KR101092047B1 - Removable And Reattachable Wallpaper - Google Patents
Removable And Reattachable Wallpaper Download PDFInfo
- Publication number
- KR101092047B1 KR101092047B1 KR1020080088554A KR20080088554A KR101092047B1 KR 101092047 B1 KR101092047 B1 KR 101092047B1 KR 1020080088554 A KR1020080088554 A KR 1020080088554A KR 20080088554 A KR20080088554 A KR 20080088554A KR 101092047 B1 KR101092047 B1 KR 101092047B1
- Authority
- KR
- South Korea
- Prior art keywords
- wallpaper
- layer
- resin
- pressure
- sensitive adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
본 발명은 탈·부착이 가능한 벽지를 제공한다. 본 발명에 따른 벽지는 입체적 형상 또는 평면적 모양이 인쇄된 인쇄층, 상기 인쇄층 하에 형성되고 수지로 된 수지층, 상기 수지층 하에 형성되고 수지가 함침된 종이로 된 기재층, 상기 기재층 하에 형성되고 실리콘 공중합체를 포함하는 수지 조성물로 된 재부착성 점착제로 형성되는 점착제층 및 상기 점착제층 하에 형성되어 상기 점착제층을 보호하고 사용시에는 제거되는 이형지를 포함한다. 본 발명에 따른 벽지는 벽지의 시공 시에 탈·부착이 가능하므로 초보자라도 용이하게 벽지를 시공할 수 있으며, 또한 시공 후 일정기간 사용 후에도 여전히 탈·부착이 가능하여 사용자의 기호에 따라 벽지를 편리하게 자주 교체할 수 있다. The present invention provides a wallpaper that can be attached and detached. The wallpaper according to the present invention is a printed layer having a three-dimensional or planar shape printed thereon, a resin layer formed under the print layer and made of resin, a base layer made of paper formed under the resin layer and impregnated with resin, and formed under the base layer. And a pressure-sensitive adhesive layer formed of a repositionable pressure-sensitive adhesive of a resin composition comprising a silicone copolymer, and a release paper formed under the pressure-sensitive adhesive layer to protect the pressure-sensitive adhesive layer and to be removed upon use. Since the wallpaper according to the present invention can be detached and attached during the construction of the wallpaper, even a beginner can easily install the wallpaper, and after the construction, the wallpaper can be detached and attached even after a certain period of time. Can be replaced as often as possible.
벽지, 재부착성 점착제 층, 실리콘 공중합체, 기재층, 수지 함침 Wallpaper, Re-adhesive Adhesive Layer, Silicone Copolymer, Substrate Layer, Resin Impregnation
Description
본 발명은 탈·부착이 가능한 벽지에 관한 것으로서, 더욱 상세하게는, 벽지의 기재층 하에 실리콘 공중합체를 포함하는 수지 조성물로 된 재부착성 점착제층을 포함함으로써 벽지의 탈·부착이 가능하여 누구라도 간편하게 시공할 수 있는 재부착이 가능한 벽지에 관한 것이다.The present invention relates to a wallpaper that can be attached and detached, and more particularly, by including a reattachable adhesive layer made of a resin composition containing a silicone copolymer under the base material layer of the wallpaper. The present invention relates to a wallpaper that can be easily reattached even if it is easily installed.
일반적으로 PVC 실크벽지 및 합지 벽지와 같은 벽지는 녹말풀이나 수지성 접착제를 벽지에 바른 후 실내의 초배지 위에 부착하는 습식방식으로 시공한다. 따라서 이러한 벽지의 시공은 전문인력에 의하여 수행되어야 하며 또한 상당한 공간과 시간이 요구된다. In general, wallpaper such as PVC silk wallpaper and laminated wallpaper is applied by a wet method of applying starch paste or resinous adhesive to the wallpaper and then attaching it to the super medium of the room. Therefore, the construction of such wallpaper must be performed by professional personnel and requires considerable space and time.
또 다른 벽지로서, PVC 수지층 하부에 점착제를 도포하여 제조되는 인테리어 필름은 점착방식으로 시공할 수 있는 장점은 있지만 기재가 없기 때문에 내열성 저하로 엠보싱이 어려워서 표면에 입체감을 표현하는데 한계가 있고, 목공, 퍼티(putty), 프라이머(primer), 샌딩(sanding) 등과 같은 사전작업을 필요로 할 뿐 만 아니라 영구적인 점착제를 사용하기 때문에 인테리어 필름의 교체가 어려우며, 전문 시공업자에 의한 시공이 필요하기 때문에 소비자가 직접 DIY(Do It Yourself) 방식으로 유행하는 패턴의 벽지로 자기만의 공간을 표현하는데 많은 한계가 있다.As another wallpaper, the interior film produced by applying a pressure-sensitive adhesive to the bottom of the PVC resin layer has the advantage that it can be applied by the adhesive method, but since there is no base material, it is difficult to emboss due to heat resistance deterioration, and thus there is a limit to expressing a three-dimensional effect on the surface. Not only does it require preliminary work like putty, primer, sanding, etc., but also permanent adhesives make it difficult to replace interior films, and it requires construction by professional contractors. There are a lot of limitations in expressing one's own space with wallpaper of pattern that is popular by consumers in DIY (Do It Yourself) method.
대한민국 공개특허 제2003-0060086호는 착탈이 용이한 인테리어 벽지를 개시하고 있다. 이 특허출원은 표면벽지의 이면에 접착제층이 마련된 통상의 벽지가 재부착이 불가능하다는 단점을 개선한 것으로서, 표면벽지와 접착제층 사이에 폴리에스탈 코팅층을 삽입시킴으로써 표면벽지를 보강함에 의해 보호하여 벽지의 탈착시에 표면벽지가 찢어지는 것을 방지한다는 것이다. 즉, 벽지의 탈·부착이 가능하도록 함으로써 초보자도 벽지를 시공할 수 있게 한다는 것이다.Korean Patent Laid-Open Publication No. 2003-0060086 discloses an interior wallpaper that is easily removable. This patent application improves the disadvantage that ordinary wallpaper provided with an adhesive layer on the back side of the surface wallpaper cannot be reattached, and is protected by reinforcing the surface wallpaper by inserting a polyester coating layer between the surface wallpaper and the adhesive layer. It is to prevent the surface wallpaper from tearing when the wallpaper is detached. In other words, by allowing the detachment and attachment of the wallpaper, even beginners can construct the wallpaper.
따라서, 본 발명의 목적은 벽지의 탈·부착이 가능하여 초보자가 용이하게 벽지를 벽에 부착하는 시공을 할 수 있는 DIY형 벽지를 제공하는 것이다. Accordingly, an object of the present invention is to provide a DIY type wallpaper that can be installed and attached to the wall can be easily attached or detached wallpaper for beginners.
또한 본 발명의 목적은 시공 시에 여러 번 탈·부착을 할 수 있을 뿐만 아니라 시공 후 일정기간 사용 후에도 여전히 탈·부착이 가능하여 사용자의 취향에 따라 자주 교체할 수 있는 DIY형 벽지를 제공하는 것이다.It is also an object of the present invention to provide a DIY wallpaper that can be replaced and detached according to the user's preference, as it can be detached and attached several times during construction, and still can be detached and attached after a certain period of use after construction. .
본 발명은 탈·부착이 가능한 벽지를 제공한다. 본 발명에 따른 벽지는 입체적 형상 또는 평면적 모양이 인쇄된 인쇄층, 상기 인쇄층 하에 형성되고 수지로 된 수지층, 상기 수지층 하에 형성되고 수지가 함침된 종이로 된 기재층, 상기 기재층 하에 형성되고 실리콘 공중합체를 포함하는 수지 조성물로 된 재부착성 점착제로 형성되는 점착제층 및 상기 점착제층 하에 형성되어 상기 점착제층을 보호하고 사용시에는 제거되는 이형지를 포함한다. 여기에서, 상기 기재층에 사용되는 수지는 아크릴계 수지, 멜라민 수지, 요소 수지 및 이들의 혼합물들로 이루어진 군으로부터 선택되는 것이 바람직하고, 상기 기재층에 함침되는 수지의 양은 상기 기재층의 종이의 양에 대하여 0.05 ~ 0.3 배인 것이 바람직하다. 특히, 상기 기재층과 상기 점착제층은 1,500 N/cm2 이상, 바람직하게는 2,000 N/cm2 이상의 수직 방향 장력으 로는 박리되지 않을 정도로 강력하게 결합되어 있는 것이 바람직하다. The present invention provides a wallpaper that can be attached and detached. The wallpaper according to the present invention is a printed layer having a three-dimensional or planar shape printed thereon, a resin layer formed under the print layer and made of resin, a base layer made of paper formed under the resin layer and impregnated with resin, and formed under the base layer. And a pressure-sensitive adhesive layer formed of a repositionable pressure-sensitive adhesive of a resin composition comprising a silicone copolymer, and a release paper formed under the pressure-sensitive adhesive layer to protect the pressure-sensitive adhesive layer and to be removed upon use. Here, the resin used in the base layer is preferably selected from the group consisting of acrylic resins, melamine resins, urea resins and mixtures thereof, and the amount of resin impregnated in the base layer is the amount of paper in the base layer. It is preferable that it is 0.05 to 0.3 times. In particular, the base material layer and the pressure-sensitive adhesive layer is preferably strongly bonded so as not to peel off with a vertical tension of 1,500 N / cm 2 or more, preferably 2,000 N / cm 2 or more.
본 발명에 따른 벽지는 벽지의 시공 시에 탈·부착이 가능하므로 초보자라도 용이하게 벽지를 시공할 수 있으며, 또한 시공 후 일정기간 사용 후에도 여전히 탈·부착이 가능하여 사용자의 기호에 따라 벽지를 편리하게 자주 교체할 수 있다.Since the wallpaper according to the present invention can be detached and attached during the construction of the wallpaper, even a beginner can easily install the wallpaper, and after the construction, the wallpaper can be detached and attached even after a certain period of time. Can be replaced as often as possible.
이하 도면을 참조하여 본 발명을 상세하게 설명한다. Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 벽지의 구조를 나타낸 단면도이다.1 is a cross-sectional view showing the structure of a wallpaper according to the present invention.
도 1에 도시된 바와 같이, 본 발명의 탈·부착이 가능한 벽지는 위로부터 아래쪽 방향으로, 인쇄층(10), 수지층(20), 기재층(30), 점착제층(40) 및 이형지(50)가 차례로 적층되어 있는 구조를 가진다. As illustrated in FIG. 1, the detachable wallpaper of the present invention has a printed layer 10, a resin layer 20, a base layer 30, an adhesive layer 40, and a release paper (from top to bottom). 50) is laminated in order.
본 발명의 구조에서 인쇄층(10)은 평면적 문양 또는 입체적 문양을 표현함으로써 벽지의 장식적 미를 더욱 표현하는 것으로서, 표면 상에 인쇄가 가능한 수지 또는 종이로 된 층에 예를 들어, 실크스크린 인쇄에 의하여 문양이 인쇄되어 있는 것이다. 이러한 인쇄층(10)은 통상적인 벽지에 구현되는 것으로서, 본 발명에서는 알려진 방법에 의하여 형성될 수 있다. 입체적 문양을 위하여 발포제가 인쇄층(10)에 포함되기도 한다.In the structure of the present invention, the print layer 10 further expresses the decorative beauty of the wallpaper by expressing a planar pattern or a three-dimensional pattern, for example, silkscreen printing on a layer of resin or paper that can be printed on the surface. The pattern is printed by. The printed layer 10 is implemented in a conventional wallpaper, it can be formed by a method known in the present invention. A foaming agent may be included in the print layer 10 for a three-dimensional pattern.
수지층(20)은 주로 벽지의 기재층(30)과 인쇄층(10)을 결합시키는 바인더 역 할을 하는 것이며, 본 발명에서 사용되는 수지로는 일반적인 수지가 사용될 수 있다. The resin layer 20 mainly serves as a binder for bonding the base material layer 30 and the print layer 10 of the wallpaper, and a general resin may be used as the resin used in the present invention.
기재층(30)은 펄프로부터 제조되는 종이 또는 합성수지로 제조되는 종이 또는 부직포로 이루어질 수 있다. 이러한 기재층의 재료는 일반적으로 알려져 있으며, 본 발명에서는 알려진 재료 및 방법에 따라 기재층을 형성할 수 있다. 본 발명에서는 특히, 기재층(30)에 수지가 함침되어 있다. 기재층(30)에 함침되는 수지로는 다른 수지들이 사용될 수 있으나, 특히 아크릴계 수지, 멜라민 수지, 요소 수지 및 이들의 혼합물들로부터 선택되는 것이 바람직하다. 함침되는 양은 기재층의 종이의 양에 대하여 0.05~0.3배 정도가 바람직하다. 즉, 예를 들어, 기재 100 g/m2에 대하여 5~30 g/m2일 수 있다. 기재층에 함침되는 수지는 기재층(30)이 수지층(20)과 잘 결합되게 할 뿐만 아니라 점착제층(40)과도 잘 결합되게 하는 역할을 한다. The base layer 30 may be made of paper or nonwoven fabric made of paper or synthetic resin made from pulp. The material of such a substrate layer is generally known, and in the present invention, the substrate layer can be formed according to known materials and methods. Especially in this invention, resin is impregnated into the base material layer 30. Other resins may be used as the resin impregnated with the base layer 30, but it is particularly preferable to select from acrylic resins, melamine resins, urea resins, and mixtures thereof. The amount of impregnation is preferably about 0.05 to 0.3 times the amount of the paper of the base layer. That is, for example, it may be from 5 to 30 g / m 2 with respect to the substrate 100 g / m 2 . The resin impregnated in the base layer serves to not only bond the base layer 30 to the resin layer 20 well but also to the adhesive layer 40.
본 발명의 벽지에 포함되는 점착제층(40)은 재부착성 점착제 조성물로 형성되는 것으로서, 바람직하게는, 표준적인 측정방법에 따라 측정한 값으로서 그 점착강도가 1.0 내지 3.0 kg/25mm 인 것이 바람직하다. 여기에서 표준적인 측정방법은 KS A 1107:1992에 의하여 측정하는 방법이다. 본 발명에서 재부착성 점착제층이라 함은 콘크리트 벽면, 기존 벽지의 수지층을 벗겨낸 벽면, 합판 또는 MDF 벽면, 일반적인 PVC실크 벽지 벽면 등 여러 가지 벽면에 부착된 후 일정한 시간(20분)이 경과된 후에도 깨끗하게 탈착/재부착이 가능하여 재시공이 가능할 뿐만 아니라 장시간(1~2년) 경과 후에도 깔끔한 탈착이 가능하여 사용자의 취향에 따라 자주 교체할 수 있는 점착제층을 말한다. 따라서, 이러한 점착제층의 성질에 의하여 본 발명의 벽지를 이미 벽에 부착되어 있는 어떤 기재 또는 다른 벽지로부터 탈착시킬 때 이미 벽에 부착되어 있는 그 기재 또는 벽지를 손상시킴이 없이 본 발명의 벽지는 용이하게 탈착될 수 있고 또한 다른 기재 또는 벽지 상에 부착할 수 있다. 지금까지 재부착성 점착제 조성물은 다른 분야에서 적용되어 왔으나 그것의 점착강도는 일반적으로 벽지에 사용되기에는 너무 약한 것이었다. 재부착성 점착제가 벽지에 사용되기 위해서는 그 강도가 일정 정도 이상, 통상 1.0 kg/25mm 이상, 즉 벽지에서 요구하는 정도가 되어야 한다. 따라서, 벽지에 재부착성 점착제층을 형성하려는 시도는 지금까지 거의 없었고, 있었다고 하더라도 적합한 재료를 적절하게 찾지 못하였다. The pressure-sensitive adhesive layer 40 included in the wallpaper of the present invention is formed of a re-adhesive pressure-sensitive adhesive composition, and preferably, a value measured according to a standard measuring method, and its adhesive strength is 1.0 to 3.0 kg / 25mm. Do. Here, the standard measuring method is a method measured by KS A 1107: 1992. Re-adhesive pressure-sensitive adhesive layer in the present invention is a certain time (20 minutes) after being adhered to a variety of walls, such as a wall of the concrete, peeling off the resin layer of the existing wallpaper, plywood or MDF wall, general PVC silk wallpaper wall It is possible to replace / reattach even after it is clean, so that it is not only possible to reconstruct, but also to be easily removed after a long time (1 ~ 2 years). Therefore, the wallpaper of the present invention can be easily removed by the nature of the pressure-sensitive adhesive layer without damaging the substrate or wallpaper already attached to the wall when the wallpaper of the present invention is detached from any substrate or other wallpaper already attached to the wall. Can be detached and attached to other substrates or wallpaper. Until now, re-adhesive pressure-sensitive adhesive composition has been applied in other fields, but its adhesive strength was generally too weak to be used for wallpaper. In order for a repositionable adhesive to be used for a wallpaper, the strength must be at least a certain level, usually 1.0 kg / 25 mm or more, that is, a degree required by the wallpaper. Therefore, few attempts have been made to form a repositionable pressure-sensitive adhesive layer on wallpaper, and even if it has been, a suitable material has not been found properly.
이에, 이러한 재부착성 점착제층을 형성하기 위하여 본 발명에서는 특정 실리콘 공중합체를 10 내지 60 중량% 포함하는 수지 조성물이 고안된다. 이러한 수지 조성물로부터 통상의 방법에 따라 기재층(30) 상에 재부착성 점착제층(40)이 형성된다. 이러한 점착제층(40)은 필요에 따라 적절한 두께로 형성될 수 있으며, 바람직하게는 0.02 ~ 0.045 mm의 두께로 형성될 수 있다. Thus, in order to form such a repositionable pressure-sensitive adhesive layer in the present invention, a resin composition containing 10 to 60% by weight of a specific silicone copolymer is devised. From such a resin composition, the repositionable adhesive layer 40 is formed on the base material layer 30 according to a conventional method. The pressure-sensitive adhesive layer 40 may be formed to an appropriate thickness as needed, preferably may be formed to a thickness of 0.02 ~ 0.045 mm.
다음으로 점착제층(40)을 보호하기 위하여 점착제층(40) 하에 이형지(50)가 형성된다. 이러한 이형지(50)는 본 발명의 벽지를 시공하기 전에 벗겨진다.Next, a release paper 50 is formed under the pressure-sensitive adhesive layer 40 to protect the pressure-sensitive adhesive layer 40. This release paper 50 is peeled off before constructing the wallpaper of the present invention.
따라서, 본 발명의 벽지는 우선적으로, 점착제층이 재부착이 가능한 점착제로 형성됨으로써 그 점착제의 특성에 따라 벽지가 벽에 부착된 상태로 유지될 수 있고 또한 정해진 강도 이상의 힘을 가하면 탈착이 이루어지고 또한 다시 부착이 가능하다는 특성을 가진다. 이러한 본 발명의 벽지는 탈착 시 피착벽면에 본 발명의 점착제를 남기지 않는다.Therefore, in the wallpaper of the present invention, the pressure-sensitive adhesive layer is first formed of an adhesive which can be reattached, so that the wallpaper can be kept attached to the wall according to the characteristics of the pressure-sensitive adhesive. It also has the property of being reattached. Such wallpaper of the present invention does not leave the pressure-sensitive adhesive of the present invention on the adhered wall surface when desorption.
본 발명의 벽지는 또한 점착제층(40)은 기재층(30)과 매우 강하게 결합되어 있다는 특징을 가진다. 특히, 바람직하게는 피착벽면과 점착제층 간의 접착력보다 점착제층과 기재층 간의 접착력이 더 크다는 특징을 가진다. 기재층(30)이 수지의 함침 없이 통상적인 조건으로, 즉 펄프로 된 종이로 만들어지는 경우에는 본 발명에서 사용하는 재부착성 점착제층과 결합하는 경우 그것의 수직방향, 즉 z-방향 장력(z-direction tensile strength)이 400 N/cm2 정도로 작용하면 기재층과 점착제층이 박리되는 반면에, 본 발명에서와 같이 수지가 함침된 기재층(30)이 재부착성 점착제층(40)과 결합하는 경우 z-방향 장력이 2,000 N/cm2 정도로 작용하여야 기재층(30)과 점착제층(40)이 비로소 박리된다. 따라서, 본 발명의 벽지에서, 기재층(30)과 점착제층(40)은 1,500 N/cm2 이상, 바람직하게는, 2,000 N/cm2의 수직 방향 장력으로는 박리되지 않을 정도로 강력하게 결합되어 있는 것이다. 이러한 기재층과 점착제층 간의 접착력은 상기에 기재된 바와 같은 피착벽면과 본 발명의 벽지의 점착제층 간의 접착력보다 크다. 따라서, 본 발명의 벽지는 탈착할 때 기재층과 점착제층 사이에서 박리가 발생하지 않는다. 즉, 본 발명의 벽지는 탈착할 때 벽지가 찢어지거나 파괴되는 일이 없다. The wallpaper of the present invention is also characterized in that the pressure-sensitive adhesive layer 40 is very strongly bonded to the base layer 30. In particular, preferably, the adhesive force between the adhesive layer and the substrate layer is greater than the adhesive force between the adhered wall surface and the adhesive layer. When the base layer 30 is made of paper made of pulp under ordinary conditions without impregnation of resin, that is, when combined with the repositionable pressure-sensitive adhesive layer used in the present invention, its vertical direction, i.e., z-direction tension ( When the z-direction tensile strength acts at about 400 N / cm 2 , the base layer and the pressure-sensitive adhesive layer are peeled off, whereas the base material layer 30 impregnated with the resin is re-adhesive pressure-sensitive adhesive layer 40 as in the present invention. In the case of bonding, the base layer 30 and the pressure-sensitive adhesive layer 40 must be peeled off when the z-direction tension acts at about 2,000 N / cm 2 . Therefore, in the wallpaper of the present invention, the base material layer 30 and the pressure-sensitive adhesive layer 40 are strongly bonded so as not to be peeled off with a vertical tension of 1,500 N / cm 2 or more, preferably 2,000 N / cm 2 . It is. The adhesive force between this base material layer and the adhesive layer is larger than the adhesive force between the adhered wall surface as described above and the adhesive layer of the wallpaper of the present invention. Therefore, when the wallpaper of the present invention is detached, no peeling occurs between the base layer and the pressure-sensitive adhesive layer. That is, the wallpaper of the present invention does not torn or destroyed when the wallpaper is detached.
따라서, 이러한 두 가지 특성의 조합에 의하여, 본 발명의 벽지는 피착벽면 의 파괴없이 그리고 본 발명의 벽지의 기재층 또는 인쇄층의 파괴없이 안전하게 탈착이 가능하고 또한 다시 부착이 가능하게 된다. 즉, 본 발명의 벽지는 특히, 수지가 함침된 기재층(30)과 특정 물질로 되는 점착제층(40)이 적층되어 형성되는 구조 및 특성에 의하여, 본 발명의 벽지가 피착벽면에 오염물질을 남기지 않으면서 그리고 그 피착벽면의 파괴없이 그 피착벽면으로부터 용이하게 탈·부착될 수 있다. 본 발명의 벽지는 또한 기재층(30)과 점착제층(40)이 매우 강하게 결합되어 있으므로, 벽지의 탈착 시에 기재층(30) 또는 인쇄층(10)이 파괴되지 않는다. Therefore, by the combination of these two characteristics, the wallpaper of the present invention can be safely detached and reattached without breaking the adhered wall surface and without destroying the base layer or the print layer of the wallpaper of the present invention. That is, the wallpaper of the present invention, in particular, due to the structure and characteristics formed by laminating the resin-impregnated base layer 30 and the pressure-sensitive adhesive layer 40 made of a specific material, the wallpaper of the present invention is a contaminant on the adhered wall surface It can be easily detached from or attached to the adhered wall surface without leaving it and without destroying the adhered wall surface. In the wallpaper of the present invention, the base layer 30 and the pressure-sensitive adhesive layer 40 are also very strongly bonded, so that the base layer 30 or the print layer 10 is not destroyed when the wallpaper is detached.
따라서, 본 발명의 벽지는 벽지의 시공 시에 탈·부착이 가능하므로 초보자라도 용이하게 벽지를 시공할 수 있으며, 또한 시공 후 일정기간 사용 후에도 여전히 탈·부착이 가능하여 사용자의 기호에 따라 벽지를 편리하게 자주 교체할 수 있다. 이러한 본 발명의 벽지는 최소한 10회 까지는 탈·부착이 가능하며, 그 이상의 회수의 사용도 가능할 것으로 예상되며, 조건을 최적화시킨다면 상당한 회수만큼 사용할 수 있을 것이다.Therefore, the wallpaper of the present invention can be detached and attached at the time of construction of the wallpaper, so even beginners can easily install the wallpaper, and after the construction, it is still possible to detach and attach the wallpaper according to the user's preference. It can be replaced frequently and conveniently. The wallpaper of the present invention can be attached and detached at least 10 times, and it is expected that the use of more times is possible, and if the conditions are optimized, it can be used as a considerable number of times.
이하, 본 발명을 실시예를 통하여 더욱 구체적으로 설명한다. 하기의 실시예는 본 발명에 대한 예시일 뿐이므로 본 발명의 범위를 제한하는 것으로 이해되어서는 아니 된다.Hereinafter, the present invention will be described in more detail with reference to Examples. The following examples are merely illustrative of the invention and should not be construed as limiting the scope of the invention.
실시예Example
통상적인 벽지의 제조방법에 따라 인쇄층, 수지층, 기재층, 점착제층 및 이 형지가 차례로 적층된 벽지를 제조하되, 기재층은 원지 100 g/m2에 함침 수지로서 수성 아크릴 수지를 10 g/m2의 함침량으로 함침시켜 제조된 것을 사용하였다. 그리고 점착제층은 특정 실리콘 공중합체를 10 내지 60 중량% 포함하는 수지 조성물로 이루어진 재부착성 점착제를 두께 0.020~0.045 mm로 코팅하여 형성하였다. 이와 같이, 제조한 벽지는 이형지를 제거한 후, 이미 PVC 실크벽지가 부착된 벽면에 부착하고 탈착하기를 반복하였다. 이러한 반복을 10회 까지 하였는데, 벽지는 이상 없이 재부착이 가능하였다. 한편, 상기와 같이 제조된 벽지를 이미 존재하는 실크벽지 벽면에 부착한 후 2~3일 후에 다시 떼어낸 후 다른 벽지 상에 부착하였는데, 이상 없이 재부착이 가능하였다.A printing layer, a resin layer, a base material layer, an adhesive layer, and a wallpaper in which the paper is laminated in this order are prepared according to a conventional method of manufacturing a wallpaper, and the base material layer is 100 g / m 2 of base paper and 10 g of an aqueous acrylic resin as an impregnating resin. The thing prepared by impregnation with the impregnation amount of / m <2> was used. And the pressure-sensitive adhesive layer was formed by coating a repositionable pressure-sensitive adhesive made of a resin composition containing 10 to 60% by weight of a specific silicone copolymer to a thickness of 0.020 ~ 0.045 mm. In this way, the prepared wallpaper was removed after the release paper, and then repeatedly attached to and detached from the wall already attached PVC silk wallpaper. This repeat was made up to 10 times, and the wallpaper could be reattached without error. On the other hand, after attaching the wallpaper prepared as described above to the existing silk wallpaper wall surface after 2-3 days after detaching again attached to another wallpaper, it was possible to reattach without abnormality.
또한 기재층과 점착제층 간의 점착강도를 알아보기 위하여 z-방향 장력을 테스트한 결과 2,000 N/m2 이상에서 비로소 두 층 간의 박리가 발생함을 확인하였다.In addition, the z-direction tension test to determine the adhesive strength between the base layer and the pressure-sensitive adhesive layer was confirmed that the peeling between the two layers only occurs at 2,000 N / m 2 or more.
비교예 1Comparative Example 1
인쇄층, 수지층 및 기재층으로 이루어진 통상적인 종래의 벽지의 기재층 하에 실시예 1에서 사용한 재부착성 점착제층을 코팅하여 벽지를 제조하였다. 이 벽지를 기존 PVC 실크 벽지 벽면에 부착한 후 탈착하였다. 이 때, 재부착성 점착제층이 벽에 이미 존재하는 벽지로부터 박리되지 않고, 이 비교예의 벽지의 기재층이 파괴되었으며 이는 기재층의 파괴는 1500 N/cm2 이하의 z-방향 장력에서 발생하였음 을 확인하였다.The wallpaper was prepared by coating the repositionable pressure-sensitive adhesive layer used in Example 1 under the substrate layer of a conventional conventional wallpaper consisting of a printing layer, a resin layer and a substrate layer. The wallpaper was attached to the existing PVC silk wallpaper and then removed. At this time, the re-adhesive pressure-sensitive adhesive layer did not peel off from the wallpaper already present on the wall, and the base layer of the wallpaper of this comparative example was broken, and the breakdown of the base layer occurred at a z-direction tension of 1500 N / cm 2 or less. It was confirmed.
비교예 2Comparative Example 2
실시예에서 재부착성 점착제층 대신에 일반 아크릴 점착제층을 사용한 것을 제외하고는 실시예와 동일한 방식으로 벽지를 제조하였다. 이 벽지를 기존 PVC 실크 벽지 벽면에 부착한 후 탈착 시 피착벽면의 벽지가 파괴되었으며, 이 벽지의 점착제층은 피착벽면의 벽지에 의하여 오염되었다. Wallpaper was prepared in the same manner as in Example, except that the general acrylic pressure-sensitive adhesive layer was used instead of the re-adhesive pressure-sensitive adhesive layer. After the wallpaper was attached to the existing PVC silk wallpaper, the wallpaper on the wall was destroyed when it was detached, and the adhesive layer of the wallpaper was contaminated by the wallpaper on the wall.
상기에서 보는 바와 같이, 아크릴 수지가 함침된 기재층과 특정 실리콘 공중합체를 포함하는 수지 조성물로 된 재부착성 점착제층이 라미네이팅되어 형성되는 본 발명의 실시예의 벽지는 기재층과 점착제층 간의 강력한 접착 그리고 재부착성 점착제의 특성의 조합에 의하여, 탈착 및 부착이 10회 이상 가능하며 또한 일정기간 후에도 여전히 탈착 및 부착이 가능함을 확인하였다. As seen above, the wallpaper of the embodiment of the present invention in which the repositionable pressure-sensitive adhesive layer formed of a resin composition containing an acrylic resin-impregnated base layer and a specific silicone copolymer is laminated is a strong adhesive between the base layer and the pressure-sensitive adhesive layer. And by the combination of the properties of the re-adhesive pressure-sensitive adhesive, it was confirmed that the desorption and attachment is possible more than 10 times, and still possible to detach and attach after a certain period.
도 1은 본 발명의 벽지의 단면 구조를 개략적으로 나타낸 것이다.Figure 1 schematically shows the cross-sectional structure of the wallpaper of the present invention.
Claims (9)