JP2505856B2 - Pack cosmetics - Google Patents
Pack cosmeticsInfo
- Publication number
- JP2505856B2 JP2505856B2 JP63090041A JP9004188A JP2505856B2 JP 2505856 B2 JP2505856 B2 JP 2505856B2 JP 63090041 A JP63090041 A JP 63090041A JP 9004188 A JP9004188 A JP 9004188A JP 2505856 B2 JP2505856 B2 JP 2505856B2
- Authority
- JP
- Japan
- Prior art keywords
- pack
- polyisoprene
- water
- trans
- skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明はフェイシャルパックまたはボディパック等の
顔面用または全身用パック化粧料に関するものである。The present invention relates to a facial or whole body pack cosmetic such as a facial pack or a body pack.
近年化粧料に関する技術の進歩は目ざましく、数多く
のパック化粧料が開発されているが、その多くは（１）
ポリビニルアルコールを被膜剤とするビニルパック、
（２）タルク、ベントナイト等の無機粉体を主とする泥
パック剤および（３）低融点パラフィンワックスを用い
るパラフィンワックス剤に分類される。そしてこれらパ
ック化粧料に期待される効果はつぎの諸点であることが
よく知られている。すなわち、 被膜形成等により皮膚に適度の緊張感を与える。In recent years, the technological progress of cosmetics has been remarkable, and many pack cosmetics have been developed.
Vinyl pack with polyvinyl alcohol as a coating agent,
It is classified into (2) a mud pack agent mainly composed of an inorganic powder such as talc and bentonite, and (3) a paraffin wax agent using a low-melting paraffin wax. It is well known that the expected effects of these pack cosmetics are as follows. That is, the skin is given an appropriate tension by forming a film or the like.
被膜形成等により皮膚温を高め発汗および血行を良
くする。The skin temperature is raised by forming a film to improve sweating and blood circulation.
被膜剤の吸着作用により皮膚表面の汚れを取り除き
皮膚を清浄にする。The adsorbing action of the film-forming agent removes dirt on the skin surface and cleanses the skin.
皮膚賦活成分等の経皮吸収を高める。 Enhances the percutaneous absorption of skin activating ingredients.
などである。And so on.
その他、使用上の具備すべき条件として、つぎのよう
な諸点が重要な問題となる。In addition, the following points become important problems as conditions to be satisfied in use.
１） 皮膚への適用がたやすく、かつ無害であること。1) Easy to apply to the skin and harmless.
２） 皮膜パック料では乾燥が速いこと。2) The film pack material should dry quickly.
３） 皮膜を剥離しやすいこと。3) The film should be easy to peel off.
などが挙げられる。And the like.
しかし、従来の皮膜性パック化粧料においては、使用
面で乾燥時間が長く、約10〜20分程度必要で、使用者に
負担をかけ、また、皮膜による皮膚への緊張感が少な
く、効能面では皮膚賦活成分の経皮吸収が悪いなどの欠
点があり、これらの欠点を解消することが、課題となっ
ていた。However, with conventional film-packed cosmetics, it takes about 10 to 20 minutes to dry the product in terms of use, which puts a burden on the user. However, there are drawbacks such as poor percutaneous absorption of the skin activating component, and it has been a problem to solve these drawbacks.
上記の課題を解決するために、この発明においては、
被膜剤と皮膚賦活成分を必須成分とするパック化粧料に
おいて、前記被膜剤はトランス−1,4−ポリイソプレン
の水分散性乳化物を配合したパック化粧料とする手段を
採用したものである。以下その詳細を述べる。In order to solve the above problems, in the present invention,
In the pack cosmetic containing a film-forming agent and a skin activating component as essential components, the film-forming agent is a pack cosmetic containing a water-dispersible emulsion of trans-1,4-polyisoprene. The details are described below.
まず、この発明のトランス−1,4−ポリイソプレンと
は、繰り返し単位が で示される重合体であり、同じ1,4−ポリイソプレン結
合を有するシス−1,4−ポリイソプレン、すなわち繰り
返し単位が の重合体とは立体異性体の関係にある。そしてシス−1,
4−ポリイソプレンは天然ゴムと同様、典型的なゴム弾
性体であるが、トランス−1,4−ポリイソプレンは結晶
性熱可塑性ポリマーであって、この発明に使用するトラ
ンス−1,4−ポリイソプレンの分子量は好ましくは20万
から150万、さらに好ましくは40万から130万の範囲内で
ある。なぜならば、分子量がこの範囲より低い場合は、
造膜したフィルムの強度が低く、パックとして用いる際
皮膚に与える緊張感が弱くなり、また皮膚からパックを
はがすにあたり破れ易いなどの欠点を有し、逆に分子量
が上記範囲より高い場合は、ポリマー重合およびこのポ
リマーの水分散性乳化物を得るための工程性が悪くな
り、製造上困難をともなうため好ましくないからであ
る。First, the trans-1,4-polyisoprene of the present invention has a repeating unit A cis-1,4-polyisoprene having the same 1,4-polyisoprene bond, that is, a repeating unit The polymer has a stereoisomeric relationship. And cis-1,
Although 4-polyisoprene is a typical rubber elastic body like natural rubber, trans-1,4-polyisoprene is a crystalline thermoplastic polymer and is used in the present invention. The molecular weight of isoprene is preferably in the range of 200,000 to 1.5 million, more preferably 400,000 to 1.3 million. Because if the molecular weight is lower than this range,
The strength of the film formed is low, the tension given to the skin when used as a pack is weakened, and it has the drawback that it is easily torn when peeling the pack from the skin. Conversely, when the molecular weight is higher than the above range, the polymer is This is because the processability for polymerizing and obtaining a water-dispersible emulsion of this polymer is deteriorated, and it is difficult to manufacture, which is not preferable.
つぎにこの発明に使用するトランス−1,4−ポリイソ
プレンの代表的なものとして（株）クラレ製TP-301を例
示することが出来、その一般的性質を第１表に、また、
溶融、押出しに成膜したフィルム物性（測定温度25℃、
テストピース50μｍ厚、20mm×150mm、引張り速度500mm
/分）を第２表に例として示した。Next, TP-301 manufactured by Kuraray Co., Ltd. can be exemplified as a typical example of trans-1,4-polyisoprene used in the present invention, and its general properties are shown in Table 1 and
Physical properties of film formed by melting and extrusion (measurement temperature 25 ℃,
Test piece 50μm thickness, 20mm × 150mm, pulling speed 500mm
/ Min) is shown in Table 2 as an example.
さらにこの発明のトランス−1,4−ポリイソプレンの
水分散性乳化物は、トランス−1,4−ポリイソプレンを
可溶性有機溶媒、たとえばベンゼン、トルエン、四塩化
炭素、テトラヒドロフラン、トリクロルエチレン、クロ
ロベンゼン、クロロホルム、二硫化炭素、テレビン油、
ナフサ、ミネラルターペン等に溶解し、市販の界面活性
剤水溶液で乳化し、低温、減圧下で使用した有機溶媒を
除去して得られるが、トランス−1,4−ポリイソプレン
が乳化物の形で水に分散されるのであれば、特にこのよ
うな方法に限定されるものではない。 Furthermore, the water-dispersible emulsion of trans-1,4-polyisoprene of the present invention is a solution of trans-1,4-polyisoprene in a soluble organic solvent such as benzene, toluene, carbon tetrachloride, tetrahydrofuran, trichloroethylene, chlorobenzene, chloroform. , Carbon disulfide, turpentine,
It can be obtained by dissolving it in naphtha, mineral terpene, etc., emulsifying it with a commercially available aqueous surfactant solution, and removing the organic solvent used under reduced pressure at low temperature, but trans-1,4-polyisoprene in the form of an emulsion. The method is not particularly limited as long as it is dispersed in water.
なお、この発明のパック化粧料には、化粧品業界で従
来から広く使用されている薬効成分や保湿剤などの皮膚
賦活成分の他、保存剤、防腐剤、香料などを適宜添加す
ることができ、また必要に応じて、その他の添加剤を加
えてもよい。In addition, in the pack cosmetic of the present invention, in addition to skin activating components such as medicinal components and moisturizers that have been widely used in the cosmetic industry, preservatives, preservatives, fragrances and the like can be added as appropriate. Moreover, you may add other additives as needed.
この発明のトランス−1,4−ポリイソプレンの水分散
性乳化物は従来のビニルパックなどと異なる作用機構に
基づくものである。すなわち、従来の被膜性パック原料
は高分子化合物を水に溶解させたものであり、高分子自
身が水に水和することにより水を包含し、溶解するもの
である。それ故、乾燥時間も必然的に長くなる。The water-dispersible emulsion of trans-1,4-polyisoprene of the present invention is based on a mechanism of action different from conventional vinyl packs and the like. That is, the conventional coating material for a pack is a polymer compound dissolved in water, and the polymer itself is hydrated in water to contain and dissolve water. Therefore, the drying time is inevitably long.
これに対してこの発明のトランス−1,4−ポリイソプ
レンの水分散性乳化物は、水に不溶性のトランス−1,4
−ポリイソプレンを界面活性剤により水に分散安定化さ
せたものであるから、ポリマー中への水の溶解がきわめ
て微量である。このためパックとして使用する際、水の
蒸発または揮発性が良く乾燥時間を短くすることができ
る。そしてトランス−1,4−ポリイソプレンは結晶性の
ものであるから、この水分散性乳化物中に添加している
皮膚賦活成分等を乾燥造膜時に外に押し出し、その押し
出された皮膚賦活成分が皮膚に効率良く接触する結果パ
ックとしてすぐれた効果を発現するようになる。On the other hand, the water-dispersible emulsion of trans-1,4-polyisoprene of the present invention is water-insoluble trans-1,4
Since polyisoprene is dispersed and stabilized in water with a surfactant, the amount of water dissolved in the polymer is extremely small. Therefore, when used as a pack, the evaporation or volatility of water is good and the drying time can be shortened. And since trans-1,4-polyisoprene is crystalline, the skin activating component or the like added to this water-dispersible emulsion is extruded out during dry film formation, and the extruded skin activating component is extruded. As a result of efficiently contacting the skin with the skin, an excellent effect will be exhibited as a pack.
また、トランス−1,4−ポリイソプレンは結晶性ポリ
マーであると同時に主鎖に二重結合を有するため、ゴム
的な挙動も示し伸縮性を有する。このため、パックとし
て用いる際常に皮膚を適度に圧迫し、緊張感をもたらし
皺を伸ばすのに効果がある。Further, since trans-1,4-polyisoprene is a crystalline polymer and simultaneously has a double bond in the main chain, it also exhibits rubber-like behavior and has elasticity. For this reason, when used as a pack, it is effective in always pressing the skin moderately, giving a feeling of tension, and extending wrinkles.
以上のように、トランス−1,4−ポリイソプレンを用
いたパックは、造膜にあたっての乾燥時間が短く、使用
時適度の緊張感をもたらすと同時に血行を促進し、経皮
吸収を高めるなどの作用を示すのである。As described above, the pack using trans-1,4-polyisoprene has a short drying time during film formation, provides an appropriate tension during use, promotes blood circulation, and enhances transdermal absorption. It shows the action.
実施例1: トランス−1,4−ポリイソプレン（クラレTP-301）10
部にトルエン50部およびポリオキシエチレンラウリルエ
ーテル（6.E.0.）0.5部を加え70℃に加温溶解し、これ
に同温の精製水39.5部を加え、 ホモミキサー（3000rpm）で10分間乳化した。ついでこ
れを50℃まで冷却し、減圧下（５〜10mmHg）でトルエン
を除去し、トランス−1,4−ポリイソプレンの水分散性
乳化物を得た。このものの物性を第３表に示した。Example 1: trans-1,4-polyisoprene (Kuraray TP-301) 10
To 50 parts of toluene and 0.5 parts of polyoxyethylene lauryl ether (6.E.0.) Were added and dissolved by heating at 70 ° C, to which 39.5 parts of purified water of the same temperature was added, The mixture was emulsified with a homomixer (3000 rpm) for 10 minutes. Then, this was cooled to 50 ° C., and toluene was removed under reduced pressure (5 to 10 mmHg) to obtain a water-dispersible emulsion of trans-1,4-polyisoprene. The physical properties of this product are shown in Table 3.
実施例２および比較例1: 実施例１で得たトランス−1,4−ポリイソプレンの水
分散性乳化物に水を加えて、固形分20w/w％溶液を調
製。一方ビニルアルコール（日本合成科学工業社製：ゴ
ーセノール25）の20w/w％水溶液を調製し、温度24〜26
℃、温度62％の室内にて、ガラス板上に両試料を0.1g/c
m2の量になるように塗布し、乾燥するまでの時間を測定
した。その結果を第４表に示した。（繰り返し数３回） 以上の結果から明らかなように、この発明によるトラ
ンス−1,4−ポリイソプレンの水分散性乳化物の乾燥時
間は通常の被膜性パックの代表であるビニルパックと比
較した場合、かなり乾燥速度が短いことが判明した。Example 2 and Comparative Example 1: Water was added to the water-dispersible emulsion of trans-1,4-polyisoprene obtained in Example 1 to prepare a 20 w / w% solid content solution. On the other hand, prepare a 20w / w% aqueous solution of vinyl alcohol (Nippon Gosei Kagaku Kogyo Co., Ltd .: Gohsenol 25) at a temperature of 24-26.
0.1g / c of both samples on a glass plate in a room at 62 ℃
The amount of m 2 was applied and the time until drying was measured. The results are shown in Table 4. (Repeat 3 times) As is apparent from the above results, the drying time of the water-dispersible emulsion of trans-1,4-polyisoprene according to the present invention is considerably higher than that of a vinyl pack which is a typical film-forming pack. Turned out to be short.
実施例3: 実施例１のトランス−1,4−ポリイソプレンの水分散
性乳化物97.88部にパラオキシ安息香酸メチル0.1部、リ
ン酸−Ｌ−アスコルビルマグネシウム1.0部、香料0.02
部、グリセリン１部を加え均一に溶解して顔面用のフェ
イシャルパック（ムース）とし、つぎの条件下でその泡
沫エアゾールを調製した。このものは、乾燥時間は短
く、緊張感および使用感の良いものであった。Example 3: 97.88 parts of water-dispersible emulsion of trans-1,4-polyisoprene of Example 1 with 0.1 part of methyl paraoxybenzoate, 1.0 part of magnesium L-ascorbyl phosphate, and 0.02 of fragrance.
And 1 part of glycerin were added and uniformly dissolved to form a facial facial pack (mousse), and the foam aerosol was prepared under the following conditions. This product had a short drying time and had a good feeling of tension and feeling of use.
（泡沫エアゾールの調製条件） パック原液:38.0g（95wt％） 43.4ml（91.9vol％） 噴 射 剤: 2.0g（ 5wt％） 3.8ml（ 8.1vol％）噴射剤組成：LPG5.0kg/cm2 合 計 40.0g 47.2ml （泡沫エアゾールの特性） 燃焼性区分：難焼性 製品圧力（25℃）:3.0〜3.5kg/cm2 噴射引火性試験 :0cm 噴射量 （25℃）:1.3〜1.6g/sec 実施例4: 実施例１のトランス−1,4−ポリイソプレンの水分散
性乳化物97.85部にパラオキシ安息香酸メチル0.1部、水
溶性コラーゲン２部、香料0.05部を加え均一に溶解して
全身肌用のボディパックを調製した。このものの粘度
（25℃）は680cpであり、これを、ハケで全身に塗布し
た時、乾燥時間は短く、緊張感および使用感も良いもの
であった。(Preparation conditions for foam aerosol) Pack stock solution: 38.0g (95wt%) 43.4ml (91.9vol%) Ejectant: 2.0g (5wt%) 3.8ml (8.1vol%) Propellant composition: LPG 5.0kg / cm 2 Total 40.0g 47.2ml (Characteristics of foam aerosol) Combustibility classification: Flame retardant Product pressure (25 ℃): 3.0-3.5kg / cm 2 Injection flammability test: 0cm Injection volume (25 ℃): 1.3-1.6g / sec Example 4: To 97.85 parts of the water-dispersible emulsion of trans-1,4-polyisoprene of Example 1, 0.1 part of methyl paraoxybenzoate, 2 parts of water-soluble collagen and 0.05 part of fragrance were added and uniformly dissolved. A body pack for whole body skin was prepared. The viscosity (25 ° C.) of this product was 680 cp, and when it was applied to the whole body by brush, the drying time was short, and the feeling of tension and the feeling of use were good.
この発明のパック化粧料は、市販の被膜性ビニル系パ
ック化粧料（顔面用）、タルク・ベントナイト系泥パッ
ク化粧料（顔面用または全身用）およびパラフィンワッ
クス系パック化粧料（全身用）のそれぞれと比較して、
つぎのような優れた効果を示す。The pack cosmetics of this invention are commercially available film-forming vinyl pack cosmetics (for face), talc / bentonite mud pack cosmetics (for face or whole body), and paraffin wax pack cosmetics (for whole body). Compared to
It has the following excellent effects.
（１） 即乾性であるため、被膜形成時間が非常に短
く、使用者に負担をかけない。(1) Since it is quick-drying, the film formation time is very short and does not burden the user.
（被膜性ビニル系パックと比較して） （２） 皮膚賦活成分の経皮吸収作用が大きい。 (Compared with a film-forming vinyl pack) (2) The percutaneous absorption of the skin activating component is large.
（被膜性ビニル系パック、タルク・ベントナイト系パ
ック、パラフィンワックス系パックと比較して） （３） 皮膚の緊張感が適度にあり、満足感が得られ
る。(Compared to a film-type vinyl pack, a talc / bentonite pack, and a paraffin wax pack) (3) The skin has a moderate tension and a satisfactory feeling is obtained.
（タルク・ベントナイト系パック、パラフィンワック
ス系パックと比較して） （４） パラフィンワックスを溶解して温度をコントロ
ールしたり、タルク・ベントナイト系パックのようにあ
らかじめ準備をする必要がなく作業性が良い。(Compared to talc / bentonite type packs and paraffin wax type packs) (4) Good workability because there is no need to melt paraffin wax to control the temperature or prepare in advance like talc / bentonite type packs. .
また、パック化粧料が本来具備している清浄効果、保
湿効果などの諸性質もバランスよく有しており、適用範
囲も顔面および全身と広い。In addition, the pack cosmetics have various properties such as a cleansing effect and a moisturizing effect, which are originally possessed by the pack cosmetics, and the application range is wide on the face and the whole body.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 紫山 裕治 大阪府大阪市東区道修町２丁目51番地 岩瀬コスファ株式会社内 (72)発明者 石井 正雄 茨城県鹿島郡波崎町太田98 (56)参考文献 特開 昭57−77611（ＪＰ，Ａ) 特開 昭57−56408（ＪＰ，Ａ) ─────────────────────────────────────────────────── ─── Continuation of front page (72) Inventor Yuji Shiyama 2-51, Doshomachi, Higashi-ku, Osaka City, Osaka Prefecture Iwase Cosfa Ltd. (72) Inventor Masao Ishii 98 Ota, Hasaki-machi, Kashima-gun, Ibaraki (56) References JP-A-57-77611 (JP, A) JP-A-57-56408 (JP, A)
Claims (1)
ック化粧料において、前記被膜剤はトランス−1,4−ポ
リイソプレンの水分散性乳化物であることを特徴とする
パック化粧料。1. A pack cosmetic comprising a coating agent and a skin activating component as essential components, wherein the coating agent is a water-dispersible emulsion of trans-1,4-polyisoprene.