RU2028158C1 - Composition for wound surface covering

Info

Publication number: RU2028158C1
Authority: RU
Inventors: В.С. Якубович; Л.П. Раскина; А.Д. Вирник; В.К. Гостищев; В.Д. Потапов; К.П. Хомяков; В.М. Гудочкова; Н.М. Атясова; А.Л. Комиссарова; М.Б. Шенкер; И.Ф. Скокова; З.Ф. Василькова; П.И. Толстых
Original assignee: Научно-исследовательский институт медицинских полимеров
Priority date: 1985-04-11
Filing date: 1985-04-11
Publication date: 1995-02-09

Abstract

FIELD: medicine. SUBSTANCE: composition for preparing of polymeric coating has aqueous solution of sodium alginate and enzyme - terrilytin and calcium gluconate taken at the following ratio of components, wt.-%: sodium alginate 0.2-0.7; terrilytin 0.015-0.035; calcium gluconate 0.1-0.4, and water - the rest. EFFECT: increased stability of enzyme in polymeric covering in the process of lyophilic drying and sterilization. 1 tbl

Description

Изобретение относится к медицине, в частности к составу, используемому при получении покрытий для лечения гнойных ран и ожогов. The invention relates to medicine, in particular to a composition used in the preparation of coatings for the treatment of purulent wounds and burns.

Известен состав, содержащий, мас. % : альгинат натрия 0,5; фермент - террилитин 0,24; воду - остальное. Покрытие, полученное на основе данного состава путем лиофильной сушки, проявляет протеолитическую активность и может применяться для лечения ран и ожогов. Однако при таком составе в процессе лиофильной сушки и последующей радиационной стерилизации происходит снижение протеолитической активности террилитина в готовом покрытии. Known composition containing, by weight. %: sodium alginate 0.5; the enzyme is terrilithin 0.24; water - the rest. The coating obtained on the basis of this composition by freeze drying exhibits proteolytic activity and can be used to treat wounds and burns. However, with this composition, in the process of freeze drying and subsequent radiation sterilization, the proteolytic activity of terrilithin in the finished coating decreases.

Цель изобретения - повышение стабильности состава в процессе лиофильной сушки и стерилизации полимерного покрытия. The purpose of the invention is to increase the stability of the composition during freeze drying and sterilization of the polymer coating.

Поставленная цель достигается за счет того, что состав для получения полимерного покрытия раневой поверхности, содержащий водный раствор альгината натрия и фермента - террилитина, содержит дополнительно глюконат кальция при следующем соотношении компонентов, мас.%: Альгинат Na 0,2-0,7 Террилитин 0,015-0,035
Глюконат кальция 0,10-0,40
П р и м е р 1. В 335 мл воды растворяют 5 г альгината натрия (0,5 мас.% ), приливают 500 мл раствора, содержащего 0,25 г террилитина (0,025 мас.%) и 165 мл раствора, содержащего 1,0 г глюконата кальция (0,1 мас.%). Состав замораживают и лиофильно высушивают, а затем стерилизуют радиационным способом дозой 2,5 рад.This goal is achieved due to the fact that the composition for obtaining a polymer coating of the wound surface, containing an aqueous solution of sodium alginate and the enzyme terrilithin, additionally contains calcium gluconate in the following ratio of components, wt.%: Na alginate 0.2-0.7 Terrylitin 0.015 -0.035
Calcium Gluconate 0.10-0.40
PRI me R 1. In 335 ml of water, 5 g of sodium alginate is dissolved (0.5 wt.%), 500 ml of a solution containing 0.25 g of terrilithin (0.025 wt.%) And 165 ml of a solution containing 1 , 0 g of calcium gluconate (0.1 wt.%). The composition is frozen and freeze-dried, and then sterilized by a radiation method with a dose of 2.5 rad.

Протеолитическую активность террилитина оценивали по видоизмененному методу Кунитца по высокомолекулярному субстрату-казеину. The proteolytic activity of terrilithin was evaluated by the modified Kunitz method using a high molecular weight casein substrate.

Примеры 2-4 отличаются от примера 1 составом (количеством террилитина и глюконата кальция). Examples 2-4 differ from example 1 in composition (amount of terrilithin and calcium gluconate).

Влияние состава на стабильность фермента (сохранение активности фермента после лиофильной сушки и стерилизации) и свойства покрытий представлены в таблице. The effect of the composition on the stability of the enzyme (maintaining the activity of the enzyme after freeze drying and sterilization) and the properties of the coatings are presented in the table.

Введение в состав для получения полимерного покрытия раневой поверхности, который содержит альгинат натрия, террилитин и воду, глюконата кальция в предлагаемых пределах приводит к повышению стабильности состава (сохранению более высокой активности фермента) после радиационной стерилизации покрытия примерно в два раза. При этом покрытие характеризуется высоким водопоглощением, что является одной из важнейших характеристик покрытий на раны и ожоги. Сроки очищения ран под такими покрытиями примерно в два раза меньше, чем в прототипе при таком же содержании фермента. Изобретение позволит сократить расход фермента при каждой перевязке примерно в 7-16 раз. The introduction of the composition to obtain a polymer coating of the wound surface, which contains sodium alginate, terrilithin and water, calcium gluconate in the proposed range leads to increased stability of the composition (maintaining higher enzyme activity) after radiation sterilization of the coating about two times. Moreover, the coating is characterized by high water absorption, which is one of the most important characteristics of coatings for wounds and burns. The terms for cleansing wounds under such coatings are approximately two times less than in the prototype with the same enzyme content. The invention will reduce the consumption of the enzyme at each dressing by about 7-16 times.

Claims

COMPOSITION FOR COVERING A WOUNDED SURFACE, containing an aqueous solution of sodium alginate and terrilithin enzyme, characterized in that, in order to increase stability, it additionally contains calcium gluconate in the following ratio of components, wt.%:
Sodium Alginate - 0.2 - 0.7
Terrilitin - 0.015 - 0.036
Calcium Gluconate - 0.10 - 0.40
Water - Else