JP2000297415A - Braille tile, and manufacture of braille tile and negative plate thereof - Google Patents
Braille tile, and manufacture of braille tile and negative plate thereofInfo
- Publication number
- JP2000297415A JP2000297415A JP11106130A JP10613099A JP2000297415A JP 2000297415 A JP2000297415 A JP 2000297415A JP 11106130 A JP11106130 A JP 11106130A JP 10613099 A JP10613099 A JP 10613099A JP 2000297415 A JP2000297415 A JP 2000297415A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- braille
- braille tile
- tile
- manufacture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、点字タイル及びそ
の製造方法に属し、さらに点字タイル用原板の製造方法
に属する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a braille tile and a method for manufacturing the same, and further relates to a method for manufacturing an original plate for a braille tile.
【０００２】[0002]
【従来の技術】歩道の路面や公共性の高い建築物の床面
には、点字タイルが敷設されている。点字タイルは表面
に凹凸が設けられたタイルで、視覚障害者の歩行を誘導
するために敷設される。点字タイルには平面視において
凸部が円形をなすもの（ポイント状点字タイル）と細長
い形をしたもの（ライン状点字タイル）とがあり、ポイ
ント状点字タイルが前方に注意すべしという意味をもつ
のに対し、ライン状点字タイルはその方向に歩行できる
という意味をもつ。2. Description of the Related Art Braille tiles are laid on the sidewalks and on the floors of highly public buildings. Braille tiles have irregularities on the surface and are laid to guide the visually impaired. Braille tiles are classified into two types: one with a circular projection in a plan view (point-shaped braille tile) and one with an elongated shape (line-shaped braille tile). The point-shaped braille tile has a meaning that attention should be paid to the front. On the other hand, a linear braille tile means that it can walk in that direction.
【０００３】従来の点字タイルは、塩化ビニールや合成
ゴムからなり、溶けた材料を金型に流し込んで成型する
ことにより製造される。従来の点字タイルの形状は、通
常３００×３００ｍｍの正方形で、路面等に敷く際には
これを一枚ずつ並べる。十字路、Ｌ字路又はＴ字路にお
いては、図６に示すように、それぞれ十字型、Ｌ字型、
Ｔ字型になるように並べ、また広い十字路等では敷設す
る枚数も増える。なお、図６中、符号Ｐは上記ポイント
状点字タイルを示し、符号Ｒは上記ライン状点字タイル
を示す。Conventional Braille tiles are made of vinyl chloride or synthetic rubber, and are manufactured by pouring a molten material into a mold and molding. Conventional Braille tiles are usually 300 × 300 mm square, and when laid on a road surface or the like, they are arranged one by one. In a crossroad, an L-shaped road or a T-shaped road, as shown in FIG.
They are arranged in a T-shape, and the number of sheets to be laid in a wide crossroad or the like increases. In FIG. 6, the symbol P indicates the point-shaped Braille tile, and the symbol R indicates the line-shaped Braille tile.
【０００４】[0004]
【発明が解決しようとする課題】しかし、従来の点字タ
イルは重く、例えば３００×３００ｍｍの点字タイルを
塩化ビニールで製造した場合、重量が約５００ｇにもな
る。そのため、点字タイルを施工現場まで輸送するのが
容易でなく、輸送コストも大きい。However, conventional Braille tiles are heavy, and for example, when a Braille tile of 300 × 300 mm is made of vinyl chloride, the weight is about 500 g. Therefore, it is not easy to transport the Braille tiles to the construction site, and the transportation cost is large.
【０００５】また、従来の点字タイルでは、敷設作業に
手間がかかり、十字路、Ｌ字路またはＴ字路での敷設作
業においては、手間がかかるばかりか熟練を要する。作
業を簡単にするためには、大きな点字タイルや、十字型
など正方形以外の点字タイルを用意して敷設する枚数を
減らせば良い。ところが、従来の製造方法では金型を用
いて成型するため、それだけ多種類の金型を用意しなけ
ればならず、またあまり大きくすることもできない。In the conventional Braille tiles, the laying work is troublesome, and the laying work at a crossroad, an L-shaped road or a T-shaped road is not only troublesome but also requires skill. In order to simplify the work, it is only necessary to prepare large Braille tiles or Braille tiles other than squares such as crosses and reduce the number of tiles to be laid. However, in the conventional manufacturing method, molding is performed using a mold, so that various types of molds must be prepared, and the size cannot be too large.
【０００６】さらに、従来の点字タイルでは、塩化ビニ
ールや合成ゴムを材料とするため、焼却するとダイオキ
シンを含む有毒ガスが発生する。したがって、環境を破
壊し、人の健康を害する怖れがある。それ故、本発明の
目的は、軽くて、敷設作業が簡単で、焼却の際にダイオ
キシンを発生させない点字タイル及びその製造方法を提
供することにある。また、本発明は、点字タイル用原板
の製造方法を提供することを目的とする。Further, in the case of conventional Braille tiles, toxic gas containing dioxin is generated when incinerated because of using vinyl chloride or synthetic rubber as a material. Therefore, there is a fear of destroying the environment and harming human health. Therefore, an object of the present invention is to provide a braille tile that is light, easy to lay, and does not generate dioxin during incineration, and a method for manufacturing the same. Another object of the present invention is to provide a method for producing a braille tile original plate.
【０００７】[0007]
【課題を解決するための手段】本発明の点字タイルは、
不織布を基材とすることを特徴としている。本発明の点
字タイルは不織布を基材とするため軽い。よって、施工
現場まで容易に輸送することができ、輸送費も削減でき
る。さらに、本発明の点字タイルは、従来の点字タイル
に比べて弾性が大きいので、その上を歩いても膝に負担
が掛からない。また、撥水性をもたせるために、不織布
表面に防水剤を塗布するか、防水シートを積層させるの
が好ましい。SUMMARY OF THE INVENTION A Braille tile of the present invention comprises:
It is characterized by using a nonwoven fabric as a base material. The braille tile of the present invention is light because it is based on a nonwoven fabric. Therefore, it can be easily transported to the construction site, and the transportation cost can be reduced. Furthermore, the braille tiles of the present invention have higher elasticity than conventional braille tiles, so that no burden is placed on the knees when walking on them. In order to impart water repellency, it is preferable to apply a waterproofing agent to the surface of the nonwoven fabric or to laminate a waterproofing sheet.
【０００８】上記点字タイルの製造方法は、扁平な不織
布を表面に凹凸ができるようにプレス成形し、所望の形
状に切断することを特徴としている。この製造方法で
は、表面に凹凸が設けられた不織布（以下、「点字タイ
ル用原板」という）をプレス成形により製造した後、こ
れを切断するだけで点字タイルが得られる。そのため、
不織布が十分に大きい限り、切断の仕方次第で大きな点
字タイルを製造することができ、また、十字型、Ｌ字
型、Ｔ字型など様々な形の点字タイルを容易に製造する
ことができる。したがって、敷設する際に必要な点字タ
イルの枚数が少なくて済み、作業が簡単になる。[0008] The method of manufacturing a braille tile is characterized in that a flat nonwoven fabric is press-formed so as to have irregularities on the surface and cut into a desired shape. In this manufacturing method, a braided tile can be obtained only by manufacturing a nonwoven fabric having irregularities on its surface (hereinafter, referred to as an “original plate for Braille tiles”) by pressing, and then cutting the nonwoven fabric. for that reason,
As long as the nonwoven fabric is sufficiently large, a large Braille tile can be manufactured depending on the cutting method, and Braille tiles of various shapes such as a cross, an L-shape, and a T-shape can be easily manufactured. Therefore, the number of Braille tiles required for laying is small, and the work is simplified.
【０００９】工場出荷段階では施工現場における点字タ
イルの配列が不明な場合などには、点字タイル用原板を
製造する際に、扁平な不織布を表面に凹凸ができるよう
にプレス成形するとともに、一群の凹凸ごとに区画する
切断用溝を設けておくと良い。切断用溝を設けることに
より、点字タイル用原板を施工現場で要求される配列に
合わせて容易に切断できるからである。また、不織布に
防水シートを積層させるには、プレス成形前の扁平な不
織布に積層させると良い。When the arrangement of Braille tiles at the construction site is unknown at the factory shipment stage, a flat nonwoven fabric is press-formed so as to have irregularities on the surface and a group of It is preferable to provide a cutting groove for partitioning each asperity. By providing the cutting grooves, the original plate for the braille tile can be easily cut in accordance with the arrangement required at the construction site. In addition, in order to laminate the waterproof sheet on the nonwoven fabric, it is preferable to laminate the flat nonwoven fabric before press molding.
【００１０】本発明において、不織布の材料をポリエチ
レンテレフタレート（ＰＥＴ）、又はポリプロピレンや
ポリエチレンなどのポリオレフィンにすることにより、
焼却に伴うダイオキシンの発生を防ぐことができる。特
に、ＰＥＴを材料にした場合には、飲料水用容器である
ペットボトルなどを再利用して作られ得るので、資源の
有効活用に役立つ。一方、ポリオレフィンの場合には、
ＰＥＴよりも軽くて、耐薬品性が良いという利点があ
る。In the present invention, the material of the nonwoven fabric is made of polyethylene terephthalate (PET) or polyolefin such as polypropylene or polyethylene.
The generation of dioxin due to incineration can be prevented. In particular, when PET is used as a material, it can be made by reusing a PET bottle or the like that is a container for drinking water, which is useful for effective use of resources. On the other hand, in the case of polyolefin,
There is an advantage that it is lighter than PET and has good chemical resistance.
【００１１】[0011]
【発明の実施の形態】本発明の実施の形態を図面ととも
に説明する。図１は本発明の第一実施形態の点字タイル
１を示す平面図であり、図２はその断面図である。この
点字タイル１は、ポリエチレンテレフタレート（ＰＥ
Ｔ）を材料にした不織布２と、その下面２３に貼り付け
られた両面テープ３とを備えている。不織布２の上面２
１には、平面視において円形をした凸部２２が設けられ
ており、また、防水剤が塗布されている。点字タイル１
の平面視における形状は３００×３００ｍｍの正方形で
あり、この正方形内に２５個の凸部２２が存在する。不
織布２の厚さは３ｍｍで、凸部２２の高さは５ｍｍであ
る。また、不織布２上面２１の凸部２２に対応して、下
面２３には窪みがある。Embodiments of the present invention will be described with reference to the drawings. FIG. 1 is a plan view showing a braille tile 1 according to a first embodiment of the present invention, and FIG. 2 is a sectional view thereof. This Braille tile 1 is made of polyethylene terephthalate (PE)
A nonwoven fabric 2 made of T) and a double-sided tape 3 attached to a lower surface 23 thereof are provided. Upper surface 2 of nonwoven fabric 2
1 is provided with a convex portion 22 having a circular shape in a plan view, and is coated with a waterproofing agent. Braille tile 1
Is a 300 × 300 mm square in plan view, and there are 25 projections 22 in this square. The thickness of the nonwoven fabric 2 is 3 mm, and the height of the projection 22 is 5 mm. The lower surface 23 has a depression corresponding to the convex portion 22 of the upper surface 21 of the nonwoven fabric 2.
【００１２】本実施形態の点字タイルは以下のようにし
て製造される。まず、ＰＥＴを材料にした扁平な不織布
２を用意する。続いて、不織布２をプレス機の上型と下
型とで挟み、プレスすることによって上面２１に凸部２
２を設ける。これにより点字タイル用原板が得られる。
ここで、プレスの適当な条件は、温度１００〜２５０
℃、圧力１〜１０kg/cm2であり、好ましくは温度１８０
〜１９０℃、圧力４kg/cm2である。The braille tile of the present embodiment is manufactured as follows. First, a flat nonwoven fabric 2 made of PET is prepared. Subsequently, the nonwoven fabric 2 is sandwiched between an upper mold and a lower mold of a press machine, and pressed to form the convex portions 2 on the upper surface 21.
2 is provided. As a result, an original plate for braille tiles is obtained.
Here, suitable conditions for pressing are a temperature of 100 to 250.
° C, pressure 1 to 10 kg / cm 2 , preferably temperature 180
１９０190 ° C., pressure 4 kg / cm 2 .
【００１３】次に、点字タイル用原板を３００×３００
ｍｍの正方形になるように切断する。そして、上面２１
に防水剤を塗布し下面２３に両面テープ３を貼り付ける
と、点字タイル１が得られる。なお、防水剤の塗布又は
両面テープ３の貼り付けを不織布２の切断前に行っても
良い。点字タイル用原板の切断は、生産現場で行っても
良いし、施工現場で行っても良い。また、施工現場でも
すぐに切断できるようにするため、不織布２をプレスす
るときに、図３に平面図、図４に断面図として示すよう
な３００×３００ｍｍに区画するＶ字型の切断用溝４を
設けておくと良い。Next, an original plate for braille tiles is 300 × 300
Cut into squares of mm. And the upper surface 21
When a waterproof agent is applied to the lower surface 23 and the double-sided tape 3 is attached to the lower surface 23, the Braille tile 1 is obtained. The application of the waterproofing agent or the attachment of the double-sided tape 3 may be performed before the cutting of the nonwoven fabric 2. The cutting of the braille tile original sheet may be performed at the production site or at the construction site. Also, in order to be able to cut immediately even at the construction site, when pressing the nonwoven fabric 2, a V-shaped cutting groove partitioned into 300 × 300 mm as shown in a plan view in FIG. 3 and a sectional view in FIG. 4 should be provided.
【００１４】本実施形態の点字タイル１では、下面２３
に両面テープ３が貼り付けられているので、敷設する際
には両面テープ３で路面や床面に固定することができ
る。ただし、粘着剤を使用するなど他の手段によっても
固定することも可能である。その場合には、下面２３に
両面テープ３を貼り付ける必要はない。In the Braille tile 1 of the present embodiment, the lower surface 23
Since the double-sided tape 3 is stuck to the road surface, the double-sided tape 3 can be fixed to a road surface or a floor surface when laying. However, it is also possible to fix by other means such as using an adhesive. In that case, there is no need to attach the double-sided tape 3 to the lower surface 23.
【００１５】本実施形態の点字タイル１の重量は約１１
０ｇであり、従来の点字タイルよりも軽い。よって、施
工現場まで容易に輸送することができ、輸送費も削減で
きる。また、この点字タイル１の製造方法では、金型を
必要とせず、形状は不織布２の切断時に決まるので、切
断の仕方を変えることによって形状を変えることができ
る。よって、不織布２が十分に大きい限り、大きな点字
タイルや十字型、Ｌ字型、Ｔ字型など様々な形の点字タ
イルの製造が容易である。したがって、路面等に敷設す
る際に必要な点字タイルの枚数が少なくて済み、作業が
簡単になる。The weight of the braille tile 1 of the present embodiment is about 11
0 g, which is lighter than conventional Braille tiles. Therefore, it can be easily transported to the construction site, and the transportation cost can be reduced. Further, in the method of manufacturing the braille tile 1, a mold is not required and the shape is determined when the nonwoven fabric 2 is cut, so that the shape can be changed by changing the cutting method. Therefore, as long as the nonwoven fabric 2 is sufficiently large, it is easy to manufacture large Braille tiles and Braille tiles of various shapes such as a cross shape, an L shape, and a T shape. Therefore, the number of Braille tiles required for laying on a road surface or the like can be reduced, and the work is simplified.
【００１６】さらに、本実施形態の点字タイル１では、
不織布２の材料としてＰＥＴを使用しているので、焼却
してもダイオキシンが発生しない。その上、ＰＥＴを材
料にした不織布２は、空のペットボトルなどを再利用し
て作られ得るので、本実施形態によると資源の有効活用
に役立つ。また、点字タイル１をより軽くするため、あ
るいは耐薬品性をもたせるために、ポリオレフィンを材
料にしても良い。ポリオレフィンを使用した場合もダイ
オキシンは発生しない。ポリオレフィンとしては汎用性
のあるポリプロピレンやポリエチレンが用いられる。な
お、本実施形態の点字タイル１はポイント状点字タイル
であるが、ライン状点字タイルについてもプレス機の上
型及び下型の形状を換えるだけで同じように製造され、
同じ効果を有する。Further, in the braille tile 1 of the present embodiment,
Since PET is used as the material of the nonwoven fabric 2, no dioxin is generated even when incinerated. In addition, since the nonwoven fabric 2 made of PET can be made by reusing an empty PET bottle or the like, according to the present embodiment, it is useful for effective use of resources. Further, in order to make the Braille tile 1 lighter or to have chemical resistance, a polyolefin material may be used. No dioxin is generated when polyolefin is used. As the polyolefin, general-purpose polypropylene or polyethylene is used. Although the braille tile 1 of the present embodiment is a point-shaped braille tile, a line-shaped braille tile is manufactured in the same manner by simply changing the shape of the upper and lower dies of the press machine.
Has the same effect.
【００１７】図５は、第二実施形態の点字タイル１１を
示す断面図である。この実施形態では、不織布１２の上
面に防水剤を塗布する替わりに、防水シートとしてポリ
エステルフィルム１４を積層させている。この点を除く
と、第一実施形態と同じである。本実施形態の点字タイ
ル１１では、重量は１２０〜１３０ｇとなり、やはり従
来の点字タイルよりも軽い。製造方法については、第一
実施形態とほとんど同じだが、製造効率を上げるために
は、ポリエステルフィルム１４の積層はプレス前にする
のが好ましい。FIG. 5 is a sectional view showing the braille tile 11 of the second embodiment. In this embodiment, instead of applying a waterproofing agent on the upper surface of the nonwoven fabric 12, a polyester film 14 is laminated as a waterproofing sheet. Except for this point, it is the same as the first embodiment. The weight of the Braille tile 11 of the present embodiment is 120 to 130 g, which is also lighter than the conventional Braille tile. Although the manufacturing method is almost the same as that of the first embodiment, it is preferable that the lamination of the polyester film 14 is performed before pressing in order to increase the manufacturing efficiency.
【００１８】[0018]
【発明の効果】本発明によると、点字タイルを軽くする
ことができ、また敷設作業を簡単にすることができる。
さらに、材料としてＰＥＴやポリオレフィンを使用する
と、焼却してもダイオキシンが発生しない。According to the present invention, the braille tiles can be lightened and the laying work can be simplified.
Further, when PET or polyolefin is used as a material, no dioxin is generated even when incinerated.
【図１】第一実施形態の点字タイルを示す平面図であ
る。FIG. 1 is a plan view showing a braille tile according to a first embodiment.
【図２】第一実施形態の点字タイルを示す断面図であ
る。FIG. 2 is a cross-sectional view illustrating a braille tile according to the first embodiment.
【図３】点字タイル用原板を示す平面図である。FIG. 3 is a plan view showing an original plate for Braille tiles.
【図４】点字タイル用原板を示す断面図である。FIG. 4 is a sectional view showing an original plate for Braille tiles.
【図５】第二実施形態の点字タイルを示す断面図であ
る。FIG. 5 is a cross-sectional view illustrating a braille tile according to a second embodiment.
【図６】十字路等における従来の点字タイルの敷設状態
を示す図である。FIG. 6 is a diagram showing a state of laying a conventional Braille tile at a crossroad or the like.
１、１１ 点字タイル ２、１２ 不織布 ２１ 上面、 ２２ 凸部、 ２３ 下面 ３ 両面テープ ４ 切断用溝 １３ ポリエステルフィルム Ｐ ポイント状点字タイル Ｒ ライン状点字タイル DESCRIPTION OF SYMBOLS 1, 11 Braille tile 2, 12 Nonwoven fabric 21 Upper surface, 22 Convex part, 23 Lower surface 3 Double-sided tape 4 Cutting groove 13 Polyester film P Point-shaped braille tile R Line-shaped braille tile
───────────────────────────────────────────────────── フロントページの続き (72)発明者 舟津 外喜男 京都府久世郡久御山町大字野村小字村東 194番地の２ 日本ハートビル工業株式会 社営業本部内 Ｆターム(参考） 2D064 AA07 AA22 CA00 CA03 EA12 JA01 ────────────────────────────────────────────────── ─── Continuing on the front page (72) Inventor Toshio Funatsu, Kumiyama-cho, Kuse-gun, Kyoto, 194-2, Nomura, Higashi, Higashi, Japan F-term (reference) 2D064 AA07 AA22 CA00 CA03 EA12 JA01
Claims (10)
タイル。1. A braille tile comprising a nonwoven fabric as a base material.
か、若しくは防水シートが積層された請求項１に記載の
点字タイル。2. The braille tile according to claim 1, wherein a waterproofing agent is applied to a surface of the nonwoven fabric, or a waterproofing sheet is laminated.
プレス成形し、所望の形状に切断することを特徴とする
点字タイルの製造方法。3. A method for producing a braille tile, comprising press-forming a flat nonwoven fabric so as to have irregularities on its surface and cutting it into a desired shape.
水シートを積層する請求項３に記載の点字タイルの製造
方法。4. The method for manufacturing a braille tile according to claim 3, wherein a waterproof sheet is laminated on one main surface of the nonwoven fabric before press molding.
を材料としている請求項３又は４に記載の点字タイルの
製造方法。5. The method according to claim 3, wherein the nonwoven fabric is made of polyethylene terephthalate.
いる請求項３又は４に記載の点字タイルの製造方法。6. The method according to claim 3, wherein the nonwoven fabric is made of a polyolefin.
プレス成形するとともに、一群の凹凸ごとに区画する切
断用溝を設けることを特徴とする点字タイル用原板の製
造方法。7. A method for producing an original plate for a braille tile, wherein a flat nonwoven fabric is press-formed so as to have irregularities on the surface, and a cutting groove is provided for dividing the flat nonwoven fabric into groups of irregularities.
水シートを積層する点字タイル用原板の製造方法。8. A method for manufacturing a braille tile original sheet, wherein a waterproof sheet is laminated on one main surface of the nonwoven fabric before press molding.
を材料としている請求項７又は８に記載の点字タイル用
原板の製造方法。9. The method according to claim 7, wherein the nonwoven fabric is made of polyethylene terephthalate.
ている請求項７又は８に記載の点字タイル用原板の製造
方法。10. The method according to claim 7, wherein the nonwoven fabric is made of polyolefin.