JP2010150446A - Pressure-sensitive adhesive tape for temporarily fixing article, method of temporarily fixing article, and temporarily fixed article - Google Patents
Pressure-sensitive adhesive tape for temporarily fixing article, method of temporarily fixing article, and temporarily fixed article Download PDFInfo
- Publication number
- JP2010150446A JP2010150446A JP2008331852A JP2008331852A JP2010150446A JP 2010150446 A JP2010150446 A JP 2010150446A JP 2008331852 A JP2008331852 A JP 2008331852A JP 2008331852 A JP2008331852 A JP 2008331852A JP 2010150446 A JP2010150446 A JP 2010150446A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- article
- adhesive tape
- temporarily fixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、物品を仮止め固定するために用いられる粘着テープ、物品の仮止め固定方法及び仮止め固定物品に関し、さらに詳しくは、ラテックスやゴム系の粘着剤を用いずに、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、また、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有し、かつ、目的を達成した後、剥離する際には容易に剥がすことができ、しかも糊残りが生じにくい物品の仮止め固定用粘着テープ、物品の仮止め固定方法及び仮止め固定物品に関する。なお、本発明の粘着テープは、テープ状またはシート状で用いられる。 The present invention relates to a pressure-sensitive adhesive tape used for temporarily fixing an article, a method for temporarily fixing an article, and a temporarily fixed article, and more particularly, without using a latex or rubber-based adhesive. After having achieved the purpose of having excellent tab aptitude that it is difficult to peel off even if stress is generated in a state where it is applied to the adherend part of an article, and that it is difficult to peel off even if the adhesive layers are attached to each other. The present invention relates to an adhesive tape for temporarily fixing and fixing an article that can be easily peeled off when peeling, and hardly causes adhesive residue, a method for temporarily fixing and fixing an article, and a temporarily fixed article. The pressure-sensitive adhesive tape of the present invention is used in a tape shape or a sheet shape.
物品の仮止め固定用粘着テープは、例えば、電化製品、ＯＡ機器等の物品を製品出荷する際に、被着体である前記物品を梱包するにあたり、物品の内部部品やドア等の被着部分（例えば印刷鋼板や樹脂板等）を仮止め固定するために、前記被着部分に貼り付けて用いられている。例えば、物品が冷蔵庫の場合には、物品の仮止め固定用粘着テープは、冷蔵庫のドア等の仮止め固定に用いられている。 For example, when an article such as an electrical appliance or an OA device is shipped, the adhesive tape for temporarily fixing the article is used to pack the article, which is an adherend, to an attached part such as an internal part of the article or a door. In order to temporarily fix (for example, a printed steel plate or a resin plate), it is used by being affixed to the adherend portion. For example, when the article is a refrigerator, the adhesive tape for temporarily fixing the article is used for temporarily fixing the refrigerator door or the like.
このような物品の仮止め固定に用いられ粘着テープに要求される特性としては、被着体である物品の内部部品やドア等の被着部分を確実に固定するために、粘着テープが被着部分に貼り付けられた状態において、応力が発生しても剥がれないことが求められる。
また、前記物品は、その使用する際には、不要になった粘着テープを最終的に被着部分から剥離するため、粘着テープには、容易に剥離することが求められる。このように、仮止め固定用粘着テープには、相反する特性が要求されている。
The property required for adhesive tape used for temporarily fixing such articles is that the adhesive tape is attached in order to securely fix the internal parts of the article, which is the adherend, and the adherend part such as the door. It is required that even when stress is generated in a state of being attached to the part, it does not peel off.
Further, when the article is used, the pressure-sensitive adhesive tape is required to be easily peeled off because the pressure-sensitive adhesive tape that is no longer needed is finally peeled off from the adherend. Thus, the temporarily fixing adhesive tape is required to have contradictory characteristics.
仮止め固定用粘着テープに使用される粘着剤としては、有機溶剤型粘着剤や水系粘着剤が用いられ、そして、水系粘着剤としては、通常、アクリル系エマルション型粘着剤が用いられている。 As the adhesive used for the temporary fixing tape, an organic solvent-type adhesive or an aqueous adhesive is used, and as the aqueous adhesive, an acrylic emulsion-type adhesive is usually used.
アクリル系エマルション型粘着剤を塗布して形成した粘着剤層は、家電製品等の物品の被着部分（例えば印刷鋼板や樹脂板等）に対する接着力が高い。しかしながら、前記基材とアクリル系エマルション型粘着剤により形成された粘着剤層とは、密着力が弱い。そのため、仮止め固定用粘着テープを被着体から剥離する際には、被着部分の印刷面が毟り取られたり、粘着剤層の層間破壊により、被着体に糊残りが生じたりする問題があった。 A pressure-sensitive adhesive layer formed by applying an acrylic emulsion-type pressure-sensitive adhesive has a high adhesive force with respect to a part to be adhered (for example, a printed steel plate or a resin plate) of an article such as a home appliance. However, the adhesive force between the base material and the pressure-sensitive adhesive layer formed from the acrylic emulsion-type pressure-sensitive adhesive is weak. For this reason, when the adhesive tape for temporarily fixing is peeled off from the adherend, the printed surface of the adherend portion is scraped off, or adhesive residue is generated on the adherend due to the interlaminar fracture of the adhesive layer. was there.
従来の仮止め固定用粘着テープの改良品として、特許文献１では、基材の片面に粘着剤層を有する、物品の仮止め固定用粘着テープにおいて、基材が、ポリエステル系フィルムであり、粘着剤層が、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有するアクリル系エマルション型粘着剤により形成されたものであり、基材と粘着剤層との間には、オキサゾリン基を含有する水系樹脂により形成された下塗り層を有することを特徴とする物品の仮止め固定用粘着テープが提案されている。
また、特許文献２では、基材の片面に粘着剤層を有する、物品の仮止め固定用粘着テープにおいて、基材が、ポリプロピレン系フィルムであり、粘着剤層が、アルキル基の炭素数が４〜１２のアルキル（メタ）アクリレートを主成分とし、かつカルボキシル基含有単量体を含有する単量体混合物から得られたアクリル系共重合体エマルションおよびオキサゾリン基含有水系架橋剤を含有するアクリル系エマルション型粘着剤により形成されたものであり、基材と粘着剤層との間には、溶剤型のアミノ基グラフト化アクリル系樹脂により形成された下塗り層を有することを特徴とする物品の仮止め固定用粘着テープが提案されている。
さらに、特許文献３では、エラストマーを主成分とし、該エラストマー１００重量部に対して、１〜２５重量部のフェノール樹脂および３〜２５重量部の架橋剤を含有する粘着剤からなる粘着剤層と支持体とを含む粘着シートが提案されている。
しかしながら、従来から提案されたものは、粘着剤層同士を貼り付けても剥がれにくいというタブ適性については、性能的に十分ではなかった。
従って、ゴム系の粘着剤を用いずに、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、また、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有し、且つ、目的を達成した後、剥離する際には容易に剥がすことができ、しかも糊残りが生じにくい物品の仮止め固定用粘着テープが強く望まれている。
Moreover, in patent document 2, in the adhesive tape for temporarily fix | fixing articles | goods which has an adhesive layer on the single side | surface of a base material, a base material is a polypropylene-type film and an adhesive layer has 4 carbon atoms of an alkyl group. Acrylic copolymer emulsion obtained from a monomer mixture containing -12 alkyl (meth) acrylate as a main component and containing a carboxyl group-containing monomer, and an acrylic emulsion containing an oxazoline group-containing aqueous crosslinking agent Temporary fixing of an article characterized by having an undercoat layer formed of a solvent-type amino group-grafted acrylic resin between the base material and the pressure-sensitive adhesive layer. Fixing adhesive tapes have been proposed.
Furthermore, in patent document 3, the adhesive layer which consists of an adhesive which has an elastomer as a main component and contains 1-25 weight part phenol resin and 3-25 weight part crosslinking agent with respect to 100 weight part of this elastomer, An adhesive sheet including a support has been proposed.
However, what was proposed conventionally was not sufficient in terms of the tab suitability that it was difficult to peel off even if the adhesive layers were pasted together.
Therefore, without using a rubber-based adhesive, it is difficult to peel off even if stress occurs in the state of being applied to the adherend part of the article that is the adherend, and it is also difficult to peel off even if the adhesive layers are attached to each other There is a strong demand for an adhesive tape for temporarily fixing and fixing an article that has excellent tab suitability and can be easily peeled off after achieving its purpose and is less likely to have adhesive residue.
本発明の目的は、従来技術の問題点に鑑み、ゴム系の粘着剤を用いずに、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、また、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有し、且つ、目的を達成した後、剥離する際には容易に剥がすことができ、しかも糊残りが生じにくい物品の仮止め固定用粘着テープを提供することにある。 In view of the problems of the prior art, the object of the present invention is not to be peeled off even if stress is generated in a state of being attached to an adherend part of an article as an adherend without using a rubber-based adhesive. In addition, it has excellent tab suitability so that it does not easily peel off even if the adhesive layers are attached to each other, and after achieving the purpose, it can be easily peeled off when peeled off, and it is possible to remove the adhesive residue. The object is to provide an adhesive tape for fastening and fixing.
本発明者らは、上記目的を達成するために、鋭意研究を重ねた結果、基材（Ａ）の片面に、特定の単量体からなるアクリル系粘着剤と特定のタッキファイアを含む粘着剤を塗布すると、特に、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有する物品の仮止め固定用粘着テープとなることを見出した。それらの知見に基づいて、本発明を完成するに至った。 As a result of intensive studies to achieve the above object, the present inventors have found that an adhesive containing an acrylic adhesive made of a specific monomer and a specific tackifier on one side of the substrate (A). In particular, the present inventors have found that an adhesive tape for temporarily fixing and fixing an article having excellent tab suitability that does not easily peel off even when the adhesive layers are attached to each other is applied. Based on these findings, the present invention has been completed.
すなわち、本発明の第１の発明によれば、二軸延伸されたポリプロピレンフィルムからなる基材（Ａ）の片面に、アクリル系粘着剤（ａ）を主成分とする粘着剤層（Ｂ）を有する物品の仮止め固定用粘着テープであって、粘着剤層（Ｂ）は、アクリル系粘着剤（ａ）１００重量部に対して、ロジン系タッキファイア（ｂ）１〜２０重量部含有し、且つ、アクリル系粘着剤（ａ）は、ブチル（メタ）アクリレート８０〜９９．９重量％とアクリル酸０．１〜２０重量％とからなることを特徴とする物品の仮止め固定用粘着テープが提供される。 That is, according to 1st invention of this invention, the adhesive layer (B) which has an acrylic adhesive (a) as a main component on the single side | surface of the base material (A) which consists of a biaxially stretched polypropylene film. A pressure-sensitive adhesive tape for temporarily fixing an article having an adhesive layer (B) containing 1 to 20 parts by weight of a rosin tackifier (b) with respect to 100 parts by weight of an acrylic pressure-sensitive adhesive (a), An acrylic pressure-sensitive adhesive (a) comprises 80 to 99.9% by weight of butyl (meth) acrylate and 0.1 to 20% by weight of acrylic acid. Provided.
本発明の第２の発明によれば、第１の発明において、粘着剤層（Ｂ）には、さらに、硬化剤（ｃ）と紫外線吸収剤（ｄ）を含有することを特徴とする物品の仮止め固定用粘着テープが提供される。
また、本発明の第３の発明によれば、第２の発明において、紫外線吸収剤（ｄ）は、ベンゾトリアゾール系紫外線吸収剤であって、アクリル系粘着剤（ａ）１００重量部に対して、１．０〜３．０重量部含有することを特徴とする物品の仮止め固定用粘着テープが提供される。
さらに、本発明の第４の発明によれば、第２の発明において、硬化剤（ｃ）は、イソシアネート系硬化剤であって、アクリル系粘着剤（ａ）１００重量部に対して、０．５〜２．０重量部含有することを特徴とする物品の仮止め固定用粘着テープが提供される。
According to a second invention of the present invention, in the first invention, the pressure-sensitive adhesive layer (B) further contains a curing agent (c) and an ultraviolet absorber (d). An adhesive tape for temporarily fixing is provided.
According to the third invention of the present invention, in the second invention, the ultraviolet absorber (d) is a benzotriazole ultraviolet absorber and is 100 parts by weight of the acrylic adhesive (a). 1.0 to 3.0 parts by weight of an adhesive tape for temporarily fixing an article is provided.
Furthermore, according to the fourth invention of the present invention, in the second invention, the curing agent (c) is an isocyanate-based curing agent, and is added to the acrylic pressure-sensitive adhesive (a) by 100 parts by weight. An adhesive tape for temporarily fixing and fixing an article characterized by containing 5 to 2.0 parts by weight is provided.
また、本発明の第５の発明によれば、第１の発明において、基材（Ａ）と粘着剤層（Ｂ）との間には、印刷層（Ｃ）を有することを特徴とする物品の仮止め固定用粘着テープが提供される。
さらに、本発明の第６の発明によれば、第５の発明において、印刷層（Ｃ）が活性水素をもつ基を有するインクからなることを特徴とする物品の仮止め固定用粘着テープが提供される。
According to the fifth invention of the present invention, in the first invention, an article having a printed layer (C) between the substrate (A) and the pressure-sensitive adhesive layer (B). An adhesive tape for temporarily fixing is provided.
Further, according to a sixth aspect of the present invention, there is provided the adhesive tape for temporarily fixing an article according to the fifth aspect, wherein the printed layer (C) is made of an ink having a group having active hydrogen. Is done.
また、本発明の第７の発明によれば、第１の発明に係る物品の仮止め固定用粘着テープを用いることを特徴とする物品の仮止め固定方法が提供される。
さらに、本発明の第８の発明によれば、第１の発明において、第１の発明に係る物品の仮止め固定用粘着テープにより、物品が、仮止め固定されていることを特徴とする仮止め固定物品が提供される。
According to a seventh aspect of the present invention, there is provided a method for temporarily fixing an article, characterized in that the adhesive tape for temporarily fixing an article according to the first invention is used.
Further, according to an eighth invention of the present invention, in the first invention, the article is temporarily fixed by the temporary fixing fixing adhesive tape for the article according to the first invention. A stop and fix article is provided.
本発明の物品の仮止め固定用粘着テープは、粘着剤層の形成にアクリル系粘着剤を用いており、物品の被着体（被着部分）に対する接着力が良好であり、被着部分に粘着テープを貼り付けた状態で応力が発生しても剥がれにくく、物品の仮止め固定を確実に行うことができる。
また、本発明では、基材として、二軸延伸されたポリプロピレンフィルムを用い、粘着剤層の形成に用いるアクリル系粘着剤には、構成する全単量体中、ブチル（メタ）アクリレート８０〜９９．９重量％とアクリル酸０．１〜２０重量％を含み、硬化剤（架橋剤）として、多官能性イソシアネート化合物を用い、かつ、ロジン系タッキファイアを特定量用いている。このように、本発明では、基材、粘着剤層のアクリル系粘着剤、架橋剤、タッキファイアとして、それぞれ、特定のものを選択して用いることにより、基材と粘着剤層との密着性を向上させ、さらに、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、また、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有している。
The pressure-sensitive adhesive tape for temporarily fixing the article of the present invention uses an acrylic pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer, and has good adhesion to the adherend (attached part) of the article. Even if stress is generated with the adhesive tape applied, it is difficult to peel off and the article can be securely fixed temporarily.
In the present invention, a biaxially stretched polypropylene film is used as the base material, and the acrylic pressure-sensitive adhesive used for forming the pressure-sensitive adhesive layer includes butyl (meth) acrylate 80 to 99 in all the constituent monomers. The polyfunctional isocyanate compound is used as a curing agent (cross-linking agent), and a specific amount of rosin tackifier is used. Thus, in the present invention, the adhesion between the base material and the pressure-sensitive adhesive layer is selected and used as the base material, the acrylic pressure-sensitive adhesive of the pressure-sensitive adhesive layer, the crosslinking agent, and the tackifier, respectively. In addition, it has excellent tab aptitude that it is difficult to peel off even if stress is generated in a state where it is attached to the adherend part of the article that is the adherend, and that it is difficult to peel off even if the adhesive layers are stuck together. Have.
そのため、本発明の物品の仮止め固定用粘着テープは、目的を達成した後、被着体からの剥離を容易に行うことができ、被着部分の印刷面の毟り取りや、糊残りを生じにくくしている。
また、本発明の物品の仮止め固定用粘着テープの粘着剤層は、接着力が良好である他、凝集力（保持力）も良好であり、かかる点からも被着部分の印刷面の毟り取りや糊残りを生じにくくしている。
さらに、本発明の物品の仮止め固定用粘着テープの粘着剤層は、ラテックスやゴム系の粘着剤を用いなくても、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、また、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有している。
For this reason, the adhesive tape for temporarily fixing and fixing the article of the present invention can be easily peeled off from the adherend after achieving the purpose, and the printed surface of the adherend portion is scraped off and the adhesive remains. It is difficult.
Further, the pressure-sensitive adhesive layer of the pressure-sensitive adhesive tape for temporarily fixing the article of the present invention not only has a good adhesive force but also a good cohesive force (holding force). Makes it difficult to remove or leave glue.
Furthermore, the pressure-sensitive adhesive layer of the adhesive tape for temporarily fixing the article of the present invention has stress in a state where it is applied to the adherend part of the article that is the adherend, without using latex or rubber adhesive. Even if it occurs, it has excellent tab suitability such that it does not easily peel off, and it does not easily peel off even if the adhesive layers are pasted together.
このように、本発明の物品の仮止め固定用粘着テープは、物品の被着部分の仮止め固定を確実に行うことができる接着力を有し、かつ、糊残りなく、容易に剥がすことができ、接着性と剥離性の相反する特性を満足することができる。仮止め固定用粘着テープが適用される物品として例示される、家電製品の国内仕様では、流通段階における環境温度として、−２０℃〜＋５０℃の範囲が想定されているが、かかる本発明の物品の仮止め固定用粘着テープは、前記仕様において、好適に用いることができる。 As described above, the adhesive tape for temporarily fixing the article of the present invention has an adhesive force capable of reliably fixing the temporarily attached portion of the article, and can be easily peeled off without any adhesive residue. It is possible to satisfy the conflicting properties of adhesiveness and peelability. In the domestic specification of household electrical appliances exemplified as an article to which the temporary fixing fixing adhesive tape is applied, the environmental temperature in the distribution stage is assumed to be in the range of -20 ° C to + 50 ° C. The temporary fixing fixing adhesive tape can be suitably used in the above specifications.
本発明の物品を仮止め固定するために用いられる粘着テープ、すなわち物品の仮止め固定用粘着テープ（以下、単に「粘着テープ」とも言う。）は、二軸延伸されたポリプロピレンフィルムからなる基材（Ａ）の片面に、アクリル系粘着剤（ａ）を主成分とする粘着剤層（Ｂ）を有する物品の仮止め固定用粘着テープであって、
粘着剤層（Ｂ）は、アクリル系粘着剤（ａ）１００重量部に対して、ロジン系タッキファイア（ｂ）１〜２０重量部含有し、且つ、アクリル系粘着剤（ａ）は、ブチル（メタ）アクリレート８０〜９９．９重量％とアクリル酸０．１〜２０重量％とからなることを特徴とするものである。
以下、本発明の粘着テープ、その粘着テープの使用方法などについて、項目毎に、詳細に説明する。
An adhesive tape used for temporarily fixing an article of the present invention, that is, an adhesive tape for temporarily fixing an article (hereinafter also simply referred to as “adhesive tape”) is a base material made of a biaxially stretched polypropylene film. On one side of (A) is an adhesive tape for temporarily fixing and fixing an article having an adhesive layer (B) mainly composed of an acrylic adhesive (a),
The pressure-sensitive adhesive layer (B) contains 1 to 20 parts by weight of a rosin tackifier (b) with respect to 100 parts by weight of the acrylic pressure-sensitive adhesive (a), and the acrylic pressure-sensitive adhesive (a) is butyl ( It is characterized by comprising 80 to 99.9% by weight of (meth) acrylate and 0.1 to 20% by weight of acrylic acid.
Hereinafter, the adhesive tape of the present invention, the method of using the adhesive tape, and the like will be described in detail for each item.
１．基材（Ａ）
本発明の粘着テープに使用される基材（Ａ）としては、プラスチックフィルムを使用することができるが、好ましくはポリエステルフィルムまたは二軸延伸されたポリプロピレンフィルム（以下ＯＰＰと略称することもある。）であり、より好ましくは二軸延伸されたポリプロピレンフィルムである。
基材（Ａ）の厚みは、機械的強度の点より、３０〜６０μｍの範囲のものを用いるのが、家電製品の部品等を確実に仮固定することができるので好ましい。なお、厚みが３０μｍ未満のポリプロピレン系フィルムでは、切れ易く、家電製品の部品を確実に仮固定するのに強度が不足する場合がある。一方、厚みが６０μｍを超えると、剛性が高くて扱い難く、コストが高くなるので好ましくない。
1. Base material (A)
As the substrate (A) used in the pressure-sensitive adhesive tape of the present invention, a plastic film can be used, but preferably a polyester film or a biaxially stretched polypropylene film (hereinafter sometimes abbreviated as OPP). More preferably, it is a biaxially stretched polypropylene film.
The thickness of the base material (A) is preferably in the range of 30 to 60 μm from the viewpoint of mechanical strength, because it is possible to reliably temporarily fix parts of home appliances and the like. In addition, a polypropylene film having a thickness of less than 30 μm is easy to cut, and the strength may be insufficient to securely fix the components of the home appliance. On the other hand, if the thickness exceeds 60 μm, it is not preferable because the rigidity is high and difficult to handle, and the cost increases.
また、上記プラスチックフィルムとしては、例えば、ポリプロピレン、ポリエチレン、ポリ塩化ビニル、ポリエチレンテレフタレート（ＰＥＴ）、ポリスチレン、ポリアミド、ポリウレタン等を任意の方法で成型したものを用いることができる。ポリプロピレン系フィルムは、優れた透明性、光沢性等の光学特性、引張特性、ヤング率に代表される機械特性、実質上の無毒性及び無臭性等の特性を備えているため、好ましい。 Moreover, as said plastic film, what shape | molded the polypropylene, polyethylene, polyvinyl chloride, polyethylene terephthalate (PET), polystyrene, polyamide, polyurethane etc. by arbitrary methods can be used, for example. Polypropylene films are preferred because they have excellent optical properties such as transparency and gloss, tensile properties, mechanical properties represented by Young's modulus, and substantially non-toxic and odorless properties.
２．粘着剤層（Ｂ）
（１）アクリル系粘着剤の原料
（ｉ）ポリ（メタ）アクリル酸エステル
本発明の物品の仮止め固定用粘着テープに使用される粘着剤層（Ｂ）の粘着剤としては、被着体への糊残りがない等の特性が要求されるため、ゴム系粘着剤を用いずに、アクリル系粘着剤（ａ）を用いる。アクリル系粘着剤の中でも、エマルジョン型でなく、溶剤型アクリル系粘着剤が好適に用いられる。
粘着剤は、アクリル系粘着剤（ａ）としてのポリ（メタ）アクリル酸エステルとタッキファイア（ｂ）を主成分とする組成物である。
2. Adhesive layer (B)
(1) Raw material of acrylic pressure-sensitive adhesive (i) Poly (meth) acrylic acid ester As the pressure-sensitive adhesive of the pressure-sensitive adhesive layer (B) used for the temporary fixing fixing pressure-sensitive adhesive tape of the article of the present invention, to the adherend Therefore, an acrylic pressure-sensitive adhesive (a) is used without using a rubber-based pressure-sensitive adhesive. Among the acrylic pressure-sensitive adhesives, a solvent-type acrylic pressure-sensitive adhesive is suitably used instead of the emulsion type.
An adhesive is a composition which has a poly (meth) acrylic acid ester and tackifier (b) as an acrylic adhesive (a) as a main component.
本発明の粘着テープでは、溶剤型アクリル系粘着剤の主成分であるポリ（メタ）アクリル酸エステルを形成する単量体として、（メタ）アクリル酸ブチル、すなわちブチル（メタ）アクリレートを主成分とするものである。
ポリ（メタ）アクリル酸エステルを形成するために、ブチル（メタ）アクリレート以外の単量体は、本発明の効果を阻害しない範囲で、少量使用してもよく、例えば、（メタ）アクリル酸プロピル、（メタ）アクリル酸ペンチル、（メタ）アクリル酸ヘキシル、（メタ）アクリル酸へプチル、（メタ）アクリル酸オクチル、（メタ）アクリル酸−２−エチルヘキシル等が挙げられる。
これらのポリ（メタ）アクリル酸エステルは、トルエン、酢酸エチル等の溶剤中でのラジカル重合法等の公知な方法で製造することができる。
In the pressure-sensitive adhesive tape of the present invention, butyl (meth) acrylate, that is, butyl (meth) acrylate as a main component is used as a monomer for forming a poly (meth) acrylic acid ester which is a main component of a solvent-type acrylic pressure-sensitive adhesive. To do.
In order to form a poly (meth) acrylate, a monomer other than butyl (meth) acrylate may be used in a small amount as long as the effect of the present invention is not impaired. For example, propyl (meth) acrylate , Pentyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, octyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, and the like.
These poly (meth) acrylic acid esters can be produced by a known method such as a radical polymerization method in a solvent such as toluene or ethyl acetate.
ブチル（メタ）アクリレートは、ポリ（メタ）アクリル酸エステルを構成する単量体の主成分として、全単量体中、８０〜９９．９重量％程度を含むことが好ましい。好ましくは９０重量％以上、さらに好ましくは９３重量％以上の割合で用いられる。ブチル（メタ）アクリレートの割合が少ないと、良好な接着性の粘着剤が得られにくい。 It is preferable that butyl (meth) acrylate contains about 80-99.9 weight% in the whole monomer as a main component of the monomer which comprises poly (meth) acrylic acid ester. The ratio is preferably 90% by weight or more, more preferably 93% by weight or more. When the proportion of butyl (meth) acrylate is small, it is difficult to obtain a pressure-sensitive adhesive having good adhesiveness.
（ｉｉ）カルボキシル基含有単量体
アクリル系粘着剤には、構成する単量体として、ブチル（メタ）アクリレートのほかに、被着体への接着力を向上させること、架橋点を導入すること、粘着剤の凝集力を高めることを目的とし、カルボキシル基含有単量体を含有する必要がある。
カルボキシル基含有単量体は、分子中に少なくとも１つのカルボキシル基を含有していればよい。カルボキシル基含有単量体としては、アクリル酸、メタクリル酸、イタコン酸、マレイン酸、クロトン酸などがあげられ、アクリル酸が好ましい。
(Ii) Carboxyl group-containing monomer In addition to butyl (meth) acrylate as a constituent monomer, the acrylic pressure-sensitive adhesive improves adhesion to the adherend and introduces crosslinking points. In order to increase the cohesive strength of the pressure-sensitive adhesive, it is necessary to contain a carboxyl group-containing monomer.
The carboxyl group-containing monomer only needs to contain at least one carboxyl group in the molecule. Examples of the carboxyl group-containing monomer include acrylic acid, methacrylic acid, itaconic acid, maleic acid and crotonic acid, and acrylic acid is preferred.
カルボキシル基含有単量体は、アクリル系粘着剤を構成する全単量体中、０．１〜２０重量％程度、好ましくは０．５〜１０重量％の割合で用いられる。カルボキシル基含有単量体が０．１重量％未満では、凝集力が低下し、基材に対する密着性が低下するおそれがある。一方、２０重量％を超える場合には、被着体へのタックが低下するおそれがある。
なお、単量体として、ブチル（メタ）アクリレートおよびカルボキシル基含有単量体を用いる際には、それらの合計量が１００重量％になるように調整する。
The carboxyl group-containing monomer is used in a proportion of about 0.1 to 20% by weight, preferably 0.5 to 10% by weight, in all monomers constituting the acrylic pressure-sensitive adhesive. When the carboxyl group-containing monomer is less than 0.1% by weight, the cohesive force is lowered and the adhesion to the substrate may be lowered. On the other hand, if it exceeds 20% by weight, the tack to the adherend may be reduced.
In addition, when using a butyl (meth) acrylate and a carboxyl group containing monomer as a monomer, it adjusts so that those total amounts may be 100 weight%.
また、アクリル系粘着剤には、本発明の効果に支障がない範囲で、前記以外の単量体を使用してもよい。これら他の単量体等は、構成する全単量体中、１０重量％以下の割合で使用するのが好ましい。 Moreover, you may use a monomer other than the above for an acrylic adhesive in the range which does not have a trouble in the effect of this invention. These other monomers and the like are preferably used in a proportion of 10% by weight or less based on the total monomers.
上述の他の単量体としては、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート、２−ヒドロキシブチル（メタ）アクリレートなどの水酸基含有単量体などがあげられる。 As said other monomer, hydroxyl-containing monomers, such as 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, etc. are mention | raise | lifted.
（ｉｉｉ）タッキファイア（粘着付与剤）
本発明の粘着テープに使用される粘着剤層（Ｂ）のタッキファイア（粘着付与剤）（ｂ）としては、例えば、ロジン、ロジン誘導体、テルペン系樹脂、石油樹脂、アルキルフェノール樹脂、キシレン樹脂、クマロンインデン樹脂等が挙げられ、ロジン、ロジン誘導体などのロジン系タッキファイアが好ましい。
上記ロジン系タッキファイアとしては、例えば、松ヤニや松根油中のアビエチン酸を主成分とするロジン酸とグリセリンやペンタエリスリトールとのエステル、および、それらの水添物、不均化物が挙げられ、具体的には、ガムロジン、トール油ロジン、ウッドロジン、水素添加ロジン、不均化ロジン、重合ロジン、変性ロジン、ロジンジオール等が好適に例示される。また、ロジン誘導体としては、ロジンエステル類、ホルマリン変性ロジン類、不飽和カルボン酸変性ロジン類、フェノール変性ロジン類などが挙げられる。
さらに、ロジン系タッキファイアは、ロジン類及び各種ロジン誘導体を単用又は併用できる。
(Iii) Tackifier (tackifier)
Examples of the tackifier (tackifier) (b) of the pressure-sensitive adhesive layer (B) used in the pressure-sensitive adhesive tape of the present invention include rosin, rosin derivatives, terpene resins, petroleum resins, alkylphenol resins, xylene resins, Examples thereof include malon indene resins, and rosin tackifiers such as rosin and rosin derivatives are preferable.
Examples of the rosin tackifier include esters of rosin acid and glycerin and pentaerythritol mainly composed of abietic acid in pine ani and pine root oil, and hydrogenated products and disproportionates thereof. Specific examples include gum rosin, tall oil rosin, wood rosin, hydrogenated rosin, disproportionated rosin, polymerized rosin, modified rosin, and rosin diol. Examples of rosin derivatives include rosin esters, formalin-modified rosins, unsaturated carboxylic acid-modified rosins, and phenol-modified rosins.
Furthermore, the rosin tackifier can be used singly or in combination with rosins and various rosin derivatives.
上記ロジン系タッキファイア（ｂ）の添加量は、アクリル系粘着剤（ａ）１００重量部に対して、１〜２０重量部含有することが望ましく、１〜１０重量部がより好ましい。 The amount of the rosin tackifier (b) added is desirably 1 to 20 parts by weight, and more preferably 1 to 10 parts by weight with respect to 100 parts by weight of the acrylic pressure-sensitive adhesive (a).
（ｉｖ）硬化剤
本発明において、粘着剤層には、硬化剤（ｃ）が含有されることが好ましい。硬化剤（ｃ）として、架橋剤を用いることにより、アクリル系ポリマーを架橋させ、粘着剤としての凝集力を一層大きくすることができる。
架橋剤には、従来公知のものが広く包含される。架橋剤としては、特に、多官能性メラミン化合物、多官能性エポキシ化合物、多官能性イソシアネート化合物が好ましく、特に多官能性イソシアネート化合物がより好ましい。具体的な多官能性イソシアネート化合物の商品名としては、日本ポリウレタン社製の「コロネートＬ４５Ｅ」が挙げられる。
硬化剤として、単独で又は２種以上混合して使用することができる。
(Iv) Curing Agent In the present invention, the pressure-sensitive adhesive layer preferably contains a curing agent (c). By using a cross-linking agent as the curing agent (c), the acrylic polymer can be cross-linked and the cohesive force as an adhesive can be further increased.
A conventionally well-known thing is widely included in a crosslinking agent. Especially as a crosslinking agent, a polyfunctional melamine compound, a polyfunctional epoxy compound, and a polyfunctional isocyanate compound are preferable, and a polyfunctional isocyanate compound is especially more preferable. As a trade name of a specific polyfunctional isocyanate compound, “Coronate L45E” manufactured by Nippon Polyurethane Co., Ltd. may be mentioned.
As a hardening | curing agent, it can use individually or in mixture of 2 or more types.
上記硬化剤（ｃ）の添加量は、アクリル系粘着剤（ａ）１００重量部に対して、０．０１〜１０重量部程度とするのが好ましく、０．５〜２．０重量部がより好ましい。 The addition amount of the curing agent (c) is preferably about 0.01 to 10 parts by weight and more preferably 0.5 to 2.0 parts by weight with respect to 100 parts by weight of the acrylic pressure-sensitive adhesive (a). preferable.
（ｉｖ）紫外線吸収剤
本発明の粘着テープに使用される粘着剤層（Ｂ）の粘着剤には、紫外線吸収剤（ｄ）が用いられることが好ましい。
紫外線吸収剤としては、ベンゾトリアゾール化合物、ベンゾフェノン化合物、トリアジン化合物、マロン酸エステル化合物、シアノアクリレート化合物、ベンゾオキサゾリン化合物等の有機紫外線吸収剤や酸化セリウム、酸化亜鉛等の無機紫外線吸収剤が挙げられ、好ましくは有機紫外線吸収剤であり、より好ましくはベンゾトリアゾール化合物である。
(Iv) Ultraviolet absorber It is preferable that an ultraviolet absorber (d) is used for the adhesive of the adhesive layer (B) used for the adhesive tape of this invention.
Examples of UV absorbers include organic UV absorbers such as benzotriazole compounds, benzophenone compounds, triazine compounds, malonic ester compounds, cyanoacrylate compounds, and benzoxazoline compounds, and inorganic UV absorbers such as cerium oxide and zinc oxide. An organic ultraviolet absorber is preferable, and a benzotriazole compound is more preferable.
ベンゾトリアゾール系紫外線吸収剤の具体例としては、例えば、２−（５−メチル−２−ヒドロキシフェニル）ベンゾトリアゾール、２−（３，５−ジ−ｔｅｒｔ−ブチル−２−ヒドロキシフェニル）ベンゾトリアゾール、２−（３−ｔｅｒｔ−ブチル−５−メチル−２−ヒドロキシフェニル）−５−クロロベンゾトリアゾール、２−（３，５−ジ−ｔｅｒｔ−ブチル−２−ヒドロキシフェニル）−５−クロロベンゾトリアゾール、２−（２’−ヒドロキシ−５−オクチルフェニル）ベンゾトリアゾール等が例示され、本発明においては、２−（３−ｔｅｒｔ−ブチル−５−メチル−２−ヒドロキシフェニル）−５−クロロベンゾトリアゾールが好適である。具体的な商品名としては、チバスペシャルティー社製の「チヌビン３２６」が挙げられる。 Specific examples of the benzotriazole ultraviolet absorber include, for example, 2- (5-methyl-2-hydroxyphenyl) benzotriazole, 2- (3,5-di-tert-butyl-2-hydroxyphenyl) benzotriazole, 2- (3-tert-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di-tert-butyl-2-hydroxyphenyl) -5-chlorobenzotriazole, 2- (2′-hydroxy-5-octylphenyl) benzotriazole and the like are exemplified, and in the present invention, 2- (3-tert-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole is Is preferred. A specific product name is “Chinubin 326” manufactured by Ciba Specialty.
ベンゾトリアゾール系紫外線吸収剤（ｄ）の配合量は、アクリル系粘着剤（ａ）１００重量部に対して、０．５〜３．０重量部が好ましく、１．０〜３．０重量部がより好ましい。 The blending amount of the benzotriazole ultraviolet absorber (d) is preferably 0.5 to 3.0 parts by weight, and 1.0 to 3.0 parts by weight with respect to 100 parts by weight of the acrylic pressure-sensitive adhesive (a). More preferred.
（ｖ）その他の配合剤
本発明の粘着テープにおいて、粘着剤層（Ｂ）を構成する組成物中には、必要に応じて、軟化剤、老化防止剤、充填剤、離型剤、可塑剤、安定剤、顔料、酸化防止剤などの公知の添加剤を添加することができる。
(V) Other compounding agents In the pressure-sensitive adhesive tape of the present invention, in the composition constituting the pressure-sensitive adhesive layer (B), if necessary, a softening agent, an anti-aging agent, a filler, a release agent, a plasticizer Known additives such as stabilizers, pigments and antioxidants can be added.
（２）形成方法
本発明の粘着テープにおいて、粘着剤層（Ｂ）の形成方法としては、粘着剤を塗工すればよく、粘着剤の塗工方法としては、基材（Ａ）の片面に、トルエン、ヘキサン、キシレン、酢酸エチルなどの溶剤に溶解させた粘着剤溶液を、ロールコータ、ダイコータなどを用いて塗布したり、または基材フィルムとの共押出などにより形成されるが、好ましくは基材フィルムの片面をコロナ放電処理し、処理面に粘着剤溶液を塗布することにより形成する。
粘着剤層（Ｂ）の厚さ（乾燥後）は、使用目的によって適宜決定され、１０〜５０μｍ程度であり、好ましくは２０〜４０μｍであり、より好ましくは２５〜３５μｍである。
(2) Forming method In the pressure-sensitive adhesive tape of the present invention, the pressure-sensitive adhesive layer (B) may be formed by applying a pressure-sensitive adhesive. It is preferably formed by applying a pressure-sensitive adhesive solution dissolved in a solvent such as toluene, hexane, xylene, or ethyl acetate, using a roll coater, a die coater, or the like, or by co-extrusion with a base film. One side of the substrate film is subjected to corona discharge treatment, and the pressure-sensitive adhesive solution is applied to the treated surface.
The thickness (after drying) of the pressure-sensitive adhesive layer (B) is appropriately determined depending on the purpose of use, and is about 10 to 50 μm, preferably 20 to 40 μm, and more preferably 25 to 35 μm.
また、次項で記載するが、印刷層（Ｃ）が基材（Ａ）と粘着剤層（Ｂ）との間に形成される場合は、基材フィルムの片面に、インクをグラビア印刷、フレキソ印刷などにより印刷した後、上記と同様な方法により粘着剤層を形成する。グラビア塗工が好適である。
塗工システムとしては、例えば、ダイレクトグラビアコーター、リバースグラビアコーター、オフセットグラビアコーター等が挙げられる。塗工実施上、必要ならば、溶剤で粘着剤の組成物の粘度を、適宜調整することが望ましい。
In addition, as described in the next section, when the printing layer (C) is formed between the base material (A) and the pressure-sensitive adhesive layer (B), the gravure printing or flexographic printing is performed on one side of the base film. After printing by the above, an adhesive layer is formed by the same method as described above. Gravure coating is preferred.
Examples of the coating system include a direct gravure coater, a reverse gravure coater, and an offset gravure coater. If necessary, it is desirable to adjust the viscosity of the pressure-sensitive adhesive composition with a solvent, as needed.
３．印刷層（Ｃ）
本発明の粘着テープは、基材（Ａ）と粘着剤層（Ｂ）との間に、印刷層（Ｃ）を設けることが好ましい。印刷層（Ｃ）は、活性水素をもつ基を有するインクから形成されるものが好ましい。活性水素をもつ基を有するインクとしては、例えば、大日精化（株）製のＮＢ−５００、ＮＢ−３００などが挙げられる。
3. Print layer (C)
In the pressure-sensitive adhesive tape of the present invention, a printing layer (C) is preferably provided between the base material (A) and the pressure-sensitive adhesive layer (B). The printing layer (C) is preferably formed from an ink having a group having active hydrogen. Examples of the ink having a group having active hydrogen include NB-500 and NB-300 manufactured by Dainichi Seika Co., Ltd.
印刷層（Ｃ）を基材（Ａ）と粘着剤層（Ｂ）との間に設けると、該インク中の活性水素が粘着剤層に含まれる架橋剤、例えば、多官能性イソシアネート化合物などと化学反応して、印刷層（Ｃ）と粘着剤層（Ｂ）との接着性を向上し、印刷層と粘着剤層の間の破壊を防止することができる。 When the printing layer (C) is provided between the substrate (A) and the pressure-sensitive adhesive layer (B), a crosslinking agent in which active hydrogen in the ink is contained in the pressure-sensitive adhesive layer, such as a polyfunctional isocyanate compound, Chemical reaction can improve the adhesion between the printing layer (C) and the pressure-sensitive adhesive layer (B), and can prevent the breakage between the printing layer and the pressure-sensitive adhesive layer.
印刷層の厚さは、特に制限されないが、通常０．５〜６μｍ程度であり、好ましくは１〜３μｍである。該印刷層には、バインダー成分としてのエラストマー、投錨性付与の添加剤（例えば、塩素化ポリエチレン、ポリウレタンなど）の添加剤を配合してもよい。 The thickness of the printing layer is not particularly limited, but is usually about 0.5 to 6 μm, preferably 1 to 3 μm. The printed layer may contain an elastomer as a binder component and an additive for imparting anchoring properties (for example, chlorinated polyethylene, polyurethane, etc.).
４．粘着テープの使用方法
本発明の物品の仮止め固定用粘着テープは、例えば、電化製品、ＯＡ機器等の物品を製品出荷する際に、被着体である前記物品を梱包するにあたり、物品の内部部品やドア等の被着部分（例えば印刷鋼板や樹脂板等）を仮止め固定するために、前記被着部分に貼り付けて用いることができる。例えば、物品が冷蔵庫の場合には、物品の仮止め固定用粘着テープは、冷蔵庫のドア等の仮止め固定に用いられる。
したがって、本発明では、物品の仮止め固定用粘着テープを用いることを特徴とする物品の仮止め固定方法や、物品の仮止め固定用粘着テープにより、物品が、仮止め固定されていることを特徴とする仮止め固定物品も、提供することができる。
4). Method of Using Adhesive Tape The adhesive tape for temporarily fixing the article of the present invention is used, for example, when packing the article, which is an adherend, when the article such as an electrical appliance or OA device is shipped. In order to temporarily fix and fix a part to be attached such as a part or a door (for example, a printed steel plate or a resin plate), the part can be attached to the part to be used. For example, when the article is a refrigerator, the adhesive tape for temporarily fixing the article is used for temporarily fixing the refrigerator door or the like.
Therefore, in the present invention, the article is temporarily fixed by the method of temporarily fixing and fixing the article characterized by using the adhesive tape for temporarily fixing the article and the adhesive tape for temporarily fixing and fixing the article. A featured temporary fix fixture can also be provided.
以下に、本発明の実施例及び比較例によって、本発明をさらに詳細に説明するが、本発明は、これらの実施例によってなんら限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples of the present invention, but the present invention is not limited to these Examples.
［実施例１］
粘着剤モノマーとして、ブチルアクリレート９４重量部、アクリル酸１２重量部、２−ヒドロキシエチル（メタ）アクリレート０．２重量部を使用し、調製したアクリル系粘着剤１００重量部に、軟化点１３５℃の重合ロジン系タッキファイア樹脂（荒川化学ペンセルＤ１３５）を２．５重量部、硬化剤として多官能性イソシアネート化合物（日本ポリウレタン工業製「コロネートＬ−４５」）を１．０重量部、紫外線吸収剤（チバスペシャルティー社製「チヌビン３２６」）を１．８重量部添加し、粘着剤を調製した。
次に、基材としての厚さ３８μｍの二軸延伸されたポリプロピレンフィルムに、調製した粘着剤を、乾燥厚みが２５μｍとなるように、アプリケーターにて塗工し、１００℃の雰囲気下で５分乾燥させ、粘着テープを作製した。
[Example 1]
As a pressure-sensitive adhesive monomer, 94 parts by weight of butyl acrylate, 12 parts by weight of acrylic acid, and 0.2 parts by weight of 2-hydroxyethyl (meth) acrylate were used, and 100 parts by weight of the prepared acrylic pressure-sensitive adhesive had a softening point of 135 ° C. 2.5 parts by weight of a polymerized rosin-based tackifier resin (Arakawa Chemical Pencel D135), 1.0 part by weight of a polyfunctional isocyanate compound (“Coronate L-45” manufactured by Nippon Polyurethane Industry) as a curing agent, an ultraviolet absorber ( 1.8 parts by weight of “Chinubin 326” manufactured by Ciba Specialty Co., Ltd. was added to prepare an adhesive.
Next, the prepared pressure-sensitive adhesive was applied to a biaxially stretched polypropylene film having a thickness of 38 μm as a base material with an applicator so that the dry thickness was 25 μm, and the reaction was performed at 100 ° C. for 5 minutes. It dried and produced the adhesive tape.
［実施例２］
実施例１において、粘着剤モノマーとして、ブチルアクリレート９０重量部、アクリル酸１０重量部、２−ヒドロキシエチル（メタ）アクリレート０．３重量部を使用し、また、タッキファイア樹脂を５重量部添加した以外は、実施例１と同様に、粘着テープを作製した。
[Example 2]
In Example 1, 90 parts by weight of butyl acrylate, 10 parts by weight of acrylic acid, 0.3 parts by weight of 2-hydroxyethyl (meth) acrylate were used as the adhesive monomer, and 5 parts by weight of tackifier resin was added. Except for the above, an adhesive tape was prepared in the same manner as in Example 1.
［実施例３］
実施例１において、粘着剤モノマーとして、ブチルアクリレート９９重量部、アクリル酸７重量部、２−ヒドロキシエチル（メタ）アクリレート０．２重量部を使用し、また、タッキファイア樹脂を１０重量部添加した以外は、実施例１と同様に、粘着テープを作製した。
[Example 3]
In Example 1, 99 parts by weight of butyl acrylate, 7 parts by weight of acrylic acid, 0.2 parts by weight of 2-hydroxyethyl (meth) acrylate were used as the adhesive monomer, and 10 parts by weight of tackifier resin was added. Except for the above, an adhesive tape was prepared in the same manner as in Example 1.
［比較例１］
実施例１において、タッキファイア樹脂を添加しない以外は、実施例１と同様に、粘着テープを作製した。
[Comparative Example 1]
In Example 1, an adhesive tape was produced in the same manner as in Example 1 except that the tackifier resin was not added.
［比較例２］
実施例２において、タッキファイア樹脂を添加しない以外は、実施例２と同様に、粘着テープを作製した。
[Comparative Example 2]
In Example 2, an adhesive tape was produced in the same manner as in Example 2 except that no tackifier resin was added.
［比較例３］
実施例３において、タッキファイア樹脂を添加しない以外は、実施例３と同様に、粘着テープを作製した。
[Comparative Example 3]
In Example 3, an adhesive tape was produced in the same manner as in Example 3 except that no tackifier resin was added.
［比較例４］
実施例１において、粘着剤モノマーとして、ブチルアクリレート６０重量部、２−エチルヘキシルアクリレート４０重量部、アクリル酸５重量部を使用し、また、タッキファイア樹脂を２．５重量部添加した以外は、実施例１と同様に、粘着テープを作製した。
[Comparative Example 4]
In Example 1, except that 60 parts by weight of butyl acrylate, 40 parts by weight of 2-ethylhexyl acrylate, 5 parts by weight of acrylic acid were used as the adhesive monomer, and 2.5 parts by weight of tackifier resin was added. In the same manner as in Example 1, an adhesive tape was produced.
（評価）
実施例１〜３と比較例１〜４で作製した粘着テープを、幅２０ｍｍに切断し、テープの先端５ｍｍを折り返し、指の腹で十分に圧着し、タブ状とした。
このタブ状テープを、ポリスチレン板に、タブ部分が接触しないように貼付し、６０℃９５％のオーブン内に放置し、タブ状体の挙動を確認した。評価結果を表１に示す。
(Evaluation)
The adhesive tapes produced in Examples 1 to 3 and Comparative Examples 1 to 4 were cut into a width of 20 mm, the tip of the tape was folded back 5 mm, and sufficiently crimped with the belly of the finger to form a tab.
This tab-like tape was affixed to a polystyrene plate so that the tab portion did not come in contact, and was left in an oven at 60 ° C. and 95% to confirm the behavior of the tab-like body. The evaluation results are shown in Table 1.
表１の評価結果から明らかなように、実施例１〜３の粘着テープは、２４０時間後でも、剥がれがなく、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を示した。一方、比較例１〜４の粘着テープでは、優れたタブ適性が得られなかった。 As is apparent from the evaluation results in Table 1, the adhesive tapes of Examples 1 to 3 showed excellent tab suitability that they did not peel off even after 240 hours and were difficult to peel off even when the adhesive layers were pasted together. On the other hand, in the adhesive tapes of Comparative Examples 1 to 4, excellent tab suitability was not obtained.
本発明の物品の仮止め固定用粘着テープは、被着体である物品の被着部分に貼り付けた状態で応力が発生しても剥がれにくく、また、粘着剤層同士を貼り付けても剥がれにくいという優れたタブ適性を有し、且つ、目的を達成した後、剥離する際には容易に剥がすことができ、しかも糊残りが生じにくいため、産業上の利用可能性が高い。 The pressure-sensitive adhesive tape for temporarily fixing the article of the present invention is hardly peeled off even when stress is generated in a state of being stuck on the adherend part of the article which is the adherend, and is peeled off even if the adhesive layers are stuck together. It has excellent tab suitability that it is difficult, and after achieving the purpose, it can be easily peeled off, and adhesive residue is hardly generated, so that it is highly industrially applicable.
Claims (8)
粘着剤層（Ｂ）は、アクリル系粘着剤（ａ）１００重量部に対して、ロジン系タッキファイア（ｂ）１〜２０重量部含有し、且つ、アクリル系粘着剤（ａ）は、ブチル（メタ）アクリレート８０〜９９．９重量％とアクリル酸０．１〜２０重量％とからなることを特徴とする物品の仮止め固定用粘着テープ。 An adhesive tape for temporarily fixing an article having an adhesive layer (B) mainly composed of an acrylic adhesive (a) on one side of a base material (A) made of a biaxially stretched polypropylene film,
The pressure-sensitive adhesive layer (B) contains 1 to 20 parts by weight of a rosin tackifier (b) with respect to 100 parts by weight of the acrylic pressure-sensitive adhesive (a), and the acrylic pressure-sensitive adhesive (a) is butyl ( An adhesive tape for temporarily fixing an article comprising 80 to 99.9% by weight of (meth) acrylate and 0.1 to 20% by weight of acrylic acid.