KR940004663Y1 - Precious metal ornaments - Google Patents
Precious metal ornaments Download PDFInfo
- Publication number
- KR940004663Y1 KR940004663Y1 KR92000166U KR920000166U KR940004663Y1 KR 940004663 Y1 KR940004663 Y1 KR 940004663Y1 KR 92000166 U KR92000166 U KR 92000166U KR 920000166 U KR920000166 U KR 920000166U KR 940004663 Y1 KR940004663 Y1 KR 940004663Y1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- precious metal
- metal layer
- colored
- ion plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
내용 없음.No content.
Description
제1도는 본고안인 귀금속 장식품의 일예를 나타낸 종단면도.Figure 1 is a longitudinal cross-sectional view showing an example of the precious metal ornaments in this paper.
제2도는 이온 도금장치의 설명 개략도.2 is a schematic view of an ion plating apparatus.
제3(a)도, 제3(b)도는 본고안과 다른 실시예에 있어서의 귀금속 장식품을 제조하는 공정을 나타낸 설명도.Fig. 3 (a) and Fig. 3 (b) are explanatory diagrams showing a step of manufacturing a precious metal ornament in an embodiment different from this paper.
제4도는 본고안의 귀금속 장식품을 다시 한번 별도의 실시예로 나타낸 종단면도이다.Figure 4 is a longitudinal cross-sectional view showing the precious metal ornaments in this article once again in a separate embodiment.
본고안은 시계, 안경프레임, 라이타, 만년필, 보러치등의 장식품 또는 장식적 요소를 겸비한 제품(본고안에 있어서 이들을 간단히 장식품이라 약칭한다)에 귀금속의 표면층을 부여하여 이루어진 귀금속 장식품에 관한 것이다.This article relates to precious metal ornaments made by adding a surface layer of precious metal to a product including ornaments or decorative elements such as watches, eyeglass frames, lighters, fountain pens, boraches, or simply decorative elements in this article.
종래에는 시계, 안경프레임, 라이타, 만년필, 브러치등의 장식품에 금색, 흑색, 청색, 암흑색등의 유색피막 및 금(金)등의 귀금속 피막을 진공증착이나 습식도금등으로 형성된 장식품이 알려져 있다.Background Art Conventionally, ornaments such as gold, black, blue, dark black and other precious metal coatings, such as gold, black, blue, dark black, and precious metal coatings such as gold are known, such as watches, eyeglass frames, lighters, fountain pens, and brushes.
상기 종래 장식품은 금속, 프라스틱, 초자등으로 이루어진 장식 기재상에 비금속의 이온도금(Ion PLATING)에 의해 질화티탄늄(Ti)에 의한 금색막, 산화티탄늄에 의한 흑색막, 산화텅스텐(W)에 의한 청색막, 탄화티탄늄에 의한 암흑색막등의 다양한 색조의 피막을 부착시켜서 유색비금속층을 형성하고, 그 유색 비금속층의 표면상에 다시 금등의 귀금속을 기상증착에 의한 드라이 도금 또는 전해 또는 무전해 도금의 습식법에 의해 부착시켜서 귀금속층을 형성하고, 그 귀금속층을 마스크 패턴에 따라 엣칭하여 이루어진 것이다.The conventional ornament is a gold film of titanium nitride (Ti), a black film of titanium oxide, tungsten oxide (W) by a non-metal ion plating (Ion PLATING) on a decorative substrate made of metal, plastic, porcelain, etc. A color non-metallic layer is formed by attaching a film of various color tones such as a blue film by using a titanium film or a dark black film by titanium carbide, and gold-plated precious metal such as gold on the surface of the colored non-metallic layer is further subjected to dry plating or electrolytic deposition or The noble metal layer is formed by attaching by a wet method of electroless plating, and the noble metal layer is etched according to a mask pattern.
그러나, 이들 상기 종래품에 있어서는 이온도금에 의한 금속산화물, 금속 탄화물, 금속질화물등의 유색 비금속층의 장식기재에 대한 밀착성에 대해서는 충분한 성능을 지니고 있지만 이온도금에 의한 유색 비금속층과 그 유색 비금속층의 표면에 귀금속을 진공 증착이나 습식 도금등으로 형성한 귀금속층과의 사이의 밀착성이 나쁘다는 결점이 지적되고 있다.However, in the above conventional products, the colored nonmetallic layer and the colored nonmetallic layer by ion plating have sufficient performance in adhesion to the decorative substrate of colored nonmetallic layers such as metal oxides, metal carbides, and metal nitrides by ion plating. The drawback of the bad adhesiveness with the noble metal layer in which the noble metal was formed in the surface of vacuum by vacuum deposition, wet plating, etc. is pointed out.
본고안자는 상기 종래 기술의 결점을 해결하기 위하여 여러가지로 검토한바, 비금속을 이온도금에 의하여 장식 기재상에 부착시켜 유색비금속층을 형성한후 그 유색 비금속층의 표면위에 귀금속층을 이온도금에 의해 형성시키면 상기 종래품에 비해 유색 비금속층사이의 밀착성이 향상된다는 것을 알수 있었다.In order to solve the drawbacks of the prior art, the present inventors have made various researches. A non-metal is attached onto a decorative substrate by ion plating to form a colored nonmetal layer, and then a precious metal layer is formed on the surface of the colored nonmetal layer by ion plating. It was found that the adhesion between the colored nonmetallic layers was improved compared to the conventional products.
그렇지만 실용(實用)에 견딜수 있을 만큼의 양호한 밀착성을 얻기에는 아직 불충분하고, 개량의 여지가 남아 있었다.However, it is still insufficient to obtain good adhesion enough to withstand practical use, and there is room for improvement.
즉, 본고안자의 실험에 의하면 귀금속층이 0.3㎛정도의 두께까지는 밀착성은 좋지만 0.3㎛이상의 두께가 되면 귀금속층의 밀착성이 불량이 되는 것을 알수 있었다.In other words, according to the experiments of the present inventors, the adhesion of the precious metal layer to the thickness of about 0.3 μm is good, but the adhesion of the precious metal layer is poor when the thickness is 0.3 μm or more.
또 유색비금속층과 귀금속층과의 밀착성을 좋게 하려고 귀금속층을 0.3㎛이하의 두께로하면 귀금속층에 있어서 내마모성의 저하나, 강도저하가 생겨나 마모에 의한 귀금속의 색조 소실이나 손상에 따른 장식성의 저하라고 하는 문제를 일으키는 것도 알 수 있었다.In addition, when the noble metal layer has a thickness of 0.3 μm or less in order to improve the adhesion between the colored nonmetallic layer and the noble metal layer, the wear resistance decreases or the strength decreases in the noble metal layer. It was found that causing the problem.
본고안은 상기 종래 기술의 단점을 해소하는 것이며, 밀착성, 내마모성, 내식성에서 우수한 귀금속장식품을 제공하려는 것이다.The present invention is to solve the disadvantages of the prior art, and to provide a precious metal ornament excellent in adhesion, wear resistance, corrosion resistance.
본고안은 첫째 장식기재(基材)와 그 장식기재의 표면에 이온도금에 의해 비금속의 피막을형성하여 이루어진 유색 비금속층과 그 유색비금속층의 표면에 이온도금에 의해 귀금속의 피막을 형성하여 이루어진 귀금속층으로 구성되고 동시에 상기 귀금속층이 크롬(Cr)을 0.1-4.5중량%함유한 귀금속으로 이루어지는 것이며, 또하나는 상기 귀금속층이 유색비금속층 표면에 부분적으로 붙여져 있는 것에 관한 것이다.This paper first consists of a colored nonmetallic layer formed by forming a nonmetallic film on the surface of a decorative substrate and its surface by ion plating, and a precious metal film formed by ion plating on the surface of the colored nonmetallic layer. The noble metal layer is composed of a noble metal layer and at the same time the noble metal layer is composed of a noble metal containing 0.1-4.5 wt% of chromium (Cr).
이하 첨부도면에 의하여 상세히 설명하면 다음과 같다.When described in detail by the accompanying drawings as follows.
제1도와 같이 본고안의 귀금속장식품(1)은 장식기재(2)와 그 장식기재(2)의 표면에 이온도금에 의해 귀금속 피막을 형성하여 구성된 유색 비금속층(3)과 그 유색비금속층(3)의 표면에 이온도금에 의해 귀금속 피막을 형성하여 이루어진 귀금속층(4)으로 구성된 기본적 구조를 가지고 상기 귀금속층(4)이 크롬(Cr)을 0.1-4.5중량% 함유한 귀금속으로 이루어진 것이다.As shown in Fig. 1, the precious metal ornament (1) of the present invention has a colored nonmetallic layer (3) and a colored nonmetallic layer (3) formed by forming a precious metal film on the surface of the decorative substrate (2) and the decorative substrate (2) by ion plating. The noble metal layer 4 has a basic structure composed of a noble metal layer 4 formed by forming a noble metal film by ion plating on the surface thereof, and the noble metal layer 4 is made of a noble metal containing 0.1 to 4.5% by weight of chromium (Cr).
장식기재(2)는 예를 들면 시계, 안경프레임, 라이타, 만년필, 브러치등의 기재이며, 그 재료로는 티탄늄(Ti), 티틴늄합금, 스테인레스, 니켈(Ni)-크롬(Cr)합금, 동합금등에 금속등의 고급장식 제품의 소재가 사용되고 있다.The decorative base material 2 is a base material such as a watch, an eyeglass frame, a lighter, a fountain pen, a brush, and the like, and the material is titanium (Ti), titanium alloy, stainless steel, nickel (Ni) -chromium (Cr) alloy, and the like. The materials of high-grade decorative products such as metals are used for copper alloys.
유색비금속층(3)은 잘 알려진 비금속류의 이온도금에 의해 형성 할수 있다.The colored nonmetallic layer 3 can be formed by ion plating of well-known nonmetals.
제2도에 도시한 바와같이 이온도금장치(5)는 진공탱크(6)속에 캐쇼드(음극) 전극(7)과 그 음극전극(7)에 대향하는 하측에 가열전원(8)을 가지고 있는 증발원 보드(蒸發源 BOARD)(9)가 설치되고, 증발원보드(9)는 음극전극(7)과 직류전원(10)을 끼워 접속하고 있다.As shown in FIG. 2, the ion plating apparatus 5 has a heating power source 8 under the cathode (cathode) electrode 7 and its cathode electrode 7 in the vacuum tank 6. An evaporation source board 9 is provided, and the evaporation source board 9 is connected with the cathode electrode 7 and the DC power supply 10 interposed therebetween.
진공탱크(6)는 진공용 배기구(11)과 반응개스 도입구(12)를 가지고 있다.The vacuum tank 6 has a vacuum exhaust port 11 and a reaction gas inlet port 12.
유색비금속층(3)을 형성하는 방법은 이온도금장치(5)의 증발원 보드(9)에 티탄늄, 티탄늄합금, 크롬, 크롬 합금, 니오븜(Nb), 지르코늄(Zr), 바나듐(V) 또는 이들의 합금등의 비금속을 증발원으로 투입하고, 음극전극(7)에 장식기재(2)를 매어단다.The method for forming the colored nonmetallic layer 3 includes titanium, titanium alloy, chromium, chromium alloy, niobium (Nb), zirconium (Zr) and vanadium (V) on the evaporation source board 9 of the ion plating apparatus 5. ) Or a base metal such as an alloy thereof is introduced into the evaporation source, and the decorative base material 2 is suspended on the cathode electrode 7.
그다음에 증발원을 가열하고 진공탱크(6)의 내부를 소정의 진공도로 하고 아세칠렌, 질소, 산소등의 반응개스를 도입한후 전자빔을 증발원 보드(9)의 비금속에 조사하여 비금속을 이온화시킨다.Then, the evaporation source is heated, the inside of the vacuum tank 6 is a predetermined vacuum, a reaction gas such as acetylene, nitrogen, oxygen or the like is introduced, and the electron beam is irradiated onto the nonmetal of the evaporation source board 9 to ionize the nonmetal.
이온화된 비금속은 반응개스와 반응하여 비금속의 탄화물, 질화물, 산화물의 형태로 장식기재(2)에 석출(析出)하여 유색 비금속층(3)을 형성시킨다.The ionized nonmetal reacts with the reaction gas to precipitate in the decorative base material 2 in the form of carbides, nitrides, and oxides of the nonmetal to form a colored nonmetallic layer 3.
유색비금속층(3)은 비금속과 반응개스의 종류를 변화시켜 다양한 색조를 얻을수 있다.The colored nonmetallic layer 3 can obtain various color tones by changing the type of nonmetal and reaction gas.
예를들면 티탄늄 및 티탄늄 합금의 경우 질화물은 금색계로 되고, 탄화물은 흑색계, 질화물, 탄화물의 혼합물의 경우는 브라운(BROWN)계 또는 핑크계로 된다.For example, in the case of titanium and titanium alloys, the nitrides are gold-based, and the carbides are black-based, nitrides, and brown-based or brown-based.
크롬 및 크롬합금의 경우 질화물, 탄화물, 산화물이더라도 백-회색-흑으로 되고 니오븜(Nb), 지르코늄(Zr), 바나듐(V) 및 이들의 합금인 경우는 티탄늄(Ti)및 티탄늄합금을 베이스로 한 경우와 가까운 색조가 된다.Nitride (Nb), zirconium (Zr), vanadium (V) and their alloys are titanium (Ti) and titanium alloys for chromium and chromium alloys. The tone is close to that of the base.
유색비금속층(3)의 두께는 0.1-2.0㎛이며 바람직한 것은 0.2-0.8㎛이다.The colored nonmetallic layer 3 has a thickness of 0.1-2.0 µm and preferably 0.2-0.8 µm.
상기와 같이 형성한 유색비금속층(3)의 표면에 귀금속층(4)의 피막을 형성한다. 귀금속층(4)은 크롬(Cr)을 0.1-4.5중량% 함유한 귀금속을 증발원으로 하여 상술한 것과 마찬가지의 장치, 수단을 사용한 이온도금에 의해 형성할 수 있다. 귀금속의 종류는 잘 알려진 장식품에 일반적으로 쓰이는 것을 사용할 수 있으며, 원하는 색조에 부응하여 선택할 수 있다.The film of the noble metal layer 4 is formed on the surface of the colored nonmetallic layer 3 formed as mentioned above. The precious metal layer 4 can be formed by ion plating using the same apparatus and means as described above, using the precious metal containing 0.1-4.5 wt% of chromium (Cr) as the evaporation source. Precious metals can be used as they are commonly used for well-known ornaments, and can be selected to suit the desired color tone.
예를 들어 금색으로 하고 싶은 경우 금, 백색으로 하고 싶은 경우는 팔라듐(Pd) 또는 백금이 쓰이고 있다.For example, gold is desired. Palladium (Pd) or platinum is used when gold is desired.
크롬의 첨가량은 0.1-4.5중량%이며, 0.1중량%미만이 되면 밀착성 향상의 효과를 얻을 수 없고, 4.5중량%를 넘으면 귀금속으로서의 외관을 얻을수 없게 된다.The addition amount of chromium is 0.1-4.5 weight%, and when it is less than 0.1 weight%, the effect of an adhesive improvement will not be acquired, and when it exceeds 4.5 weight%, the appearance as a noble metal will not be obtained.
귀금속층(4)의 두께는 0.1-1㎛로 형성할 수 있다.The thickness of the noble metal layer 4 may be formed to be 0.1-1 μm.
본고안의 귀금속 장식품(1)은 귀금속층(4)을 유색비금속층(3)의 표면에 붙이는 것도 가능하다.In the precious metal ornament 1 of the present invention, the precious metal layer 4 may be attached to the surface of the colored nonmetallic layer 3.
제3(a)도에 나타난 바와같이, 유색비금속층(3)의 표면에 귀금속층(4)을 이온도금에 의해 전면적으로 형성한후 귀금속층(4)을 남는 부분에 마스킹(13)을 시행하고, 귀금속 박리액에 침적하여 마스킹(13)을 시행하지 않은 부분의 귀금속층을 용해 제거한후 마스킹(13)을 제거함으로써 제3(b)도에서와 같이 유색비금속층(3)의 표면에 귀금속층(4)을 부분적으로 형성하여 이루어진 본고안 귀금속 장식품(1)을 얻을 수 있다.As shown in FIG. 3 (a), the noble metal layer 4 is formed entirely on the surface of the colored nonmetallic layer 3 by ion plating, and then the masking 13 is applied to the portion of the noble metal layer 4 remaining. Then, the noble metal layer was dissolved in the noble metal stripping solution, and the noble metal layer of the portion not subjected to the masking 13 was dissolved and removed, and then, the masking 13 was removed, and as shown in FIG. The precious metal ornament 1 of the present invention obtained by partially forming the layer 4 can be obtained.
이온도금에 의해 귀금속층(4)을 형성한후 마스킹을 시행하여 불 필요한 귀금속층을 제거하는 방법은 유색비금속층(3)에 마스킹을 시행하고 이온도금에 의해 귀금속층을 붙이는 방법에 비교하여 이온도금시에 마스킹이 분해될 염려나 분해한 마스킹에 의해 이온도금이 저해될 염려가 없으며, 유색 비금속층을 형성한 후에, 귀금속층을 연속적으로 형성할 수 있다.Forming the precious metal layer 4 by ion plating and then removing the unnecessary precious metal layer by masking is performed in comparison with the method of masking the colored nonmetallic layer 3 and attaching the precious metal layer by ion plating. There is no fear that masking will decompose at the time of plating, or ion plating will not be inhibited by the decomposed masking, and after forming a colored nonmetallic layer, a noble metal layer can be formed continuously.
또 마스킹의 제거도 용이하다.It is also easy to remove masking.
본고안에 있어서 두께가 큰 귀금속층을 얻고 싶은 경우(예를들면, 1㎛를 넘는 두께로 하고 싶은 경우)에는 제4도에서와 같이 귀금속층(4)의 표면에 습식도금등의 방법에 의해 귀금속도금층(14)을 형성할 수 있다.In this paper, when a precious metal layer having a large thickness is to be obtained (for example, a thickness exceeding 1 μm), the precious metal layer is wet-plated on the surface of the precious metal layer 4 as shown in FIG. The plating layer 14 can be formed.
[실시예]EXAMPLE
본고안을 구체적인 실시예에 의해 더욱더 상세히 설명한다.The present invention will be described in more detail by way of specific examples.
[실시예 1]Example 1
이온도금장치(5)의 진공탱크(6)내의 음극전극(7)에 티탄늄제의 안경프레임을 걸어놓고 증발원보드(9)에 티탄늄을 투입하고 반응개스로서 질소 및 에칠렌개스를 도입하여 진공도를 10-6-10-6Torr로 하고 석출속도를 0.01-0.02㎛/분으로 조절해서 30분간 이온 도금을 하여 티탄늄 안경프레임의 표면에 0.5㎛의 유색 비금속층을 형성하였다.Titanium glasses are placed on the cathode electrode 7 in the vacuum tank 6 of the ion plating apparatus 5, titanium is added to the evaporation source board 9, and nitrogen and ethylene gas are introduced as a reaction gas to improve the vacuum degree. 10 -6 -10 -6 Torr and the precipitation rate was adjusted to 0.01-0.02㎛ / min ion plating for 30 minutes to form a colored non-metallic layer of 0.5㎛ on the surface of the titanium eyeglass frame.
이 유색비금속층의 색은 회색이었다. 다음에 반응개스를 정지하고 크롬을 2중량% 함유한 금을 귀금속으로 증발원 보드(9)에 투입하여 진공도를 10-4-10-5Torr로 조절해서 8분간 이온도금을 하여 유색 비금속층 표면에 0.3㎛의 크롬을 2중량% 함유한 금으로 이루어진 귀금속층을 형성하였다.The color of this colored nonmetallic layer was gray. Next, the reaction gas was stopped, and gold containing 2% by weight of chromium was added to the evaporation source board (9) as a precious metal, and the degree of vacuum was adjusted to 10 -4 -10 -5 Torr for 8 minutes, followed by ion plating to the surface of the colored nonmetallic layer. A precious metal layer made of gold containing 2 wt% of 0.3 μm chromium was formed.
얻어진 안경프레임은 유색비금속층과 귀금속층과의 사이에 밀착력이 양호하며 10개의 안경프레임을 상기 조작으로 반복하여 제조한바 밀착성불량의 발생율은 0%였다.The obtained eyeglass frames had good adhesion between the colored nonmetallic layer and the noble metal layer, and ten glasses frames were repeatedly produced by the above operation, and the incidence of poor adhesion was 0%.
[실시예 2]Example 2
이온도금장치(5)의 진공탱크(6)내의 음극전극(7)에 티탄늄제의 안경프레임을 걸어 놓고 증발원보드(9)에 티탄늄을 튜입하고, 반응개스로서 질소 및 에칠렌개스를 도입하여 진공도를 10-2-10-6Torr로 하고 석출속도를 0.01-0.02㎛/분으로 조절해서 30분간 이온도금을 하여 티탄늄 안경프레임의 표면에 0.5㎛의 유색비금속층을 형성하였다.Titanium glasses are hanged on the cathode electrode 7 in the vacuum tank 6 of the ion plating apparatus 5, and titanium is introduced into the evaporation source board 9, and nitrogen and ethylene gas are introduced as reaction gas. It was 10 -2 -10 -6 Torr and the precipitation rate was adjusted to 0.01-0.02㎛ / min ion plating for 30 minutes to form a colored non-metallic layer of 0.5㎛ on the surface of the titanium eyeglass frame.
이 유색비금속층의 색은 회색이었다.The color of this colored nonmetallic layer was gray.
다음에 반응개스를 정지하고 크롬을 3중량% 함유한 파라듐(Pd)으로 이루어진 귀금속층을 형성하였다.Next, the reaction gas was stopped to form a precious metal layer made of palladium (Pd) containing 3% by weight of chromium.
파라듐 귀금속층을 형성한 티탄늄 안경프레임을 이온 도금장치(5)의 진공탱크(6)에서 꺼내어 그 안경 프레임의 브릿지 부분에 아크릴계 도료를 도포하여 마스킹을 실시한후 귀금속 박리액에 침적하여 마스킹되어 있지않은 부분에 파라듐 귀금속층을 박리한후 마스킹재를 제거하여 림(RIM)과 탬플(TEMPLE)부는 유색비금속층이 노출되어 회색(GRAY)으로 되고 브릿지부에는 파라듐 귀금속층이 남아 백색으로 되며, 이렇게 해서 백색과 회색과의 조합으로 이루어진 외관색조의 티탄늄제 안경 프레임을 얻을 수 있다.Titanium eyeglass frames having a palladium noble metal layer were taken out of the vacuum tank 6 of the ion plating apparatus 5, and an acrylic paint was applied to the bridge portions of the eyeglass frames, followed by masking. After peeling off the palladium precious metal layer on the part that is not present, the masking material is removed and the colored nonmetallic layer is exposed to gray and the gray portion is left on the bridge part. In this way, a spectacle-colored titanium eyeglass frame made of a combination of white and gray can be obtained.
얻어진 안경 프레임은 유색비금속층과 귀금속층과의 사이에 밀착력이 양호하며, 10개의 안경프레임을 상기 조작으로 반복하여 제조한바 밀착성불량의 발생율은 0%였다.The obtained eyeglass frames had good adhesion between the colored nonmetallic layer and the noble metal layer, and ten glasses frames were repeatedly produced by the above operation. As a result, the incidence of poor adhesion was 0%.
[실시예 3]Example 3
이온도금장치(5)의 진공탱크(6)내의 음극전극(7)에 티탄늄제의 안경프레임을걸어놓고 증발원보드(9)에 티탄늄을 투입하고 반응개스로서 질소 및 에칠렌개스를 도입하여 진공도를 10-2-10-6Torr로 하고 석출속도를 0.01-0.02㎛/분으로 조절해서 30분간 이온도금을 하여 티탄늄 안경프레임의 표면에 0.5㎛의 유색 비금속층을 형성하였다.Titanium glasses were placed on the cathode electrode 7 in the vacuum tank 6 of the ion plating apparatus 5, titanium dioxide was introduced into the evaporation source board 9, and nitrogen and ethylene gas were introduced as reaction gas to improve the vacuum degree. 10 -2 -10 -6 Torr and the precipitation rate was adjusted to 0.01-0.02㎛ / min ion plating for 30 minutes to form a colored non-metallic layer of 0.5 ㎛ on the surface of the titanium eyeglass frame.
이 유색비금속층의 색은 회색이었다.The color of this colored nonmetallic layer was gray.
다음에 반응개스를 정지하고 크롬을 2중량% 함유한 금을 증발원 보드(9)에 투입하여 진공도를 10-4-10-5Torr로 조절해서 8분간 이온도금을 하여 유색 비금속층 표면에 0.3㎛의 크롬을 2중량% 함유한 금으로 이루어진 귀금속층을 형성하였다.Next, the reaction gas was stopped, and gold containing 2% by weight of chromium was added to the evaporation source board 9, and the degree of vacuum was adjusted to 10 -4 -10 -5 Torr, followed by ion plating for 8 minutes, and 0.3 µm on the surface of the colored nonmetallic layer. A precious metal layer made of gold containing 2% by weight of chromium was formed.
귀금속층을 형성한 티탄늄 안경프레임을 이온 도금장치(5)의 진공탱크(6)에서 꺼내어 잘 알려져 있는 습식도금에 의해 귀금속층의 표면에 다시 1㎛의 두께로 20캐럿의 금-Pd의 귀금속 도금층을 형성하였다.Titanium eyeglass frames having a precious metal layer were taken out from the vacuum tank 6 of the ion plating apparatus 5, and the well-known wet plating was carried out on the surface of the precious metal layer again with a thickness of 1 μm. A plating layer was formed.
다음에 금-Pd 귀금속 도금층을 형성한 안경프레임의 브릿지부분에 아크릴계 도료를 도포하여 마스킹을 한 후 금 박리액에 침적하고 마스킹이 되어 있지 않은 부분에 금-Pd 합금 도금층을 박리한후 마스킹재를 제거하여 림과 탬플부는 유색비금속층이 노출되어 암흑색으로 되고 브릿지부에는 금-Pd 합금도금층이 남아 금색으로 되며 이렇게 해서 금색과 회색과의 조합으로 이루어진 외관색조의 티탄늄제 안경프레임을 얻을 수 있다.Next, an acrylic paint is applied to the bridge portion of the eyeglass frame on which the gold-Pd noble metal plating layer is formed and then masked. Then, it is immersed in the gold stripping solution and the gold-Pd alloy plating layer is peeled off on the unmasked portion. By removing the rim and the temple part, the colored non-metallic layer is exposed to become dark black, and in the bridge part, the gold-Pd alloy plating layer remains and becomes gold. Thus, the eyeglass frame of the appearance color titanium made of a combination of gold and gray can be obtained. .
얻어진 프레임은 유색비금속층과 귀금속층과의 사이에 밀착력이 양호하며 10개의 안경프레임을 상기 조작으로 반복하여 제조한바, 불량의 발생율은 0%였다.The obtained frame had good adhesion between the colored nonmetallic layer and the noble metal layer, and ten eyeglass frames were repeatedly produced by the above operation, and the occurrence rate of the defect was 0%.
[비교예 1]Comparative Example 1
비교를 위하여 실시예 1의 귀금속에 크롬을 첨가한 금 대신에 크롬을 첨가하지 않은 금만을 사용하여 귀금속층을 형성한 다른 것을 실시예 1과 마찬가지로 티탄늄제의 안경 프레임을 처리하여 유색 비금속층의 표면에 크롬을 포함하지 않는 금만의 귀금속층을 형성하였다.For comparison, another precious metal layer was formed using only gold without chromium instead of gold with chromium added to the precious metal of Example 1. To form a precious metal layer of gold only does not contain chromium.
얻어진 안경 프레임은 유색 비금속층과 귀금속층과의 사이에 밀착력이 불량하며, 10개의 안경 프레임을 상기 조작으로 반복하여 제조한바 밀착력 발생율은 40%였다.The obtained eyeglass frames had poor adhesion between the colored nonmetallic layer and the precious metal layer, and ten glasses frames were repeatedly produced by the above operation.
이상과 같이 본고안의 귀금속 장식품은 이온도금에 의해 형성한 유색 비금속층의 표면에 크롬을 0.1-4.5중량% 함유한 귀금속의 이온도금에 의하여 형성된 귀금속층을 형성한 것이기 때문에 종래의 크롬을 포함하지 않은 귀금속층을 유색 비금속층의 표면에 형성한 귀금속 장식품에 비교하여 귀금속층과 유색비금속층과의 사이에 밀착성이 향상되고 제조시의 밀착성 불량제품의 발생이 전무한 동시에 제품 사용시에 있어서도 귀금속층이 박리도 염려할 필요가 없다.As described above, since the precious metal ornament of the present invention forms the precious metal layer formed by ion plating of the precious metal containing 0.1-4.5% by weight of chromium on the surface of the colored nonmetallic layer formed by ion plating, it does not contain conventional chromium. Compared with the precious metal ornament formed on the surface of the colored nonmetallic layer, the adhesion between the precious metal layer and the colored nonmetallic layer is improved, and there is no occurrence of poor adhesiveness in manufacturing, and the precious metal layer is peeled off even when using the product. There is no need to worry.
또 본고안의 귀금속 장식품은 귀금속층과 유색 비금속층의 밀착성이 양호하기 때문에 귀금속층을 두껍게 형성 하더라도 밀착성 불량의 문제가 생기지않으며, 예를 들어 귀금속층의 두께가 0.3㎛이상이더라도 양호한 밀착성을 얻을 수 있고 귀금속층이 박리될 우려가 없다.In addition, the precious metal ornament of this paper has good adhesion between the noble metal layer and the colored non-metallic layer, so even if the noble metal layer is formed thick, no problem of poor adhesion occurs. There is no fear that the noble metal layer may peel off.
그리고, 본고안에 의하면 귀금속층의 두께를 크게 형성시킨 결과 제품의 내마모성을 향상시키는 효과가 있었다.In addition, according to the present proposal, as the thickness of the noble metal layer was increased, the wear resistance of the product was improved.
더우기, 유색 비금속층의 표면에 귀금속층을 부분적으로 만듬으로서 유색 비금속층의 색조와 귀금속층의 색조를 변화시키는 것이 가능하게 되었고 변화가 풍부하고 장식성을 향상시키는 효과가 있다.Furthermore, by partially making the precious metal layer on the surface of the colored nonmetallic layer, it becomes possible to change the color tone of the colored nonmetallic layer and the color tone of the precious metal layer, and the change is rich and has an effect of improving the decorativeness.
Claims (1)