KR101675215B1 - Finishing sheet coated with polyurethane for floor mat - Google Patents
Finishing sheet coated with polyurethane for floor mat Download PDFInfo
- Publication number
- KR101675215B1 KR101675215B1 KR1020150010663A KR20150010663A KR101675215B1 KR 101675215 B1 KR101675215 B1 KR 101675215B1 KR 1020150010663 A KR1020150010663 A KR 1020150010663A KR 20150010663 A KR20150010663 A KR 20150010663A KR 101675215 B1 KR101675215 B1 KR 101675215B1
- Authority
- KR
- South Korea
- Prior art keywords
- polyurethane
- floor mat
- layer
- coating layer
- mat
- Prior art date
Abstract
본 발명은 폴리우레탄이 코팅된 바닥 매트용 마감시트에 관한 것으로, 더욱 상세하게는 필름층, 상기 필름층의 상부면에 형성되는 인쇄층 및 상기 인쇄층의 상부면에 형성되는 코팅층으로 이루어진다.
상기의 구조로 이루어지는 폴리우레탄이 코팅된 바닥 매트용 마감시트는 접착제를 사용하지 않고도 바닥 매트의 표면에 열융착의 과정을 통해 형성되기 때문에 친환경적이며, 폴리우레탄으로 표면처리되어 피부트러블을 유발하지 않고, 다양한 무늬를 형성할 수 있는 바닥용 매트를 제공하는 효과를 나타낸다.The present invention relates to a flooring sheet for a polyurethane-coated floor mat, and more particularly, to a flooring sheet for a polyurethane-coated floor mat, which comprises a film layer, a printing layer formed on the upper surface of the film layer and a coating layer formed on the upper surface of the printing layer.
Since the polyurethane-coated flooring mat having the above structure is formed through the process of heat fusion on the surface of the floor mat without using an adhesive, it is environmentally-friendly, and is surface-treated with polyurethane to cause no skin trouble , And a floor mat capable of forming various patterns.
Description
본 발명은 폴리우레탄이 코팅된 바닥 매트용 마감시트에 관한 것으로, 더욱 상세하게는 접착제를 사용하지 않고도 바닥 매트의 표면에 열융착의 과정을 통해 형성되기 때문에 친환경적이며, 폴리우레탄으로 표면처리되어 피부트러블을 유발하지 않고, 다양한 무늬를 형성할 수 있는 바닥용 매트를 제공하는 폴리우레탄이 코팅된 바닥 매트용 마감시트에 관한 것이다.
The present invention relates to a flooring mat for polyurethane-coated floor mats, and more particularly, to a flooring mat for polyurethane-coated floor mats, which is environmentally-friendly, To a floor sheet for a polyurethane-coated floor mat which provides a floor mat capable of forming various patterns without causing troubles.
최근 주택의 형태가 단독주택에서 아파트와 같은 공동주택으로 변화하면서 층간소음으로 인한 다양한 문제점이 발생하고 있다. 일반적으로 아파트 등과 같은 복층건물의 경우에는 바닥슬래브와 경량기포 콘크리트층 사이에 층간소음을 저감시키는 완충흡음재가 개재됨에 따라, 상층으로부터 하층으로 전달되는 진동 및 소음이 어느 정도로는 방지될 수 있지만 충분치 않은 실정이며, 빌라 등과 같은 복층건물에는 경량기포 콘크리트층 사이에 층간소음을 저감시키는 완충흡음재가 개재되지 않는 경우가 많아 일상생활에서 발생되는 진동 및 소음이 상층으로부터 하층으로 전달되어 주민간의 분쟁을 야기시키고 있다.Recently, the type of housing has changed from a single house to a apartment like apartment, and various problems have arisen due to the interlayer noise. Generally, in the case of a multi-storey building such as an apartment, a vibration absorbing material for reducing the interlayer noise is interposed between the floor slab and the lightweight foamed concrete layer, vibration and noise transmitted from the upper layer to the lower layer can be prevented to some extent, In a multi-storey building such as a villa, vibration absorbing materials that reduce interlayer noise between lightweight foamed concrete layers are often not present, so that vibrations and noise generated in daily life are transmitted from the upper layer to the lower layer, causing disputes among residents have.
따라서, 아파트나 빌라 등과 같은 복층건물에서는 방바닥 또는 거실바닥 상에 다수개가 서로 조립된 상태로 배열되어 소정 크기의 층간소음 방지용 매트가 주로 사용되고 있는데, 이러한 종래의 층간소음 방지용 매트는 폴리에틸렌 등과 같은 합성수지가 발포성형하여 형성되는 매트블럭본체와, 상기 매트블럭본체의 가장자리를 따라 형성되어 인접될 매트블럭본체가 조립되도록 하는 요철결합부로 이루어지는 단순한 구조로 이루어져 있다.Therefore, in a multi-storey building such as an apartment or a villa, a plurality of mats are arranged in a state where they are assembled together on a floor or a living room floor, so that a mat for preventing noise between rooms of a predetermined size is mainly used. Such a mat for preventing noise between rooms is made of synthetic resin such as polyethylene A mat block body formed by foam molding and a concave-convex engaging portion formed along an edge of the mat block body to be assembled to be adjacent to the mat block body.
그러나, 상기의 구조로 이루어지는 종래의 바닥용 매트는 매트블럭본체가 발포성형되기 때문에, 인쇄잉크를 직접도포하게 되면, 인쇄잉크가 매트블럭본체로 흡수되어 인쇄품질이 저하되기 때문에, 매트블럭본체의 표면에 직물로 이루어진 직물층을 접착제로 접착한 후에, 접착제로 접착된 직물의 표면에 인쇄잉크를 도포하여 각종 무늬 및 로고를 인쇄하는 방법이 주로 사용되었는데, 상기의 방법은 접착제가 사용되기 때문에 매트를 사용하는 과정에서 접착제에 함유된 각종 용제성분이 방출되어 인해 인체에 유해하며, 피부트러블을 유발하고, 직물의 표면에 형성된 인쇄층이 마찰력에 의해 쉽에 손상되는 문제점이 있었다.
However, since the mat for the floor of the related art having the structure described above is formed by foam molding, when the printing ink is applied directly, the printing ink is absorbed into the mat block body and the printing quality is lowered. A method of printing various patterns and logos by applying a printing ink on the surface of a fabric bonded with an adhesive has been mainly used after bonding a fabric layer made of a fabric to the surface with an adhesive, There is a problem that the printed layer formed on the surface of the fabric is easily damaged by the frictional force because the various solvent components contained in the adhesive are released.
본 발명의 목적은 접착제를 사용하지 않고도 바닥 매트의 표면에 열융착의 과정을 통해 형성되기 때문에 친환경적이며, 폴리우레탄으로 표면처리되어 피부트러블을 유발하지 않고, 다양한 무늬를 형성할 수 있는 바닥용 매트를 제공하는 폴리우레탄이 코팅된 바닥 매트용 마감시트를 제공하는 것이다.
An object of the present invention is to provide a floor mats which are environmentally friendly and which are surface-treated with polyurethane and do not cause skin troubles because they are formed on the surface of a floor mat through a process of heat fusion without using an adhesive. To provide a finish sheet for a polyurethane-coated floor mat.
본 발명의 목적은 필름층, 상기 필름층의 상부면에 형성되는 인쇄층 및 상기 인쇄층의 상부면에 형성되며, 폴리우레탄으로 이루어진 코팅층으로 이루어지는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트를 제공함에 의해 달성된다.An object of the present invention is to provide a finish for a polyurethane-coated floor mat, characterized by comprising a film layer, a printing layer formed on the upper surface of the film layer, and a coating layer formed on the upper surface of the printing layer, Sheet. ≪ / RTI >
본 발명의 바람직한 특징에 따르면, 상기 필름층은 폴리에틸렌 또는 에틸렌비닐아세테이트로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the film layer is made of polyethylene or ethylene vinyl acetate.
본 발명의 더 바람직한 특징에 따르면, 상기 코팅층은 3 내지 7 마이크로미터의 두께로 형성되며, 투명 폴리우레탄으로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the coating layer is formed to a thickness of 3 to 7 micrometers and is made of transparent polyurethane.
본 발명의 더욱 바람직한 특징에 따르면, 상기 투명 폴리우레탄은 수분의 함량이 0.01 내지 0.05 중량%이며, 경화제의 주원료인 폴리에스테르폴리올의 점도를 500 내지 2,000cps(40℃)로 제한하고, 가교제의 함량을 2 내지 5 중량%로 제한하며, 주제 및 경화제를 포함하는 반응 원료의 사용 온도를 50 내지 60℃로 하여 제조되는 것으로 한다.
According to a further preferred feature of the present invention, the transparent polyurethane has a water content of 0.01 to 0.05% by weight, the viscosity of the polyester polyol as the main material of the curing agent is limited to 500 to 2,000 cps (40 캜) Is limited to 2 to 5% by weight, and the reaction material containing the base and the curing agent is used at a temperature of 50 to 60 캜.
또한, 본 발명의 목적은 전사인쇄층 및 상기 전사인쇄층의 상부면에 형성되며, 폴리우레탄으로 이루어진 코팅층으로 이루어지는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트를 제공함에 의해서도 달성될 수 있다.The object of the present invention can also be achieved by providing a finish sheet for a polyurethane-coated floor mat, which is formed on the transfer printing layer and on the upper surface of the transfer printing layer and is formed of a coating layer of polyurethane have.
본 발명의 바람직한 특징에 따르면, 상기 코팅층은 3 내지 7 마이크로미터의 두께로 형성되며, 투명 폴리우레탄으로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the coating layer is formed to a thickness of 3 to 7 micrometers and is made of transparent polyurethane.
본 발명의 더 바람직한 특징에 따르면, 상기 투명 폴리우레탄은 수분의 함량이 0.01 내지 0.05 중량%이며, 경화제의 주원료인 폴리에스테르폴리올의 점도를 500 내지 2,000cps(40℃)로 제한하고, 가교제의 함량을 2 내지 5 중량%로 제한하며, 주제 및 경화제를 포함하는 반응 원료의 사용 온도를 50 내지 60℃로 하여 제조되는 것으로 한다.
According to a more preferred feature of the present invention, the transparent polyurethane has a water content of 0.01 to 0.05% by weight, the viscosity of the polyester polyol as the main raw material of the curing agent is limited to 500 to 2,000 cps (40 캜) Is limited to 2 to 5% by weight, and the reaction material containing the base and the curing agent is used at a temperature of 50 to 60 캜.
본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트는 접착제의 사용없이 바닥 매트의 표면에 열융착의 과정을 통해 형성되기 때문에 친환경적이며, 폴리우레탄으로 표면처리되어 피부트러블을 유발하지 않고, 다양한 무늬를 형성할 수 있는 바닥용 매트를 제공하는 탁월한 효과를 나타낸다.
The finish sheet for a polyurethane-coated floor mat according to the present invention is environmentally-friendly because it is formed on the surface of the floor mat through the process of thermal fusion without using an adhesive, is surface-treated with polyurethane, And provides a mat for a floor that can form a pattern.
도 1은 본 발명의 일 실시예에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트를 나타낸 분해사시도이다.
도 2는 본 발명의 다른 실시예에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트를 나타낸 분해사시도이다.1 is an exploded perspective view showing a finish sheet for a polyurethane-coated floor mat according to an embodiment of the present invention.
2 is an exploded perspective view showing a finish sheet for a polyurethane-coated floor mat according to another embodiment of the present invention.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
Hereinafter, preferred embodiments of the present invention and physical properties of the respective components will be described in detail with reference to the accompanying drawings. However, the present invention is not limited thereto, And this does not mean that the technical idea and scope of the present invention are limited.
본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트는 필름층(10), 상기 필름층(10)의 상부면에 형성되는 인쇄층(20) 및 상기 인쇄층(20)의 상부면에 형성되는 코팅층(30)으로 이루어진다.
A finish sheet for a polyurethane-coated floor mat according to the present invention comprises a
상기 필름층(10)은 폴리에틸렌 또는 에틸렌비닐아세테이트로 이루어지며, 0.03 내지 0.05 밀리미터의 두께로 형성되는데, 열접착의 과정을 통해 바닥용 매트와 본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트를 접착할 뿐만 아니라, 상기 인쇄층(20)을 형성하는 인쇄잉크와의 우수한 접착성을 나타내어 바닥용 매트의 표면에 다양한 무늬 또는 로고 등을 형성할 수 있도록 하는 역할을 한다.The
이때, 상기 필름층(10)은 열접착의 과정을 통해 바닥용 매트와 접착될 수 있도록, 열접착 공정에 적용가능한 열가소성의 폴리에틸렌 또는 에틸렌비닐아세테이트를 사용하는 것이 바람직하며, 바닥용 매트와 본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트의 접착력을 향상시키기 위해 바닥용 매트를 구성하는 재료와 동일한 성분으로 이루어지는 것이 더욱 바람직하다.At this time, it is preferable to use thermoplastic polyethylene or ethylene vinyl acetate applicable to the heat bonding process so that the
상기 필름층(10)의 두께가 0.03 밀리미터 미만으로 형성되면 연성이 지나치게 증가하여 쉽게 변형되며, 열접착과정에서 필름층(10)의 형상유지가 어려워 상기 인쇄층(20)을 제대로 형성할 수 없고, 상기 필름층(10)의 두께가 0.05 밀리미터를 초과하게 되면 필름층(10)의 유연성이 저하되어 바닥용 매트와 접착된 상태에서 외부의 충격에 의해 바닥용 매트로부터 박리되는 현상이 발생할 수 있고 제조비용을 증가시키게 된다.
If the thickness of the
상기 인쇄층(20)은 상기 필름층(10)의 상부면 0.05 내지 0.1 밀리미터의 두께로 형성되는데, 다양한 색상 및 무늬를 나타내는 바닥용 매트를 제공하는 역할을 한다.The
이때, 상기 인쇄층(20)을 형성하는 인쇄잉크는 상기 필름층(10)에 적용할 수 있는 성분이면 특별히 한정되지 않고 어떠한 것이든 사용가능하나, 항균성과 선명한 무늬나 로고를 구현할 수 있으며 친환경 성분으로 이루어지는 것을 사용하는 것이 바람직한데, 수성 알코올 60 내지 65 중량부, 폴리비닐알코올 5 내지 10 중량부, 메틸에틸케톤 5 내지 10 중량부, 수성 분산액 20 내지 25중량부를 포함하여 이루어지는 인쇄잉크를 사용하는 것이 바람직하다.The printing ink forming the
이때, 상기 수성 분산액은 착색제 5 내지 7 중량부, 분산 안정제 2 내지 4 중량부, 조습 항균제 2 내지 4 중량부, 과산화수소 1.5 중량부, 음이온 발생 희토류 광물 2 내지 2.5 중량부, 정제수 5 내지 7 중량부를 포함하는 것이 바람직하며, 상기 조습 항균제는 Sr-페라이트(Sr-Fe12O19), Ba-페라이트(Ba-Fe12O19), 마그네타이트(Fe3O4), 마그헤마이트(γ-Fe2O3), 니켈페라이트(Ni-Fe2O4) 및 코발트페라이트(Co-Fe2O4)로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 30 내지 100nm의 입자 크기의 산화물 세라믹계 자성 나노분말로 이루어지는 것이 바람직하고, 상기 분산 안정제는 에탄올 아민, 메틸디에탄올아민, 트리에탄올아민, 헥사놀아민, 히드록시알킬아민, 피페리딘 및 N-메틸 피페리딘으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하다.At this time, the aqueous dispersion contains 5 to 7 parts by weight of a colorant, 2 to 4 parts by weight of a dispersion stabilizer, 2 to 4 parts by weight of a humidity-controlling antibacterial agent, 1.5 parts by weight of hydrogen peroxide, 2 to 2.5 parts by weight of anion- (Ba-Fe 12 O 19 ), magnetite (Fe 3 O 4 ), maghemite (? -Fe 2 O 3 ), and the like, and the humidity control antimicrobial agent is preferably at least one selected from the group consisting of Sr-Fe 12 O 19 , Ba- O 3), it is formed of a nickel ferrite (Ni-Fe 2 O 4), and cobalt ferrite (Co-Fe 2 O 4) of from 30 to 100nm particle size of the oxide composed of at least one selected from the group consisting of ceramic-based magnetic nanopowders Preferably, the dispersion stabilizer is at least one selected from the group consisting of ethanolamine, methyldiethanolamine, triethanolamine, hexanolamine, hydroxyalkylamine, piperidine and N-methylpiperidine. It is right.
상기 인쇄층(20)의 두께가 0.05 밀리미터 미만이면 외관품질이 우수한 인쇄층(20)을 제공할 수 없으며, 상기 인쇄층(20)의 두께가 0.1 밀리미터를 초과하게 되면 외부의 충격에 의해 인쇄층(20)에 균열이 쉽게 발생할 수 있다.
When the thickness of the
상기 코팅층(30)은 상기 인쇄층(20)의 상부면에 3 내지 7 마이크로미터의 두께로 형성되며, 투명 폴리우레탄으로 이루어지는데, 상기의 두께로 형성되는 코팅층(30)은 상기 인쇄층(20)을 보호하며, 본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트의 외관품질을 개선할 뿐만 아니라, 투명 폴리우레탄으로 이루어져 피부트러블을 유발하지 않는 매트를 제공하는 역할을 한다.The
상기 코팅층(30)의 두께가 3 마이크로미터 미만이면 상기 인쇄층(20)의 보호효과가 저하되며, 상기 코팅층(30)의 두께가 7 마이크로미터를 초과하게 되면 코팅층(30)의 투명도가 저하되어 상기 인쇄층(20)에 형성되는 각종 무늬나 로고 등의 품질이 저하될 수 있다.When the thickness of the
이때, 상기 코팅층(30)을 구성하는 폴리우레탄은 상기 인쇄층에 형성되는 각종 무늬나 로고 등의 품질이 저하되지 않도록 안료나 마스터 배치 등이 함유되지 않은 투명한 폴리우레탄을 사용하는 것이 바람직한데, 상기 투명 폴리우레탄은 수분의 함량이 0.01 내지 0.05 중량%이며, 경화제의 주원료인 폴리에스테르폴리올의 점도를 500 내지 2,000cps(40℃)로 제한하고, 가교제의 함량을 2 내지 5 중량%로 제한하며, 주제 및 경화제를 포함하는 반응 원료의 사용 온도를 50 내지 60℃로 하여 제조되는 것이 바람직하다.At this time, the polyurethane constituting the
상기 투명 폴리우레탄의 제조방법을 더욱 상세하게 설명하면, 상기 투명 폴리우레탄은 주제와 경화제의 혼합시 임펠러의 날개 방향을 이중화하여 임펠러가 회전할 때에, 제1방향의 날개에 의하여 발생하는 기포가 제2방향으로 편향된 날개에 의하여 상쇄되도록 임펠러의 회전 방향을 이중화하는 방법으로 제조되며, 우레탄의 제조를 위한 주제와 경화제의 혼합시 임펠러의 회전 속도를 1,000 내지 5,000rpm으로 하는 것이 바람직하며, 주제와 경화제의 혼합 이전에 주제 및 경화제의 각 원료 탱크에서 교반기를 작동시키지 않고 원료 탱크에 건조 공기 주입을 차단하는 것이 바람직하다.
The method of manufacturing the transparent polyurethane according to the present invention will be described in more detail. When the impeller is rotated by doubling the direction of impeller blending when mixing a main body and a curing agent, the transparent polyurethane has a structure in which bubbles generated by the wings in the first direction It is preferable that the rotational speed of the impeller is set to 1,000 to 5,000 rpm when mixing the curing agent with the subject for the production of the urethane, It is preferable to block the dry air injection into the raw material tank without operating the agitator in the respective raw material tanks of the main and hardening agent before mixing.
또한, 본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트는 전사인쇄층(20-1) 및 상기 전사인쇄층(20-1)의 상부면에 형성되며, 폴리우레탄으로 이루어진 코팅층(30-1)으로 이루어질 수도 있다.The finish sheet for a polyurethane-coated floor mat according to the present invention is formed on the upper surface of the transfer printing layer 20-1 and the transfer printing layer 20-1, and the coating layer 30- 1).
상기 전사인쇄층(20-1)은 고온의 특정온도와 압력에서 전사를 통해 형성되는 인쇄층으로 전사를 통해 상기 바닥용 매트의 표면에 형성된 전사인쇄층(20-1)은 바닥용 매트의 표면과 우수한 밀착성을 나타내며, 발포체로 이루어진 바닥용 매트에 스며들지 않고 우수한 품질을 나타내는 무늬나 로고를 제공하는 역할을 하며, 상기 코팅층(30-1)은 상기에 기재된 코팅층(30)의 내용과 성분, 두께 및 역할이 동일하므로 이에 대한 내용은 생략하기로 한다.
The transfer printing layer 20-1 formed on the surface of the bottom mat through transfer to a printing layer formed through transfer at a high temperature and at a specific temperature and pressure is formed on the surface of the floor mat And serves to provide a pattern or logo that does not permeate the bottom mat made of foam and exhibits excellent quality. The coating layer 30-1 is formed of the content and composition of the
따라서, 본 발명에 따른 폴리우레탄이 코팅된 바닥 매트용 마감시트는 접착제의 사용없이 바닥 매트의 표면에 열융착의 과정을 통해 형성되기 때문에 친환경적이며, 폴리우레탄으로 표면처리되어 피부트러블을 유발하지 않고, 다양한 무늬를 형성할 수 있는 바닥용 매트를 제공한다.
Thus, the polyurethane-coated floor mat according to the present invention is environmentally-friendly because it is formed on the surface of the floor mat by thermal fusion without the use of an adhesive, and is surface-treated with polyurethane to cause no skin trouble , And a floor mat capable of forming various patterns.
10 ; 필름층
20 ; 인쇄층
20-1 ; 전사인쇄층
30, 30-1 ; 코팅층10; Film layer
20; Printing layer
20-1; Transfer printing layer
30, 30-1; Coating layer
Claims (7)
상기 필름층의 상부면에 형성되는 인쇄층; 및
상기 인쇄층의 상부면에 형성되며, 폴리우레탄으로 이루어진 코팅층;으로 이루어지고,
상기 코팅층은, 투명 폴리우레탄으로 이루어지고,
상기 투명 폴리우레탄은 수분의 함량이 0.01 내지 0.05 중량%이며, 경화제의 주원료인 폴리에스테르폴리올의 점도를 500 내지 2,000cps(40℃)로 제한하고, 가교제의 함량을 2 내지 5 중량%로 제한하며, 주제 및 경화제를 포함하는 반응 원료의 사용 온도를 50 내지 60℃로 하여 제조되는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트.
A film layer;
A printing layer formed on an upper surface of the film layer; And
And a coating layer formed on the upper surface of the printing layer and made of polyurethane,
Wherein the coating layer is made of a transparent polyurethane,
The content of water in the transparent polyurethane is 0.01 to 0.05% by weight, the viscosity of the polyester polyol as the main ingredient of the curing agent is limited to 500 to 2,000 cps (40 캜), the content of the crosslinking agent is limited to 2 to 5% , A base, and a curing agent at a temperature of 50 to 60 占 폚. The finish sheet for a polyurethane-coated floor mat according to claim 1,
상기 필름층은 폴리에틸렌 또는 에틸렌비닐아세테이트로 이루어지는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트.
The method according to claim 1,
Wherein the film layer is made of polyethylene or ethylene vinyl acetate.
상기 코팅층은 3 내지 7 마이크로미터의 두께로 형성되며, 투명 폴리우레탄으로 이루어지는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트.
The method according to claim 1,
Wherein the coating layer is formed to a thickness of 3 to 7 micrometers and is made of transparent polyurethane.
상기 전사인쇄층의 상부면에 형성되며, 폴리우레탄으로 이루어진 코팅층;으로 이루어지고,
상기 코팅층은, 투명 폴리우레탄으로 이루어지고,
상기 투명 폴리우레탄은 수분의 함량이 0.01 내지 0.05 중량%이며, 경화제의 주원료인 폴리에스테르폴리올의 점도를 500 내지 2,000cps(40℃)로 제한하고, 가교제의 함량을 2 내지 5 중량%로 제한하며, 주제 및 경화제를 포함하는 반응 원료의 사용 온도를 50 내지 60℃로 하여 제조되는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트.
A transfer printing layer; And
And a coating layer formed on the upper surface of the transfer printing layer and made of polyurethane,
Wherein the coating layer is made of a transparent polyurethane,
The content of water in the transparent polyurethane is 0.01 to 0.05% by weight, the viscosity of the polyester polyol as the main ingredient of the curing agent is limited to 500 to 2,000 cps (40 캜), the content of the crosslinking agent is limited to 2 to 5% , A base, and a curing agent at a temperature of 50 to 60 占 폚. The finish sheet for a polyurethane-coated floor mat according to claim 1,
상기 코팅층은 3 내지 7 마이크로미터의 두께로 형성되며, 투명 폴리우레탄으로 이루어지는 것을 특징으로 하는 폴리우레탄이 코팅된 바닥 매트용 마감시트.
The method of claim 5,
Wherein the coating layer is formed to a thickness of 3 to 7 micrometers and is made of transparent polyurethane.