NL1020700C2 - Hot forming method for making fixing device used as e.g. splint, by securing plastic blank to mandrel, heating and cooling before removing mandrel

Info

Publication number: NL1020700C2
Application number: NL1020700A
Authority: NL
Inventors: Marinus Johannes De Vos
Original assignee: Marinus Johannes De Vos
Priority date: 2002-05-28
Filing date: 2002-05-28
Publication date: 2003-12-01

Abstract

The blank is fixed around a mandrel, heated to a temperature above the softening point of the plastic and cooled to room temperature before detaching it from the mandrel and removing the latter. A method for making a plastic fixing device comprises hot-forming a plastic blank to the desired shape and then cooling. The blank is fixed around a mandrel, heated to a temperature above the softening point of the plastic and cooled to room temperature before detaching it from the mandrel and removing the latter.

Description

« * , Korte aanduiding: Werkwijze voor het vervaardigen van een kunststof bevattend fixeerorgaan, aldus verkregen fixeerorgaan en toepassing van het fixeerorgaan.Brief description: Method for manufacturing a fixing member containing a plastic, fixing member thus obtained and application of the fixing member.

5 De uitvinding heeft betrekking op een werkwijze voor het vervaardigen van een al of niet geperforeerd kunststof bevattend fixeerorgaan door uit te gaan van een kunststoffen plano en deze te verwarmen tot een nagenoeg gewenste tussenvorm is aangenomen, die door afkoel en wordt gefixeerd. De uitvinding heeft verder betrekking op het 10 aldus vervaardigde fixeerorgaan en op de toepassing van het fixeerorgaan voor diverse doeleinden.The invention relates to a method for manufacturing a fixer, which may or may not be perforated, by starting from a plastic blank and heating it until a substantially desired intermediate shape is adopted, which is cooled and fixed. The invention further relates to the fixation member thus produced and to the use of the fixation member for various purposes.

Met name heeft de uitvinding betrekking op het vervaardigen van een fixeerorgaan dat medisch wordt toegepast als vormdeel ter ondersteuning en bescherming van lichaamsdelen en voor technisch en 15 huishoudelijk gebruik.In particular, the invention relates to the manufacture of a fixing member which is used medically as a molded part for supporting and protecting body parts and for technical and domestic use.

De meest bekende werkwijze voor het spalken van lichaamsdelen is het gebruik van gipsmateriaal dat wordt bevochtigd, rond het te spalken lichaamsdeel wordt aangebracht en vervolgens tot harden wordt gebracht. Een dergelijk spalkmateriaal heeft het nadeel dat het 20 slechts door deskundige personen kan worden aangelegd, het aanbrengen van een dergelijk spalkmateriaal tijdrovend is en per definitie slechts eenmaal kan worden gebruikt. Verder is dergelijk spalkmateriaal niet vriendelijk in het gebruik omdat het transpiratie veroorzaakt en volumineus is.The most well-known method for splinting body parts is the use of gypsum material that is moistened, applied around the body part to be splinted and then hardened. Such a splint material has the disadvantage that it can only be applied by skilled persons, the application of such a splint material is time-consuming and can by definition only be used once. Furthermore, such splint material is not friendly to use because it causes perspiration and is bulky.

25 In de loop van de jaren zijn diverse verbeteringen op dit spalkmateriaal bedacht. Een dergelijke verbetering is beschreven in het Amerikaanse octrooi schrift 3.592.190. Volgens dit Amerikaanse octrooi schrift wordt een bandage gewikkeld rond het lichaamsdeel dat moet worden geïmmobiliseerd, welk bandagemateriaal is vervaardigd uit een 30 thermoplast gevormd uit een niet gevulkaniseerde neopreen die zacht wordt gemaakt door te verwarmen tot een temperatuur van ongeveer 55 °C en ^ m 2 vervolgens afgekoeld tot kamertemperatuur zodat de bandage stijf wordt. Verder is de bandage voorzien van perforaties en een klevende deklaag, waarbij de hechtlaag dienst doet om de bandage te fixeren en de perforaties dienst doen om een ventilatie te bereiken.25 Various improvements have been made to this splint material over the years. Such an improvement is described in U.S. Pat. No. 3,592,190. According to this US patent a bandage is wrapped around the body part to be immobilized, which bandage material is made from a thermoplastic formed from a non-vulcanized neoprene that is softened by heating to a temperature of about 55 ° C. and 2 m 2 then cooled to room temperature so that the bandage becomes stiff. The bandage is furthermore provided with perforations and an adhesive covering layer, wherein the adhesive layer serves to fix the bandage and the perforations serve to achieve ventilation.

5 Het zal duidelijk zijn dat om deze bandage goed aan te brengen deskundige verpleegkundigen nodig zijn en zoals in de beschrijving aangegeven bij het verwijderen van de bandage het materiaal wordt opengesneden zodat het slechts één keer kan worden gebruikt.It will be clear that skilled nurses are required to properly apply this bandage and, as indicated in the description when removing the bandage, the material is cut open so that it can only be used once.

Volgens de uitvinding is een fixeerorgaan ontworpen dat 10 steeds opnieuw kan worden gebruikt en makkelijk is aan te brengen. In hét fixeerorgaan volgens de uitvinding is zogenaamd "geheugen" aangebracht zodat het materiaal makkelijk van het lichaamsdeel kan worden verwijderd en opnieuw kan worden aangebracht nadat het lichaamsdeel bijvoorbeeld is gereinigd, voorzien van een zalf of aan andere behandelingen is 15 onderworpen.According to the invention, a fixing member has been designed which can be used again and again and which is easy to apply. In the fixing device according to the invention, so-called "memory" is arranged so that the material can be easily removed from the body part and reapplied after the body part has for instance been cleaned, provided with an ointment or has been subjected to other treatments.

De werkwijze voor het vervaardigen van een kunststof bevattend fixeerorgaan volgens de uitvinding wordt hierdoor gekenmerkt dat de plano wordt aangebracht rond een vormdeel en vastgezet, verwarmd tot boven het verwekingspunt van de kunststof, afgekoeld tot 20 kamertemperatuur, het vastzetten opgeheven en het aldus verkregen fixeerorgaan wordt verwijderd van het vormdeel. Als vormdeel wordt een voorwerp gebruikt dat gelijkenis vertoont met het lichaamsdeel dat moet worden geïmmobiliseerd. Dit voorwerp kan zijn vervaardigd uit hout of uit een ander willekeurig materiaal dat bestand is bij een verhoogde 25 temperatuur. Zoals blijkt uit het kenmerkend deel van de hoofdconclusie wordt de (niet-starre) plano aangebracht rond een vormdeel, dat bij medische toepassing gelijkend is op het lichaamsdeel dat moet worden geïmmobiliseerd en rond dit vormdeel vastgezet en vervolgens verwarmd tot boven het verwekingspunt van de kunststof. Zodra de kunststoffen plano de 30 vorm heeft aangenomen van het vormdeel wordt het geheel van vormdeel en de tussenvorm afgekoeld tot kamertemperatuur zodat de vorm is gefixeerd, 3 het vastzetorgaan wordt verwijderd en het aldus verkregen fixeerorgaan wordt afgewikkeld van het vormdeel. Daarmee is dan een fixeerorgaan verkregen dat ontrold kan worden eri kan worden aangebracht rond het lichaamsdeel dat moet worden geïmmobiliseerd. Na aanbrengen rond het 5 lichaamsdeel neemt het fixeerorgaan de vorm aan die het had rond het vormdeel. Daarmee is dan het lichaamsdeel geïmmobiliseerd op een voor het lichaam vriendelijke wijze.The method for manufacturing a plastic-containing fixing member according to the invention is characterized in that the blank is arranged around a molded part and fixed, heated to above the softening point of the plastic, cooled to room temperature, the fixing is canceled and the fixing member thus obtained is removed from the molded part. The shaped part used is an object that is similar to the body part to be immobilized. This article can be made from wood or from any other material that can withstand an elevated temperature. As is apparent from the characterizing part of the main claim, the (non-rigid) blank is applied around a molded part, which in medical application is similar to the body part to be immobilized and fixed around this molded part and then heated to above the plastic's softening point . As soon as the plastic blank has assumed the shape of the molded part, the whole of molded part and the intermediate mold are cooled to room temperature so that the mold is fixed, the securing member is removed and the fixing member thus obtained is unwound from the molded part. A fixing member is then obtained which can be unrolled and can be arranged around the body part to be immobilized. After application around the body part, the fixing member takes on the shape it had around the mold part. The body part is thus immobilized in a manner that is friendly to the body.

Als kunststof kan een polyester worden gebruikt met name een polyester in de handel gebracht door DuPont onder het merk Mylar. Het 10 is echter ook mogelijk om andere materialen te gebruiken die thermoplastisch van aard zijn en na verwarmen en omzetten tot een bepaalde vorm deze vorm steeds opnieuw aannemen. De plano kan al of niet zijn geperforeerd. De geperforeerde plano verdient de voorkeur om het gewicht te verlagen van het fixeerorgaan en om . een betere 15 luchtdoorlaatbaarheid mogelijk te maken.As a plastic, a polyester can be used, in particular a polyester marketed by DuPont under the Mylar brand. However, it is also possible to use other materials which are thermoplastic in nature and which, after heating and converting to a certain shape, repeatedly assume this shape. The blank may or may not be perforated. The perforated blank is preferable to reduce the weight of the fixing member and around. to allow better air permeability.

Om het gevoel van kunststof op een lichaamsdeel te voorkomen verdient het de voorkeur dat de plano wordt bekleed met een zachtmakende stof zoals verbandmateriaal. De van een zachtmakend materiaal beklede plano wordt vervolgens rond het vormdeel aangebracht, 20 vastgezet en verwarmd tot boven het verwekingspunt van de kunststof. Voor een polyester kan het verwekingspunt liggen boven 150 °C.To prevent the feeling of plastic on a body part, it is preferable that the blank is coated with a softening substance such as dressing material. The blank coated with a softening material is then placed around the molded part, fixed and heated to above the softening point of the plastic. For a polyester, the softening point can be above 150 ° C.

Op deze wijze kan een fixeerorgaan worden verkregen dat rond armen en benen kan worden aangebracht of ter ondersteuning van de rug. Ook is het mogelijk op deze wijze een goedkope, goed toe te passen 25 beenbeschermer te vervaardigen.In this way a fixation member can be obtained which can be arranged around arms and legs or to support the back. It is also possible to manufacture an inexpensive, good-to-use leg protector in this way.

Een ander toepassingsgebied is het vervaardigen van een ondersteuning voor planten of boompjes, waarbij het fixeerorgaan wordt aangebracht rond de stam. Het voordeel van dit fixeerorgaan is dat bij het groeien van de stam het fixeerorgaan zich enigszins aanpast aan de 30 dikker wordende stam en op deze wijze weinig onderhoud vereist.Another field of application is the production of a support for plants or trees, wherein the fixing member is arranged around the trunk. The advantage of this fixing member is that as the stem grows, the fixing member adapts somewhat to the thickening trunk and requires little maintenance in this way.

De uitvinding wordt nader toegelicht aan de hand van het 4 volgende voorbeeld.The invention is further elucidated with reference to the following example.

Voorbeeld.Example.

Een plano van polyester (Mylar) wordt bekleed met verbandmateriaal en vervolgens aangebracht rond een nagenoeg rond 5 vormdeel vervaardigd uit hout met afmetingen als van een onderarm van een gemiddeld persoon van ongeveer 30 jaar. De plano wordt redelijk strak aangebracht rond het vormdeel en vastgezet. Vervolgens wordt het beklede vormdeel in een oven geplaatst en gebracht op een temperatuur van 155 °C, zodat de polyester verweekt.A polyester blank (Mylar) is covered with bandage material and then applied around a substantially round molded part made of wood with dimensions as forearm of an average person of about 30 years. The blank is applied fairly tightly around the molded part and secured. The coated molded part is then placed in an oven and brought to a temperature of 155 ° C, so that the polyester softens.

10 Na ongeveer 10 minuten wordt het beklede vormdeel uit de oven verwijderd en wordt het beklede vormdeel afgekoeld tot kamertemperatuur. Daarna kan de plano na opheffen van het vastzetten van het vormdeel worden afgewikkeld, waarna de plano de nagenoeg ronde vorm weer spontaan aanneemt. Op deze wijze is een fixeerorgaan volgens de 15 uitvinding verkregen dat kan worden aangebracht rond de arm van een persoon zodat de onderarm van de persoon wordt ondersteund met het fixeerorgaan volgens de uitvinding.After about 10 minutes, the coated molded article is removed from the oven and the coated molded article is cooled to room temperature. The blank can then be unwound after the fixing of the molded part has been released, after which the blank resumes the substantially round shape spontaneously. In this way a fixing member according to the invention is obtained which can be arranged around the arm of a person so that the lower arm of the person is supported with the fixing member according to the invention.

1 020 '1 020 '

Claims

Method according to claim 1, characterized in that the blank is made of a polyester.

Method according to claims 1-2, characterized in that the blank is coated with a softening material.

4. Method according to claim 2, characterized in that the polyester corresponds to Mylar (brand).

Method according to claims 1-4, characterized in that the heating takes place at a temperature between 100 and 250 ° C.

Fixing member manufactured according to a method as described in claims 1-5, characterized in that it is used as material for supporting body parts.

Fixing member according to claim 6, characterized in that the plastic blank is perforated.

Use of the fixing member according to claims 6-7 as splint material.

Use of the fixing member according to claims 6-7 as a leg protector.

Use of the fixing member as claimed in claims 6-7 as supporting material for the back or parts thereof. II. Use of the fixing member as claimed in claims 6-7 as a member for supporting plants or other vegetable material.