KR100275552B1 - Manufacturing method of non-flammable non-flammable coating waterproofing material and construction method using the waterproofing material - Google Patents
Manufacturing method of non-flammable non-flammable coating waterproofing material and construction method using the waterproofing material Download PDFInfo
- Publication number
- KR100275552B1 KR100275552B1 KR1019980035275A KR19980035275A KR100275552B1 KR 100275552 B1 KR100275552 B1 KR 100275552B1 KR 1019980035275 A KR1019980035275 A KR 1019980035275A KR 19980035275 A KR19980035275 A KR 19980035275A KR 100275552 B1 KR100275552 B1 KR 100275552B1
- Authority
- KR
- South Korea
- Prior art keywords
- flammable
- rubber
- waterproofing material
- coating
- coating waterproofing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
본 발명의 미가류 상태의 불연성 도막 방수재는 천연고무와 합성고무들 중 적어도 하나의 고무주재와 이 고무주재에 혼합되는 첨가물 및 이 첨가물이 혼합된 고무주재를 용해하므로써 미가류 상태의 불연성 도막 방수재를 형성하기 위한 불연성 용제로 이루어진다. 도막 방수재의 첨가물에는 가류조제, 점착부여제, 충진제, 가류제 등이 있으며, 불연성 용제는 트리크로로 에칠렌, 트리크로로 에탄, 퍼크로로 에칠렌 중 적어도 하나를 사용한다. 이와 같은 미가류 상태의 불연성 도막 방수재는 천연고무와 합성고무들 중 적어도 하나의 고무주재에 소정 첨가물을 혼합하여 생지고무를 준비하는 단계와 이 생지고무의 중량에 대응되도록 소정 불연성 용제를 생지고무와 혼합하여 생지고무를 불연성 용제에 용해하므로써 제조된다. 본 발명의 미가류 상태의 불연성 도막 방수재를 이용한 시공방법은 붓, 롤러, 그리고 스프레이 등으로 하도의 프라이머로 도막 방수 시공을 1차로 한 후 보강재인 PP,PE 또는 폴리에스테르 등 고분자 합성 섬유 재질의 부직포 또는 동일한 재질의 구멍이 뚤린 망사를 깔아 주고 그 위에 상도의 도막 방수재를 도포한 후, 3일 내지 5일간 용제가 충분히 건조하면서 2차로 활성화하여 성형 가류고무로 전환한다.The non-flammable non-flammable coating waterproofing material of the present invention dissolves at least one rubber main material of natural rubber and synthetic rubber, an additive mixed with the rubber main material, and a rubber main material mixed with the additive, thereby producing a non-flammable non-flammable coating waterproofing material. It consists of a nonflammable solvent to form. The additive of the coating waterproofing material includes a vulcanization aid, a tackifier, a filler, a vulcanizing agent, and the like, and a nonflammable solvent uses at least one of trichloroethylene, trichloroethane, and perchlorethylene. Such a non-vulcanized non-flammable coating waterproofing material is prepared by mixing a predetermined additive in at least one rubber base of natural rubber and synthetic rubber, and preparing a non-flammable solvent to correspond to the weight of the raw rubber. It is prepared by mixing raw rubber in a nonflammable solvent. The construction method using the non-vulcanized non-flammable coating waterproofing material of the present invention is a nonwoven fabric made of polymer synthetic fiber material such as PP, PE or polyester, which is a reinforcing material after first coating coating waterproofing with a primer of a primer, such as a brush, roller, and spray. Or lay a perforated mesh of the same material and apply a coating film waterproofing material on top of it, and then the solvent is sufficiently dried for 3 to 5 days to switch to a molding vulcanized rubber.
Description
본 발명은 불연성(난연성) 도막 방수재의 제조방법 및 그 방수재를 이용한 시공방법에 관한 것으로, 좀 더 상세하게는 불연성 용제에 미가류 고무를 용해한 미가류 상태(익지 않은 고무를 뜻함)의 도박 방수재로 시공한 후 용제가 증발하면서 활성화하여 성형 가류고무(익은 고무를 뜻함)로 전환되도록 하는 미가류 상태의 불연성 도막 방수재의 제조방법 및 그 방수재를 이용한 시공방법에 관한 것이다.The present invention relates to a method of manufacturing a non-flammable (flame retardant) coating waterproofing material and a construction method using the waterproofing material. The present invention relates to a method of manufacturing a non-vulcanized non-flammable coating waterproofing material which is activated by evaporation of a solvent after conversion and converted into molded vulcanized rubber (meaning ripe rubber), and a construction method using the waterproofing material.
최근, 급격한 교통량의 증가로 아스팔트 포장도로의 노면 파손이 증가하고 있으며 이에 따른 아스팔트 포장도로의 유지 및 보수를 위한 비용이 증가하고 있다. 교량의 경우, 철근 콘크리트 상판은 타 콘크리트 부재에 비교하여 두께가 얇고 포장면에 직접 교통하중을 받는 극한 상황 조건하에 있기 때문에 비교적 손상되기 쉽니다. 특히, 교량 포장면의 손상과 균열은 상판 표면으로 유입된 산성 빗물이 상판 내부에 침투하는 원인이 되어 콘크리트의 노화와 상판부의 철근부식을 촉진하고, 상판의 내구성을 현저하게 저하시키고 있어 이의 개선책이 절실히 필요하게 되었다. 즉, 급격한 교통량에 의한 교통하중의 증가로 인한 진동, 차량 배기가스, 그리고 산성비 등의 기상 조건에 대하여 아스팔트 포장도로와 교량의 상판을 보호하기 위해서는 내진동성과 내약품성(내산성)을 겸비하고 내구성이 우수하면서도 방수기능이 있는 소재가 필요하게 되었다.Recently, road damage on asphalt pavement has increased due to the rapid increase in traffic volume, and thus the cost for maintenance and repair of asphalt pavement has increased. In the case of bridges, reinforced concrete slabs are relatively fragile because they are thinner than other concrete members and under extreme conditions of direct traffic loads on the pavement. In particular, damage and cracks on the bridge pavement cause acid rainwater introduced into the top surface to penetrate the inside of the top plate, thereby promoting aging of the concrete and corrosion of the reinforcement of the top plate, and significantly reducing the durability of the top plate. It is desperately needed. That is, in order to protect the asphalt pavement and the top of the bridge against weather conditions such as vibration, vehicle exhaust gas, and acid rain due to the increase of traffic load due to the rapid traffic volume, it has vibration resistance and chemical resistance (acid resistance) and durability. Excellent and waterproof material is needed.
이와 같은 목적으로 종래에는 실리콘 침투 방수재, 고무화 아스팔트 시트, 고무화 아스팔트 도료(수성 도막방수), 성형 가류고무시트, 그리고 유기 용제형 고무도료(유성도막방수) 등을 방수재로 사용하여 왔다.For this purpose, conventionally, a silicon penetration waterproofing material, rubberized asphalt sheet, rubberized asphalt paint (waterproof film waterproofing), molded vulcanized rubber sheet, organic solvent type rubber paint (oilproof film waterproofing) and the like have been used as waterproofing materials.
그러나, 상술한 종래 방수재들은 각각 다음과 같은 문제점들 있다.However, the above-described conventional waterproof materials have the following problems, respectively.
상기 침투방수재는 최근 토목기술의 향상으로 시멘트의 강도가 350kg/cm 이상으로 강화되면서 침투시공 자체가 여의치 않아 불합리한 소재로 판명되었으며, 그 사용이 기피되고 있다.The penetration waterproofing material has recently been found to be an unreasonable material due to the infiltration construction itself as the strength of cement is enhanced to 350kg / cm or more due to the improvement of civil engineering technology, and its use has been avoided.
아스팔트를 주재료로 하는 방수재들인 상기 고무화 아스팔트 시트와 수용성 아스팔트 도료는 아스팔트 물성이므로 방수성을 갖고 있어 단기적으로 양호한 방수 성능을 발휘한다. 그러나, 상기 아스팔트를 주재료로하는 방수재들은 시간이 지날수록 탄성력이 감소된다. 특히, 여름철의 지표면이 30-40℃ 이상 올라가면, 상기 방수재들은 분해 증발하면서 경화되어 체적이 감소되고, 이에 따른 공간이 발생되므로 부분적으로 균열이 발생되면서 탈피상태가 되며, 반복하여 통과하는 차량하중에 의하여 더욱 더 균열 및 탈피 현상이 확대되면서 방수의 기능이 없어짐과 동시에 포장층이 파괴되는 문제점이 있다.As the asphalt-based waterproofing materials, the rubberized asphalt sheet and the water-soluble asphalt paint are asphalt physical properties and thus have waterproof properties and thus exhibit good waterproof performance in the short term. However, the waterproofing materials based on the asphalt decrease in elasticity over time. In particular, when the surface of the summer rises above 30-40 ℃, the waterproofing materials are hardened by decomposition and evaporation, the volume is reduced, and the space is generated accordingly, so that the cracks are partially peeled off, and the vehicle load repeatedly passes. Thereby, the crack and peeling phenomenon is further expanded, there is a problem that the waterproofing function is lost and the packaging layer is destroyed.
상기 성형 가류고무시트는 고무가 주재료이고 익혀서 시트를 제조하였으므로 고무 본래의 특성인 우수한 인장강도 및 신장률을 가지고 있다. 따라서, 진동과 충격 방지에도 좋고, 내약품성도 우수하며, 가류고무시트 자체의 방수기능도 우수하다. 그러나, 시트와 시트를 접속하는 연결부분의 시공이 까다롭고, 접착이 불완전한 경우가 많이 발생하며, 연결 부분의 누수로 인해 방수기능이 상실되는 폐단이 있었다.The molded vulcanized rubber sheet has a good tensile strength and elongation, which are inherent properties of rubber because the rubber is the main material and the sheet is prepared by cooking. Therefore, it is also good for vibration and shock prevention, excellent chemical resistance, and excellent waterproofing function of the vulcanized rubber sheet itself. However, the construction of the connection portion connecting the sheet and the sheet is difficult, often incomplete adhesion occurs, there was a closed end of the waterproof function is lost due to leakage of the connection portion.
고무를 주재료로 한 상기 유기 용제형 고무도료 방수재는 상기 성형 가류고무시트의 단점을 극복하기 위하여 개발되어 사용되고 있는 방수재이다. 상기 유성 고무도료 방수재의 제조방법은 주재료인 고무를 유기 용제인 톨루엔, 신너(thinner), 그리고 벤젠 등의 휘발성 용제에 액상 교반기로 용해하여 제조하게 된다. 따라서, 유성 고무도료 방수재는 성형 가류고무시트 방수재와 다르게 액상의 고무이므로 요철 부위의 시공이 간편하게 되고, 용제가 건조되면 고무만으로 조성된 고무시트가 형성된다. 그러나, 고무시트가 미가류된 고무생지 상태의 고무이므로 가류성형된 고무에 비하여 고무의 고유한 특성인 탄성과 인장강도 및 신장율이 떨어지게 된다. 게다가, 휘발성이 강한 방향족 유기 용제를 사용하기 때문에 시공 중에 대형 화재의 위험이 매우 크고 균일한 두께로 시공 작업하기가 어렵다.The organic solvent-type rubber paint waterproofing material based on rubber is a waterproofing material that has been developed and used to overcome the disadvantages of the molded vulcanized rubber sheet. The manufacturing method of the oil-based rubber paint waterproofing material is prepared by dissolving a rubber as a main material in a liquid stirrer in volatile solvents such as toluene, thinner, and benzene, which are organic solvents. Therefore, since the oil-based rubber paint waterproofing material is a liquid rubber unlike the molded vulcanized rubber sheet waterproofing material, the construction of the uneven portion is simplified, and when the solvent is dried, a rubber sheet composed of rubber is formed. However, since the rubber sheet is rubber in an unvulcanized rubber dough state, elasticity, tensile strength, and elongation, which are inherent to rubber, are inferior to those of vulcanized rubber. In addition, the use of highly volatile aromatic organic solvents greatly increases the risk of large fires during construction, and makes construction difficult to uniform thickness.
본 발명은 이와 같은 종래의 문제점을 해결하기 위한 것으로, 그 목적은 도로의 포장층, 교량의 상판, 그리고 건물의 천장·벽면·바닥 등에 용이하게 시공할 수 있고, 안정적이 작업을 유지할 수 있는 새로운 형태의 불연성 도막 방수재의 제조방법을 제공하는데 있다. 특히, 본 발명은 고무 본래의 특성인 탄성, 강인한 인장강도, 그리고 높은 신장률을 겸비하여 내구성이 우수하고 진동과 충격을 완화하며, 방수 성능이 향상된 미가류 상태의 불연성 도막 방수재의 제조방법을 제공하는데 있다. 본 발명의 다른 목적은 본 발명의 제조방법에 의한 미가류 상태의 불연성 도막 방수재를 이용하여 아스팔트를 포장하는 도로나 교량 또는 건축물 옥상이나 벽면의 방수성을 극대화시킬 수 있는 새로운 형태의 미가류 상태의 불연성 도막 방수재를 이용한 시공방법을 제공하는데 있다.The present invention is to solve such a conventional problem, the object of the present invention is to provide a paving layer of the road, the top plate of the bridge, and the ceiling, wall, floor, etc. of the building can be easily installed, new work that can maintain a stable work It is to provide a method of manufacturing a non-combustible coating waterproofing of the form. In particular, the present invention provides a method of manufacturing a non-flammable non-flammable coating waterproofing material having excellent durability, alleviating vibration and shock, and having improved waterproof performance by combining rubber's inherent properties such as elasticity, strong tensile strength, and high elongation. have. Another object of the present invention is a non-flammable non-flammable state of the new form that can maximize the waterproofness of roads, bridges or roofs or walls paving asphalt by using a non-volatile non-flammable coating waterproofing material according to the manufacturing method of the present invention It is to provide a construction method using a coating film waterproofing material.
상술한 목적을 달성하기 위한 본 발명의 특징에 의하면, 미가류 상태의 불연성 도막 방수재의 제조방법은 천연고무와 합성고무들 중 적어도 하나의 고무주재에 가류조제, 점착부여제, 충진제, 난연제 및 가류제를 포함하는 첨가물을 혼합하여 생지고무를 준비하는 단계 및; 상기 생지고무의 중량에 대응되도록 소정 불연성 용제를 상기 생지고무와 혼합하여 상기 생지고무를 상기 불연성 용제에 용해하므로써 미가류 상태의 불연성 도막 방수재를 형성하는 단계를 포함한다.According to a feature of the present invention for achieving the above object, a method of manufacturing a non-flammable non-flammable coating waterproofing material is a vulcanization aid, tackifier, filler, flame retardant and vulcanization in at least one rubber base of natural rubber and synthetic rubber Preparing a raw rubber by mixing the additive including the agent; And mixing the non-flammable solvent with the raw rubber so as to correspond to the weight of the raw rubber, thereby dissolving the raw rubber in the non-flammable solvent to form a non-volatile non-flammable coating waterproofing material.
이와 같은 본 발명에서 상기 불연성 용제는 트리크로로 에칠렌, 트리크로로 에탄, 퍼크로로 에칠렌 중 적어도 하나를 포함할 수 있다. 또, 상기 점착부여제는 아스팔트를 더 포함할 수 있다. 또, 상기 불연성 용제는 트리크로로 에칠렌, 트리크로로 에탄, 퍼크로로 에칠렌 중 적어도 하나에 대하여 톨루엔, 신나, 벤젠 중 적어도 하나를 30% 내지 50%의 비율로 섞은 혼합물을 포함할 수 있다.In the present invention as described above, the incombustible solvent may include at least one of trichloroethylene, trichloroethane, and percroethylene. In addition, the tackifier may further include asphalt. In addition, the non-combustible solvent may include a mixture of at least one of toluene, thinner, and benzene in a ratio of 30% to 50% with respect to at least one of trichloroethylene, trichloroethane, and perchlorethylene.
이와 같은 본 발명에서 상기 생지고무 1kg에 대하여 상기 불연성 용제 2000cc의 비율로 상도의 미가류 상태의 불연성 도막 방수재를 형성하고, 상기 생지고무 1kg에 대하여 상기 불연성 용제 3000cc의 비율로 하도의 프라이머를 형성할 수 있다.In the present invention as described above to form a non-flammable non-flammable coating waterproofing material of a top coat at a ratio of 2000cc of the nonflammable solvent with respect to 1kg of the raw rubber, and to form a primer undercoat at a rate of 3000cc of the nonflammable solvent with respect to 1kg of the raw rubber Can be.
상술한 목적을 달성하기 위한 다른 본 발명의 특징에 의하면, 미가류 상태의 불연성 도막 방수재를 사용한 시공방법은 프라이머와 미가류 상태의 불연성 도막 방수재들을 각각 준비하는 단계와; 상기 프라이머를 아스팔트를 포장하는 도로 또는 교량 구조물의 표면에 1차로 도포하는 단계와; 상기 프라이머가 도포된 구조물의 표면에 소정 보강재를 도포하는 단계와; 상기 보강재가 도포된 상기 구조물의 표면에 상기 미가류 상태의 불연성 도막 방수재를 도포하는 단계와; 상기 미가류 상태의 불연성 도막 방수재가 도포된 상기 구조물을 건조시키는 단계 및; 상기 건조된 구조물의 표면에 120도 내지 160도의 고열 아스팔트 골재를 포장하는 단계를 포함한다.According to another aspect of the present invention for achieving the above object, the construction method using the non-vulcanized non-flammable coating waterproofing material comprising the steps of preparing a primer and a non-flammable non-flammable coating waterproofing material, respectively; First applying the primer to a surface of a road or bridge structure paving asphalt; Applying a predetermined reinforcement on the surface of the structure to which the primer is applied; Applying a non-vulcanizable non-flammable coating waterproofing material to a surface of the structure to which the reinforcing material is applied; Drying the structure to which the non-flammable non-combustible coating waterproofing material is applied; Paving 120 to 160 degrees high temperature asphalt aggregate on the surface of the dried structure.
이와 같은 본 발명에서 상기 보강재는 천연섬유 또는 합성섬유 재질의 부직포, 망사 중 어느 하나를 포함할 수 있다.In the present invention as described above, the reinforcing material may include any one of a nonwoven fabric and a mesh of natural fiber or synthetic fiber material.
상술한 목적을 달성하기 위한 또 다른 본 발명의 특징에 의하면, 프라이머와 미가류 상태의 불연성 도막 방수재들을 각각 준비하는 단계와; 상기 프라이머를 건축물의 옥상 또는 벽면 구조물의 표면에 1차로 도포하는 단계와; 상기 프라이머가 도포된 구조물의 표면에 상기 미가류 상태의 불연성 도막 방수재를 도포하는 단계와; 상기 미가류 상태의 불연성 도막 방수재를 도포한 후, 상기 구조물을 건조시키는 단계를 포함한다.According to still another aspect of the present invention for achieving the above object, comprising the steps of preparing a primer and a non-flammable non-flammable coating film waterproofing material, respectively; First applying the primer to the surface of the roof or wall structure of the building; Applying the non-vulcanized non-flammable coating film waterproof material to the surface of the structure to which the primer is applied; After applying the non-flammable non-flammable coating waterproofing material, and drying the structure.
이와 같은 본 발명에서 상기 건조 단계가 완료된 후, 상기 구조물의 표면에 벽돌 쌓기, 보호재 부착, 시멘트 모르타르 중 하나로 마감처리하는 단계를 더 포함할 수 있다.In the present invention as described above, after the drying step is completed, it may further comprise the step of finishing with one of the brick stacking, protective material, cement mortar on the surface of the structure.
이와 같은 본 발명의 미가류 상태의 불연성 도막 방수재에 의하면, 미가류 상태의 고무 주재료를 도막 방수재로 사용하므로, 시공시 고무층의 두께가 일정하고, 요철부위의 시공이 간편하므로 도로의 포장층, 교량의 상판, 그리고 건물의 천장·벽면·바닥 등에 방수 시공을 할 때 용이하게 시공할 수 있고, 화재에 의한 대형 사고의 위험 없이 안정적이 작업을 유지할 수 있다. 그리고, 시공한 후에 2차 활성화하여 가류고무로 전환하므로, 고무 고유의 특성인 탄성 및 인장강도와 신장률 등이 우수한 가류된 고무시트로 이음매 없이 시공한 효과를 얻게 할 수 있다.According to the non-vulcanized non-flammable coating waterproofing material of the present invention, since the rubber main material in the unvulcanized state is used as the coating waterproofing material, the thickness of the rubber layer is constant at the time of construction, and the construction of the uneven portion is easy, so that the pavement layer and the bridge It can be easily installed when waterproofing the ceiling, wall, and floor of the building, and can maintain stable work without the risk of large accidents caused by fire. In addition, since the secondary activation after the conversion to the vulcanized rubber, it is possible to obtain a seamless effect of the vulcanized rubber sheet excellent in elasticity, tensile strength and elongation, etc. that are inherent in rubber.
이하, 본 발명의 바람직한 실시예를 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail.
본 발명의 실시예에 따른 미가류 상태의 불연성 도막 방수재는 다음과 같은 성분으로 성형된다.The non-flammable non-flammable coating film waterproofing material according to the embodiment of the present invention is molded from the following components.
1) 고무주재 ; 천연고무 또는 합성고무 중의 하나 --------- 100%1) rubber base; One of natural or synthetic rubber --------- 100%
2) 가류조제 ; 스테아린 산(Stearic Acid) ---------------- 1%2) vulcanization preparation; Stearic Acid ---------------- 1%
산화마그네슘(Magnesium Oxide) --------- 5%Magnesium Oxide --------- 5%
아연화(Zinc Oxide) ----------------------- 5%Zinc Oxide ----------------------- 5%
유황(Sulphur) ----------------------- 3%Sulphur ----------------------- 3%
3) 점착부여제 ; 석유수지(Petroleum Resin) -------------- 15%3) tackifiers; Petroleum Resin -------------- 15%
변성훼놀수지(Alkyl Phenol Formaldehyde Resin)Alkyl Phenol Formaldehyde Resin
---------------- 10%---------------- 10%
송지(Rosin) ----------------------- 10%Rosin ----------------------- 10%
쿠마론수지(Cumarone Resin) ---------- 5%Coumarone Resin ---------- 5%
아스팔트(Asphalt)----------------------- 7%Asphalt ----------------------- 7%
4) 충 진 제 ; 탄산칼슘(Calcium Carbonate) ---------- 35%4) fillers; Calcium Carbonate ---------- 35%
크레이(Activated Clay) ----------------- 25%Activated Clay ----------------- 25%
벤토나이트(Bentonite) ----------------- 10%Bentonite ----------------- 10%
5) 난 연 제 ; 염화 파라핀(Chlorinated Paraffins) -------- 3%5) flame retardant; Chlorinated Paraffins -------- 3%
산화 안티몬(Antimony Trioxide) ---------- 7%Antimony Oxide ---------- 7%
6) 가 류 제 ; DM ----------------------------- 1%6) vulcanizing agents; DM ----------------------------- 1%
T/T ----------------------------- 0.5%T / T ----------------------------- 0.5%
PZ ----------------------------- 0.5%PZ ----------------------------- 0.5%
NA 22 ------------------------------ 1%NA 22 ------------------------------ 1%
이때, 상기 가류조제, 점착부여제, 충진제, 그리고 가류제들의 배합 비율은 고무주재에 대한 첨가비율이다. 이와 같은 배합 비율로 상기 고무주재는 고무 교반기(Open Roller)에 의해서 혼합된다. 그리고, 혼합된 고무주재의 중량 100g에 대하여 불연성이고 염화물 용제인 트리크로로 에칠렌(Trichloroethlylene), 트리크로로 에탄, 및 파크로로 에칠렌 300cc에 미가류 고무 배합물(혼합물)을 용해하여 하도인 프라이머(Primer)를 제조하고, 상기 혼합된 고무주재의 중량 100g에 대하여 상기 염화물인 불연성 용제 200cc를 가하여 혼합물을 용해하면 상도인 미가류 상태의 불연성 도막 방수재를 제조한다.At this time, the blending ratio of the vulcanization aid, tackifier, filler, and vulcanizing agent is the addition ratio to the rubber base. In such a blending ratio, the rubber material is mixed by a rubber stirrer (Open Roller). Then, a non-flammable rubber compound (mixture) was dissolved in 300 cc of trichloroethlylene, trichloroethane, and chlorochloroethylene, which are nonflammable and chloride solvents, based on 100 g of the mixed rubber base. Primer), and 200cc of the nonflammable solvent, chloride, is added to 100g of the mixed rubber base to dissolve the mixture, thereby preparing a non-flammable non-flammable coating waterproofing material having a top coat.
본 발명의 미가류 상태의 불연성 도막 방수재는 점착 부여제인 석유수지, 변성훼놀수지, 송지, 그리고 쿠마론수지를 첨가하여 시멘트 콘크리트와 접착을 강화하였다. 또한, 도로 포장 마감제인 아스팔트와 접착이 원활하게 하기 위하여 아스팔트를 소량 첨가하였다. 상기 점착부여제인 수지 및 고무를 첨가한 아스팔트가 상호 보완 상승 작용을 하여 도로 포장 마감제인 아스팔트 콘트리트와 강력하게 접착이 되어 일체로 형성되게 된다.In the unvulcanized non-flammable coating waterproofing material of the present invention, petroleum resin, modified phenol resin, pine resin, and coumarone resin as tackifiers were added to enhance adhesion with cement concrete. In addition, a small amount of asphalt was added in order to facilitate adhesion with the asphalt pavement finish. Asphalt to which the resin and rubber as the tackifier is added complementary synergistic effect is strongly bonded to the asphalt concrete which is a road pavement finishing agent is formed integrally.
상기 고무주재는 고무의 종류 별로 고유한 물성과 특성이 다르다. 이때, 시험 검토한 결과, 상기 고무주재는 천연고무 또는 합성고무 단독으로 사용하는 것도 좋지만, 서로 다른 종류의 고무를 혼합하여 도막 방수재를 제조하는 것이 더욱더 우수한 물성을 발휘하였다. 즉, 사용하는 목적과 용도에 따라 천연고무 및 합성고무를 혼합하여 도막 방수재를 제조하지만, 시험 검토한 결과, CR고무 또는 IIR 고무를 단독으로 사용하거나 혼합하여 사용하는 것이 가장 우수(優秀) 하였다.The rubber material is different in its physical properties and properties for each type of rubber. At this time, as a result of examination and examination, the rubber main body may be used as natural rubber or synthetic rubber alone, but it is more excellent to produce a coating film waterproofing material by mixing different types of rubber. In other words, according to the purpose and purpose of use, natural rubber and synthetic rubber are mixed to produce a coating film waterproofing material. However, as a result of examination and examination, it is best to use CR rubber or IIR rubber alone or to mix.
상기 불연성 용제는 염화물이 주성분인 트리크로로 엔탄, 트리크로로 에칠렌, 퍼크로로 에칠렌(Perchloro Ethylene)등의 용제를 단독으로 사용하여도 좋지만, 가격이 비교적 고가에 속함으로, 제조비의 절감을 희망하면, 상기의 불연성 용제 50%에 일반 방향족 용제인 토루엔, 신나, 벤젠 등의 용제를 30% 내지 50% 혼합하여 사용하여도 불연성 도막 방수재를 제조할 수 있다.The non-combustible solvent may be a sole solvent such as trichloroethane, trichloroethylene, and perchloroethylene, mainly composed of chlorides, but the price is relatively high, and thus the manufacturing cost is reduced. The non-flammable coating film waterproofing material can be manufactured even if it mixes 30%-50% of solvents, such as toluene, thinner, and benzene which are general aromatic solvents, with 50% of said nonflammable solvents.
이와 같은 성분과 비율에 따른 미가류 상태의 불연성 도막 방수재의 제조방법은, 먼저 밀폐식 혼합 교반 기계인 니-더 믹서(Kneade Mixer) 또는 밴버리 혼합기(Banbury Mixer)에 천연고무 또는 합성고무(SBR고무,BR고무,EPT고무,IIR고무,CR고무,NBR고무,Urethan고무,CPE고무) 가운데 하나(100%)를 넣어 교반하면서 가류조제인 스테아린산(1%), 산화마그네슘(4%), 아연화(5%), 유황(3%)를 첨가하여 고르게 교반하여 잘 섞이도록 한다. 그리고, 점착부여제인 석유수지(15%), 변성훼놀수지(10%), 송지(10%), 쿠마론수지(5%), 아스팔트(7%)를 첨가하여 교반하여 고르게 분산 혼합되도록 한다. 충진제인 탄산칼슘(35%), 크레이(25%), 벤토나이트(10%)를 넣어 고르게 잘 분산 혼합되도록 교반한 후, 최종적으로 가류제인 DM(1%), T/T(0.5%), PZ(0.5%), NA22(1%)를 첨가하여 고르게 분산 혼합되도록 잘 교반한다. 이와 같이 교반하여 혼합된 고무 생지를 로-라(Open Roller)에서 냉각하면서 재차 교반하여 고르게 분산 혼합되도록 한 후, 폭이 약 30Cm, 두께가 약 10mm 정도의 규격이 되도록 생지고무를 시트상태로 제조한다. 상기 시트상태의 생지고무를 용제에 생지고무가 용해가 잘되도록 고무용 제단기로 잘게 재단한다.The manufacturing method of the non-flammable non-flammable coating waterproofing material according to such a component and ratio is a natural rubber or synthetic rubber (SBR rubber) in the Kneade Mixer or Banbury Mixer which is a closed mixing stirring machine. Stirring (1%), magnesium oxide (4%), zinc oxide (1%) of vulcanizing aids by adding one (100%) of BR rubber, EPT rubber, IIR rubber, CR rubber, NBR rubber, Urethan rubber or CPE rubber 5%), sulfur (3%) is added and stirred evenly to mix well. In addition, petroleum resin (15%), modified phenol resin (10%), pine (10%), coumarone resin (5%), and asphalt (7%), which are tackifiers, are added to the mixture to be stirred and dispersed evenly. After filling with calcium carbonate (35%), cray (25%) and bentonite (10%), the fillers were dispersed and mixed well. Finally, DM (1%), T / T (0.5%), and PZ as vulcanizing agents were mixed. (0.5%), NA22 (1%) is added and stirred well to evenly disperse and mix. After mixing the rubber dough mixed by stirring as described above, the mixture is cooled and then dispersed and mixed evenly while cooling in an open roller, and then the raw rubber is manufactured in a sheet state so as to have a width of about 30 cm and a thickness of about 10 mm. do. The raw rubber in the sheet state is finely cut with a rubber mill so that the rubber is dissolved in the solvent.
이와 같이 형성된 생지고무를 액상 교반기에 넣고, 상기 생지고무 1 Kg에 대하여 불연성 용제인 트리크로로 에탄, 트리크로로 에칠렌, 퍼크로로 에칠렌 중 어나 하나를 2,000cc 넣어 상기 생지고무가 풀릴 때까지 서서히 교반한다. 상기 불연성 용제에 상기 생지고무가 완전하게 용해하면 본 발명의 상도의 도막 방수재가 제조된다. 그리고, 하도인 프라이머(Primer)의 제조는 상기의 생지고무 1kg에 대하여 상기 불연성 용제를 3,000cc를 넣어 교반하여 완전하게 용해하면 점도가 묽은 하도인 프라이머가 제조된다.The raw rubber thus formed is placed in a liquid stirrer, and 2,000 cc of any one of trifluoro ethane, trichloro ethylene, and percro ethylene is added to 1 kg of the raw rubber until the raw rubber is released. Stir. When the raw rubber is completely dissolved in the incombustible solvent, a top coat waterproofing material of the present invention is produced. And, in the preparation of primer primer (Primer) is added to 3,000cc of the non-flammable solvent with respect to 1kg of the raw rubber, and stirred completely to prepare a primer with a thin viscosity.
한편, 본 발명의 실시예에 따른 미가류 상태의 불연성 도막 방수재는 염화 파라핀과 산화 안티몬과 같은 난연제를 첨가할 수 있다. 상기 난연제는 미가류 상태의 불연성 도막 방수재를 시공한 후에 불연성 용재가 증발하여 고무층이 형성되었을 때 화기와 접촉하여도 불이 붙지 않도록 하는 2차적인 불연성을 발휘한다. 물론, 상기 미가류 상태의 불연성 도막 방수재는 액상일 때 불연성 용제에 의하여 1차적인 불연성을 발휘한다. 즉, 본 발명의 도막 방수재가 불연성으로 제조되는 근본은 트리크로로 에탄, 트리크로로 에칠렌, 퍼크로로 에칠렌 등의 염화물이고 불연성인 용제에 기인한다.On the other hand, the non-flammable non-flammable coating film waterproofing material according to an embodiment of the present invention may be added a flame retardant such as paraffin chloride and antimony oxide. The flame retardant exhibits secondary non-combustibility to prevent fire from coming into contact with fire when the non-flammable material evaporates and a rubber layer is formed after constructing the non-vulcanized non-flammable coating waterproofing material. Of course, the non-flammable non-flammable coating waterproofing material exhibits primary non-combustibility by the incombustible solvent when the liquid phase. That is, the base from which the coating film waterproofing material of the present invention is made nonflammable is due to chloride and nonflammable solvents such as trichloroethane, trichloroethylene and perchlorethylene.
이와 같이 제조된 본 발명의 미가류 상태의 불연성 도막 방수재는, 종래의 도막 방수재와 다르게, 난연성 도막 방수재이므로 화재에 의한 대형 사고의 위험 없이 안정적인 시공을 할 수 있다.The non-flammable non-flammable coating waterproofing material of the present invention prepared as described above is a flame-retardant coating waterproofing material, unlike the conventional coating waterproofing material, so that stable construction can be performed without risk of a large accident due to fire.
상기 미가류 상태의 불연성 도막 방수재를 이용한 시공 방법은 붓, 롤러, 그리고 스프레이 등으로 상기 하도의 프라이머로 도막 방수 시공을 1차로 한 후 보강재인 PP,PE 또는 폴리에스테르 등 고분자 합성 섬유 재질의 부직포 또는 동일한 재질의 구멍이 뚤린 망사를 깔아 주고 그 위에 상기 상도의 도막 방수재를 도포한다. 상기 미가류 불연성 도막 방수재는 액상이므로 요철 부위나 코너 부분 등의 방수시공에 안전하고 편리하고, 시공 작업이 간단하며, 중간 부위에 고분자 합성 섬유를 삽입하였으므로 고무 본래의 강인한 인장강도가 상승 작용하여 더욱 더 강인하고 내구성이 우수한 방수시공 효과를 얻을 수 있다. 또한, 방수층의 두께 형성에도 유리하며, 방수시공이 완료된 후 3일 내지 5일간 완전 건조시키면 첨가된 용제는 증발하면서 한 장의 미가류 고무시트로 전체 면적을 방수 시공한 효과를 얻게 된다. 상기 보강재는, 천연섬유 또는 합성섬유 중 어느 것이나 사용 가능하지만, 내구성에서 합성섬유가 우수했으며, 합성섬유 중에서도 고분자 합성 섬유인 PP, PE, 그리고 폴리에스테르 부직포를 사용하는 것이 좋다. 그러나, 동일한 소재의 망사 또는 망사와 같이 구멍이 있는 합성섬유가 부착이 더욱 더 우수하였다.The construction method using the non-vulcanized non-combustible coating waterproofing material is a non-woven fabric made of a polymer synthetic fiber material such as PP, PE or polyester, which is a reinforcement material after first coating coating waterproofing with the primer of the lower coat using a brush, roller, and spray or the like. A perforated mesh of the same material is laid and the top coat waterproofing material is applied thereon. Since the unvulcanized non-combustible coating waterproof material is a liquid, it is safe and convenient for waterproof construction such as uneven or corner parts, and the construction work is simple, and since the synthetic polymer is inserted into the middle part, the tensile strength of rubber inherently increases, thereby increasing the strength. Stronger and more durable waterproof effect can be obtained. In addition, it is advantageous to form the thickness of the waterproof layer, and if the complete drying for 3 to 5 days after the waterproofing is completed, the added solvent is evaporated while obtaining the effect of waterproofing the entire area with one sheet of unvulcanized rubber sheet. The reinforcing material may be any one of natural fiber and synthetic fiber, but excellent in synthetic fiber in durability, and it is preferable to use PP, PE, and polyester nonwoven fabric which is a polymer synthetic fiber among synthetic fibers. However, the adhesion was even better with perforated synthetic fibers such as mesh or mesh of the same material.
이와 같이, 방수시공이 완료된 후 아스팔트 포장도로의 마감 시공제인 120℃ ∼ 160℃의 고열 아스팔트 골재를 일정한 두께로 펴나가면서 무거운 롤러 차량(Roller Car)으로 다지면서 압축하여 아스팔트 도로 공사의 시공을 완료하게 된다. 방수시공이 완료되어 형성된 본 발명의 미가류 고무층은 아스팔트 포장도로의 마감제인 아스팔트 골재의 뜨거운 열과 압축에 의하여 2차로 급속히 활성화하여 가류 성형된 고무층으로 형성된다. 따라서, 고무 본래의 특성인 탄성과 강인한 인장강도와 신장율을 겸비한 완전 무결한 고무층을 형성하므로 아무리 넓은 시공 면적도 한 장의 성형된 가류고무로 이음세 없는 방수시공을 한 효과를 얻는다.As such, after the waterproof construction is completed, the high-temperature asphalt aggregate of 120 ° C. to 160 ° C., which is a finishing work on the asphalt pavement, is compressed to a heavy roller vehicle while compacting to a certain thickness to complete the construction of the asphalt road construction. do. The unvulcanized rubber layer of the present invention formed by completing the waterproof construction is rapidly formed by a vulcanization-molded rubber layer by rapidly activating secondarily by hot heat and compression of the asphalt aggregate, which is a finishing agent of the asphalt pavement. Thus, since a completely flawless rubber layer having elasticity, tough tensile strength and elongation, which is an inherent property of rubber, is formed, no matter how wide the construction area, it is possible to obtain a seamless waterproof construction with one piece of molded vulcanized rubber.
또한, 건축물의 옥상 또는 벽면의 방수를 위하여 본 발명의 미가류 상태의 불연성 도막 방수재를 용이하게 적용할 수 있다. 즉, 기존 설치되어 경화된 시멘트 콘크리트에, 전술한 시공방법과 같이, 하도인 프라이머를 붓 또는 롤러 등으로 칠하거나 스프레이로 칠하여 도포한 후 상도인 도막 방수재를 도포한 후에 3일 내지 5일간 건조시켜 용제가 충분히 건조되도록 한다. 시공 완료한 방수층을 보호하기 위하여 벽돌 쌓기, 보호재 부착, 시멘트 모르타르(콘크리트)로 마감 처리하여 방수시공을 끝내면 상기 미가류 불연성 도막 방수재는 상온에서 서서히 활성화하여 시간이 가면서 성형된 고무층이 형성됨으로 상술한 바와 같은 효과를 얻는다.In addition, in order to waterproof the roof or the wall of the building, it is possible to easily apply the non-flammable non-flammable coating waterproofing material of the present invention. In other words, the previously installed and cured cement concrete, like the above-described construction method, by applying a primer or a painter with a brush or a roller, or by spraying and then coating the coating film waterproofing material of the top coat and dried for 3 to 5 days Allow the solvent to dry sufficiently. In order to protect the completed waterproof layer, the uncurable non-combustible coating waterproofing material is gradually activated at room temperature by forming brick layer, attaching protective material, finishing with cement mortar (concrete), and forming a rubber layer formed over time. Get the same effect as
이와 같은 본 발명의 제조방법에 의한 미가류 상태의 불연성 도막 방수재는 교량의 상판이나 건물의 천장, 벽면, 바닥 등에 사용되어 고무 본래의 특성인 탄성, 강인한 인장강도, 높은 신장률을 겸비하면서도 내구성이 우수하고 진동과 충격을 완화하며, 방수 성능도 향상된 성형 가류 고무로 전환된다.The non-flammable non-flammable coating waterproofing material according to the manufacturing method of the present invention is used for the top plate of a bridge, the ceiling, the wall, the floor of a building, and the like, and has excellent durability while having elasticity, tough tensile strength, and high elongation, which are inherent in rubber. It is converted to molded vulcanized rubber which mitigates vibration and shock and improves water resistance.
이와 같은 본 발명을 적용하면, 화재의 위험성이 없이 용이하게 시공할 수 있는 도막 방수재를 제공할 수 있다. 미가류 상태의 고무 주재료를 도막 방수재로 사용하므로, 시공시 고무층의 두께가 일정하고, 요철부위의 시공이 간편하므로 도로의 포장층, 교량의 상판, 그리고 건물의 천장·벽면·바닥 등에 방수 시공을 할 때 용이하게 시공할 수 있고, 화재에 의한 대형 사고의 위험 없이 안정적이 작업을 유지할 수 있다. 그리고, 시공한 후에 2차 활성화하여 가류고무로 전환하므로, 고무 고유의 특성인 탄성 및 인장강도와 신장률 등이 우수한 가류된 고무시트로 이음매 없이 시공한 효과를 얻게 할 수 있다.Applying the present invention as described above, it is possible to provide a coating film waterproofing material that can be easily installed without the risk of fire. Since the rubber main material of the unvulcanized state is used as the waterproofing film, the thickness of the rubber layer is constant at the time of construction, and the construction of the uneven parts is easy, so that the waterproofing is applied to the pavement of the road, the top of the bridge, and the ceiling, wall, floor of the building It can be easily installed and can maintain stable work without risk of large accidents caused by fire. In addition, since the secondary activation after the conversion to the vulcanized rubber, it is possible to obtain a seamless effect of the vulcanized rubber sheet excellent in elasticity, tensile strength and elongation, etc. that are inherent in rubber.
Claims (9)