KR20110105133A - Stainless steel double cup and its manufacturing method - Google Patents
Stainless steel double cup and its manufacturing method Download PDFInfo
- Publication number
- KR20110105133A KR20110105133A KR1020100024228A KR20100024228A KR20110105133A KR 20110105133 A KR20110105133 A KR 20110105133A KR 1020100024228 A KR1020100024228 A KR 1020100024228A KR 20100024228 A KR20100024228 A KR 20100024228A KR 20110105133 A KR20110105133 A KR 20110105133A
- Authority
- KR
- South Korea
- Prior art keywords
- coating layer
- cup
- stainless steel
- double cup
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
컵 표면에 형성되는 인쇄층의 색채 및 색조를 양호하게 나타낼 수 있는 스테인리스 이중 컵 및 그 제조방법에 관한 것이다.
본 발명의 스테인리스 이중 컵은 스테인리스 재질로 이루어지면서 컵의 내부를 이루는 내측부와 컵의 외부를 이루는 외측부 및 이들 내측부와 외측부 사이가 공간부로 이루어진 이중 컵 본체; 상기 외측부 표면에 도장된 제1도장층; 상기 제1도장층에 형성된 인쇄층; 을 포함하는 스테인리스 이중 컵을 제공한다.
상기 제1도장층은 미색계열로 이루어지고, 제1도장층의 외측으로는 코팅층으로 이루어진 제2도장층이 형성되고 이 제2도장층층은 펄 안료로 이루어진다.
또한 본 발명은 스테인리스 재질로 이루어지면서 컵의 내부를 이루는 내측부와 컵의 외부를 이루는 외측부 및 이들 내측부와 외측부 사이가 공간부로 이루어진 이중 컵을 제조하는 단계; 상기 이중 컵의 외측부에 제1도장층을 도장하는 단계; 상기 제1도장층을 소성하는 단계; 상기 건조된 제1도장층에 인쇄층을 형성하는 단계; 를 포함하는 스테인리스 이중 컵 제조방법을 제공한다.
상기 제1도장층 도장단계에서는 미색계열의 안료가 사용된다. 상기 제1도장층 소성단계 후 인쇄층의 질감을 부드럽고 화려하게 할 수 있도록 펄 안료로 이루어진 제2도장층 도장단계가 더 행하여진다.The present invention relates to a stainless double cup capable of satisfactorily exhibiting color and hue of a printing layer formed on a cup surface, and a method of manufacturing the same.
Stainless steel double cup of the present invention is made of a stainless material, the inner cup forming the inside of the cup and the outer portion forming the outside of the cup, and the cup portion between the inner portion and the outer portion formed of a space portion; A first coating layer coated on the outer surface; A printing layer formed on the first coating layer; It provides a stainless steel double cup comprising a.
The first coating layer is an off-white series, a second coating layer made of a coating layer is formed on the outside of the first coating layer, the second coating layer is made of a pearl pigment.
In addition, the present invention comprises the steps of manufacturing a double cup made of stainless steel and the inner portion forming the inside of the cup and the outer portion forming the outside of the cup and the space portion between the inner portion and the outer portion; Painting a first coating layer on an outer side of the double cup; Firing the first coating layer; Forming a printing layer on the dried first coating layer; It provides a stainless steel double cup manufacturing method comprising a.
In the first coating layer coating step, an off-white pigment is used. After the first coating layer firing step, a second coating layer coating step made of a pearl pigment is further performed to make the texture of the printing layer smooth and colorful.
Description
본 발명은 스테인리스 이중 컵에 관한 것으로서, 더욱 상세하게는 컵 표면에 형성되는 인쇄층의 색채 및 색조를 양호하게 나타낼 수 있는 스테인리스 이중 컵 및 그 제조방법에 관한 것이다.The present invention relates to a stainless steel double cup, and more particularly, to a stainless steel double cup and a method of manufacturing the same that can exhibit the color and color tone of the printing layer formed on the cup surface.
일반적으로 음료나 차(茶) 등을 마시기 위하여 컵이 사용되고 있으며, 컵은 음료나 차의 종류 및 특성에 따라서 여러 가지 소재를 이용하여 다양한 모양으로 제작되고 있다.In general, a cup is used to drink a drink or tea, and the cup is manufactured in various shapes using various materials according to the type and characteristics of the drink or tea.
이러한 컵 중에서 컵의 벽을 이중으로 형성한 이중 컵이 알려져 있는데, 이 이중 컵은 컵의 내부를 이루는 내측부와 컵의 외부를 이루는 외측부로 2겹으로 형성하면서 내측부와 외측부 사이는 공간부로 이루어진 구조로 제작된다.Among these cups, a double cup having a double cup wall is known. The double cup is formed in two layers, an inner part forming the inside of the cup and an outer part forming the outside of the cup, and a space part between the inner part and the outer part. Is produced.
이러한 구조로 인하여 내측부가 외부 온도의 영향을 직접적으로 받지 않도록 하여 컵에 담긴 내용물의 온도를 상당시간동안 유지할 수 있도록 되어 있다.Due to this structure, the inner part is not directly affected by the external temperature, so that the temperature of the contents contained in the cup can be maintained for a considerable time.
이중 컵은 금속재료를 사용하여 제조하는 경우가 많은데, 금속재료를 이용할 경우 통상적으로 스테인리스를 이용하여 이중 컵을 제조하게 된다.The double cup is often manufactured using a metal material, and when using a metal material, a double cup is usually manufactured using stainless steel.
스테인리스 이중 컵은 파손될 우려가 거의 없고 보관 및 휴대가 편리한 장점 등으로 인하여 다양한 용도 및 디자인으로 제조되어 판매되고 있다. 이 스테인리스 이중 컵은 대부분의 경우 외측부에 다양한 무늬, 문자, 그림 등으로 이루어진 인쇄층을 전사인쇄 방식으로 형성하게 된다.Stainless steel double cups are manufactured and sold in a variety of applications and designs due to the advantages of little damage and easy storage and portability. In most cases, this stainless steel double cup is formed by a transfer printing method on the outside of a printed layer made of various patterns, letters, and pictures.
그러나 이와 같이 스테인리스 이중 컵 표면에 인쇄층을 형성할 경우, 금속면에 직접 인쇄하는 방식이므로 인쇄층의 색채가 이질적으로 보일 수 있고, 시각적으로 색조가 명확하게 나타나지 않을 수 있다.However, when the printing layer is formed on the stainless double cup surface as described above, since the printing method is directly printed on the metal surface, the colors of the printing layer may be heterogeneous, and the color may not be clearly seen visually.
또한 종래의 스테인리스 이중 컵은 금속재료의 특성상 도자기의 질감이 나타나도록 할 수 없는 단점도 있다.In addition, the conventional stainless steel double cup has a disadvantage that the texture of the ceramics can not appear due to the nature of the metal material.
본 발명은 상기한 바와 같은 종래의 문제점을 해결하기 위하여 제안된 것으로서, 본 발명의 목적은 컵 표면에 형성되는 인쇄층의 색채 및 색조를 양호하게 나타낼 수 있는 스테인리스 이중 컵 및 그 제조방법을 제공하는데 있다.The present invention has been proposed to solve the conventional problems as described above, and an object of the present invention is to provide a stainless double cup and a method of manufacturing the same that can exhibit the color and color tone of the printing layer formed on the surface of the cup well have.
본 발명이 제안하는 스테인리스 이중 컵은 스테인리스 재질로 이루어지면서 컵의 내부를 이루는 내측부와 컵의 외부를 이루는 외측부 및 이들 내측부와 외측부 사이가 공간부로 이루어진 이중 컵 본체; 상기 외측부 표면에 도장된 제1도장층; 상기 제1도장층에 형성된 인쇄층; 을 포함하는 스테인리스 이중 컵을 제공한다.The stainless double cup proposed by the present invention comprises a double cup body made of stainless steel and having an inner portion forming the inside of the cup and an outer portion forming the outside of the cup and a space portion between the inner portion and the outer portion; A first coating layer coated on the outer surface; A printing layer formed on the first coating layer; It provides a stainless steel double cup comprising a.
상기 제1도장층은 미색계열로 이루어지고, 제1도장층의 외측으로는 코팅층으로 이루어진 제2도장층이 형성되며, 이 제2도장층은 펄 안료로 이루어진다.The first coating layer is off-white, a second coating layer made of a coating layer is formed on the outside of the first coating layer, the second coating layer is made of a pearl pigment.
또한 본 발명은 스테인리스 재질로 이루어지면서 컵의 내부를 이루는 내측부와 컵의 외부를 이루는 외측부 및 이들 내측부와 외측부 사이가 공간부로 이루어진 이중 컵을 제조하는 단계; 상기 이중 컵의 외측부에 제1도장층을 도장하는 단계; 상기 제1도장층을 소성하는 단계; 상기 건조된 제1도장층에 인쇄층을 형성하는 단계; 를 포함하는 스테인리스 이중 컵 제조방법을 제공한다.In addition, the present invention comprises the steps of manufacturing a double cup made of stainless steel and the inner portion forming the inside of the cup and the outer portion forming the outside of the cup and the space portion between the inner portion and the outer portion; Painting a first coating layer on an outer side of the double cup; Firing the first coating layer; Forming a printing layer on the dried first coating layer; It provides a stainless steel double cup manufacturing method comprising a.
상기 제1도장층 도장단계에서는 미색계열의 안료가 사용된다. 상기 제1도장층 소성단계 후 인쇄층의 질감을 부드럽고 화려하게 할 수 있도록 제2도장층 도장단계가 더 행하여지며, 이 제2도장층 도장단계에서는 펄 안료가 사용된다.In the first coating layer coating step, an off-white pigment is used. After the first coating layer firing step, the second coating layer coating step is further performed to make the texture of the printing layer smooth and colorful. In this second coating layer coating step, a pearl pigment is used.
본 발명에 의한 스테인리스 이중 컵은 외측부에 미색계열의 제1도장층이 도장되어 인쇄층의 색채를 이질감 없이 나타낼 수 있으면서 인쇄층의 색조를 명확하게 나타낼 수 있어 제품의 품질을 높일 수 있다.The stainless steel double cup according to the present invention may be coated with an off-white first coating layer on the outer side to express the color of the printed layer without dissimilarity and to clearly indicate the color tone of the printed layer, thereby improving product quality.
또한 미색계열의 제1도장층으로 인하여 스테인리스 재질을 도자기 질감으로 표현할 수 있으므로 고급스런 이미지를 연출할 수 있다.In addition, because of the first coating layer of the off-white series, stainless steel material can be expressed as a porcelain texture, thereby producing a luxurious image.
도 1은 본 발명에 따른 스테인리스 이중 컵 제조방법에 따른 공정도이다.
도 2는 본 발명의 스테인리스 이중 컵을 제작하기 위하여 이중 컵이 제작된 초기 상태의 단면도이다.
도 3은 도 1의 공정에 따라서 본 발명의 스테인리스 이중 컵이 제조되는 과정을 순차적으로 도시한 단면도이다.
도 4는 도 1의 공정에 따라서 제조된 본 발명의 스테인리스 이중 컵의 사시도이다.1 is a process chart according to the stainless double cup manufacturing method according to the present invention.
2 is a cross-sectional view of an initial state in which a double cup is manufactured to manufacture a stainless double cup of the present invention.
3 is a cross-sectional view sequentially illustrating a process of manufacturing a stainless double cup of the present invention according to the process of FIG.
4 is a perspective view of a stainless double cup of the present invention made according to the process of FIG.
이하, 본 발명의 바람직한 실시 예를 첨부한 도면을 참조하여 더욱 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in more detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 스테인리스 이중 컵 제조방법에 따른 공정도이고, 도 2는 본 발명의 스테인리스 이중 컵을 제조하기 위하여 제작된 이중 컵의 초기 상태의 단면도이며, 도 3은 도 1의 공정에 따라서 본 발명의 스테인리스 이중 컵이 제조되는 과정을 순차적으로 도시한 단면도를 나타낸다.1 is a process chart according to a stainless double cup manufacturing method according to the present invention, Figure 2 is a cross-sectional view of the initial state of a double cup manufactured to manufacture a stainless double cup of the present invention, Figure 3 is in accordance with the process of FIG. Sectional drawing which shows the process which manufactures the stainless steel double cup of this invention sequentially is shown.
도시된 바와 같이 본 발명에 따른 스테인리스 이중 컵을 제조하기 위하여 도 2에서와 같이 스테인리스를 이용하여 상부가 개방부로 이루어지고 컵의 내부를 이루는 내측부(2)와 컵의 외부를 이루는 외측부(4) 및 이들 내측부와 외측부 사이가 공간부(6)로 이루어진 이중 컵을 제조하는 단계(P1)를 통하여 스테인리스 이중 컵을 제조한다.As shown in order to manufacture a stainless double cup according to the invention as shown in Figure 2 using the stainless steel as shown in the upper portion and the inner portion (2) forming the inside of the cup and the outer portion (4) forming the outside of the cup and A stainless double cup is produced through the step P1 of manufacturing a double cup between these inner and outer portions of the
상기 이중 컵 제조단계(P1)에서는 이 기술 분야에서 통상적으로 사용되고 있는 방법으로 제조할 수 있으므로 상세한 설명은 생략한다.In the double cup manufacturing step (P1) it can be manufactured by a method commonly used in the art, so a detailed description thereof will be omitted.
이렇게 스테인리스 재질로 이루어진 이중 컵이 제작되면 상기 이중 컵의 외측부(4)에 제1도장층(8)을 도장하는 단계(P2)를 행한다.When a double cup made of stainless steel is manufactured as described above, a step (P2) of coating the
상기 제1도장층(8)은 이중 컵의 외측면에 인쇄층을 형성하기 전에 바탕색을 형성하는 것으로서, 이러한 제1도장층(8)으로 인하여 이후에 이 제1도장층에 인쇄층을 형성하면 인쇄층의 색채가 이질적으로 보이지 않을 뿐만 아니라 시각적으로 색조를 명료하게 나타낼 수 있다.The
이와 같은 제1도장층(8)의 도장은 다양한 색깔로 이루어질 수 있는데, 상기와 같은 특징을 극대화 할 수 있도록 본 발명에서는 미색계열의 안료를 이용하여 제1도장층(8)을 형성한다.The coating of the
이렇게 제1도장층(8)을 미색계열로 형성하면 이중 컵의 외형을 도자기 느낌의 질감과 유사한 질감이 나타나게 할 수 있다. 또 후 공정으로서 뒤에서 상세하게 설명되는 인쇄층형성단계를 통하여 제1도장층(8)의 표면에 인쇄층을 형성하면 이 인쇄층의 색채 및 색조를 더욱 명료하고 명확하게 표현할 수 있다.When the
즉, 미색계열로 제1도장층(8)을 형성하면 인쇄층이 어떠한 색깔로 이루어져도 인쇄층의 색채를 이질감 없이 나타낼 수 있고, 인쇄층의 색조를 명확하게 나타낼 수 있다.That is, when the
상기와 같이 제1도장층 도장단계(P2)를 통하여 제1도장층(8)이 도포된 이중 컵은 소성로 등에 넣고 150℃~250℃의 온도에서 대략 20~40분 정도의 소성단계(P3)를 행하면 제1도장층(8)의 도막이 건조 및 소성 되면서 이중 컵의 외측부(4)에 고착된다.(도 3a 참조)The double cup coated with the
이때 상기 온도조건 및 시간조건이 설정치 하한 값보다 낮으면 제1도장층(8)이 외측부(4)에 잘 고착되지 않고, 상한 값보다 높으면 제1도장층(8)이 연소되어 소멸될 수 있으므로 상기 조건으로 진행하는 것이 바람직하다.At this time, if the temperature condition and the time condition are lower than the set value lower limit value, the
그리고 제1도장층(8)이 완전히 건조되면 제1도장층(8)의 도장상태를 확인한다. 이 제1도장층 도장단계(P2)는 한 번의 공정으로 이루어질 수도 있고 2번 이상의 공정으로 이루어질 수도 있다.When the
이렇게 제1도장층(8)의 소성이 완료되면 제1도장층(8)에 제2도장층(10)을 형성하는 제2도장층 도장단계(P4) 행한다.When the firing of the
상기 제2도장층(10)은 다음 공정으로 형성될 인쇄층의 질감을 부드럽고 화려하게 할 수 있도록 하기 위한 것으로서, 투명 또는 반투명한 안료가 사용될 수 있다 . 본 발명에서는 제2도장층(10)을 형성할 때 사용되는 안료로 펄 안료가 사용된다.The
펄 안료는 여러 층의 얇은 막이 겹쳐 있는 구조를 하고 있으므로 세분되어진 펄 안료의 각각의 층에 빛이 비추면 각 층마다 청색 빛이 강한 색만을 반사시키거나 적색 빛이 강한 색만을 반사시켜서 각층마다 미묘한 빛의 선택 흡수 또는 반사로 광채가 변하는 특성을 갖는다.Since the pearl pigment has a structure in which multiple layers of thin films overlap, when light shines on each of the subdivided pearl pigments, each layer reflects only the strong color of blue light, or only the strong color of red light is subtle. Selective absorption or reflection of light has the property of changing its brilliance.
따라서 제2도장층(10)이 펄 안료로 이루어짐으로서 그 표면에 인쇄될 인쇄층의 고품질화 및 부드러운 느낌을 얻을 수 있고, 그 저면에 형성된 제1도장층(8)과의 조합에 의하여 인쇄층을 더욱 화려하게 해주면서 새로운 색채효과가 발현되어 이중 컵의 미감을 증진시킬 수 있다.Therefore, since the
상기와 같이 제2도장층 도장단계(P4)를 행하여 제1도장층(8)에 제2도장층(10)이 도포되면, 컵을 소성로 등에 넣어 280℃~320℃의 온도에서 대략 1~3분 정도의 소성단계(P5)를 행한다. 그러면 제2도장층(10)의 도막이 건조 및 소성 되면서 제1도장층(8) 외측에 제2도장층(10)이 코팅된다.(도 3b 참조)When the
이때 상기 온도조건 및 시간조건이 설정치 하한 값보다 낮으면 제2도장층(10)이 제1도장층(10)에 잘 고착되지 않고, 상한 값보다 높으면 제2도장층(10)이 연소되어 소멸될 수 있으므로 상기 조건에서 진행하는 것이 좋다.At this time, if the temperature condition and time condition are lower than the set value lower limit value, the
그리고 제2도장층(10)이 완전히 소성되면 제2도장층(10)의 도장상태를 확인하여 수정 및 보완할 부분이 없는지 검사 한다.When the
이와 같이 제1도장층(8)의 표면에 제2도장층(10)이 형성되면 인쇄층형성단계(P6)를 행하여 제2도장층(10)에 인쇄층(12)을 형성한다.As described above, when the
상기 인쇄층(12)은 다양한 무늬, 문자, 그림 등으로 이루어지며, 색깔도 다양하게 이루어진다.The printed
인쇄층형성단계(P6)를 통에서 형성되는 인쇄층(12)은 전사지를 이용한 전사인쇄방식 또는 안료 등을 이용한 직접인쇄방식 등으로 형성할 수 있다.The
전사인쇄 및 직접인쇄는 인쇄분야에서 통상적으로 사용하는 방법이 적용될 수 있고 그 이외의 방법으로 인쇄층을 형성하여도 무방하다.Transfer printing and direct printing may be applied to a method commonly used in the printing field, and the printing layer may be formed by other methods.
이와 같이 이중 컵의 표면에 인쇄층(12)이 형성되면 소성단계(P7)를 행하게 되는데, 이때 인쇄층(12)이 형성된 이중 컵을 소성로 등에서 200℃~240℃의 온도조건에서 대략 2~4분정도를 소성시키면 인쇄층(12)이 제2도장층(10)에 고착된다.(도 3c 참조)When the
이때 상기 온도조건 및 시간조건이 설정치 하한 값보다 낮으면 인쇄층(12)이 제2도장층(10)에 잘 고착되지 않고, 상한 값보다 높으면 인쇄층(12)이 연소되어 소멸될 수 있으므로 상기 조건에서 진행하는 것이 좋다.At this time, if the temperature and time conditions are lower than the set value lower limit value, the printed
이와 같이 인쇄층(12)이 형성되면 이중 컵의 제조가 완료되며, 필요하면 도 4에서와 같이 손잡이(14)와, 컵의 개방부에 분리 가능하게 안착되면서 주출구(16)가 형성된 뚜껑(18)을 더 제공할 수도 있다.When the printed
상기 공정에서는 제1도장층(8)에 제2도장층(10)을 도장하고, 이 제2도장층(10)에 인쇄층(12)을 형성하는 것으로 설명하였지만, 이에 한정되는 것은 아니고 제2도장층 도장단계(P4) 및 소성단계(P5)를 생략하여 제2도장층(10)을 생략하고 제1도장층(8)에 인쇄층(12)을 형성하는 방법으로 이중 컵을 제조할 수도 있다.In the above process, the
상기에서는 본 발명의 바람직한 실시예가 예시를 목적으로 설명되어 있으나 이에 제한되지는 않으며, 특허청구범위와 발명의 상세한 설명 및 첨부한 도면의 범위 내에서 여러 가지로 변형하여 실시하는 것도 가능하다.While the preferred embodiments of the present invention have been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
2: 내측부 4: 외측부
6: 공간부 8: 제1도장층
10: 제2도장층 12: 인쇄층
14: 손잡이 16: 주출구
18: 뚜껑2: inner part 4: outer part
6: space part 8: 1st coating layer
10: second coating layer 12: printing layer
14: handle 16: outlet
18: lid
Claims (8)
상기 외측부 표면에 도장된 제1도장층;
상기 제1도장층에 형성된 인쇄층;
을 포함하는 스테인리스 이중 컵.A double cup body made of stainless steel and having an inner portion forming the inside of the cup and an outer portion forming the outside of the cup and a space portion between the inner portion and the outer portion;
A first coating layer coated on the outer surface;
A printing layer formed on the first coating layer;
Stainless steel dual cup containing.
상기 제1도장층은 미색계열로 이루어진 것을 특징으로 하는 스테인리스 이중 컵.The method according to claim 1,
Stainless steel double cup, characterized in that the first coating layer made of off-white series.
상기 제1도장층의 외측으로는 코팅층으로 이루어진 제2도장층이 더 형성되는 것을 특징으로 하는 스테인리스 이중 컵.The method according to claim 1,
Stainless steel double cup, characterized in that the second coating layer consisting of a coating layer is further formed on the outside of the first coating layer.
상기 제2도장층은 펄 안료로 이루어진 것을 특징으로 하는 스테인리스 이중 컵.The method according to claim 3,
Stainless steel double cup is characterized in that the second coating layer is made of a pearl pigment.
상기 이중 컵의 외측부에 제1도장층을 도장하는 단계;
상기 제1도장층을 소성하는 단계;
상기 소성 완료된 제1도장층에 인쇄층을 형성하는 단계;
를 포함하는 스테인리스 이중 컵 제조방법.Manufacturing a double cup made of stainless steel and having an inner part forming the inside of the cup and an outer part forming the outside of the cup and a space part between the inner part and the outer part;
Painting a first coating layer on an outer side of the double cup;
Firing the first coating layer;
Forming a printing layer on the calcined first coating layer;
Stainless steel double cup manufacturing method comprising a.
상기 제1도장층 도장단계에서는 미색계열의 안료가 사용되는 것을 특징으로 하는 스테인리스 이중 컵 제조방법.The method according to claim 5,
Stainless steel double cup manufacturing method, characterized in that the off-white pigment is used in the first coating layer coating step.
상기 제1도장층 소성단계 후 코팅층으로 이루어진 제2도장층 도장단계가 더 행하여지는 것을 특징으로 하는 스테인리스 이중 컵 제조방법.The method according to claim 5,
Stainless steel double cup manufacturing method characterized in that the second coating layer coating step consisting of a coating layer after the first coating layer firing step is further performed.
상기 제2도장층 도장단계에서는 펄 안료가 사용되는 것을 특징으로 하는 스테인리스 이중 컵 제조방법.The method according to claim 7,
In the second coating layer coating step, a stainless steel double cup manufacturing method, characterized in that the pearl pigment is used.