KR102694948B1 - 도배풀 조성물 - Google Patents
도배풀 조성물 Download PDFInfo
- Publication number
- KR102694948B1 KR102694948B1 KR1020220101774A KR20220101774A KR102694948B1 KR 102694948 B1 KR102694948 B1 KR 102694948B1 KR 1020220101774 A KR1020220101774 A KR 1020220101774A KR 20220101774 A KR20220101774 A KR 20220101774A KR 102694948 B1 KR102694948 B1 KR 102694948B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- water
- based adhesive
- emulsifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
본 발명은 도배풀 조성물에 관한 것으로서, 보다 구체적으로는 전분을 증숙하는 과정을 생략하여 제조원가를 낮출 수 있고, 인체에 미치는 유해성을 없애며, 시공 후 풀자국, 부패 등으로 인한 얼룩을 방지할 수 있고, 장기간 보관에도 변질이 되지 않고 제품의 무게를 1/3 수준까지 줄일 수 있는 도배풀 조성물에 관한 것이다.
Description
본 발명은 도배풀 조성물에 관한 것으로서, 보다 구체적으로는 접착력이 우수하며, 전분을 증숙하는 과정을 생략하여 제조원가를 낮출 수 있고, 인체에 미치는 유해성을 없애며, 시공 후 풀자국, 부패 등으로 인한 얼룩을 방지할 수 있고, 장기간 보관에도 변질이 되지 않고 제품의 무게를 1/3 수준까지 줄일 수 있는 도배풀 조성물에 관한 것이다.
현재 사용되고 있는 밀가루 풀은 밀가루를 물에 혼합하고 적정한 온도로 익히는 증숙 과정을 거쳐 수분이 함유된 상태로 제조하여 사용하는데, 이러한 습식 밀가루 풀은 습식 상태이다 보니 부패하거나, 접착 품질이 저하되는 등 변질의 우려가 많아 유독성이 큰 공업용 약품, 예를 들어 황산, MIT 계열 방부제, 염화아연 등을 첨가하여 사용할 수 밖에 없다.
이러한 공업용 약품은 풀 제조시는 물론, 사용시에 인체에 심각한 풀독과, 부작용이 발생하지만, 대체품이 없어 수 십년간 사용한 결과 시공자(도배사)의 부작용 내지 후유증이 심각한 실정이다.
도배용 풀은 접착력과, 수분함유량, 습식인 상태에서 장시간 보관성 등이 있어야 하고, 시공하고 난 뒤에도 풀 시공자국으로 시공 후 하자처리를 해야하는 일이 종종 발생한다. 이러한 도배용 풀의 품질을 유지하며 유해성을 없애기 위해서는 증숙을 하지 않고, 공업용 약품을 사용하지 않으며, 접착 성능을 유지할 수 있는 도배용 풀의 개발이 필요한 실정이다.
본 발명은 종래 기술의 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 접착력이 우수하며, 전분을 증숙하는 과정을 생략하여 제조원가를 낮출 수 있고, 인체에 미치는 유해성을 없애며, 시공 후 풀자국, 부패 등으로 인한 얼룩을 방지할 수 있고, 장기간 보관에도 변질이 되지 않고 제품의 무게를 1/3 수준까지 줄일 수 있는 도배풀 조성물을 제공하는 것이다.
본 발명의 해결하고자 하는 과제는 이상에서 언급된 것들에 한정되지 않으며, 언급되지 아니한 다른 해결과제들은 아래의 기재로부터 당업자에게 명확하게 이해되어 질 수 있을 것이다.
상기한 목적을 달성하기 위하여 본 발명에 따른 도배풀 조성물은 폴리비닐아세테이트(PVA)와 메틸메타아크릴레이트와, 아크릴산과, 유화제로 구성되는 수성접착제 10~15중량부와; 카복시메틸셀룰로스나트륨 2~3중량부와; 에틸아크릴레이트와, 부틸아크릴레이트와, 2-하이드록시에틸아크릴레이트와, 유화제로 구성되는 제2 수성접착제 10~15중량부와; 수산화칼슘 0.1~0.5중량부와; 실리카흄 0.5~2.5중량부와; 물 100~150중량부;를 포함하되, 상기 수성접착제는 폴리비닐아세테이트(PVA) 100중량부를 기준으로 메틸메타아크릴레이트 20중량부와, 아크릴산 10중량부와, 유화제 3중량부를 포함하여 구성되고, 상기 제2 수성접착제는 에틸아크릴레이트 100중량부를 기준으로 부틸아크릴레이트 20중량부와, 2-하이드록시에틸아크릴레이트 20중량부와, 유화제 3중량부를 포함하여 구성되는 것을 특징으로 한다.
삭제
삭제
삭제
삭제
본 발명에 따른 도배풀 조성물에 의하면, 접착력이 우수하며, 전분을 증숙하는 과정을 생략하여 제조원가를 낮출 수 있고, 인체에 미치는 유해성을 없애며, 시공 후 풀자국, 부패 등으로 인한 얼룩을 방지할 수 있고, 장기간 보관에도 변질이 되지 않고 제품의 무게를 1/3 수준까지 줄일 수 있는 효과가 있다.
본 발명의 효과는 이상에서 언급된 것들에 한정되지 않으며, 언급되지 아니한 다른 효과들은 아래의 기재로부터 당업자에게 명확하게 이해되어 질 수 있을 것이다.
이하 본 발명의 바람직한 실시예에 대하여 구체적으로 설명한다.
본 발명을 설명함에 있어서, 관련된 공지기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명은 생략한다. 또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 판례 등에 따라 달라질 수 있다. 그러므로 그 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.
본 발명에 따른 도배풀 조성물은 기존의 물가루를 끓여서 제조하는 습식풀을 대체하기 위한 것으로서, 수성접착제 10~15중량부와, 증점제 2~3중량부와, 제2 수성접착제 10~15중량부와, 조절제 0.1~0.5중량부 및 물 100~150중량부를 포함하여 이루어진다.
본 발명의 수성접착제는 물을 용매로 사용하는 에멀젼 형태이기 때문에 안전하게 사용할 수 있으며, 유성접착제와 대비할 때 냄새가 나지 않으며 인체에 유해한 물질이 포함되지 않아 친환경적이다.
상기 수성접착제의 주성분은 아세트산 비닐 모노머(VAM)와 아크릴 화합물과, 유화제로 구성될 수 있다.
상기 아세트산 비닐 모노머(VAM)는 폴리비닐아세테이트(Polyvinyl Acetate, PVA) 또는 에틸렌비닐아세테이트(Ethylene Vinyl Acetate, EVA)인 것을 예시할 수 있다.
상기 아크릴 화합물은 메틸메타아크릴레이트(Methyl Methacrylate, MMA)와, 아크릴산으로 구성되는 것으로서, 메틸메타아크릴레이트는 결합력을 높여주며, 아크릴산은 메틸메타아크릴레이트에 친수기를 부여하고 가교 결합이 가능하도록 개질시키는 역할을 한다.
삭제
이러한 수성접착제는 폴리비닐아세테이트(PVA) 100중량부와, 상기 폴리비닐아세테이트 100중량부를 기준으로 메틸메타아크릴레이트 10~30중량부와, 아크릴산 1~10중량부와, 유화제 0.1~5중량부를 포함하는 것을 예시할 수 있다.
본 발명의 제2 수성접착제는 피막을 형성하여 내습성을 제공하고 기공이 많은 다공성의 초배지와의 접착력을 크게 향상시키기 위한 것으로서, 3종의 아크릴레이트를 조합하여 구성된다.
구체적으로 제2 수성접착제는 에틸아크릴레이트 100중량부와, 상기 에틸아크릴레이트 100중량부를 기준으로 부틸아크릴레이트 10~30중량부와, 2-하이드록시에틸아크릴레이트 10~30중량부와, 유화제 0.1~5중량부를 포함하여 이루어지는 것을 예시할 수 있다.
그리고 본 발명의 도배풀 조성물에는 기능성 충진재를 더욱 포함할 수 있는데, 기능성 충진재는 마이크로 입경을 가지는 실리카 입자, 예를 들어 실리카흄인 것을 예시할 수 있다. 상기 실리카흄은 규소합금을 정련하는 과정에서 배기가스 중에 함유된 부산물로써, 평균 입경이 1~3㎛인 미세 입자이며 내수성, 단열성 및 진동 흡수력을 제공하고, 일부는 조절제 중 하나인 수산화칼슘과 수화반응을 하여 결합력을 높여줄 수 있다.
이러한 실리카흄은 앞서 설명한 효과를 모두 발휘하기 위해서는 적어도 조절제 함량보다 과량으로 첨가되는 것이 바람직하며 예를 들어 조절제 중량 대비 실리카흄의 함량비는 1 : 5~15인 것을 예시할 수 있다.
상기 조절제는 도배풀 조성물의 pH를 알칼리성으로 유지하기 위한 것으로서, 탄산칼륨, 탄산수소나트륨, 폴리인산나트륨, 피로인산나트륨, 제2인산칼륨, 제2인산나트륨, 수산화칼슘 중에서 적어도 하나가 선택되는 것을 예시할 수 있다.
상기 증점제는 카복시메틸셀룰로스나트륨(Sodium Carboxymethylcellulose)인 것을 예시할 수 있다.
삭제
그리고 본 발명의 조성물은 식용 방부제, 예를 들어 소르빈산, 안식향산, 파라옥시안식향산, 프로피온산 중 적어도 어느 하나가 선택되며 2~3중량부를 더 포함하여 이루어질 수 있다.
이하에서는 본 발명에 따른 탄성포장재 제조방법의 바람직한 실시예를 통해 보다 상세하게 설명한다.
수성접착제 1.2kg, 카복시메틸셀룰로스나트륨 300g, 제2 수성접착제 1.0kg, 탄산칼륨 20g, 소르빈산 200g, 물 11kg을 혼합하여 도배풀 조성물을 제조하였다.
여기서, 수성접착제는 폴리비닐아세테이트(PVA) 100중량부와, 메틸메타아크릴레이트 20중량부와, 아크릴산 10중량부와, 유화제 3중량부로 구성되고, 제2 수성접착제는 에틸아크릴레이트 100중량부와, 부틸아크릴레이트 20중량부와, 2-하이드록시에틸아크릴레이트 20중량부와, 유화제 3중량부로 구성된다.
수성접착제 1.1kg, 카복시메틸셀룰로스나트륨 300g, 제2 수성접착제 1.0kg, 수산화칼슘 20g, 소르빈산 200g 및 실리카흄 100g 물 11kg을 혼합하여 도배풀 조성물을 제조하였다.
여기서, 수성접착제는 폴리비닐아세테이트(PVA) 100중량부와, 메틸메타아크릴레이트 20중량부와, 아크릴산 10중량부와, 유화제 3중량부로 구성되고, 제2 수성접착제는 에틸아크릴레이트 100중량부와, 부틸아크릴레이트 20중량부와, 2-하이드록시에틸아크릴레이트 20중량부와, 유화제 3중량부로 구성된다.
실시예 1, 2의 접착강도를 KS F 3217:2010의 접착강도 규격에 따라 측정하였으며, 그 결과는 아래 표 1에 기재하였다.
| 실시예 1 | 실시예 2 | |
| 접착강도[N/25mm] | 11.3 | 12.9 |
위 표 1에서 확인할 수 있듯이, 본 발명의 실시예 1, 2는 모두 전분풀의 기준치인 8.0[N/25mm] 보다 높은 접착강도를 가진다는 것을 확인할 수 있었다. 특히 실시예 2의 경우 실시예 1보다 수성접착제의 함량이 적음에도 불구하고 실시예 1보다 더 높은 접착강도를 가지는데, 이는 실리카흄과 수산화칼슘의 조합으로 인해 수화반응이 이루어지고 실리카흄이 공극을 메워 결합재 역할을 하기 때문인 것으로 판단된다.
이상에서 설명된 본 발명은 예시적인 것에 불과하며, 본 발명이 속한 기술분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 잘 알 수 있을 것이다. 그러므로 본 발명은 상기의 상세한 설명에서 언급되는 형태로만 한정되는 것은 아님을 잘 이해할 수 있을 것이다. 따라서 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다. 또한, 본 발명은 첨부된 청구범위에 의해 정의되는 본 발명의 정신과 그 범위 내에 있는 모든 변형물과 균등물 및 대체물을 포함하는 것으로 이해되어야 한다.
Claims (5)
- 폴리비닐아세테이트(PVA)와 메틸메타아크릴레이트와, 아크릴산과, 유화제로 구성되는 수성접착제 10~15중량부와;
카복시메틸셀룰로스나트륨 2~3중량부와;
에틸아크릴레이트와, 부틸아크릴레이트와, 2-하이드록시에틸아크릴레이트와, 유화제로 구성되는 제2 수성접착제 10~15중량부와;
수산화칼슘 0.1~0.5중량부와;
실리카흄 0.5~2.5중량부와;
물 100~150중량부;를 포함하되,
상기 수성접착제는 폴리비닐아세테이트(PVA) 100중량부를 기준으로 메틸메타아크릴레이트 20중량부와, 아크릴산 10중량부와, 유화제 3중량부를 포함하여 구성되고,
상기 제2 수성접착제는 에틸아크릴레이트 100중량부를 기준으로 부틸아크릴레이트 20중량부와, 2-하이드록시에틸아크릴레이트 20중량부와, 유화제 3중량부를 포함하여 구성되는 것을 특징으로 하는 도배풀 조성물. - 삭제
- 삭제
- 삭제
- 삭제