KR101724553B1 - The method for manufacturing of mask sheet - Google Patents

Abstract

The present invention relates to a method for manufacturing a Mask Sheet of Mica Mica in which an eco-friendly mica wood yarn as a main raw material is light and soft and gives a feeling of warmth and is excellent in adhesion and is evenly adhered to the face to exert whitening effect of Mica.
According to the present invention, there is provided a method for producing a mulberry bark, comprising the steps of: subjecting a bark of a mulberry tree to wax processing several times through a wet process; A step of removing impurities contained in the mulberry wool; A step of mixing the emulsion, the polyurea cotton, and the rayon cotton at a predetermined ratio to the raw mackerel cotton in a state of being treated as a raw material by treating the crumbs of the sorted mulberry cotton; A dyeing step of dyeing the martensin cotton with the desired color; A surface and a tapping step of tapping the developed mulberry sheet while developing the sheet in the form of rubbing the dyed mulberry paper; Folding and folding the folded and folded mulberry wood sheets so as to overlap each other in the longitudinal direction so as to form a folded mulberry cotton sheet, Folding step, a horizontal folding deformation step, and a superimposing development step, and finally holding the paper sheet with a final sheet of mulberry cotton sheet to perform final rubbing and developing step; A lengthwise cutting step of keeping the mulberry cotton sheet having the main raw material of mulberry mulberry as a main material and cutting it in the longitudinal direction; A winding step of winding a sheet of the mulberry cotton sheet cut to a predetermined width according to the shape of the product to be produced according to the thickness and tension of the yarn to form a mulberry thread; And a mask manufacturing step of fabricating a mask sheet using the wrapped mica wood.

Description

BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a method of manufacturing a mask sheet,

More particularly, the present invention relates to a method for producing a mask sheet using a mulberry tree, and more particularly, to a method for producing a mask sheet using an environmentally friendly mulberry tree as a main raw material, which is light and soft, The present invention relates to a method of manufacturing a seal mask sheet.

Interest in women's skin care has continued, and Hyundai is now entering an aging society. Especially today, the concept of wellbeing has emerged as the best socio-cultural topic for a happy and healthy life, The desire to keep beautiful skin constantly is increasing.

Accordingly, many mask packs and sheets useful for skin care have been developed, and the skin care related industry is developing. In response to this trend, various dermatology clinics and skin care specialty shops have been popular recently.

Generally, the skin of the human body begins to aging in the late 20s, and wrinkles begin to appear and the skin becomes elastic.

In order to suppress the aging phenomenon, conventional skin care means used in homes, skin care rooms, dermatology clinics, and the like have been mainly used to massage various functional cosmetics and massage cream into the face by massage, and recently, Functionally oriented coating agents are also used.

The management method in the skin care specialty store is to apply a mask such as gauze for a certain period of time after appropriately applying a nutritional cream or a functional oil for facial removal and wrinkle removal by a massage for a certain period of time or a massage by machine action, Most of them help to penetrate functional materials.

In addition, a disposable mask pack is marketed in consideration of this, and skin rash effect by mask is easily achieved at home.

However, as described above, skin care and cosmetic services or treatments received by professional skin care clinics or dermatology related clinics are usually expensive and time consuming, which is disadvantageous to the contemporary life patterns of busy people. In addition, the disposable mask pack which is easily handled at home is rather harmful to the skin cosmetic because it contains a large amount of preservative. When the long period of the shelf life is passed, the functional material penetrates effectively into the dermis of the skin, There are also difficult problems. In addition, since the conventional disposable mask pack is applied at a room temperature different from the skin temperature, there is a drawback in that it can not penetrate deeply into the skin.

Especially, facial stimulation due to the frequent use of color cosmetics by modern women, skin damage due to outdoor leisure activities, environmental pollution, etc. are often caused by roughening or troubles of the face, thereby making a considerable economic time investment in skin care management It became common.

Natural materials such as milk, cucumber, green tea, aroma, herb, honey, ocher, jade, etc. to supply nourishment to the rough and dull face caused by internal and external environmental factors such as stress, environmental pollution, And massage facial masks with nutritional creams, massage packs, disposable facial masks, and electrical vibration functions are used.

Currently available commercially available disposable facial massage packs or mask sheets are made by impregnating or gelating functional ingredients such as non-woven fabric, paper, etc. to remove wasted skin, wrinkle removing whitening, moisturizing, whitening, soothing, etc., It is common.

Such disposable facial masks may be adhesives used to firmly attach to the face, or in other cases, nonwoven fabrics may be made thin in microns and then adhered to the face using a massaging liquid.

Korean Patent Application No. 2000-0048152 discloses a massage device which is made by impregnating a cosmetic massaging agent and then formed into a shape using a face mask, so that a user can easily massage it, and a uniform massage effect can be obtained throughout the face. A massage pack having a face printing pattern formed on the outer surface of a pack of a mask shape so as not to have a dislike, and Korean Patent Laid-Open Publication No. 0287269 discloses a massage pack which is a raw material of Korean paper having a high viscosity, The present invention relates to a facial-shaped massage pack which comprises a mixture of soil mud pulp, ground mud pulp and ground water, and mixes and precipitates the mixture of loess, ointment and germanium biotite with a far-infrared radiation material.

However, since the mackerel fiber itself has a weak strength and a short fiber length, it can be manufactured only in the case of the paper making process, and it is possible to obtain a durability, a preservation property, a ventilation property, a soft texture, a flexible folding, Because of its excellent thermal insulation properties, the fibers of mulberry tree have not yet been widely used in clothing, clothing cotton, and bedding cotton in the real world.

[Prior Art Literature]

Korean Utility Model Registration No. 0287269

It is an object of the present invention to provide a mask sheet which is manufactured by using a mulberry tree, and which has a lightweight, soft and strong tension by using the produced yarn as a main raw material.

In order to accomplish the above object, the present invention provides a method for producing a mulberry bark, comprising the steps of: subjecting a mulberry bark to wet processing through several wet processes; A step of removing impurities contained in the mulberry wool; A step of mixing the emulsion, the polyurea cotton, and the rayon cotton at a predetermined ratio to the raw mackerel cotton in a state of being treated as a raw material by treating the crumbs of the sorted mulberry cotton; A dyeing step of dyeing the martensin cotton with the desired color; A step of rubbing the dyed mulberry cotton sheet and kneading the developed mulberry cotton sheet while spreading it in the form of a sheet; Folding and folding the folded and folded mattress pad sheets so as to overlap each other in the longitudinal direction to form a folded mattress pad sheet, and folding and spreading the folded mattress pad sheet so that the folded mattress pad sheet is repeatedly moved left and right; A step of folding and folding the sheet of the mulberry cotton sheet consisting of the vertical folding step, the horizontal folding deformation step, and the overlapping expansion step; A lengthwise cutting step of keeping the mulberry cotton sheet having the main raw material of mulberry mulberry as a main material and cutting it in the longitudinal direction; A winding step of regulating the thickness and tension of the yarn according to the type of the product to be produced from the mulberry cotton sheet cut to a predetermined width to form a mulberry thread; And a mask manufacturing step of fabricating a mask sheet using the wrapped mica wood.

According to one embodiment of the present invention, the selecting step carries out carbonization to remove vegetative matters, and performs a combing process of vertically and horizontally interlacing the raw materials in the state of being entangled with each other ;

According to an embodiment of the present invention, the mixing and mixing step may include a primary mixing step of mixing or precipitating the marmalade so that the marmalade has house properties and smoothness as well as antistatic properties so as not to generate static electricity; And a secondary mixing step of mixing 50 to 60% by weight of the total weight of the mica wood pulp, 15 to 20% by weight of the polyolefine cotton and 25 to 30% by weight of the rayon cotton.

According to an embodiment of the present invention, the folding and stacking step includes a vertical folding step of vertically folding a plurality of folded sheets of mulberry wool which are spread and spread in a wide film shape and holding the folded sheets in a vertically folded mulberry paper sheet. A horizontal folding deformation step of vertically folding vertically folded vertical folded mattress pad sheets horizontally folded and holding them with horizontal folded mattress pad sheets; Folded horizontally folded sheets of mattress cotton sheets are repeatedly moved leftward and rightward to overlap each other.

According to an embodiment of the present invention, a hydrogel containing a skin active ingredient is applied in a thickness of 0.001 to 1 cm in the mask making step.

According to one embodiment of the present invention, a functional composition comprising one or more selected from the group consisting of a whitening composition, a moisturizing composition, a soothing composition, a wrinkle preventing composition and a relaxation composition is added .

The present invention has the effect of providing a mask sheet made of mulberry and having a lightweight, soft and strong tension by using the produced yarn as a main raw material.

FIG. 1 is a flowchart showing a process for manufacturing a sheet of mica wood in a method of manufacturing a mask sheet using a mica wood according to an embodiment of the present invention.
FIG. 2 is a flow chart showing a process for manufacturing a mica sheet in a method of manufacturing a mask sheet using a mica wood according to an embodiment of the present invention.
FIG. 3 is a flowchart showing a manufacturing process for manufacturing a mask sheet by using a Mammal Seal in a method of manufacturing a mask sheet using a Mammal Seal according to an embodiment of the present invention.
FIGS. 4 and 5 are schematic views illustrating a state in which a mulberry sheet is manufactured using a mulberry wood in a method of manufacturing a mask sheet using the mulberry wood according to an embodiment of the present invention.

Specific structural and functional descriptions of the embodiments of the present invention disclosed herein are for illustrative purposes only and are not to be construed as limitations of the scope of the present invention. And should not be construed as limited to the embodiments set forth herein or in the application.

The embodiments according to the present invention can make various changes and have various forms, so that specific embodiments are illustrated in the drawings and described in detail in this specification or application. It is to be understood, however, that it is not intended to limit the embodiments according to the concepts of the present invention to the particular forms of disclosure, but includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention.

The terms first and second, etc. may be used to describe various elements, but the elements should not be limited by the terms. The terms are intended to distinguish one element from another, for example, without departing from the scope of the invention in accordance with the concepts of the present invention, the first element may be termed the second element, The second component may also be referred to as a first component.

It is to be understood that when an element is referred to as being "connected" or "connected" to another element, it may be directly connected or connected to the other element, . On the other hand, when an element is referred to as being "directly connected" or "directly connected" to another element, it should be understood that there are no other elements in between. Other expressions that describe the relationship between components, such as "between" and "between" or "neighboring to" and "directly adjacent to" should be interpreted as well.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In this specification, the terms "comprises ", or" having ", or the like, specify that there is a stated feature, number, step, operation, , Steps, operations, components, parts, or combinations thereof, as a matter of principle.

Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as ideal or overly formal in the sense of the art unless explicitly defined herein Do not.

The mask sheet according to the present invention first produces a mulch cotton, uses the mulberry mulberry produced to produce a shorted wood yarn, and then uses it to produce a mask sheet.

Here, a brief description of mackerel, mackerel is composed of the outer skin (husk) and the inner skin (white mackerel). The mackerel can be loosened by loosening the white mackerel, It has been used as raw paper, paper money, coin, paperboard, windpower, etc. to filter out the fibers.

The fiber of mulberry tree is rarely used for textile products because it is relatively weak in fiber and short in fiber length among the same kind of bast fiber.

However, since the fiber of mackerel is weak and has a short fiber length, it has excellent properties of warmth, breathability, and deodorization. Therefore, various methods of using the mackerel fiber having excellent properties In fact.

In recent years, as interest in natural fibers has increased, it has been used to make clothes using Hanji, which is made of mulberry fiber. However, this is only used as clothing for clothes and dolls for exhibitions.

In other words, since the mackerel fiber itself has a weak strength and a short fiber length, it can be manufactured only in the case of Hanji as it has various stages of manufacturing process, so that it has durability, preservability, air permeability, soft texture, flexible folding, This is because it has excellent thermal insulation properties.

As a result, the fibers of mulberry tree have not yet been widely used in real life as garments, clothes cotton, and bedding cotton.

Accordingly, it is an object of the present invention to provide a mask sheet using the produced Mackle room.

First, a method for manufacturing a mica wood cotton for manufacturing a mica wood yarn is made by a mica wood manufacturing process (S100) as shown in Fig.

(S110) is carried out in which the skin of the mulberry tree is processed with a soft back fat containing water by 20 to 30% through wet processes several times.

This step of sacking (S110) is a step of preparing and processing the mackerel white mackerel. The mackerel mackerel is first steamed for 1 hour to 3 hours using water vapor so that the mackerel is peeled off easily. The steamed mackerel bark is peeled off and dried in the sun , Dried mackerel bark is routed for about 10 hours, and the surface is peeled off with a knife and dried in the sun to make white peach.

In addition, the dried white wax is soaked in cold water for a day or two and is dried. When the white wax is soaked in water and dried, the white wax can be softened by repeating the process twice or three times.

In order to smooth the pulverization of the thus-prepared white puff, a thick fiber prepared by cutting a white cotton into a length of 7 to 10 cm with a cutter prepared in advance was used to prepare a white puff containing 20 ~ 30% .

In addition, the processed baguette is subjected to a trimming process (S120) in which the trimming is performed so as to cut through aberrations (preferably, two-thirds) through three narrow cuts.

In addition, when the three sections are completed, the fine fibers cut from the three seasons are pulled and finely disassembled to be spun into a light and soft cotton, or the synthetic fibers are mixed with the above-mentioned fine white fibers, and the mixed fibers are lightly soft, The cotton paddy can be obtained by performing the spongy process (S130) in which cotton is formed.

When the production process of the mulberry tree cotton is completed, the actual mulberry process S200 is performed to produce the mulberry tree using the mulberry tree cotton.

The actual mulberry tree preparation step (S200) is carried out as follows to produce a mulberry tree.

The stocking step is carried out by putting the mulberry cotton produced by the manufacturing process (S100) of the mulberry cotton into the supply hopper of the actual mulching device and putting it in the stocking step (S210).

Thereafter, the sorting step S220 of removing the imported mulberry cotton, that is, the impurities contained in the raw material, is performed.

In this sorting step, carbonization is performed to remove vegetative matters contained in the raw material (mulberry cotton), and a combing process is performed in which raw materials in the state of being entangled with each other, that is, mulberry cotton wool, are cross- .

In addition, the raw materials that have been sorted are subjected to a semi-hardening step in which the debris of the raw materials that occurs during the screening or coaming process is treated and regenerated in the state of raw materials, and the polyurea cotton and rayon cotton are mixed at a predetermined ratio Mixing and mixing steps are performed to perform the half-blending and blending steps (S230)

Here, mixing of the mulberry leaves and the emulsion for a predetermined period of time is for the purpose of fiber rinsing, and in particular, to have not only house property and smoothness of the mulberry leaves but also static electricity to prevent static electricity from being generated.

Here, the polyolefine cotton is a synthetic fiber cotton made from a polymer of urea and nonamethylene diamine, which is blended to increase the strength of the raw material of mulberry tree, that is, mulberry cotton, It has a similar elasticity to that of nylon, similar to wool, with a lower specific gravity, higher heat resistance than nylon (softening point 230 to 240 ° C), and elasticity.

In the present invention, it is preferable to use one or more of polyethylene, polyester, polyurethane, polychal, and polypropylene, but not limited thereto.

In addition, the rayon cotton is made of pulp made of pure cellulose by treating it with wood or an obscure debris by a suitable chemical method, chemically dissolving it, and then coagulating it into a fibrous form. The rayon cotton has a soft texture and a cold feeling, This is a strong feature.

In the secondary mixing process of the present invention, 50 to 60% by weight of mulberry wood (raw material) made of mulberry, 15 to 20% by weight of polyurea cotton and 25 to 30% by weight of rayon cotton are mixed. However, the present invention is not limited to this, and it is needless to say that the blending ratio may be varied depending on the length of the cut mica wood room, and the deviation should be within about 4%.

After completion of the flattening and mixing process, a dyeing step of dyeing the raw material with an arbitrary color is performed, thereby performing a dyeing step of forming the raw material of various colors (S240)

When dyeing is completed, the dyed mulberry cotton sheet is developed in a sheet form, and the mulch wood cotton sheet 1, which is developed, is rubbed and the mulch wood cotton sheet 1 is softly held while being weighted, And tapping are performed (S250)

The smoothed mulberry cotton sheet 1 is subjected to a sheet folding and stacking step S260 as illustrated in Figs. 3A to 3C.

The sheet folding and stacking step S260 of folding and folding the sheet of mulberry wool is performed by vertically folding the sheet of mulberry wool which is spread and transported in a wide film form as illustrated in Fig. (S260-1). As shown in FIG. 3B, the vertically folded vertically folded vertically folded mattress pad sheet 2 is horizontally deformed to form the horizontally folded mattress pad sheet 3, (S260-2) for horizontally folding and folding the horizontally folded sheet of mica sheet 3 horizontally folded so as to maintain the horizontal folded sheet (3) in the horizontal direction.

The above-described mattress cotton sheet surface and tapping step S250 and the folding and overlapping step S260 of the mattress pad may be repeated one or more times. In this manner, (S250) and the folding of the sheet of mulberry cotton sheet and the step S260 of repeating the overlapping step are repeated a plurality of times, the mulberry thread produced at a later time can be smoothly maintained and the tension can be strengthened.

After the folding step and the overlapping and expanding step S260 of the vertical folding step S260-1, the horizontal folding deformation step S260-2 and the overlapping expansion step S260-3 are finally performed, And a developing step S265 are executed to keep the sheet in a sheet form.

In order to easily manufacture the sheet of cotton mats to be developed, a longitudinal cutting step of cutting the sheet in the longitudinal direction is performed while maintaining a constant width (S250).

This is to cut into a length of 7 to 10 cm in length cut during sacking in the production process of the mica wood cotton (S100) so as to be made into a thick fiber form. When mixing with an emulsion through a mixing step to be described later, To be mixed with the surface of the raw material.

The lengthwise cutting step is performed in which the mattress cotton sheet is cut in a predetermined width while being moved in parallel so that the mattress cotton sheet can be formed into a continuous yarn of an appropriate thickness,

Each of the cut pieces of the mattress cotton sheet is molded into a twisted yarn while applying pressure, and the tension of the mattress thread can be changed according to the number of twists.

Also, according to the shape of the product to be shipped, the twisted mica yarn yarn is subjected to a winding step of winding up the mica yarn by adjusting the thickness of the yarn and the winding amount to be wound (S280)

In this case, a twisting step may be included in which twisted yarns are selectively twisted in succession depending on the product, or twist yarns to twist yarns of more than two yarns.

And a step of curing the functional composition to the masked muffin thread to produce a mask sheet (S300)

In step S300 of manufacturing the mask sheet, a hydrogel containing a skin active ingredient is applied at a thickness of 0.001 to 1 cm. (S310) The skin active ingredient is compounded at 50 DEG C or lower and administered. At this time, 0.001 cm or less is a thickness that is difficult to contain an appropriate amount of an efficacious substance.

Further, in the mask making step, the functional composition is further added (S320), wherein the functional composition is selected from the group consisting of a whitening composition, a moisturizing reinforcing composition, a soothing composition, a wrinkle preventing composition and a relaxation composition But may be any one or more.

After completion of the production of the mask sheet, the inspection and packaging step (S330) is performed to inspect whether the product is in good condition and pack the product so that it can be stored in a warehouse or a warehouse only for a good product.

The mask sheet using the mica wood produced through such a manufacturing method is a very useful invention having excellent lightness and warmth because it uses the mica wood fiber as the main material.

S100: Mulberry cotton manufacturing process S110: Saw white fixing
S120: Sieving process S130: Spongy process
S200: Actual mulberry process S210: Mulberry process step
S220: Selection step S230: Half-face and mixing step
S240: dyeing step S250: rubbing and tapping step
S260: folding and overlapping developing step S270: longitudinal cutting step
S280: winding step S300: mask manufacturing step
S310: Hydrogel application step S320: Addition of functional composition
S330: Inspection and packaging step

Claims (6)

Processing the mulberry tree bark through a wet process several times and finely dividing the mulberry bark to produce a mulberry cotton;
A step of removing impurities contained in the mulberry wool;
A step of mixing the emulsion, the polyurea cotton, and the rayon cotton at a predetermined ratio to the raw mackerel cotton in a state of being treated as a raw material by treating the crumbs of the sorted mulberry cotton;
A dyeing step of dyeing the martensin cotton with the desired color;
A face and a tapping step of tapping the developed sheet of mulberry cotton while spreading the sheet in the form of rubbing the colored cotton dyed cotton;
Folding and folding the folded and folded mattress pad sheets so as to overlap each other in the longitudinal direction to form a folded mattress pad sheet, and folding and spreading the folded mattress pad sheet so that the folded mattress pad sheet is repeatedly moved left and right;
A step of folding and folding the sheet of mulberry paper comprising the vertical folding step, the horizontal folding deformation step, and the overlapping expansion step;
A lengthwise cutting step of keeping the mulberry cotton sheet having the main raw material of mulberry mulberry as a main material and cutting it in the longitudinal direction;
A winding step of regulating the thickness and tension of the yarn according to the type of the product to be produced from the mulberry cotton sheet cut to a predetermined width to form a mulberry thread; And
And a mask manufacturing step of fabricating a mask sheet by using the mica wood yarn thus wound.
The method according to claim 1,
A method for manufacturing a mask sheet using a mica tree, the method comprising: performing carbonization to remove vegetative matters, and performing a combing process of vertically and horizontally interlacing raw materials, i.e. cotton, in an entangled state.
[2] The method of claim 1,
A primary mixing step of mixing or precipitating the emulsion so as to have not only house property and smoothness but also antistatic property to prevent static electricity from being generated in the tea tree; And
A second mixing step of mixing 50 to 60% by weight of a cottonwood, 15 to 20% by weight of a polyolefine cotton and 25 to 30% by weight of a rayon cotton.
The method of claim 1,
A vertically folding step of folding vertically folded sheets of mulberry cotton spread and spreading in a wide film shape and holding the sheets with vertical folded mulberry paper sheets;
A horizontal folding deformation step of vertically folding vertically folded vertical folded mattress pad sheets horizontally folded and holding them with horizontal folded mattress pad sheets;
And a superimposing step of superimposing the horizontally folded horizontally folded mattress cotton sheet repeatedly to the left and right so as to overlap with each other.
The method according to claim 1,
Wherein a hydrogel containing a skin active ingredient is applied in a thickness of 0.001 to 1 cm in the mask making step.
The method according to claim 1,
Characterized in that a functional composition comprising one or more selected from the group consisting of a whitening composition, a moisturizing reinforcing composition, a soothing composition, a wrinkle preventing composition and a relaxation composition is added in the mask making step / RTI >