JP3512481B2 - Toilet paper for flush toilet with washing device - Google Patents
Toilet paper for flush toilet with washing deviceInfo
- Publication number
- JP3512481B2 JP3512481B2 JP20082194A JP20082194A JP3512481B2 JP 3512481 B2 JP3512481 B2 JP 3512481B2 JP 20082194 A JP20082194 A JP 20082194A JP 20082194 A JP20082194 A JP 20082194A JP 3512481 B2 JP3512481 B2 JP 3512481B2
- Authority
- JP
- Japan
- Prior art keywords
- toilet
- paper
- wet
- toilet paper
- washing device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】
【０００１】
【産業上の利用分野】本願発明は、洗浄装置付き水洗ト
イレ用トイレットペーパーに関するものである。
【０００２】
【従来の技術】近年、衛生上の理由から洗浄装置付き水
洗トイレが普及してきている。この場合、お尻を洗浄し
た後、温風により乾燥することができるものも知られて
いるが、短時間の温風乾燥では完全な乾燥状態が得られ
ないなどの理由で、トイレットペーパーにより拭き取り
たいという要求がある。
【０００３】ところが、従来から使用されているトイレ
ットペーパーは、使用後において水に容易に溶けること
を主眼に製造されているため、濡れたお尻を拭くとすぐ
破れてしまい、洗浄装置付き水洗トイレ用としては不向
きである。一方、ティッシュペーパーやペーパータオル
などにおいて従来使用されている湿潤紙力増強剤は、湿
潤紙の強度強化には有効であるが、水洗した場合におい
てトイレットペーパーに不可欠な水にほぐれる特性が失
われる。
【０００４】ところで、イオン性を有するポリビニルア
ミド共重合体と二価アルデヒドとの反応により得られる
熱硬化性樹脂が紙の湿潤紙力増強剤として有効であり、
しかもこの樹脂で湿潤紙力を付加した紙は水に小時間浸
すことにより加水分解することが知られている（例え
ば、特公昭４４ー２６６７０号公報、特公昭５６ー１５
７４０３号公報参照）。
【０００５】
【発明が解決しようとする課題】洗浄装置付き水洗トイ
レ用のトイレットペーパーは、濡れた肌を拭き取るのに
耐える特性と、便器に流した時に水にほぐれる特性とを
同時に要求される。
【０００６】上記した湿潤紙力増強剤をトイレットペー
パーに混入することにより、洗浄装置付き水洗トイレ用
として使用に耐えるものとすることが考えられるが、ト
イレットペーパーには、下記のような日本工業規格が定
められており、当該規格に合致することが要求される。
特にその品質として、「ほぐれやすさ」の規格を満たす
必要がある。
【０００７】即ち、トイレットペーパーの品質について
は、「衛生的で適度の柔軟性があり、水にほぐれやす
く、すきむら、破れ、穴など使用上の欠点がなく、表１
の規定に適合しなければならない」と定められている。
【０００８】
【表１】
【０００９】この「ほぐれやすさ」の試験は、水３００
ｍｌ（水温２０±５℃）を入れた３００ｍｌのビーカー
をマグネチックスターラーに載せ、回転子（直径３５ｍ
ｍ、厚さ１２ｍｍの円盤）の回転数を６００±１０回転
／分となるように調整し、その中に一辺が１１４±２ｍ
ｍ角の試験片を投入して行われ、回転開始時点から前記
回転子の回転数が一旦約５００回転／分に下降した後、
再び５４０回転／分まで回復した時点までの時間を秒単
位で表示するようにしている。なお、「ほぐれやすさ」
の結果は５回の試験の平均値で表すこととなっている。
【００１０】ところで、トイレットペーパーに湿潤紙力
増強剤を混入して湿潤紙力を増強する場合、単に湿潤紙
力が増強されればよいのではなく、上記した規格をクリ
アするためには、湿潤紙力増強されたトイレットペーパ
ーが「ほぐれやすさ」を有するものでなければならな
い。そのためには、トイレットペーパーにおける湿潤紙
力増強剤の含有量を最適に調整する必要がある。
【００１１】本願発明は、上記の点に鑑みてなされたも
ので、濡れたお尻を拭いてもすぐに破れることなく、し
かも使用後において容易に水に溶け得るようなトイレッ
トペーパーを提供することを目的とするものである。
【００１２】
【課題を解決するための手段】本願発明のトイレットペ
ーパーは、陽イオン性アルデヒド変成ポリアクリルアミ
ド系共重合体を乾燥状態において０．０５％〜０．２％
の含有量で含有せしめてなり、ほぐれやすさが１００秒
以内とされていることを特徴としている。
【００１３】
【作用】本願発明のトイレットペーパーは、陽イオン性
アルデヒド変成ポリアクリルアミド系共重合体を適正な
混入率で混入したことにより、湿潤紙力が増強され、濡
れたお尻を拭いた場合であってもすぐに破れるというこ
とがない。しかも、陽イオン性アルデヒド変成ポリアク
リルアミド系共重合体は水素イオンの存在により容易に
分解して湿潤強度剤としての機能が低下するところか
ら、使用後に水道水に浸されると従来のトイレットペー
パーと同様に短時間で溶けてしまい、トイレットペーパ
ーにおける「ほぐれやすさ」に関するＪＩＳ規格である
１００秒以内をクリアできる。
【００１４】なお、陽イオン性アルデヒド変成ポリアク
リルアミド系共重合体は極めて少量添加しても湿潤紙力
増強作用が得られるが、湿潤紙力増強効果により破れに
くさが得られる望ましい範囲を勘案すると、０．０５％
を添加量の下限とするのがより望ましい。また、陽イオ
ン性アルデヒド変成ポリアクリルアミド系共重合体の含
有量が０．２％を超えた場合、湿潤紙力増強作用が高く
なり過ぎて「ほぐれやすさ」に関するＪＩＳ規格である
１００秒以内を満足することができなくなる。
【００１５】
【発明の効果】本願発明によれば、トイレットペーパー
に、湿潤紙力増強剤として作用する陽イオン性アルデヒ
ド変成ポリアクリルアミド系共重合体を適量に（即ち、
０．０５％〜０．２％の含有量で）含有させてなり、ほ
ぐれやすさが１００秒以内とされているので、濡れたお
尻を拭いた程度ではすぐに破れず、使用後に水道水に浸
されると容易に溶けることとなり、洗浄装置付き水洗ト
イレ用として最適なものとなるという優れた効果があ
る。
【００１６】
【実施例】以下、本願発明を実施例および比較例により
詳細に説明する。
【００１７】濃度５ｇ／ｌのパルプ液に、下記式（１）
で表される共重合体と下記式（２）で表される２価アル
デヒドとの反応により得られる易溶解性熱硬化性樹脂
（即ち、陽イオン性アルデヒド変成ポリアクリルアミド
系共重合体）水溶液を乾燥紙あたり０．２％添加し、丸
型抄紙機を使用して抄紙した後脱水プレスを行い、その
後熱板プレスを使用して乾燥し、易溶解性熱硬化性樹脂
を含有するトイレットペーパーが得られた。このように
して得られたトイレットペーパーは、下記式（３）に示
すように、該樹脂の作用により繊維間が結合され湿潤強
度を有する。しかも、水に小時間浸すと、該樹脂は下記
式（４）、（５）、（６）に示すように加水分解するこ
とが知られており、湿潤紙力増強剤としての機能が低下
し、容易に溶解する。
【００１８】
【数１】
【００１９】
【数２】
【００２０】
【数３】
【００２１】
【数４】
【００２２】
【数５】【００２３】
【数６】
【００２４】ところで、陽イオン性アルデヒド変成ポリ
アクリルアミド系共重合体の含有量が、トイレットペー
パーにおける湿潤紙力増強に寄与する度合い、トイレッ
トペーパーの「ほぐれやすさ」の度合いに大きく影響す
る。
【００２５】そこで、上記実施例の他に、陽イオン性ア
ルデヒド変成ポリアクリルアミド系共重合体の含有量を
種々変更したトイレットペーパーを試作し、従来のトイ
レットペーパー（即ち、陽イオン性アルデヒド変成ポリ
アクリルアミド系共重合体を含有しないもの）と比較し
たところ、下記表２および表３の結果が得られた。ここ
で、表２には、「ほぐれやすさ」試験の結果が示されて
おり、表３には、湿潤時の裂断長試験の結果が示されて
いる。なお、「ほぐれやすさ」試験は、米坪量２２ｇ／
ｍ2のトイレットペーパーを水と接触させた後、前述し
た試験法により行い、裂断長試験は、米坪量２２ｇ／ｍ
2のトイレットペーパーを水と接触させた後、ＪＩＳ−
Ｐ−８１３５の試験法に準拠して行った。
【００２６】
【表２】
【００２７】
【表３】【００２８】ここで、裂断長（ｋｍ）＝｛引張強度（ｋ
ｇ）／試験片の幅（ｍ）｝／試験片の坪量（ｋｇ／
ｍ2）×１０００とされる。
【００２９】「ほぐれやすさ」評価の上限は、湿潤時間
に関係なく１００秒（ＪＩＳ規格）とされ、裂断長評価
の下限は、湿潤時間０分で０．１（ｋｍ）程度とされ
る。
【００３０】上記結果によれば、陽イオン性アルデヒド
変成ポリアクリルアミド系共重合体を極めて少量（例え
ば、０．０１％）添加しても陽イオン性アルデヒド変成
ポリアクリルアミド系共重合体による湿潤紙力増強作用
が得られることが分かる。また、陽イオン性アルデヒド
変成ポリアクリルアミド系共重合体の含有量が０．２％
を超えると、湿潤紙力増強作用が高くなり過ぎて「ほぐ
れやすさ」に関するＪＩＳ規格を満足することができな
くなることが分かる。
【００３１】上記の結果を勘案すると、陽イオン性アル
デヒド変成ポリアクリルアミド系共重合体の含有量を
０．２％以下（望ましくは、０．０１〜０．２％）とし
たものが、洗浄装置付き水洗トイレ用トイレットペーパ
ーとして適していることが分かるが、湿潤紙力増強効果
により破れにくさが得られる望ましい範囲を勘案する
と、湿潤時間１分で０．１５ｋｍの裂断長が得られる
０．０５％を添加量の下限とするのがより望ましい。Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to toilet paper for flush toilets with a washing device. 2. Description of the Related Art In recent years, flush toilets with a washing device have become widespread for sanitary reasons. In this case, it is known that the buttocks can be dried with warm air after washing the buttocks.However, it is not possible to obtain a completely dry state with a short time hot air drying, so that it is wiped off with toilet paper. There is a demand to want. [0003] However, the toilet paper which has been conventionally used is manufactured mainly for the purpose of easily dissolving in water after use, so that it is torn immediately when a wet ass is wiped, and the flush toilet with a washing device is provided. Not suitable for use. On the other hand, a wet paper strength enhancer conventionally used in tissue paper and paper towels is effective in enhancing the strength of wet paper, but loses the property of loosening water that is essential for toilet paper when washed with water. Meanwhile, a thermosetting resin obtained by reacting an ionic polyvinyl amide copolymer with a dihydric aldehyde is effective as a wet paper strength enhancer for paper.
Further, it is known that paper to which wet paper strength is applied with this resin is hydrolyzed by immersing it in water for a short time (for example, Japanese Patent Publication No. 44-26670, Japanese Patent Publication No. 56-15).
7403). [0005] Toilet paper for flush toilets with a washing device is required to have the property of withstanding the wiping of wet skin and the property of unraveling with water when flushed into the toilet. [0006] By mixing the above-mentioned wet paper strength enhancer into toilet paper, it is conceivable that the paper can be used for flush toilets with a washing device. Toilet paper has the following Japanese Industrial Standards. And it is required to conform to the standard.
In particular, the quality must meet the standard of "easiness of loosening". [0007] That is, regarding the quality of the toilet paper, it is described in Table 1 that it is sanitary, has a moderate flexibility, is easily loosened with water, has no drawbacks in use such as gaps, tears and holes.
It must conform to the provisions of ". [Table 1] [0009] The test of "easiness of loosening"
ml (water temperature 20 ± 5 ° C.) was placed on a magnetic stirrer and placed in a rotor (35 m in diameter).
m, a disk having a thickness of 12 mm) is adjusted to be 600 ± 10 rotations / minute, and one side is 114 ± 2 m.
The test was performed by inserting a test piece of m-square, and after the rotation speed of the rotor once decreased to about 500 rotations / minute from the start of rotation,
The time until recovery to 540 revolutions / minute is displayed in seconds. In addition, "easiness of loosening"
Are to be expressed as the average of five tests. When the wet paper strength is enhanced by mixing a wet paper strength enhancer into the toilet paper, the wet paper strength is not merely increased, but the wet paper strength is required to meet the above-mentioned standard. The strengthened toilet paper must have "easiness of loosening". For that purpose, it is necessary to optimally adjust the content of the wet strength agent in the toilet paper. [0011] The present invention has been made in view of the above points, and provides a toilet paper that does not tear immediately after wiping a wet ass and that can be easily dissolved in water after use. The purpose is. [0012] The toilet paper of the present invention comprises a cationic aldehyde-modified polyacrylamide copolymer in a dry state of 0.05% to 0.2%.
And the ease of loosening is set to within 100 seconds. The toilet paper of the present invention has a wet paper strength which is enhanced by mixing a cationic aldehyde-modified polyacrylamide-based copolymer at an appropriate mixing ratio. Even if it does not break immediately. Moreover, the cationic aldehyde-modified polyacrylamide-based copolymer is easily decomposed due to the presence of hydrogen ions and deteriorates in function as a wet strength agent. Similarly, it melts in a short time, and can clear the JIS standard for toilet paper within 100 seconds, which is the standard for ease of loosening. Although the cationic aldehyde-modified polyacrylamide-based copolymer can provide an effect of enhancing wet paper strength even when it is added in a very small amount, taking into consideration a desirable range in which tearing is obtained by the effect of enhancing wet paper strength. , 0.05%
Is more preferably set as the lower limit of the addition amount. Further, when the content of the cationic aldehyde-modified polyacrylamide-based copolymer exceeds 0.2%, the wet paper strength enhancing effect becomes too high, and the JIS standard of “frayability” is within 100 seconds. You cannot be satisfied. According to the present invention, a proper amount of a cationic aldehyde-modified polyacrylamide copolymer acting as a wet paper strength agent is added to toilet paper (ie,
(With a content of 0.05% to 0.2%) and the ease of loosening is assumed to be within 100 seconds. When it is immersed in water, it is easily melted and has an excellent effect that it is most suitable for a flush toilet with a washing device. The present invention will be described below in detail with reference to examples and comparative examples. The following formula (1) is added to a pulp solution having a concentration of 5 g / l.
An aqueous solution of an easily soluble thermosetting resin (that is, a cationic aldehyde-modified polyacrylamide copolymer) obtained by reacting a copolymer represented by the following formula with a divalent aldehyde represented by the following formula (2): After adding 0.2% per dry paper, making paper using a round paper machine, performing dehydration pressing, and then drying using a hot plate press, toilet paper containing easily soluble thermosetting resin is obtained. Obtained. In the toilet paper thus obtained, as shown in the following formula (3), the fibers are bonded by the action of the resin and have wet strength. Moreover, it is known that when immersed in water for a short time, the resin hydrolyzes as shown in the following formulas (4), (5) and (6), and the function as a wet paper strength enhancer is reduced. Dissolves easily. ## EQU1 ## [Equation 2] [Equation 3] [Equation 4] ## EQU5 ## [Equation 6] Incidentally, the content of the cationic aldehyde-modified polyacrylamide-based copolymer greatly affects the degree of contributing to the enhancement of wet paper strength in toilet paper and the degree of "easiness of loosening" of toilet paper. Therefore, in addition to the above examples, toilet papers having various contents of the cationic aldehyde-modified polyacrylamide-based copolymer were experimentally produced, and conventional toilet papers (ie, cationic aldehyde-modified polyacrylamide) were produced. As a result, the results shown in Tables 2 and 3 below were obtained. Here, Table 2 shows the results of the “easiness of loosening” test, and Table 3 shows the results of the tear length test when wet. The "easiness of loosening" test was based on a rice basis weight of 22 g /
After contacting the m 2 toilet paper with water, the test was performed according to the test method described above.
After contacting the toilet paper of No. 2 with water, JIS-
It carried out based on the test method of P-8135. [Table 2] [Table 3] Here, the breaking length (km) = ｛tensile strength (k
g) / width of test piece (m)｝ / basis weight of test piece (kg /
m 2 ) × 1000. The upper limit of the evaluation of "easiness of loosening" is 100 seconds (JIS standard) regardless of the wet time, and the lower limit of the evaluation of the breaking length is about 0.1 (km) when the wet time is 0 minute. . According to the above results, even when an extremely small amount (for example, 0.01%) of the cationic aldehyde-modified polyacrylamide copolymer is added, the wet paper strength of the cationic aldehyde-modified polyacrylamide copolymer is increased. It can be seen that an enhancing effect is obtained. Further, the content of the cationic aldehyde-modified polyacrylamide copolymer is 0.2%.
It can be seen that, when it exceeds, the wet paper strength enhancing effect becomes too high and the JIS standard regarding “easiness of loosening” cannot be satisfied. Taking the above results into consideration, the cleaning apparatus in which the content of the cationic aldehyde-modified polyacrylamide-based copolymer is 0.2% or less (preferably 0.01 to 0.2%) is used. It can be seen that it is suitable as toilet paper for flush toilets, but in consideration of a desirable range in which it is difficult to tear due to a wet paper strength enhancing effect, a tearing length of 0.15 km can be obtained in 1 minute of wet time. More preferably, the lower limit of the addition amount is 05%.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭48−24005（ＪＰ，Ａ) 特開 平２−124912（ＪＰ，Ａ) 特開 平２−124911（ＪＰ，Ａ) 特開 平６−101191（ＪＰ，Ａ) 特開 平６−184985（ＪＰ，Ａ) ────────────────────────────────────────────────── ─── Continuation of front page (56) References JP-A-48-24005 (JP, A) JP-A-2-124912 (JP, A) JP-A-2-124911 (JP, A) JP-A-6-101191 (JP, A) JP-A-6-184985 (JP, A)
Claims (1)
アミド系共重合体を乾燥状態において０．０５％〜０．
２％の含有量で含有せしめてなり、ほぐれやすさが１０
０秒以内とされていることを特徴とする洗浄装置付き水
洗トイレ用トイレットペーパー。(57) [Claims 1] The cationic aldehyde-modified polyacrylamide-based copolymer is dried at 0.05% to 0.1%.
Ri Na and the additional inclusion in the content of 2%, is unraveling ease 10
For cleaning apparatus with a flush toilet and it said that you have been within 0 seconds toilet paper.