-5 atm before curing. In this case, the compositions of the polymer binder containing coloring pigments of various colors are applied sequentially, not allowing the previous layer to dry [3]
With this coating method, the composition of the coating is not constant and is selected depending on the substrate, for example, for chipboard-epoxy base plus an epoxy decorative additive; for fiberglass, both layers are pentaphthalic enamels of various colors; for gypsum, both layers are oil paints of various colors.

В этом случае режимы образования покрытия (давление воздуха, время, температура) зависят как от выбранной подложки, так и от состава покрытия. In this case, the modes of coating formation (air pressure, time, temperature) depend both on the selected substrate and on the composition of the coating.

Качество покрытия при отделке этим способом зависит от режима последующей обработки поверхности, времени обработки струей сжатого воздуха. Для более точного воспроизведения желаемой текстуры требуется тщательная обработка поверхности подложки. Кроме того, покрытие, полученное таким способом, не имитирует глубину, прозрачность структуры. The quality of the coating when finishing in this way depends on the mode of subsequent surface treatment, the processing time by a stream of compressed air. For more accurate reproduction of the desired texture requires careful processing of the surface of the substrate. In addition, the coating obtained in this way does not simulate the depth, transparency of the structure.

Известен способ получения покрытия путем последовательного нанесения прозрачных лакокрасочных материалов [4] Для нанесения подложки сначала наносится композиция на основе термореактивного пленкообразующего, содержащего светоотражающий чешуйчатый пигмент, который всплывает при определенных условиях отверждения и образует специальный слой, на который наносится второй слой пленкобразующего с малой концентрацией подцвечивающего красителя. Однако этот метод имеет ряд ограничений:
указанный способ позволяет наносить покрытия только на электропроводные подложки;
способ требует четкого соблюдения температурных интервалов при образовании первого слоя покрытия; т.к. пленкообразующее содержит скрытый катализатор, температура деблокирования которого может быть близкой к температуре плавления пленкообразующего.A known method of coating by sequentially applying transparent coatings [4] To apply the substrate, a composition is first applied based on thermosetting film-forming, containing reflective scaly pigment, which pops up under certain curing conditions and forms a special layer on which a second film-forming layer with a low concentration of highlighting is applied dye. However, this method has several limitations:
said method allows coating only electrically conductive substrates;
the method requires strict observance of temperature ranges during the formation of the first coating layer; because the film-forming contains a hidden catalyst, the release temperature of which may be close to the melting temperature of the film-forming.

Нарушение температурного интервала может не обеспечить всплывание частиц пигмента и их ориентацию относительно поверхности, что в последующем может повлиять на светоотражающие свойства первого слоя; данный способ требует сложного специального оборудования, энергозатрат. Violation of the temperature range may not ensure the emergence of the pigment particles and their orientation relative to the surface, which subsequently may affect the reflective properties of the first layer; This method requires sophisticated special equipment, energy consumption.

Задачей, на решение которой направлено заявляемое изобретение, является получение покрытия высокого качества практически на любой подложке, достижение точности воспроизводимого рисунка, имитирующего горную породу. The problem to which the invention is directed, is to obtain high-quality coatings on virtually any substrate, to achieve the accuracy of reproducible patterns that simulate rock.

Указанная задача решается за счет того, что в известном способе получения покрытия путем последовательного нанесения на обрабатываемую поверхность прозрачных пигментированных лакокрасочных материалов, содержащих красящие пигменты различной световой гаммы, и отверждения после нанесения каждого слоя лакокрасочных материалов используют прозрачные пигментированные лакокрасочные материалы одного и того же состава независимо от материала обрабатываемой поверхности, а выпаривание жидких фракций и отверждение пленкообразующего происходит при комнатной температуре. This problem is solved due to the fact that in the known method for coating by successively applying transparent pigmented paints and varnishes containing coloring pigments of different light colors to the surface to be treated and curing after applying each layer of paints and varnishes, transparent pigmented paints and varnishes of the same composition are used independently from the material of the treated surface, and the evaporation of liquid fractions and the curing of the film-forming occur Audit at room temperature.

Покрытие, полученное таким способом, обладает высокой адгезией к подложке, механической прочностью, износостойкостью. Покрытие имитирует прозрачность и глубину структуры камня (гранита) с чередованием плотных цветовых вкраплений. Текстура, воспроизведенная таким способом, скрывает дефекты подложки, не требуется тщательного выполнения подготовительных операций к покраске. The coating obtained in this way has high adhesion to the substrate, mechanical strength, wear resistance. The coating imitates the transparency and depth of the stone structure (granite) with an alternation of dense color blotches. The texture, reproduced in this way, hides the defects of the substrate, it is not necessary to carefully carry out preparatory operations for painting.

Точное воспроизведение рисунка структуры горных пород на любой подложке определяется тем, что состав покрытия, режимы нанесения и отверждения не зависят от выбранного материала подложки, что делает этот способ универсальным. Данное покрытие может быть нанесено на любую подложку (дерево, металл, стекло- и углепластик и др.) Для получения декоративного слоя используются прозрачные различно пигментированные лакокрасочные материалы одного и того же состава, нанесенные в 5 6 слоев. Режимы нанесения и образования покрытия постоянны и не зависят от применяемой подложки. Покрытия, полученные указанным способом, ремонтнопригодны, возможно нанесение покрытия прямо на объекте его использования. The exact reproduction of the rock structure pattern on any substrate is determined by the fact that the coating composition, application and curing modes are independent of the selected substrate material, which makes this method universal. This coating can be applied to any substrate (wood, metal, glass and carbon fiber, etc.). To obtain a decorative layer, transparent differently pigmented paints and varnishes of the same composition are applied, applied in 5 to 6 layers. The application and coating conditions are constant and independent of the substrate used. Coatings obtained by this method are repairable; it is possible to apply coatings directly at the object of its use.

Сущность способа получения покрытия заключается в следующем: для создания надежного сцепления покрытия с окрашиваемой поверхностью на последнюю наносят грунтовку, тем самым образуют нижний (грунтовочный) слой лакокрасочного покрытия; далее создают специальный подслой, который образует основу для нанесения имитационного покрытия. В качестве основы возможно использование пигментированных лакокрасочных материалов, способных создать покрытия типа "шагрень" (например, эмали ЭП-1294). The essence of the method for producing the coating is as follows: to create a reliable adhesion of the coating to the surface to be painted, a primer is applied to the latter, thereby forming a lower (primer) layer of paint coating; then create a special sublayer, which forms the basis for applying the imitation coating. As a basis, it is possible to use pigmented paints and varnishes capable of creating “shagreen” coatings (for example, enamel EP-1294).

Возможно образование основы путем нанесения на загрунтованную поверхность слоя шпаклевки, разбавленной для нанесения пульверизатором. После высушивания этого слоя поверхность зашкуривают до тесненного состояния и перекрывают пигментированным лакокрасочным материалом;
Нанесение имитационного декоративного слоя заключается в нанесение на подготовленную поверхность последовательно 5 6 раз прозрачных различно пигментированных лакокрасочных материалов одного и того же состава.It is possible to form a base by applying a putty layer diluted for spraying onto the primed surface. After drying this layer, the surface is sanded to a cramped state and covered with a pigmented paint material;
The application of the imitation decorative layer consists in applying to the prepared surface sequentially 5 to 6 times transparent differently pigmented paints and varnishes of the same composition.

Нанесение и образование прозрачных декоративных слоев, а также окончательное отверждение покрытия происходит при этом при комнатной температуре. The application and formation of transparent decorative layers, as well as the final curing of the coating, occurs at room temperature.

Пример 1. Получение покрытия "серый гранит" на дереве. Example 1. Obtaining a coating of "gray granite" on a tree.

На деревянную поверхность наносится из пульверизатора шпаклевка НЦ-0038, высушивается, вышкуривается мелкой шкуркой до создания тесненного состояния. На подготовленную таким способом поверхность наносится 1 2 слоя эмали НЦ-11 серого цвета исходной вязкости (примерно 18 с по В3 4)7 Покрытие высушивается при комнатной температуре в течение 1 часа, затем начинают последовательно наносить покрытие путем набрызгивания состава НЦ-11 черного, белого, серого и снова черного цвета с малым количеством пигмента (вязкость составов примерно 6-8 по В3-4). После нанесения каждого из декоративных слоев необходима выдержка для просушивания в течении 10 мин. Окончательная сушка покрытия происходит при комнатной температуре в течение 3 4 часов. Putty NTs-0038 is applied from a spray gun onto a wooden surface, dried, sanded out with a fine sandpaper to create a cramped condition. On the surface prepared in this way, 1 2 layers of NTs-11 enamel of gray color of the initial viscosity are applied (approximately 18 seconds according to B3 4) 7 The coating is dried at room temperature for 1 hour, then the coating is successively applied by spraying the NTs-11 composition with black, white , gray and again black with a small amount of pigment (the viscosity of the compounds is about 6-8 according to B3-4). After applying each of the decorative layers, exposure is required to dry for 10 minutes. Final drying of the coating occurs at room temperature for 3 to 4 hours.

Пример 2. Получение покрытия "серый гранит" на металле. Example 2. Obtaining a coating of "gray granite" on the metal.

На металлическую поверхность, обезжиренную и загрунтованную, наносится эмаль ЭП-1294 "М", создающая покрытие типа "шагрень". Покрытие высушивается в соответствии с ТУ на эту эмаль. В дальнейшем поступают так же, как указано в примере 1. EP-1294 "M" enamel is applied onto a metal surface, degreased and primed, creating a shagreen coat. The coating is dried in accordance with the technical specifications for this enamel. Subsequently, proceed as described in example 1.

Источники информации. Sources of information.

1. Орлов Ю. Д. Отделка изделий из древесины. М. Высшая школа, 1986, с. 19-28. 1. Orlov Yu. D. Finishing of wood products. M. Higher School, 1986, p. 19-28.

2. Там же, с. 99. 2. Ibid., P. 99.

3. Авторское свидетельство СССР N 770563, кл. B 05 D 1-34. 3. Copyright certificate of the USSR N 770563, cl. B 05 D 1-34.

4. Патент US N 4097639.1 4. Patent US N 4097639.1

Claims

A method of obtaining a decorative coating by successively applying layers of transparent paints and varnishes containing transparent film-forming and additives of pigments of various colors, drying and curing the film-forming after applying each layer of paint and varnish material, characterized in that at least 5 layers of paint and varnish materials are applied, for all layers use paints and varnishes of the same composition regardless of the material of the processed surface, but additives pigments of different colors in each layer, imitating natural stone, the coating layers, drying and curing of the binder is carried out at room temperature.