KR200282228Y1 - Protect panel for ballistic and stab attack - Google Patents

Abstract

The present invention protects the human body from bullets by preventing penetration of bullets fired from firearms such as pistols and rifles, which minimizes the use of expensive fabrics pre- filed by the present applicant to reduce weight and maximize defense. On the front of the plate was added a sword plate that protects the human body from attacks from weapons such as knives, awls, bamboo spears, etc., which have a relatively sharp but sharp end, but with a sharp end. Combination consists of a STAB RESISTANCE PANEL that prevents penetration or impact by the blade or tip to the human body and a BALLISTIC RESISTANCE PANEL that absorbs and disperses the impact to the human body by bullets having a high speed impact force. Probe and bulletproof panel characterized in that it has a function of both a sword and a bullet-proof at the same time (PROTECT PANEL FO R BALLISTIC AND STAB ATTACK).

Thus, the anti-glare and bullet-proof panel of the present invention has a silol and cotton shape in which a plurality of aromatic polyamide-based woven fabrics 41 and aromatic polyamide-based fibers or high-density polyethylene films are woven in the form of a mesh, which is a design filed by the present applicant. Felt (50) consisting of a shock-absorbing member in which a narrow aromatic polyamide-based fiber or a high-density polyethylene film is forced between the nets and a plurality of aromatic polyamide-based woven fabric (43) are sewn in order to integrate A plurality of high density polyethylene films 44 laminated to disperse the impact energy and the front plate 46 and a rear plate 45 which minimizes frictional heat and deformation sewn by the plurality of aromatic polyamide-based woven fabrics. In the body armor ballistic plate 40 is formed integrally in the order of, the polyamide on the front surface of the ballistic plate 40 Sand of the size corresponding to sandpaper 100 to 500 after applying the resin-based adhesive (61) to any one surface of the woven fabric 41 or a high-density polyethylene woven fabric or a woven fabric having an equivalent or higher strength ( 62) is projected onto the applied resin-based adhesive 61, characterized in that it consists of 5-12 sheets in a row overlapping the inspection plate 60 adhered without gaps.

The sword and bulletproof panel 100 is integrated by being enclosed by a separate jacket pocket and inserted into the panel insertion portion as a part of a component forming a body armor or a body armor.

Description

PROTECTION PANEL FOR BALLISTIC AND STAB ATTACK}

The present invention relates to a sword and body armor that protects the human body from attack by firearms such as bullets or weapons such as swords and spears, and more specifically, firearms such as pistols and rifles among the components constituting the sword and body armor. BALLISTIC RESISTANCE PANEL, which protects the human body from firearms by preventing bullet penetration, and attacks from weapons such as knives, awls, bamboo spears, etc., which have a relatively slow but sharp edge compared to the speed of the bullet. PROTECT PANEL PANEL FOR BALLISTIC AND STAB ATTACK, characterized in that the combination of the stab resistance panel to protect the human body in a row to have a function of both the sword and bulletproof at the same time will be.

In general, body armor to protect the human body from firearms is composed of a garment (Garment), ballistic plate and panel (Panel Panel Covering) and a bulletproof plate (Plate), ballistic plate, the core component of these body armor is the most widely recognized internationally Manufactured in accordance with the National Body Institute's National Police Body Armor Testing Standard (NIJ 0101.03) and HP WHITE LAB. Product testing and results from the competent test institutes such as the company to determine whether the compliance to the above standards are used.

In addition, a lot of sword suits and cushion suits are manufactured to protect the human body when attacked by weapons with sharp tips such as knives, awls, bamboo shoots, etc. In the well-known one in which layers of carbon fiber cloth are laid in layers between the outer skin and the inner skin where the male and female magic tapes are formed on the front and front of the vest, as shown in FIG. It has a configuration in which a braided plate in which a plurality of pieces of fiber reinforced plastic (FRP) is attached to the attachment fabric using an adhesive instead of the rubber plate 11 or the rubber plate is embedded between inner surfaces of the central portion of the carbon fiber cloth, It is easy to manufacture when manufacturing protective clothing by making cloth fabric, and it can be bent by the characteristics of rubber material. It is possible, but the movement of the body is inconvenient due to the weight of the rubber material, and the weight increases further when using the protective cloth with the rubber plate inserted as a fabric, which has the disadvantage of limiting the behavior of the human body when fighting with the other party. In the case of the self-defense vest of No. 91-009505, the neck insertion hole 23 and the arm insertion hole 24 are formed as shown in FIG. Form a vest body (A) to cover the shoulder and the chest by the squeezed stretch piece (21) and the lower portion of each of the stretched fabric (26) in the lower part of the piece (22) and then several small pieces on the surface Self-defense piece (27) is formed by attaching the casing so that the lower end overlaps the outside bar, when the person wearing the self-protection vest stabs the chest from the front with a sharp knife, awl or bamboo spear, etc. It is protected by a large piece of armor, but it is attached stepwise to the surface of the span fabric. When the slip is generated in the small self-defense piece due to the stabbing force of the other side and the space is formed, there is a disadvantage in that the weapon penetrates into the space formed between the self-defense piece and the self-defense piece and injuries the body. In case of stabbing, a small piece of armor attached to the outer side of the vest can be heard while penetrating the span fabric and causing serious injury to the body.

As described above, there are many bulletproof plates to protect the human body from fast-fired bullets fired from weapons such as swords, awls, bamboo spears, sharp edged weapons, or components such as sword plates, pistols, and rifles. Bulletproof plates that can block bullets can harm the human body by knives or spears that have sharp blade edges. Conversely, high speed bullets can penetrate or harm spears or swords that can block bullets. There is no sword and bulletproof panel that simultaneously possesses both a sword and a bulletproof function satisfying each offensive weapons. Therefore, according to the urgent situation or purpose of dealing with the situation, the detection plate and the bulletproof plate are used separately, and in the situation where the firearms and the weapons are used at the same time, there is a problem that the task must be carried out while taking a considerable risk.

For the above problems, the applicant has been manufactured according to the National Police Agency's National Body Examination Standard (NIJ 0101.03) of the National Institute of Justice (NIJ 0101.03) through Korean Patent Application No. 1999-0007174 and as shown in Table 1 HP, the jurisdiction WHITE LAB. As can be seen in the accompanying FIG. 4, which has been qualified by the company, a plurality of aromatic polyamide-based woven fabrics 41 and aromatic polyamide-based fibers or high-density polyethylene films are woven in sills and cotton-like woven meshes. Felt 50 consisting of a shock absorbing member in which a multi-aromatic polyamide fiber or a high density polyethylene film is press-fitted between the nets and a plurality of aromatic polyamide woven fabrics 43 are sewn in order to integrate the front plate (46) and a plurality of high density polyethylene films (44) stacked to disperse impact energy, and a rear plate (45) to minimize frictional heat and deformations sewn with a plurality of aromatic polyamide-based woven fabrics. The ballistic plate for bulletproof body armor 40, characterized in that the unit consists of the first election.

Aromatic Polyamide Woven Fabric (100%) High Density Polyethylene (100%) A pre-ballistic plaque NIJ Standard ⅢA ⅢA ⅢA Where to use and basis National Police Agency 2. H.P.WHITE LAB. TEST Special Forces 2. Recommended by the manufacturer of the material 3. Military unit self-test National Police Agency, Special Forces 2. H.P.WHITE LAB. TEST How to make DUPONT A363F 36-ply (National Police Agency standard) A363F1. Weight: 208 g / m 2. Density: 28 × 28 (all / inch) DSM Corporation SB2 34-ply (Special Forces Standard) SB21. Weight: 160 g / m 2. Density: film Self-developed 25 layers (Police Office, Special Forces Standard) PARA-ARAMID1. Weight: 220g / m 2. Density: 30 × 30 (all / inch) SB2: 160g / ㎡PARA-ARAMID Felt: 613g / ㎡ (1 layer) Weight (Kg / ㎡) 36 ply × 208 g / ㎡ = 7.49 34 layers × 160g / ㎡ = 5.44 12 ply × 220g / ㎡ = 2.6212 ply × 160g / ㎡ = 1.921 ply × 613g / ㎡ = 0.615.17 weight 7.49 / 5.17 × 100 = 144.9% Approximately 45% heavier than the present invention 5.44 / 5.17 × 100 = 105.2% Approximately 5% heavier than the present invention This product is 100% (standard) lightest thickness This invention is the thinnest Fit This invention is the thinnest, softest and comfortable to wear price usually Slightly expensive cheap

However, as described above, the antiballistic ballistic plate previously filed by the present applicant also has a defensive ability when attacking a human body by firearms, but still has an unsafe problem when attacked by a knife or a spear having a sharp end.

The suit usually consists of a garment, a plate and its shell, which is a key part of the suit and is the most widely recognized internationally recognized National Institute of Justice (NIJ). It is manufactured in accordance with the Police Barrier Suit Test Criteria (NIJ 0115.00).

For reference, the NIJ's criteria for sword plates refer to the common threats of various swords, their sharpness, pointedness, style, handle and blade design. Depending on the blade design, the attacking angle, the physical condition of the attacker, and the skill of the attacker, the NIJ classifies the type of sword suit as the type of threat environment. Pertaining to machined ends or blades in good condition, generally regarded as the "Edged Blade" class, and for weapons such as the blades of low quality being blunt or spikes, usually the "Spike" class. Classified into two different protection classes, the sword suit within each of these classes is further divided into three protection levels as follows.

Level 1 Sword Suit: A low-level sword suit suitable for wear.

Level 2 Sword Suit: Garment of a normal work suit suitable for wearing.

Level 3 Sword Suit: A high level sword suit worn under high risk situations.

Of course, the sword suit method should protect the wearer from penetrating from a weapon having a knife or a sharp blade or a sharp tip without being limited to the wearer's movement.

There are three levels of defense against NIJ's sword suits as shown in Table 2 below. These levels are derived from the distribution of energy applied by a normal adult male through several stab actions under the 1997-1999 PSDB program, with the lowest level being 85% of that energy, the next level being 90%, The highest level is 96% of its energy. The energy level in Table 2, or "E 1", is in accordance with the above and in this condition up to 7 mm of blade and spike penetration is allowed. The test standard calls for an overtest where the blade or spike's kinetic energy is increased by 50%. This higher energy condition, called "E 2", means that penetration of blades or spikes up to 20 mm is not possible. Is allowed. This overtest ensures safety margins in the design of the suit.

Protect Levels "E 1" Strike Energy "E 2" Overtest S. Energy One 17.7 ± 0.36 26.6 ± 0.44 2 24.3 ± 0.44 36.9 ± 0.51 3 31.7 ± 0.44 47.9 ± 0.59

※ Unit: ft-lbf

In the manufacture of ballistic plates and sword plates, the defense against knives or bullets must be good, and the deformation of the plates must be considered.In other words, the ballistic plates minimize damage from bullets even if bullets do not penetrate the body. It should be taken into account that the deformation to the rear should be as small as possible so as not to avoid it. In addition to this, there is a problem in that it must be lighter, have a good fit, and have to meet various conditions such as low price.

The present invention has been devised to solve such a problem in the prior art, by combining the plurality of anti-ballistic plate of the present invention on the front of the ballistic body ballistic plate of the applicant filed by the present applicant equipped with a defense against the sword and bulletproof at the same time The purpose is to provide panels for sword and ballistic protection.

According to a form of the present invention for achieving the above object, in the ballistic body ballistic plate of the invention proposed by the present applicant, an aromatic polyamide-based woven fabric 41 or a high-density polyethylene woven fabric on the front surface of the ballistic plate or After the resin-based adhesive is applied to any one of the woven fabrics having the same or higher strength, sandproofing sand of the size of 100 to 500 sandpaper is projected onto the applied resin-based adhesive, and the inspection plate is closely bonded. Provided is a panel for a sword and a bulletproof ball, characterized in that is made by overlapping 5 to 12 sheets in a row.

1 is an enlarged perspective view of a conventional rubber plate extract,

Figure 2 is a perspective view showing a vest and a hoshin piece of the prior art,

3 is an explanatory diagram showing a process of absorbing and stopping a bullet impact by a ballistic plate;

Figure 4 is a longitudinal cross-sectional view showing a laminated state of the ballistic plate of the invention proposed by the applicant,

5 is an enlarged perspective view showing a felt forming one component in FIG.

Figure 6 is a longitudinal cross-sectional view showing a configuration for a single check plate of the present invention,

FIG. 7 is an explanatory view showing a deformation state of the inspection plate at the time of attack by the sharp weapons with respect to the inspection plate in the state where the plurality of inspection plates of FIG. 6 are closely arranged in a row; FIG.

FIG. 8 is an enlarged longitudinal sectional view showing a stacking state of the inspection and bulletproof panel of the present invention, which is composed of a plurality of sheets of the inspection plate of FIG. 6 on a ballistic plate pre- filed by the present applicant;

FIG. 9 is a state diagram showing that the designed sword and bulletproof panel of FIG. 8 is inserted into the outer pocket and integrated into the panel body of the body armor.

<Description of the symbols for the main parts of the drawings>

40: ballistic plate 41,43: aromatic polyamide-based weaving fabric

44: high density polyethylene 45: front panel

46: backplane 50: felt

51: shock absorbing member 52: silol

60: detection plate 61: resin adhesive

62: sand 100: panel for bulletproof and bulletproof

B: weapon

DETAILED DESCRIPTION In order to achieve the above object, the present invention will be more clearly described with reference to the accompanying drawings.

In the following description of the present invention, if it is determined that the detailed description of the related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted. In addition, terms to be described below are terms defined in consideration of functions in the present invention, which may vary according to intention or custom of a user or an operator. Therefore, the definition should be made based on the contents throughout the specification.

According to the present invention, the anti-glare and bulletproof panel includes a silol in which a plurality of aromatic polyamide-based woven fabrics 41 and aromatic polyamide-based fibers or high-density polyethylene films are woven in a mesh form, as shown in FIG. 8 of the accompanying drawings. Felt (50) and a plurality of aromatic polyamide-based woven fabric (43) composed of an impact-absorbing member in which cotton-like thin aromatic polyamide-based fibers or high-density polyethylene films are forced into the net are sewn in order, An integrated front plate 45 and a back plate minimizing frictional heat and deformation sewn by a plurality of high density polyethylene films 44 stacked to disperse impact energy and a plurality of aromatic polyamide-based woven fabrics ( In the ballistic body ballistic plate 40, characterized in that the body consisting of a sequence of 46), in front of the ballistic plate (40) It is comprised by attaching several sheets of the inspection plate 60 in a line.

Hereinafter, the present invention will be described in more detail with reference to FIGS. 3 to 9.

Figure 3 is an explanatory view showing a process of absorbing and stopping the impact of bullets by the ballistic plate, Figure 4 is a longitudinal cross-sectional view showing a stacking state of the ballistic plate of the invention proposed by the applicant, Figure 5 is Figure 6 is an enlarged perspective view showing a felt forming one component, Figure 6 is a longitudinal cross-sectional view showing a configuration for a single sheet of the invention of the present invention, Figure 7 is a state in which the plurality of sheets of the check plate of Figure 6 in close contact It is an explanatory view showing the deformation state of the inspection plate during the attack by the sharp weapons with respect to the inspection plate, Figure 8 is the inspection of the present invention made by configuring a plurality of inspection plates on the ballistic plate filed by the applicant 9 is a longitudinal cross-sectional view showing an enlarged state of the bulletproof panel, and FIG. 9 is a panel of a body armor after the designed sword and bulletproof panel of FIG. 8 is inserted into an outer pocket and integrated. Using a state diagram showing that which is used to insert a.

3 is an explanatory diagram illustrating a process of absorbing and stopping the impact of a bullet by a ballistic plate. The bullet 30, which is fired from the gun and starts from the muzzle, is hot due to friction with air. The impact energy is diffused in all directions, and the progress of the bullet 30 is suppressed by the ballistic plate 31, and as it is gradually compressed as shown in the figure, the progression of the ballistic plate 31 is stopped. The ballistic plate 31 should have a characteristic that absorbs the impact energy well and withstands high temperature well and minimizes the deformation of the ballistic plate 31 due to the impact energy so that the ballistic plate 31 does not penetrate even if the ballistic plate is not penetrated. It should have sufficient tensile strength so as not to adversely affect the human body.

4 and 5 are related to the ballistic plate 40 of the present applicant with the above-described characteristics, the plurality of aromatic polyamide-based woven fabric 41 and the aromatic polyamide-based fiber or high-density polyethylene film in the form of a mesh Felt (50) and a plurality of aromatic polyamide-based woven fabrics (43) composed of a shock absorbing member in which woven silol and cotton-like thin aromatic polyamide-based fibers or high-density polyethylene films are forcibly pressed between the nets are Minimizes frictional heat and deformations sewn in order by sewing the integrated front plate 45 and the plurality of high density polyethylene films 44 stacked to disperse the impact energy and the plurality of aromatic polyamide-based woven fabrics. To be made in the order of the back plate 46 is characterized in that it is configured integrally.

The characteristics of the felt 50 are shown in Table 3 below.

Aromatic polyamide High density polyethylene This invention 1. Weight More than 600g / ㎡ 400g / ㎡ or more 400 to 600 g / ㎡ 2. Thickness More than 3m / m More than 3m / m 3 to 3.5 m / m 3. Tensile strength (inclined / weft) More than 280Kg 350Kg or more 280-350Kg 4. Wheat degree 11 × 7

FIG. 6 shows one piece of the inspection plate 60 according to the present invention, wherein either one of an aromatic polyamide-based woven fabric 41 or a high-density polyethylene woven fabric or a woven fabric having a strength equivalent thereto or higher is selected. After applying the resin-based adhesive (61) on the sand sand of the size corresponding to the sandpaper 100-500 times projected onto the applied resin-based adhesive (61) is configured to adhere tightly.

In the above, the material of one sheet is 64 to 60% by weight of the aromatic polyamide-based woven fabric 41 or a high density polyethylene woven fabric or any one selected from the group consisting of woven fabrics having an equivalent or higher strength. 61) 1 to 2% by weight, sand (62) 35 to 38% by weight. The physical characteristics of the inspection plate configured as described above are shown in the following Table 4 through the test results of the Korea Yarn Textile Testing Institute, a nationally recognized inspection organization.

Test Item (Korean Standard) Test result Remarks Mixed use rate (KS K 0210) Aromatic Polyamide Fiber 100% -Test method: Quantitative mixing ratio, FTIR method-Except resin, only fabric is tested Balance discrimination (KS K0210) Mineral, Synthetic Rubber, Acrylic Resin -Test method: FTIR method Ash (KS K0215) 38.7% Density (KS K0511) Slope-55.2 Weft-50.2 -Standard: All / 5cm Weight (KS K0514) 423.4 g / ㎡ Tensile Strength (KS K0520) Tilt-474.6 Weft-317.9 -Test method: C.R.E. Strip method- Standard: kgf / 2.5cm

FIG. 7 shows the 5-12 sheets of the inspection plates 60 without being glued to each other as closely as possible, and then, when attacked by the weapon B having a sharp end, the inspection plates 60 installed by the plurality of sheets. As an explanatory diagram showing a process of transmitting a shock, when the weapon (B) applied from the attacker (not shown) touches the inspection plate 60, the impact energy due to the pressurization is immediately transmitted, especially the sharp end of the weapon (B). The enormous pressing force generated by the concentrated loads is gradually suppressed by the inspection plates 60 while being transmitted and progressed to the inspection plates 60. The pressing force concentrated at one point of the inspection plate 60 is gradually relaxed as it is transmitted to the rearviewed inspection plates successively. It becomes It is as if the bullets fired from the firearms are similar to those received by the ballistic plate upon impact on the ballistic plate, when the ballistic plate 40 is filed by the applicant who is addressed to the plurality of inspection plates 60. Defensive action completely eliminates the risk of injury to the human body.

In this regard, the anti-ballistic and bulletproof panel 100 of the present invention has the ballistic plate 40 pre- filed by the present applicant after the installation of 5-12 sheets of the inspection plate 60 in close contact with the front part as shown in FIG. 8. The sword and bulletproof panel 100 is not shown, but is enclosed by a separate jacket pocket to be configured integrally, and the panel is inserted as part of the components constituting the body armor or the sword suit as shown in FIG. 9. It is used by inserting into the part.

In accordance with the National Institute of Justice, the National Institute of Justice (NIJ), the National Police Juvenile Suit Test Standard (NIJ 0115.00), as described above, for the performance verification of the anti-ballistic and bulletproof panel 100 of the present invention configured as described above. HP, the jurisdiction testing institution of the NIJ Test request to WHITE LABORATORY INC. (Report No. 8245-03A, 8245-03B, 8245-03C) The NIJ criterion was satisfied.

The present invention may be variously modified and may take various forms, and only the specific embodiments thereof are described in the detailed description of the above design. It is to be understood, however, that the present invention is not limited to the specific forms referred to in the description, but rather includes all modifications, equivalents, and substitutions within the spirit and scope of the invention as defined by the appended claims. Should be.

As described above, the anti-glare and bullet-proof panel of the present invention must be a very excellent design that can have a user's comfort and at the same time have a bullet-proof effect.

Claims (3)

A plurality of aromatic polyamide-based woven fabrics 41 and silols in which aromatic polyamide-based fibers or high-density polyethylene films are woven in a mesh form and a thin, aromatic aromatic polyamide-based fiber or high-density polyethylene film are forced between the nets. Felt 50 composed of a press-fitted shock absorbing member and a plurality of aromatic polyamide-based woven fabrics 43 are sewn in sequence to form a high density of a plurality of sheets stacked to disperse the impact energy with the integrated front plate 45. Antiballistic ballistic plate (40) characterized in that the polyethylene film 44 and a plurality of aromatic polyamide-based weaving fabric sewn in the order consisting of the back plate 46 minimizes the frictional heat and deformation (miniformation) ), A panel for a sword and ballistic protection, characterized in that the ballistic plate (60) on the front of the ballistic plate 40 is in close contact with each other in a line. The method of claim 1, The inspection plate 60 is 100 to 500 times after applying the resin-based adhesive (61) to any one surface selected from among the aromatic polyamide-based woven fabric 41 or a high-density polyethylene woven fabric or a woven fabric having an equivalent strength A sandproof and bulletproof panel characterized in that the sand (62) of the size corresponding to the sand paper projected onto the applied resin-based adhesive (61) to adhere tightly. The method according to claim 1 or 2, The inspection plate 60 is 64 to 60% by weight of any one of the aromatic polyamide-based woven fabric 41 or a high density polyethylene woven fabric or a woven fabric having an equivalent strength, and the resin adhesive 61 1 to 2 A panel for anti-glare and ballistic prevention, characterized by consisting of 35% by weight to 35% by weight of sand (62).