JP2001279024A - Reinforcing staple fiber-containing rubber composition and transmission belt using the same - Google Patents
Reinforcing staple fiber-containing rubber composition and transmission belt using the sameInfo
- Publication number
- JP2001279024A JP2001279024A JP2000090110A JP2000090110A JP2001279024A JP 2001279024 A JP2001279024 A JP 2001279024A JP 2000090110 A JP2000090110 A JP 2000090110A JP 2000090110 A JP2000090110 A JP 2000090110A JP 2001279024 A JP2001279024 A JP 2001279024A
- Authority
- JP
- Japan
- Prior art keywords
- belt
- fibers
- rubber
- rubber layer
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は補強用短繊維含有ゴ
ム組成物及びこれを用いた伝動ベルトに係り、詳しくは
耐摩耗性を維持しかつ摩擦係数を向上させた補強用短繊
維含有ゴム組成物、及びスリップを抑えて耐発音性に優
れベルトの走行寿命を改善した伝動ベルトに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rubber composition containing a reinforcing short fiber and a power transmission belt using the same, and more particularly to a rubber composition containing a reinforcing short fiber which maintains abrasion resistance and improves a friction coefficient. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a power transmission belt that suppresses an object and slips, has excellent sound resistance, and has an improved running life.
【0002】[0002]
【従来の技術】Vリブドベルトはクッションゴム層中に
心線を埋設し、該クッションゴム層の上部には必要に応
じてカバー帆布を積層し、そして該クッションゴム層の
下部に複数のリブ部を設けている。このVリブドベルト
はVベルトに代わって自動車のエアーコンプレッサーや
オルタネータ等の補機駆動の動力伝動用として広く使用
されている。従来、ベルトの動力を効率よく伝達するた
めには、ベルトとプーリ間のスリップ率を小さくする必
要があり、ベルト張力を高めてスリップ率を小さくして
いた。2. Description of the Related Art In a V-ribbed belt, a core wire is buried in a cushion rubber layer, a cover canvas is laminated on an upper portion of the cushion rubber layer as necessary, and a plurality of rib portions are provided below the cushion rubber layer. Provided. This V-ribbed belt is widely used in place of the V-belt for power transmission of auxiliary equipment such as an air compressor and an alternator of an automobile. Conventionally, in order to efficiently transmit the power of the belt, it is necessary to reduce the slip ratio between the belt and the pulley, and the belt tension is increased to reduce the slip ratio.
【0003】この種のベルトでは、リブ部に綿、ナイロ
ン、ビニロン、レーヨン、アラミド繊維などの短繊維群
をベルト幅への配向性を保って埋設することにより、ベ
ルトの摩擦伝動部の耐側圧性を高め、更に埋設した短繊
維の一部を積極的に摩擦伝動部の両側壁面に露出させる
ことによって、耐摩耗性を向上させている。In this type of belt, a short fiber group such as cotton, nylon, vinylon, rayon, and aramid fibers is buried in a rib portion while maintaining the orientation to the belt width, so that a lateral pressure resistance of a friction transmission portion of the belt is improved. In addition, the wear resistance is improved by positively exposing a part of the buried short fibers to both side walls of the friction transmission portion.
【0004】更に、埋設した短繊維の一部をベルト側面
より意図的に突出させることによって、リブ部の摩擦性
能および粘着による発音の抑止効果を狙った伝動ベルト
も提案されている。Further, there has been proposed a power transmission belt which aims at a frictional performance of a rib portion and an effect of suppressing sound generation due to adhesion by intentionally protruding a part of embedded short fibers from a side surface of the belt.
【0005】また、上記ベルトの効果をさらに前進する
ために摩擦伝動部の両側壁面に突出させる短繊維とし
て、特にアラミド繊維を用いることにより、アラミド繊
維特有の耐摩耗性によりベルト自体の耐久性の向上を意
図した伝動ベルトが、例えば特開平1−164839号
公報に開示されている。[0005] Further, in order to further advance the effect of the belt, aramid fibers are used as the short fibers protruding from both side walls of the friction transmission portion. A transmission belt intended for improvement is disclosed, for example, in Japanese Patent Application Laid-Open No. 1-164839.
【0006】[0006]
【発明が解決しようとする課題】しかし、ベルトの圧縮
ゴム層内に埋設させたアラミド繊維をリブ部表面から突
出させ、あるいは突出して折れ曲げた場合には、アラミ
ド繊維の剛性が高過ぎて、ベルト走行時に耳ざわりなこ
すれ音が発生することがあった。However, when the aramid fiber embedded in the compressed rubber layer of the belt is projected from the surface of the rib portion or is bent by projecting, the rigidity of the aramid fiber is too high. A harsh rubbing noise was sometimes generated during belt running.
【0007】また、最近の代替フロンを用いたエアーコ
ンプレッサー等の補機を駆動させるときには、とりわけ
張力の低下したベルトがエアーコンプレッサーの回転を
スタートさせた時に瞬時にスリップにより鳴き音を発生
していた。この鳴き音は連続的でなく、エアーコンプレ
ッサーのピークトルク時に発生していた。Further, when driving an auxiliary machine such as an air compressor using a recent substitute for chlorofluorocarbon, a belt, whose tension has decreased, particularly generates a squealing sound due to slipping when the rotation of the air compressor is started. . This squealing sound was not continuous and was generated at the peak torque of the air compressor.
【0008】更に、リブ部に綿、ナイロン、ビニロン、
レーヨン、アラミド繊維などの短繊維群をベルト幅への
配向性を保って埋設しても、これらの短繊維が塊りなっ
てゴム中へ分散することがあった。特に、帆布、デニム
等を構成しているスパン糸の綿糸をカット糸として使用
した場合には、綿糸には撚りが掛かっているため、綿糸
自体を解して単糸にする必要があり、これをしないと分
散性に欠き、ゴム中で短繊維が塊りなって分散不良にな
り、またスリップによる発音が発生した。Further, cotton, nylon, vinylon,
Even when a group of short fibers such as rayon and aramid fibers is buried while maintaining the orientation to the belt width, these short fibers may be aggregated and dispersed in the rubber. In particular, when a spun cotton yarn constituting canvas, denim, or the like is used as a cut yarn, the cotton yarn is twisted. Otherwise, the dispersibility was lacking, short fibers clumped in the rubber, resulting in poor dispersion, and sound was generated due to slip.
【0009】本発明はこのような問題点を改善するもの
であり、これに対処するもので耐摩耗性を維持しかつ摩
擦係数を向上させた補強用短繊維含有ゴム組成物、及び
スリップを抑えて耐発音性に優れベルトの走行寿命を改
善した伝動ベルトを提供することを目的とする。The present invention has been made to solve the above problems, and in order to solve the problems, a rubber composition containing a reinforcing short fiber, which has improved abrasion coefficient while maintaining abrasion resistance, and suppresses slip. It is an object of the present invention to provide a power transmission belt having excellent sound-resistance and improved running life of the belt.
【0010】[0010]
【課題を解決するための手段】即ち、本願の請求項1記
載の発明では、補強用短繊維をゴム中に分散させた補強
用短繊維含有ゴム組成物において、上記補強用短繊維と
してアラミド繊維とノボロイド繊維を併用した補強用短
繊維含有ゴム組成物にあり、アラミド繊維によって耐摩
耗性を維持して伝達性能を良好にし、更にはノボロイド
繊維を配合することによって摩擦係数を制御することが
できるために、スリップを抑えることができて耐発音性
にも効果がある。According to the first aspect of the present invention, there is provided a rubber composition containing short fibers for reinforcement in which short fibers for reinforcement are dispersed in rubber, wherein aramid fibers are used as the short fibers for reinforcement. In the rubber composition containing short fibers for reinforcement, which is used in combination with a novoloid fiber, the abrasion resistance is maintained by the aramid fiber to improve the transmission performance, and further, the friction coefficient can be controlled by blending the novoloid fiber. Therefore, the slip can be suppressed, and the pronunciation resistance is also effective.
【0011】本願の請求項2記載の発明では、補強用短
繊維としてアラミド繊維とノボロイド繊維を併用した補
強用短繊維含有ゴム組成物を、伝動ベルトを構成するゴ
ム部材の少なくとも一部に使用した伝動ベルトにあり、
アラミド繊維によって耐摩耗性を維持して伝達性能を良
好にし、更にはノボロイド繊維を配合することによって
摩擦係数を制御してスリップを抑え耐発音性に優れる伝
動ベルトを得ることができる効果がある。In the invention according to claim 2 of the present application, the rubber composition containing short fibers for reinforcement, which uses both aramid fibers and novoloid fibers as short fibers for reinforcement, is used for at least a part of the rubber member constituting the power transmission belt. On the transmission belt,
The aramid fiber maintains the wear resistance to improve the transmission performance, and the addition of the novoloid fiber has the effect of controlling the friction coefficient to suppress the slip and obtain a power transmission belt having excellent sound resistance.
【0012】本願の請求項3記載の発明では、伝動ベル
トがベルト長さ方向に沿って心線を埋設した接着ゴム層
と、ベルト長さ方向に延びる少なくとも2つのリブ部を
有する圧縮ゴム層とからなるVリブドベルトであり、少
なくとも上記圧縮ゴム層に、補強用短繊維含有ゴム組成
物を用いた場合である。According to the third aspect of the present invention, the transmission belt has an adhesive rubber layer having a core buried along the belt length direction and a compression rubber layer having at least two rib portions extending in the belt length direction. V-ribbed belt comprising a rubber composition containing short reinforcing fibers for at least the compressed rubber layer.
【0013】本願の請求項4記載の発明では、伝動ベル
トがベルト長さ方向に沿って心線を埋設した接着ゴム層
と、圧縮ゴム層とからなり、少なくとも上記圧縮ゴム層
に、補強用短繊維含有ゴム組成物を用いた場合である。[0013] In the invention according to claim 4 of the present application, the power transmission belt is composed of an adhesive rubber layer having a core wire buried along the belt length direction and a compression rubber layer. This is the case where a fiber-containing rubber composition is used.
【0014】[0014]
【発明の実施の形態】図1は補強用短繊維含有ゴム組成
物を使用したVリブドベルトの断面図を示しており、こ
のVリブドベルト1は、ポリエステル繊維、アラミド繊
維、ガラス繊維を素材とする高強度で低伸度のコードよ
りなる心線2を接着ゴム層3中に埋設し、その下側に弾
性体層である圧縮ゴム層4を有している。この圧縮ゴム
層4にはベルト長手方向にのびる断面略三角形の複数の
リブ7が設けられ、またベルト表面には付着したゴム付
帆布5が設けられている。FIG. 1 is a sectional view of a V-ribbed belt using a rubber composition containing a reinforcing short fiber. This V-ribbed belt 1 is made of polyester fiber, aramid fiber and glass fiber. A cord 2 made of a cord having high strength and low elongation is embedded in an adhesive rubber layer 3, and a compression rubber layer 4 as an elastic layer is provided below the core wire. The compressed rubber layer 4 is provided with a plurality of ribs 7 having a substantially triangular cross section extending in the longitudinal direction of the belt, and a rubber attached canvas 5 is provided on the surface of the belt.
【0015】前記圧縮ゴム層4には、ゴム中における補
強用短繊維の分散性を改善した補強用短繊維含有ゴム組
成物が使用されるが、ここで使用するゴムとしては水素
化ニトリルゴム、エチレン−α−オレフィンエラストマ
ー、クロロプレンゴム、天然ゴム、クロロスルファ化ポ
リエチレン、アルキル化クロロスルファ化ポリエチレ
ン、天然ゴム、スチレン・ブタジエンゴム、あるいはオ
レフィン系、エステル系、ウレタン系の熱可塑性エラス
トマーが使用される。For the compressed rubber layer 4, a rubber composition containing a reinforcing short fiber having improved dispersibility of the reinforcing short fiber in the rubber is used. The rubber used here is hydrogenated nitrile rubber, Ethylene-α-olefin elastomers, chloroprene rubber, natural rubber, chlorosulfated polyethylene, alkylated chlorosulfated polyethylene, natural rubber, styrene / butadiene rubber, or olefin, ester, or urethane thermoplastic elastomers are used.
【0016】上記のエチレン−α−オレフィンエラスト
マーは、エチレン−プロピレンゴム(EPR)やエチレ
ン−プロピレン−ジエンモノマー(EPDM)からなる
ゴムをいう。ジエンモノマーの例としては、ジシクロペ
ンタジエン、メチレンノルボルネン、エチリデンノルボ
ルネン、1,4−ヘキサジエン、シクロオクタジエンな
どがあげられる。The above-mentioned ethylene-α-olefin elastomer refers to a rubber composed of ethylene-propylene rubber (EPR) or ethylene-propylene-diene monomer (EPDM). Examples of diene monomers include dicyclopentadiene, methylene norbornene, ethylidene norbornene, 1,4-hexadiene, cyclooctadiene, and the like.
【0017】補強用短繊維としては、アラミド繊維とノ
ボロイド繊維を併用することが必要であり、これらの繊
維に加えてナイロン、ポリエステル、ビニロン、レーヨ
ン、綿等も混入することができる。通常、アラミド繊維
やノボロイド繊維の長さは1〜10mmであり、素繊維
径が数μ〜数10μmである。It is necessary to use aramid fibers and novoloid fibers in combination as short reinforcing fibers, and in addition to these fibers, nylon, polyester, vinylon, rayon, cotton and the like can be mixed. Usually, the length of the aramid fiber or the novoloid fiber is 1 to 10 mm, and the elementary fiber diameter is several μm to several tens μm.
【0018】上記アラミド繊維は分子構造中に芳香環を
もつポリアミド繊維、例えば商品名コーネックス、ノー
メックス、ケブラー、テクノーラ、トワロン等である。The aramid fiber is a polyamide fiber having an aromatic ring in the molecular structure, for example, trade names such as Conex, Nomex, Kevlar, Technora, Twaron and the like.
【0019】ノボロイド繊維はノボラック型フェノール
繊維を紡糸後に硬化させて得られる繊維であり、この繊
維を添加することによって摩耗係数を制御することがで
きる。このノボロイド繊維の繊維長は3mm程度を下限
とし、10mm程度を上限とする3〜10mmの範囲が
適切である。なお、このような繊維長のノボロイド繊維
は、一般にチョップドファイバまたはミルドファイバと
して得ることができ、また、その繊維径は10〜30μ
m程度が好ましい。上記ノボロイド繊維は、例えば商品
名としてカイノール繊維(郡栄化学工業株式会社製)が
ある。The novoloid fiber is a fiber obtained by curing a novolak-type phenol fiber after spinning, and the abrasion coefficient can be controlled by adding this fiber. The fiber length of the novoloid fiber is suitably in a range of 3 to 10 mm with a lower limit of about 3 mm and an upper limit of about 10 mm. The novoloid fiber having such a fiber length can be generally obtained as a chopped fiber or a milled fiber, and the fiber diameter is 10 to 30 μm.
m is preferable. The novoloid fiber is, for example, a kainol fiber (manufactured by Gunei Chemical Industry Co., Ltd.) as a trade name.
【0020】アラミド繊維とノボロイド繊維の添加量は
ゴム100重量部に10〜40重量部であり、10重量
部未満であるとベルトに使用した場合に、ベルトの耐側
圧性が発揮されない。また、40重量部を超えると、短
繊維を混入することが困難になってくる。The addition amount of the aramid fiber and the novoloid fiber is 10 to 40 parts by weight per 100 parts by weight of rubber, and when the amount is less than 10 parts by weight, the belt does not exhibit the lateral pressure resistance when used for a belt. If it exceeds 40 parts by weight, it becomes difficult to mix short fibers.
【0021】アラミド繊維とノボロイド繊維の配合比率
の範囲は1/9〜9/1であり、好ましくは3/7〜7
/3であり、1/9未満の場合には、摩耗の進行が速
く、伝動ベルトの張力低下が大きく、伝達性が低下し、
スリップが発生する。一方、9/1を超えると、摩耗性
が良いが摩擦係数が小さくなってスリップしやすくな
る。The mixing ratio of the aramid fiber and the novoloid fiber is in the range of 1/9 to 9/1, preferably 3/7 to 7/1.
/ 3, and if it is less than 1/9, the progress of wear is fast, the tension of the transmission belt is greatly reduced, and the transmission is reduced.
Slip occurs. On the other hand, if it exceeds 9/1, the abrasion is good, but the coefficient of friction is small, and slip is likely to occur.
【0022】上記アラミド繊維とノボロイド繊維の補強
用短繊維は、レゾルシン・ホルマリン・ラテックス(R
F/L)の固形分重量比が1/1〜1/5であるRFL
液(レゾルシンとホルマリンとの初期縮合物をラテック
スに混合したもの)で処理され、かつRFL液の固形分
付着量が3〜10重量%である。RF/Lの比が1/1
を超えると、短繊維の凝集力が大きくなって分散性が悪
くなり、逆にRF/Lの比が1/5未満になると、ゴム
と短繊維との接着力が低下し、引張強さも低下する。更
に、RFL液の固形分付着量が10重量%を超えると、
処理液が固まって短繊維のフィラメント同士が分割しに
くくなり、逆に3重量%未満の場合には分割したフィラ
メント同士が絡まりやすくなって分散性が低下し、また
引張強さも低下する。無論、アラミド繊維とノボロイド
繊維の補強用短繊維は上記の接着処理を行う必要がな
い。The short fibers for reinforcement of the aramid fiber and the novoloid fiber are resorcinol-formalin latex (R).
F / L) having a solid content weight ratio of 1/1 to 1/5.
The RFL solution is treated with a liquid (a mixture of a latex of an initial condensate of resorcinol and formalin) and the RFL liquid has a solid content of 3 to 10% by weight. RF / L ratio is 1/1
When the ratio exceeds the above, the cohesive force of the short fibers increases and the dispersibility deteriorates. Conversely, when the RF / L ratio is less than 1/5, the adhesive force between the rubber and the short fibers decreases, and the tensile strength also decreases. I do. Further, when the solid content of the RFL liquid exceeds 10% by weight,
When the treatment liquid is solidified, the filaments of the short fibers are hardly divided, and when the content is less than 3% by weight, the divided filaments are apt to be entangled with each other, resulting in reduced dispersibility and reduced tensile strength. Needless to say, it is not necessary to perform the above-mentioned bonding treatment on the reinforcing short fibers of the aramid fiber and the novoloid fiber.
【0023】上記ラテックスはスチレン・ブタジエン・
ビニルピリジン三元共重合体、クロロスルフォン化ポリ
エチレン、水素化ニトリルゴム、エピクロルヒドリン、
天然ゴム、SBR、クロロプレンゴム、オレフィン−ビ
ニルエステル共重合体等である。The latex is styrene-butadiene.
Vinylpyridine terpolymer, chlorosulfonated polyethylene, hydrogenated nitrile rubber, epichlorohydrin,
Natural rubber, SBR, chloroprene rubber, olefin-vinyl ester copolymer and the like.
【0024】更に、本発明のゴム組成物には、軟化剤、
カーボンブラックからなる補強剤、充填剤、老化防止
剤、加硫促進剤、加硫剤等が添加される。The rubber composition of the present invention further comprises a softener,
A reinforcing agent composed of carbon black, a filler, an antioxidant, a vulcanization accelerator, a vulcanizing agent and the like are added.
【0025】上記軟化剤としては、一般的なゴム用の可
塑剤、例えばジブチルフタレート(DBP)、ジオクチ
ルフタレート(DOP)等のフタレート系、ジオクチル
アジペート(DOA)等のアジペート系、ジオクチルセ
バケート(DOS)等のセバケート系、トリクレジルホ
スフェート等のホスフェートなど、あるいは一般的な石
油系の軟化剤が含まれる。上記軟化剤の添加量は、短繊
維の10vol%以上、好ましくは短繊維の30vol
%以上である。10vol%未満の場合には、軟化剤が
短繊維全体に行き渡らず、分散の悪い部分が生じる可能
性がある。Examples of the softener include plasticizers for general rubbers, for example, phthalates such as dibutyl phthalate (DBP) and dioctyl phthalate (DOP), adipates such as dioctyl adipate (DOA), and dioctyl sebacate (DOS). ), Phosphates such as tricresyl phosphate, and general petroleum softeners. The amount of the softener is 10 vol% or more of the short fibers, preferably 30 vol% of the short fibers.
% Or more. When the content is less than 10 vol%, the softener does not cover the entire short fiber, and there is a possibility that a poorly dispersed portion may be generated.
【0026】アラミド繊維とノボロイド繊維の補強用短
繊維含有ゴム組成物を作製する方法としては、まず第1
ステップのマスターバッチ練りとして、バンバリミキサ
ーのような密閉式混練機に、ゴム100重量部に10〜
40重量部の補強用短繊維と1〜10重量部の軟化剤を
投入して混練した後、混練したマスターバッチをいった
ん放出し、これを20〜50°Cまで冷却する。これは
ゴムのスコーチを防止するためである。次いで、得られ
たマスターバッチに所定量の補強剤、充填剤、老化防止
剤、加硫促進剤、加硫剤等をバンバリミキサー、オープ
ンロールを用いて仕上げ練りする。しかし、ゴム種によ
っては混練したマスターバッチをいったん放出し、冷却
する必要はなく、連続して仕上げ練りを行うことも可能
である。As a method for producing a rubber composition containing short fibers for reinforcement of aramid fibers and novoloid fibers, the first method is as follows.
As the master batch kneading of the step, 10 to 10 parts by weight of rubber were mixed in a closed kneader such as Banbury mixer.
After 40 parts by weight of the reinforcing short fibers and 1 to 10 parts by weight of the softening agent are added and kneaded, the kneaded master batch is once released and cooled to 20 to 50 ° C. This is to prevent rubber scorch. Next, a predetermined amount of a reinforcing agent, a filler, an antioxidant, a vulcanization accelerator, a vulcanizing agent, and the like are kneaded with the obtained master batch using a Banbury mixer and an open roll. However, depending on the type of rubber, it is not necessary to release the kneaded master batch once and cool it, and it is also possible to perform finish kneading continuously.
【0027】Vリブドベルト1の製造方法の一例は以下
の通りである。まず、円筒状の成形ドラムの周面に1〜
複数枚のカバー帆布とクッションゴム層とを巻き付けた
後、この上にロープからなる心線を螺旋状にスピニング
し、更に圧縮ゴム層を順次巻き付けて積層体を得た後、
これを加硫して加硫スリーブを得る。次に、加硫スリー
ブを駆動ロールと従動ロールに掛架され所定の張力下で
走行させ、更に回転させた研削ホイールを走行中の加硫
スリーブに当接するように移動して加硫スリーブの圧縮
ゴム層表面に3〜100個の複数の溝状部を一度に研削
する。このようにして得られた加硫スリーブを駆動ロー
ルと従動ロールから取り外し、該加硫スリーブを他の駆
動ロールと従動ロールに掛架して走行させ、カッターに
よって所定の幅に切断して個々のVリブドベルトに仕上
げる。An example of a method for manufacturing the V-ribbed belt 1 is as follows. First, on the peripheral surface of the cylindrical forming drum,
After winding a plurality of cover canvases and a cushion rubber layer, a cord made of a rope is spirally spun on this, and a compressed rubber layer is sequentially wound thereon to obtain a laminate,
This is vulcanized to obtain a vulcanized sleeve. Next, the vulcanizing sleeve is hung on a driving roll and a driven roll, and is run under a predetermined tension, and the rotated grinding wheel is moved so as to contact the running vulcanizing sleeve to compress the vulcanizing sleeve. A plurality of 3 to 100 groove portions are ground on the surface of the rubber layer at a time. The vulcanized sleeve obtained in this manner is removed from the drive roll and the driven roll, and the vulcanized sleeve is hung on another drive roll and the driven roll to travel, cut to a predetermined width by a cutter, and individually cut. Finish with a V-ribbed belt.
【0028】むろん、本発明においては、上記のVリブ
ドベルト以外にも、図2に示すようにベルトの上下表面
のみにゴム付帆布を付着したVベルト8も含む。このV
ベルト8は、心線2を接着ゴム層3中に埋設し、その下
側に弾性体層である圧縮ゴム層4を有している。この圧
縮ゴム層4には、コグを長手方向に沿って所定間隔で設
けてもよい。Of course, in the present invention, in addition to the above-described V-ribbed belt, a V-belt 8 having a rubber-attached cloth attached only to the upper and lower surfaces of the belt as shown in FIG. 2 is also included. This V
The belt 8 has the core wire 2 embedded in the adhesive rubber layer 3, and has a compressed rubber layer 4 as an elastic layer below the core wire 2. Cogs may be provided on the compressed rubber layer 4 at predetermined intervals along the longitudinal direction.
【0029】[0029]
【実施例】以下、本発明を実施例にて詳細に説明する。 実施例1〜4、比較例1〜2 表2に示すアラミド繊維とノボロイド繊維を表3に示す
RFL液に浸漬した後、200℃で2分間熱処理した。
その後、表1に示す配合からバンバリーミキサーで混練
後、カレンダーで圧延して厚さ1mmの短繊維入りゴム
シートを作製し、そして153°Cで20分加硫して得
られた加硫ゴムシートの物性を評価した。The present invention will be described below in detail with reference to examples. Examples 1-4, Comparative Examples 1-2 The aramid fibers and the novoloid fibers shown in Table 2 were immersed in the RFL solution shown in Table 3, and then heat-treated at 200 ° C for 2 minutes.
Thereafter, the mixture shown in Table 1 was kneaded with a Banbury mixer, rolled with a calender to produce a rubber sheet containing short fibers having a thickness of 1 mm, and then vulcanized at 153 ° C. for 20 minutes to obtain a vulcanized rubber sheet. Were evaluated for physical properties.
【0030】[0030]
【表1】 [Table 1]
【0031】[0031]
【表2】 [Table 2]
【0032】[0032]
【表3】 [Table 3]
【0033】更に、上記のゴム組成物を圧縮ゴム層に用
いたVリブドベルトを作製した。このVリブドベルトで
は、ポリエステル繊維のコードからなる心線が接着ゴム
層内に埋設され、その上側にゴム付綿帆布を2プライ積
層され、他方接着ゴム層の下側には圧縮ゴム層があって
3個のリブがベルト長手方向に有している。得られたV
リブドベルトはRMA規格による長さ1100mmのK
型3リブドベルトであり、リブピッチ3.56mm、リ
ブ高さ2.9mm、ベルト厚さ5.3mm、リブ角度4
0°である。Further, a V-ribbed belt using the above rubber composition for a compressed rubber layer was produced. In this V-ribbed belt, a cord made of a polyester fiber cord is buried in an adhesive rubber layer, and two layers of cotton canvas with rubber are laminated on the upper side thereof, while a compressed rubber layer is provided below the adhesive rubber layer. Three ribs are provided in the belt longitudinal direction. V obtained
The ribbed belt is 1100 mm long according to RMA standard.
Type 3 ribbed belt, rib pitch 3.56 mm, rib height 2.9 mm, belt thickness 5.3 mm, rib angle 4
0 °.
【0034】ここで圧縮ゴム層及び接着ゴム層を、それ
ぞれ上記のゴム組成物をカレンダーロールで圧延したも
のを用いた。圧縮ゴム層には短繊維が含まれベルト巾方
向に配向している。The compressed rubber layer and the adhesive rubber layer were each obtained by rolling the above rubber composition with a calender roll. The compressed rubber layer contains short fibers and is oriented in the belt width direction.
【0035】得られたゴム組成物の物性評価、作製した
Vリブドベルトの性能(摩耗減量、摩擦係数)を以下の
方法により調べた。その結果を表4に示す。The physical properties of the obtained rubber composition were evaluated, and the performance (loss of wear, coefficient of friction) of the produced V-ribbed belt was examined by the following methods. Table 4 shows the results.
【0036】1.ウイリアムズ摩擦試験 試験試料を短繊維が摩耗面に対して直角に配向するよう
に作製し、この試料を用いてJIS K6264に準
じ、1000回当たりの摩耗減量、摩擦力を測定した。1. Williams friction test A test sample was prepared so that the short fibers were oriented perpendicular to the wear surface, and the wear loss and friction force per 1000 times were measured using this sample according to JIS K6264.
【0037】2.DIN摩耗試験 試験試料を短繊維が摩耗面に対して直角に配向するよう
に作製し、この試料を用いてJIS K6264に準
じ、摩耗減量を測定した。2. DIN abrasion test A test sample was prepared so that the short fibers were oriented at right angles to the wear surface, and the wear loss was measured using this sample according to JIS K6264.
【0038】3.ベルト摩耗減量の測定 Vリブドベルトを直径80mmの駆動プーリ、直径80
mmの従動プーリ、そして直径120mmのテンション
プーリに所定の張力で懸架し、駆動プーリの回転数30
00rpm、従動プーリに係るトルク6.9N.mで、
6%のスリップを強制的に与えながら24時間走行させ
た。走行前後のベルト重量を測定し、その差から摩耗減
量を算出した。3. Measurement of loss of belt wear A V-ribbed belt was driven with a driving pulley having a diameter of 80 mm, and a diameter of 80 mm.
mm driven pulley, and a tension pulley having a diameter of 120 mm.
00 rpm, the torque of the driven pulley is 6.9 N. m
The vehicle ran for 24 hours while forcibly giving a 6% slip. The weight of the belt before and after running was measured, and the wear loss was calculated from the difference.
【0039】4.ベルト摩擦係数の測定 直径60mmのプーリに巻き掛けたVリブドベルトの一
端を固定し、他端に17.2Nの荷重をかけ、プーリを
43rpmで回転させながらベルト張力を測定し、次式
により摩擦係数を算出した。 摩擦係数=2×ln(T/17.2)/π (T:ベル
ト張力)4. Measurement of belt friction coefficient One end of a V-ribbed belt wound around a 60 mm diameter pulley is fixed, a load of 17.2 N is applied to the other end, and the belt tension is measured while rotating the pulley at 43 rpm. Was calculated. Coefficient of friction = 2 × ln (T / 17.2) / π (T: belt tension)
【0040】[0040]
【表4】 [Table 4]
【0041】この結果、アラミド短繊維のみの比較例1
は、摩耗減量が小さく、また摩擦力と摩擦係数も小さい
が、アラミド繊維とノボロイド繊維とを併用することに
より、摩耗減量を小さく抑えながら、摩擦力と摩擦係数
を上げることができる。As a result, Comparative Example 1 using only aramid short fibers
Although abrasion loss is small and frictional force and coefficient of friction are small, the combined use of aramid fiber and novoloid fiber can increase the frictional force and friction coefficient while keeping the loss on wear small.
【0042】[0042]
【発明の効果】以上のように本願請求項記載の補強用短
繊維含有ゴム組成物及びこれを用いた伝動ベルトでは、
上記補強用短繊維としてアラミド繊維とノボロイド繊維
を併用することにより、アラミド繊維によって耐摩耗性
を維持して伝達性能を良好にし、更にはノボロイド繊維
を配合することによって摩擦係数を制御することができ
るために、スリップを抑えることができて耐発音性にも
効果がある。As described above, the reinforcing short fiber-containing rubber composition and the power transmission belt using the same according to the present invention,
By using an aramid fiber and a novoloid fiber in combination as the reinforcing short fibers, the abrasion resistance is maintained by the aramid fiber to improve the transmission performance, and the friction coefficient can be controlled by blending the novoloid fiber. Therefore, the slip can be suppressed, and the pronunciation resistance is also effective.
【図1】本発明の補強用短繊維含有ゴム組成物を使用し
たVリブドベルトの断面図を示す。FIG. 1 is a sectional view of a V-ribbed belt using a reinforcing short fiber-containing rubber composition of the present invention.
【図2】本発明に係るVカットエッジタイプのVベルト
の縦断面図である。FIG. 2 is a vertical sectional view of a V-cut edge type V-belt according to the present invention.
1 Vリブドベルト 2 心線 3 接着ゴム層 4 圧縮ゴム層 5 ゴム付帆布 7 リブ Reference Signs List 1 V-ribbed belt 2 core wire 3 adhesive rubber layer 4 compressed rubber layer 5 canvas with rubber 7 rib
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) F16G 5/06 F16G 5/20 A 5/20 B29K 61:04 // B29K 61:04 77:00 77:00 105:12 105:12 B29L 29:00 B29L 29:00 B29C 67/14 Y Fターム(参考) 4F072 AA02 AB06 AB07 AD02 AL19 4F205 AA30 AA37 AA45 AB25 AG17 HA06 HA08 HA36 HA42 HB02 HC04 HC12 HC14 HC20 HE06 HF05 HK03 HK04 HM02 4J002 AC011 AC081 AC091 AC111 BB151 BB271 CC043 CF001 CK021 CL062 FA042 FA043 GM00 GN00 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) F16G 5/06 F16G 5/20 A 5/20 B29K 61:04 // B29K 61:04 77:00 77: 00 105: 12 105: 12 B29L 29:00 B29L 29:00 B29C 67/14 Y F term (reference) 4F072 AA02 AB06 AB07 AD02 AL19 4F205 AA30 AA37 AA45 AB25 AG17 HA06 HA08 HA36 HA42 HB02 HC04 HC12 HC14 HC20 HE06 HF05 HK03 HK04 HM02 4J002 AC011 AC081 AC091 AC111 BB151 BB271 CC043 CF001 CK021 CL062 FA042 FA043 GM00 GN00
Claims (4)
用短繊維含有ゴム組成物において、上記補強用短繊維と
してアラミド繊維とノボロイド繊維を併用することを特
徴とする補強用短繊維含有ゴム組成物。1. A reinforcing short fiber-containing rubber composition in which short reinforcing fibers are dispersed in rubber, wherein aramid fibers and novoloid fibers are used in combination as the reinforcing short fibers. Rubber composition.
ロイド繊維を併用した補強用短繊維含有ゴム組成物を、
伝動ベルトを構成するゴム部材の少なくとも一部に使用
したことを特徴とする伝動ベルト。2. A reinforcing short fiber-containing rubber composition comprising a combination of aramid fibers and novoloid fibers as reinforcing short fibers,
A power transmission belt used for at least a part of a rubber member constituting a power transmission belt.
線を埋設した接着ゴム層と、ベルト長さ方向に延びる少
なくとも2つのリブ部を有する圧縮ゴム層とからなるV
リブドベルトであり、少なくとも上記圧縮ゴム層に、補
強用短繊維含有ゴム組成物を用いた請求項2記載の伝動
ベルト。3. A transmission belt comprising: an adhesive rubber layer having a core embedded in a belt length direction; and a compression rubber layer having at least two rib portions extending in the belt length direction.
The power transmission belt according to claim 2, wherein the power transmission belt is a ribbed belt, and a rubber composition containing short reinforcing fibers is used for at least the compressed rubber layer.
線を埋設した接着ゴム層と、圧縮ゴム層とからなり、少
なくとも上記圧縮ゴム層に、補強用短繊維含有ゴム組成
物を用いた請求項2記載の伝動ベルト。4. The power transmission belt comprises an adhesive rubber layer in which a cord is embedded along the belt length direction and a compression rubber layer, and a rubber composition containing a reinforcing short fiber is used at least for the compression rubber layer. The power transmission belt according to claim 2.