JPS6160478A - Spray can filled with water-repellent surface treatment - Google Patents
Spray can filled with water-repellent surface treatmentInfo
- Publication number
- JPS6160478A JPS6160478A JP17777784A JP17777784A JPS6160478A JP S6160478 A JPS6160478 A JP S6160478A JP 17777784 A JP17777784 A JP 17777784A JP 17777784 A JP17777784 A JP 17777784A JP S6160478 A JPS6160478 A JP S6160478A
- Authority
- JP
- Japan
- Prior art keywords
- spray
- water
- surface treatment
- treatment agent
- silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
発明の目的
（産業上の利用分野）
この発明は、撥水性表面処理剤を充填したスプレー化に
関するものである。DETAILED DESCRIPTION OF THE INVENTION Object of the Invention (Field of Industrial Application) This invention relates to a spray filled with a water-repellent surface treatment agent.
（従来の技術）
北海道、北米、北欧等の寒冷地において、自動車のウェ
ザ−ストリップやカギ穴等の水の侵入をきらう部分には
、従来より１８水性表面処理剤がスプレー化によってス
プレー塗布されており、その部分に水が付着しないよう
にしている。ところが、前記処理剤の撥水性は必ずしも
高くなく、俤布部分においてすら水が氷°結してしまう
という問題があった。(Prior art) In cold regions such as Hokkaido, North America, and Northern Europe, 18 water-based surface treatment agents have traditionally been applied by spraying to areas where water should not enter, such as automobile weather strips and keyholes. This prevents water from adhering to that area. However, the water repellency of the treatment agent is not necessarily high, and there is a problem in that water freezes even in the covered area.
また、この種のスプレー化は缶内のガス圧が高温時にも
できるだけ低、いことが望まれている（例えば、５０℃
において１２ｋＧ／Ｃｌ１１以下）が、この要望を満足
しながら上記撥水性を向上するのは困難であった。In addition, for this type of spraying, it is desirable that the gas pressure inside the can be as low as possible even at high temperatures (for example, at 50°C).
(12 kG/Cl11 or less), it was difficult to improve the water repellency while satisfying this demand.
（発明が解決しようとする問題点）
従−）で、本発明は撥水性表面処理剤の１８水牲不足に
起因し、寒冷地において、残留水分の氷結が起こり、剥
離すべき物が固着してしまうとか、前記スプレー缶内の
高調状態におけるガス圧を低く保つことが困ｆｆ１ｌで
あるとかいう問題点を解決するためのものである。(Problems to be Solved by the Invention) In sub-), the present invention solves the problem that, due to insufficient water hydration of the water-repellent surface treatment agent, residual moisture freezes in cold regions, causing the material to be peeled to stick. This is to solve the problems that it is difficult to keep the gas pressure low in the high-temperature state inside the spray can.
発明の構成 （問題点を解決するための手段） 本発明は上記問題点に鑑み、一般式Ｒ工○［Ｒ。Composition of the invention (Means for solving problems) In view of the above problems, the present invention is based on the general formula R [R].
Ｒ２５ｔ○］ｎＲ，（ただし、Ｒ工は水素又はアルキル
基を示し、Ｒ，Ｒ，は水素、アルキル基又はブ
フェニル基を示し、ｎは５０００以下の数を示す。R25t○]nR, (wherein R represents hydrogen or an alkyl group, R and R represent hydrogen, an alkyl group, or a buphenyl group, and n represents a number of 5000 or less.
）で表わされるシリコーンを溶剤とともに松露容器につ
めた構成を採っている。) is packed in a pine dew container along with a solvent.
（作用）
上記構成のｌａ水性表面処理剤をスプレー化に充填した
ことにより、寒冷地における撥水性が向上づるとともに
、同スプレー缶は８０℃〜１００℃の高調状態に放置さ
れても、缶内のガス圧は所定圧力以上にはあがらなくな
った。(Function) By filling the spray can with the LA water-based surface treatment agent having the above structure, water repellency in cold regions is improved, and even if the spray can is left at high temperatures of 80℃ to 100℃, The gas pressure no longer rises above the specified pressure.
（実施例） 次に本発明を具体化した一実施例について説明する。(Example) Next, an embodiment embodying the present invention will be described.
まず、この発明の１８水性表面処理剤において、代表的
な配合例を５種顕示す。First, five typical formulation examples of the 18 aqueous surface treatment agent of the present invention will be shown.
配合例１
下記に示す通りのｍｆＦｔ部率で配合された１θ水性表
面処理剤が用いられている。Formulation Example 1 A 1θ aqueous surface treatment agent blended at the mfFt part ratio shown below is used.
シリコーン
ＨＯ［、（ＣＨ，）、 ＳｚＯコＪｔｌｌ（１＠
・・・ ３ 部シリコ
ーン溶解用溶剤
１．１．１−トリクロルエタン ・・・９７部高圧
液化ガス
フロン１２ ・・・３１０部上記
混合物をスプレー化に充１ｉした。Silicone HO[, (CH,), SzOkoJtll(1@
...3 parts Solvent for dissolving silicone 1.1.1-Trichloroethane ...97 parts High-pressure liquefied gas Freon 12 ...310 parts The above mixture was charged into a spray for 1 hour.
配合例２
シリコーン
ＣＨａＯ［（ＣＨｓム ＳＬＯ］、、、、ＣＨ３・・・
３ 部シリコーン溶解用溶剤
１．１．１−トリクロルエタン ・・・９７部高圧
液化ガス
フロン１２ ・・・３１０部上記
混合物をスプレー化に充填した。Formulation example 2 Silicone CHaO [(CHs SLO],..., CH3...
3 parts Solvent for dissolving silicone 1.1.1-Trichloroethane...97 parts High pressure liquefied gas Freon 12...310 parts The above mixture was charged into a sprayer.
配合例３
シリコーン
ＣＨ，○ ［（ＣＨ，）ユｓ、 ○ コ＞ａ−ｏ Ｃ
Ｈ３・・・ ３ 部シリコーン溶解用溶剤
１．１．１−トリクロルエタン ・・・９７部高Ｅ
′ｆＩ化ガス
フロン］２ ・・・３１０部上記
混合物をスプレー化に充填した。Formulation example 3 Silicone CH, ○ [(CH,)yus, ○ ko>a-o C
H3... 3 parts Solvent for dissolving silicone 1.1.1-Trichloroethane...97 parts High E
310 parts of the above mixture was filled into a spray bottle.
配合例４
シリコーン
Ｈ○ ［（ＣＩ−１，＞ （Ｃ，Ｈ，） Ｓ２０
し、、、Ｈ・ ３ 部シリコーン溶解用溶剤
１．１．１−トリクロルエタン ・・・９７部高圧
液化ガス
フロン］２ ・・・３１０部上記
混合物をスプレー化に充填した。Formulation example 4 Silicone H○ [(CI-1,> (C,H,) S20
H. 3 parts Solvent for dissolving silicone 1.1.1-Trichloroethane 97 parts High pressure liquefied gas Freon] 2 310 parts The above mixture was charged into a spray tube.
配合例５
シリ−１−ン
１−１０ｃ＜ＣＨ，厄ＳＬ○ し、、、 ｌ−１・・・
３部シリコーン溶解用溶剤
１．１．１−トリクロルエタン ・・・９７部高圧
液化ガス
フロン１２ ・・・３１０部上記
混合物牙スプレー缶に充填した。Formulation example 5 Series 1-1-10c<CH, SL○ shi... l-1...
3 parts Solvent for dissolving silicone 1.1.1-Trichloroethane...97 parts High pressure liquefied gas Freon 12...310 parts The above mixture was filled into a spray can.
前記シリコーン濃度はシリコーン溶解用溶剤に対して１
〜１ＱＷｔ％にすれば良く、好ましくは２〜５Ｗｔ％程
度であり、さらに好ましくは２．５〜３．５Ｗｔ％であ
る。固形分温度が１０Ｗｔ％以上であるとスプレーが不
可能となり、１Ｗｔ％以下だと撥水性が低下するからで
ある。更に詳しくは、５Ｗｔ％以上ではシリコーンによ
る効果が飽和状態となり、２Ｗ（％以下ではスプレー塗
布後の１８水性の耐久性が低下するからである。The silicone concentration is 1% relative to the silicone dissolving solvent.
-1QWt%, preferably about 2 to 5Wt%, more preferably 2.5 to 3.5Wt%. This is because if the solid content temperature is 10 Wt% or higher, spraying becomes impossible, and if the solid content temperature is 1 Wt% or lower, water repellency decreases. More specifically, at 5 Wt% or more, the effect of silicone becomes saturated, and at 2W (% or less), the durability of 18 water-based after spray coating decreases.
前記シリコーン溶解用溶剤としては、前記１゜１．１−
トリクロルエタンの外、ｎ−へキサン、ｎ−へブタン、
ガソリン、ベンゼン、トルエン、イソプロピルアルコー
ル、ブチルアルコール、メチルエチルケトン、トリクロ
ルエタン、ジメチルエーテル、）８化メチレン等が使用
可能である。As the silicone dissolving solvent, the above-mentioned 1°1.1-
In addition to trichloroethane, n-hexane, n-hebutane,
Gasoline, benzene, toluene, isopropyl alcohol, butyl alcohol, methyl ethyl ketone, trichloroethane, dimethyl ether, methylene octide, and the like can be used.
前記高ＩＴＥ液化ガスとしては、前記フロン１２の外、
フロンＲ−１１、フロンＲ−１３、フロンＲ−１４、フ
ロンＲ−２１、フロンＲ−２２、フロンＲ−１１２、フ
ロンＲ−１１５等が使用可能である。The high ITE liquefied gas includes, in addition to the Freon 12,
Freon R-11, Freon R-13, Freon R-14, Freon R-21, Freon R-22, Freon R-112, Freon R-115, etc. can be used.
上記各スプレー化の１發水性表面処理剤の効果を示Ｊ方
法として下記に示す試験を行なった。すなわち、自動車
のドアウェザ−ストリップのドアとの接触面に前記表面
処理剤をスプレー塗布し、自動車を一２０’Ｃの冷凍室
に５時間放置し、ドアを開く力を測定した。The following tests were conducted to demonstrate the effectiveness of each of the above sprayed aqueous surface treatment agents. That is, the surface treatment agent was spray applied to the contact surface of the door weather strip of a car, and the car was left in a freezing room at -20'C for 5 hours, and the force to open the door was measured.
次の表１にその測定結果を示す。Table 1 below shows the measurement results.
以下余白
表１
なお、無処理とは前記スプレー塗布を行なわない状態の
ものを言い、比較例１において開用したスプレー化はＣ
ＲＣ５−５６＜呉工業株式会社製の撥水性表面処理剤を
充填したスプレー化）である。Margin Table 1 below. Note that "untreated" refers to the state in which the above-mentioned spray coating is not performed, and the spray coating used in Comparative Example 1 is C.
RC5-56 (spray filled with water-repellent surface treatment agent manufactured by Kure Kogyo Co., Ltd.).
同表１から明らかなように本実施例の撥水性表面処理剤
を塗布することにより、無処理の場合の略半分以下の力
で開くことができるばかりでなく、比較例１の処理剤と
比較しても半分程度の力で開くことができる。つまり、
本実施例の１ｇ水性表面処理剤を塗布することにより、
ドアとウェザ−ストリップの表面に残留する水分が効果
的に除去され、それらの間に生ずる氷結が最小限に抑え
られるからである。As is clear from Table 1, by applying the water-repellent surface treatment agent of this example, it was not only possible to open with approximately half the force of the untreated case, but also compared to the treatment agent of Comparative Example 1. However, it can be opened with about half the force. In other words,
By applying 1 g of the aqueous surface treatment agent of this example,
This is because moisture remaining on the surfaces of the door and weatherstrip is effectively removed and ice formation therebetween is minimized.
また、上記各実施例においてそのスプレー化のガス圧変
化を設定したところ、外気温度を１００℃にまで上昇さ
せたときに始めてガス圧は１２ｋｇ／Ｃｍとなった。こ
れは、現在−５般に使用されている撥水性表面処理剤入
りのスプレー化のガス圧、すなわち５０°Ｃ１，：オイ
て１２に！１１／Ｃｍと比較してもはるかに低く抑え（
専ることを可能としている。Further, when the gas pressure change for spraying was set in each of the above Examples, the gas pressure reached 12 kg/Cm only when the outside temperature was raised to 100°C. This is the gas pressure of the spray containing water-repellent surface treatment agent that is currently commonly used, that is, 50°C1: 12! It is much lower than 11/Cm (
It allows you to focus on your work.
次に、比較例として上述した現在−投に使用されでいる
撥水性表面処理剤入りのスプレー化の配合例をｆｆｌｆ
ｌ部率で示すと、
シリコーンオイル（１０ｃｓｔ、東芝「−・４５１装）
・・・ １００部
１．１．１−トリクロロエタン８％溶液・・・ １００
部ヒ記の組成物に３０６部のフロンＲ−１２とジメチル
エーテル２０２ｇを加えてスプレー化に充填している。Next, as a comparative example, an example of the formulation of a spray containing a water-repellent surface treatment agent, which is currently used in the above-mentioned
In terms of l parts, silicone oil (10 cst, Toshiba "-451 units")
... 100 parts 1.1.1-Trichloroethane 8% solution ... 100
306 parts of Freon R-12 and 202 g of dimethyl ether were added to the composition described in Part 1 and filled into a spray.
次に不発明のスプレー化の一用途について説明する。Next, one application of the uninvented spray will be explained.
北海道、北米、北欧等の寒冷地では、冬期自動車の各部
品に水が付着し外気温が一５度以下になったとき、例え
ばドアとウェザ−ストリップとの接触面、トランクとウ
ェザ−ストリップとの接触面、マッドガード、キー穴等
で水が氷結しドア又はトランクを開く場合大きな力が必
要になったり、ときにはウェザ−ストリップが破壊する
場合がある。ここに、前記撥水性表面処理剤を前記接触
面等にスプレー塗布すると、次のような効果が得られる
。In cold regions such as Hokkaido, North America, and Scandinavia, water adheres to various parts of automobiles during the winter, and when the outside temperature drops to 15 degrees Celsius or less, the contact surfaces between doors and weather strips, the trunk and weather strips, etc. Water may freeze on contact surfaces, mudguards, keyholes, etc., requiring a great deal of force to open the door or trunk, and sometimes damaging the weather strip. When the water-repellent surface treatment agent is spray applied to the contact surface, etc., the following effects can be obtained.
■ドアとウェザ−ストリップとの接触面で氷結した場合
、子供の手でも開けられるほど軽くドアを開くことがで
きる。■If ice forms on the contact surface between the door and the weather strip, the door can be opened easily enough that even a child can open it.
■トランクとウェザ−ストリップとの接触面で氷結した
場合も上記と同様に簡単に開くことができる。■If ice forms on the contact surface between the trunk and the weather strip, it can be opened easily in the same way as above.
■キー穴にスプレー塗布した場合、水が氷結せず節単に
キーをさし込むことができる。■If you spray it on the key hole, the water will not freeze and you can easily insert the key.
なお、不発明は前記各実施例に限定されるものではなく
、前記例示物質を適宜選択し使用することによって生成
された組成物ならば良い。Incidentally, the invention is not limited to the above-mentioned examples, but may be any composition produced by appropriately selecting and using the above-mentioned exemplified substances.
また、この撥水性表面処理剤は前記自動車の部品に限定
されるものではなく、例えば、寒冷地の家屋の窓枠や、
ドア枠等に塗布１°ることによっても上記と同様の効果
を奏する。Furthermore, this water-repellent surface treatment agent is not limited to the above-mentioned automobile parts, but includes, for example, window frames of houses in cold regions,
The same effect as above can be obtained by applying 1 degree to a door frame or the like.
以上、前記撥水性表面処理剤をスプレー缶に充ポした本
発明について詳述したが、同処理剤自体優れた蔀水効果
を奏するためこれを他の方法で使用することもできる。The present invention has been described in detail above, in which a spray can is filled with the water-repellent surface treatment agent, but since the treatment agent itself has an excellent water repellent effect, it can also be used in other ways.
例えば、撥水性表面処理剤を霧吹き器に注入して使用し
たり、はけ塗りで使用したりする等である。For example, the water-repellent surface treatment agent may be injected into a sprayer or applied by brushing.
発明の効果
以上詳述したように、本発明のスプレー缶は低温状態に
おいて、優れた撥水性を有するため、水の侵入をきらう
部分に塗布することによって、その部分の残留水分分を
減少させ氷結を防止することができる。更に、高温状態
におけるスプレー缶内のガス圧上昇をも低く抑えること
が可能となり、はるかに安全側となるという優れた効果
を奏する。Effects of the Invention As detailed above, the spray can of the present invention has excellent water repellency at low temperatures, so by applying it to areas where water should not enter, it reduces the residual moisture content in those areas and prevents freezing. can be prevented. Furthermore, it is possible to suppress the increase in gas pressure inside the spray can in high temperature conditions, which has an excellent effect of being much safer.
Claims (1)
ただし、Ｒｘは水素又はアルキル基を示し、Ｒ＿ｙ、Ｒ
＿ｚは水素、アルキル基又はフェニル基を示し、ｎは５
０００以下の数を示す。）で表わされるシリコーンを溶
剤とともに噴霧容器につめたことを特徴とする撥水性表
面処理剤を充填したスプレー缶。 ２、前記溶剤は前記シリコーンを溶解するための溶剤と
高圧液化ガスとの混合物であることを特徴とする特許請
求の範囲第１項記載の撥水性表面処理剤を充填したスプ
レー缶。 ３、前記シリコーンの濃度は同シリコーンを溶解するた
めの溶剤に対して１〜１０Ｗｔ％であることを特徴とす
る特許請求の範囲第１項記載の撥水性表面処理剤を充填
したスプレー缶。[Claims] 1. General formula R_xO[R_yR_zSiO]nR_x(
However, Rx represents hydrogen or an alkyl group, R_y, R
_z represents hydrogen, an alkyl group, or a phenyl group, and n is 5
Indicates a number less than or equal to 000. ) A spray can filled with a water-repellent surface treatment agent, which is characterized by filling a spray container with a silicone represented by the formula ( ) together with a solvent. 2. The spray can filled with the water-repellent surface treatment agent according to claim 1, wherein the solvent is a mixture of a solvent for dissolving the silicone and high-pressure liquefied gas. 3. A spray can filled with a water-repellent surface treatment agent according to claim 1, wherein the concentration of the silicone is 1 to 10 wt% based on the solvent used to dissolve the silicone.