JP5602997B2 - Glass fiber reinforced aromatic polycarbonate resin composition - Google Patents

Description

  The present invention relates to a glass fiber reinforced aromatic polycarbonate resin composition with improved dimensional accuracy. More specifically, the present invention relates to a glass fiber reinforced resin composition having both a flat cross-section glass fiber and good mechanical strength, low anisotropy, and flame retardancy reinforced with a fibrous filler other than the flat cross section glass fiber. .

  Thermoplastic resins reinforced with glass fibers are widely used because of their excellent mechanical strength and processability. In particular, polycarbonate resins are used in many applications such as mechanical parts, automobile parts, electrical / electronic parts, and office equipment parts because of their excellent properties such as mechanical strength, dimensional stability and flame retardancy. Reinforced polycarbonate resins obtained by adding various reinforcing agents to polycarbonate resins are also used in a wide range of applications due to their excellent mechanical strength and heat resistance. On the other hand, although the resin composition which mix | blended glass fiber with the polycarbonate resin is excellent in mechanical strength and rigidity, it has the fault that the anisotropy of the mold shrinkage ratio by fiber orientation will arise. In recent years, when used for molded parts such as precision machine parts such as camera parts and office equipment parts, a glass fiber reinforced thermoplastic resin having good mechanical strength, low anisotropy, and flame retardancy is required.

  For example, an aromatic polycarbonate resin composition with improved fluidity comprising an aromatic polycarbonate resin, a fiber filler, and an organic phosphate is known (see Patent Document 1). However, such a resin composition has a problem that the anisotropy of the molding shrinkage rate is large and the warp tends to be warped. A polycarbonate resin composition having an improved warping property composed of an aromatic polycarbonate resin, a specific non-circular fiber, and a plate-like filler is known (see Patent Document 2). However, such a resin composition has insufficient flame retardancy.

A resin composition comprising a polycarbonate resin, a styrene resin, and a glass fiber having a cross-sectional shape is known (see Patent Document 3). Moreover, the resin composition which consists of a polyamide resin and an eyebrows-shaped cross-section glass fiber is well-known (refer patent document 4).
However, this publication does not disclose knowledge that is effective in improving good mechanical strength, low anisotropy, and flame retardancy.

Japanese Patent Laid-Open No. 7-3140 JP-A-6-207089 JP-A-8-20694 JP 2003-82228 A

  In view of the above, an object of the present invention is to provide a flat cross-section glass fiber and an aromatic polycarbonate resin reinforced with a fibrous filler other than the flat cross-section glass fiber as a base, good mechanical strength, low anisotropy, and flame retardancy. It is in providing the reinforced resin composition which has these. The present inventor has intensively studied to achieve the above object, and as a result, has found that such an object can be achieved by using a glass fiber having a specific cross-sectional shape and a fibrous filler, and further eagerly studied. The present invention has been completed.

  According to the present invention, the above-mentioned problems are 40 to 99 parts by weight of a thermoplastic resin made of an aromatic polycarbonate resin (A-1 component), the average value of the major axis of the fiber cross section is 10 to 50 μm, and the ratio of the major axis to the minor axis ( It comprises a flat cross-section glass fiber (B-1 component) having an average value of the major axis / minor axis) of 1.5 to 8 (B-1 component) and a fibrous filler (B-2 component) excluding the B-1 component, and (B-1 Component) to (B-2 component) weight ratio (B-1 component / B-2 component) is 30/70 to 99/1 reinforcing filler (B component) 1 to 60 parts by weight, and A component This is achieved by a glass fiber reinforced resin composition comprising 0.001 to 20 parts by weight of a flame retardant (component C) with respect to 100 parts by weight of the total B component.

  Further, the above-mentioned problems are 40 to 99 parts by weight of a thermoplastic resin made of an aromatic polycarbonate resin (A-1 component) and the average value of the major axis of the fiber cross section is 10 to 50 μm, and the ratio of major axis to minor axis (major axis / minor axis). It consists of a flat cross-section glass fiber (B-1 component) having an average value of 1.5 to 8 and a fibrous filler (B-2 component) excluding the B-1 component, and (B-1 component) and (B -2 component) weight ratio (B-1 component / B-2 component) of 30/70 to 99/1, 1 to 60 parts by weight of reinforcing filler (B component), and a total of 100 of A component and B component This is solved by a resin molded product obtained by molding a glass fiber reinforced resin composition comprising 0.001 to 20 parts by weight of a flame retardant (component C) with respect to parts by weight.

Hereinafter, the details of the present invention will be described.
(Component A: thermoplastic resin)
(A-1 component: aromatic polycarbonate resin)
The aromatic polycarbonate resin used in the thermoplastic resin of component A in the present invention is obtained by reacting a dihydric phenol and a carbonate precursor. Examples of the reaction method include an interfacial polymerization method, a melt transesterification method, a solid phase transesterification method of a carbonate prepolymer, and a ring-opening polymerization method of a cyclic carbonate compound. The aromatic polycarbonate resin (component A-1) is preferably contained in an amount of 50% by weight or more in the thermoplastic resin (component A).

  Representative examples of the dihydric phenol used here include hydroquinone, resorcinol, 4,4′-biphenol, 1,1-bis (4-hydroxyphenyl) ethane, and 2,2-bis (4-hydroxyphenyl). ) Propane (commonly called bisphenol A), 2,2-bis (4-hydroxy-3-methylphenyl) propane, 2,2-bis (4-hydroxyphenyl) butane, 1,1-bis (4-hydroxyphenyl)- 1-phenylethane, 1,1-bis (4-hydroxyphenyl) cyclohexane, 1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane, 2,2-bis (4-hydroxyphenyl) Pentane, 4,4 ′-(p-phenylenediisopropylidene) diphenol, 4,4 ′-(m-phenylenediisopropyl Pyridene) diphenol, 1,1-bis (4-hydroxyphenyl) -4-isopropylcyclohexane, bis (4-hydroxyphenyl) oxide, bis (4-hydroxyphenyl) sulfide, bis (4-hydroxyphenyl) sulfoxide, bis (4-hydroxyphenyl) sulfone, bis (4-hydroxyphenyl) ketone, bis (4-hydroxyphenyl) ester, bis (4-hydroxy-3-methylphenyl) sulfide, 9,9-bis (4-hydroxyphenyl) Examples include fluorene and 9,9-bis (4-hydroxy-3-methylphenyl) fluorene. A preferred dihydric phenol is bis (4-hydroxyphenyl) alkane, and bisphenol A is particularly preferred from the viewpoint of impact resistance, and is widely used.

  In the present invention, in addition to the bisphenol A-based polycarbonate, which is a general-purpose polycarbonate, it is possible to use a special polycarbonate produced using other dihydric phenols as the A component.

  For example, as part or all of the dihydric phenol component, 4,4 ′-(m-phenylenediisopropylidene) diphenol (hereinafter sometimes abbreviated as “BPM”), 1,1-bis (4-hydroxy) Phenyl) cyclohexane, 1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane (hereinafter sometimes abbreviated as “Bis-TMC”), 9,9-bis (4-hydroxyphenyl) Polycarbonate (homopolymer or copolymer) using fluorene and 9,9-bis (4-hydroxy-3-methylphenyl) fluorene (hereinafter sometimes abbreviated as “BCF”) has dimensions due to water absorption. It is suitable for applications where the demands for change and shape stability are particularly severe. These dihydric phenols other than BPA are preferably used in an amount of 5 mol% or more, particularly 10 mol% or more of the entire dihydric phenol component constituting the polycarbonate.

In particular, when high rigidity and better hydrolysis resistance are required, it is particularly preferable that the component A constituting the resin composition is a copolymerized polycarbonate of the following (1) to (3). is there.
(1) BPM is 20 to 80 mol% (more preferably 40 to 75 mol%, more preferably 45 to 65 mol%) in 100 mol% of the dihydric phenol component constituting the polycarbonate, and BCF Of 20 to 80 mol% (more preferably 25 to 60 mol%, more preferably 35 to 55 mol%).
(2) BPA is 10 to 95 mol% (more preferably 50 to 90 mol%, more preferably 60 to 85 mol%) in 100 mol% of the dihydric phenol component constituting the polycarbonate, and BCF Is 5 to 90 mol% (more preferably 10 to 50 mol%, more preferably 15 to 40 mol%).
(3) BPM is 20 to 80 mol% (more preferably 40 to 75 mol%, more preferably 45 to 65 mol%) in 100 mol% of the dihydric phenol component constituting the polycarbonate, and Bis -Copolymer polycarbonate in which TMC is 20 to 80 mol% (more preferably 25 to 60 mol%, still more preferably 35 to 55 mol%).

  These special polycarbonates may be used alone or in combination of two or more. Moreover, these can also be mixed and used for the bisphenol A type polycarbonate generally used.

  The production method and characteristics of these special polycarbonates are described in detail in, for example, JP-A-6-172508, JP-A-8-27370, JP-A-2001-55435, and JP-A-2002-117580. ing.

Of the various polycarbonates described above, those having a water absorption and Tg (glass transition temperature) adjusted within the following ranges by adjusting the copolymer composition, etc. have good hydrolysis resistance of the polymer itself, and Since it is remarkably excellent in low warpage after molding, it is particularly suitable in a field where form stability is required.
(I) polycarbonate having a water absorption of 0.05 to 0.15%, preferably 0.06 to 0.13% and Tg of 120 to 180 ° C, or (ii) Tg of 160 to 250 ° C, Polycarbonate which is preferably 170 to 230 ° C. and has a water absorption of 0.10 to 0.30%, preferably 0.13 to 0.30%, more preferably 0.14 to 0.27%.

  Here, the water absorption of the polycarbonate is a value obtained by measuring the moisture content after being immersed in water at 23 ° C. for 24 hours in accordance with ISO 62-1980 using a disc-shaped test piece having a diameter of 45 mm and a thickness of 3.0 mm. is there. Moreover, Tg (glass transition temperature) is a value calculated | required by the differential scanning calorimeter (DSC) measurement based on JISK7121.

  As the carbonate precursor, carbonyl halide, carbonic acid diester, haloformate or the like is used, and specific examples include phosgene, diphenyl carbonate, dihaloformate of dihydric phenol, and the like.

  In producing the aromatic polycarbonate resin by the interfacial polymerization method using the dihydric phenol and the carbonate precursor, a catalyst, a terminal terminator, and an antioxidant for preventing the dihydric phenol from being oxidized as necessary. Etc. may be used. The aromatic polycarbonate resin of the present invention is a branched polycarbonate resin copolymerized with a trifunctional or higher polyfunctional aromatic compound, a polyester copolymerized with an aromatic or aliphatic (including alicyclic) difunctional carboxylic acid. Carbonate resin, copolymer polycarbonate resin copolymerized with bifunctional alcohol (including alicyclic), and polyester carbonate resin copolymerized with such bifunctional carboxylic acid and bifunctional alcohol are included. Moreover, the mixture which mixed 2 or more types of the obtained aromatic polycarbonate resin may be sufficient.

  The branched polycarbonate resin can impart anti-drip performance and the like to the reinforced aromatic polycarbonate resin composition of the present invention. Examples of the trifunctional or higher polyfunctional aromatic compound used in the branched polycarbonate resin include phloroglucin, phloroglucid, or 4,6-dimethyl-2,4,6-tris (4-hydroxydiphenyl) heptene-2, 2 , 4,6-trimethyl-2,4,6-tris (4-hydroxyphenyl) heptane, 1,3,5-tris (4-hydroxyphenyl) benzene, 1,1,1-tris (4-hydroxyphenyl) Ethane, 1,1,1-tris (3,5-dimethyl-4-hydroxyphenyl) ethane, 2,6-bis (2-hydroxy-5-methylbenzyl) -4-methylphenol, 4- {4- [ Trisphenol such as 1,1-bis (4-hydroxyphenyl) ethyl] benzene} -α, α-dimethylbenzylphenol, tetra (4-hydride) Loxyphenyl) methane, bis (2,4-dihydroxyphenyl) ketone, 1,4-bis (4,4-dihydroxytriphenylmethyl) benzene, or trimellitic acid, pyromellitic acid, benzophenonetetracarboxylic acid and their acids Among them, 1,1,1-tris (4-hydroxyphenyl) ethane and 1,1,1-tris (3,5-dimethyl-4-hydroxyphenyl) ethane are preferable. 1-Tris (4-hydroxyphenyl) ethane is preferred.

  The structural unit derived from the polyfunctional aromatic compound in the branched polycarbonate is 0.1% in a total of 100 mol% of the structural unit derived from the dihydric phenol and the structural unit derived from the polyfunctional aromatic compound. It is 01 to 1 mol%, preferably 0.05 to 0.9 mol%, particularly preferably 0.05 to 0.8 mol%.

In particular, in the case of the melt transesterification method, a branched structural unit may be generated as a side reaction. However, the amount of the branched structural unit is also 0.1% in a total of 100 mol% with a structural unit derived from a dihydric phenol. Those having a ratio of 001 to 1 mol%, preferably 0.005 to 0.9 mol%, particularly preferably 0.01 to 0.8 mol% are preferred. The ratio of the branched structure can be calculated by ¹ H-NMR measurement.

The aliphatic bifunctional carboxylic acid is preferably α, ω-dicarboxylic acid. Examples of aliphatic difunctional carboxylic acids include sebacic acid (decanedioic acid), dodecanedioic acid, tetradecanedioic acid, octadecanedioic acid, icosanedioic acid, and other straight-chain saturated aliphatic dicarboxylic acids, and cyclohexanedicarboxylic acid. Preferred are alicyclic dicarboxylic acids such as As the bifunctional alcohol, an alicyclic diol is more preferable, and examples thereof include cyclohexanedimethanol, cyclohexanediol, and tricyclodecane dimethanol.
Further, a polycarbonate-polyorganosiloxane copolymer obtained by copolymerizing polyorganosiloxane units can also be used.

  The reaction forms such as interfacial polymerization, melt transesterification, solid phase transesterification of carbonate prepolymer, and ring-opening polymerization of cyclic carbonate compounds, which are methods for producing the polycarbonate resin of the present invention, are various documents and patent publications. This is a well-known method.

  In producing the glass fiber reinforced resin composition of the present invention, the viscosity average molecular weight (M) of the aromatic polycarbonate resin is not particularly limited, but is preferably 10,000 to 50,000, more preferably 14,000. It is -30,000, More preferably, it is 14,000-24,000.

  With an aromatic polycarbonate resin having a viscosity average molecular weight of less than 10,000, good mechanical properties cannot be obtained. On the other hand, a resin composition obtained from an aromatic polycarbonate resin having a viscosity average molecular weight exceeding 50,000 is inferior in versatility in that it is inferior in fluidity during injection molding.

  The aromatic polycarbonate resin may be obtained by mixing those having a viscosity average molecular weight outside the above range. In particular, an aromatic polycarbonate resin having a viscosity average molecular weight exceeding the range (50,000) improves the entropy elasticity of the resin. As a result, good moldability is exhibited in gas assist molding and foam molding which may be used when molding a reinforced resin material into a structural member. Such improvement in moldability is even better than that of the branched polycarbonate. As a more preferred embodiment, the A component is an aromatic polycarbonate resin having a viscosity average molecular weight of 70,000 to 300,000 (component A-1-1), and an aromatic polycarbonate resin having a viscosity average molecular weight of 10,000 to 30,000. An aromatic polycarbonate resin (A-1 component) (hereinafter referred to as “high molecular weight component-containing aromatic polycarbonate resin”) having a viscosity average molecular weight of 16,000 to 35,000. May also be used.

  In such a high molecular weight component-containing aromatic polycarbonate resin (A-1 component), the molecular weight of the A-1-1 component is preferably 70,000 to 200,000, more preferably 80,000 to 200,000, still more preferably. 100,000 to 200,000, particularly preferably 100,000 to 160,000. The molecular weight of the A-1-2 component is preferably 10,000 to 25,000, more preferably 11,000 to 24,000, still more preferably 12,000 to 24,000, and particularly preferably 12,000 to 23. , 000.

  The high molecular weight component-containing aromatic polycarbonate resin (component A-1) is obtained by mixing the components A-1-1 and A-1-2 at various ratios and adjusting them so as to satisfy a predetermined molecular weight range. Can do. Preferably, in 100% by weight of the A-1 component, the A-1-1 component is 2 to 40% by weight, more preferably the A-1-1 component is 3 to 30% by weight, and still more preferably The A-1-1 component is 4 to 20% by weight, and particularly preferably the A-1-1 component is 5 to 20% by weight.

  As the preparation method of the component A-1, (1) a method in which the components A-1-1 and A-1-2 are independently polymerized and mixed, and (2) JP-A-5-306336. The method of producing an aromatic polycarbonate resin showing a plurality of polymer peaks in a molecular weight distribution chart by GPC method, represented by the method shown in Japanese Patent Publication No. Gazette, in the same system, the aromatic polycarbonate resin of the present invention A- A method of producing so as to satisfy the conditions of one component, and (3) an aromatic polycarbonate resin obtained by the production method (production method of (2)), a separately produced A-1-1 component and / or Examples thereof include a method of mixing the A-1-2 component.

The viscosity average molecular weight referred to in the present invention is first determined by using an Ostwald viscometer from a solution obtained by dissolving 0.7 g of aromatic polycarbonate in 100 ml of methylene chloride at 20 ° C. with a specific viscosity (η _SP ) calculated by the following formula. ,
Specific viscosity (η _SP ) = (t−t ₀ ) / t ₀
[T ₀ is methylene chloride falling seconds, t is sample solution falling seconds]
The viscosity average molecular weight M is calculated from the determined specific viscosity (η _SP ) by the following formula.
η _SP /c=[η]+0.45×[η] ² c (where [η] is the intrinsic viscosity)
[Η] = 1.23 × 10 ⁻⁴ M ^0.83
c = 0.7

  The calculation of the viscosity average molecular weight of the aromatic polycarbonate resin in the glass fiber reinforced resin composition of the present invention is performed as follows. That is, the composition is mixed with 20 to 30 times its weight of methylene chloride to dissolve the soluble component in the composition. Such soluble matter is collected by Celite filtration. Thereafter, the solvent in the obtained solution is removed. The solid after removal of the solvent is sufficiently dried to obtain a solid component that dissolves in methylene chloride. A specific viscosity at 20 ° C. is determined from a solution obtained by dissolving 0.7 g of the solid in 100 ml of methylene chloride in the same manner as described above, and the viscosity average molecular weight M is calculated from the specific viscosity in the same manner as described above.

(A-2 component: styrene resin)
The styrenic resin used in the thermoplastic resin of component A of the present invention has good molding processability, moderate heat resistance and flame retardancy, and is therefore preferable for maintaining a balance between these properties. Resin.

  Such a styrenic resin is a copolymer or copolymer of an aromatic vinyl compound, and, if necessary, at least one selected from other vinyl monomers and rubbery polymers copolymerizable therewith. It is a polymer obtained by polymerization.

  As the aromatic vinyl compound, styrene is particularly preferable. Preferable examples of the other vinyl monomer copolymerizable with the aromatic vinyl compound include a vinyl cyanide compound and a (meth) acrylic acid ester compound. A particularly preferred vinyl cyanide compound is acrylonitrile, and a particularly preferred (meth) acrylic acid ester compound is methyl methacrylate.

  Other vinyl monomers copolymerizable with aromatic vinyl compounds other than vinyl cyanide compounds and (meth) acrylic acid ester compounds include epoxy group-containing methacrylic acid esters such as glycidyl methacrylate, maleimide, N-methylmaleimide, Examples thereof include maleimide monomers such as N-phenylmaleimide, α, β-unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic acid, maleic anhydride, phthalic acid and itaconic acid, and anhydrides thereof.

  Examples of the rubbery polymer copolymerizable with the aromatic vinyl compound include polybutadiene, polyisoprene, and diene copolymers (eg, styrene / butadiene random copolymers and block copolymers, acrylonitrile / butadiene copolymers). , And (meth) acrylic acid alkyl ester and butadiene copolymers), ethylene and α-olefin copolymers (eg, ethylene / propylene random copolymers and block copolymers, ethylene / butene random copolymers). Polymers and block copolymers), copolymers of ethylene and unsaturated carboxylic acid esters (for example, ethylene / methacrylate copolymers and ethylene / butyl acrylate copolymers), copolymers of ethylene and aliphatic vinyl. Polymer (for example, ethylene / vinyl acetate copolymer) ), Ethylene, propylene and non-conjugated diene terpolymers (eg, ethylene / propylene / hexadiene copolymer), acrylic rubbers (eg, polybutyl acrylate, poly (2-ethylhexyl acrylate), and butyl acrylate 2 A copolymer with ethylhexyl acrylate, etc.), and a silicone rubber (for example, polyorganosiloxane rubber, IPN type rubber comprising a polyorganosiloxane rubber component and a polyalkyl (meth) acrylate rubber component; that is, two rubber components And rubbers having a structure in which they are entangled with each other so that they cannot be separated, and an IPN type rubber composed of a polyorganosiloxane rubber component and a polyisobutylene rubber component.

  Specific examples of the styrene resin include styrene resins such as polystyrene resin, HIPS resin, MS resin, ABS resin, AS resin, AES resin, ASA resin, MBS resin, MABS resin, MAS resin, and SMA resin. And (hydrogenated) styrene-butadiene-styrene copolymer resin, (hydrogenated) styrene-isoprene-styrene copolymer resin, and the like. In addition, the notation of (hydrogenated) means that both non-hydrogenated resin and hydrogenated resin are included. Here, the MS resin is a copolymer resin mainly composed of methyl methacrylate and styrene, the AES resin is a copolymer resin mainly composed of acrylonitrile, ethylene-propylene rubber, and styrene, and the ASA resin is mainly composed of acrylonitrile, styrene, and acrylic rubber. MABS resin is a copolymer resin mainly composed of methyl methacrylate, acrylonitrile, butadiene and styrene, MAS resin is a copolymer resin mainly composed of methyl methacrylate, acrylic rubber and styrene, and SMA resin is styrene and A copolymer resin mainly composed of maleic anhydride (MA) is shown.

  Such a styrenic resin may have a high stereoregularity such as syndiotactic polystyrene by using a catalyst such as a metallocene catalyst during the production thereof. Further, in some cases, polymers and copolymers having a narrow molecular weight distribution, block copolymers, and polymers and copolymers having high stereoregularity obtained by methods such as anion living polymerization and radical living polymerization are used. It is also possible.

  Among these, acrylonitrile / styrene copolymer resin (AS resin) and acrylonitrile / butadiene / styrene copolymer resin (ABS resin) are preferable. It is also possible to use a mixture of two or more styrenic polymers.

  The AS resin used in the present invention is a thermoplastic copolymer obtained by copolymerizing a vinyl cyanide compound and an aromatic vinyl compound. As such a vinyl cyanide compound, acrylonitrile can be particularly preferably used. As the aromatic vinyl compound, styrene and α-methylstyrene can be preferably used. The proportion of each component in the AS resin is 5 to 50% by weight, preferably 15 to 35% by weight of vinyl cyanide compound, 95 to 50% by weight of aromatic vinyl compound, when the total is 100% by weight. Preferably it is 85 to 65% by weight. Further, these vinyl compounds may be used in combination with other copolymerizable vinyl compounds described above, and the content ratio thereof is preferably 15% by weight or less in the AS resin component. Moreover, conventionally well-known various things can be used for the initiator, chain transfer agent, etc. which are used by reaction as needed.

Such an AS resin may be produced by any of bulk polymerization, suspension polymerization, and emulsion polymerization, but is preferably bulk polymerization. The copolymerization method may be either one-stage copolymerization or multistage copolymerization. The AS resin has a reduced viscosity of 0.2 to 1.0 dl / g, preferably 0.3 to 0.5 dl / g. The reduced viscosity is a value obtained by precisely weighing 0.25 g of AS resin and measuring a solution obtained by dissolving in 50 ml of dimethylformamide over 2 hours in an environment of 30 ° C. using an Ubbelohde viscometer. A viscometer having a solvent flow time of 20 to 100 seconds is used. The reduced viscosity is determined from the following formula from the solvent flow down seconds (t ₀ ) and the solution flow down seconds (t).
Reduced viscosity (η _sp / C) = {(t / t ₀ ) −1} /0.5
When the reduced viscosity is less than 0.2 dl / g, the impact is lowered, and when it exceeds 1.0 dl / g, the fluidity is deteriorated.

  The ABS resin used in the present invention is a mixture of a thermoplastic graft copolymer obtained by graft polymerization of a vinyl cyanide compound and an aromatic vinyl compound to a diene rubber component, and a copolymer of a vinyl cyanide compound and an aromatic vinyl compound. It is. As the diene rubber component forming the ABS resin, for example, rubber having a glass transition temperature of −30 ° C. or less such as polybutadiene, polyisoprene and styrene-butadiene copolymer is used, and the proportion thereof is 100% by weight of the ABS resin component. The content is preferably 5 to 80% by weight, more preferably 8 to 50% by weight, and particularly preferably 10 to 30% by weight. As the vinyl cyanide compound grafted on the diene rubber component, acrylonitrile is particularly preferably used. As the aromatic vinyl compound grafted on the diene rubber component, styrene and α-methylstyrene are particularly preferably used. The ratio of the component grafted to the diene rubber component is preferably 95 to 20% by weight, particularly preferably 90 to 50% by weight, based on 100% by weight of the ABS resin component. Furthermore, it is preferable that the vinyl cyanide compound is 5 to 50% by weight and the aromatic vinyl compound is 95 to 50% by weight with respect to 100% by weight of the total amount of the vinyl cyanide compound and the aromatic vinyl compound. Further, methyl (meth) acrylate, ethyl acrylate, maleic anhydride, N-substituted maleimide and the like can be mixed and used for a part of the components grafted to the diene rubber component, and the content ratio thereof is in the ABS resin component. What is 15 weight% or less is preferable. Furthermore, conventionally known various initiators, chain transfer agents, emulsifiers and the like can be used as necessary.

  In the ABS resin of the present invention, the rubber particle diameter is preferably 0.1 to 5.0 μm, more preferably 0.15 to 1.5 μm, and particularly preferably 0.2 to 0.8 μm. As the distribution of the rubber particle diameter, either a single distribution or a rubber particle having two or more peaks can be used, and the rubber particles form a single phase in the morphology. Alternatively, it may have a salami structure by containing an occluded phase around the rubber particles.

  In addition, it is well known that the ABS resin contains a vinyl cyanide compound and an aromatic vinyl compound that are not grafted to the diene rubber component, and the ABS resin of the present invention is free of the occurrence of such polymerization. The polymer component may be contained. The reduced viscosity of the copolymer comprising such free vinyl cyanide compound and aromatic vinyl compound is preferably 0.2 to 1.0 dl / g, more preferably reduced viscosity (30 ° C.) determined by the method described above. 0.3 to 0.7 dl / g.

  The ratio of the grafted vinyl cyanide compound and aromatic vinyl compound is preferably 20 to 200%, more preferably 20 to 70% in terms of graft ratio (% by weight) with respect to the diene rubber component. is there.

  Such an ABS resin may be produced by any of bulk polymerization, suspension polymerization, and emulsion polymerization, but is preferably bulk polymerization. Further, as such bulk polymerization method, typically, the continuous bulk polymerization method (so-called Toray method) described in Chemical Engineering, Vol. 48, No. 6, page 415 (1984), and Chemical Engineering, Vol. 53, No. 6, page 423 (1989). ) Is a continuous bulk polymerization method (so-called Mitsui Toatsu method). Any ABS resin is preferably used as the ABS resin of the present invention. Further, the copolymerization may be carried out in one step or in multiple steps. Moreover, what blended the vinyl compound polymer obtained by copolymerizing an aromatic vinyl compound and a vinyl cyanide component separately to the ABS resin obtained by this manufacturing method can also be used preferably.

  As the AS resin and the ABS resin, those having a reduced amount of alkali (earth) metal are more preferable from the viewpoint of good thermal stability and hydrolysis resistance. The amount of alkali (earth) metal in the styrenic resin is preferably less than 100 ppm, more preferably less than 80 ppm, still more preferably less than 50 ppm, and particularly preferably less than 10 ppm. Also from this point, AS resin and ABS resin by a bulk polymerization method are preferably used. Furthermore, in relation to such good thermal stability and hydrolysis resistance, when an emulsifier is used in the AS resin and ABS resin, the emulsifier is preferably a sulfonate salt, more preferably an alkyl sulfonic acid. It is salt. When a coagulant is used, the coagulant is preferably sulfuric acid or an alkaline earth metal salt of sulfuric acid.

  The blending amount of the styrenic resin is preferably 1 to 100 parts by weight, more preferably 5 to 80 parts by weight, and still more preferably 10 to 70 parts by weight per 100 parts by weight of the component A-1.

(B component: reinforcing filler)
(B-1 component: flat cross-section glass fiber)
The glass fiber used as B-1 component of this invention is a flat cross-section glass fiber. The flat cross-section glass fiber of the present invention has an average value of the major axis of the fiber cross section of 10 to 50 μm, preferably 15 to 40 μm, more preferably 20 to 35 μm, and an average value of the ratio of major axis to minor axis (major axis / minor axis). Is 1.5 to 8, preferably 2 to 6, more preferably 2.5 to 5. When using a flat cross-section glass fiber having an average ratio of the major axis to the minor axis within this range, the anisotropy and appearance are greatly improved compared to the case of using a non-circular cross-section fiber of less than 1.5. When used in combination with a flame retardant, flame retardancy can be greatly improved. This improvement in flame retardancy is achieved by aligning the long side surface of the flat cross-section glass fiber parallel to the surface of the molded product on the surface of the molded product. It is considered that the blocking effect works more effectively than the circular cross-section fiber. In addition to the flat shape, the flat cross-sectional shape includes an elliptical shape, an eyebrow shape, a trefoil shape, or a similar non-circular cross-sectional shape. Of these, a flat shape is preferable from the viewpoint of improving mechanical strength and low anisotropy. The ratio of the average fiber length to the average fiber diameter (aspect ratio) of the flat cross-section glass fiber is 2 to 120, preferably 2.5 to 70, more preferably 3 to 50, and the ratio of the fiber length to the average fiber diameter. If the ratio is less than 2, the effect of improving the mechanical strength is small, and if the ratio of the fiber length to the average fiber diameter exceeds 120, the anisotropy increases and the appearance of the molded product also deteriorates. The average fiber diameter of such flat cross-section glass fibers refers to the number average fiber diameter when the flat cross-sectional shape is converted to a true circle of the same area. The average fiber length refers to the number average fiber length in the glass fiber reinforced resin composition of the present invention. The number-average fiber length is a value calculated by an image analyzer from an image obtained by observing the residue of the filler collected by processing such as high-temperature ashing of a molded product, dissolution with a solvent, and decomposition with a chemical, using an optical microscope. It is. Further, when calculating such a value, the fiber diameter is used as a guide and the length is less than that.

Various glass compositions represented by A glass, C glass, E glass, etc. are applied to the glass composition of said flat cross-section glass fiber, and it is not specifically limited. Such a glass filler may contain components such as TiO ₂ , SO ₃ , and P ₂ O ₅ as necessary. Among these, E glass (non-alkali glass) is more preferable. Such flat cross-section glass fibers are preferably subjected to a surface treatment with a known surface treatment agent such as a silane coupling agent, a titanate coupling agent, or an aluminate coupling agent from the viewpoint of improving mechanical strength. In addition, those that have been subjected to bundling treatment with olefin resin, styrene resin, acrylic resin, polyester resin, epoxy resin, urethane resin, etc. are preferable. From the viewpoint of mechanical strength, epoxy resin and urethane resin are preferred. Particularly preferred. The amount of the sizing agent attached to the flat cross-section glass fiber subjected to the bundling treatment is preferably 0.1 to 3 wt%, more preferably 0.2 to 2 wt% in 100 wt% of the flat cross-section glass fiber.

(B-2 component: fibrous filler)
As a fibrous filler used as B-2 component in the composition of this invention, well-known fibrous fillers other than B-1 component can be mix | blended. As such a fibrous filler, glass fibers other than the B-1 component, wollastonite, and carbon-based filler are preferably exemplified. As such a fibrous filler, a filler whose surface is coated with a metal oxide such as titanium oxide, zinc oxide, cerium oxide, and silicon oxide can also be used. Examples of the carbon-based filler include carbon fiber, metal-coated carbon fiber, carbon milled fiber, vapor-grown carbon fiber, carbon nanotube, and carbon black. The carbon nanotube may be any one of a fiber diameter of 0.003 to 0.1 μm, a single layer, a double layer, and a multilayer, and a multilayer (so-called MWCNT) is preferable. Among these, carbon fiber and metal-coated carbon fiber are preferable in that they are excellent in mechanical strength and can impart good electrical conductivity.

  The fibrous filler may be surface-treated with various surface treatment agents in advance. Such surface treatment agents include silane coupling agents (including alkylalkoxysilanes and polyorganohydrogensiloxanes), higher fatty acid esters, acid compounds (for example, phosphorous acid, phosphoric acid, carboxylic acid, and carboxylic acid anhydrides). Etc.) and various surface treatment agents such as wax. Furthermore, it may be granulated with a sizing agent such as various resins, higher fatty acid esters, and waxes.

  The reinforcing filler (component B) of the present invention is 1 to 60% by weight in a total of 100% by weight of the thermoplastic resin (component A) and the reinforcing filler (component B) made of an aromatic polycarbonate resin, preferably It is 3 to 60% by weight, more preferably 5 to 50% by weight. If the component B is less than 1% by weight, the mechanical strength is insufficient, and if it exceeds 60% by weight, the molding fluidity and the appearance of the molded product are deteriorated.

  The weight ratio of the flat cross-section glass fiber (B-1 component), which is the reinforcing filler (B component) of the present invention, and the fibrous filler (B-2 component) excluding the B-1 component is 30/70 to 99/1. And preferably 40/60 to 99/1, more preferably 50/50 to 99/1. If the weight ratio of the flat cross-section glass fibers is 30% by weight or more, good bending elastic modulus and molding shrinkage anisotropy can be obtained.

(C component: flame retardant)
Various compounds known as flame retardants are blended in the glass fiber reinforced resin composition of the present invention. The compounding of the compound used as a flame retardant not only improves the flame retardancy but also provides, for example, an improvement in antistatic properties, fluidity, rigidity, and thermal stability based on the properties of each compound.

  Examples of such flame retardants include (1) organometallic salt flame retardants (for example, alkali (earth) organic sulfonate metal salts, borate metal salt flame retardants, stannate metal salt flame retardants, etc.), (2) Organophosphorous flame retardants (for example, monophosphate compounds, phosphate oligomer compounds, phosphonate oligomer compounds, phosphonitrile oligomer compounds, and phosphonic acid amide compounds), (3) silicone flame retardants comprising silicone compounds, and (4) halogens And flame retardant (for example, brominated epoxy resin, brominated polystyrene, brominated polycarbonate (including oligomers), brominated polyacrylate, chlorinated polyethylene, etc.).

(1) Organometallic salt-based flame retardant An organic metal salt-based flame retardant is advantageous in that heat resistance is substantially maintained and antistatic properties can be imparted. The organometallic salt flame retardant most advantageously used in the present invention is a fluorine-containing organometallic salt compound. The fluorine-containing organometallic salt compound of the present invention refers to a metal salt compound comprising an anion component composed of an organic acid having a fluorine-substituted hydrocarbon group and a cation component composed of a metal ion. More preferred specific examples include metal salts of fluorine-substituted organic sulfonic acids, metal salts of fluorine-substituted organic sulfates, and metal salts of fluorine-substituted organic phosphates. Fluorine-containing organometallic salt compounds can be used alone or in combination of two or more. Among them, a metal salt of a fluorine-substituted organic sulfonic acid is preferable, and a metal salt of a sulfonic acid having a perfluoroalkyl group is particularly preferable. Here, the carbon number of the perfluoroalkyl group is preferably in the range of 1-18, more preferably in the range of 1-10, and still more preferably in the range of 1-8.

  The metal constituting the metal ion of the organometallic salt flame retardant is an alkali metal or an alkaline earth metal. Examples of the alkali metal include lithium, sodium, potassium, rubidium and cesium. Examples of the alkaline earth metal include beryllium. , Magnesium, calcium, strontium and barium. More preferred is an alkali metal. Accordingly, a preferred organometallic salt flame retardant is an alkali metal perfluoroalkyl sulfonate. Among such alkali metals, rubidium and cesium are suitable when transparency requirements are higher, but these are not general-purpose and difficult to purify, resulting in disadvantages in terms of cost. is there. On the other hand, although lithium and sodium are advantageous in terms of cost and flame retardancy, they may be disadvantageous in terms of transparency. In consideration of these, the alkali metal in the perfluoroalkylsulfonic acid alkali metal salt can be properly used, but perfluoroalkylsulfonic acid potassium salt having an excellent balance of properties is most suitable in any respect. Such potassium salts and alkali metal salts of perfluoroalkylsulfonic acid composed of other alkali metals can be used in combination.

  Such alkali metal perfluoroalkylsulfonates include potassium trifluoromethanesulfonate, potassium perfluorobutanesulfonate, potassium perfluorohexanesulfonate, potassium perfluorooctanesulfonate, sodium pentafluoroethanesulfonate, perfluorobutanesulfone. Acid sodium, sodium perfluorooctane sulfonate, lithium trifluoromethane sulfonate, lithium perfluorobutane sulfonate, lithium perfluoroheptane sulfonate, cesium trifluoromethane sulfonate, cesium perfluorobutane sulfonate, cesium perfluorooctane sulfonate, Cesium perfluorohexane sulfonate, rubidium perfluorobutane sulfonate, and perful B hexane sulfonate rubidium, and these may be used in combination of at least one or two. Of these, potassium perfluorobutanesulfonate is particularly preferred.

  The fluorine-containing organometallic salt preferably has a fluoride ion content as measured by ion chromatography of 50 ppm or less, more preferably 20 ppm or less, and even more preferably 10 ppm or less. The lower the fluoride ion content, the better the flame retardancy and light resistance. The lower limit of the fluoride ion content can be substantially zero, but is practically preferably about 0.2 ppm in view of the balance between the refining man-hour and the effect. Such alkali metal salt of perfluoroalkylsulfonic acid having a fluoride ion content is purified, for example, as follows. The perfluoroalkylsulfonic acid alkali metal salt is dissolved in 2 to 10 times by weight of the metal salt in ion-exchanged water in the range of 40 to 90 ° C. (more preferably 60 to 85 ° C.). The alkali metal salt of perfluoroalkylsulfonic acid is a method of neutralizing perfluoroalkylsulfonic acid with an alkali metal carbonate or hydroxide, or perfluoroalkylsulfonyl fluoride with an alkali metal carbonate or hydroxide. It is produced by a neutralizing method (more preferably by the latter method). The ion-exchanged water is particularly preferably water having an electric resistance value of 18 MΩ · cm or more. The solution in which the metal salt is dissolved is stirred at the above temperature for 0.1 to 3 hours, more preferably 0.5 to 2.5 hours. Thereafter, the liquid is cooled to 0 to 40 ° C, more preferably in the range of 10 to 35 ° C. Crystals precipitate upon cooling. The precipitated crystals are removed by filtration. This produces a suitable purified perfluoroalkylsulfonic acid alkali metal salt.

  The blending amount of the fluorine-containing organometallic salt compound is preferably 0.005 to 0.6 parts by weight, more preferably 0.005 to 0.2 parts by weight, based on the total of 100 parts by weight of the component A and the component B. Preferably it is 0.008-0.13 weight part. The more preferable range is, the effects (for example, flame retardancy and antistatic properties) expected by the blending of the fluorine-containing organic metal salt are exhibited, and the adverse effect on the light resistance of the polycarbonate resin composition is reduced.

  In addition, as an organic metal salt flame retardant other than the above-mentioned fluorine-containing organic metal salt compound, a metal salt of an organic sulfonic acid not containing a fluorine atom is suitable. Examples of the metal salt include an alkali metal salt of an aliphatic sulfonic acid, an alkaline earth metal salt of an aliphatic sulfonic acid, an alkali metal salt of an aromatic sulfonic acid, and an alkaline earth metal salt of an aromatic sulfonic acid (any Also does not contain a fluorine atom).

  Preferable examples of the aliphatic sulfonic acid metal salt include an alkali (earth) metal salt of an alkyl sulfonate, and these can be used alone or in combination of two or more (here, alkali The (earth) metal salt is used to include both alkali metal salts and alkaline earth metal salts). Preferred examples of the alkane sulfonic acid used for the alkali (earth) metal salt of the alkyl sulfonate include methane sulfonic acid, ethane sulfonic acid, propane sulfonic acid, butane sulfonic acid, methyl butane sulfonic acid, hexane sulfonic acid, and heptane. Examples thereof include sulfonic acid and octanesulfonic acid, and these can be used alone or in combination of two or more.

  The aromatic sulfonic acid used in the aromatic (earth) metal salt of aromatic sulfonate includes monomeric or polymeric aromatic sulfide sulfonic acid, aromatic carboxylic acid and ester sulfonic acid, monomeric or polymeric sulfonic acid. Aromatic ether sulfonic acid, aromatic sulfonate sulfonic acid, monomeric or polymeric aromatic sulfonic acid, monomeric or polymeric aromatic sulfonic acid, aromatic ketone sulfonic acid, heterocyclic sulfonic acid, Examples include at least one acid selected from the group consisting of sulfonic acids of aromatic sulfoxides and condensates of methylene type bonds of aromatic sulfonic acids, and these are used alone or in combination of two or more. be able to.

  Specific examples of the aromatic (earth) metal salt of an aromatic sulfonate include, for example, disodium diphenyl sulfide-4,4′-disulfonate, dipotassium diphenyl sulfide-4,4′-disulfonate, potassium 5-sulfoisophthalate, Sodium 5-sulfoisophthalate, polysodium polyethylene terephthalate polysulfonate, calcium 1-methoxynaphthalene-4-sulfonate, disodium 4-dodecylphenyl ether disulfonate, polysodium poly (2,6-dimethylphenylene oxide) polysulfonate Poly (1,3-phenylene oxide) polysulfonic acid polysodium, poly (1,4-phenylene oxide) polysulfonic acid polysodium, poly (2,6-diphenylphenylene oxide) polysulfonic acid poly Lithium, poly (2-fluoro-6-butylphenylene oxide) polysulfonate, potassium sulfonate of benzenesulfonate, sodium benzenesulfonate, strontium benzenesulfonate, magnesium benzenesulfonate, dipotassium p-benzenedisulfonate, naphthalene-2 , 6-disulfonic acid dipotassium, biphenyl-3,3'-disulfonic acid calcium, diphenylsulfone-3-sulfonic acid sodium, diphenylsulfone-3-sulfonic acid potassium, diphenylsulfone-3,3'-disulfonic acid dipotassium, diphenylsulfone Α, α, α-trifluoroacetophenone sodium 4-sulfonate, dipotassium benzophenone-3,3′-disulfonate, Nene-2,5-disulfonate, dipotassium thiophene-2,5-disulfonate, calcium thiophene-2,5-disulfonate, sodium benzothiophenesulfonate, potassium diphenylsulfoxide-4-sulfonate, naphthalene Examples thereof include a formalin condensate of sodium sulfonate and a formalin condensate of sodium anthracene sulfonate.

  On the other hand, the alkali (earth) metal salt of sulfate ester may include, in particular, the alkali (earth) metal salt of sulfate ester of monovalent and / or polyhydric alcohols. Alcohol sulfates include methyl sulfate, ethyl sulfate, lauryl sulfate, hexadecyl sulfate, polyoxyethylene alkylphenyl ether sulfate, pentaerythritol mono, di, tri, tetrasulfate, and lauric acid monoglyceride. And sulfuric acid esters of palmitic acid monoglyceride and stearic acid monoglyceride sulfate. The alkali (earth) metal salts of these sulfates are preferably alkali (earth) metal salts of lauryl sulfate.

  Examples of other alkali (earth) metal salts include alkali (earth) metal salts of aromatic sulfonamides such as saccharin, N- (p-tolylsulfonyl) -p-toluenesulfonimide, N Examples include-(N'-benzylaminocarbonyl) sulfanilimide and alkali (earth) metal salts of N- (phenylcarboxyl) sulfanilimide.

  Among the above, preferable metal salts of organic sulfonic acids not containing fluorine atoms are aromatic (earth) metal salts of aromatic sulfonates, and potassium salts are particularly preferable. When blending such an alkali (earth) sulfonic acid metal salt, the content is 0.001 to 1 part by weight, more preferably 0.005 based on the total of 100 parts by weight of component A and component B. It is -0.5 weight part, More preferably, it is 0.01-0.1 weight part.

(2) Organophosphorous flame retardant As the organophosphorous flame retardant of the present invention, an aryl phosphate compound is suitable. This is because such a phosphate compound is generally excellent in hue and hardly adversely affects high light reflectivity. Moreover, since the phosphate compound has a plasticizing effect, it is advantageous in that the moldability of the resin composition of the present invention can be improved. As the phosphate compound, various phosphate compounds known as conventional flame retardants can be used, and more preferably, one or more phosphate compounds represented by the following general formula (1) can be mentioned.

（式（１）中のＸは、二価フェノールから誘導される二価の有機基を表し、Ｒ^１、Ｒ^２、Ｒ^３、およびＲ^４はそれぞれ一価フェノールから誘導される一価の有機基を表し、ｎは０〜５の整数を表す。）

(X in Formula (1) represents a divalent organic group derived from a dihydric phenol, and R ¹ , R ² , R ³ , and R ⁴ are each a monovalent organic group derived from a monohydric phenol. And n represents an integer of 0 to 5.)

  The phosphate compound of the above formula may be a mixture of compounds having different n numbers, in which case the average n number is preferably 0.5 to 1.5, more preferably 0.8 to 1. 2, More preferably, it is 0.95-1.15, Most preferably, it is the range of 1-1.14.

  Preferable specific examples of the dihydric phenol for deriving X include hydroquinone, resorcinol, bis (4-hydroxydiphenyl) methane, bisphenol A, dihydroxydiphenyl, dihydroxynaphthalene, bis (4-hydroxyphenyl) sulfone, bis (4 -Hydroxyphenyl) ketone and bis (4-hydroxyphenyl) sulfide are exemplified, among which resorcinol, bisphenol A, and dihydroxydiphenyl are preferable.

Preferable specific examples of the monohydric phenol for deriving R ¹ , R ² , R ³ , and R ⁴ include phenol, cresol, xylenol, isopropylphenol, butylphenol, and p-cumylphenol. Are phenol and 2,6-dimethylphenol.

  The monohydric phenol may be substituted with a halogen atom. Specific examples of the phosphate compound having a group derived from the monohydric phenol include tris (2,4,6-tribromophenyl) phosphate and tris. Examples include (2,4-dibromophenyl) phosphate, tris (4-bromophenyl) phosphate, and the like.

  On the other hand, specific examples of the phosphate compound not substituted with a halogen atom include monophosphate compounds such as triphenyl phosphate and tri (2,6-xylyl) phosphate, and resorcinol bisdi (2,6-xylyl) phosphate). Preferred are phosphate oligomers mainly composed of phosphate oligomers, phosphate oligomers mainly composed of 4,4-dihydroxydiphenyl bis (diphenyl phosphate), and phosphate oligomers mainly composed of bisphenol A bis (diphenyl phosphate). Indicates that a small amount of other components having different degrees of polymerization may be included, and more preferably, the component of n = 1 in the formula (1) is 80% by weight or more, more preferably 85% by weight or more, and still more preferably Contains over 90% by weight Are shown.).

  The compounding amount of the organic phosphorus flame retardant is preferably 1 to 20 parts by weight, more preferably 2 to 10 parts by weight, still more preferably 2 to 7 parts by weight based on 100 parts by weight of the total of the A component and the B component. Part.

(3) Silicone-based flame retardant The silicone compound used as the silicone-based flame retardant of the present invention improves flame retardancy by a chemical reaction during combustion. As the compound, various compounds conventionally proposed as flame retardants for aromatic polycarbonate resins can be used. The silicone compound binds itself during combustion or binds to a component derived from the resin to form a structure, or gives a flame retardant effect to the polycarbonate resin by a reduction reaction during the structure formation. It is considered. Therefore, it is preferable that a group having high activity in such a reaction is contained, and more specifically, a predetermined amount of at least one group selected from an alkoxy group and a hydrogen (ie, Si—H group) is contained. preferable. As a content rate of this group (alkoxy group, Si-H group), the range of 0.1-1.2 mol / 100g is preferable, the range of 0.12-1 mol / 100g is more preferable, 0.15-0. The range of 6 mol / 100 g is more preferable. Such a ratio can be determined by measuring the amount of hydrogen or alcohol generated per unit weight of the silicone compound by the alkali decomposition method. The alkoxy group is preferably an alkoxy group having 1 to 4 carbon atoms, and particularly preferably a methoxy group.

Generally, the structure of a silicone compound is constituted by arbitrarily combining the following four types of siloxane units. That is,
M units: (CH ₃ ) ₃ SiO _1/2 , H (CH ₃ ) ₂ SiO _1/2 , H ₂ (CH ₃ ) SiO _1/2 , (CH ₃ ) ₂ (CH ₂ = CH) SiO _1/2 Monofunctional siloxane units such as (CH ₃ ) ₂ (C ₆ H ₅ ) SiO _1/2 , (CH ₃ ) (C ₆ H ₅ ) (CH ₂ ═CH) SiO _1/2 ,
D unit: (CH ₃ ) ₂ SiO, H (CH ₃ ) SiO, H ₂ SiO, H (C ₆ H ₅ ) SiO, (CH ₃ ) (CH ₂ ═CH) SiO, (C ₆ H ₅ ) ₂ SiO Bifunctional siloxane units such as
T unit: (CH ₃ ) SiO _3/2 , (C ₃ H ₇ ) SiO _3/2 , HSiO _3/2 , (CH ₂ ═CH) SiO _3/2 , (C ₆ H ₅ ) SiO _3/2 etc. A trifunctional siloxane unit of
Q unit: a tetrafunctional siloxane unit represented by SiO ₂ .

Specifically, the structure of the silicone compound used in the silicone-based flame retardant is represented by the following formulas: D _n , T _p , M _m D _n , M _m T _p , M _m Q _q , M _m D _n T _{p , M m D n Q q,} M m T p Q q, M m D n T p Q q, D n T p, D n Q q, include _{D n} T p _{Q q.} Among these, preferable structures of the silicone compound are M _m D _n , M _m T _p , M _m D _n T _p , and M _m D _n Q _q , and more preferable structures are M _m D _n or M _m D _n. T _p .

  Here, the coefficients m, n, p, and q in the above formulas are integers of 1 or more representing the degree of polymerization of each siloxane unit, and the sum of the coefficients in each formula is the average degree of polymerization of the silicone compound. . This average degree of polymerization is preferably in the range of 3 to 150, more preferably in the range of 3 to 80, still more preferably in the range of 3 to 60, and particularly preferably in the range of 4 to 40. The better the range, the better the flame retardancy. Further, as described later, a silicone compound containing a predetermined amount of an aromatic group is excellent in transparency and hue.

  When any of m, n, p, and q is a numerical value of 2 or more, the siloxane unit with the coefficient can be two or more types of siloxane units having different hydrogen atoms or organic residues to be bonded. .

  The silicone compound may be linear or have a branched structure. The organic residue bonded to the silicon atom is preferably an organic residue having 1 to 30 carbon atoms, more preferably 1 to 20 carbon atoms. Specific examples of such an organic residue include alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a hexyl group, and a decyl group, a cycloalkyl group such as a cyclohexyl group, an aryl group such as a phenyl group, And aralkyl groups such as tolyl groups. More preferably, they are a C1-C8 alkyl group, an alkenyl group, or an aryl group. As the alkyl group, an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, and a propyl group is particularly preferable.

  Further, the silicone compound used as the silicone flame retardant preferably contains an aryl group. More preferably, the ratio (aromatic group amount) of the aromatic group represented by the following general formula (2) is 10 to 70% by weight (more preferably 15 to 60% by weight).

（式（２）中、Ｘはそれぞれ独立にＯＨ基、炭素数１〜２０の一価の有機残基を示す。ｎは０〜５の整数を表わす。さらに式（２）中においてｎが２以上の場合はそれぞれ互いに異なる種類のＸを取ることができる。）

(In formula (2), each X independently represents an OH group and a monovalent organic residue having 1 to 20 carbon atoms. N represents an integer of 0 to 5. Further, in formula (2), n is 2) In these cases, different types of X can be taken.)

  The silicone compound used as the silicone-based flame retardant may contain a reactive group in addition to the Si-H group and the alkoxy group. Examples of the reactive group include an amino group, a carboxyl group, an epoxy group, and a vinyl group. Examples thereof include a group, a mercapto group, and a methacryloxy group.

  As the silicone compound having a Si—H group, a silicone compound containing at least one of structural units represented by the following general formulas (3) and (4) is preferably exemplified.

（式（３）および式（４）中、Ｚ^１〜Ｚ^３はそれぞれ独立に水素原子、炭素数１〜２０の一価の有機残基、または下記一般式（５）で示される化合物を示す。α^１〜α^３はそれぞれ独立に０または１を表わす。ｍ１は０もしくは１以上の整数を表わす。さらに式（３）中においてｍ１が２以上の場合の繰返し単位はそれぞれ互いに異なる複数の繰返し単位を取ることができる。）

(In formula (3) and formula (4), Z ^{1 to} Z ³ each independently represent a hydrogen atom, a monovalent organic residue having 1 to 20 carbon atoms, or a compound represented by the following general formula (5). Α ^{1 to} α ³ each independently represents 0 or 1. m1 represents 0 or an integer of 1 or more, and in formula (3), when m1 is 2 or more, the repeating unit is a plurality of different repeating units. Can take units.)

（式（５）中、Ｚ^４〜Ｚ^８はそれぞれ独立に水素原子、炭素数１〜２０の一価の有機残基を示す。α^４〜α^８はそれぞれ独立に０または１を表わす。ｍ２は０もしくは１以上の整数を表わす。さらに式（５）中においてｍ２が２以上の場合の繰返し単位はそれぞれ互いに異なる複数の繰返し単位を取ることができる。）

(In formula (5), Z ^{4 to} Z ⁸ each independently represents a hydrogen atom or a monovalent organic residue having 1 to 20 carbon atoms. Α ^{4 to} α ⁸ each independently represents 0 or 1. m 2 Represents 0 or an integer greater than or equal to 1. Further, in the formula (5), when m2 is 2 or more, the repeating unit may take a plurality of different repeating units.

  In the silicone compound used for the silicone-based flame retardant, examples of the silicone compound having an alkoxy group include at least one compound selected from compounds represented by the general formula (6) and the general formula (7).

（式（６）中、β^１はビニル基、炭素数１〜６のアルキル基、炭素数３〜６のシクロアルキル基、並びに炭素数６〜１２のアリール基およびアラルキル基を示す。γ^１、γ^２、γ^３、γ^４、γ^５、およびγ^６は炭素数１〜６のアルキル基およびシクロアルキル基、並びに炭素数６〜１２のアリール基およびアラルキル基を示し、少なくとも１つの基がアリール基またはアラルキル基である。δ^１、δ^２、およびδ^３は炭素数１〜４のアルコキシ基を示す。）

(In Formula (6), β ¹ represents a vinyl group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms, and an aryl group and an aralkyl group having 6 to 12 carbon atoms. Γ ¹ , γ ² , γ ³ , γ ⁴ , γ ⁵ , and γ ⁶ represent an alkyl group and a cycloalkyl group having 1 to ⁶ carbon atoms, and an aryl group and an aralkyl group having 6 to 12 carbon atoms, and at least one group is aryl. And δ ¹ , δ ² , and δ ³ are each an alkoxy group having 1 to 4 carbon atoms.)

（式（７）中、β^２およびβ^３はビニル基、炭素数１〜６のアルキル基、炭素数３〜６のシクロアルキル基、並びに炭素数６〜１２のアリール基およびアラルキル基を示す。γ^７、γ^８、γ^９、γ^１０、γ^１１、γ^１２、γ^１３およびγ^１４は炭素数１〜６のアルキル基、、炭素数３〜６のシクロアルキル基、並びに炭素数６〜１２のアリール基およびアラルキル基を示し、少なくとも１つの基がアリール基またはアラルキルである。δ^４、δ^５、δ^６、およびδ^７は炭素数１〜４のアルコキシ基を示す。）

(In formula (7), β ² and β ³ represent a vinyl group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms, and an aryl group and an aralkyl group having 6 to 12 carbon atoms. γ ⁷ , γ ⁸ , γ ⁹ , γ ¹⁰ , γ ¹¹ , γ ¹² , γ ^13, and γ ¹⁴ are each an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms, and 6 to 12 carbon atoms. And at least one group is an aryl group or an aralkyl group, and δ ⁴ , δ ⁵ , δ ⁶ , and δ ⁷ represent an alkoxy group having 1 to 4 carbon atoms.)

(4) Halogen flame retardant As the halogen flame retardant of the present invention, brominated polycarbonate (including oligomers) is particularly suitable. Brominated polycarbonate has excellent heat resistance and can greatly improve flame retardancy. In the brominated polycarbonate used in the present invention, the structural unit represented by the following general formula (8) is at least 60 mol%, preferably at least 80 mol%, particularly preferably substantially the following general formula. It is a brominated polycarbonate compound consisting of the structural unit represented by (8).

（式（８）中、Ｘは臭素原子、Ｒは炭素数１〜４のアルキレン基、炭素数１〜４のアルキリデン基または−ＳＯ_２−である。）

(In the formula (8), X is a bromine atom, R represents an alkylene group having 1 to 4 carbon atoms, an alkylidene group or -SO ₂ 1 to 4 carbon atoms - a.)

In the formula (8), R preferably represents a methylene group, an ethylene group, an isopropylidene group, —SO ₂ —, and particularly preferably an isopropylidene group.

  The brominated polycarbonate has a small number of remaining chloroformate groups and preferably has a terminal chlorine content of 0.3 ppm or less, more preferably 0.2 ppm or less. The amount of terminal chlorine is determined by dissolving a sample in methylene chloride, adding 4- (p-nitrobenzyl) pyridine and allowing it to react with terminal chlorine (terminal chloroformate). -3200). When the amount of terminal chlorine is 0.3 ppm or less, the thermal stability of the polycarbonate resin composition becomes better, and molding at a higher temperature becomes possible. As a result, a polycarbonate resin composition that is superior in molding processability is provided.

The brominated polycarbonate preferably has a small number of remaining hydroxyl terminals. More specifically, the amount of terminal hydroxyl groups is preferably 0.0005 mol or less, more preferably 0.0003 mol or less with respect to 1 mol of the structural unit of brominated polycarbonate. The amount of terminal hydroxyl groups can be determined by dissolving a sample in deuterated chloroform and measuring it by ¹ H-NMR method. Such a terminal hydroxyl group amount is preferable because the thermal stability of the polycarbonate resin composition is further improved.

  The specific viscosity of the brominated polycarbonate is preferably in the range of 0.015 to 0.1, more preferably in the range of 0.015 to 0.08. The specific viscosity of the brominated polycarbonate is calculated according to the above-described specific viscosity calculation formula used for calculating the viscosity average molecular weight of the polycarbonate resin which is the component A of the present invention.

(D component: fluorine-containing anti-drip agent)
The glass fiber reinforced resin composition of the present invention may contain a fluorine-containing dripping inhibitor. By using such a fluorine-containing anti-drip agent in combination with the above flame retardant, better flame retardancy can be obtained. Examples of such a fluorine-containing anti-drip agent include a fluorine-containing polymer having a fibril-forming ability. Examples of such a polymer include polytetrafluoroethylene and tetrafluoroethylene copolymers (for example, tetrafluoroethylene / hexafluoropropylene copolymer). Polymer, etc.), partially fluorinated polymers as shown in US Pat. No. 4,379,910, polycarbonate resins produced from fluorinated diphenols, and the like, preferably polytetrafluoroethylene (hereinafter referred to as PTFE). May be called).

Polytetrafluoroethylene (fibrillated PTFE) having fibril-forming ability has a very high molecular weight, and exhibits a tendency to bind PTFE to each other by an external action such as shearing force to form a fiber. Its number average molecular weight ranges from 1.5 million to tens of millions. The lower limit is more preferably 3 million. The number average molecular weight is calculated based on the melt viscosity of polytetrafluoroethylene at 380 ° C. as disclosed in JP-A-6-145520. That is, the fibrillated PTFE has a melt viscosity at 380 ° C. measured by the method described in this publication in the range of 10 ⁷ to 10 ¹³ poise, preferably in the range of 10 ⁸ to 10 ¹² poise.

  Such PTFE can be used in solid form or in the form of an aqueous dispersion. In addition, PTFE having such fibril-forming ability can improve the dispersibility in the resin, and it is also possible to use a PTFE mixture in a mixed form with other resins in order to obtain better flame retardancy and mechanical properties. is there. Further, as disclosed in JP-A-6-145520, those having a structure having such a fibrillated PTFE as a core and a low molecular weight polytetrafluoroethylene as a shell are also preferably used.

  Examples of commercially available fibrillated PTFE include Teflon (registered trademark) 6J from Mitsui DuPont Fluorochemical Co., Ltd., Polyflon MPA FA500, F-201L from Daikin Chemical Industries, Ltd., and the like. Commercially available aqueous dispersions of fibrillated PTFE include: Fluon AD-1, AD-936 manufactured by Asahi IC Fluoropolymers, Fluon D-1, D-2 manufactured by Daikin Industries, Ltd., Mitsui A representative example is Teflon (registered trademark) 30J manufactured by DuPont Fluorochemical Co., Ltd.

  As a mixed form of fibrillated PTFE, (1) a method in which an aqueous dispersion of fibrillated PTFE and an aqueous dispersion or solution of an organic polymer are mixed and co-precipitated to obtain a co-agglomerated mixture (JP-A-60-258263). (2) A method of mixing an aqueous dispersion of fibrillated PTFE and dried organic polymer particles (Japanese Patent Laid-Open No. 4-272957). Described method), (3) A method in which an aqueous dispersion of fibrillated PTFE and an organic polymer particle solution are uniformly mixed, and the respective media are simultaneously removed from the mixture (Japanese Patent Laid-Open Nos. 06-220210, (Method described in Japanese Patent Application Laid-Open No. 08-188653), (4) A method of polymerizing monomers forming an organic polymer in an aqueous dispersion of fibrillated PTFE (Method described in JP-A-9-95583), and (5) an aqueous dispersion of PTFE and an organic polymer dispersion are uniformly mixed, and then a vinyl monomer is further polymerized in the mixed dispersion. Thereafter, those obtained by a method for obtaining a mixture (a method described in JP-A No. 11-29679) can be used. Commercial products of these mixed forms of fibrillated PTFE include “Metablene A3800” (trade name) manufactured by Mitsubishi Rayon Co., Ltd., “BLENDEX B449” (trade name) manufactured by GE Specialty Chemicals, and “Products manufactured by Pacific Interchem Corporation” “POLY TS AD001” (product name) is exemplified.

  In order to more effectively utilize the good mechanical strength of the glass fiber reinforced flame retardant resin composition of the present invention, the fibrillated PTFE is preferably finely dispersed as much as possible. As a means of achieving such fine dispersion, the above mixed form of fibrillated PTFE is advantageous. A method of directly supplying an aqueous dispersion in a melt kneader is also advantageous for fine dispersion. However, in the case of the aqueous dispersion form, consideration is required in that the hue is slightly deteriorated. The proportion of fibrillated PTFE in the mixed form is preferably 10 to 80% by weight, more preferably 15 to 75% by weight, in 100% by weight of the mixture. When the ratio of fibrillated PTFE is in such a range, good dispersibility of fibrillated PTFE can be achieved.

  The content of the D component of the present invention is preferably 0.01 to 3 parts by weight, more preferably 0.01 to 2 parts by weight, and still more preferably 0.00, based on a total of 100 parts by weight of the A and B components. 05 to 1.5 parts by weight. When the D component exceeds 3 parts by weight, the appearance of the molded product deteriorates, and when it is less than 0.01 parts by weight, an effective drip prevention effect cannot be obtained. The content of fibrillated PTFE as component D is preferably 0.01 to 1 part by weight, more preferably 0.1 to 0.7 part by weight based on 100 parts by weight of the total of component A and component B. is there.

(Other additives)
In the glass fiber reinforced resin composition of the present invention, various stabilizers, mold release agents, coloring materials, flame retardants, and the like for stabilizing the molecular weight reduction and hue at the time of molding can be used.

(I) Stabilizer Various known stabilizers can be blended in the glass fiber reinforced resin composition of the present invention. Examples of the stabilizer include phosphorus stabilizers, hindered phenol antioxidants, ultraviolet absorbers, and light stabilizers.

(I-1) Phosphorus stabilizer Examples of the phosphorous stabilizer include phosphorous acid, phosphoric acid, phosphonous acid, phosphonic acid and esters thereof, and tertiary phosphine. Among these, phosphorous acid, phosphoric acid, phosphonous acid, and phosphonic acid, triorganophosphate compounds, and acid phosphate compounds are particularly preferable. The organic group in the acid phosphate compound includes any of mono-substituted, di-substituted, and mixtures thereof. Any of the following exemplified compounds corresponding to the compound is similarly included.

  Triorganophosphate compounds include trimethyl phosphate, triethyl phosphate, tributyl phosphate, trioctyl phosphate, tridecyl phosphate, tridodecyl phosphate, trilauryl phosphate, tristearyl phosphate, tricresyl phosphate, triphenyl phosphate, trichlorophenyl phosphate, diphenyl Examples include cresyl phosphate, diphenyl monoorthoxenyl phosphate, and tributoxyethyl phosphate. Among these, trialkyl phosphate is preferable. The carbon number of the trialkyl phosphate is preferably 1 to 22, more preferably 1 to 4. A particularly preferred trialkyl phosphate is trimethyl phosphate.

  Examples of the acid phosphate compound include methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, butoxyethyl acid phosphate, octyl acid phosphate, decyl acid phosphate, lauryl acid phosphate, stearyl acid phosphate, oleyl acid phosphate, behenyl acid phosphate, behenyl acid phosphate Nonylphenyl acid phosphate, cyclohexyl acid phosphate, phenoxyethyl acid phosphate, alkoxy polyethylene glycol acid phosphate, bisphenol A acid phosphate, and the like. Among these, long-chain dialkyl acid phosphates having 10 or more carbon atoms are effective for improving thermal stability, and the acid phosphate itself is preferable because of high stability.

  Examples of the phosphite compound include triphenyl phosphite, tris (nonylphenyl) phosphite, tridecyl phosphite, trioctyl phosphite, trioctadecyl phosphite, didecyl monophenyl phosphite, dioctyl monophenyl phosphite, diisopropyl Monophenyl phosphite, monobutyl diphenyl phosphite, monodecyl diphenyl phosphite, monooctyl diphenyl phosphite, tris (diethylphenyl) phosphite, tris (di-iso-propylphenyl) phosphite, tris (di-n-butyl) Phenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphite, tris (2,6-di-tert-butylphenyl) phosphite, distearyl Taerythritol diphosphite, bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis (2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite, bis ( 2,6-di-tert-butyl-4-ethylphenyl) pentaerythritol diphosphite, bis {2,4-bis (1-methyl-1-phenylethyl) phenyl} pentaerythritol diphosphite, phenylbisphenol A penta Examples include erythritol diphosphite, bis (nonylphenyl) pentaerythritol diphosphite, and dicyclohexylpentaerythritol diphosphite.

  Further, as other phosphite compounds, those which react with dihydric phenols and have a cyclic structure can be used. For example, 2,2′-methylenebis (4,6-di-tert-butylphenyl) (2,4-di-tert-butylphenyl) phosphite, 2,2′-methylenebis (4,6-di-tert- Examples include butylphenyl) (2-tert-butyl-4-methylphenyl) phosphite and 2,2-methylenebis (4,6-di-tert-butylphenyl) octyl phosphite.

  Examples of the phosphonite compound include tetrakis (2,4-di-tert-butylphenyl) -4,4′-biphenylenediphosphonite, tetrakis (2,4-di-tert-butylphenyl) -4,3′-biphenylenedi. Phosphonite, tetrakis (2,4-di-tert-butylphenyl) -3,3′-biphenylenediphosphonite, tetrakis (2,6-di-tert-butylphenyl) -4,4′-biphenylenediphosphonite Tetrakis (2,6-di-tert-butylphenyl) -4,3′-biphenylene diphosphonite, tetrakis (2,6-di-tert-butylphenyl) -3,3′-biphenylene diphosphonite, bis (2,4-di-tert-butylphenyl) -4-phenyl-phenylphosphonite, bis (2,4-di tert-butylphenyl) -3-phenyl-phenylphosphonite, bis (2,6-di-n-butylphenyl) -3-phenyl-phenylphosphonite, bis (2,6-di-tert-butylphenyl)- 4-phenyl-phenylphosphonite, bis (2,6-di-tert-butylphenyl) -3-phenyl-phenylphosphonite, and the like, and tetrakis (di-tert-butylphenyl) -biphenylenediphosphonite, bis (Di-tert-butylphenyl) -phenyl-phenylphosphonite is preferred, tetrakis (2,4-di-tert-butylphenyl) -biphenylenediphosphonite, bis (2,4-di-tert-butylphenyl)- More preferred is phenyl-phenylphosphonite. Such a phosphonite compound is preferable because it can be used in combination with a phosphite compound having an aryl group in which two or more alkyl groups are substituted.

  Examples of the phosphonate compound include dimethyl benzenephosphonate, diethyl benzenephosphonate, and dipropyl benzenephosphonate.

  The tertiary phosphine includes triethylphosphine, tripropylphosphine, tributylphosphine, trioctylphosphine, triamylphosphine, dimethylphenylphosphine, dibutylphenylphosphine, diphenylmethylphosphine, diphenyloctylphosphine, triphenylphosphine, tri-p-tolyl. Examples include phosphine, trinaphthylphosphine, and diphenylbenzylphosphine. A particularly preferred tertiary phosphine is triphenylphosphine.

  Suitable phosphorus stabilizers are a triorganophosphate compound, an acid phosphate compound, and a phosphite compound represented by the following general formula (9). It is particularly preferable to add a triorganophosphate compound.

（式（９）中、ＲおよびＲ’は炭素数６〜３０のアルキル基または炭素数６〜３０のアリール基を表し、互いに同一であっても異なっていてもよい。）

(In Formula (9), R and R ′ represent an alkyl group having 6 to 30 carbon atoms or an aryl group having 6 to 30 carbon atoms, and may be the same or different from each other.)

  As described above, tetrakis (2,4-di-tert-butylphenyl) -biphenylenediphosphonite is preferable as the phosphonite compound, and the stabilizer containing phosphonite as a main component is Sandostab P-EPQ (trademark, manufactured by Clariant). ) And Irgafos P-EPQ (trademark, manufactured by CIBA SPECIALTY CHEMICALS) and both can be used.

  Among the above formulas (1), more preferred phosphite compounds are distearyl pentaerythritol diphosphite, bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis (2,6-di). -Tert-butyl-4-methylphenyl) pentaerythritol diphosphite, and bis {2,4-bis (1-methyl-1-phenylethyl) phenyl} pentaerythritol diphosphite.

(I-2) Hindered phenolic antioxidant As the hindered phenolic compound, various compounds that are usually blended in resins can be used. Examples of such hindered phenol compounds include α-tocopherol, butylhydroxytoluene, sinapyl alcohol, vitamin E, octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate, 2-tert -Butyl-6- (3'-tert-butyl-5'-methyl-2'-hydroxybenzyl) -4-methylphenyl acrylate, 2,6-di-tert-butyl-4- (N, N-dimethylamino) Methyl) phenol, 3,5-di-tert-butyl-4-hydroxybenzylphosphonate diethyl ester, 2,2'-methylenebis (4-methyl-6-tert-butylphenol), 2,2'-methylenebis (4-ethyl) -6-tert-butylphenol), 4,4'-methylenebis (2,6 Di-tert-butylphenol), 2,2′-methylenebis (4-methyl-6-cyclohexylphenol), 2,2′-dimethylene-bis (6-α-methyl-benzyl-p-cresol), 2,2 ′ -Ethylidene-bis (4,6-di-tert-butylphenol), 2,2'-butylidene-bis (4-methyl-6-tert-butylphenol), 4,4'-butylidenebis (3-methyl-6-tert) -Butylphenol), triethylene glycol-N-bis-3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionate, 1,6-hexanediol bis [3- (3,5-di- tert-butyl-4-hydroxyphenyl) propionate], bis [2-tert-butyl-4-methyl 6- (3-tert-butyl) Ru-5-methyl-2-hydroxybenzyl) phenyl] terephthalate, 3,9-bis {2- [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionyloxy] -1,1, -Dimethylethyl} -2,4,8,10-tetraoxaspiro [5,5] undecane, 4,4'-thiobis (6-tert-butyl-m-cresol), 4,4'-thiobis (3- Methyl-6-tert-butylphenol), 2,2′-thiobis (4-methyl-6-tert-butylphenol), bis (3,5-di-tert-butyl-4-hydroxybenzyl) sulfide, 4,4 ′ -Di-thiobis (2,6-di-tert-butylphenol), 4,4'-tri-thiobis (2,6-di-tert-butylphenol), 2,2-thiodie Renbis- [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], 2,4-bis (n-octylthio) -6- (4-hydroxy-3,5-di-tert- Butylanilino) -1,3,5-triazine, N, N′-hexamethylenebis- (3,5-di-tert-butyl-4-hydroxyhydrocinnamide), N, N′-bis [3- (3 , 5-Di-tert-butyl-4-hydroxyphenyl) propionyl] hydrazine, 1,1,3-tris (2-methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,3,5-trimethyl -2,4,6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene, tris (3,5-di-tert-butyl-4-hydroxyphenyl) iso Cyanurate, tris (3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris (4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanurate, 1,3,5-tris2 [3 (3,5-di-tert-butyl-4-hydroxyphenyl) propionyloxy] ethyl isocyanurate, tetrakis [methylene-3- (3,5-di-tert-butyl- 4-hydroxyphenyl) propionate] methane, triethylene glycol-N-bis-3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionate, triethylene glycol-N-bis-3- (3- tert-butyl-4-hydroxy-5-methylphenyl) acetate, 3,9-bis [2 {3- (3-tert-butyl-4-hydroxy-5-methylphenyl) acetyloxy} -1,1-dimethylethyl] -2,4,8,10-tetraoxaspiro [5,5] undecane, tetrakis [Methylene-3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionate] methane, 1,3,5-trimethyl-2,4,6-tris (3-tert-butyl-4-hydroxy Examples include -5-methylbenzyl) benzene and tris (3-tert-butyl-4-hydroxy-5-methylbenzyl) isocyanurate.

  Among the above compounds, tetrakis [methylene-3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionate] methane, octadecyl-3- (3,5-di-tert-butyl-) is used in the present invention. 4-hydroxyphenyl) propionate, and 3,9-bis [2- {3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionyloxy} -1,1-dimethylethyl] -2,4 , 8,10-Tetraoxaspiro [5,5] undecane is preferably used. In particular, 3,9-bis [2- {3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionyloxy} -1,1-dimethylethyl] -2,4,8,10-tetraoxa Spiro [5,5] undecane is preferred. The said hindered phenolic antioxidant can be used individually or in combination of 2 or more types.

  It is preferable that either a phosphorus stabilizer or a hindered phenol antioxidant is blended. In particular, a phosphorus stabilizer is preferably blended, and a triorganophosphate compound is more blended. The compounding amount of the phosphorus stabilizer and the hindered phenol antioxidant is 0.005 to 1 part by weight, preferably 0.01 to 0.3 part by weight, based on the total of 100 parts by weight of component A and component B, respectively. Part.

(I-3) Ultraviolet Absorber The glass fiber reinforced resin composition of the present invention can contain an ultraviolet absorber. Since the resin composition of the present invention also has a good hue, such a hue can be maintained for a long time even when used outdoors by blending an ultraviolet absorber.

  Specific examples of the ultraviolet absorber of the present invention include, for example, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-octoxybenzophenone, 2-hydroxy-4 in the benzophenone series. -Benzyloxybenzophenone, 2-hydroxy-4-methoxy-5-sulfoxybenzophenone, 2-hydroxy-4-methoxy-5-sulfoxytrihydridolate benzophenone, 2,2'-dihydroxy-4-methoxybenzophenone, 2, 2 ′, 4,4′-tetrahydroxybenzophenone, 2,2′-dihydroxy-4,4′-dimethoxybenzophenone, 2,2′-dihydroxy-4,4′-dimethoxy-5-sodiumsulfoxybenzophenone, bis (5-benzoyl-4-hydro Shi-2-methoxyphenyl) methane, 2-hydroxy -4-n-dodecyloxy benzoin phenone, and 2-hydroxy-4-methoxy-2'-carboxy benzophenone may be exemplified.

  Specific examples of the ultraviolet absorber include, for example, 2- (2-hydroxy-5-methylphenyl) benzotriazole and 2- (2-hydroxy-5-tert-octylphenyl) benzotriazole in the benzotriazole series. 2- (2-hydroxy-3,5-dicumylphenyl) phenylbenzotriazole, 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole, 2,2′- Methylenebis [4- (1,1,3,3-tetramethylbutyl) -6- (2H-benzotriazol-2-yl) phenol], 2- (2-hydroxy-3,5-di-tert-butylphenyl) ) Benzotriazole, 2- (2-hydroxy-3,5-di-tert-butylphenyl) -5-chlorobenzotriazol 2- (2-hydroxy-3,5-di-tert-amylphenyl) benzotriazole, 2- (2-hydroxy-5-tert-octylphenyl) benzotriazole, 2- (2-hydroxy-5- tert-butylphenyl) benzotriazole, 2- (2-hydroxy-4-octoxyphenyl) benzotriazole, 2,2'-methylenebis (4-cumyl-6-benzotriazolephenyl), 2,2'-p -Phenylenebis (1,3-benzoxazin-4-one), and 2- [2-hydroxy-3- (3,4,5,6-tetrahydrophthalimidomethyl) -5-methylphenyl] benzotriazole, and 2- (2'-Hydroxy-5-methacryloxyethylphenyl) -2H-benzotriazole and co-polymerized with the monomer 2 such as a copolymer with a possible vinyl monomer and a copolymer of 2- (2′-hydroxy-5-acryloxyethylphenyl) -2H-benzotriazole with a vinyl monomer copolymerizable with the monomer Examples include polymers having a -hydroxyphenyl-2H-benzotriazole skeleton.

  Specific examples of the ultraviolet absorber include 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-hexyloxyphenol and 2- (4) in hydroxyphenyltriazine series. , 6-Diphenyl-1,3,5-triazin-2-yl) -5-methyloxyphenol, 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-ethyloxy Phenol, 2- (4,6-diphenyl-1,3,5-triazin-2-yl) -5-propyloxyphenol, and 2- (4,6-diphenyl-1,3,5-triazine-2- Yl) -5-butyloxyphenol and the like. Furthermore, the phenyl group of the above exemplary compounds such as 2- (4,6-bis (2,4-dimethylphenyl) -1,3,5-triazin-2-yl) -5-hexyloxyphenol is 2,4-dimethyl. Examples of the compound are phenyl groups.

  As the ultraviolet absorber, specifically, in the cyclic imino ester type, for example, 2,2′-p-phenylenebis (3,1-benzoxazin-4-one), 2,2 ′-(4,4′-diphenylene) ) Bis (3,1-benzoxazin-4-one), 2,2 ′-(2,6-naphthalene) bis (3,1-benzoxazin-4-one) and the like.

  Further, as the ultraviolet absorber, specifically, for cyanoacrylate, for example, 1,3-bis-[(2′-cyano-3 ′, 3′-diphenylacryloyl) oxy] -2,2-bis [(2- Examples include cyano-3,3-diphenylacryloyl) oxy] methyl) propane and 1,3-bis-[(2-cyano-3,3-diphenylacryloyl) oxy] benzene.

  Further, the ultraviolet absorber has a structure of a monomer compound capable of radical polymerization, whereby the ultraviolet-absorbing monomer and / or the light-stable monomer having a hindered amine structure, and an alkyl (meth) acrylate. A polymer type ultraviolet absorber obtained by copolymerization with a monomer such as may be used. Preferred examples of the UV-absorbing monomer include compounds containing a benzotriazole skeleton, a benzophenone skeleton, a triazine skeleton, a cyclic imino ester skeleton, and a cyanoacrylate skeleton in the ester substituent of (meth) acrylate. The

  Among them, benzotriazole and hydroxyphenyltriazine are preferable from the viewpoint of ultraviolet absorption ability, and cyclic imino ester and cyanoacrylate are preferable from the viewpoint of heat resistance and hue. You may use the said ultraviolet absorber individually or in mixture of 2 or more types.

  The content of the ultraviolet absorber is 0.01 to 2 parts by weight, preferably 0.03 to 2 parts by weight, more preferably 0.02 to 1 part by weight, based on 100 parts by weight of the total of component A and component B. More preferably, it is 0.05-0.5 weight part.

(I-4) Other Heat Stabilizers The glass fiber reinforced resin composition of the present invention may contain other heat stabilizers other than the phosphorus stabilizers and hindered phenol antioxidants. Such other heat stabilizers are preferably used in combination with any of these stabilizers and antioxidants, and particularly preferably used in combination with both. Examples of such other heat stabilizers include lactone stabilizers represented by the reaction product of 3-hydroxy-5,7-di-tert-butyl-furan-2-one and o-xylene (such stabilizers). Is described in detail in JP-A-7-233160). Such a compound is commercially available as Irganox HP-136 (trademark, manufactured by CIBA SPECIALTY CHEMICALS) and can be used. Furthermore, a stabilizer obtained by mixing the compound with various phosphite compounds and hindered phenol compounds is commercially available. For example, Irganox HP-2921 manufactured by the above company is preferably exemplified. In the present invention, such a premixed stabilizer can also be used. The blending amount of the lactone-based stabilizer is preferably 0.0005 to 0.05 parts by weight, more preferably 0.001 to 0.03 parts by weight, based on 100 parts by weight of the total of component A and component B.

  Other stabilizers include sulfur-containing stabilizers such as pentaerythritol tetrakis (3-mercaptopropionate), pentaerythritol tetrakis (3-laurylthiopropionate), and glycerol-3-stearylthiopropionate. Illustrated. Such a stabilizer is particularly effective when the resin composition is applied to rotational molding. The amount of the sulfur-containing stabilizer is preferably 0.001 to 0.1 parts by weight, more preferably 0.01 to 0.08 parts by weight, based on the total of 100 parts by weight of the component A and the component B.

(Ii) Mold Release Agent The glass fiber reinforced resin composition of the present invention is further prepared with a fatty acid ester, a polyolefin wax, a silicone compound, and a fluorine compound for the purpose of improving productivity during molding and improving the dimensional accuracy of a molded product. Known release agents such as paraffin wax and beeswax can also be blended (such as fluorine oil typified by polyfluoroalkyl ether). Since the glass fiber reinforced resin composition of the present invention has good fluidity, a pressure propagation is good and a molded article with uniform strain can be obtained. On the other hand, since the molding shrinkage rate is low, the mold release resistance tends to increase, and as a result, the molded product tends to be deformed at the time of mold release. The compounding of the specific component solves such a problem without impairing the properties of the glass fiber reinforced resin composition.

  Such fatty acid esters are esters of aliphatic alcohols and aliphatic carboxylic acids. Such an aliphatic alcohol may be a monohydric alcohol or a dihydric or higher polyhydric alcohol. Moreover, carbon number of this alcohol becomes like this. Preferably it is 3-32, More preferably, it is 5-30. On the other hand, the aliphatic carboxylic acid is preferably an aliphatic carboxylic acid having 3 to 32 carbon atoms, more preferably 10 to 30 carbon atoms. Of these, saturated aliphatic carboxylic acids are preferred. The fatty acid ester of the present invention is preferable in that all esters (full esters) are excellent in thermal stability at high temperatures. The acid value in the fatty acid ester of the present invention is preferably 20 or less (can take substantially 0). The hydroxyl value of the fatty acid ester is more preferably in the range of 0.1-30. Further, the iodine value of the fatty acid ester is preferably 10 or less (can take substantially 0). These characteristics can be obtained by a method defined in JIS K 0070.

  As the polyolefin wax, an ethylene homopolymer having a molecular weight of 1,000 to 10,000, a homopolymer or copolymer of an α-olefin having 3 to 60 carbon atoms, or ethylene and a carbon atom having 3 to 3 carbon atoms. A copolymer with 60 α-olefins is exemplified. The molecular weight is a number average molecular weight measured in terms of standard polystyrene by GPC (gel permeation chromatography) method. The upper limit of the number average molecular weight is more preferably 6,000, and still more preferably 3,000. The carbon number of the α-olefin component in the polyolefin wax is preferably 60 or less, more preferably 40 or less. More preferred specific examples include propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, 1-octene and the like. A suitable polyolefin wax is an ethylene homopolymer or a copolymer of ethylene and an α-olefin having 3 to 60 carbon atoms. The proportion of the α-olefin having 3 to 60 carbon atoms is preferably 20 mol% or less, more preferably 10 mol% or less. What is marketed as what is called polyethylene wax is used suitably.

  The content of the release agent is preferably 0.005 to 5 parts by weight, more preferably 0.01 to 4 parts by weight, and still more preferably 0.02 based on the total of 100 parts by weight of the component A and the component B. ~ 3 parts by weight.

(Iii) Dye / pigment The glass fiber reinforced resin composition of the present invention can further provide a molded product containing various dyes / pigments and exhibiting various design properties. Examples of dyes used in the present invention include perylene dyes, coumarin dyes, thioindigo dyes, anthraquinone dyes, thioxanthone dyes, ferrocyanides such as bitumen, perinone dyes, quinoline dyes, quinacridone dyes, Examples thereof include dioxazine dyes, isoindolinone dyes, and phthalocyanine dyes. Furthermore, the resin composition of this invention can mix | blend a metallic pigment, and can also obtain a better metallic color. As the metallic pigment, aluminum powder is suitable. In addition, by blending a fluorescent brightening agent or other fluorescent dyes that emit light, a better design effect utilizing the luminescent color can be imparted.

Examples of the fluorescent dye (including a fluorescent brightening agent) used in the present invention include a coumarin fluorescent dye, a benzopyran fluorescent dye, a perylene fluorescent dye, an anthraquinone fluorescent dye, a thioindigo fluorescent dye, and a xanthene fluorescent dye. And xanthone fluorescent dyes, thioxanthene fluorescent dyes, thioxanthone fluorescent dyes, thiazine fluorescent dyes, and diaminostilbene fluorescent dyes. Among these, coumarin fluorescent dyes, benzopyran fluorescent dyes, and perylene fluorescent dyes are preferable because they have good heat resistance and little deterioration during molding of the polycarbonate resin.
The content of the dye / pigment is preferably 0.00001 to 1 part by weight, and more preferably 0.00005 to 0.5 part by weight, based on 100 parts by weight of the total of component A and component B.

(Iv) Compound having heat absorption ability The glass fiber reinforced resin composition of the present invention may contain a compound having heat absorption ability. Such compounds include phthalocyanine-based near-infrared absorbers, metal oxide-based near-infrared absorbers such as ATO, ITO, iridium oxide and ruthenium oxide, and metal boride-based near infrared rays such as lanthanum boride, cerium boride and tungsten boride. Preferred examples include various metal compounds having excellent near-infrared absorption ability such as an absorber, and carbon filler. As such a phthalocyanine-based near infrared absorber, for example, MIR-362 manufactured by Mitsui Chemicals, Inc. is commercially available and easily available. Examples of the carbon filler include carbon black, graphite (including both natural and artificial) and fullerene, and carbon black and graphite are preferable. These can be used alone or in combination of two or more. The content of the phthalocyanine-based near infrared absorber is preferably 0.0005 to 0.2 parts by weight, more preferably 0.0008 to 0.1 parts by weight, based on the total of 100 parts by weight of the component A and the component B. 0.001 to 0.07 part by weight is more preferable. The content of the metal oxide near-infrared absorber, the metal boride-based near infrared absorber, and the carbon filler is preferably in the range of 0.1 to 200 ppm (weight ratio) in the resin composition of the present invention. A range of ˜100 ppm is more preferable.

(V) Light diffusing agent The glass fiber reinforced resin composition of the present invention can be provided with a light diffusing effect by blending a light diffusing agent. Examples of such light diffusing agents include polymer fine particles, inorganic fine particles having a low refractive index such as calcium carbonate, and composites thereof. Such polymer fine particles are fine particles that are already known as light diffusing agents for polycarbonate resins. More preferably, acrylic crosslinked particles having a particle size of several μm, silicone crosslinked particles represented by polyorganosilsesquioxane, and the like are exemplified. Examples of the shape of the light diffusing agent include a spherical shape, a disk shape, a column shape, and an indefinite shape. Such spheres need not be perfect spheres, but include deformed ones, and such columnar shapes include cubes. A preferred light diffusing agent is spherical, and the more uniform the particle size is. The content of the light diffusing agent is preferably 0.005 to 20 parts by weight, more preferably 0.01 to 10 parts by weight, and still more preferably 0.01 to 3 parts by weight based on the total of 100 parts by weight of the component A and the component B. Parts by weight. Two or more light diffusing agents can be used in combination.

(Vi) White pigment for light high reflection The glass fiber reinforced resin composition of the present invention can be provided with a light reflection effect by blending a white pigment for light high reflection. As such a white pigment, a titanium dioxide (particularly titanium dioxide treated with an organic surface treating agent such as silicone) pigment is particularly preferred. The content of the white pigment for high light reflection is preferably 3 to 30 parts by weight, more preferably 8 to 25 parts by weight based on the total of 100 parts by weight of the A component and the B component. Two or more kinds of white pigments for high light reflection can be used in combination.

(Vii) Antistatic agent The glass fiber reinforced resin composition of the present invention may require antistatic performance, and in such a case, an antistatic agent is preferably included. Examples of such antistatic agents include (1) organic sulfonic acid phosphonium salts such as (1) aryl sulfonic acid phosphonium salts represented by dodecylbenzene sulfonic acid phosphonium salts, and alkyl sulfonic acid phosphonium salts, and tetrafluoroboric acid phosphonium salts. Examples thereof include phosphonium borate salts. The content of the phosphonium salt is suitably 5 parts by weight or less, preferably 0.05 to 5 parts by weight, more preferably 1 to 3.5 parts by weight, based on a total of 100 parts by weight of component A and component B. More preferably, it is in the range of 1.5 to 3 parts by weight.

  Antistatic agents include, for example: (2) lithium organic sulfonate, organic sodium sulfonate, organic potassium sulfonate, cesium organic sulfonate, rubidium organic sulfonate, calcium organic sulfonate, magnesium organic sulfonate, and barium organic sulfonate And organic sulfonate alkali (earth) metal salts. Such metal salts are also used as flame retardants as described above. More specific examples of such metal salts include metal salts of dodecylbenzene sulfonic acid and metal salts of perfluoroalkane sulfonic acid. The content of the organic sulfonate alkali (earth) metal salt is suitably 0.5 parts by weight or less, preferably 0.001 to 0.3 parts by weight, based on the total of 100 parts by weight of component A and component B. More preferably, it is 0.005-0.2 weight part. In particular, alkali metal salts such as potassium, cesium, and rubidium are preferable.

  Examples of the antistatic agent include (3) organic sulfonic acid ammonium salts such as alkylsulfonic acid ammonium salt and arylsulfonic acid ammonium salt. The ammonium salt is suitably 0.05 parts by weight or less based on the total of 100 parts by weight of the A component and the B component. Examples of the antistatic agent include (4) a polymer containing a poly (oxyalkylene) glycol component such as polyether ester amide as a constituent component. The polymer is suitably 5 parts by weight or less based on a total of 100 parts by weight of the component A and the component B.

(Viii) Other additives The glass fiber reinforced resin composition of the present invention includes a thermoplastic resin other than the component A, a rubbery polymer, other flow modifiers, an antibacterial agent, a dispersant such as liquid paraffin, a photocatalyst. A system antifouling agent and a photochromic agent can be blended.

  Examples of thermoplastic resins other than the component A include aromatic polyester resins (polyethylene terephthalate resin (PET resin), polybutylene terephthalate resin (PBT resin), cyclohexanedimethanol copolymerized polyethylene terephthalate resin (so-called PET-G resin), polyethylene naphthalate. Phthalate resin, polybutylene naphthalate resin, etc.), polymethyl methacrylate resin (PMMA resin), cyclic polyolefin resin, polylactic acid resin, polycaprolactone resin, thermoplastic fluororesin (for example, represented by polyvinylidene fluoride resin), and Examples include polyolefin resins (polyethylene resin, ethylene- (α-olefin) copolymer resin, polypropylene resin, propylene- (α-olefin) copolymer resin, and the like). Examples of the rubbery polymer include various core-shell type graft copolymers and thermoplastic elastomers. The other thermoplastic resin and rubber polymer are preferably 10 parts by weight or less, more preferably 5 parts by weight or less based on the total of 100 parts by weight of the component A and the component B.

(Manufacture of glass fiber reinforced resin composition)
Arbitrary methods are employ | adopted in order to manufacture the glass fiber reinforced resin composition of this invention.
For example, component A, component B, component C and optionally other additives are mixed thoroughly using premixing means such as a V-type blender, Henschel mixer, mechanochemical device, extrusion mixer, etc. A method of granulating such a premix by an extrusion granulator or a briquetting machine, then melt-kneading with a melt kneader represented by a vent type twin screw extruder, and then pelletizing with a pelletizer.

  In addition, a method of supplying each component independently to a melt kneader represented by a vent type twin screw extruder, or a part of each component is premixed and then supplied to the melt kneader independently of the remaining components. The method of doing is also mentioned. Examples of the method of premixing a part of each component include a method in which components other than the component A are premixed in advance and then mixed with the component A or directly supplied to the extruder.

  As a premixing method, for example, when a component having a powder form is included as the component A, a part of the powder and an additive to be blended are mixed to produce a master batch of the additive diluted with the powder. A method using a master batch can be mentioned. Furthermore, the method etc. which supply one component independently from the middle of a melt extruder are mentioned. In addition, when there exists a liquid thing in the component to mix | blend, what is called a liquid injection apparatus or a liquid addition apparatus can be used for supply to a melt extruder.

As the extruder, one having a vent capable of degassing moisture in the raw material and volatile gas generated from the melt-kneaded resin can be preferably used. From the vent, a vacuum pump is preferably installed for efficiently discharging generated moisture and volatile gas to the outside of the extruder. It is also possible to remove a foreign substance from the resin composition by installing a screen for removing the foreign substance mixed in the extrusion raw material in the zone in front of the extruder die. Examples of such a screen include a wire mesh, a screen changer, a sintered metal plate (such as a disk filter), and the like.
Examples of the melt kneader include a banbury mixer, a kneading roll, a single screw extruder, a multi-screw extruder having three or more axes, in addition to a twin screw extruder.

  The resin extruded as described above is directly cut into pellets, or after forming strands, the strands are cut with a pelletizer to be pelletized. When it is necessary to reduce the influence of external dust during pelletization, it is preferable to clean the atmosphere around the extruder. Furthermore, in the manufacture of such pellets, various methods already proposed for polycarbonate resin for optical discs are used to narrow the shape distribution of pellets, reduce miscuts, and reduce fine powder generated during transportation or transportation. In addition, it is possible to appropriately reduce bubbles (vacuum bubbles) generated inside the strands and pellets. By these prescriptions, it is possible to increase the molding cycle and reduce the occurrence rate of defects such as silver. Moreover, although the shape of a pellet can take common shapes, such as a cylinder, a prism, and a spherical shape, it is a cylinder more suitably. The diameter of such a cylinder is preferably 1 to 5 mm, more preferably 1.5 to 4 mm, and still more preferably 2 to 3.3 mm. On the other hand, the length of the cylinder is preferably 1 to 30 mm, more preferably 2 to 5 mm, and still more preferably 2.5 to 3.5 mm.

  The glass fiber reinforced resin composition of the present invention can be produced in various products by usually injection-molding the pellets produced as described above to obtain molded products. In such injection molding, not only ordinary molding methods but also injection compression molding, injection press molding, gas assist injection molding, foam molding (including a method of injecting a supercritical fluid), insert molding, in-mold coating molding, heat insulation Examples thereof include mold molding, rapid heating / cooling mold molding, two-color molding, sandwich molding, and ultra-high speed injection molding. In addition, either a cold runner method or a hot runner method can be selected for molding.

  The glass fiber reinforced resin composition of the present invention can also be used in the form of various shaped extrusions, sheets, films, etc. by extrusion molding. For forming sheets and films, an inflation method, a calendar method, a casting method, or the like can also be used. It is also possible to form a heat-shrinkable tube by applying a specific stretching operation. In addition, the glass fiber reinforced resin composition of the present invention can be formed into a molded product by rotational molding or blow molding.

  Thereby, a glass fiber reinforced resin composition and a molded article having good mechanical strength, low anisotropy and flame retardancy are provided. That is, according to the present invention, the average value of the major axis of the thermoplastic resin (component A) 40 to 99 parts by weight and the fiber cross section made of the aromatic polycarbonate resin (component A-1) is 10 to 50 μm, the major axis and the minor axis. It consists of a flat cross-section glass fiber (B-1 component) having an average ratio (major axis / minor axis) of 1.5 to 8 and a fibrous filler (B-2 component) excluding the B-1 component, and (B -1 component) and (B-2 component) in a weight ratio of 30/70 to 99/1, 1-60 parts by weight of reinforcing filler (B component), and a total of 100 parts by weight of component A and component B A molded product obtained by melt-molding a resin composition comprising 0.001 to 20 parts by weight of a flame retardant (component C) is provided.

  Molded articles in which the resin composition of the present invention is used include various electronic / electric equipment parts, camera parts, OA equipment parts, precision machine parts, machine parts, vehicle parts, other agricultural materials, transport containers, playground equipment, miscellaneous goods, etc. It is useful for various uses, particularly for a lens barrel, and its industrial effect is exceptional.

  Furthermore, various surface treatments can be performed on the molded article made of the resin composition of the present invention. Surface treatment here refers to a new layer on the surface of resin molded products such as vapor deposition (physical vapor deposition, chemical vapor deposition, etc.), plating (electroplating, electroless plating, hot dipping, etc.), painting, coating, printing, etc. A method used for ordinary polycarbonate resin is applicable. Specific examples of the surface treatment include various surface treatments such as hard coat, water / oil repellent coat, ultraviolet absorption coat, infrared absorption coat, and metalizing (evaporation). Hard coat is a particularly preferred and required surface treatment.

  In addition, since the resin composition of the present invention has improved metal adhesion, application of vapor deposition and plating is also preferable. The molded product thus provided with the metal layer can be used for electromagnetic wave shielding parts, conductive parts, antenna parts, and the like. Such parts are particularly preferably sheet-like and film-like.

  Since the glass fiber reinforced resin composition of the present invention is excellent in mechanical strength and low anisotropy, and also has good flame retardancy, as described above, buildings, building materials, agricultural materials, marine materials, vehicles It is widely useful in various fields such as electrical and electronic equipment, machinery, and particularly, useful for a lens barrel. Therefore, the industrial effect exhibited by the present invention is extremely great.

  The form of the present invention considered to be the best by the present inventor is a collection of the preferable ranges of the above requirements. For example, typical examples are described in the following examples. Of course, the present invention is not limited to these forms.

(I) Evaluation of glass fiber reinforced resin composition (i) Flexural modulus: measured in accordance with ASTM D790 (measurement condition 23 ° C.). In addition, the test piece was shape | molded by the cylinder temperature of 310 degreeC and the mold temperature of 100 degreeC with the injection molding machine (Sumitomo Heavy Industries, Ltd. SG-150U).
(Ii) Bending strength (with weld, without weld): ASTM D638 type I test piece is used, and the test piece with weld is filled from the side gates provided on both sides of the test piece and welded at the center of the test piece. It was created. A test piece without weld was prepared by sealing one gate. The obtained test piece was measured according to ASTM D790 (measurement condition 23 ° C.). In addition, the test piece was shape | molded by the cylinder temperature of 310 degreeC and the mold temperature of 100 degreeC with the injection molding machine (Sumitomo Heavy Industries, Ltd. SG-150U).
(Iii) Weld strength retention rate: (bending strength with weld) / (bending strength without weld) × 100 = weld strength retention rate (%).
(Iv) Mold shrinkage: A flat plate having a short side of 50 mm, a long side of 100 mm and a thickness of 4 mm having a film gate having a thickness of 1.5 mm on one short side is molded and conditioned at 23 ° C., 50% RH for 24 hours. Thereafter, the flow direction and the perpendicular direction dimension of the flow of the flat plate were measured using a three-dimensional measuring machine (MICROPAK 550 manufactured by Mitoyo Seisakusho Co., Ltd.), and the molding shrinkage in the flow direction and the perpendicular direction was determined.
(V) Anisotropy: The ratio of the molding shrinkage ratio determined above to the direction perpendicular to the flow direction was determined as anisotropy. The anisotropy value is preferably closer to 1.
(Vi) Roundness: Using a SG-150U molding machine, Sumitomo Heavy Industries, Ltd., cylinder temperature (15 mm, inner diameter 20 mm, wall thickness 2.5 mm) at a cylinder temperature of 300 ° C., A lens barrel molded body was molded at a mold temperature of 80 ° C., and the roundness of the inner diameter was measured using RONDCOM 41A manufactured by Tokyo Seimitsu Co., Ltd. The difference in length between the longest part and the shortest part of the inner diameter of the cylindrical molded body was defined as roundness. The smaller the difference, the higher the roundness.
(Vii) Appearance: Judgment of presence / absence of gloss is visually determined, and “G” indicates that the glass float is small and glossy, and “X” indicates that the glass float is large and no gloss. (Viii) Flame retardancy: Complies with UL94 standard The maximum combustion seconds and UL94 rank were evaluated at thicknesses of 0.8 mm and 1.6 mm. The shorter the maximum burning time, the better the flame retardancy. In addition, the test piece was shape | molded by the cylinder temperature of 310 degreeC and the mold temperature of 100 degreeC with the injection molding machine (Sumitomo Heavy Industries, Ltd. SG-150U).

[Examples 1-8, Comparative Examples 1-7]
After mixing the polycarbonate resin and various additives shown in Table 1 in various blending amounts in a blender, the mixture was melt-kneaded using a vent type twin screw extruder to obtain pellets. Various additives to be used were prepared in advance by premixing with a polycarbonate resin with a concentration of 10 to 100 times the blending amount as a guide, and then the whole was mixed by a blender. The vent type twin-screw extruder used was TEX-30XSST (completely meshing, rotating in the same direction, two-thread screw) manufactured by Nippon Steel Works. The extrusion conditions are a discharge rate of 20 kg / h, a screw rotation speed of 150 rpm, and a vent vacuum of 3 kPa. did. The reinforcing filler was supplied from the second supply port using the side feeder of the extruder, and the remaining polycarbonate resin and additives were supplied to the extruder from the first supply port. The first supply port here is a supply port farthest from the die, and the second supply port is a supply port located between the die of the extruder and the first supply port.
The obtained pellets were dried with a hot air circulation dryer at 120 ° C. for 5 hours, and then a test piece for evaluation was molded using an injection molding machine. The evaluation results are shown in Table 1.

Each component of the symbol notation in Table 1 is as follows.
(A component)
PC: Linear polycarbonate resin powder having a viscosity average molecular weight of 22400 (manufactured by Teijin Chemicals Ltd .: Panlite L-1225WP)
ABS: Acrylonitrile-styrene-butadiene copolymer (“Santac UT-61” (trade name) manufactured by Nippon Air and L Co., Ltd.), bulk polymerization, about 80% by weight of free AS polymer component and ABS polymer component (acetone Insoluble gel content) About 20% by weight, butadiene rubber component content is about 15% by weight of the total)
(B component)
(B-1 component)
HGF-1: flat cross-section chopped glass fiber (manufactured by Nittobo Co., Ltd .: CSG 3PA-830, major axis 27 μm, minor axis 4 μm, cut length 3 mm, epoxy sizing agent)
HGF-2: flat cross-section chopped glass fiber (manufactured by Nitto Boseki Co., Ltd .: CSG 3PA-820, major axis 27 μm, minor axis 4 μm, cut length 3 mm, urethane sizing agent)
(B-2 component)
GF: Circular cross-section chopped glass fiber (manufactured by Nippon Electric Glass Co., Ltd .; ECS-03T-511, diameter 13 μm, cut length 3 mm, surface treatment with aminosilane and urethane sizing agent)
CF: Carbon fiber [Beast Fight HTA-C6-U, diameter 7 μm, manufactured by Toho Rayon Co., Ltd.]
(C component)
FR-1: phosphate ester mainly composed of bisphenol A bis (diphenyl phosphate) (“CR-741” (trade name) manufactured by Daihachi Chemical Industry Co., Ltd., TGA 5% weight reduction temperature = 335.9 ° C.)
FR-2: potassium perfluorobutane sulfonate (Dainippon Ink Chemical Co., Ltd. MegaFuck F-114P)
(D component)
PTFE: Polytetrafluoroethylene having a fibril forming ability (“Polyflon MPA FA500” (trade name) manufactured by Daikin Industries, Ltd.)
(Other ingredients)
TMP: Trimethyl phosphate (TMP manufactured by Daihachi Chemical Industry Co., Ltd.)
CB: 30 parts by weight of carbon black (carbon black MA-100 manufactured by Mitsubishi Chemical Corporation), 3 parts by weight of white mineral oil (Crystol N352 manufactured by ExxonMobil), 0.2 parts by weight of montanic ester wax (Clariant Japan) 100 parts by weight in total of 4 components of Ricoh WE-1 powder manufactured by Co., Ltd.) and 66.8 parts by weight of bisphenol A type polycarbonate resin (CM-1000 manufactured by Teijin Chemicals Ltd., viscosity average molecular weight 16,000) Carbon black master pellets produced by melt mixing using a twin screw extruder

Claims (14)

40 to 99 parts by weight of a thermoplastic resin (component A) containing 50% by weight or more of an aromatic polycarbonate resin, the average value of the major axis of the fiber cross section is 10 to 50 μm, and the ratio of the major axis to the minor axis (major axis / minor axis) A flat cross-section glass fiber (B-1 component) and a fibrous filler excluding the B-1 component that have a value of 1.5 to 8 and are focused with an epoxy resin or a urethane resin (however, the aspect ratio is (Except for the short cross-section glass short fiber of 10 or less) (component B-2), and the weight ratio (component B-1 / component B-2) of component (B-1) to component (B-2). Flame retardant (C component) of 0.001 to 20 parts by weight with respect to 1 to 60 parts by weight of reinforcing filler (B component) being 30/70 to 99/1 and a total of 100 parts by weight of A component and B component A glass fiber reinforced resin composition.   The glass fiber reinforced resin composition according to claim 1, wherein the average value of the ratio of the major axis to the minor axis (major axis / minor axis) of the component B-1 is 2.5 to 5.   The glass fiber reinforced resin composition according to claim 1 or 2, wherein the ratio (aspect ratio) of the average fiber length and the average fiber diameter of the component B-1 is 2 to 120.   The B-2 component is at least one selected from the group consisting of glass fibers other than the B-1 component (excluding short glass fibers having an aspect ratio of 10 or less), wollastonite, and carbon-based filler. It is a fibrous filler, The glass fiber reinforced resin composition in any one of Claims 1-3.   The glass fiber reinforced resin composition according to any one of claims 1 to 4, wherein the component C is at least one flame retardant selected from the group consisting of an organic metal salt flame retardant and an organic phosphorus flame retardant.   6. The resin composition according to claim 5, wherein the component C is an organic phosphorus flame retardant.   6. The glass fiber reinforced resin composition according to claim 5, wherein the organic metal salt flame retardant is an alkali (earth) metal sulfonate.   The glass fiber reinforced resin composition according to claim 7, wherein the alkali (earth) metal salt of an organic sulfonate is an alkali (earth) metal salt of a perfluoroalkyl sulfonate. The glass fiber reinforced resin composition according to claim 6, wherein the organophosphorus flame retardant is a flame retardant represented by the following general formula (1).

(However, X in the above formula is hydroquinone, resorcinol, bis (4-hydroxydiphenyl) methane, bisphenol A, dihydroxydiphenyl, dihydroxynaphthalene, bis (4-hydroxyphenyl) sulfone, bis (4-hydroxyphenyl) ketone, bis And a divalent group derived from (4-hydroxyphenyl) sulfide, wherein j, k, l and m are each independently 0 or 1, n is an integer of 0 to 5, or n number In the case of a mixture of phosphoric acid esters having different values, the average value is 0 to 5, and R ¹ , R ² , R ³ , and R ⁴ are each independently substituted or not substituted with one or more halogen atoms From phenol, cresol, xylenol, isopropylphenol, butylphenol, p-cumylphenol A monovalent group that is derived.) Of the thermoplastic resin is an aromatic polycarbonate resins (A-1 component) 100 parts by weight, the glass according to any one of claims 1 to 9 containing 1 to 100 parts by weight of styrene-based resin (A-2 component) Fiber reinforced resin composition.   The glass fiber reinforced resin composition according to claim 10, wherein the styrenic resin is at least one resin selected from the group consisting of polystyrene, ABS resin, AS resin, and HIPS resin.   The resin composition according to any one of claims 1 to 11, comprising 0.01 to 3 parts by weight of a fluorine-containing anti-dripping agent (D component) with respect to 100 parts by weight of the total of the A component and the B component.   The resin molded product formed by injection-molding the glass fiber reinforced resin composition in any one of Claims 1-12.   The resin molded product according to claim 13, wherein the resin molded product is a lens barrel.