JPH06100828A - Water-base ink composition for ball-point pen - Google Patents

Abstract

PURPOSE:To obtain the subject compsn. which has such an excellent lubricity as to reduce the abrasion of a ball holder, and is excellent in durability and feeling during writing. CONSTITUTION:The objective water-base ink compsn. contains a water-sol. dye or a water-dispersible pigment, a water-sol. org. solvent, water, and at least one compd. selected from the group consisting of a keto acid amide and an amide of a keto acid deriv.

Description

Detailed Description of the Invention

[0001]

FIELD OF THE INVENTION The present invention relates to an aqueous ink composition for ballpoint pens. More specifically, the present invention relates to a water-based ink composition for a ball-point pen, which exhibits excellent lubricity, suppresses abrasion between the ball receiving seat and the ball of the ball-point pen tip, and makes ink flow out smoothly.

[0002]

2. Description of the Related Art Conventionally, water-based ink compositions for ballpoint pens have been formed by adding a water-soluble organic solvent such as a polyhydric alcohol or its derivative to an aqueous solution containing a water-soluble dye or a water-dispersible pigment. However, such a water-based ink composition for a ballpoint pen has poor lubricity, and the distance between the ball and the holder increases due to the rotation of the ball during writing, which causes rattling of the ball and poor rotation of the ball, resulting in poor writing quality. There is a drawback that so-called line skipping occurs in which parts of the handwriting are blurred.

[0003]

SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide a water-based ink composition for ball-point pens that overcomes the drawbacks of conventional water-based ball-point pens and has excellent lubricity and little bleeding and is stable over time. That is.

[0004]

As a result of intensive studies to solve these drawbacks, the present inventor has found that a water-based ink composition for ball-point pens comprising a water-soluble dye or water-dispersible pigment, a water-soluble organic solvent, and water. By providing a water-based ink composition for a ballpoint pen, which contains at least one keto acid amide or an amide of a keto acid derivative,
The above problems were solved.

The present invention will be described in detail below. The amide of keto acid or its derivative is added as a lubricant, and specifically, α-keto acid amide is pyruvic acid amide, 2-keto butyric acid amide, and β-keto acid amide is acetoacetic acid amide, propionyl acetic acid amide. Examples of the γ-keto acid amide include levulinic acid amide, and examples of the amide of the keto acid derivative include acetone dicarboxylic acid amide, oxamic acid amide, oxalic acid amide, oxalic acid amide, and meso-sulfuric acid amide. The amount used can be from 0.1 to 20% by weight, and preferably from 0.5 to 5% by weight, based on the total amount of the ink composition. If the amount used is small, a sufficient lubricating effect cannot be obtained, and if the amount used is large, the stability over time deteriorates.

The water-soluble dye contained in the water-based ink composition for ball-point pens of the present invention may be the one used in ordinary water-based inks. I. Acid Red 87, C.I. I. Acid Orange 56, C.I. I. Acids By Ole 4
9, C.I. I. Acid dyes such as Acid Blue 9, C.I. I.
Direct Yellow 50, C.I. I. Direct black 1
Direct dyes such as C.9. I. Basic Blue 9, C.I.
I. Basit clad 1, C.I. I. Basic dyes such as Basic Yellow 35 can be used, and they may be used alone or in combination of two or more kinds. As the pigment, various known pigments can be used, and specific examples include azo pigments, condensed polyazo pigments, phthalocyanine pigments,
Organic pigments such as quinacridone pigments, anthraquinone pigments, dioxazine pigments, indigo pigments, thioindigo pigments, perinone and perylene pigments, titanium oxide,
Inorganic pigments such as iron oxide and carbon black, and fluorescent pigments may be used, and these may be used alone or in combination of two or more kinds. The colorant may be used in an amount of 0.1 to 30% by weight, preferably 1 to 20% by weight, based on the total ink composition. If the amount used is small, the handwriting becomes thin, and if the amount used is large, the viscosity of the ink composition increases and the writing quality becomes poor.

As the dispersant, those generally used as pigment dispersants such as resins and surfactants can be used, and the amount thereof is preferably 1 to 20% by weight based on the total amount of the ink.

Examples of the water-soluble organic solvent include polyhydric alcohols such as ethylene glycol, propylene glycol and glycerin, glycol ethers such as propylene glycol monomethyl ether and glycol ether acetates such as propylene glycol monomethyl ether acetate. These may be used alone or in combination of two or more. The content of these water-soluble organic solvents is preferably 1 to 40% by weight based on the total amount of the ink. If the amount used is small, the pen tip will dry quickly, and if the writing line is blurred, if it is large, the handwriting will dry slowly.

In addition, if necessary, pseudoplasticity-imparting agents, rust preventives, surfactants, antiseptic / antifungal agents and the like can be appropriately selected and used. As the pseudoplasticity-imparting agent, natural polysaccharides and semi-synthetic cellulosic polymers can be used among general water-soluble polymers. More specifically, as a natural polysaccharide,
It is possible to use guar gum, locust bean gum, welan gum, rhamsan gum, xanthan gum and the like having a high molecular chemical structure composed of monosaccharides such as glucose, galactose, rhamnose, mannose and glucuronate. Further, as the semi-synthetic cellulose-based polymer,
It is possible to use methyl cellulose, ethyl cellulose, carboxymethyl cellulose, etc., which are water-soluble by esterifying or etherifying the hydroxyl groups of cellulose. Benzotriazole can be used as the rust preventive. As the preservative, phenol, potassium sorbate, sodium benzoate or the like can be used. As the mildew-proofing agent, 1,2-benzisothiazolin-3-one can be used.

[0010]

Although it is not clear why the water-based ink composition for a ballpoint pen of the present invention is effective in preventing abrasion of the ball receiving portion, it is presumed as follows. That is, it is considered that the keto acid amide or the amide of a keto acid derivative is adsorbed on the surface of the ball or the ball seat to form a thin film, and the lubricity of ball rotation is improved.

[0011]

EXAMPLES The present invention will be described in more detail with reference to examples. In the following, "part" means "% by weight". Example 1 Eosin (CI Acid Reed 87) 6.0 parts Propylene glycol 25.0 parts Neugen P (manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd., nonionic activator) 0.5 parts Sodium benzoate (preservative) 1. 0 part Proxel XL-2 (ICCIYAPAN Co., Ltd., fungicide) 0.5 part Pyruvamide 30.0 parts Benzotriazole (rust inhibitor) 0.5 parts Water 46.5 parts Above Each component was heated to 50 to 60 ° C., stirred for 2 hours, cooled, and then filtered to obtain a red ink. Example 2 Water black R455 (CI Acid Black 2) 8.0 parts Ethylene glycol 20.0 parts Sodium benzoate (preservative) 1.0 parts Proxel XL-2 (ICCI Japan Co., Ltd. , Antifungal agent 0.5 part Benzotriazole (rust inhibitor) 0.5 part Kerzan (manufactured by Sansei Co., Ltd., xanthan gum, pseudoplasticity imparting agent) 0.5 part Acetoacetamide 4.5 parts Water 65.0 Parts Of the above components, first, Kerzan was added to water little by little so as not to cause mamako, and completely dissolved by stirring. After the remaining components were added and dissolved by stirring, the mixture was filtered to obtain a black ink. Example 3 Carbon black 10.0 parts Sodium salt of styrene-acrylic acid copolymer (dispersant) 2.5 parts Glycerin 5.0 parts Bropyrene glycol 10.0 parts Phenols (preservatives) 0.5 parts Proxel XL-2 (manufactured by ICCI Japan Co., Ltd., mildewproofing agent) 0.5 part Benzotriazole (rust inhibitor) 0.5 part Oxamic acid amide 2.5 parts Water 68.5 parts In the above components , Carbon black, sodium salt of styrene-acrylic acid copolymer and water were dispersed in a sand mill for 1 hour, and the remaining components were mixed, dissolved by stirring and filtered to obtain a black ink. Example 4 Copper phthalocyanine blue 10.0 parts Sodium salt of styrene-maleic acid copolymer (dispersant) 2.0 parts Ethylene glycol 15.0 parts Diethylene glycol 5.0 parts Sodium benzoate (preservative) 1.0 parts Proxel XL-2 (ICCI Japan Co., Ltd., fungicide) 0.5 part Benzotriazole (rust inhibitor) 0.5 part Ramzan gum (Daiichi Kogyo Seiyaku Co., Ltd., pseudoplasticizer) 0.3 part Levulinic acid amide 0.5 part Water 65.2 parts Copper phthalocyanine blue, sodium salt of styrene-maleic acid copolymer and 30 parts of water in the above components were dispersed in a sand mill for 1 hour, and then other than rhamsan gum. 35.2 parts of the remaining components of the above are mixed with water, and ramzan gum is added little by little so that it cannot be mamako.
After stirring for 1 hour, a blue ink was obtained by filtration.

Comparative Example 1 A red ink was obtained by the same method as in Example 1 except that the pyruvic acid amide in the ink component was replaced with the same amount of water. Comparative Example 2 A black ink was obtained in the same manner as in Example 2, except that the acetoacetamide in the ink component was replaced with the same amount of water. Comparative Example 3 A black ink was obtained in the same manner as in Example 3, except that the same amount of water was used instead of oxamic acid. Comparative Example 4 A levulinic acid amide in the ink component of Example 4 was replaced with the same amount of water, and a blue ink was obtained by the same method.

[0013]

[Effect] The water-based ink compositions obtained in Examples 1 and 3 and Comparative Examples 1 and 3 were equipped with a super hard ball having a diameter of 0.6 mm and a ballpoint pen socket made of nickel silver with a built-in ink absorber and a relay core. With a so-called center-type writing instrument that fills an aqueous ball-point pen into a pen body, and the water-based ink compositions obtained in Examples 2 and 4 and Comparative Examples 2 and 4 have a ball-point pen tip at one end of a polypropylene tube. The effect was confirmed by using a spiral writing tester with a so-called free ink writing instrument obtained by press-fitting and further removing bubbles in the ink by centrifugation. The conditions of the tester at that time were a writing angle of 65 degrees and a load of 1
Test paper is JIS P320 at 00g and speed of 7cm / sec.
It was 1 writing paper A, and the ball sinking after 500 m writing under these conditions was measured using a tool microscope. In addition, a handwriting sensory test was performed by handwriting. The results are shown in Table 1.

[Table 1] Evaluation standard for writing feeling Smooth ─── Writing smoothly. Squeak ─── There is resistance and I cannot write smoothly. As described above, the water-based ink composition for a ballpoint pen according to the present invention has excellent lubricity, has an effect of reducing abrasion of the ball receiving seat, and has excellent durability and writing feeling.

Claims (1)

[Claims] 1. A water-based ink composition for a ballpoint pen containing a water-soluble dye or a water-dispersible pigment, a water-soluble organic solvent and water, which contains at least one keto acid amide or keto acid derivative amide. A water-based ink composition for a ballpoint pen, which is characterized in that