HK1013863B - Base sheet for retroreflective articles and method for making same - Google Patents

Description

Field of the Invention

The invention concerns a novel base sheet and retroreflective articles, e.g., used as transparent overlays to protect documents from tampering, comprising same. The invention also concerns a method for making such base sheets and retroreflective articles.

Background of the Invention

Documents often have adherent transparent overlays to provide protection against dirt, moisture, and general wear and tear. A typical protective transparent overlay has a plastic film bearing an aggressive adhesive layer by which it can be permanently adhered to the face of a document. A transparent overlay which does not obscure underlying information is disclosed in U.S. Patent No. 3,801,183 (Sevelin et al.). The patent discloses legend-containing sheet materials which have retroreflective legend and retroreflective background areas that are substantially indistinguishable under ordinary diffuse light viewing conditions but are clearly distinguishable under retroreflective viewing conditions. Attempts to tamper with information over which the overlay has been applied result in readily detectable disruption of the overlay.

Subsequent to U.S. Patent No. 3,801,183, a number of patents have issued disclosing other transparent overlays, each of which can be imaged with a pattern or legend that is readily noticeable only when viewed retroreflectively and can be adhesively bonded to a document without obscuring the face of the document. See, for example, U.S. Patent No. 4,099,838 (Cook et al.) which discloses an overlay wherein the retroreflection from the background and image areas of the pattern is of contrasting colors. See also U.S. Patent Nos. 4,688,894 (Hockert) and No. 4,691,993 (Porter et al.), which disclose transparent overlays that function similarly as those of U.S. Patent No. 3,801,183 while having the added capability of permitting an authenticating message to be formed in the overlay after it has been adhesively bonded to a document.

The transparent protective overlays of each of the above-cited patents each comprise a monolayer of glass microspheres that makes the overlay expensive and difficult to counterfeit.

U.S. Patent No. 4,869,946 (Clay) discloses a security card comprising a transparent upper layer having narrow parallel lenses on its outer surface and an image-containing substrate on its inner surface. The two layers form a lenticular system by which images on the substrate are selectively viewable depending upon the angle from which the card is viewed.

U.S. Patent No. 3,503,315 (de Montebello) discloses a lenticular plate or sheet comprising adjacent lenslets with spherical convex surfaces on both sides. The sheet is used for the production and display of a picture in panoramic stereoscopic relief.

U.S. Patent No. 2,951,419 (Lemelson) discloses reflex-reflector devices which appear, to an observer moving with a light source, to flash on and off, scintillate, or change optical composition. In one embodiment, the device includes a transparent sheet and a reflex-reflector which meet at an interface. At the interface, there is provided two groups of adjacent bands or strips having different color or light reflectivity. At its front surface, the sheet is formed with a number of lens-like formations. An observer moving with a light source sees alternating patterns of color as the discrete bands of light from the moving light source enter the sheet in such a manner that the bands shift from one group to the other group and vice versa.

AT-A-332 763 discloses a reflex-reflector sheet which has an array of convex micro-lens surfaces on both the front and rear side of the sheet, the rear side also being reflective. The rear lens surfaces comprise spherical hemispheroidal microlenses while those on the front side of the sheet are non-spherical spheroidal microlenses. The microlenses on one side of the sheet cooperate with the microlenses on the other side in order to obtain the desired reflectivity characteristics.

U.S. Patent No. 4,576,850 (Martens) concerns shaped plastic articles made by replicating a microstructure-bearing surface with an ultraviolet-curable organic oligomeric composition.

A number of other patents also concern shaped plastic articles made by replicating a microstructure-bearing surface. For example, see U.S.Patent Nos. 3,689,346 (Rowland); 4,414,316 (Conley); 4,420,502 (Conley); and 4,373,077 (Kerfield).

U.S. Patent No. 1,824,353 discloses an array of ellipsoidal microlenses for focusing incident collimated light through corresponding apertures in a screen or onto a photographic plate, having respective applications for rear-projection cinema screens and low-light level photography.

Summary of the Invention

According to a first aspect of this invention there is provided a transparent base sheet as claimed in claim 1 herein.

According to a second aspect of this invention there is provided a method of making a base sheet as claimed in claim 14 herein.

The invention provides a transparent base sheet which can be used to make retroreflective articles, including, for example, transparent protective overlays for documents. The overlays can be imaged with information to enhance the authenticity of the document, e.g., a design or the bearer's photograph, and also provide high tamperresistance. Some of the information can be in the form of so-called "flip-flop" images that are viewable only across a narrow range of angles and change color across that range of angles. Such images can be viewable in ambient light, thus affording a readily apparent verification of the authenticity of the document. A "flip-flop" image can afford a second level of authenticity, by becoming bright when viewed retroreflectively, thus making it especially difficult either to tamper with the document or to counterfeit the novel overlay. The invention also provides a method of making such base sheets.

Typically, a specularly reflective layer will be applied to the second side of the substrate to yield a retroreflective article. If the reflective layer is transparent, the retroreflective article can be used as an overlay.

Brief Description of the Drawing

The invention will be further explained with reference to the drawing. In the drawing:

• FIG. 1 is a schematic cross section of a portion of a retroreflective sheeting of the invention;
• FIG. 2 is a schematic cross section of a portion of one embodiment of transparent protective overlay of the invention after it has laminated to the face of a document;
• FIG. 3 is a schematic cross section of a portion of another embodiment of transparent protective overlay of the invention; and
• FIG. 4 is a photomicrograph the microlens-covered face of a base sheet of the invention.

FIGs. 1-3, which are idealized, are not to scale and are intended to be merely illustrative and non-limiting.

Detailed Description of Illustrative Embodiments

As shown in FIG. 1, in a typical retroreflective embodiment, article 10, e.g., reflective sheeting, comprises base sheet 11 having first and second broad faces, arrangement 14 of substantially hemi-spheroidal microlenses on the first broad face, and substantially continuous specularly reflective layer 17 on the second face. Base sheet 11 is substantially transparent and has the proper refractive index and dimensions that collimated light orthogonally incident to the arrangement of microlenses is focused approximately at the second face of base sheet 11, i.e., at specularly reflective layer 17.

In the base sheets, the second or rear face is substantially flat and planar whereas the first or front face has an arrangement of convex microlenses thereon. The microlenses are substantially hemi-spheroidal. A spheroid is the figure generated by revolving an ellipse about one of its axes. As used herein, "hemi-spheroidal" refers to the fact that each microlenses is only a portion of a spheroid. The axis of each microlens is substantially perpendicular to the plane of the base sheet at the base of the microlens. The perimeter of each microlens is widest at its base where it protrudes from the base sheet. The microlenses are generally very tiny, i.e., typically on the order of about 50 to about 150 micrometers wide at their bases. The base of each microlens is proportionally wider than a base of a true hemisphere of the same height, to widen the width of the conical field in which incident light is focused to the second face of the base sheet. Typically, light which is incident to the microlens arrangement within a conical field oriented perpendicularly to the base sheet and having a full width of about 5 to about 10 degrees will be focused at the second face of the base sheet, and in retroreflective embodiments will be retroreflected. Incident light within this orientation is referred to herein as substantially orthogonal.

Preferably, the microlenses are closely packed within the arrangement to enhance the degree of focusing, and in retroreflective embodiments, increase the retroreflective brightness. In some embodiments, the microlenses may be so closely packed as to be substantially contiguous, i.e., the adjacent microlens are in contact rather than being spaced apart. In some instances, adjacent microlenses may be partially overlapping as shown in FIG. 4. An advantage of the invention is that the microlenses are not arranged in ordered fashion, i.e., no particular arrangement such as cubic or hexagonal arrangement is necessary. As shown in FIG. 4, the microlenses are arranged in essentially random arrangement.

When the article is to be used as a document overlay, the reflective layer is preferably transparent. Illustrative examples of reflective layers include zinc sulfide, cryolite, lithium fluoride, silicon oxides, and magnesium fluoride. U.S. Patent No. 3,700,305 (Bingham et al.) and the aforementioned U.S. Patent No. 3,801,183 disclose the use of dielectric mirrors as partially light transmissive reflectors and are incorporated herein by reference. When the reflective layer is transparent, it can be continuous without obscuring any information on the face of a document to which the novel protective overlay is applied. However, the reflective layer can be opaque when it is discontinuous and applied so as to not mask information on the face of the document to which it is applied.

A pattern of imaging material, i.e., clear ink or varnish, may be applied to the second face of the base sheet before a dielectric mirror is applied thereover to provide a legend or legends within an overlay of the invention.

Instead of or in addition to a message or pattern of clear ink, the second face of the transparent polymeric layer (beneath the reflective layer) can be imprinted with an opaque ink. For example, when the overlay is to be used to protect a document that has been preprinted with information standard to all like documents, e.g., with boxes labeled to receive a bearer's name, address, and the like, the opaque ink printing can fill those boxes with information specific to the bearer. If someone were able to peel such an overlay from a document, it would carry with it at least some of the opaque ink coating. Then to change the information, one would need to erase any part of that coating remaining on either the document or the overlay and add counterfeit information to fill the boxes. The task of doing so would be especially difficult when part of the ink coating is transparent and forms a so-called "flip-flop" image in a pattern that is easily disrupted upon tampering with the overlay.

To provide a "flip-flop" image, a message or pattern of clear ink is imprinted on the second face of the base sheet prior to application of a reflective layer thereover. The resultant change in nature of the surface of the base sheet tends to result in variations in thickness of the reflective layer when it is applied, thus producing an image that can repeat across the full face of the overlay and can be seen in ambient light with the naked eye across a narrow range of angles. The color of the image changes at differing viewing angles and is thus sometimes referred to as a "flip-flop" image. Any attempt to peel back the overlay to change underlying information is likely to disrupt the colored "flip-flop" image and thus alert anyone who looks at the document. Because the colored "flip-flop" image is bright when viewed retroreflectively, a retroreflective examination can provide secure proof that the document is authentic.

FIG. 2 illustrates another embodiment, wherein overlay 20 comprises base sheet 21 which consists of two strata, i.e., transparent spacing layer 22 and arrangement 24 of microlenses. An advantage of such multi-strata embodiments is that the materials used for spacing layer 22 and lens arrangement 24 may be independently selected to optimize the overall properties of the article. For instance, a high performance casting material which is used to make the random arrangement may be relatively expensive so that a cheaper material is used in the spacing layer to reduce the overall cost of the article. In another example, in the case of a document overlay, the random arrangement can be selected to be very hard and resistant to abrasion to impart greater durability whereas the spacing layer is selected to have a relatively low tensile strength to make its intact removal from a document more difficult.

Referring again to FIG. 2, on the rear face of spacing layer 22, i.e., the face opposite random arrangement 24, is discontinuous coating 26 of clear ink over which is continuous transparent reflective layer 27. Covering reflective layer 27 is adhesive layer 28 which may be used to secure overlay 20 to the face of document 29 over information 29A printed thereon.

Because retroreflective material 27 adhered better to the areas of clear ink 26 than it did to uninked areas of spacing layer 22 during application, e.g., by sputtering, it is thicker at the inked areas. The resultant variations in thickness of the transparent reflective layer 27 produce a colored "flip-flop" image that can be seen in ambient light through the polymeric layer, which image is bright when viewed retroreflectively.

Many different adhesives may be used on articles of the invention, including, for instance, hot melt adhesives, pressure-sensitive adhesives, and actinicly activated adhesives, e.g., heat-activated and ultraviolet-activated adhesives. In the case of document overlays, the adhesive should be substantially transparent.

In some embodiments, document overlays may be made with a layer of adhesive disposed between the second face of the base sheet and the reflective layer as well as on the opposite side of the reflective layer as the base sheet. FIG. 3 shows such an embodiment wherein overlay 30 comprises transparent base sheet 31 consisting of spacing layer 32, random arrangement of microlenses 34, and transparent adhesive stratum 33. In such embodiments, light incident to the arrangement 34 is focused at the back side of adhesive stratum 33, i.e., the side opposite spacing layer 32. Applied to the back of adhesive 33, i.e., the face opposite base sheet 31, is pattern of ink 36 over which has been applied transparent reflective layer 37 that has adhered to ink 36 but not to adhesive 33. Covering reflective layer 37 is another layer of adhesive 38 by which overlay 30 can be adhered to the face of a document (not shown). When adhesive layers 33 and 38 are of identical composition, an attempt to remove overlay 30 from a document is likely to cause splitting of both layers of adhesive, thus making it especially difficult for anyone to tamper with the document and then replace the overlay without leaving a clear indication of the tampering.

An advantage of base sheets of the present invention is that they may be used to make retroreflective articles without utilizing a monolayer of relatively expensive microspheres. Retroreflective articles of the invention provide selective angularity as mentioned above and can be made relatively inexpensively. In the case of document overlays, any information and patterns printed between the back of the base sheet and the face of the document are protected by the base sheet. Resins used in forming the base sheet, and particularly the random arrangement of microlenses, can be selected to have excellent resistance both to abrasion and to weathering.

A base sheet composite that can be converted to retroreflective sheeting of the invention can be made by using, as an initial master, retroreflective sheeting that includes a monolayer of enclosed glass microspheres and a space coat bearing a metallic coating, e.g., the specularly reflective layer of Fig. 4 of U.S. Patent No. 4,505,967 (Bailey). Such a metallic coating has a surface with hemi-spheroidal protrusions on which a forming master can be formed by the following method:

• a) preparing transparent curable composition, such as an ultraviolet-curable oligomeric composition, e.g., as disclosed in U.S. Patent No. 4,576,850;
• b) depositing that oligomeric composition onto the continuously cured surface of the initial master;
• c) spreading a bead of the composition between a substrate film and the initial master, the substrate being substantially planar, at least one of the substrate or master being flexible, as taught in U.S. Patent No. 4,374,077;
• d) curing the deposited composition, e.g., by ultraviolet radiation, to yield a composite of the substrate and cured oligomeric composition; and
• e) stripping the composite from the initial master to yield a forming master with surface having hemi-spheroidal cavities therein.

The aforementioned U.S. Patent No. 4,374,077 discloses replication by polymerization of a liquid mass deposited between a shaped surface and a substrate to which the mass is to adhere.

The composite with its surface of hemi-spheroidal cavities may be used as a forming master from which a base sheet of the invention is made. This can be done by performing a similar process utilizing the thusly made forming master and a substrate film or base film of proper thickness to act as a spacing layer. Illustrative examples of useful base films include flexible films of polyester, polyvinyl chloride, and polymethyl methacrylate. Alternatively, the forming master may be specially tooled to form a desired random arrangement of microlenses. It will typically be somewhat expensive to produce masters in that fashion, an advantage of the technique described above being that a suitable forming master can be obtained rather economically.

The curable composition is selected in part for its processing properties, i.e., viscosity, curing conditions, etc., and its post-cure properties, i.e., abrasion resistance, clarity, etc. In illustrative class of curable compositions are the ultraviolet-curable compositions disclosed in the aforementioned U.S. Patent No. 4,576,850. That patent discloses one-part, solvent-free, radiation addition-polymerizable oligomeric compositions containing hard and soft segments. The compositions typically contain between about 0.1 and about 0.5 percent by weight of photoinitiator. The hard segments preferably are polyurethane, and the soft segments preferably are polyester.

The curable composition is preferably applied to the forming master in limited quantity, e.g., such that the composition completely fills the hemi-spheroidal cavities but does not extend above the surface of the forming master by a distance greater than about 20 percent of the average depth of the cavities. In this fashion, the substrate film which becomes at least part of the spacing layer may be used to substantially define the desired overall tensile and film-like integrity of the article. Also, the curable composition is typically more expensive than the substrate film material, and it is typically easier to control shrinking and warping during curing if the curable mass is of reduced thickness. Preferably, the microlens random arrangement is between about 0.01 and about 0.05 millimeter in thickness when a retroreflective sheeting containing a monolayer of microspheres having an average diameter of about 65 micrometers is used as an initial master as described above. In such instances, the spacing layer is typically between about 0.2 and about 0.3 millimeters thick.

The viscosity of the oligomeric composition as deposited in step b) preferably is within the range of about 1,000 to about 5,000 centipoise ("cps"). Above that range, air bubbles might tend to be entrapped, and the resin might not completely fill the cavities of the master molding surface. Below that range, the resin would tend to shrink upon curing to such an extent that the cured resin may not faithfully replicate the master molding surface. Preferably, the viscosity of the resin is between about 2,000 and about 3,000 cps. Within that preferred range, the oligomeric composition should completely fill the master cavities without any need to apply pressure. However, when the cavities are unusually deep and/or narrow, it may be desirable to reduce the viscosity below 2,000 cps, because some shrinkage is to be preferred over any failure to fill the features completely.

In order to achieve the desired viscosity in compositions such as disclosed in U.S. Patent No. 4,576,850, it may be necessary to include in the oligomeric composition an ethylenically unsaturated monomer such as an alkyl acrylate, preferably an alkyl acrylate of which the alkyl group contains a straight chain of from 4 to 12 carbon atoms. The relative amounts of oligomer and monomer should be controlled so that the overall equivalent weight of the composition is not so low that there is unacceptably high shrinkage upon curing.

Polyvinyl chloride is a preferred substrate for use in step c) as it is typically economical, durable, transparent, and dimensionally stable. Other illustrative examples of useful substrates include polycarbonate, biaxially oriented polypropylene and biaxially oriented polyethylene terephthalate films, the surfaces of which have been treated to promote adhesion to the oligomeric composition, e.g., by corona treatment. Any of those substrates, typically used in thicknesses between about 0.05 and about 0.4 millimeter, can be flexed to propagate a bead of resin as taught in U.S. Patent No. 4,374,077. Additional illustrative examples of useful substrates include cellulose acetate butyrate, cellulose acetate propionate, polyether sulfone, polymethyl methacrylate, and polyurethane films, and glass.

The curable composition and substrate are preferably selected that upon curing a strong bond is formed therebetween.

The optimum thickness of the substrate layer or spacing layer is dependent in part upon the average size and shape of the microlenses. In typical retroreflective sheeting such as used as an initial master as described above, 80 percent of the microspheres have a diameter within 15 percent of the average. When the average diameter of the microspheres is about 65 micrometers, the microlenses of the resultant base sheet of the invention have an approximate average focal length of between about 0.2 and about 0.3 millimeter, thus allowing a spacing layer to be between about 0.2 and about 0.3 millimeter in thickness, or somewhat thinner when a transparent adhesive layer is provided between the base sheet and reflective layer. Because a thinner substrate would be more economical and equally useful, it may be preferred to start with retroreflective sheeting having glass microspheres of smaller average diameter.

Articles of the invention may be made in substantially rigid or flexible form. For instance, with selection of suitable materials, articles of the invention may be so flexible as to be capable of being wound into roll form about a mandrel 1 centimeter in diameter.

Examples

The invention will be further explained by the following illustrative examples which are intended to be nonlimiting. Unless otherwise indicated, all amounts are expressed in parts by weight.

Reflective Brightness

Retroreflective Brightness was measured at 0.2° divergence angle and -4° entrance angle in candellas per lumen using a retroluminometer as described in United States defensive publication T987,003.

Example 1

A one-part, solvent-free, radiation addition-polymerizable, crosslinkable, organic oligomeric composition having hard segments and soft segments and a viscosity of 1600 cps was prepared by blending together the following components:

	Parts
acrylate-capped polycaprolactone urethane oligomer	54.3
N-vinyl pyrrolidone	16.3
[(ethoxy)-2-ethoxy]ethyl acrylate	11.3
1,6-hexanediol diacrylate	5.7
N-(isobutoxy methyl)acrylamide	11.1
tertiary amine mixture (TINUVIN 292 from Ciba-Geigy)	1.0
1-hydroxy cyclohexyl acetophenone	0.25

Used as an initial master surface was the metallic reflective layer of an enclosed-lens retroreflective sheeting comprising a monolayer of glass microspheres having an average diameter of about 65 micrometers (note that true spheres are not within the scope of the present invention). Onto the metallic layer was deposited the liquid oligomeric composition in an amount barely sufficient to fill the cavities of the metallic layer. This was overlaid with clear polycarbonate film 0.125 millimeter in thickness through which the oligomeric composition was irradiated using 2 passes of a medium-pressure mercury lamp of 350 to 380 nanometers, 125 watts per linear centimeter, thus providing a total exposure of 110 millijoule/centimeter2. The contoured surface of the resulting first composite consisted of substantially contiguous hemi-spheroidal concavities.

The same procedure was repeated using the resultant composite as a forming master, thus producing a second composite having a total thickness of about 0.2 millimeter and consisting of a polycarbonate substrate and an arrangement of substantially hemi-spheroidal microlenses.

Over the flat surface of the second composite, aluminum was applied by vacuum deposition to a thickness of about 70 nanometers. The resulting retroreflective sheeting had a Reflective Brightness of 390 candellas per lumen.

Example 2

A composite was made like the second composite of Example 1 except that the thickness of its polycarbonate substrate was 0.25 millimeter. The photomicrograph of FIG. 4 shows the resultant microlens random arrangement.

Onto the flat surface of the polycarbonate substrate was screen-printed a pattern of colorless ink (RAGE-800 Ink from Advance Process Supply of Chicago) that dried to a thickness of less than 0.01 millimeter. Over this, zinc sulfide was applied by vacuum deposition to a thickness of about a quarter wavelength at 520 nanometer to provide a transparent reflective layer. The ZnS tended to stick to only the clear ink and the areas immediately around the ink deposits, leaving the exposed areas of polycarbonate uncovered. A 0.05 millimeter thick layer of ELVAX 550, an ethylene/vinyl acetate copolymer hot melt adhesive from Du Pont was then laminated thereover. The resulting transparent protective overlay of the drawing was laminated by its adhesive layer at 82°C to the face of a driver license bearing printed information.

When viewed through the overlay, that printed information was clearly readable in spite of a faintly colored "flip-flop" image where the clear ink had been applied, which image was in a pattern extending over the whole face of the driver license and was clearly visible in ambient light. When viewed retroreflectively, the pattern was bright.

The microlenses were rubbed with fine sandpaper to simulate the wear that could be expected over a period of several years in normal use, after which the printed information remained readable and the colored "flip-flop" pattern remained clearly visible in ambient light.

Example 3

A driver license was made in the same manner as in Example 1 except as follows:

• a) the substrate was poly(vinyl chloride);
• b) two layers of the adhesive were applied as illustrated in FIG. 3;
• c) a pattern of the colorless ink was screen-printed onto the exposed face of the adhesive layer that was applied to the second face of the base sheet;
• d) ZnS was applied over this pattern and adhered only to the ink and not to the adhesive.

When this driver license was viewed through the overlay, a "flip-flop" image like that of Example 2 was visible in ambient light and was bright when viewed retroreflectively.

Example 4

A composite (about 15 x 28 centimeters) was made like the second composite of Example 1 except that the substrate was polyvinyl chloride 0.25 millimeter in thickness, and it was converted to retroreflective sheeting by applying ZnS by vacuum deposition to a thickness of about a quarter wavelength at 520 nanometers. Reflective Brightness measurements were made at each of the four corners and at the midpoints along the long sides. Results, in candellas per lumen, were:

68	78	71
56	71	69.

In view of the fact that the thermoplastic polyvinyl chloride film inevitably has variations in thickness which result in a somewhat non-uniformly thick spacing layer and that the microlenses varied in size, these values are remarkably uniform.

Example 5

A composite was prepared as in Example 2 except that the colorless ink was replaced by a colored transparent ink formulated as follows: 80 parts of colorless ink (Roto/Flexo Extender FA-1626 from Sinclair and Valentine, St. Paul, Minnesota) and 20 parts of AFFLAIR 235 Rutile Green Pearl Interference pigment from EM Industries, Inc., Hawthorne, New York. The composite was then, as in Example 2, converted into a retroreflective sheeting that was adhered to the face of a driver license. The resulting "flip-flop" image was more strongly colored than was that obtained in Example 2, but printed information on the face of the driver license was readable through the image.

Various modifications and alterations of this invention will become apparent to those skilled in the art without departing from the scope of this invention which is limited to that defined in the appended claims.

Claims (19)

1. A transparent base sheet (11,21,31) having a first and a second broad face said second face being substantially planar, and said first face including an arrangement of substantially hemispheroidal microlenses said microlenses being wider at their bases than true hemispheres of the same height, and the shape of said microlenses and thickness of said base sheet(11,21,31) being such that collimated light substantially orthogonally incident to said first face is focused approximately at said second face; characterised in that said arrangement of microlenses is constituted by a random arrangement (14,24,34) of said substantially hemispheroidal microlenses having different heights.
2. The base sheet (11,21,31) of claim 1, wherein said microlenses are substantially contiguous.
3. The base sheet of claim 1 or 2, wherein said base sheet (21,31) comprises a transparent spacing layer (22,32) having substantially planar first and second broad faces and a microlens layer comprising said arrangement (24,34) of microlenses, said microlens layer being bonded to said first broad face of said spacing layer (22,32).
4. A retroreflective article (10,20,30) comprising the base sheet (11,21,31) of claim 1 or 2, wherein said second face of said base sheet (11, 21,31) has a specularly reflective layer (17,27,37) thereon such that collimated light substantially orthogonally incident to said microlens arrangement (14,24,34) is focused approximately at said second face so as to be retroreflected by said article (10,20,30).
5. The article (30) of claim 4, wherein said reflective layer (37) is discontinuous.
6. The article (20,30) of claim 4, wherein said base sheet (21,31) comprises a transparent spacing layer (22,32) having substantially planar first and second broad faces and a microlens layer comprising said arrangement (24,34) of microlenses, said spacing layer (22,32) and said microlens layer being bonded together, said spacing layer being disposed between said microlens layer and said reflective layer (27,37).
7. The article (20,30) of claim 6, wherein

   a) the total thickness of said article (20,30) is between 0.05 and 0.4 millimeters; and/or

   b) the total thickness of said spacing layer (22,32) is between 0.2 and 0.3 millimeters.
8. The article (20,30) of claim 6, wherein said article (20,30) further comprises a layer of adhesive (28,38) on the side of said reflective layer (27,37) opposite said spacing layer (22,32).
9. The article (20,30) of claim 8, wherein said reflective layer (27,37) and said layer of adhesive (28,38) are transparent.
10. The article (20,30) of claim 9, wherein said article (20,30) further comprises an imaging material (26,36) disposed between said second face of said base sheet (21,31) and said reflective layer (27,37).
11. The article (20) of claim 10, wherein at least part of said imaging material (26) is clear and forms an image that, when the article (20) is adhered to a document (29) with information (29A) thereon by said adhesive layer (28), can be seen in ambient light by the unaided eye without interfering with the readability of the information (29A) on the document (29).
12. The article (30) of claim 4, wherein said reflective layer (37) is opaque and discontinuous.
13. The article (20) of claim 4, wherein said reflective layer (27) of said article (20) is bonded to a document substrate (29) through a layer of adhesive (28).
14. A method of making a base sheet (11,21,31) wherein said method comprises:

    a) preparing a curable composition;

    b) depositing said composition onto a forming master surface having a random arrangement of substantially hemispheroidal concavities of different depths therein, said concavities having wider openings than true hemispherical concavities of the same depth;

    c) spreading a bead of the composition between a transparent substrate film and said forming master, said substrate film being substantially planar, at least one of said forming master and said substrate film being flexible;

    d) curing the deposited composition to yield a composite comprising a random arrangement (14,24,34) of substantially hemispheroidal microlenses of different heights bonded to said substrate film; and

    e) removing said composite from said forming master to yield said base sheet, the shape of said microlenses and thickness of said base sheet (11,21,31) being such that collimated light substantially orthogonally incident to the arrangement (14,24,34) of microlenses on the first face of said base sheet is focused approximately at the substantially planar second face of said sheet.
15. The method of claim 14, wherein said curable composition is an ultraviolet-curable, one-part, solvent-free, radiation addition-polymerizable, crosslinkable, organic oligomeric composition containing hard segments and soft segments and wherein said curing comprises exposure to ultraviolet radiation.
16. The method of claim 15, wherein said hard segments are polyurethane and said soft segments are polyester.
17. The method of claim 14, wherein said composition does not extend above said surface of said forming master by a distance greater than 20 percent of the average depth of said hemispheroidal concavities.
18. The method of claim 14 or 17, wherein said method further comprises applying a specularly reflective layer (17, 27,37) over the exposed face of said substrate film to yield a retroreflective sheeting (10,20,30).
19. The method of claim 14, wherein said forming master is manufactured by the steps of:

    a) providing an initial master comprising a retroreflective sheeting, said sheeting comprising a monolayer of randomly arranged microspheres and a space coat bearing a metallic coating having hemispheroidal protrusions, said protrusions being wider at their bases than true hemispherical protrusions of the same height;

    b) preparing a second curable composition;

    c) depositing said second composition onto said metallic coating;

    d) spreading a bead of said second composition between a second substrate film and said initial master, said second substrate film being substantially planar, at least one of said initial master and said second substrate film being flexible;

    e) curing said second composition to yield a second composite comprising said second substrate film and said second composition;

    f) removing said second composite from said initial master to yield the forming master.