JPH07228817A - Fluorine coating composition - Google Patents

Abstract

(57) [Summary] [Structure] Fluoroolefin-based copolymer (A) having a crosslinkable functional group X ₁ such as a carboxyl group, and fluoroolefin-based copolymer having a crosslinkable functional group X ₂ such as a hydroxyl group that reacts with X _1. A copolymer (B), a (meth) acrylic copolymer (C) having a crosslinkable functional group Y such as an epoxy group that reacts with at least one of X ₁ and X ₂ and an auxiliary crosslinking agent (D). A fluorine-containing coating composition containing the same. [Effect] The composition of the present invention provides a coating film excellent in acid rain resistance, scratch resistance, stain resistance, weather resistance and the like, and is extremely useful particularly as a top coat for automobile bodies.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fluorine-containing coating composition, and more particularly to a fluorine-containing coating composition excellent in acid rain resistance, scratch resistance, stain resistance, and weather resistance.

[0002]

2. Description of the Related Art Conventionally, acrylic melamine-based paint has been widely used industrially as a top coat for automobile bodies because it is a one-pack type and has excellent coating workability and finished appearance and high cost performance. However, in recent years, acid rain has become a social problem, and the conventional acrylic melamine type has a drawback that the acid resistance of the cross-linking site of melamine is poor.

[0003]

Therefore, in recent years, compounds such as melamine resin, blocked isocyanate, silanol group, etc. as auxiliary cross-linking agents, which are mainly cured by epoxy group or carboxyl group of acrylic resin as a new curing system, have been developed. The added coating composition is promising or has been partially adopted. However, since these coating compositions have an acrylic resin as a main component, they have a drawback of hydrolysis of an acrylic ester bond by an acid, and there is a limit to improvement of acid resistance and stain removal.

Further, since the main component is an acrylic resin, there is a problem that although the initial acid resistance is good, the acid resistance after weather resistance deterioration is lowered. There is also a problem that stains remain on the coating film against contaminants such as bird droppings, and the stain does not recover even after washing with water.

Although a coating composition in which a hydroxyl group-containing fluororesin is crosslinked with melamine or the like has remarkably better coating performance than an acrylic melamine coating, since it also uses melamine, it is acid-resistant under severe test conditions of 80 ° C. or higher. There is a problem with sex.

[0006]

SUMMARY OF THE INVENTION The object of the present invention is to solve the various drawbacks of the prior art described above and to provide a new one having excellent stain resistance and weather resistance in addition to acid rain resistance and scratch resistance. Another object is to provide a useful fluorinated coating composition.

Accordingly, the present invention is the crosslinking functional fluoroolefin copolymer having a group X ₁ (A), fluoroolefin copolymer having a crosslinking functional group X ₂ which reacts with X ₁ (B), wherein A fluorine-based coating composition containing a (meth) acrylic copolymer (C) having a crosslinkable functional group Y that reacts with at least one of X ₁ and X ₂ and an auxiliary crosslinking agent (D).

The fluoroolefin copolymers (A) and (B) used in the present invention are polymers based on a fluoroolefin-based polymerized unit and an ethylenically unsaturated monomer having a crosslinkable functional group X ₁ or X _2. The copolymer containing the unit described above is preferable, and the copolymer containing the polymerized unit based on an ethylenically unsaturated monomer not containing the crosslinkable functional group X ₁ or X ₂ together with the polymerized unit is particularly preferable.

[0009] Copolymerization based on fluoroolefin in the body polymerized units / crosslinking functional group X ₁ or X ₂ units / crosslinking functional group X ₁ or X ₂ polymerized based on an ethylenically unsaturated monomer having a The copolymerization ratio of the polymerized units based on the ethylenically unsaturated monomer not contained is 30 to 70 mol% / 1 to 70 mol% / 0 to 60 mol%, preferably 40
-60 mol% / 5-50 mol% / 0-45 mol%.

As the ethylenically unsaturated monomer, ethylenically unsaturated monomers such as vinyl ethers, allyl ethers, isopropenyl ethers, vinyl esters, allyl esters and olefins are preferably used.
Vinyl ethers are particularly desirable from the viewpoints of solvent solubility, control of coating film hardness, weather resistance, alternate copolymerizability, and polymerization yield.

Specific examples thereof include alkyl vinyl ethers and cycloalkyl vinyl ethers having an alkyl group or cycloalkyl group having about 2 to 8 carbon atoms such as ethyl vinyl ether and cyclohexyl vinyl ether.

Fluoroolefin copolymer (A),
The molecular weight of (B) is 3,000 to 10 in terms of weight average molecular weight.
50,000 is preferable, and if it is less than 3,000, the weather resistance is deteriorated, which is not preferable.

Fluoroolefin copolymer (A),
The fluoroolefin in (B) has the general formula CF ₂ ═C
FZ (however, Z is hydrogen, chlorine, fluorine, carbon number 1 to 3)
Or a perfluoroalkoxy group having 1 to 3 carbon atoms. The compound represented by the formula (4) is preferably adopted. Specifically, tetrafluoroethylene,
Examples include chlorotrifluoroethylene, hexafluoropropylene, perfluoropropyl vinyl ether and the like. The fluoroolefins may be used alone or in combination of two or more.

The crosslinkable functional group X ₁ or X ₂ of the fluoroolefin copolymer (A) or (B) is a hydroxyl group, an epoxy group, a carboxyl group, a carboxylic acid anhydride group, a hydrolyzable silyl group, Silanol group, amino group,
Examples thereof include a carbonyl group, an ester group, a thiol group and an aldehyde group.

Examples of the ethylenically unsaturated monomer having a hydroxyl group include hydroxyalkyl vinyl ethers such as hydroxybutyl vinyl ether and hydroxyethyl vinyl ether, hydroxyalkyl (meth) acrylates such as hydroxyethyl (meth) acrylate, and hydroxyethyl allyl ether. Examples thereof include hydroxyalkyl alloyl ether, hydroxyalkyl isopropenyl ether such as hydroxybutyl isopropenyl ether, and allyl alcohol.

Of these, hydroxyalkyl vinyl ethers and hydroxyalkyl isopropenyl ethers are preferable, and hydroxyalkyl vinyl ethers are particularly preferable in terms of copolymerizability with fluoroolefins.

Examples of the ethylenically unsaturated monomer having an epoxy group include aliphatic epoxy group-containing ethylenically unsaturated monomers such as glycidyl vinyl ether, glycidyl allyl ether and glycidyl (meth) acrylate, 3,4
Examples thereof include an alicyclic epoxy group-containing ethylenically unsaturated monomer such as epoxycyclohexyl vinyl ether and 3,4-epoxycyclohexylmethyl (meth) acrylate. Further, for the same reason as described above, the vinyl ether type is preferable as the ethylenically unsaturated monomer having an epoxy group.

Examples of the ethylenically unsaturated monomer having a carboxylic acid anhydride group include maleic anhydride, itaconic anhydride, citraconic anhydride, tetrahydrophthalic anhydride, hymic acid anhydride and 1,3-dicarboxylic acid. Carboxy-2-
Propene acid anhydride, 1,2-dicarboxy-4-hexene acid anhydride, 1,6-dicarboxy-4-hexane acid anhydride, vinyl succinic anhydride, allyl succinic anhydride, 1,2- In addition to acid anhydrides of dicarboxy-4-allylcyclohexane, acid anhydrides of vinyl trimellitate, acid anhydrides of vinyl 1,2,3-propanetricarboxylate, vinyl 1,2,4-butanetricarboxylate Acid anhydride, 3- (2 ', 3'-dicarboxypropyl)-
Acid anhydrides of polycarboxylic acid vinyl esters such as vinyl butyrate acid anhydrides or 1,2-ethyne vinyl diadipate acid anhydrides, 1,2-dicarboxyethyl vinyl ether acid anhydrides, 1,2-dicarboxy Allyl vinyl ether acid anhydride, 1,2-dicarboxypropyl vinyl ether acid anhydride, 1,2-dicarboxypropyl allyl ether acid anhydride, 3- (2 ′, 3′-dicarboxypropyl) butyl vinyl ether Acid anhydrides or acid anhydrides of polyhydric carboxylic acid vinyl ethers such as acid anhydrides of 1,2-cicarboxy-4-hydroxycyclohexane vinyl ether, acid anhydrides of 1,2,5,6-tetracarboxy-3-hexane , 1, 2, 6, 7-
Tetracarboxy-3-heptene acid anhydride, 1,2-
Examples thereof include vinyl monomers having two or more acid anhydride groups in the molecule such as bis (dicarboxypropionyloxy) ethylene acid anhydride.

As the ethylenically unsaturated monomer having a carboxyl group, carboxyalkyl vinyl ether,
Examples include carboxyalkyl vinyl ester and carboxyalkyl (meth) acrylate. Further, the fluoroolefin-based copolymer containing a polymerized unit based on the hydroxyl group-containing ethylenically unsaturated monomer may be half-esterified with an acid anhydride or the like to convert the hydroxyl group into a carboxyl group.

The ethylenically unsaturated monomer having a hydrolyzable silyl group is a compound having an olefinic unsaturated bond, an alkylene group, and a hydrolyzable alkoxysilyl group or silanol group in the molecule. Specifically, allyltrimethoxysilane, allyltriethoxysilane, 3-butenyltrimethoxysilane, 3-butenyltriethoxysilane, 1-methyl-2-propenyltrimethoxysilane, 1-methyl-2-propenyl. Trimethoxysilane, 1-methyl-2-propenyltriethoxysilane, 4-pentenyltrimethoxysilane, 4-pentenyltriethoxysilane, 1-methyl-3-butenyltrimethoxysilane, 1-methyl-3-butynyltriethoxysilane Methoxysilane, 2-methyl-3-butenyltrimethoxysilane, 2-meth Le-3-butenyltriethoxysilane, 5-hexenyltrimethoxysilane, 5-hexenyltriethoxysilane, 1-methyl-4-pentenyltrimethoxysilane, 6-heptenyltrimethoxysilane, 6-heptenyltriethoxysilane , 1-methyl-
5-hexenyltrimethoxysilane, 7-octenyltrimethoxysilane, 7-octenyltriethoxysilane, 3-methyl-6-heptenyltrimethoxysilane,
8-nonenyltrimethoxysilane, 8-nonenyltriethoxysilane, 2-methyl-7-octenyltrimethoxysilane, 9-decenyltrimethoxysilane, 9-decenyltriethoxysilane, 2-methyl-8- Nonenyltrimethoxysilane, 10-undecenyltrimethoxysilane, 10-undecenyltrimethoxysilane, 11-
Dodecenyl trimexisilane, 11-dodecenyltriethoxysilane, γ- (meth) acryloxypropyltrihydroxysilane, γ- (meth) acryloxypropylmethyldihydroxysilane, γ- (meth) acryloxybutylphenyldihydroxy Examples thereof include silane and γ- (meth) acryloxypropylphenylmethylhydroxysilane.

The (meth) acrylic copolymer (C) in the present invention is preferably a copolymer containing as an essential component a polymerized unit based on a derivative of (meth) acrylic acid having a crosslinkable functional group Y. The unit is contained in the copolymer in an amount of 1 to 80 mol%, preferably 5 to 50 mol%.

As the derivative of (meth) acrylic acid having a crosslinkable functional group Y, when the crosslinkable functional group Y is a hydroxyl group, hydroxymethyl (meth) acrylate, hydroxyethyl (meth) acrylate, hydroxypropyl (meth)
Acrylate, hydroxyalkyl (meth) acrylate such as hydroxybutyl (meth) acrylate, ring-opening adduct of hydroxyalkyl (meth) acrylate and ε-caprolactone, ring-opening adduct of (meth) acrylic acid and propylene oxide, and ( Examples thereof include ring-opening adducts of (meth) acrylic acid and ethylene oxide.

When the crosslinkable functional group Y is an epoxy group, it contains an aliphatic epoxy group-containing (meth) acrylate such as glycidyl (meth) acrylate and an alicyclic epoxy group such as 3,4-epoxycyclohexylmethyl (meth) acrylate. (Meth) acrylate etc. are mentioned.

When the crosslinkable functional group Y is a carboxyl group,
Monocarboxylic acids such as (meth) acrylic acid, polycarboxylic acids such as itaconic acid, fumaric acid, maleic acid, trimellitic acid, monoesters of these carboxylic acids, and acid anhydrides and hydroxyl group-containing compounds of these carboxylic acids And the additions thereof and the like.

When the crosslinkable functional group Y is a carboxylic acid anhydride group, succinic anhydride, methylsuccinic anhydride, dodecenylsuccinic anhydride, octadecenylsuccinic anhydride, phthalic anhydride, tetrahydrophthalic anhydride, Methyl (tetrahydrophthalic anhydride), hexahydrophthalic anhydride, methyl (hexahydrophthalic anhydride), tetrachlorophthalic anhydride, endomethylenetetrahydrophthalic anhydride, chlorendic anhydride, itaconic acid Examples thereof include anhydrides, citraconic anhydride, maleic anhydride, and the like.

When the crosslinkable functional group Y is a hydrolyzable silyl group, it is specifically γ- (meth) acryloxyethyltrimethoxysilane, γ- (meth) acryloxypropyltrimethoxysilane, γ- (meth). Acryloxypropyltriethoxysilane, γ- (meth) acryloxypropyltripropoxysilane, γ- (meth) acryloxypropylmethyldimethoxysilane, γ- (meth) acryloxypropylmethyldiethoxysilane, γ- (meth) acryl Roxypropylmethyldipropoxysilane, γ- (meth) acryloxybutylphenyldimethoxysilane, γ
-(Meth) acryloxybutylphenyldiethoxysilane, γ- (meth) acryloxybutylphenyldipropoxysilane, γ- (meth) acryloxypropyldimethylmethoxysilane, γ- (meth) acryloxypropyldimethylethoxysilane, γ Examples include-(meth) acryloxypropylphenylmethylmethoxysilane and γ- (meth) acryloxypropylphenylmethylethoxysilane.

Examples of the other crosslinkable functional group Y include silanol group, amino group, carbonyl group, ester group, thiol group and aldehyde group.

Further, other polymerizable monomers constituting the acrylic copolymer (A) include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, and (meth) acrylic. Ester of acrylic acid or methacrylic acid such as butyl acrylate, 2-ethylhexyl (meth) acrylate, lauryl (meth) acrylate, stearyl (meth) acrylate and monohydric alcohol having 1 to 22 carbon atoms, styrene, vinyltoluene At least one of various polymerizable monomers such as, (meth) acrylonitrile, α-methylstyrene, and acrylamide can be used.

The (meth) acrylic copolymer (C) is produced by a known method. That is, a (meth) acrylic acid derivative having a crosslinkable functional group Y or another polymerizable monomer is added in the presence of an azo-based or peroxide-based radical polymerization initiator at 60 to 180 ° C., more preferably 80 to 180 ° C. 1
It is obtained by continuing the reaction at a reaction temperature of 60 ° C. for 4 to 12 hours.

As the azo radical polymerization initiator, 2,
2-azobisisobutyronitrile, 2,2-azobis (2,4-dimethylvaleronitrile), 2,2-azobis (2-methylbutyronitrile) and the like are used as the peroxide radical polymerization initiator. , Benzoyl peroxide,
Examples thereof include lauryl peroxide and di-t-butyl peroxide.

The polymerization method is also not particularly limited, but solution polymerization is advantageous in terms of productivity and performance. As the polymerization medium, organic solvents such as aromatic hydrocarbons such as toluene and xylene, ketones such as methyl ethyl ketone and methyl isobutyl ketone, and esters such as ethyl acetate and n-butyl acetate are used. . If necessary, n-
Chain transfer agents such as dodecyl mercaptan, thioglycolic acid and α-methylstyrene dimer can also be used.

The weight average molecular weight of the (meth) acrylic copolymer (C) is preferably 3,000 to 100,000. When it is less than 3,000, performances such as solvent resistance, water resistance and weather resistance are significantly deteriorated, which is not preferable.

There are various combinations of the crosslinkable functional groups X ₁ and X ₂ of the fluoroolefin copolymers (A) and (B) of the present invention, and the top coat for automobile bodies and the like, which is the field of application of the present invention. When used as a combination, [X ₁ / X ₂ ] is [carboxyl group / hydroxyl group], [carboxyl group / hydroxyl group and epoxy group],
[Carboxylic anhydride group / epoxy group], [Carboxylic anhydride group / hydroxyl group and epoxy group], [Carboxyl group and hydroxyl group / epoxy group and hydroxyl group], [Epoxy group and hydroxyl group / hydrolyzable silyl group and hydroxyl group] ,
A combination of [hydroxyl group / hydrolyzable silyl group and hydroxyl group] and the like is preferable.

The combination of the functional groups [X ₁ or X ₂ / Y] or [Y / X ₁ or X ₂ ] is [carboxyl group / hydroxyl group], [carboxyl group / hydroxyl group and epoxy group], [carboxylic acid Anhydride group / epoxy group], [carboxylic acid anhydride group / hydroxyl group and epoxy group], [carboxyl group and hydroxyl group / epoxy group and hydroxyl group], [epoxy group and hydroxyl group / hydrolyzable silyl group and hydroxyl group] or [hydroxyl group] / Hydrolyzable silyl group and hydroxyl group] and the like are preferable.

Of course, the combination of the crosslinkable functional groups is not limited to the above-mentioned combination, and the above-mentioned combination may be used as a main crosslinking component, and a third crosslinkable functional group may be supplementarily used in combination if necessary. You can also A large number of combinations can be selected according to the following combinations of mutually reactive crosslinkable functional groups.

A carboxyl group, a carboxylic acid anhydride group, an epoxy group and a hydrolyzable silyl group react with the hydroxyl group, and an epoxy group and a hydrolyzable silyl group with respect to the carboxyl group in addition to the above hydroxyl group. React with the carboxylic acid anhydride group, in addition to the hydroxyl group, an epoxy group and a hydrolyzable silyl group react, and with respect to the epoxy group, the hydroxyl group, the carboxyl group, the carboxylic acid anhydride group of In addition, the hydrolyzable silyl group reacts, and the hydrolyzable silyl group reacts with the hydrolyzable silyl group in addition to the hydroxyl group, the carboxyl group, the carboxylic acid anhydride group, the epoxy group.

The composition ratio of the fluoroolefin copolymer (A), (B) and (meth) acrylic copolymer (C) of the present invention in the coating composition is not particularly limited.
(A) / (B) / (C) = 1 to 100/1 by weight ratio
00/1 to 100, preferably (A) / (B) / (C)
= 1 to 50/1 to 50/1 to 50. When it is out of this range, the functional group of the fluoroolefin copolymer (A), (B) or (meth) acrylic copolymer (C) is likely to remain in the coating film, and chemical resistance,
It is not preferable because the weather resistance decreases.

[0038] As the auxiliary crosslinking agent (D), crosslinking functional group X ₁ of the fluoroolefin copolymer (A), fluoroolefin copolymer (B) of the crosslinkable functional groups X ₂ and acrylic copolymerization A compound having reactivity with at least one functional group selected from the crosslinkable functional groups Y of the combination (C) is used. The amount of auxiliary cross-linking agent (D) used is (A), (B)
And (C) 0.1 to 100 relative to 100 parts by weight in total.
Parts by weight, preferably 1 to 50 parts by weight.

Examples of such cross-linking agents include melamine cross-linking agents,
Examples include amino resin-based crosslinking agents such as urea resin crosslinking agents and polybasic acid crosslinking agents, and polyisocyanate crosslinking agents such as blocked polyisocyanates.

Examples of the melamine cross-linking agent include butylated melamine, methylated melamine, and epoxy-modified melamine. Depending on the application, various degrees of modification of 0 to 6 can be used, and the degree of self-condensation can be appropriately selected. be able to. Examples of the urea resin crosslinking agent include methylated urea and butylated urea. As the polybasic acid crosslinking agent, long-chain aliphatic dicarboxylic acids, aromatic polyvalent carboxylic acids or acid anhydrides of these carboxylic acids are useful.

Examples of polyisocyanates include m
(Or p) -xylylene diisocyanate, 2,4
(Or 2,6) -tolylene diisocyanate, m (or p) -phenylene diisocyanate, aromatic diisocyanate compounds such as 4,4′-diphenylmethane diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2, Four
Aliphatic (alicyclic) diisocyanate compounds such as (or 2,6) -diisocyanate, 1,3- (isocyanatomethyl) cyclohexane, hexamethylene diisocyanate, isophorone diisocyanate, dimer acid diisocyanate, diisocyanate compounds and polyols (ethylene glycol, tris (Such as methylolpropane)
And adducts thereof, polymers of diisocyanate compounds and burette type polyisocyanate compounds.

As the blocking agent for the polyisocyanate compound, a volatile low-molecular active hydrogen compound is used. Methanol, ethanol, propanol, butanol, ethylene glycol, methyl cellosolve, butyl cellosolve, methyl carbinol, benzyl alcohol, phenyl cellosolve, and full. Alcohol compounds such as furyl alcohol and cyclohexanol, hydroxy tertiary amine compounds such as dimethylaminoethanol and diethylaminoethanol, amine compounds such as diphenylamine, phenylnaphthylamine, aniline and carbazole, formaldoxime and acetoald Oximes such as oximes, methyl ethyl ketoxime, cyclohexanone oxime, dimethyl malonate, diethyl malonate, Active methylene compounds such as ethyl acetate, lactam compounds such as ε-caprolactam, phenol, cresol, xylenol, p-ethylphenol, o-isopropylphenol, α (or β) -naphthol, p-nitrophenol, Phenol compounds such as p-chlorophenol, mercaptan compounds such as butyl mercaptan and thiophenol, acid amide compounds such as acetanilide and benzamide, imide compounds such as succinimide and maleic imide, imidazole compounds, Examples thereof include urea compounds, carbamate compounds, and imine sulfite compounds.

In addition to the components (A), (B) and (C), the composition of the present invention may optionally contain a conventional acrylic resin (having a crosslinkable functional group Y) generally used in coating compositions. No), polyester resin, amino resin, epoxy resin, polyurethane resin, etc. can also be mixed. In particular, the composition of the present invention can further increase the crosslink density by mixing a silicone resin having a siloxane bond.

Further, if necessary, a curing catalyst, a rheology modifier (for example, organic bentonite, crosslinked polymer particles, microgel, wax, etc.), a surface modifier, an ultraviolet absorber, a coloring pigment, a metallic pigment, an extender pigment, etc. are blended. be able to.

Examples of the curing catalyst include acids, bases, blocked acids, blocked bases, organic amines, organometallic compounds and metal chelate compounds.

The coating composition of the present invention is preferably used by dissolving or dispersing the above components in an organic solvent or water, and can be used as a solid color coating, a metallic coating and a clear coating.

[0047]

【Example】

"Synthesis Example of Fluoroolefin Copolymer" The monomer mixture shown in Table 1 was polymerized by appropriately adding the radical polymerization initiator t-butylperoxypivalate so that the weight average molecular weight shown in Table 1 was obtained. . The resin characteristic values of the obtained copolymer are shown in Table 1.

“Synthesis Example of (Meth) acrylic Copolymer”
A monomer mixture to which the radical polymerization initiator 2,2-azobis (2-methylbutyronitrile) was appropriately added so as to have the weight average molecular weight shown in Table 2, was added to the mixture in the same amount as n-butanol / Solvesso # 100. (Aromatic hydrocarbon manufactured by Esso Co.) = 20/80 (weight ratio) The solution was added dropwise to the solution at 120 ° C. for 4 hours, and aged at the same temperature for 3 hours. The resin characteristic values of the obtained copolymer are shown in Table 2.

"Preparation example of paint for base coat" Stirrer,
A flask equipped with a thermometer and a condenser was charged with 10 parts of n-butanol and 90 parts of toluene, and heated to 100 ° C. 40 parts of methyl methacrylate, 30 parts of ethyl acrylate, 15 parts of n-butyl acrylate,
A raw material consisting of 12 parts of 2-hydroxyethyl methacrylate, 3 parts of methacrylic acid and 1 part of azobisisobutyronitrile was mixed and continuously added dropwise for 4 hours. 3 at the same temperature
By holding for a while, the conversion rate to the resin was increased to obtain an acrylic resin having a solid content of 50% by weight. The weight average molecular weight of this acrylic resin was 40,000.

100 parts of this acrylic resin, Uban 20
SE-60 (Butylated melamine resin manufactured by Mitsui Toatsu Chemicals,
Solid content 60% by weight) 25 parts, Alpaste # 1700N
14 parts of L (aluminum paste manufactured by Toyo Aluminum Co., Ltd., solid content: 65% by weight) were mixed to obtain a base coat coating composition.

Next, this base coat coating composition was diluted with a mixed solvent of ethyl acetate / toluene / Solvesso # 150 (Aromatic hydrocarbon manufactured by Esso Co.) = 40/30/30 (weight ratio), and Ford cup # 4 was then diluted. And diluted for 13 seconds to obtain a silver metallic base coat paint.

[Examples 1 to 22] Weight ratios shown in Table 3 from the fluoroolefin copolymers A-1 to A-11 and the (meth) acrylic copolymers C-1 to C-6 shown in the synthesis examples. A coating composition was prepared. Each paint is diluted with a solvent,
Wet-on-wet spray coating on a steel sheet coated with the silver metallic base coat shown in the synthesis example, heat-curing at 140 ° C. for 30 minutes, and dry coating to 40
A clear coating of ~ 45 μm was obtained. The following coating film performance tests were conducted for each example, and the results are also shown in Table 3.

Acid resistance: 0.3 wt of 10% by weight sulfuric acid aqueous solution
Was spotted on the coated surface, heated at 70 ° C. for 1 hour and washed with water, and the edge depth of the spot portion was measured with a three-dimensional surface roughness meter.

Scratch resistance: A felt impregnated with a cleanser was reciprocated 50 times under a load of 500 g, and the gloss retention was calculated from the initial gloss and the scratch gloss.

Stain removing property: Carbon black is dispersed in water at a concentration of 0.1% by weight, and sprayed on a coated plate at 60 ° C.
The operation of baking for 20 minutes is repeated twice, and the operation of washing with water is defined as one cycle, and the stain removal property after 5 cycles is visually evaluated (○: dirt is removed well, Δ: some stains remain, ×: stain is considerably Remain).

Weather resistance: The gloss retention of the coating film after 3000 hours of exposure with a sunshine weather meter was indicated.

"Comparative Examples 1 to 8" Paints were prepared with the formulations shown in Table 4, and test plates were prepared in the same manner as in the examples. The results are shown in Table 4.
Shown in.

MF is Nikalac MW30 (Melamine resin manufactured by Sanwa Chemical Co., Ltd.), and BI is Coronate # 251.
3 (blocked isocyanate manufactured by Nippon Polyurethane Industry Co., Ltd.).

[0059]

[Table 1]

[0060]

[Table 2]

[0061]

[Table 3]

[0062]

[Table 4]

[0063]

INDUSTRIAL APPLICABILITY The composition of the present invention provides a coating film excellent in acid rain resistance, scratch resistance, stain resistance, weather resistance and the like, and is extremely useful particularly as a top coat for automobile bodies.

 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Nobuyuki Miyazaki, Nobuyuki Miyazaki 3-474 Tsukoshi, Tsukoshi, Kawasaki-ku, Kawasaki-ku, Kanagawa Pref., Asahi Glass Co., Ltd. 3 474 Address 2 Asahi Glass Co., Ltd. Tamagawa Branch Room (72) Inventor Atsuji Kido 4-60 Sunadabashi, Higashi-ku, Aichi Prefecture Nagoya City Mitsubishi Rayon Co., Ltd. Product Development Laboratory (72) Inventor Kazuhiko Hotta East, Nagoya City, Aichi Prefecture 4-60 Sunadabashi, Ku, Mitsubishi Rayon Co., Ltd. Product Development Laboratory (72) Inventor Takeshi Kato 4-1-1, Sunadabashi, Higashi-ku, Nagoya, Aichi Prefecture Mitsubishi Rayon Co., Ltd. Product Development Laboratory (72) Inventor Akio Iwamoto Product development, Mitsubishi Rayon Co., Ltd., 4-chome, Sunadabashi, 4-chome, Higashi-ku, Nagoya, Aichi Research house

Claims (12)

[Claims] 1. A fluoroolefin copolymer (A) having a crosslinkable functional group X ₁ , a crosslinkable functional group X which reacts with X _1.
A fluoroolefin copolymer (B) having ₂ and a crosslinkable functional group Y which reacts with at least one of the above X ₁ and X _2.
A fluorinated coating composition containing the (meth) acrylic copolymer (C) and an auxiliary crosslinking agent (D). 2. The composition according to claim 1, wherein the functional group X ₁ is at least one selected from a hydroxyl group, an epoxy group, a carboxyl group, a carboxylic acid anhydride group and a hydrolyzable silyl group. 3. The composition according to claim 1, wherein the functional group X ₂ is at least one selected from a hydroxyl group, an epoxy group, a carboxyl group, a carboxylic acid anhydride group and a hydrolyzable silyl group. 4. The composition according to claim 1, wherein the functional group Y is at least one selected from a hydroxyl group, an epoxy group, a carboxyl group, a carboxylic acid anhydride group and a hydrolyzable silyl group. 5. The combination of functional groups [X ₁ / X ₂ ] is [carboxyl group / hydroxyl group], [carboxyl group / hydroxyl group and epoxy group], [carboxylic acid anhydride group / epoxy group], [carboxylic acid anhydride]. Group / hydroxyl group and epoxy group], [carboxyl group and hydroxyl group / epoxy group and hydroxyl group], [epoxy group and hydroxyl group / hydrolyzable silyl group and hydroxyl group] or [hydroxyl group / hydrolyzable silyl group and hydroxyl group] The composition of 1. 6. A functional group [X ₁ or X ₂ / Y] or [Y
/ X ₁ or X ₂ ] is [carboxyl group /
[Hydroxyl group], [carboxyl group / hydroxyl group and epoxy group], [carboxylic acid anhydride group / epoxy group], [carboxylic acid anhydride group / hydroxyl group and epoxy group], [carboxyl group and hydroxyl group / epoxy group and hydroxyl group], [ An epoxy group and a hydroxyl group / a hydrolyzable silyl group and a hydroxyl group] or a [hydroxyl group / a hydrolyzable silyl group and a hydroxyl group]. 7. The composition ratio of the fluoroolefin copolymer (A), the fluoroolefin copolymer (B) and the acrylic copolymer (C) is (A) / (B) / by weight.
The composition according to claim 1, wherein (C) = 1-100 / 1-100 / 1-100. 8. The amount of auxiliary crosslinking agent (D) used is (A),
0.1 to 100 parts by weight of (B) and (C) in total
The composition of claim 1 which is 100 parts by weight. 9. A fluoroolefin copolymer (A) comprises:
A copolymer containing a polymerized unit based on a fluoroolefin and a polymerized unit based on an ethylenically unsaturated monomer having a crosslinkable functional group X ₁ and having a weight average molecular weight of 3,000 to
The composition of claim 1 which is 100,000. 10. A fluoroolefin copolymer (B)
Is a copolymer containing a polymerized unit based on a fluoroolefin and a polymerized unit based on an ethylenically unsaturated monomer having a crosslinkable functional group X ₂ and having a weight average molecular weight of 3,000.
The composition of claim 1 which is 0-100,000. 11. A (meth) acrylic copolymer (C) is
The composition according to claim 1, which is a copolymer containing polymerized units based on a derivative of (meth) acrylic acid having a crosslinkable functional group Y and having a weight average molecular weight of 3,000 to 100,000. 12. The composition according to claim 1, wherein the auxiliary crosslinking agent (D) is an amino resin or a polyisocyanate.