JP3126804B2 - Manufacturing method of waterproof sheet - Google Patents
Manufacturing method of waterproof sheetInfo
- Publication number
- JP3126804B2 JP3126804B2 JP04104894A JP10489492A JP3126804B2 JP 3126804 B2 JP3126804 B2 JP 3126804B2 JP 04104894 A JP04104894 A JP 04104894A JP 10489492 A JP10489492 A JP 10489492A JP 3126804 B2 JP3126804 B2 JP 3126804B2
- Authority
- JP
- Japan
- Prior art keywords
- waterproof sheet
- polymer cement
- base fabric
- polymer
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、特に、各種構築物、特
に一般家屋の屋根の防水に効果的に使用できる防水シー
トの製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a waterproof sheet which can be effectively used for waterproofing various structures, particularly roofs of ordinary houses.
【０００２】[0002]
【従来の技術】従来、一般家屋の屋根構造として、コン
クリート製の屋根材の外面に防水シートを貼着したもの
がある。2. Description of the Related Art Conventionally, as a roof structure of a general house, there is a structure in which a waterproof sheet is attached to an outer surface of a roof material made of concrete.
【０００３】かかる防水シートとして、その防水効果を
高めるために、複数の合成樹脂層からなるラミネートシ
ート等の完全防水シートが用いられている。As such a waterproof sheet, a complete waterproof sheet such as a laminate sheet comprising a plurality of synthetic resin layers is used in order to enhance the waterproof effect.
【０００４】[0004]
【発明が解決しようとする課題】しかし、かかる従来の
防水シートは、未だ、以下の解決すべき課題を有してい
た。However, such a conventional waterproof sheet still has the following problems to be solved.
【０００５】即ち、かかるラミネートシートからなる防
水シートは、一般に、その表面が平滑であるため、作業
者が、屋根の野地板にラミネートシートを釘等で取付け
る際、滑って屋根から地上へ落下するといった事故も発
生していた。[0005] That is, the waterproof sheet made of such a laminate sheet generally has a smooth surface, so that when the worker attaches the laminate sheet to the roof base plate with nails or the like, the waterproof sheet slips from the roof to the ground. Such accidents had also occurred.
【０００６】また、ラミネートシートは、水の透過を防
止するのみならず、空気の透過も完全に遮断するもので
ある。The laminate sheet not only prevents the permeation of water but also completely blocks the permeation of air.
【０００７】従って、一般家屋の屋根材がコンクリート
製の場合、屋根材の内部の水分が水蒸気として上方に抜
けようとしても、防水シートによって外部への放出が阻
害されるので、水蒸気が防水シートを上方に押上げ、防
水シートを破ることにもなっていた。[0007] Therefore, when the roof material of a general house is made of concrete, even if the water inside the roof material tries to escape upward as water vapor, the release to the outside is hindered by the waterproof sheet. He had to push it up and break the tarpaulin.
【０００８】本発明は、上記した課題を解決することが
できる防水シートの製造方法を提供することを目的とす
る。An object of the present invention is to provide a method for manufacturing a waterproof sheet which can solve the above-mentioned problems.
【０００９】[0009]
【課題を解決するための手段】本発明は、目の粗い基布
の一側側面にポリマーセメントを塗布し、基布の多数の
隙間を通してポリマーセメントを基布の他側側面より突
出させて多数の小突起を形成し、かつ、基布の一側側面
に塗布したポリマーセメントの表面に、アスファルト乳
剤又はアルファルトゴムを塗布して製造することを特徴
とする防水シートの製造方法に係るものである。SUMMARY OF THE INVENTION According to the present invention, a polymer cement is applied to one side surface of a coarse base fabric, and the polymer cement is projected from the other side surface of the base fabric through a plurality of gaps in the base fabric. The method according to the present invention relates to a method for producing a waterproof sheet, characterized in that asphalt emulsion or alphalt rubber is applied to the surface of a polymer cement applied to one side surface of a base fabric to form small projections. is there.
【００１０】上記方法において用いる基布としては、通
気性の優れた織布や不織布を好適に用いることができ
る。As the base fabric used in the above method, a woven fabric or a nonwoven fabric having excellent air permeability can be suitably used.
【００１１】また、ポリマーセメントは、酸化珪素、酸
化カルシウム、酸化鉄を主成分とした主材に、少なくと
もアクリル酸エステル共重合体を主成分としてなる複合
ポリマーエマルジョンを混和して生成したものを用いる
ことができる。The polymer cement is obtained by mixing a main polymer mainly composed of silicon oxide, calcium oxide and iron oxide with a composite polymer emulsion mainly composed of at least an acrylate copolymer. be able to.
【００１２】[0012]
【実施例】以下、添付図である図１〜図４に示す実施例
を参照して、本発明に係る防水シートの製造方法を、具
体的に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A method for manufacturing a waterproof sheet according to the present invention will be specifically described below with reference to the accompanying drawings shown in FIGS.
【００１３】まず、図１に示すように、目の粗い基布10
を用意する。かかる基布10の大きさ、形状、厚みは、屋
根の基布貼着面の大きさや形状に合わせて任意に選択す
ることができる。First, as shown in FIG.
Prepare The size, shape, and thickness of the base cloth 10 can be arbitrarily selected according to the size and shape of the base cloth bonding surface of the roof.
【００１４】また、基布10は、シート状、ロール状のい
ずれでも用意しておくことができ、ロール状とした場合
は、倉庫管理や搬送に便宜である。The base fabric 10 can be prepared in either a sheet form or a roll form. When the base cloth 10 is formed in a roll form, it is convenient for warehouse management and transportation.
【００１５】また、好ましくは、基布10は、ガラス繊維
や、ナイロン、ポリエステル、ポリアミド等の合成樹脂
繊維等を素材とした織布や不織布を用いる。Preferably, the base fabric 10 is made of a woven or nonwoven fabric made of glass fiber, synthetic resin fiber such as nylon, polyester, or polyamide.
【００１６】次に、図２に示すように、リシンガン等の
吹付装置を用いて、後述するポリマーセメント11を、目
の粗い基布10の一側側面に塗布する。同塗布によって、
ポリマーセメント11の一部が基布10の多数の目、即ち、
間隙を通して、基布10の他側側面から突出し、ポリマー
セメント11からなる多数の突起11a を形成することがで
きた。Next, as shown in FIG. 2, a polymer cement 11, which will be described later, is applied to one side surface of the coarse base cloth 10 by using a spraying device such as a ricin gun. By the same application,
A part of the polymer cement 11 has a large number of eyes of the base fabric 10, that is,
A large number of protrusions 11a made of the polymer cement 11 were projected from the other side surface of the base cloth 10 through the gap.
【００１７】さらに、上記した突起11a が十分に硬化し
た後、図３に示すように、アスファルト乳剤12又はアス
ファルトゴムを、基布10の一側側面に塗布したポリマー
セメント11上にリシンガン装置を用いて吹付ける。この
吹付によって、アスファルト乳剤12は、ポリマーセメン
ト11上にさらにアスファルト塗膜を形成して防水シート
Ａを製造することができる。Further, after the above-mentioned projections 11a are sufficiently hardened, as shown in FIG. Spray. By this spraying, the asphalt emulsion 12 can further form an asphalt coating film on the polymer cement 11 to manufacture the waterproof sheet A.
【００１８】なお、ポリマーセメント11とアスファルト
乳剤12の塗膜の厚さは、それぞれ、水の通過を確実に防
止することができるとともに、空気の円滑な通過は確保
できる厚さ、例えば、0.2 〜0.8 mmとするのが好まし
い。The thicknesses of the coating films of the polymer cement 11 and the asphalt emulsion 12 are each such that the passage of water can be reliably prevented and the smooth passage of air can be ensured. It is preferably 0.8 mm.
【００１９】その後、図４及び図５に示すように、上記
した防水シートＡを、反転した状態で、釘14によって、
コンクリート製又は木製の野地板からなる屋根材13に貼
着する。Then, as shown in FIG. 4 and FIG. 5, the waterproof sheet A is
It is attached to a roofing material 13 made of a concrete or wooden board.
【００２０】かかる防水シートＡは、その表面に多数の
突起11a を具備しており、これが滑り止め機能を発揮す
るので、作業者は、防水シートＡ上での瓦葺き作業等を
極めて安全に行うことができる。The waterproof sheet A has a large number of projections 11a on its surface, which exerts a non-slip function, so that the worker can perform the roofing work or the like on the waterproof sheet A extremely safely. Can be.
【００２１】また、上記した防水シートＡに塗布したポ
リマーセメント11やアスファルト乳剤12は、それぞれ、
十分な防水機能を有する一方で、適当な通気性を有す
る。The polymer cement 11 and the asphalt emulsion 12 applied to the waterproof sheet A are respectively
While having a sufficient waterproof function, it has a suitable air permeability.
【００２２】従って、防水シートＡは、雨水等の屋根材
13を通した構造物内部への侵入を確実に防止することが
できるとともに、コンクリート製の屋根材13の内部から
同屋根材13の表面に上昇して水蒸気を、速やかに通過さ
せて、大気中に放出することができ、シート内部滞留水
蒸気による防水シートＡの破損も確実に防止することが
できる。Therefore, the waterproof sheet A is made of a roof material such as rainwater.
13 can be reliably prevented from entering the interior of the structure, and from the interior of the concrete roofing material 13, rising to the surface of the roofing material 13, water vapor can be quickly passed, and The waterproof sheet A can be reliably prevented from being damaged due to water vapor retained inside the sheet.
【００２３】さらに、アスファルト乳剤12の特性によっ
て、防水シートＡが釘14に弾性的に絡まるので、同釘打
付部を通しての水の侵入も確実に防止することができ
る。Further, the waterproof sheet A is elastically entangled with the nail 14 due to the properties of the asphalt emulsion 12, so that the intrusion of water through the nail driving portion can be reliably prevented.
【００２４】また、基布10は可撓性を有するものとした
場合、アスファルト乳剤12も一定の伸縮性を有するの
で、ビル等の屋根材13の表面が曲面をなしている場合で
あっても、容易に、同屋根材13表面に沿って防水シート
Ａを貼着することができる。When the base cloth 10 is flexible, the asphalt emulsion 12 also has a certain elasticity, so that even if the surface of the roofing material 13 such as a building has a curved surface, The waterproof sheet A can be easily stuck along the surface of the roofing material 13.
【００２５】なお、上記した防水シートＡの製造方法に
用いるポリマーセメントとしては、例えば、酸化珪素、
酸化カルシウム、酸化鉄を主成分とした主材に、少なく
ともアクリル酸エステル共重合体を主成分としてなる複
合ポリマーエマルジョンを混和して生成したものを用い
ることができ、以下に、具体的成分及び配合割合を示
す。The polymer cement used in the method for producing the waterproof sheet A is, for example, silicon oxide,
A mixture obtained by mixing at least a composite polymer emulsion mainly composed of an acrylate ester copolymer with a main material mainly composed of calcium oxide and iron oxide can be used. Indicates the ratio.
【００２６】本実施例では、ポリマーエマルジョンとし
て、以下の組成を有する複合ポリマーエマルジョンＰを
用いた。In this embodiment, a composite polymer emulsion P having the following composition was used as the polymer emulsion.
【００２７】（複合ポリマーエマルジョンＰ) （実施例１） （実施例２） そして、上記した組成を有する複合ポリマーエマルジョ
ンＰと以下の組成を有する主剤Ｍとを混合してポリマー
セメントを製造した。(Composite Polymer Emulsion P) (Example 1) (Example 2) Then, a polymer cement was manufactured by mixing the composite polymer emulsion P having the above-described composition and the base material M having the following composition.
【００２８】（主剤Ｍ) なお、上記白色セメントの成分重量比は、以下の通りで
あった。(Main agent M) The component weight ratio of the white cement was as follows.
【００２９】 また、上記した主剤Ｍに代えて、砂とセメントを混合し
たモルタルを用いることができる。[0029] In addition, mortar obtained by mixing sand and cement can be used in place of the main agent M described above.
【００３０】そして、複合ポリマーエマルジョンＰを攪
拌容器に入れ、主剤Ｍを徐々に加えながらハンドミキサ
ーで攪拌し、ポリマーセメントを製造した。Then, the composite polymer emulsion P was placed in a stirring vessel, and the mixture was stirred with a hand mixer while gradually adding the base material M, thereby producing a polymer cement.
【００３１】なお、ポリマーセメントの配合比は、複合
ポリマーエマルジョンＰの１重量部に対して、主剤Ｍを
３〜５重量部とすることが望ましい。本実施例では、
１：４であった。The compounding ratio of the polymer cement is desirably 3 to 5 parts by weight of the main agent M to 1 part by weight of the composite polymer emulsion P. In this embodiment,
1: 4.
【００３２】なお、基布10と、ポリマーセメント11と、
アスファルト乳剤12とからなる本発明の防水シートＡに
ついて、気体通過試験及び防水試験を行ったので、その
結果を以下に示す。The base cloth 10, the polymer cement 11,
A gas passage test and a waterproof test were performed on the waterproof sheet A of the present invention comprising the asphalt emulsion 12, and the results are shown below.
【００３３】なお、気体通過試験はＪＩＳ Ｋ7126- Ａ
法 (差圧法) に基づいて、防水試験はＪＩＳ Ｋ6328に
基づいて行った。また、試料ａ, ｂ, ｃ, ｄ, ｅは、そ
れぞれ、ナイロン織布からなる厚さ0.2 mmの基布10に、
ポリマーセメント11と、アスファルト乳剤12との積層厚
みを0.3 mmとしたものを用いた。The gas passage test was performed according to JIS K7126-A.
The waterproof test was performed based on JIS K6328 based on the pressure method (differential pressure method). Samples a, b, c, d, and e were respectively placed on a 0.2 mm thick base cloth 10 made of nylon woven cloth.
A polymer cement 11 and an asphalt emulsion 12 having a laminated thickness of 0.3 mm were used.
【００３４】 (気体通過試験)(試験気体: 空気) (気体透過度 ml/m2・24h ・atm) 試料ａ 10000以上 試料ｂ 10000以上 試料ｃ 10000以上 試料ｄ 10000以上 試料ｅ 10000以上 (防水試験)全ての試料ａ〜ｅについて 1kfg/cm2 で１分
間保持したが、漏水その他の異常は認められなかった。(Gas passage test) (Test gas: air) (Gas permeability ml / m 2 · 24h · atm) Sample a 10,000 or more Sample b 10,000 or more Sample c 10,000 or more Sample d 10,000 or more Sample e 10,000 or more (Waterproof test ) All samples a to e were kept at 1 kfg / cm 2 for 1 minute, but no water leakage or other abnormalities were observed.
【００３５】このように、以上の試験結果からも明らか
なように、本発明に係る防水シートＡは、十分な防水機
能を有する一方で、適当な通気性を有し、防水シートと
して好適に用いることができる。As is clear from the above test results, the waterproof sheet A according to the present invention has a sufficient waterproof function, has appropriate air permeability, and is suitably used as a waterproof sheet. be able to.
【００３６】[0036]
【発明の効果】上記したように、本発明に係る防水シー
トは、目の粗い基布の一側側面にポリマーセメントを塗
布し、基布の多数の隙間を通してポリマーセメントを基
布の他側側面より突出させて多数の小突起を形成し、か
つ、基布の一側側面に塗布したポリマーセメントの表面
に、アスファルト乳剤又はアルファルトゴムを塗布して
製造することにしている。As described above, in the waterproof sheet according to the present invention, the polymer cement is applied to one side of the coarse base cloth, and the polymer cement is applied to the other side of the base cloth through a number of gaps in the base cloth. A plurality of small projections are formed by projecting the asphalt emulsion or asphalt rubber on the surface of the polymer cement applied to one side surface of the base fabric.
【００３７】従って、以下の効果を奏する。Therefore, the following effects are obtained.
【００３８】 防水シートは、その一側表面に多数の
突起を具備しており、これが滑り止め機能を発揮するの
で、作業者は、一般家屋等における防水シート上での瓦
葺き作業等を極めて安全に行うことができる。The waterproof sheet has a large number of protrusions on one side surface thereof, which exerts a non-slip function. Therefore, the worker can perform the roofing work or the like on the waterproof sheet in a general house or the like extremely safely. It can be carried out.
【００３９】 防水シートに含浸させたポリマーセメ
ント及びアスファルト乳剤は、それぞれ、十分な防水機
能を有する一方で、適当な通気性を有する。従って、防
水シートは、雨水等の構造物内部への侵入を確実に防止
することができるとともに、コンクリート製や木製の屋
根材等の内部から同屋根材等の表面に上昇して水蒸気
を、速やかに通過させて、大気中に放出することがで
き、シート内部滞留水蒸気による防水シートの破損も確
実に防止することができる。The polymer cement and the asphalt emulsion impregnated in the waterproof sheet each have a sufficient waterproof function, and have appropriate air permeability. Therefore, the waterproof sheet can surely prevent rainwater or the like from entering the inside of the structure, and can quickly move water vapor from the inside of the concrete or wooden roof material to the surface of the roof material. , And can be released to the atmosphere, and the waterproof sheet can be reliably prevented from being damaged by water vapor retained in the sheet.
【００４０】基布は可撓性を有するとともに、ポリマ
ーセメントとアスファルト乳剤等も一定の伸縮性を有す
るので、ビル等の屋根材等が曲面をなしている場合であ
っても、容易に、同壁面に沿って防水シートを貼着する
ことができる。Since the base fabric is flexible and the polymer cement and the asphalt emulsion have a certain elasticity, even if the roofing material of a building or the like has a curved surface, the same can be easily obtained. A waterproof sheet can be attached along the wall surface.
【００４１】[0041]
【図１】本発明に係る防水シートの製造方法の工程説明
図である。FIG. 1 is a process explanatory view of a method for producing a waterproof sheet according to the present invention.
【図２】本発明に係る防水シートの他の貼着方法の説明
図である。FIG. 2 is an explanatory view of another method of attaching a waterproof sheet according to the present invention.
【図３】本発明に係る防水シートの製造方法の工程説明
図である。FIG. 3 is a process explanatory view of a method for producing a waterproof sheet according to the present invention.
【図４】本発明に係る防水シートの屋根材への取付状態
説明図である。FIG. 4 is an explanatory view showing a state in which a waterproof sheet according to the present invention is attached to a roof material.
【図５】取付状態の拡大説明図である。FIG. 5 is an enlarged explanatory view of an attached state.
Ａ 防水シート 10 基布 11 ポリマーセメント 12 アスファルト乳剤 13 屋根材 14 釘 A Waterproof sheet 10 Base cloth 11 Polymer cement 12 Asphalt emulsion 13 Roofing material 14 Nail
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ｂ３２Ｂ 27/20 Ｂ３２Ｂ 27/20 Ｚ Ｅ０４Ｄ 5/10 Ｅ０４Ｄ 5/10 Ｂ (58)調査した分野(Int.Cl.7，ＤＢ名) D06N 5/00 B32B 3/30 B32B 11/04 B32B 25/04 B32B 27/04 B32B 27/20 E04D 5/10 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 identification code FI B32B 27/20 B32B 27/20 Z E04D 5/10 E04D 5/10 B (58) Investigated field (Int.Cl. 7 , DB Name) D06N 5/00 B32B 3/30 B32B 11/04 B32B 25/04 B32B 27/04 B32B 27/20 E04D 5/10
Claims (3)
トを塗布し、基布の多数の隙間を通してポリマーセメン
トを基布の他側側面より突出させて多数の小突起を形成
し、かつ、基布の一側側面に塗布したポリマーセメント
の表面に、アスファルト乳剤又はアルファルトゴムを塗
布して製造することを特徴とする防水シートの製造方
法。A first step of forming a plurality of small projections by applying polymer cement to one side surface of the coarse base fabric and projecting the polymer cement from the other side surface of the base fabric through a plurality of gaps in the base fabric; A method for producing a waterproof sheet, comprising: applying an asphalt emulsion or an alphalt rubber to a surface of a polymer cement applied to one side surface of a base fabric.
とする請求項１記載の防水シートの製造方法。2. The method according to claim 1, wherein the base fabric is a woven fabric or a non-woven fabric.
シウム、酸化鉄を主成分とした主材に、少なくともアク
リル酸エステル共重合体を主成分としてなる複合ポリマ
ーエマルジョンを混和して生成したものからなることを
特徴とする請求項１又は２記載の防水シートの製造方
法。3. The polymer cement is formed by mixing a main polymer mainly composed of silicon oxide, calcium oxide and iron oxide with a composite polymer emulsion mainly composed of at least an acrylate ester copolymer. The method for producing a waterproof sheet according to claim 1 or 2, wherein: