JP6804381B2 - Non-combustible liquid composition and method for producing non-combustible wood using it - Google Patents
Non-combustible liquid composition and method for producing non-combustible wood using it Download PDFInfo
- Publication number
- JP6804381B2 JP6804381B2 JP2017092012A JP2017092012A JP6804381B2 JP 6804381 B2 JP6804381 B2 JP 6804381B2 JP 2017092012 A JP2017092012 A JP 2017092012A JP 2017092012 A JP2017092012 A JP 2017092012A JP 6804381 B2 JP6804381 B2 JP 6804381B2
- Authority
- JP
- Japan
- Prior art keywords
- combustible
- wood
- liquid composition
- mass
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、不燃液組成物及びそれを用いた不燃木材の製造方法に関し、更に詳しくは、対象物に付与することにより、当該対象物を不燃化すると共に、薬剤が経時的に対象物の表面に析出することを十分に抑制できる不燃液組成物、及び、それを用いた不燃木材の製造方法に関する。 The present invention relates to a non-combustible liquid composition and a method for producing non-combustible wood using the non-combustible liquid composition. The present invention relates to a non-combustible liquid composition capable of sufficiently suppressing precipitation in, and a method for producing non-combustible wood using the same.
建築材料（建材）として用いられる木材は、リサイクル可能な天然資源であり、独特の風合い、調湿性、吸音性、断熱性等を有するという利点があるため、建築材料として数多く利用されている。
その一方で、木材は、火に弱いという欠点がある。
そのため、木材においては、この欠点を解決するため、種々検討が行われている。
Wood, which is used as a building material (building material), is a recyclable natural resource and has advantages such as unique texture, humidity control, sound absorption, and heat insulation, and is therefore widely used as a building material.
On the other hand, wood has the disadvantage of being vulnerable to fire.
Therefore, in wood, various studies have been conducted in order to solve this drawback.
その解決策の一つとして、木材を不燃材で被覆して不燃化する方法が知られている。具体的には、例えば、可燃性の木材を、石膏ボード等の不燃材で覆うという方法である。
ところが、木材を不燃材で被覆する場合、上述した木材特有の利点が失われてしまうという欠点がある。
また、木材を不燃材で被覆するという作業が別途必要となり、不燃材の厚みを加味した木材の寸法の再調整も必要となるため、作業効率が悪く、経済性にも劣るものである。
As one of the solutions, a method of coating wood with a non-combustible material to make it non-combustible is known. Specifically, for example, a method of covering flammable wood with a non-combustible material such as gypsum board.
However, when wood is coated with a non-combustible material, there is a drawback that the above-mentioned advantages peculiar to wood are lost.
Further, the work of covering the wood with a non-combustible material is required separately, and the size of the wood needs to be readjusted in consideration of the thickness of the non-combustible material, so that the work efficiency is poor and the economy is inferior.
これに対し、不燃液組成物を対象物である木材に付与し、当該木材自体を不燃化する技術が開発されている。
かかる薬剤としては、例えば、家具や障子等の生活用木質系材料体を防炎、難燃化する剤として、硫酸アンモニウム、第一リン酸アンモニウム、第二リン酸アンモニウム、ホウ酸アンモニウム、ホウ酸ナトリウム及びホウ酸からなる群から選ばれた少なくとも１種の化合物と、寸法安定効果のある固着化合物とを含有する水系防炎・難燃化剤が知られている（例えば、特許文献１参照）。
また、繊維、塗料、紙材、プラスチック等の材料に、不燃性を付与する不燃材として、硫酸アンモニウム、ホウ酸、リン酸水素二アンモニウムおよび重炭酸ナトリウムを有効成分として含む不燃剤が知られている（例えば、特許文献２参照）。
On the other hand, a technique has been developed in which a non-combustible liquid composition is applied to the target wood to make the wood itself non-combustible.
Examples of such chemicals include ammonium sulfate, ammonium monophosphate, ammonium dibasic phosphate, ammonium borate, and sodium borate as agents for flameproofing and flame-retardant wood-based materials for daily life such as furniture and obstacles. An aqueous flameproof / flame retardant agent containing at least one compound selected from the group consisting of boric acid and a fixing compound having a dimensional stabilizing effect is known (see, for example, Patent Document 1).
Further, as a non-combustible material that imparts non-combustibility to materials such as fibers, paints, paper materials, and plastics, a non-combustible agent containing ammonium sulfate, boric acid, diammonium hydrogen phosphate, and sodium bicarbonate as active ingredients is known. (See, for example, Patent Document 2).
しかしながら、特許文献１及び特許文献２に記載の不燃液組成物においては、木材の表面に経時的に不燃材が析出する現象（以下「粉吹き」という。）をある程度抑制することができるものの、極めて長期間屋外に晒される木材においては、十分に防止することはできない。
また、仮に、粉吹きを抑制するため、付与する不燃液組成物の量を減らす方法も考えられるが、この場合、不燃化効果が不十分となる欠点がある。
However, in the non-combustible liquid compositions described in Patent Document 1 and Patent Document 2, although the phenomenon that the non-combustible material is deposited on the surface of wood with time (hereinafter referred to as "powder blowing") can be suppressed to some extent, Wood that is exposed to the outdoors for an extremely long period of time cannot be sufficiently prevented.
Further, if a method of reducing the amount of the non-combustible liquid composition to be applied is conceivable in order to suppress powder blowing, in this case, there is a drawback that the non-combustible effect is insufficient.
本発明は上記事情に鑑みてなされたものであり、対象物に付与することにより該対象物を不燃化すると共に、不燃液組成物に含まれる固形分が経時的に対象物の表面に析出することを十分に抑制できる不燃液組成物及びそれを用いた不燃木材の製造方法を提供することを目的とする。 The present invention has been made in view of the above circumstances, and by applying it to an object, the object is made incombustible, and the solid content contained in the non-combustible liquid composition is precipitated on the surface of the object over time. It is an object of the present invention to provide a non-combustible liquid composition capable of sufficiently suppressing this and a method for producing non-combustible wood using the same.
本発明者は、上記課題を解決するため鋭意検討したところ、硫酸アンモニウムと、硼酸と、硼砂とを含有するものとし、これらの配合量を定め、更に、配合量同士の関係を定めることにより、上記課題を解決し得ることを見出し、本発明を完成させるに至った。 As a result of diligent studies to solve the above problems, the present inventor has determined that ammonium sulfate, boric acid, and borax are contained, and by determining the blending amounts of these, and further determining the relationship between the blending amounts, the above We have found that the problem can be solved and have completed the present invention.
本発明は、（１）硫酸アンモニウムと、硼酸と、硼砂と、水とを含有し、水の配合量１００質量部に対する硫酸アンモニウムの配合量Ａが１〜３５質量部であり、硼酸の配合量Ｂが１〜４０質量部であり、硼砂の配合量Ｃが１．５〜５０質量部であり、配合量Ａ、配合量Ｂ及び配合量Ｃが、
Ｃ＞Ｂ≧Ａ
の関係を満たす不燃液組成物に存する。
The present invention contains (1) ammonium sulfate, boric acid, borax, and water, and the amount A of ammonium sulfate is 1 to 35 parts by mass with respect to 100 parts by mass of water, and the amount B of boric acid is B. 1 to 40 parts by mass, the blending amount C of borax is 1.5 to 50 parts by mass, and the blending amount A, the blending amount B and the blending amount C are
C> B ≧ A
It exists in a non-combustible liquid composition satisfying the above relationship.
本発明は、（２）リン酸化合物を更に含有し、水の配合量１００質量部に対するリン酸化合物の配合量Ｄが０．１〜２０質量部であり、配合量Ａ及び配合量Ｄが、
Ａ＞Ｄ
の関係を満たす上記（１）記載の不燃液組成物に存する。
The present invention further contains (2) a phosphoric acid compound, and the compounding amount D of the phosphoric acid compound is 0.1 to 20 parts by mass with respect to 100 parts by mass of the compounding amount of water, and the compounding amount A and the compounding amount D are:
A> D
The non-combustible liquid composition according to (1) above, which satisfies the above relationship.
本発明は、（３）金属フッ化物を更に含有し、水の配合量１００質量部に対する金属フッ化物の配合量が０．１〜１０質量部である上記（１）又は（２）に記載の不燃液組成物に存する。 The present invention relates to (3) further containing metal fluoride, and the amount of metal fluoride blended is 0.1 to 10 parts by mass with respect to 100 parts by mass of water, according to (1) or (2) above. It exists in the non-combustible liquid composition.
本発明は、（４）シランカップリング剤を更に含有し、水の配合量１００質量部に対するシランカップリング剤の配合量が０．０５質量部以下である上記（１）〜（３）のいずれか１つに記載の不燃液組成物に存する。 The present invention further contains (4) a silane coupling agent, and any of the above (1) to (3), wherein the blending amount of the silane coupling agent is 0.05 parts by mass or less with respect to 100 parts by mass of water. It exists in the non-combustible liquid composition according to one.
本発明は、（５）浸透剤を更に含有し、該浸透剤が、アニオン性界面活性剤又はノニオン性界面活性剤である上記（１）〜（４）のいずれか１つに記載の不燃液組成物に存する。 The incombustible liquid according to any one of (1) to (4) above, which further contains (5) a penetrant, and the penetrant is an anionic surfactant or a nonionic surfactant. Resident in the composition.
本発明は、（６）上記（１）〜（５）のいずれか１つに記載の不燃液組成物を用いた不燃木材の製造方法であって、耐圧容器に木材を投入する投入工程と、耐圧容器内を０．０９ＭＰａ以下に減圧する減圧工程と、耐圧容器内に、不燃液組成物を注入する注入工程と、耐圧容器内を０．５〜１．２ＭＰａに加圧することにより、木材を、不燃液組成物が浸透した不燃液含有木材にする加圧浸透工程と、不燃液含有木材を５０〜８０℃で乾燥する乾燥工程と、を備え、不燃木材の体積あたりの付着固形分量が１００〜４００ｋｇ／ｍ３である不燃木材の製造方法に存する。 The present invention is (6) a method for producing non-combustible wood using the non-combustible liquid composition according to any one of (1) to (5) above, wherein the wood is charged into a pressure-resistant container. A decompression step of reducing the pressure inside the pressure-resistant container to 0.09 MPa or less, an injection step of injecting a non-combustible liquid composition into the pressure-resistant container, and a pressure inside the pressure-resistant container to 0.5 to 1.2 MPa are used to press the wood. , A pressure permeation step for making non-combustible liquid-containing wood infiltrated with the non-combustible liquid composition and a drying step for drying the non-combustible liquid-containing wood at 50 to 80 ° C. It exists in the method for producing non-combustible wood having a weight of ~ 400 kg / m 3 .
本発明は、（７）注入工程と、加圧浸透工程とを連続して行う上記（６）記載の不燃木材の製造方法に存する。 The present invention resides in the method for producing non-combustible wood according to (6) above, wherein (7) the injection step and the pressure infiltration step are continuously performed.
本発明の不燃液組成物においては、硫酸アンモニウムと、硼酸と、硼砂とを含有し、硫酸アンモニウムの配合量Ａ、硼酸の配合量Ｂ及び硼砂の配合量Ｃを上記範囲内としているので、対象物に付与した場合に、当該対象物を不燃化することが可能となり（不燃化効果）、また、不燃液組成物に含まれる固形分が経時的に対象物の表面に析出する、いわゆる粉吹きを十分に抑制することが可能となる（粉吹き抑制効果）。
このとき、配合量Ａ、配合量Ｂ及び配合量Ｃを、
Ｃ＞Ｂ≧Ａ
の関係を満たすようにすることで、上述した不燃化効果及び粉吹き抑制効果を両立させることができる。すなわち、当該対象物を、極めて長期間屋外に晒される建材として使用する場合であっても、経時的に粉吹きが生じることを極力抑制することができ、また、不燃化効果も維持することが可能となる。
The non-combustible liquid composition of the present invention contains ammonium sulfate, boric acid, and borax, and the amount A of ammonium sulfate, the amount B of boric acid, and the amount C of borax are within the above ranges. When applied, it becomes possible to make the object incombustible (non-combustible effect), and the solid content contained in the incombustible liquid composition is sufficiently precipitated on the surface of the object over time, so-called powder blowing. (Powder blowing suppression effect).
At this time, the blending amount A, the blending amount B, and the blending amount C are
C> B ≧ A
By satisfying the above-mentioned relationship, the above-mentioned non-combustible effect and powder blowing suppressing effect can be achieved at the same time. That is, even when the object is used as a building material exposed to the outdoors for an extremely long period of time, it is possible to suppress the occurrence of powder blowing over time as much as possible, and it is possible to maintain the non-combustible effect. It will be possible.
本発明の不燃液組成物においては、リン酸化合物を更に有し、リン酸化合物の配合量Ｄを上記範囲内とし、配合量Ａ及び配合量Ｄを、
Ａ＞Ｄ
の関係を満たすことにより、硼酸及び硼砂の溶解性を向上させることができる（溶解効果）。このことにより、不燃液組成物を対象物に付与した場合、硼酸及び硼砂が析出することなく、不燃液組成物を対象物の内部にまで浸透させることができる。その結果、硼酸及び硼砂が対象物の表面に析出して粉吹きが生じることを抑制することができる。
In the non-combustible liquid composition of the present invention, the phosphoric acid compound is further contained, the blending amount D of the phosphoric acid compound is within the above range, and the blending amount A and the blending amount D are set to.
A> D
By satisfying the above relationship, the solubility of boric acid and borax can be improved (dissolving effect). As a result, when the non-combustible liquid composition is applied to the object, the non-combustible liquid composition can be permeated into the object without precipitation of boric acid and borax. As a result, it is possible to prevent boric acid and borax from precipitating on the surface of the object and causing powder blowing.
本発明の不燃液組成物においては、金属フッ化物を更に含有し、金属フッ化物の配合量を上記範囲内とした場合、金属フッ化物の触媒作用により、硼酸及び硼砂の溶解度を向上させることができる。その結果、上述したことと同様に、硼酸及び硼砂による粉吹きが生じることを抑制することができる。 In the non-combustible liquid composition of the present invention, when the metal fluoride is further contained and the blending amount of the metal fluoride is within the above range, the solubility of boric acid and borax can be improved by the catalytic action of the metal fluoride. it can. As a result, it is possible to suppress the occurrence of powder blowing due to boric acid and borax, as described above.
本発明の不燃液組成物においては、シランカップリング剤を更に含有し、シランカップリング剤の配合量を上記範囲内とした場合、不燃液組成物に含まれる固形分の少なくとも一部を対象物に接着させることができる。これにより、上述した不燃化効果及び粉吹き抑制効果をより長期間継続して発揮することが可能となる。 In the non-combustible liquid composition of the present invention, when the silane coupling agent is further contained and the blending amount of the silane coupling agent is within the above range, at least a part of the solid content contained in the non-combustible liquid composition is the object. Can be adhered to. This makes it possible to continuously exert the above-mentioned non-combustible effect and powder blowing suppressing effect for a longer period of time.
本発明の不燃液組成物においては、浸透剤を更に含有し、当該浸透剤が、アニオン性界面活性剤又はノニオン性界面活性剤である場合、不燃液組成物の対象物への浸透性を向上させることができる。 The non-combustible liquid composition of the present invention further contains a penetrant, and when the penetrant is an anionic surfactant or a nonionic surfactant, the permeability of the non-combustible liquid composition to an object is improved. Can be made to.
本発明の不燃木材の製造方法においては、上述した不燃液組成物を用いるため、得られる不燃木材は、十分に不燃化されたものになると共に、不燃液組成物に含まれる固形分による粉吹きも生じ難い。
また、投入工程、減圧工程、注入工程、加圧浸透工程及び乾燥工程を備えることにより、不燃液組成物が対象物の内部にまで浸透するので、得られる不燃木材を、極めて長期間屋外に晒される建材として使用する場合であっても、経時的に粉吹きが生じることを極力抑制することができ、また、不燃化効果も維持することが可能となる。
このとき、注入工程と、加圧浸透工程とを連続して行うことにより、作業性及び経済性も向上する。
Since the non-combustible liquid composition described above is used in the method for producing non-combustible wood of the present invention, the obtained non-combustible wood becomes sufficiently non-combustible and powder blown by the solid content contained in the non-combustible liquid composition. Is unlikely to occur.
Further, by providing the charging step, the depressurizing step, the injection step, the pressure infiltration step and the drying step, the non-combustible liquid composition permeates into the inside of the object, so that the obtained non-combustible wood is exposed to the outdoors for an extremely long period of time. Even when it is used as a building material, it is possible to suppress the occurrence of powder blowing over time as much as possible, and it is possible to maintain the non-combustible effect.
At this time, workability and economy are also improved by continuously performing the injection step and the pressure infiltration step.
本発明に係る不燃液組成物は、対象物に付与して用いられる。すなわち、不燃液組成物は、対象物を不燃化するためのいわゆる不燃加工に用いられる。
ここで、対象物としては、建材、又は、輸送機械の内装材が挙げられる。
上記建材としては、木材、繊維、紙（和紙）、木質ボード、多孔質樹脂体等が挙げられる。
また、建材が用いられる部位は、特に限定されず、例えば、屋根材、壁材、床材、建具、建築物の内装材等に用いられる。
上記輸送機械としては、自動車、鉄道、船舶、航空機等が挙げられる。
The non-combustible liquid composition according to the present invention is applied to an object and used. That is, the non-combustible liquid composition is used for so-called non-combustible processing for making the object non-combustible.
Here, examples of the object include building materials and interior materials of transportation machines.
Examples of the building material include wood, fiber, paper (Japanese paper), wood board, and a porous resin body.
The part where the building material is used is not particularly limited, and is used for, for example, a roof material, a wall material, a floor material, a fitting, an interior material of a building, and the like.
Examples of the transportation machine include automobiles, railways, ships, aircraft and the like.
以下、必要に応じて図面を参照しつつ、本発明の好適な実施形態について詳細に説明する。なお、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。また、図面の寸法比率は図示の比率に限られるものではない。
本実施形態においては、対象物が建材であり、建材として木材を用いた場合について説明する。
なお、かかる木材の材質としては、特に限定されず、例えば、針葉樹や広葉樹の製材製品、集成材、合板、単板積層材（ＬＶＬ）、木粉ボード、繊維材、銘木等が挙げられる。
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the drawings as necessary. Unless otherwise specified, the positional relationship such as up, down, left, and right shall be based on the positional relationship shown in the drawings. Moreover, the dimensional ratio of the drawing is not limited to the ratio shown in the drawing.
In the present embodiment, a case where the object is a building material and wood is used as the building material will be described.
The material of the wood is not particularly limited, and examples thereof include sawn timber products of softwood and hardwood, laminated wood, plywood, single-plate laminated material (LVL), wood flour board, fiber material, and famous wood.
本実施形態に係る不燃液組成物は、硫酸アンモニウムと、硼酸と、硼砂と、リン酸化合物と、金属フッ化物と、シランカップリング剤と、浸透剤と、水とを含有する。
不燃液組成物においては、少なくとも、硫酸アンモニウムと、硼酸と、硼砂とを含有するので、木材に付与した場合、当該木材を不燃化した不燃木材とすることが可能となる（不燃化効果）。
また、得られる不燃木材は、不燃液組成物に含まれる固形分が経時的に不燃木材の表面に析出する、いわゆる粉吹きを十分に抑制することが可能となる（粉吹き抑制効果）。
なお、本明細書において、「不燃化」とは、対象物を燃えなくする、又は、炎が着かないようにすることであり、「不燃木材」は、不燃化させた木材を意味する。
The non-combustible liquid composition according to the present embodiment contains ammonium sulfate, boric acid, borax, a phosphoric acid compound, a metal fluoride, a silane coupling agent, a penetrant, and water.
Since the non-combustible liquid composition contains at least ammonium sulfate, boric acid, and borax, when it is applied to wood, the wood can be made into non-combustible wood (non-combustible effect).
Further, the obtained non-combustible wood can sufficiently suppress so-called powder blowing, in which the solid content contained in the non-combustible liquid composition is deposited on the surface of the non-combustible wood over time (powder blowing suppressing effect).
In addition, in this specification, "non-combustible" means making an object incombustible or preventing flames from arriving, and "non-combustible wood" means non-combustible wood.
不燃液組成物において、水の配合量１００質量部に対する硫酸アンモニウムの配合量Ａは１〜３５質量部である。この場合、硫酸アンモニウムが吸湿性に優れるので、硼酸や硼砂等の再結晶化を遅らせることができる。これにより、粉吹きを十分に抑制することができる。また、吸湿することによる不燃効果も期待できる。 In the non-combustible liquid composition, the amount A of ammonium sulfate compounded is 1 to 35 parts by mass with respect to 100 parts by mass of water compounded. In this case, since ammonium sulfate is excellent in hygroscopicity, recrystallization of boric acid, borax and the like can be delayed. Thereby, powder blowing can be sufficiently suppressed. In addition, a non-combustible effect can be expected by absorbing moisture.
水の配合量１００質量部に対する硫酸アンモニウムの配合量Ａが１質量部未満であると、硫酸アンモニウムによる吸湿効果が十分に得られない場合があり、配合量Ａが３５質量部を超えると、硫酸アンモニウムによる吸湿効果が大き過ぎて、不燃木材を乾燥することが困難となり、仮に乾燥したとしても、直ぐに再吸湿してしまうという欠点がある。 If the amount A of ammonium sulfate is less than 1 part by mass with respect to 100 parts by mass of water, the moisture absorption effect of ammonium sulfate may not be sufficiently obtained, and if the amount A exceeds 35 parts by mass, moisture absorption by ammonium sulfate may not be obtained. The effect is so great that it becomes difficult to dry the non-combustible wood, and even if it is dried, it has a drawback that it immediately reabsorbs moisture.
不燃液組成物において、水の配合量１００質量部に対する硼酸の配合量Ｂは１〜４０質量部である。この場合、硼酸が木材の熱分解による発熱を抑制するので、仮に、不燃木材が加熱されたとしても発熱して発火することを防止することができる。 In the non-combustible liquid composition, the amount B of boric acid is 1 to 40 parts by mass with respect to 100 parts by mass of water. In this case, since boric acid suppresses heat generation due to thermal decomposition of wood, even if non-combustible wood is heated, it is possible to prevent heat generation and ignition.
水の配合量１００質量部に対する硼酸の配合量Ｂが１質量部未満であると、硼酸による発熱防止効果を十分に発揮することができない場合があり、配合量Ｂが４０質量部を超えると、極めて長期間屋外に晒された場合に粉吹きの原因となる場合がある。 If the amount B of boric acid is less than 1 part by mass with respect to 100 parts by mass of water, the effect of preventing heat generation by boric acid may not be sufficiently exhibited, and if the amount B exceeds 40 parts by mass, It may cause powder blowing when exposed to the outdoors for an extremely long period of time.
不燃液組成物において、水の配合量１００質量部に対する硼砂の配合量Ｃは１．５〜５０質量部である。この場合、硼砂が不燃木材に対して被膜を形成するので、不燃木材を酸素から遮断することができる。 In the non-combustible liquid composition, the blending amount C of borax is 1.5 to 50 parts by mass with respect to 100 parts by mass of water. In this case, the borax forms a film on the non-combustible wood, so that the non-combustible wood can be shielded from oxygen.
水の配合量１００質量部に対する硼砂の配合量Ｃが１．５質量部未満であると、硼砂による被膜効果を十分に発揮することができない場合があり、配合量Ｃが５０質量部を超えると、極めて長期間屋外に晒された場合に粉吹きの原因となる場合がある。 If the blending amount C of borax is less than 1.5 parts by mass with respect to 100 parts by mass of water, the coating effect of borax may not be sufficiently exhibited, and if the blending amount C exceeds 50 parts by mass. , May cause powder blowing when exposed to the outdoors for an extremely long period of time.
不燃液組成物においては、水の配合量１００質量部に対する硫酸アンモニウムの配合量Ａと、水の配合量１００質量部に対する硼酸の配合量Ｂと、水の配合量１００質量部に対する硼砂の配合量Ｃとが、
Ｃ＞Ｂ≧Ａ
の関係を満たしている。
In the non-combustible liquid composition, the amount of ammonium sulfate compounded with respect to 100 parts by mass of water, the amount of boric acid compounded with respect to 100 parts by mass of water, and the amount of borax compounded with respect to 100 parts by mass of water C. And,
C> B ≧ A
Meet the relationship.
不燃液組成物においては、上記配合量を前提とし、硼砂の配合量Ｃを硼酸の配合量Ｂよりも多くすることにより、硼砂による被膜を緻密に形成したところに、硼酸が存在することになるので、不燃化効果をより効果的に発揮することができる。
また、硫酸アンモニウムの配合量Ａを、硼酸の配合量Ｂ以下とすることにより、吸湿性が高くなり過ぎずに、硼酸及び硼砂の再結晶化に基づく粉吹きを十分に抑制することができる。
したがって、不燃液組成物においては、上記関係を満たすことにより、不燃化効果及び粉吹き抑制効果を両立させることができる。
In the non-combustible liquid composition, on the premise of the above-mentioned blending amount, by making the blending amount C of borax larger than the blending amount B of boric acid, boric acid is present in the place where the film made of borax is densely formed. Therefore, the non-combustible effect can be exhibited more effectively.
Further, by setting the amount A of ammonium sulfate to be less than or equal to the amount B of boric acid, it is possible to sufficiently suppress powder blowing based on the recrystallization of boric acid and borax without excessively increasing hygroscopicity.
Therefore, in the non-combustible liquid composition, by satisfying the above relationship, both the non-combustible effect and the powder blowing suppressing effect can be achieved at the same time.
不燃液組成物においては、リン酸化合物が含まれていることが好ましい。
リン酸化合物としては、リン酸、リン酸ナトリウム、リン酸アンモニウム、リン酸カリウム、リン酸カルシウム、リン酸マグネシウム等が挙げられる。
これらの中でも、不燃液組成物は、リン酸化合物としてリン酸を含有していることがより好ましい。
The non-combustible liquid composition preferably contains a phosphoric acid compound.
Examples of the phosphoric acid compound include phosphoric acid, sodium phosphate, ammonium phosphate, potassium phosphate, calcium phosphate, magnesium phosphate and the like.
Among these, the non-combustible liquid composition more preferably contains phosphoric acid as a phosphoric acid compound.
不燃液組成物においては、水の配合量１００質量部に対するリン酸化合物の配合量Ｄは０．１〜２０質量部であることが好ましい。この場合、リン酸化合物が吸湿性に優れるので、硼酸や硼砂等の再結晶化を遅らせることができる。これにより、粉吹きをより抑制することができる。
また、吸湿することによる不燃効果も期待できる。
In the non-combustible liquid composition, the amount D of the phosphoric acid compound is preferably 0.1 to 20 parts by mass with respect to 100 parts by mass of water. In this case, since the phosphoric acid compound is excellent in hygroscopicity, recrystallization of boric acid, borax and the like can be delayed. As a result, powder blowing can be further suppressed.
In addition, a non-combustible effect can be expected by absorbing moisture.
水の配合量１００質量部に対するリン酸化合物の配合量Ｄが０．１質量部未満であると、配合量Ｄが上記範囲内にある場合と比較して、リン酸化合物による吸湿効果が十分に得られない場合があり、配合量Ｄが２０質量部を超えると、配合量Ｄが上記範囲内にある場合と比較して、リン酸化合物による吸湿効果が大き過ぎて、不燃木材を乾燥することが困難となり、また、不燃液組成物自体がベタついて取り扱い難くなる欠点がある。 When the amount D of the phosphoric acid compound is less than 0.1 parts by mass with respect to 100 parts by mass of water, the hygroscopic effect of the phosphoric acid compound is sufficient as compared with the case where the amount D is within the above range. In some cases, when the blending amount D exceeds 20 parts by mass, the hygroscopic effect of the phosphoric acid compound is too large as compared with the case where the blending amount D is within the above range, and the non-combustible wood is dried. In addition, the non-combustible liquid composition itself is sticky and difficult to handle.
不燃液組成物においては、水の配合量１００質量部に対する硫酸アンモニウムの配合量Ａと、水の配合量１００質量部に対するリン酸化合物の配合量Ｄとが、
Ａ＞Ｄ
の関係を満たすことが好ましい。この場合、不燃液組成物は、粉吹き抑制効果を発揮できると共に、ベタつくことや腐食することも防止することができる。
In the non-combustible liquid composition, the blending amount A of ammonium sulfate with respect to 100 parts by mass of water and the blending amount D of the phosphoric acid compound with respect to 100 parts by mass of water are
A> D
It is preferable to satisfy the relationship of. In this case, the non-combustible liquid composition can exert the effect of suppressing powder blowing, and can also prevent stickiness and corrosion.
不燃液組成物においては、金属フッ化物が含まれていることが好ましい。
金属フッ化物としては、フッ化リチウム、フッ化ナトリウム、フッ化カリウム等のアルカリ金属フッ化物、フッ化カルシウム、フッ化マグネシウム等のアルカリ土類金属フッ化物が挙げられる。
これらの中でも、不燃液組成物は、金属フッ化物としてフッ化ナトリウムを含有していることがより好ましい。
The non-combustible liquid composition preferably contains metal fluoride.
Examples of the metal fluoride include alkali metal fluorides such as lithium fluoride, sodium fluoride and potassium fluoride, and alkaline earth metal fluorides such as calcium fluoride and magnesium fluoride.
Among these, the non-combustible liquid composition more preferably contains sodium fluoride as a metal fluoride.
不燃液組成物において、水の配合量１００質量部に対する金属フッ化物の配合量は０．１〜１０質量部であることが好ましい。この場合、金属フッ化物の触媒作用により、硼酸及び硼砂の溶解性が向上するので、不燃液組成物を木材に付与した場合、硼酸及び硼砂が析出することなく、不燃液組成物を木材の内部にまで浸透させることが可能となる。その結果、硼酸及び硼砂が木材の表面に析出して粉吹きが生じることを抑制することができる。 In the non-combustible liquid composition, the blending amount of the metal fluoride is preferably 0.1 to 10 parts by mass with respect to 100 parts by mass of the blending amount of water. In this case, the catalytic action of the metal fluoride improves the solubility of boric acid and borax. Therefore, when the incombustible liquid composition is applied to wood, the incombustible liquid composition is applied to the inside of the wood without precipitation of boric acid and borax. It is possible to infiltrate up to. As a result, it is possible to prevent boric acid and borax from depositing on the surface of the wood and causing powder blowing.
水の配合量１００質量部に対する金属フッ化物の配合量が０．１質量部未満であると、配合量が上記範囲内にある場合と比較して、金属フッ化物による効果を十分に発揮できない場合があり、配合量が１０質量部を超えると、配合量が上記範囲内にある場合と比較して、金属フッ化物による効果に向上が認められず、コスト高となる欠点がある。 When the amount of metal fluoride compounded with respect to 100 parts by mass of water is less than 0.1 part by mass, the effect of metal fluoride cannot be sufficiently exhibited as compared with the case where the compounding amount is within the above range. If the blending amount exceeds 10 parts by mass, the effect of the metal fluoride is not improved as compared with the case where the blending amount is within the above range, and there is a drawback that the cost is high.
不燃液組成物においては、シランカップリング剤が含まれていることが好ましい。
シランカップリング剤としては、アルキルシラン、アルコキシシラン、ビニルシラン、エポキシシラン、アミノシラン、アクリルシラン、メタクリルシラン、スチリルシラン、メルカプトシラン、スルフィドシラン、ウレイドシラン、イソシアネートシラン、サルファーシラン、アルキルクロロシラン等が挙げられる。
The non-combustible liquid composition preferably contains a silane coupling agent.
Examples of the silane coupling agent include alkylsilane, alkoxysilane, vinylsilane, epoxysilane, aminosilane, acrylicsilane, methacrylsilane, styrylsilane, mercaptosilane, sulfidesilane, ureidosilane, isocyanatesilane, sulfersilane, and alkylchlorosilane. ..
不燃液組成物において、水の配合量１００質量部に対するシランカップリング剤の配合量は０．０５質量部以下であることが好ましい。この場合、不燃液組成物に含まれる固形分の少なくとも一部を木材に接着させることができる。これにより、上述した不燃化効果及び粉吹き抑制効果をより長期間継続して発揮することが可能となる。 In the non-combustible liquid composition, the blending amount of the silane coupling agent with respect to 100 parts by mass of water is preferably 0.05 parts by mass or less. In this case, at least a part of the solid content contained in the non-combustible liquid composition can be adhered to the wood. This makes it possible to continuously exert the above-mentioned non-combustible effect and powder blowing suppressing effect for a longer period of time.
水の配合量１００質量部に対するシランカップリング剤の配合量が０．０５質量部を超えると、配合量が上記範囲内にある場合と比較して、不燃液組成物の保存時に、副反応を引き起こし、保存安定性を阻害する恐れがある。 When the blending amount of the silane coupling agent exceeds 0.05 parts by mass with respect to 100 parts by mass of water, a side reaction occurs during storage of the non-combustible liquid composition as compared with the case where the blending amount is within the above range. It may cause and impair storage stability.
不燃液組成物においては、浸透剤が含まれていることが好ましい。
浸透剤としては、アニオン性界面活性剤又はノニオン性界面活性剤が挙げられる。
アニオン性界面活性剤としては、特に限定されず、市販のものを適宜採用することができる。例えば、脂肪酸塩、モノアルキル硫酸塩、アルキルポリオキシエチレン硫酸塩、アルキルベンゼンスルホン酸塩、モノアルキルリン酸塩等が挙げられる。
ノニオン性界面活性剤としては、特に限定されず、市販のものを適宜採用することができる。例えば、ポリオキシエチレンアルキルエーテル、脂肪酸ソルビタンエステル、アルキルポリグルコシド、脂肪酸ジエタノールアミド、アルキルモノグリセリルエーテル等が挙げられる。
The non-combustible liquid composition preferably contains a penetrant.
Examples of the penetrant include an anionic surfactant or a nonionic surfactant.
The anionic surfactant is not particularly limited, and commercially available ones can be appropriately adopted. Examples thereof include fatty acid salts, monoalkyl sulfates, alkyl polyoxyethylene sulfates, alkylbenzene sulfonates, monoalkyl phosphates and the like.
The nonionic surfactant is not particularly limited, and a commercially available surfactant can be appropriately used. For example, polyoxyethylene alkyl ether, fatty acid sorbitan ester, alkyl polyglucoside, fatty acid diethanolamide, alkyl monoglyceryl ether and the like can be mentioned.
不燃液組成物において、水の配合量１００質量部に対する浸透剤の配合量は０．１〜３．０質量部であることが好ましい。この場合、不燃液組成物の木材への浸透性を向上させることができる。 In the non-combustible liquid composition, the blending amount of the penetrant is preferably 0.1 to 3.0 parts by mass with respect to 100 parts by mass of water. In this case, the permeability of the non-combustible liquid composition to wood can be improved.
上述したように、不燃液組成物は、例えば、建材である木材に付与して用いられる。好ましくは、乾燥させた木材に付与して用いられる。
付与方法は、特に限定されず、浸漬、スプレー、コーティング等が挙げられる。
なお、不燃液組成物を木材に付与した後は、乾燥して水分を除去することにより、不燃木材が得られる。
As described above, the non-combustible liquid composition is used, for example, by applying it to wood as a building material. Preferably, it is applied to dried wood for use.
The application method is not particularly limited, and examples thereof include immersion, spraying, and coating.
After the non-combustible liquid composition is applied to the wood, the non-combustible wood is obtained by drying and removing water.
次に、不燃液組成物を用いた不燃木材の製造方法の一例について説明する。
図１は、本発明に係る不燃木材の製造方法を示すフローチャートである。
図１に示すように、不燃木材の製造方法は、投入工程Ｓ１と、減圧工程Ｓ２と、注入工程Ｓ３と、加圧浸透工程Ｓ４と、乾燥工程Ｓ５とを備える。
不燃木材の製造方法においては、これらの工程を順次行うことにより、耐火性が極めて優れる木粉ボードを比較的容易に製造することができる。
Next, an example of a method for producing non-combustible wood using the non-combustible liquid composition will be described.
FIG. 1 is a flowchart showing a method for producing non-combustible wood according to the present invention.
As shown in FIG. 1, the method for producing non-combustible wood includes a charging step S1, a depressurizing step S2, an injection step S3, a pressure infiltration step S4, and a drying step S5.
In the method for producing non-combustible wood, by sequentially performing these steps, it is possible to relatively easily produce a wood flour board having extremely excellent fire resistance.
投入工程Ｓ１は、耐圧容器に木材を投入し、該耐圧容器を密閉する工程である。
図２の（ａ）は、本実施形態に係る木粉ボードの製造方法の投入工程において用いられる耐圧容器を模式的に示す斜視図であり、（ｂ）は、その概略側面図である。
図２の（ａ）に示すように、耐圧容器１０は、横方向に延びる中空円筒状であり、前側に蓋１１を備え、後ろ側の図示しない側面に注入管１２が取り付けられている。
また、図２の（ｂ）に示すように、当該注入管１２には、ポンプＰが取り付けられている。
そして、注入管１２の先には、後述する不燃液が貯留されたタンク１３が、耐圧容器１０の上方位置に取り付けられている。すなわち、タンク１３は、ポンプＰが取り付けられた注入管１２を介して、耐圧容器１０に連結されている。
The charging step S1 is a step of charging wood into a pressure-resistant container and sealing the pressure-resistant container.
FIG. 2A is a perspective view schematically showing a pressure-resistant container used in the charging process of the wood powder board manufacturing method according to the present embodiment, and FIG. 2B is a schematic side view thereof.
As shown in FIG. 2A, the pressure-
Further, as shown in FIG. 2B, a pump P is attached to the
A
投入工程Ｓ１においては、木材１を耐圧容器１０内に投入し、耐圧容器１０の前側の蓋１１を閉めて、耐圧容器１０内を密閉状態とする。
In the charging step S1, the wood 1 is charged into the pressure-
減圧工程Ｓ２は、耐圧容器１０内を密閉した状態で、耐圧容器１０内をポンプＰによって強制的に減圧する工程である。これにより、木材１の内部の空気も同時に除去することができる。
The decompression step S2 is a step of forcibly depressurizing the inside of the pressure-
ここで、減圧工程Ｓ２においては、耐圧容器１０内の圧力が０．０９ＭＰａ以下となるまで減圧することが好ましい。
耐圧容器１０内の圧力が０．０９ＭＰａを超えた値であると、圧力が上記範囲内にある場合と比較して、後の加圧浸透工程において、不燃液組成物が木材１に十分に浸透しない恐れがある。
Here, in the depressurizing step S2, it is preferable to reduce the pressure until the pressure in the pressure-
When the pressure in the pressure-
注入工程Ｓ３は、タンク１３に貯留された不燃液組成物を、注入管１２内を介して、耐圧容器１０内に注入する工程である。これにより、空気が除去された木材の内部にまで不燃液組成物は侵入することになる。
なお、注入工程Ｓ３により、耐圧容器１０内は減圧環境下から解放される。
The injection step S3 is a step of injecting the incombustible liquid composition stored in the
In the injection step S3, the inside of the pressure-
加圧浸透工程Ｓ４は、タンク１３に貯留された不燃液組成物を、注入管１２内を介して、ポンプＰによって強制的に耐圧容器１０内に注入し、耐圧容器内を加圧する工程である。これにより、耐圧容器１０内は、加圧環境下となり、木材１の内部に不燃液組成物を確実に浸透させることができる。
こうして、木材１に不燃液組成物が浸透した不燃液含有木材が得られる。
The pressurized permeation step S4 is a step of forcibly injecting the non-combustible liquid composition stored in the
In this way, a non-combustible liquid-containing wood in which the non-combustible liquid composition has penetrated into the wood 1 can be obtained.
ここで、加圧浸透工程Ｓ４においては、耐圧容器１０内の圧力が０．５〜１．２ＭＰａとなるまで加圧することが好ましい。
耐圧容器１０内の圧力が０．５ＭＰａ未満の値であると、圧力が上記範囲内にある場合と比較して、木材１への不燃液組成物の浸透が不十分となる場合があり、耐圧容器１０内の圧力が１．２ＭＰａを超えた値であると、圧力が上記範囲内にある場合と比較して、木材１の組織が不燃液組成物によって破壊される恐れがある。
Here, in the pressure infiltration step S4, it is preferable to pressurize until the pressure in the pressure
If the pressure in the pressure-
また、耐圧容器１０内は、温度を管理することが好ましい。具体的には、耐圧容器１０内の温度を２０℃〜８０℃とすることが好ましい。
温度が２０℃未満であると、温度が上記範囲内にある場合と比較して、不燃液組成物を十分に活性化させることができず、不燃液組成物の浸透に時間を要する場合があり、温度が８０℃を超えると、加圧が安定せず不燃液組成物が浸透しにくくなる可能性がある。
Further, it is preferable to control the temperature inside the pressure-
If the temperature is less than 20 ° C., the non-combustible liquid composition cannot be sufficiently activated as compared with the case where the temperature is within the above range, and it may take time for the non-combustible liquid composition to permeate. If the temperature exceeds 80 ° C., the pressurization may not be stable and the incombustible liquid composition may not easily permeate.
乾燥工程Ｓ５は、不燃液含有木材を耐圧容器１０から取り出し、乾燥させることにより、不燃液含有木材に含まれる不燃液組成物の水分を除去した不燃木材とする工程である。
なお、乾燥方法は、特に限定されず、熱風乾燥、風乾等で行えばよい。
The drying step S5 is a step of taking out the non-combustible liquid-containing wood from the pressure-
The drying method is not particularly limited, and may be performed by hot air drying, air drying, or the like.
ここで、乾燥工程Ｓ５における温度は、５０〜８０℃であることが好ましい。
温度が５０℃未満の値であると、温度が上記範囲内にある場合と比較して、不燃液含有木材の乾燥が不十分となる場合があり、温度が８０℃を超えると、温度が上記範囲内にある場合と比較して、水分の蒸発の際に、不燃液組成物に含まれる固形分がマイグレーションを引き起こし、木材１に十分に定着しない恐れがある。
Here, the temperature in the drying step S5 is preferably 50 to 80 ° C.
If the temperature is less than 50 ° C, the drying of the non-combustible liquid-containing wood may be insufficient as compared with the case where the temperature is within the above range, and if the temperature exceeds 80 ° C, the temperature is described above. Compared with the case where the temperature is within the range, the solid content contained in the non-combustible liquid composition may cause migration and may not be sufficiently fixed to the wood 1 when the water is evaporated.
また、乾燥工程Ｓ５は、不燃木材の重量含水率が５〜２０％となるまで行うことが好ましい。
重量含水率が５％未満とすると、重量含水率が上記範囲内にある場合と比較して、後に不燃木材が吸水して、寸法が変化する恐れがあり、重量含水率が２０％を超えると、重量含水率が上記範囲内にある場合と比較して、不燃液組成物に含まれる固形分が木材１に十分に定着しない恐れがある。
Further, the drying step S5 is preferably performed until the weight moisture content of the non-combustible wood reaches 5 to 20%.
If the weight moisture content is less than 5%, the non-combustible wood may absorb water later and the dimensions may change compared to the case where the weight moisture content is within the above range, and if the weight moisture content exceeds 20%. Compared with the case where the weight moisture content is within the above range, the solid content contained in the non-combustible liquid composition may not be sufficiently fixed to the wood 1.
こうして、木材１に不燃液組成物を付与することにより、木材１自体を不燃化した不燃木材が得られる。
ここで、不燃木材の体積あたりの付着固形分量は１００〜４００ｋｇ／ｍ３であることが好ましく、１２０〜４００ｋｇ／ｍ３であることがより好ましい。
By imparting the non-combustible liquid composition to the wood 1 in this way, a non-combustible wood obtained by incombustible the wood 1 itself can be obtained.
Here, it is preferable that deposition solid content per volume of non-combustible timber is 100~400kg / m 3, more preferably 120~400kg / m 3.
不燃木材の製造方法においては、上述した不燃液組成物を用いるため、得られる不燃木材は、十分に不燃化されたものになると共に、不燃液組成物に含まれる固形分による粉吹きも生じ難い。
また、投入工程Ｓ１、減圧工程Ｓ２、注入工程Ｓ３、加圧浸透工程Ｓ４及び乾燥工程Ｓ５を備えることにより、不燃液組成物が木材１の内部にまで浸透するので、得られる不燃木材を、極めて長期間屋外に晒される建築材料として使用する場合であっても、経時的に粉吹きが生じることを極力抑制することができ、また、不燃化効果も維持することが可能となる。
Since the non-combustible liquid composition described above is used in the method for producing non-combustible wood, the obtained non-combustible wood is sufficiently incombustible, and powder blowing due to the solid content contained in the non-combustible liquid composition is unlikely to occur. ..
Further, by providing the charging step S1, the depressurizing step S2, the injection step S3, the pressure infiltration step S4, and the drying step S5, the noncombustible liquid composition permeates into the inside of the wood 1, so that the obtained noncombustible wood can be extremely produced. Even when it is used as a building material exposed to the outdoors for a long period of time, it is possible to suppress the occurrence of powder blowing over time as much as possible, and it is possible to maintain the non-combustible effect.
なお、不燃木材の製造方法においては、注入工程Ｓ３と、加圧浸透工程Ｓ４とを連続して行うことが好ましい。この場合、作業性及び経済性も向上する。 In the method for producing non-combustible wood, it is preferable that the injection step S3 and the pressure infiltration step S4 are continuously performed. In this case, workability and economy are also improved.
以上、本発明の好適な実施形態について説明したが、本発明は上記実施形態に限定されるものではない。 Although the preferred embodiment of the present invention has been described above, the present invention is not limited to the above embodiment.
本実施形態に係る不燃液組成物においては、対象物として、建材を用いた例で説明しているが、輸送機器の内装材を用いてもよい。
本実施形態に係る不燃木材の製造方法においては、木材を不燃化する場合について説明しているが、木材以外の建材を用いてもよい。なお、この場合、不燃木材ではなく、木材以外の建材の不燃物が得られることになる。
In the non-combustible liquid composition according to the present embodiment, an example in which a building material is used as an object is described, but an interior material of a transportation device may be used.
In the method for producing non-combustible wood according to the present embodiment, the case of making wood non-combustible is described, but a building material other than wood may be used. In this case, non-combustible materials of building materials other than wood can be obtained instead of non-combustible wood.
本実施形態に係る不燃液組成物は、硫酸アンモニウムと、硼酸と、硼砂と、リン酸化合物と、金属フッ化物と、シランカップリング剤と、浸透剤と、水とを含有しているが、リン酸化合物、金属フッ化物、シランカップリング剤及び浸透剤は、必ずしも必須の成分ではない。 The non-combustible liquid composition according to the present embodiment contains ammonium sulfate, boric acid, borax, a phosphoric acid compound, a metal fluoride, a silane coupling agent, a penetrant, and water. Acid compounds, metal fluorides, silane coupling agents and penetrants are not necessarily essential components.
本実施形態に係る不燃液組成物においては、ポリフェノール系化合物が更に含まれていることが好ましい。
ポリフェノール系化合物としては、タンニン、カテキン、アントシアニン等が挙げられる。この場合、ポリフェノール化合物が、不燃液組成物に含まれる固形分の少なくとも一部を木材に接着させることができる。
これらの中でも、ポリフェノール系化合物としては、木材との親和性の観点から、タンニンを用いることが好ましい。
It is preferable that the non-combustible liquid composition according to the present embodiment further contains a polyphenol compound.
Examples of the polyphenol compound include tannin, catechin, anthocyanin and the like. In this case, the polyphenol compound can adhere at least a part of the solid content contained in the non-combustible liquid composition to the wood.
Among these, as the polyphenol compound, it is preferable to use tannin from the viewpoint of affinity with wood.
不燃液組成物においては、添加剤が更に含まれていてもよい。
添加剤としては、防腐剤、防虫剤、忌避剤、抗菌剤、消泡剤、樹脂、フィラー、ｐＨ調整剤等が挙げられる。
In the non-combustible liquid composition, additives may be further contained.
Examples of the additive include preservatives, insect repellents, repellents, antibacterial agents, antifoaming agents, resins, fillers, pH adjusters and the like.
本発明の不燃液組成物は、対象物を不燃化するために、当該対象物に付与して用いられる。また、木材に不燃液組成物が付与され、不燃化された不燃木材は、例えば、建築材料として好適に用いられる。
本発明の不燃液組成物によれば、対象物に付与することにより該対象物を不燃化すると共に、不燃液組成物に含まれる固形分が経時的に対象物の表面に析出することを十分に抑制できる。
The non-combustible liquid composition of the present invention is applied to an object and used in order to make the object non-combustible. Further, the non-combustible wood to which the non-combustible liquid composition is applied to the wood and made non-combustible is preferably used as a building material, for example.
According to the non-combustible liquid composition of the present invention, it is sufficient to make the target object incombustible by applying it to the target object and to allow the solid content contained in the non-combustible liquid composition to precipitate on the surface of the target object over time. Can be suppressed.
１・・・木材
１０・・・耐圧容器
１１・・・蓋
１２・・・注入管
１３・・・タンク
Ｐ・・・ポンプ
Ｓ１・・・投入工程
Ｓ２・・・減圧工程
Ｓ３・・・注入工程
Ｓ４・・・加圧浸透工程
Ｓ５・・・乾燥工程
1 ...
Claims (7)
前記水の配合量１００質量部に対する前記硫酸アンモニウムの配合量Ａが１〜３５質量部であり、前記硼酸の配合量Ｂが１〜４０質量部であり、前記硼砂の配合量Ｃが１．５〜５０質量部であり、
前記配合量Ａ、前記配合量Ｂ及び前記配合量Ｃが、
Ｃ＞Ｂ≧Ａ
の関係を満たす不燃液組成物。 Contains ammonium sulphate, boric acid, borax, and water,
The amount A of ammonium sulfate is 1 to 35 parts by mass, the amount B of boric acid is 1 to 40 parts by mass, and the amount C of borax is 1.5 to 100 parts by mass with respect to 100 parts by mass of the water. 50 parts by mass
The compounding amount A, the compounding amount B, and the compounding amount C are
C> B ≧ A
A non-combustible liquid composition that satisfies the relationship of.
前記水の配合量１００質量部に対する前記リン酸化合物の配合量Ｄが０．１〜２０質量部であり、
前記配合量Ａ及び前記配合量Ｄが、
Ａ＞Ｄ
の関係を満たす請求項１記載の不燃液組成物。 Further containing a phosphoric acid compound,
The amount D of the phosphoric acid compound is 0.1 to 20 parts by mass with respect to 100 parts by mass of the water.
The compounding amount A and the compounding amount D are
A> D
The non-combustible liquid composition according to claim 1, which satisfies the above relationship.
前記水の配合量１００質量部に対する前記金属フッ化物の配合量が０．１〜１０質量部である請求項１又は２に記載の不燃液組成物。 Further containing metal fluoride,
The non-combustible liquid composition according to claim 1 or 2, wherein the amount of the metal fluoride compounded is 0.1 to 10 parts by mass with respect to 100 parts by mass of the water compounded.
前記水の配合量１００質量部に対する前記シランカップリング剤の配合量が０．０５質量部以下である請求項１〜３のいずれか１項に記載の不燃液組成物。 Further containing a silane coupling agent,
The non-combustible liquid composition according to any one of claims 1 to 3, wherein the blending amount of the silane coupling agent is 0.05 parts by mass or less with respect to 100 parts by mass of the blended amount of water.
該浸透剤が、アニオン性界面活性剤又はノニオン性界面活性剤である請求項１〜４のいずれか１項に記載の不燃液組成物。 Contains more penetrant,
The non-combustible liquid composition according to any one of claims 1 to 4, wherein the penetrant is an anionic surfactant or a nonionic surfactant.
耐圧容器に木材を投入する投入工程と、
前記耐圧容器内を０．０９ＭＰａ以下に減圧する減圧工程と、
前記耐圧容器内に、前記不燃液組成物を注入する注入工程と、
前記耐圧容器内を０．５〜１．２ＭＰａに加圧することにより、前記木材を、前記不燃液組成物が浸透した不燃液含有木材にする加圧浸透工程と、
前記不燃液含有木材を５０〜８０℃で乾燥する乾燥工程と、
を備え、
前記不燃木材の体積あたりの付着固形分量が１００〜４００ｋｇ／ｍ３である不燃木材の製造方法。 A method for producing non-combustible wood using the non-combustible liquid composition according to any one of claims 1 to 5.
The process of loading wood into a pressure-resistant container and
A decompression step of reducing the pressure inside the pressure-resistant container to 0.09 MPa or less,
An injection step of injecting the incombustible liquid composition into the pressure-resistant container, and
A pressure permeation step of converting the wood into a non-combustible liquid-containing wood in which the non-combustible liquid composition has permeated by pressurizing the inside of the pressure-resistant container to 0.5 to 1.2 MPa.
A drying step of drying the non-combustible liquid-containing wood at 50 to 80 ° C.
With
A method for producing non-combustible wood, wherein the amount of adhering solids per volume of the non-combustible wood is 100 to 400 kg / m 3 .