RU2053243C1

RU2053243C1 - Polymer composition for protective coating

Info

Publication number: RU2053243C1
Authority: RU
Inventors: Е.И. Цюкшо; Л.Г. Шодэ; Т.Н. Фомичева; О.И. Клочков
Original assignee: Малое многопрофильное предприятие "Инпредком"
Priority date: 1992-07-23
Filing date: 1992-07-23
Publication date: 1996-01-27

Abstract

FIELD: production of protective coating. SUBSTANCE: proposed composition contains binder (which includes epoxy diane resin, diluent, mineral filler and aerosil) and amine hardener. Epoxy diane resin on the base of polyoxypropylene glycol having molecular weight 500 is used as said diluent. Polymethyl phenyl siloxane is used as additive, its ratio to aerosil being 1: 1. Said composition contains (mass %): epoxy diane resin 38.5-53.8, epoxy resin on the base of polyoxypropylene glycol (its molecular weight being 500) 7.7-17.5, mineral filler 5.3-7.7, pigments 15.0-16.0, aerosil 0.15-0.8, polymethyl phenyl siloxane 0.15-0.8, amine hardener 15.0-23.0. Proposed composition has high resistance against detergents and high decorative properties. EFFECT: improves quality of desired product. 2 tbl

Description

Изобретение относится к низковязким эпоксидным композициям, не содержащих растворителей, которые могут найти применение для формирования защитных покрытий сантехнического оборудования, в том числе и при их ремонте. The invention relates to low-viscosity solvent-free epoxy compositions that can be used to form protective coatings for plumbing equipment, including during their repair.

Известна эпоксидная композиция для защитного покрытия, содержащая связующее, включающая эпоксидную диановую смолу, разбавитель, минеральный накопитель и аэросил, и аминный отвердитель, при этом в композиции качестве пластификатора используется эпоксидированный каучук, в качестве разбавителя фенилглицидиловый эфир и дополнительно аэросил. Known epoxy composition for a protective coating containing a binder comprising an epoxy diane resin, a diluent, a mineral accumulator and Aerosil, and an amine hardener, while the composition uses an epoxidized rubber as a plasticizer, phenyl glycidyl ether and additionally Aerosil as a diluent.

Покрытия на основе этой композиции обладают хорошими физико-механическими свойствами, однако при действии горячей воды покрытия отслаиваются. Отмечается также плохая стойкость покрытий к действию моющих средств. Кроме того, покрытия не отвечают требованиям декоративности. Coatings based on this composition have good physical and mechanical properties, however, when exposed to hot water, the coatings peel off. Poor resistance of coatings to the action of detergents is also noted. In addition, the coatings do not meet the requirements of decorativeness.

Технической задачей изобретения является получение защитной композиции стойкой к действию моющих средств, горячей воде, получение защитной композиции, обладающей хорошей декоративностью. An object of the invention is to obtain a protective composition resistant to the action of detergents, hot water, obtaining a protective composition having good decorative effect.

Это достигается тем, что связующее в качестве разбавителя содержит эпоксидную смолу на основе полиоксипропиленгликоля с ММ 500 и дополнительно введены добавка полиметилфенилсилоксан в отношении аэросил:полиметилсилоксан 1:1 и пигменты при следующем соотношении компонентов, мас. This is achieved by the fact that the binder as a diluent contains an epoxy resin based on polyoxypropylene glycol with MM 500 and an addition of polymethylphenylsiloxane in relation to aerosil: polymethylsiloxane 1: 1 and pigments in the following ratio of components, wt.

Эпоксидная диановая смола 38,5-53,8
Эпоксидная смола на
основе полиоксипропи- ленгликоля ММ 500 7,7-17,5
Минеральный наполни- тель тальк 5,3-7,7 Пигменты 15,0-16,0 Аэросил 0,15-0,8 Полиметилфенилсил- оксан 0,15-0,8 Аминный отвердитель 15,0-23,0
В композиции использованы следующие компоненты: низкомолекулярная диановая эпоксидная смола ЭД-20 (мол. масса 400, ГОСТ 10587-84); разбавитель: алифатическая эпоксидная смола лапроксид 503 (ТУ 6-05-221-740-86); пигменты: диоксид титана TiO₂ (ГОСТ 9808-75), оксид цинка ZnO (ГОСТ 202-76); наполнитель тальк МТ ГШМ (ГОСТ 19284-79); аэросил 175, 380 (ГОСТ 14922-77); добавки: полиметилфенилсилоксан ПФМС-4; отвердители: аддукт бутилметакрилата с диэтилентриамином ДТБ-2, (ТУ 6-05-241-444-79), полиэтиленполиамины ПЭПА (ТУ 6-05-241-202-78), цианэтилированные амины УП-0633М (ТУ 6-05-1863-78), трис-диметиламинометил- фенол УП-606/ (ТУ 6-09-4136-75).Epoxy Dianova Resin 38.5-53.8
Epoxy resin
based on polyoxypropylene glycol MM 500 7.7-17.5
Mineral filler talc 5.3-7.7 Pigments 15.0-16.0 Aerosil 0.15-0.8 Polymethylphenylsiloxane 0.15-0.8 Amine hardener 15.0-23.0
The following components were used in the composition: low molecular weight Diane epoxy resin ED-20 (mol. Mass 400, GOST 10587-84); diluent: aliphatic epoxy resin laproxide 503 (TU 6-05-221-740-86); pigments: titanium dioxide TiO ₂ (GOST 9808-75), zinc oxide ZnO (GOST 202-76); filler talc MT GSHM (GOST 19284-79); Aerosil 175, 380 (GOST 14922-77); additives: polymethylphenylsiloxane PFMS-4; hardeners: butyl methacrylate adduct with diethylene triamine DTB-2, (TU 6-05-241-444-79), polyethylene polyamines PEPA (TU 6-05-241-202-78), cyanethylated amines UP-0633M (TU 6-05-1863 -78), Tris-dimethylaminomethyl-phenol UP-606 / (TU 6-09-4136-75).

В табл.1 приведены примеры составов предлагаемой композиции и по прототипу. Table 1 shows examples of the compositions of the proposed composition and the prototype.

Композицию получают следующим образом. The composition is prepared as follows.

Сначала в закрытой емкости при перемешивании совмещают до однородности эпоксидную диановую смолу, лапроксид, пигменты и наполнители. Затем смесь диспергируют на краскотерочной машине до степени перетира по клину 15-20. По достижении требуемой степени перетира краску загружают в смеситель с Z-образной мешалкой, добавляют аэросил и добавку полиметилфенилсилоксан и перемешивают массу в течение 0,5-1 ч. First, in a sealed container, with mixing, the epoxy diane resin, laproxide, pigments and fillers are combined until uniform. Then the mixture is dispersed on a paint-and-mortar machine to the degree of milling along the wedge 15-20. Upon reaching the desired degree of grinding, the paint is loaded into a mixer with a Z-shaped mixer, aerosil and the addition of polymethylphenylsiloxane are added and the mass is mixed for 0.5-1 hours.

В табл. 2 приведены свойства полученной композиции в сравнении со свойствами композиции-прототипа. In the table. 2 shows the properties of the obtained composition in comparison with the properties of the composition of the prototype.

При содержании в композиции эпоксидной диановой смолы за пределами предлагаемого диапазона ухудшаются прочностные показатели покрытия, снижается адгезия покрытия. When the composition contains epoxy Dianova resin outside the proposed range, the strength characteristics of the coating deteriorate, and the adhesion of the coating decreases.

При содержании разбавителя менее минимального значения предлагаемого диапазона высокое значение вязкости покрытия, что вызывает трудность его нанесения, при значении больше максимального значения предлагаемого диапазона плохие прочностные свойства (покрытие отслаивается). When the diluent content is less than the minimum value of the proposed range, a high viscosity value of the coating, which causes difficulty in applying it, with a value greater than the maximum value of the proposed range, poor strength properties (the coating exfoliates).

При содержании отвердителей менее минимального значения предлагаемого диапазона покрытие не отверждается, при содержании отвердителя более максимального значения предлагаемого диапазона покрытие теряет декоративный вид. When the content of hardeners is less than the minimum value of the proposed range, the coating does not cure, when the content of hardeners is more than the maximum value of the proposed range, the coating loses its decorative appearance.

Введение добавки полиметилфенилсилоксана обеспечивает высокие декоративные свойства. The introduction of polymethylphenylsiloxane additives provides high decorative properties.

Соотношение аэросил: полиметилфенилсилоксан 1:1 выбрано из обеспечения высокого декоративного эффекта. The ratio of aerosil: polymethylphenylsiloxane 1: 1 is selected to ensure a high decorative effect.

Указанный диапазон пигментов определяется кроющей способностью покрытия. The specified range of pigments is determined by the opacity of the coating.

Пример нанесения композиции. Композицию готовят перед нанесением ее на защищаемую поверхность. Емкость с композицией помещают в горячую воду. Температура нагрева не должна превышать 45^оС. По окончании нагрева композицию необходимо тщательно перемешать в течение 3-5 мин. При нанесении первого слоя покрытия композиция содержит ускоритель. Композиция наносится кистью.An example of applying the composition. The composition is prepared before applying it to the surface to be protected. The container with the composition is placed in hot water. The heating temperature should not exceed 45 ^° C. At the end of heating, the composition must be thoroughly mixed for 3-5 minutes. When applying the first coating layer, the composition contains an accelerator. The composition is applied by brush.

При резком возрастании температуры при нанесении слоя, либо при увеличении вязкости, в композицию необходимо ввести растворитель (например, ацетон) и быстро и тщательно перемешать. With a sharp increase in temperature when applying the layer, or with an increase in viscosity, it is necessary to introduce a solvent (for example, acetone) into the composition and mix it quickly and thoroughly.

При приготовлении композиции для нанесения второго слоя допускается небольшое изменение насыщенности цвета в более темные тона. When preparing the composition for applying the second layer, a slight change in the color saturation into darker tones is allowed.

Композиция наносится слоем толщиной 0,2 мм первый слой, 0,4 мм второй слой. The composition is applied in a layer 0.2 mm thick first layer, 0.4 mm second layer.

Предлагаемая композиция образует покрытие с высокой водостойкостью, в том числе в горячей воде и в растворах моющих средств. После двенадцатичасового кипячения физико-механические свойства покрытия практически сохранились на том же уровне. В отличие от прототипа покрытие обладает высоким блеском и бездефектностью, отсутствием оспин и кратеров. The proposed composition forms a coating with high water resistance, including in hot water and in detergent solutions. After twelve-hour boiling, the physicomechanical properties of the coating practically remained at the same level. In contrast to the prototype, the coating has a high gloss and defect-free, the absence of pock and craters.

Claims

POLYMER COMPOSITION FOR PROTECTIVE COATING, containing a binder comprising an epoxy Dianova resin, a diluent, a mineral filler and Aerosil, and an amine hardener, characterized in that the binder contains a polyoxypropylene glycol based epoxy resin with a mol. m. 500, additionally introduced additive - polymethylphenylsiloxane in relation to aerosil: polymethylphenylsiloxane 1: 1 and pigments in the following ratio of components, wt.%:
Epoxy Dianova Resin - 38.5 - 53.8
Polyoxypropylene glycol-based epoxy with mol.m.500 - 7.7 - 17.5
Mineral filler - talc - 5.3 - 7.7
Pigments - 15.0 - 16.0
Aerosil - 0.15 - 0.8
Polymethylphenylsiloxane - 0.15 - 0.8
Amine hardener - 15.0 - 23.0