NL2000132C2 - Tarpaulin repair material for truck tarpaulins, has adhesive layer comprising resin and acrylic polymer - Google Patents
Tarpaulin repair material for truck tarpaulins, has adhesive layer comprising resin and acrylic polymer Download PDFInfo
- Publication number
- NL2000132C2 NL2000132C2 NL2000132A NL2000132A NL2000132C2 NL 2000132 C2 NL2000132 C2 NL 2000132C2 NL 2000132 A NL2000132 A NL 2000132A NL 2000132 A NL2000132 A NL 2000132A NL 2000132 C2 NL2000132 C2 NL 2000132C2
- Authority
- NL
- Netherlands
- Prior art keywords
- resin
- repair
- layer
- glue
- adhesive
- Prior art date
Abstract
Description
NL8542-He/vwNL8542-He / vw
Reparatiemiddel voor dekzeilenRepair material for tarpaulins
De onderhavige uitvinding heeft betrekking op een reparatiemiddel voor flexibele materialen, zoals bijvoorbeeld dekzeilen.The present invention relates to a repair means for flexible materials, such as, for example, tarpaulins.
Dekzeilen voor het afdekken van de toegangsopeningen 5 van containers en laadbakken van vrachtwagens moeten in geval van beschadiging op adequate wijze gerepareerd kunnen worden. Deze reparatie moet zodanig van kwaliteit zijn dat deze in staat is de hoge krachten waaraan het dekzeil tijdens vervoer over de weg blootgesteld wordt te weerstaan.Tarpaulins for covering the access openings 5 of containers and loading troughs of trucks must be able to be adequately repaired in the event of damage. This repair must be of such a quality that it is able to withstand the high forces to which the tarpaulin is exposed during road transport.
10 Er is een zelfklevend reparatiemiddel op de markt voor het repareren van dekzeilen voor gebruik in laadbakken van vrachtwagens. Dit middel bestaat uit een reparatiemateriaal met een lijmlaag en een folie om de lijmlaag af te schermen. Dit reparatiemateriaal kan op eenvoudige wijze, ook door een niet 15 vakkundige, op de plaats van beschadiging aangebracht worden door de beschermende folie te verwijderen en het reparatiemateriaal aan te brengen en vast te drukken met bijvoorbeeld een rolletje. De lijm die in dit reparatiemiddel toegepast is heeft een hoge initiële kleefkracht ("tack"), maar 20 nadeligerwijs een zeer geringe afschuifweerstand. De kleefkracht van deze lijm wordt o.a. verkregen door zijn zeer hoge lijmopdracht (80 g/m2 of meer). Na langdurig contact met een weekgemaakt PVC dekzeil wordt de lijm van dit product echter uitermate zacht en verliest een groot deel van zijn 25 hechtingsvermogen. Hierbij verliest het product zowel aan kleefkracht als aan afschuifweerstand. Het product is daarom uitsluitend bruikbaar voor reparaties op korte termijn.10 There is a self-adhesive repair tool on the market for repairing tarpaulins for use in truck bodies. This agent consists of a repair material with a layer of glue and a foil to protect the layer of glue. This repair material can be applied in a simple manner, also by a non-skilled person, to the place of damage by removing the protective film and applying the repair material and pressing it with, for example, a roll. The glue used in this repair means has a high initial tack ("tack"), but disadvantageously a very low shear resistance. The adhesive power of this glue is obtained by, among other things, its very high glue order (80 g / m2 or more). However, after prolonged contact with a plasticized PVC tarpaulin, the glue of this product becomes extremely soft and loses much of its adhesiveness. The product loses both adhesive strength and shear resistance. The product can therefore only be used for short-term repairs.
De onderhavige uitvinding verschaft een reparatiemiddel dat deze nadelen niet bezit. In het bijzonder bezit de lijm die 30 in dit reparatiemiddel gebruikt wordt een hoge initiële kleefkracht, maar tevens een hogere afschuifkracht dan de lijm die in het bestaande product gebruikt wordt. De uiteindelijke kleefkracht na veroudering blijft bij dit reparatiemiddel tevens op een hoger niveau dan met bestaande producten. Dit alles is 35 mogelijk met een lijmopdracht die aanzienlijke lager is dan met de bestaande producten en die normale productiesnelheden 2 toelaat. Uitstekende resultaten zijn verkregen met lijmopdrachten van tenminste 3 0 g/m2, zoals 3 0 tot 80 g/m2.The present invention provides a repair means that does not have these disadvantages. In particular, the glue used in this repair means has a high initial adhesive force, but also a higher shear force than the glue used in the existing product. The final adhesive strength after aging also remains at a higher level with this repair product than with existing products. All this is possible with an adhesive assignment that is considerably lower than with the existing products and that allows normal production speeds 2. Excellent results have been obtained with adhesive orders of at least 30 g / m2, such as 30 to 80 g / m2.
Derhalve verschaft de onderhavige uitvinding een reparatiemiddel voor dekzeilen, welk middel tenminste bestaat 5 uit een toplaag, een middenlaag en een onderlaag, waarbij de toplaag bestaat uit een materiaal geschikt voor het uitvoeren van reparaties, de middenlaag een lijm omvat om het materiaal van de toplaag te hechten aan een te repareren materiaal en een onderlaag om de lijm van de middenlaag te beschermen, met het 10 kenmerk dat de lijm van de middenlaag tenminste bestaat uit een acrylaat polymeer en een hars in een verhouding van 10-30 gewichtsdelen hars op 100 gewichtsdelen acrylaat polymeer.The present invention therefore provides a repair means for tarpaulins, which means consists at least of a top layer, a middle layer and a bottom layer, the top layer consisting of a material suitable for carrying out repairs, the middle layer comprising an adhesive around the material of the top layer to adhere to a material to be repaired and a bottom layer to protect the glue of the middle layer, characterized in that the glue of the middle layer consists at least of an acrylate polymer and a resin in a ratio of 10-30 parts by weight resin to 100 parts by weight acrylic polymer.
Naast een betere afschuifkracht heeft de lijm die in het reparatiemiddel van de onderhavige uitvinding toegepast 15 wordt de voordelige eigenschap dat de lijm zijn optimale kleefkracht bereikt na gedeeltelijke migratie van de (gewoonlijk monomere) weekmaker (binnen 24 uur). De uiteindelijke kleefkracht blijft tevens op een hoger niveau dan bij de bestaande producten. Dit in tegenstelling tot de lijmen die 20 gewoonlijk voor deze toepassing gebruikt worden, deze bereiken hun maximale kleefkracht bijna direct na aanbrengen en verliezen dan kleefkracht door migratie van de weekmaker.In addition to a better shear force, the glue used in the repair means of the present invention has the advantageous property that the glue reaches its optimum adhesive force after partial migration of the (usually monomeric) plasticizer (within 24 hours). The final adhesive strength also remains at a higher level than with the existing products. This is in contrast to the adhesives commonly used for this application, they reach their maximum adhesive power almost immediately after application and then lose adhesive power due to migration of the plasticizer.
Het acrylaat polymeer dat in de lijm van het reparatiemiddel volgens onderhavige uitvinding gebruikt wordt 25 verschaft een lijm met een hoge kleefkracht en een hoge afschuifkracht. Het acrylaat polymeer bezit bij voorkeur een glastransitie temperatuur tussen -50°C en -15°C, met meer voorkeur tussen -40°C en -20°C. Het acrylaat polymeer is een homo- of copolymeer dat bij voorkeur 2-ethylhexyl acrylaat 30 (2EHA) eenheden bevat. Met meer voorkeur is het acrylaat polymeer een copolymeer gebaseerd op in hoofdzaak 2-ethylhexyl acrylaat (2EHA) dat verder tenminste butylacrylaat (BA) en/of acrylzuur (AA) eenheden omvat. Voorbeelden van geschikte acrylaat copolymeren zijn te vinden in o.a. de DuroTak® reeks 35 van de firma National Starch and Adhesives en de Solucryl® reeks van de firma Cytec.The acrylate polymer used in the adhesive of the repair agent according to the present invention provides an adhesive with a high adhesive force and a high shear. The acrylate polymer preferably has a glass transition temperature between -50 ° C and -15 ° C, more preferably between -40 ° C and -20 ° C. The acrylate polymer is a homo- or copolymer that preferably contains 2-ethylhexyl acrylate 30 (2EHA) units. More preferably, the acrylate polymer is a copolymer based on substantially 2-ethylhexyl acrylate (2EHA) which further comprises at least butyl acrylate (BA) and / or acrylic acid (AA) units. Examples of suitable acrylic copolymers can be found in, inter alia, the DuroTak® series 35 from the National Starch and Adhesives company and the Solucryl® series from the company Cytec.
De lijm van de middenlaag bevat verder een kleverig makende hars met een smeltpunt van 60-140°C, bij voorkeur van 70-120°C, bij meer voorkeur van 80-100°C. De hars is bij 3 voorkeur een hars van natuurlijke oorsprong op basis van gom harsen of terpentijn, bijvoorbeeld afkomstig van bomen, bij voorkeur van de familie van de naaldbomen. Voorbeelden van dergelijke producten zijn de Tall oil derivaten, de rosin 5 derivaten of de terpeenfenol of terpeen harsen. Deze natuurlijke harsen zijn meestal gemodificeerd, bijvoorbeeld door gedeeltelijke of volledige hydrogenatie; verestering (bijvoorbeeld met glycerol en/of pentaerythritol). Voorbeelden van geschikte harsen zijn o.a. de Dertophene of Dercolyte reeks 10 van DRT of de SP reeks van Schenectady. Synthetische harsen met dezelfde eigenschappen als de natuurlijke harsen zijn ook geschikt voor gebruik in de lijm.The glue of the middle layer further comprises a tackifying resin with a melting point of 60-140 ° C, preferably of 70-120 ° C, more preferably of 80-100 ° C. The resin is preferably a resin of natural origin based on gum resins or turpentine, for example from trees, preferably from the conifer family. Examples of such products are the Tall oil derivatives, the rosin derivatives or the terpene phenol or terpene resins. These natural resins are usually modified, for example by partial or complete hydrogenation; esterification (e.g. with glycerol and / or pentaerythritol). Examples of suitable resins include the Dertophene or Dercolyte series 10 from DRT or the SP series from Schenectady. Synthetic resins with the same properties as the natural resins are also suitable for use in the glue.
De lijm bevat hars en acrylaat polymeer in een verhouding van 10-30 gewichtsdelen hars, bij voorkeur 15-25 15 gewichtsdelen hars, op 100 gewichtsdelen acrylaat polymeer.The glue contains resin and acrylate polymer in a ratio of 10-30 parts by weight of resin, preferably 15-25 parts by weight of resin, to 100 parts by weight of acrylate polymer.
Er bestaat tevens de mogelijkheid om aan een dergelijke formulering andere componenten toe te voegen zoals o.a. pigmenten, vulstoffen, antioxidantia en/of UV stabilisatoren.It is also possible to add other components to such a formulation, such as pigments, fillers, antioxidants and / or UV stabilizers.
Het daadwerkelijke reparatiemateriaal van de toplaag 20 kan van elk materiaal gemaakt zijn dat flexibel is en geschikt voor reparatie van flexibel materiaal zoals bijvoorbeeld dekzeilen. Het materiaal is bij voorkeur weekgemaakt PVC.The actual repair material of the top layer 20 can be made of any material that is flexible and suitable for repairing flexible material such as, for example, tarpaulins. The material is preferably plasticized PVC.
Een als reparatiemateriaal uitermate geschikt materiaal heeft de volgende specificaties: 25 Weefsel 100% PES 1100 DtexA material that is extremely suitable as a repair material has the following specifications: 25 Fabric 100% PES 1100 Dtex
Gewicht 680 g/m2 DIN 53 352, BS 3424 methode 5A.Weight 680 g / m2 DIN 53 352, BS 3424 method 5A.
Vernis l/l alle kleuren.Varnish l / l all colors.
Treksterkte ketting 3000 N/5cm en inslag 2800 N/5cmTensile strength chain 3000 N / 5 cm and impact 2800 N / 5 cm
30 DIN 53 354, BS 3424 methode 6ADIN 53 354, BS 3424 method 6A
Scheurweerstand ketting 300 N en inslag 300 NTear resistance chain 300 N and impact 300 N
DIN 53 356, BS 3424 methode 7A Kleefkracht 90 N/5cm DIN 53 357, BS 3424 methode 98.DIN 53 356, BS 3424 method 7A Adhesive power 90 N / 5 cm DIN 53 357, BS 3424 method 98.
35 Temperatuurbestendigheid -30°C/+70°C35 Temperature resistance -30 ° C / + 70 ° C
DIN 53 372, BS 3424 methode 10. Lichtechtheid (behalve wit) 7-8 DIN 53 388, BS 3424 methode 15 4DIN 53 372, BS 3424 method 10. Lightfastness (excluding white) 7-8 DIN 53 388, BS 3424 method 15 4
De onderlaag dient ter bescherming van de lijm en kan elk flexibel substraat zijn dat voor dit doel geschikt is, variërend van plastic tot papier. Gewoonlijk is deze laag een gesiliconiseerde film of gesiliconiseerd papier.The bottom layer serves to protect the glue and can be any flexible substrate suitable for this purpose, ranging from plastic to paper. Usually this layer is a siliconized film or siliconized paper.
5 Het is ook mogelijk een drager aan te brengen in de lijmlaag. De lijmlaag zal dan effectief uit drie lagen bestaan, een bovenste lijmlaag die in contact staat met het reparatiemateriaal, de dragerlaag en een onderste lijmlaag die in contact staat met de beschermende laag. De drager kan 10 polyester, PVC, nonwoven, weefsel, en dergelijke zijn.It is also possible to provide a carrier in the adhesive layer. The adhesive layer will then effectively consist of three layers, an upper adhesive layer that is in contact with the repair material, the carrier layer and a lower adhesive layer that is in contact with the protective layer. The carrier can be polyester, PVC, nonwoven, fabric, and the like.
Direct voor gebruik kan de onderlaag verwijderd worden, waarna het reparatiemateriaal eenvoudig middels het uitoefenen van druk op het te repareren materiaal aangebracht kan worden. Het te repareren materiaal dient bij voorkeur schoon en vet- en 15 stofvrij te zijn. Bij het reparatiemiddel volgens de uitvinding kunnen kant-en-klare schoonmaaktissues geleverd worden om het te repareren materiaal schoon te maken.The bottom layer can be removed immediately before use, after which the repair material can be simply applied to the material to be repaired by applying pressure. The material to be repaired should preferably be clean and free of grease and dust. With the repair means according to the invention, ready-made cleaning tissues can be supplied to clean the material to be repaired.
Het reparatiemiddel van de onderhavige uitvinding is uitermate geschikt voor reparatie van dekzeilen van 20 vrachtwagens. Het is goed bestand tegen alle (weers)omstandigheden, in het bijzonder tegen blootstelling aan zonlicht en aan hoge wrijvingskrachten die gegenereerd worden door snelheid en/of harde wind tijdens transport. Het reparatiemateriaal kan indien gewenst weer verwijderd worden 25 waarbij er geen resten van de lijm of reparatiemateriaal achterblijven op het te repareren materiaal die definitieve reparatie in een later stadium zouden kunnen bemoeilijken. De reparatie met het reparatiemateriaal van de uitvinding kan tevens permanent gemaakt worden door verhitting van het 30 aangebrachte reparatiemateriaal met een industriële föhn.The repair means of the present invention is extremely suitable for repairing tarpaulins of 20 trucks. It is highly resistant to all (weather) conditions, in particular to exposure to sunlight and to high frictional forces that are generated by speed and / or strong wind during transport. The repair material can be removed again if desired, leaving no residues of the glue or repair material on the material to be repaired which could complicate final repair at a later stage. The repair with the repair material of the invention can also be made permanent by heating the applied repair material with an industrial hair dryer.
Het reparatiemateriaal volgens de uitvinding is niet alleen geschikt voor reparatie van dekzeilen voor vrachtwagens, maar kan ook voor reparatie van andere flexibele materialen toegepast worden, zoals tentzeil, springkussens, luchtbedden, 35 fietsbanden, of voor PVC dakbedekking.The repair material according to the invention is not only suitable for repairing tarpaulins for lorries, but can also be used for repair of other flexible materials, such as tent canvas, inflatables, air beds, bicycle tires, or for PVC roof covering.
Het reparatiemiddel volgens de uitvinding kan middels bekende technologie vervaardigd worden. Aan een acrylaat polymeer oplossing van gewoonlijk 40-50 gewichts% wordt de gewenste hoeveelheid hars (10-30, bij voorkeur 15-25, 5 gewichtsdelen hars op 100 gewichtsdelen acrylaat polymeer) toegevoegd, waarna gemengd wordt tot de hars opgelost is en volledig gemengd met het acrylaat polymeer. De hars is gewoonlijk in de vorm van poeder, snippers of korrels. Toevoegen 5 en mengen geschiedt gewoonlijk bij kamertemperatuur of verhoogde temperatuur zolang het kookpunt van de oplosmiddelen niet overschreden wordt en er voldoende maatregelen genomen worden om explosiegevaar uit te sluiten. Het acrylaat polymeer is opgelost in een geschikt oplosmiddel, gewoonlijk ethylacetaat, tolueen 10 en/of hexaan, maar niet hiertoe beperkt. Het hars/polymeer mengsel wordt aangebracht op de onderlaag, waarna gedroogd wordt bij een temperatuur van 85-120°C. Tijdens drogen vindt tevens curing plaats. Het is tevens mogelijk een soortgelijke lijm te maken op basis van acrylaat polymeren met een vaste stof gehalte 15 van 100%, met toevoeging van identieke harsen als in de oplosmiddel gebaseerde werkwijze, of op basis van water gedragen systemen met toevoeging van water gedragen harsen van dezelfde chemische structuur als de bovenvermelde harsen.The repair means according to the invention can be manufactured by known technology. The desired amount of resin (10-30, preferably 15-25, 5 parts by weight of resin per 100 parts by weight of acrylate polymer) is added to an acrylate polymer solution of usually 40-50% by weight, after which mixing is carried out until the resin is dissolved and completely mixed with the acrylic polymer. The resin is usually in the form of powder, chips or granules. Addition and mixing is usually carried out at room temperature or elevated temperature as long as the boiling point of the solvents is not exceeded and sufficient measures are taken to rule out the risk of explosion. The acrylate polymer is dissolved in, but not limited to, a suitable solvent, usually ethyl acetate, toluene and / or hexane. The resin / polymer mixture is applied to the bottom layer, after which it is dried at a temperature of 85-120 ° C. Curing also takes place during drying. It is also possible to make a similar glue based on acrylate polymers with a solids content of 100%, with the addition of identical resins as the solvent-based process, or water-based systems with the addition of water-borne resins of The same chemical structure as the above-mentioned resins.
Daarna wordt het daadwerkelijke reparatiemateriaal 20 aangebracht op de zelfklevende lijmlaag door laminatie met bestaande machines onder drukken vanaf 1 bar en temperaturen variërend van 5°C tot 50'C.Thereafter, the actual repair material 20 is applied to the self-adhesive glue layer by lamination with existing machines under pressures from 1 bar and temperatures ranging from 5 ° C to 50 ° C.
Het uiteindelijke product kan op elk gewenst formaat worden gesneden. Een uitermate geschikt formaat voor dekzeilen 25 is A4 formaat.The final product can be cut to any desired size. An extremely suitable format for tarpaulins 25 is A4 format.
Claims (7)