JP4125413B2 - Urethane prepolymer composition and one-component urethane sealant - Google Patents
Urethane prepolymer composition and one-component urethane sealant Download PDFInfo
- Publication number
- JP4125413B2 JP4125413B2 JP07376798A JP7376798A JP4125413B2 JP 4125413 B2 JP4125413 B2 JP 4125413B2 JP 07376798 A JP07376798 A JP 07376798A JP 7376798 A JP7376798 A JP 7376798A JP 4125413 B2 JP4125413 B2 JP 4125413B2
- Authority
- JP
- Japan
- Prior art keywords
- urethane prepolymer
- urethane
- sealant
- compound
- carbon atoms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【発明の属する技術分野】
本発明は、潜在性硬化剤を含有するウレタンプレポリマーや、潜在性硬化剤を含有するウレタンプレポリマーを含有するシーラントの貯蔵安定性を向上させるウレタンプレポリマー組成物と、このウレタンプレポリマー組成物を含有する１液型ウレタンシーラントに関する。
【０００２】
【従来の技術】
従来より、各種のウレタン樹脂組成物が、建築用シーラント、目地材、接着剤、塗料、防水材、床材等として広く使用されている。
このようなウレタン樹脂組成物として、最近では、現地施工における樹脂組成物の混合調整が不要で取扱いが容易であるなどの理由から、湿気硬化性の１液型ウレタン樹脂組成物の利用が拡大している。
湿気硬化性の１液型ウレタン樹脂組成物（以下、１液型ウレタン組成物と記す）の架橋硬化反応は施工場所の表面から始まり、内部へと進行する。このため、完全に硬化するまでには３日から１週間という長時間を要した。そこで、従来は、スタナスオクトエイト、ジブチルチンジラウレートなどの錫あるいは鉛の有機金属化合物、またはトリエチルアミンあるいはトリエチレンジアミン、Ｎ−メチルモルフォリンなどの３級アミンを、単独あるいは組み合わせて使用し、硬化するまでの時間の短縮が図られてきた。
しかし、このような硬化触媒が添加された１液型ウレタン組成物は、硬化時間は短縮されるものの、貯蔵安定性が低下するという問題を持っていた。
【０００３】
このような問題点を解決し、硬化性、貯蔵安定性が共に良好な１液型ウレタン組成物を実現するために、貯蔵安定性の低下が少ない硬化触媒を配合した１液型ウレタン組成物や、貯蔵安定性を改善するための添加剤を配合した１液型ウレタン組成物が、各種提案されている。
例えば、ウレタンプレポリマーにオキサゾリジン化合物を適当量配合したシーラント用１液型ウレタン組成物が提案されている。この１液型ウレタン組成物では、シーラントの硬化反応速度は向上するが、貯蔵安定性が低下してしまう。このように、硬化性、貯蔵安定性が両立し、共に良好な１液型ウレタン組成物はいまだ見出されていない。
【０００４】
【発明が解決しようとする課題】
本発明の目的は、硬化性に優れ、さらに貯蔵安定性にも優れるウレタンプレポリマー組成物およびそれを含有する１液型ウレタンシーラントを提供することである。
【０００５】
【課題を解決するための手段】
すなわち、本発明は、
１）末端イソシアネート基を有するウレタンプレポリマーと、
２）下記式（２）で表されるオキサゾリジン化合物を前記ウレタンプレポリマーのＮＣＯ当量に対し０．０５〜０．５当量と、
３）ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンからなる群より選択される少なくとも１つの化合物を前記ウレタンプレポリマー１００重量部に対し０．０１〜１０重量部含有するウレタンプレポリマー組成物を提供する。
【化２】
【０００７】
また、本発明は、前記ウレタンプレポリマー組成物よりなる１液型ウレタンシーラントを提供する。
【０００８】
【発明の実施の形態】
以下、本発明をさらに詳細に説明する。
本発明のウレタンプレポリマー組成物は、１）末端イソシアネート基を有するウレタンプレポリマーと、２）上記式（１）で表されるオキサゾリジン化合物を前記ウレタンプレポリマーのＮＣＯ当量に対し０．１〜２当量、または上記式（２）で表されるオキサゾリジン化合物を前記ウレタンプレポリマーのＮＣＯ当量に対し０．０５〜０．５当量と、３）ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンからなる群より選択される少なくとも１つの化合物を前記ウレタンプレポリマー１００重量部に対し０．０１〜１０重量部含有するウレタンプレポリマー組成物である。
【０００９】
本発明に用いられる、末端イソシアネート基を有するウレタンプレポリマーとは、水の存在によりイソシアネート基部分がウレタン結合を形成しながら、架橋、硬化して高分子となる化合物で、ポリヒドロキシル化合物とポリイソシアネート化合物との反応生成物である。本発明に用いる上記ウレタンプレポリマーは、ポリヒドロキシル化合物の一種であるポリオールとポリイソシアナートから生成されるウレタンプレポリマーであればいかなるものでもよく、特に限定されない。
【００１０】
ポリオールとは、炭化水素の複数個の水素を水酸基で置換したアルコール類の総称であり、例えば、エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド、テトラヒドロフラン等のアルキレンオキサイドの１種または２種以上を、２個以上の活性水素を有する化合物に付加重合させた生成物である。
ここで、２個以上の活性水素を有する化合物としては、例えば、多価アルコール類、アミン類、アルカノールアミン類、多価フェノール類等が挙げられる。
多価アルコール類としては、エチレングリコール、プロピレングリコール、ブタンジオール、ジエチレングリコール、グリセリン、ヘキサントリオール、トリメチロールプロパン、ペンタエリスリトール等が、また、アミン類としては、エチレンジアミン、ヘキサメチレンジアミン等が、アルカノールアミン類としては、エタノールアミン、プロパノールアミン等が、そして多価フェノール類としては、レゾルシン、ビスフェノール類等を挙げることができる。
【００１１】
具体的には、ポリテトラメチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、ポリオキシプロピレングリコール、ポリオキシブチレングリコール等のポリエーテル系ポリオール、ポリブタジエンポリオール、ポリイソプレンポリオール等のポリオレフィン系ポリオール、その他アジペート系ポリオール、ラクトン系ポリオール、ヒマシ油等のポリエステル系ポリオール等が好ましく、必要に応じてこれらのポリオールを併用することも可能である。
これらの化合物は単独で使用しても、あるいは２種以上を併用してもよいが、重量平均分子量は１００〜１００００程度のものが好ましく、５００〜７０００程度のものがさらに好ましい。
【００１２】
ポリイソシアネート化合物としては、通常のポリウレタン樹脂の製造に用いられる種々のものが使用可能である。具体的には、２，４−トリレンジイソシアナートまたは２，６−トリレンジイソシアナート、ジフェニルメタン−４，４’−ジイソシアナートおよびこれらの変性品、１，５−ナフタレンジイソシアナート、ヘキサメチレンジイソシアネート、イソホロンジイソシアナート、キシリレンジイソシアネート等が挙げられる。
これらのポリイソシアナート化合物は、単独でも２種以上を併用してもよい。
【００１３】
末端イソシアネート基を有するウレタンプレポリマー製造の際のポリヒドロキシル化合物とポリイソシアネート化合物の量比は、ポリイソシアネート化合物中のイソシアネート基１個あたり、ポリヒドロキシル化合物中のヒドロキシル基が１個以下となる量比とするが、好ましくは０．５０〜０．９５個である。
また、ウレタンプレポリマーの製造条件は、通常のウレタンプレポリマーの製造条件でよい。すなわち、前述のヒドロキシル化合物とポリイソシアネート化合物を反応温度５０〜１００℃程度で、常圧下で反応させればよい。
【００１４】
本発明で用いるオキサゾリジン化合物は、下記式（２）で表される化合物を用いる。
【００１５】
【化３】
式（２）中、Ｒ 2 は、炭素数２〜６のアルキレン基である。
Ｒ 3 は炭素数２〜６のアルキレン基であるが、より好ましくは、炭素数２のアルキレン基である。
Ｒ 4 およびＲ 5 は、それぞれ独立に水素原子、炭素数１以上のアルキル基、炭素数５〜７の脂環式アルキル基、または炭素数６〜１０のアリール基である。
本発明に用いるオキサゾリジン化合物として、式（２）で表される化合物を単独で用いてもよいし、両方を併用してもよい。
【００１７】
オキサゾリジン化合物は、水により加水分解し第２アミンを生成し、第２アミンは、イソシアネート基と反応してウレア結合を形成する架橋反応を起こす。このため、オキサゾリジン化合物は、ウレタンシーラントの潜在性硬化剤として機能する。
【００１８】
オキサゾリジン化合物の製造方法としては、例えば、式（２）で表されるオキサゾリジン化合物は、アルカノールアミンとケトンまたはアルデヒドとの脱水縮合反応による方法等の通常の方法により製造することができる。
式（２）で表されるオキサゾリジン化合物を用いる場合の配合量は、前記ウレタンプレポリマーのＮＣＯ当量に対し０．０５〜０．５当量であるのが好ましい。０．０５当量未満では硬化速度が遅く、０．５当量超では化学量論的に不適である。より好ましくは、０．２〜０．４当量である。
【００１９】
本発明のウレタンプレポリマー組成物は、オキサゾリジン化合物を加えたウレタンプレポリマーに、さらに、ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンからなる群より選択される少なくとも１つの化合物を含有することを特徴とする。これらの化学構造式を以下に示す。
【化２】
式（３）中、Ｒ6 は、炭素数１〜２０のアルキル基であり、炭素数１〜４のアルキル基であることが好ましい。式（３）で表される化合物の具体例としては、ジエチルマロネート等が例示される。
式（４）中、Ｒ7 は炭素数１〜２０のアルキル基であり、炭素数１〜４のアルキル基であることが好ましい。式（４）で表される化合物の具体例としては、アセト酢酸メチル等が例示される。
式（５）中、Ｒ8 は炭素数１〜２０のアルキル基であり、炭素数１〜４のアルキル基であることが好ましい。式（５）で表される化合物の具体例としては、ニトロエタン等が例示される。
【００２１】
ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンは、潜在性硬化剤としてウレタンプレポリマーに配合されるオキサゾリジン化合物の安定剤として働く。
すなわち、ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンは、前記オキサゾリジン化合物とともにウレタンプレポリマーに配合されると、分子内に有する弱い酸性水素が、オキサゾリジン化合物の３級アミンと相互作用し、この相互作用によりオキサゾリジン化合物とウレタンプレポリマーのイソシアネート基との反応を抑制すると考えられる。
このようなオキサゾリジン化合物の作用を安定化する上記特定化合物の作用により、上記特定化合物を配合した、オキサゾリジン化合物を加えたウレタンプレポリマーの貯蔵安定性を向上させることができる。
【００２２】
ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンのそれぞれ単独、もしくはこれらを組み合わせた合計の配合量は、前記ウレタンプレポリマー１００重量部に対し、０．０１〜１０重量部であり、０．１〜２．０重量部が好ましい。この範囲内であれば、得られるウレタンプレポリマー組成物の貯蔵安定性が優れたものとなるからである。
【００２３】
本発明のウレタンプレポリマー組成物は、上記必須の化合物を、減圧下または不活性雰囲気下で十分混練し均一に分散させて製造することができる。
このようにして得られる本発明のウレタンプレポリマー組成物は、上記構成を採ることにより、一液型のウレタンプレポリマー組成物として貯蔵することが可能で、容器から出した際の硬化速度に優れるとともに、容器中に貯蔵中、安定に保存でき貯蔵安定性に優れる。また、これを用いてシーラントとすれば、１液型ウレタンシーラントの貯蔵安定性が高い。
【００２４】
本発明の１液型ウレタンシーラント（以下、本発明のシーラントと記す）は、上記ウレタンプレポリマー組成物を主成分として含有するシーラントである。本発明のシーラントは、上記ウレタンプレポリマー組成物を含有するので、硬化性に優れ、貯蔵安定性に優れる。
本発明のシーラントは、本発明の目的を損なわない範囲で、シリルエステル化合物、充填剤、可塑剤、酸化防止剤、顔料、シランカップリング剤、分散剤、溶剤等を含有することができる。
【００２５】
ここで、シリルエステル化合物とは、カルボン酸とシラノールから製造される、分子末端に−Ｓｉ−（ＯＣＯＲ）n を有するシリルエステル化合物をさす。式中、Ｒは炭素数１〜２０の炭化水素基を、ｎは１〜３の整数を表す。このようなシリルエステル化合物として例えば下記式（７）、（８）で表される化合物を示すことができる。下記式中、ｐは約３０である。
【化３】
また、炭素鎖の長いカルボン酸は、シーラント中に配合される充填剤、例えば、炭酸カルシウムフィラー等の表面に結合し、揺変性付与剤として機能し、シーラントに良好なチクソ性を与える。
このような炭素数１０〜２０の長い炭素鎖を有するシリルエステル化合物の配合量は、前記ウレタンプレポリマー組成物１００重量部に対して、０．１〜２０重量部が好ましく、１〜１０重量部がより好ましい。上記範囲であると、貯蔵安定性の観点から好ましいからである。
【００２６】
また、上記シリルエステル化合物の中で、Ｒが炭素数１〜９の炭化水素基であるシリルエステル化合物を、本発明のシーラントの製造過程において、好ましくは、上記長い炭素鎖をもつシリルエステル化合物により配合系内の水分が十分に除去された後に添加すると、加水分解することなくエステルの状態で配合系内に存在して、シーラント使用時に空気中の水分により加水分解する。このとき生じるカルボン酸は、炭素数１〜９の、炭素鎖の短いカルボン酸である。炭素鎖の短いカルボン酸は酸性度が高く、オキサゾリジン化合物やイソシアネート基を活性化し加水分解・硬化反応を促進する。従って、このような炭素鎖の短いシリルエステル化合物は、シーラントの貯蔵安定性になんら悪影響を与えることなく、速硬化性を与える潜在性速硬化触媒として機能する。
上記炭素数１〜９の炭素鎖の短いシリルエステル化合物式の配合量は、前記ウレタンプレポリマー組成物１００重量部に対して、０．０１〜１０重量部が好ましく、０．１〜５重量部がより好ましい。上記範囲であると、速硬化性の観点から好ましいからである。
【００２７】
充填剤としては、表面処理炭酸カルシウム、カーボンブラック、クレー、タルク、酸化チタン、生石灰、カオリン、ゼオライト、ケイソウ土、塩化ビニルペーストレジン、ガラスバルーン、塩化ビニリデン樹脂バルーン等が挙げられる。これらの充填剤は、単独で、または混合して使用することができる。
充填剤の配合量は、前記ウレタンプレポリマー組成物１００重量部に対して、５０〜２００重量部が好ましく、１００〜１８０重量部がより好ましい。上記範囲であると、速硬化性の観点から好ましいからである。
【００２８】
可塑剤としては、例えば、ジオクチルフタレート（ＤＯＰ）、ジブチルフタレート（ＤＢＰ）、ジラウリルフタレート（ＤＬＰ）、ジブチルベンジルフタレート（ＢＢＰ）、ジオクチルアジペート、ジイソデシルアジペート、トリオクチルフォスフェート、トリス（クロロエチル）フォスフェート、トリス（ジクロロプロピル）フォスフェート、アジピン酸プロピレングリコールポリエステル、アジピン酸ブチレングリコールポリエステル、エポキシステアリン酸アルキル、エポキシ化大豆油等が挙げられる。これらの可塑剤は、単独で、あるいは混合して使用することができる。
【００２９】
酸化防止剤としては、ブチルヒドロキシトルエン（ＢＨＴ）、ブチルヒドロキシシアニソール（ＢＨＡ）、ジフェニルアミン、フェニレンジアミン、亜リン酸トリフェニル等を挙げることができる。
顔料としては、二酸化チタン、酸化亜鉛、群青、弁柄、リトボン、鉛、カドミウム、鉄、コバルト、アルミニウム、塩酸塩、硫酸塩等の無機顔料；アゾ顔料、銅フタロシアニン顔料等の有機顔料等が挙げられる。
溶剤としては、キシレン、トルエン等の芳香族系炭化水素溶媒を挙げることができる。
【００３０】
本発明のシーラントの製造方法としては、上記化合物を、好ましくは、上記シリルエステル化合物の配合のタイミングに従って、減圧下または不活性雰囲気下に十分混練し、均一に分散させて組成物とする方法を示すことができる。
このようにして得られる本発明のシーラントは、硬化性に優れるばかりでなく、貯蔵安定性にも優れ、硬化性と貯蔵安定性を両立することができる。このため、本発明のシーラントは、建築用に用いる１液型シーラントとして好適である。
【００３１】
【実施例】
以下に、実施例を示して本発明を具体的に説明するが、本発明はこれらに限られるものではない。
【００３２】
（ウレタンプレポリマーとオキサゾリジン化合物の混合物の調整）
水酸基を３個有する平均分子量６０００のポリオキシプロピレントリオール（旭硝子（株）製）５００重量部と、平均分子量３０００のポリオキシプロピレンジオール７４０重量部と、フタル酸ジオクチル５３６重量部を反応容器に入れて、１１０℃、１０ｍｍＨｇの条件で、２４時間脱水処理した。ついで、１００重量部の２，４−トリレンジイソシアネートと２，６−トリレンジイソシアネートの混合物（混合比、２，４−ＴＤＩ：２，６−ＴＤＩ＝８０：２０）を添加して、窒素雰囲気下８０℃で６時間撹拌し、ＮＣＯ基含量が１．０６重量％になったことを確認した。反応液に下記式で表されるオキサゾリジン化合物を３７重量部添加し、窒素雰囲気下６０℃にて２時間撹拌してウレタンプレポリマーとオキサゾリジン化合物の混合物（表中、ＰＰＧ・ＴＤＩ・ＰＨＯウレタンプレポリマーと記す）を得た。
【化４】
ウレタンプレポリマー組成物の調整と評価
得られたウレタンプレポリマーとオキサゾリジン化合物の混合物（ＰＰＧ・ＴＤＩ・ＰＨＯウレタンプレポリマー）と、ジエチルマロネート、アセト酢酸エチル、ニトロエタン、あるいは、シクロペンタジエンを下記表１に記載の配合比で混合し、ウレタンプレポリマー組成物を得た。
【００３４】
１液型ウレタンシーラントの調整と評価
得られたウレタンプレポリマー組成物と、表面処理炭酸カルシウム（丸尾カルシウム（株）製）と、前記式（７）で表されるシリルエステル化合物Ａ、前記式（８）で表されるシリルエステル化合物Ｂを下記表１に記載の配合比で混合し、シーラントを得た。
【００３５】
（実施例１〜１１、比較例１〜２）
上述のようにして得られたウレタンプレポリマー組成物について、粘度変化率を測定して貯蔵安定性を評価した。貯蔵安定性の合格範囲は、１．００〜１．５０とした。
また、上述のようにして得られたシーラントについて、貯蔵安定性を評価するとともに、硬化時間の変化率を測定して硬化性を評価した。シーラントの貯蔵安定性の合格範囲は、０．７５〜１．２５、硬化性の合格範囲は、０．６５〜１．００とした。
【００３６】
【表１】
（１）ウレタンプレポリマー組成物の粘度変化率（貯蔵安定性の評価）
東京計器社製のＥ型粘度計３°コーンを使用し、２０℃、１ｒｐｍ／１０ｒｐｍの条件で、初期粘度および貯蔵後粘度を測定した。貯蔵後粘度は、組成物を８０℃の雰囲気下に２４時間放置した後に測定した。貯蔵後粘度の初期粘度に対する比を粘度変化率として求めた。
（２）１液型ウレタンシーラントの粘度変化率（貯蔵安定性の評価）
東京計器社製のＢＳ型粘度計Ｎｏ．７ローターを使用し、２０℃、１ｒｐｍ／１０ｒｐｍの条件で、初期粘度および貯蔵後粘度を測定した。貯蔵後粘度は、組成物を７０℃の雰囲気下に２４時間放置した後に測定した。貯蔵後粘度の初期粘度に対する比を粘度変化率として求めた。
（３）硬化時間変化率（硬化性の評価）
２０℃、相対湿度６０％の条件下で、初期硬化時間および貯蔵後硬化時間を測定した。なお、シーラントをポリエチレンフィルムに付着させ、付着が起こらなくなるまでの時間を測定し、付着しなくなった時間を硬化時間とした。貯蔵後硬化時間は、シーラントを７０℃の雰囲気下に２４時間放置した後に測定した。貯蔵後硬化時間の初期硬化時間に対する比を硬化時間変化率として求めた。
【００３８】
【発明の効果】
本発明のウレタンプレポリマー組成物は、硬化時間が短く、特に貯蔵安定性に優れる。そのため、このようなウレタンプレポリマー組成物を含有する本発明の１液型ウレタンシーラントは、硬化性に優れ、さらに貯蔵安定性に優れる。従って、本発明の１液型ウレタンシーラントは、打設後の硬化が速く、速やかに塗料等を塗布することができ、長期貯蔵後であっても、良好な作業性を有する建築用シーラントとして有用である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a urethane prepolymer containing a latent curing agent, a urethane prepolymer composition that improves the storage stability of a sealant containing a urethane prepolymer containing a latent curing agent, and the urethane prepolymer composition. Relates to a one-component urethane sealant containing
[0002]
[Prior art]
Conventionally, various urethane resin compositions have been widely used as architectural sealants, joint materials, adhesives, paints, waterproofing materials, flooring materials and the like.
As such a urethane resin composition, recently, the use of a moisture-curable one-component urethane resin composition has expanded due to the fact that mixing adjustment of the resin composition in field construction is unnecessary and handling is easy. ing.
The cross-linking curing reaction of a moisture curable one-component urethane resin composition (hereinafter referred to as a one-component urethane composition) starts from the surface of the construction site and proceeds to the inside. For this reason, it took a long time of 3 days to 1 week to be completely cured. Therefore, conventionally, stannous octoate, dibutyltin dilaurate and other tin or lead organometallic compounds, or triethylamine, triethylenediamine, and tertiary amines such as N-methylmorpholine are used alone or in combination to cure. Has been shortened.
However, the one-component urethane composition to which such a curing catalyst is added has a problem that the storage stability is lowered although the curing time is shortened.
[0003]
In order to solve such problems and realize a one-component urethane composition having both good curability and storage stability, a one-component urethane composition containing a curing catalyst with little decrease in storage stability, Various one-component urethane compositions containing additives for improving storage stability have been proposed.
For example, a one-component urethane composition for sealants in which an appropriate amount of an oxazolidine compound is blended with a urethane prepolymer has been proposed. In this one-component urethane composition, the curing reaction rate of the sealant is improved, but the storage stability is lowered. As described above, a one-component urethane composition that has both curability and storage stability and is excellent has not been found yet.
[0004]
[Problems to be solved by the invention]
An object of the present invention is to provide a urethane prepolymer composition having excellent curability and storage stability and a one-pack type urethane sealant containing the same.
[0005]
[Means for Solving the Problems]
That is, the present invention
1) a urethane prepolymer having a terminal isocyanate group;
2) and 0.05 to 0.5 equivalent of NCO equivalent of the urethane prepolymer oxazolidine compound represented by the following following formula (2),
3) Urethane containing 0.01 to 10 parts by weight of at least one compound selected from the group consisting of dialkyl malonate, acetoacetate, aliphatic nitro compound, and cyclopentadiene with respect to 100 parts by weight of the urethane prepolymer. A prepolymer composition is provided.
[Chemical 2]
[0007]
The present invention also provides a one-component urethane sealant comprising the urethane prepolymer composition.
[0008]
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, the present invention will be described in more detail.
The urethane prepolymer composition of the present invention comprises 1) a urethane prepolymer having a terminal isocyanate group, and 2) an oxazolidine compound represented by the above formula (1) in an amount of 0.1 to 2 with respect to the NCO equivalent of the urethane prepolymer. Equivalents, or 0.05 to 0.5 equivalents of the oxazolidine compound represented by the above formula (2) with respect to the NCO equivalent of the urethane prepolymer, and 3) a dialkyl malonate, an acetoacetate ester, an aliphatic nitro compound, and A urethane prepolymer composition containing 0.01 to 10 parts by weight of at least one compound selected from the group consisting of cyclopentadiene and 100 parts by weight of the urethane prepolymer .
[0009]
The urethane prepolymer having a terminal isocyanate group used in the present invention is a compound that becomes a polymer by crosslinking and curing while forming an urethane bond in the presence of water, and a polyhydroxyl compound and a polyisocyanate. It is a reaction product with a compound. The urethane prepolymer used in the present invention is not particularly limited as long as it is a urethane prepolymer produced from a polyol which is a kind of polyhydroxyl compound and a polyisocyanate.
[0010]
Polyol is a general term for alcohols in which a plurality of hydrocarbon hydrogens are substituted with hydroxyl groups. For example, two or more alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran, etc. It is a product obtained by addition polymerization to the compound having the above active hydrogen.
Here, examples of the compound having two or more active hydrogens include polyhydric alcohols, amines, alkanolamines, and polyhydric phenols.
Examples of polyhydric alcohols include ethylene glycol, propylene glycol, butanediol, diethylene glycol, glycerin, hexanetriol, trimethylolpropane, pentaerythritol, and the like, and examples of amines include ethylenediamine, hexamethylenediamine, and alkanolamines. Examples thereof include ethanolamine and propanolamine, and examples of the polyhydric phenols include resorcin and bisphenols.
[0011]
Specifically, polyether polyols such as polytetramethylene glycol, polyethylene glycol, polypropylene glycol, polyoxypropylene glycol and polyoxybutylene glycol, polyolefin polyols such as polybutadiene polyol and polyisoprene polyol, other adipate polyols, and lactones Polyester polyols such as system polyols and castor oil are preferred, and these polyols can be used in combination as required.
These compounds may be used alone or in combination of two or more, but the weight average molecular weight is preferably about 100 to 10000, more preferably about 500 to 7000.
[0012]
As the polyisocyanate compound, various compounds used for the production of ordinary polyurethane resins can be used. Specifically, 2,4-tolylene diisocyanate or 2,6-tolylene diisocyanate, diphenylmethane-4,4′-diisocyanate and modified products thereof, 1,5-naphthalene diisocyanate, hexamethylene Examples include diisocyanate, isophorone diisocyanate, and xylylene diisocyanate.
These polyisocyanate compounds may be used alone or in combination of two or more.
[0013]
The amount ratio of the polyhydroxyl compound and the polyisocyanate compound in the production of the urethane prepolymer having a terminal isocyanate group is such that the number of hydroxyl groups in the polyhydroxyl compound is 1 or less per isocyanate group in the polyisocyanate compound. However, it is preferably 0.50 to 0.95.
Moreover, the manufacturing conditions of a urethane prepolymer may be the manufacturing conditions of a normal urethane prepolymer. That is, the above hydroxyl compound and polyisocyanate compound may be reacted at a reaction temperature of about 50 to 100 ° C. under normal pressure.
[0014]
As the oxazolidine compound used in the present invention, a compound represented by the following formula (2) is used.
[0015]
[Chemical 3]
In formula (2), R 2 Is an alkylene group having 2 to 6 carbon atoms.
R 3 Is an alkylene group having 2 to 6 carbon atoms, more preferably an alkylene group having 2 carbon atoms.
R 4 And R 5 Are each independently a hydrogen atom, an alkyl group having 1 or more carbon atoms, an alicyclic alkyl group having 5 to 7 carbon atoms, or an aryl group having 6 to 10 carbon atoms.
As the oxazolidine compound used in the present invention, the compound represented by the formula (2) may be used alone, or both may be used in combination.
[0017]
The oxazolidine compound is hydrolyzed with water to produce a secondary amine, and the secondary amine reacts with an isocyanate group to cause a crosslinking reaction to form a urea bond. For this reason, an oxazolidine compound functions as a latent curing agent for a urethane sealant.
[0018]
As a method for producing the oxazolidine compound, for example, the oxazolidine compound represented by the formula (2) can be produced by a usual method such as a method using a dehydration condensation reaction between an alkanolamine and a ketone or an aldehyde .
When the oxazolidine compound represented by the formula (2) is used, the blending amount is preferably 0.05 to 0.5 equivalent relative to the NCO equivalent of the urethane prepolymer. If it is less than 0.05 equivalent, the curing rate is slow, and if it exceeds 0.5 equivalent, it is not stoichiometrically suitable. More preferably, it is 0.2 to 0.4 equivalent.
[0019]
The urethane prepolymer composition of the present invention is obtained by adding at least one compound selected from the group consisting of a dialkylmalonate, an acetoacetate ester, an aliphatic nitro compound, and a cyclopentadiene to a urethane prepolymer to which an oxazolidine compound is added. It is characterized by containing. These chemical structural formulas are shown below.
[Chemical 2]
In formula (3), R 6 is an alkyl group having 1 to 20 carbon atoms, preferably an alkyl group having 1 to 4 carbon atoms. Specific examples of the compound represented by the formula (3) include diethyl malonate.
In formula (4), R 7 is an alkyl group having 1 to 20 carbon atoms, preferably an alkyl group having 1 to 4 carbon atoms. Specific examples of the compound represented by the formula (4) include methyl acetoacetate and the like.
Wherein (5), R 8 is an alkyl group having 1 to 20 carbon atoms, preferably an alkyl group having 1 to 4 carbon atoms. Specific examples of the compound represented by the formula (5) include nitroethane.
[0021]
Dialkyl malonates, acetoacetic esters, aliphatic nitro compounds, and cyclopentadiene serve as stabilizers for oxazolidine compounds that are incorporated into urethane prepolymers as latent curing agents.
That is, when dialkyl malonate, acetoacetic acid ester, aliphatic nitro compound, and cyclopentadiene are blended in a urethane prepolymer together with the oxazolidine compound, the weak acidic hydrogen in the molecule is converted to the tertiary amine of the oxazolidine compound. It is thought that this interaction suppresses the reaction between the oxazolidine compound and the isocyanate group of the urethane prepolymer.
Due to the action of the specific compound that stabilizes the action of the oxazolidine compound, it is possible to improve the storage stability of the urethane prepolymer containing the specific compound and added with the oxazolidine compound.
[0022]
The total amount of dialkyl malonate, acetoacetate ester, aliphatic nitro compound, and cyclopentadiene alone or in combination is 0.01 to 10 parts by weight with respect to 100 parts by weight of the urethane prepolymer. Yes, 0.1 to 2.0 parts by weight is preferable. It is because the storage stability of the urethane prepolymer composition obtained will be excellent if it is in this range.
[0023]
The urethane prepolymer composition of the present invention can be produced by sufficiently kneading and uniformly dispersing the above essential compound under reduced pressure or in an inert atmosphere.
The urethane prepolymer composition of the present invention thus obtained can be stored as a one-pack type urethane prepolymer composition by adopting the above configuration, and has an excellent curing rate when taken out from a container. In addition, it can be stably stored during storage in a container and has excellent storage stability. Moreover, if it is used as a sealant, the storage stability of the one-pack type urethane sealant is high.
[0024]
The one-component urethane sealant of the present invention (hereinafter referred to as the sealant of the present invention) is a sealant containing the urethane prepolymer composition as a main component. Since the sealant of the present invention contains the urethane prepolymer composition, it has excellent curability and storage stability.
The sealant of the present invention can contain a silyl ester compound, a filler, a plasticizer, an antioxidant, a pigment, a silane coupling agent, a dispersant, a solvent and the like as long as the object of the present invention is not impaired.
[0025]
Here, the silyl ester compound refers to a silyl ester compound produced from carboxylic acid and silanol and having —Si— (OCOR) n at the molecular end. In the formula, R represents a hydrocarbon group having 1 to 20 carbon atoms, and n represents an integer of 1 to 3. Examples of such silyl ester compounds include compounds represented by the following formulas (7) and (8). In the following formula, p is about 30.
[Chemical 3]
In addition, a carboxylic acid having a long carbon chain binds to the surface of a filler, for example, a calcium carbonate filler, incorporated in the sealant, functions as a thixotropic agent, and imparts good thixotropy to the sealant.
The blending amount of the silyl ester compound having a long carbon chain having 10 to 20 carbon atoms is preferably 0.1 to 20 parts by weight with respect to 100 parts by weight of the urethane prepolymer composition. Is more preferable. It is because it is preferable from a viewpoint of storage stability as it is the said range.
[0026]
In the silyl ester compound, R is a hydrocarbon group having 1 to 9 carbon atoms. In the production process of the sealant of the present invention, preferably, the silyl ester compound having a long carbon chain is used. When added after the water in the compounding system is sufficiently removed, it is present in the compounded system in an ester state without being hydrolyzed, and hydrolyzed by moisture in the air when the sealant is used. The carboxylic acid generated at this time is a carboxylic acid having 1 to 9 carbon atoms and a short carbon chain. A carboxylic acid having a short carbon chain has a high acidity and activates an oxazolidine compound or an isocyanate group to promote a hydrolysis / curing reaction. Therefore, such a silyl ester compound having a short carbon chain functions as a latent fast curing catalyst that imparts fast curing properties without adversely affecting the storage stability of the sealant.
The blend amount of the silyl ester compound formula having a short carbon chain having 1 to 9 carbon atoms is preferably 0.01 to 10 parts by weight, preferably 0.1 to 5 parts by weight with respect to 100 parts by weight of the urethane prepolymer composition. Is more preferable. It is because it is preferable from a viewpoint of quick curability as it is the said range.
[0027]
Examples of the filler include surface-treated calcium carbonate, carbon black, clay, talc, titanium oxide, quicklime, kaolin, zeolite, diatomaceous earth, vinyl chloride paste resin, glass balloon, and vinylidene chloride resin balloon. These fillers can be used alone or in combination.
50-200 weight part is preferable with respect to 100 weight part of said urethane prepolymer compositions, and, as for the compounding quantity of a filler, 100-180 weight part is more preferable. It is because it is preferable from a viewpoint of quick curability as it is the said range.
[0028]
Examples of the plasticizer include dioctyl phthalate (DOP), dibutyl phthalate (DBP), dilauryl phthalate (DLP), dibutyl benzyl phthalate (BBP), dioctyl adipate, diisodecyl adipate, trioctyl phosphate, tris (chloroethyl) phosphate. , Tris (dichloropropyl) phosphate, propylene glycol adipate polyester, butylene glycol adipate polyester, alkyl epoxy stearate, epoxidized soybean oil and the like. These plasticizers can be used alone or in combination.
[0029]
Examples of the antioxidant include butylhydroxytoluene (BHT), butylhydroxycyanisol (BHA), diphenylamine, phenylenediamine, and triphenyl phosphite.
Examples of the pigment include inorganic pigments such as titanium dioxide, zinc oxide, ultramarine, petal, litbon, lead, cadmium, iron, cobalt, aluminum, hydrochloride and sulfate; organic pigments such as azo pigment and copper phthalocyanine pigment It is done.
Examples of the solvent include aromatic hydrocarbon solvents such as xylene and toluene.
[0030]
As a method for producing the sealant of the present invention, the above compound is preferably kneaded sufficiently under reduced pressure or under an inert atmosphere in accordance with the blending timing of the silyl ester compound, and uniformly dispersed to obtain a composition. Can show.
The sealant of the present invention thus obtained has not only excellent curability but also excellent storage stability, and can achieve both curability and storage stability. For this reason, the sealant of the present invention is suitable as a one-component sealant used for construction.
[0031]
【Example】
EXAMPLES Hereinafter, the present invention will be specifically described with reference to examples, but the present invention is not limited thereto.
[0032]
(Preparation of mixture of urethane prepolymer and oxazolidine compound)
500 parts by weight of polyoxypropylene triol having an average molecular weight of 6000 (produced by Asahi Glass Co., Ltd.) having 3 hydroxyl groups, 740 parts by weight of polyoxypropylene diol having an average molecular weight of 3000, and 536 parts by weight of dioctyl phthalate are placed in a reaction vessel. , 110 ° C. and 10 mmHg for 24 hours. Subsequently, 100 parts by weight of a mixture of 2,4-tolylene diisocyanate and 2,6-tolylene diisocyanate (mixing ratio, 2,4-TDI: 2,6-TDI = 80: 20) was added, and a nitrogen atmosphere was added. Under stirring at 80 ° C. for 6 hours, it was confirmed that the NCO group content was 1.06% by weight. 37 parts by weight of an oxazolidine compound represented by the following formula was added to the reaction solution, and the mixture was stirred for 2 hours at 60 ° C. in a nitrogen atmosphere, and a mixture of urethane prepolymer and oxazolidine compound (in the table, PPG / TDI / PHO urethane prepolymer) Was written).
[Formula 4]
Preparation and evaluation of urethane prepolymer composition The resulting mixture of urethane prepolymer and oxazolidine compound (PPG / TDI / PHO urethane prepolymer) and diethyl malonate, ethyl acetoacetate, nitroethane, or cyclopentadiene Were mixed at a blending ratio shown in Table 1 below to obtain a urethane prepolymer composition.
[0034]
Preparation and evaluation of one-pack type urethane sealant The obtained urethane prepolymer composition, surface-treated calcium carbonate (manufactured by Maruo Calcium Co., Ltd.), and silyl ester compound A represented by the above formula (7) The silyl ester compound B represented by the formula (8) was mixed at the blending ratio shown in Table 1 below to obtain a sealant.
[0035]
(Examples 1-11, Comparative Examples 1-2)
About the urethane prepolymer composition obtained as mentioned above, the viscosity change rate was measured and storage stability was evaluated. The acceptable range of storage stability was 1.00 to 1.50.
Moreover, about the sealant obtained as mentioned above, while evaluating storage stability, the rate of change of hardening time was measured and hardenability was evaluated. The acceptable range of storage stability of the sealant was 0.75 to 1.25, and the acceptable range of curability was 0.65 to 1.00.
[0036]
[Table 1]
(1) Viscosity change rate of urethane prepolymer composition (evaluation of storage stability)
Using an E-type viscometer 3 ° cone manufactured by Tokyo Keiki Co., Ltd., the initial viscosity and the viscosity after storage were measured under the conditions of 20 ° C. and 1 rpm / 10 rpm. The viscosity after storage was measured after the composition was left in an atmosphere of 80 ° C. for 24 hours. The ratio of the viscosity after storage to the initial viscosity was determined as the rate of change in viscosity.
(2) Viscosity change rate of 1-component urethane sealant (evaluation of storage stability)
BS Viscometer No. manufactured by Tokyo Keiki Co., Ltd. The initial viscosity and the viscosity after storage were measured using 7 rotors at 20 ° C. and 1 rpm / 10 rpm. The viscosity after storage was measured after the composition was left in an atmosphere at 70 ° C. for 24 hours. The ratio of the viscosity after storage to the initial viscosity was determined as the rate of change in viscosity.
(3) Curing time change rate (evaluation of curability)
Initial curing time and post-storage curing time were measured under the conditions of 20 ° C. and relative humidity 60%. The sealant was adhered to the polyethylene film, the time until adhesion did not occur was measured, and the time when adhesion did not occur was defined as the curing time. The curing time after storage was measured after leaving the sealant in an atmosphere at 70 ° C. for 24 hours. The ratio of the curing time after storage to the initial curing time was determined as the rate of change in curing time.
[0038]
【The invention's effect】
The urethane prepolymer composition of the present invention has a short curing time and is particularly excellent in storage stability. Therefore, the one-pack type urethane sealant of the present invention containing such a urethane prepolymer composition is excellent in curability and further excellent in storage stability. Therefore, the one-pack type urethane sealant of the present invention is fast after setting and can be applied quickly, and is useful as an architectural sealant having good workability even after long-term storage. It is.
Claims (2)
２）下記式（２）で表されるオキサゾリジン化合物を前記ウレタンプレポリマーのＮＣＯ当量に対し０．０５〜０．５当量と、
３）ジアルキルマロネート、アセト酢酸エステル、脂肪族ニトロ化合物、および、シクロペンタジエンからなる群より選択される少なくとも１つの化合物を前記ウレタンプレポリマー１００重量部に対し０．０１〜１０重量部含有するウレタンプレポリマー組成物。
2) and 0.05 to 0.5 equivalent of NCO equivalent of the urethane prepolymer oxazolidine compound represented by the following following formula (2),
3) Urethane containing 0.01 to 10 parts by weight of at least one compound selected from the group consisting of dialkyl malonate, acetoacetate, aliphatic nitro compound, and cyclopentadiene with respect to 100 parts by weight of the urethane prepolymer. Prepolymer composition.