JPS59174253A - Production of lead alloy by continuous rolling - Google Patents

Production of lead alloy by continuous rolling

Info

Publication number
JPS59174253A
JPS59174253A JP4607283A JP4607283A JPS59174253A JP S59174253 A JPS59174253 A JP S59174253A JP 4607283 A JP4607283 A JP 4607283A JP 4607283 A JP4607283 A JP 4607283A JP S59174253 A JPS59174253 A JP S59174253A
Authority
JP
Japan
Prior art keywords
rolls
width
plate
lead
lead alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP4607283A
Other languages
Japanese (ja)
Other versions
JPS6410309B2 (en
Inventor
Yukihiro Nagata
永田 幸広
Yasushi Watanabe
康 渡辺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Furukawa Electric Co Ltd
Furukawa Battery Co Ltd
Original Assignee
Furukawa Electric Co Ltd
Furukawa Battery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Furukawa Electric Co Ltd, Furukawa Battery Co Ltd filed Critical Furukawa Electric Co Ltd
Priority to JP4607283A priority Critical patent/JPS59174253A/en
Publication of JPS59174253A publication Critical patent/JPS59174253A/en
Publication of JPS6410309B2 publication Critical patent/JPS6410309B2/ja
Granted legal-status Critical Current

Abstract

PURPOSE:To produce a product having uniform quality and stable performance at high efficiency by specifying the ratio between the max. effective width of a plate to be produced and the width of a tapping port of a nozzle. CONSTITUTION:A molten lead alloy is charged into the space 3 between a pair of rolls 2 and 2' and is cooled by the outside circumferential surfaces 2a, 2a' of the rolls. The solidified phase formed by the cooling is continuously rolled to produce a rod or plate. When (l) and (t) are designated as the max. effective width and thickness of the rod or strip to be produced in such a case and L, T are designated as the width and height of a tapping port 4a of the nozzle, l/L is set at 2-60 at 2-30 value of T/t. The rod or plate of the lead or lead alloy having a desired size and shape and good appearance is obtd. at a high yield with uniform quality and high efficiency.

Description

【発明の詳細な説明】 本発明は、凝固相mがコンパクト形態を示す鉛基合金の
連続圧延製造法に関する。
DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for producing a lead-based alloy by continuous rolling, in which the solidified phase m has a compact form.

従来、凝固組織がコンパクト形態を示す鉛基合金の条乃
至は板を連続的に製造する方法として\水冷された回転
ドラムの表面に溶湯を凝固させ、該凝固層を剥離して条
乃至は板を製造するDM方式や、連に鋳造法でつくられ
たスラブを熱間或いは冷間で圧延して製造する圧延方式
が最も広く知られていたが、DM方式においては腐食を
うけやすく、圧延方式においては応力腐食のため腐食速
度が大きくまた圧延のだめの加工費1設備費が大きいと
いう不都合があった。かかる不都合を解消すべく、1対
のロールの間に金属溶湯を注入し、これを該ロールの外
周面で冷却して凝固相を形成しこれを連続的に圧延する
方法が知られているが1製出される条乃至は板において
、端部をトリミングして得られた健全条乃至は板の最大
有効幅tが、ノズル出湯口の幅りよりも小さくなるよう
になっているため、製出された条乃至は板の縁部に材料
の欠損部或いは割れ、亀裂等の側斜欠陥が連続的に発生
するという不都合を有している。
Conventionally, as a method for continuously manufacturing lead-based alloy strips or plates with a compact solidified structure, molten metal is solidified on the surface of a water-cooled rotating drum, and the solidified layer is peeled off to produce strips or plates. The most widely known were the DM method, which produced slabs, and the rolling method, which produced slabs by hot or cold rolling, but the DM method was susceptible to corrosion, and the rolling method However, there were disadvantages in that the corrosion rate was high due to stress corrosion, and the processing cost and equipment cost of the rolling pool was high. In order to solve this problem, a method is known in which molten metal is injected between a pair of rolls, cooled on the outer peripheral surface of the rolls to form a solidified phase, and then continuously rolled. The maximum effective width t of the sound strip or plate obtained by trimming the ends of the strip or plate produced in 1-manufacturing is smaller than the width of the nozzle outlet. This has the disadvantage that laterally diagonal defects such as missing portions of material, cracks, and cracks continuously occur at the edges of the strips or plates.

本発明はかかる不都合を有しない、品質か均一で安定し
た性能を有する製品を高能率で連続生産することができ
る凝固組織がコンパクト形態を示シ呻基合金の連続圧延
製造法を提供することを1そ、♀見的として、凝固組織
がコンパクト形態を°′糸す鉛基合金溶湯を1対のロー
ルの間隙に注入し、これを該ロールの外周面で冷却して
生成した凝固相を連続的に圧延することにより、条乃至
は板金製造する方法において、製造される条乃至は板の
最大有効幅及び厚さを夫々t、tとし、ノズル出湯口の
幅及び高さを夫々L1Tとするとき、T/lが2乃至6
0の値においてt/Lが2乃至60であることを特徴と
する。
The present invention aims to provide a continuous rolling manufacturing method for a solidified base alloy having a compact solidified structure, which does not have such disadvantages and can continuously produce products with uniform quality and stable performance with high efficiency. 1. As a hypothetical, the solidified structure has a compact form. Molten lead-based alloy is injected into the gap between a pair of rolls, and it is cooled on the outer circumferential surface of the rolls to produce a continuous solidified phase. In the method of producing a strip or sheet metal by rolling, the maximum effective width and thickness of the produced strip or plate are t and t, respectively, and the width and height of the nozzle outlet are L1T, respectively. When T/l is 2 to 6
It is characterized in that t/L is 2 to 60 at a value of 0.

以下図面に付いて本発明船乃至鉛基合金の連続圧延製造
法を説明する。
DESCRIPTION OF THE PREFERRED EMBODIMENTS The continuous rolling manufacturing method of a lead-based alloy according to the present invention will be explained below with reference to the drawings.

凝固組織がコンパクト形態全示す鉛乃至鉛基合金の溶湯
(1)としては純Pb、 Pb−0a−3n −(At
)、Pb−3r−8n −(At)等が用いられ、該溶
湯(1)を冷却された1対のロール(2)、 (2′)
の間隙(3)の前面に設けたタンディツシュ(図示しな
い〕に取り付けたノズル(4)の出湯口(4a)を通し
て該間隙(3)に向って供給し、該ロールt2L (2
)の外周面(2a)t  (2a)でこれを冷却して凝
固相(51を形成し、該凝固相(5)を直ちに該ロール
(2)、 (i)で圧延して所定形状の条(6)を得た
。この場合T/lを2乃至30とし、t、/Lを2乃至
6oの範囲となるよう調整した。
The molten metal (1) of lead or lead-based alloy whose solidified structure is compact is pure Pb, Pb-0a-3n -(At
), Pb-3r-8n -(At), etc. are used, and the molten metal (1) is cooled by a pair of rolls (2) and (2').
The roll t2L (2
) to form a solidified phase (51), and the solidified phase (5) is immediately rolled by the rolls (2) and (i) to form a strip of a predetermined shape. (6) was obtained. In this case, T/l was set to 2 to 30, and t and /L were adjusted to be in the range of 2 to 6o.

Claims (1)

【特許請求の範囲】[Claims] 凝固組織がコンパクト形態を示す鉛基合金溶湯を1対の
ロールの間隙に注入し、これを該ロールの外周面で冷却
して生成した凝固相を連続的に圧延することにより、条
乃至り板を製造する方法において、製造される条乃至は
板の最大有効幅及び厚さを夫々t% tとし、ノズル出
湯口の幅及び高さを夫々LITとするとき一、 T/l
が2乃至30の値においてt/Lが2乃至60であるこ
とを特徴とする鉛基合金の連続圧延製造法。
A molten lead-based alloy with a compact solidified structure is injected into the gap between a pair of rolls, and the solidified phase produced by cooling it on the outer peripheral surface of the rolls is continuously rolled. In the method for manufacturing, when the maximum effective width and thickness of the manufactured strip or plate are respectively t% and t, and the width and height of the nozzle outlet are LIT, then T/l.
1. A continuous rolling manufacturing method for a lead-based alloy, characterized in that t/L is 2 to 60 when is 2 to 30.
JP4607283A 1983-03-22 1983-03-22 Production of lead alloy by continuous rolling Granted JPS59174253A (en)