GB906022A - Improvements in or relating to methods of metallising ceramic surfaces - Google Patents

Improvements in or relating to methods of metallising ceramic surfaces

Info

Publication number
GB906022A
GB906022A GB1813958A GB1813958A GB906022A GB 906022 A GB906022 A GB 906022A GB 1813958 A GB1813958 A GB 1813958A GB 1813958 A GB1813958 A GB 1813958A GB 906022 A GB906022 A GB 906022A
Authority
GB
United Kingdom
Prior art keywords
bodies
particles
ceramic
metallized
joined
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB1813958A
Inventor
Leonard William Bean
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co PLC
Original Assignee
General Electric Co PLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co PLC filed Critical General Electric Co PLC
Priority to GB1813958A priority Critical patent/GB906022A/en
Publication of GB906022A publication Critical patent/GB906022A/en
Expired legal-status Critical Current

Abstract

The surface of a ceramic body is metallized by coating it with particles of Mo and/or W and/or one or more of their reducible oxygen-containing compounds, together with particles of titanium hydride and/or zirconium hydride, and heating the coated surface to produce an at least partly vitrified layer containing titanium oxide and/or zirconium oxide with particles of Mo and/or W bonded to it. Preferably the weight of the Ti and Zr atoms lies in the range of 1-20% of the total metal atoms present in the coating. The particles may be applied as an intimate mixture in suspension, for example, in an ethyl lactate solution of pyroxylin: alternatively, they may be applied as separate layers of the different ingredients. The coated surface is heated at 1200-1600 DEG C. in an atmosphere non-oxidizing to Mo and W, e.g. in wet hydrogen, a rare gas or in vacuo. Among ceramic bodies which may be coated are those consisting wholly or mainly of alumina, steatite or forsterite. Bodies metallized in this way may be joined to metal bodies or to a metallized surface of another ceramic body by soldering or brazing. Alternatively, two ceramic bodies may be joined in a single operation by interposing a layer of Mo &c. between abutting surfaces of the bodies and then heating. The invention is particularly described with reference to the manufacture of a composite ceramic-metal envelope for a semi-conductor junction rectifier.
GB1813958A 1958-06-06 1958-06-06 Improvements in or relating to methods of metallising ceramic surfaces Expired GB906022A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB1813958A GB906022A (en) 1958-06-06 1958-06-06 Improvements in or relating to methods of metallising ceramic surfaces

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB1813958A GB906022A (en) 1958-06-06 1958-06-06 Improvements in or relating to methods of metallising ceramic surfaces

Publications (1)

Publication Number Publication Date
GB906022A true GB906022A (en) 1962-09-19

Family

ID=10107313

Family Applications (1)

Application Number Title Priority Date Filing Date
GB1813958A Expired GB906022A (en) 1958-06-06 1958-06-06 Improvements in or relating to methods of metallising ceramic surfaces

Country Status (1)

Country Link
GB (1) GB906022A (en)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1273404B (en) * 1964-07-30 1968-07-18 Bertold Berberich Dipl Ing Formation of an ultra-high vacuum-tight, hard-soldered surface of a ceramic part
FR2407181A1 (en) * 1977-10-25 1979-05-25 Bfg Glassgroup PROCESS FOR MANUFACTURING AN ENVELOPE INCLUDING AT LEAST ONE GLASS OR PARTLY GLASS WALL AND PRODUCT OBTAINED BY THIS PROCESS
EP0467462A1 (en) * 1990-07-20 1992-01-22 F.M. Velterop B.V. Method of connecting ceramic material to another material
PL126984U1 (en) * 2018-01-29 2019-08-12 Politechnika Warszawska Device for frictional application of coatings on ceramic surfaces

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1273404B (en) * 1964-07-30 1968-07-18 Bertold Berberich Dipl Ing Formation of an ultra-high vacuum-tight, hard-soldered surface of a ceramic part
FR2407181A1 (en) * 1977-10-25 1979-05-25 Bfg Glassgroup PROCESS FOR MANUFACTURING AN ENVELOPE INCLUDING AT LEAST ONE GLASS OR PARTLY GLASS WALL AND PRODUCT OBTAINED BY THIS PROCESS
EP0467462A1 (en) * 1990-07-20 1992-01-22 F.M. Velterop B.V. Method of connecting ceramic material to another material
US5139191A (en) * 1990-07-20 1992-08-18 F. M. Velterop B.V. Method of connecting ceramic material to another material
AU641788B2 (en) * 1990-07-20 1993-09-30 Velterop B.V. Method of connecting ceramic material to another material
PL126984U1 (en) * 2018-01-29 2019-08-12 Politechnika Warszawska Device for frictional application of coatings on ceramic surfaces

Similar Documents

Publication Publication Date Title
US2667432A (en) Metalized ceramic
US2776472A (en) Method of making a ceramic-to-metal bond
GB1110706A (en) Pressure bonded ceramic-to-metal gradient seals
GB1427287A (en) X-ray tube rotary anode
US3403043A (en) Ceramic-metal seals
SE8605071D0 (en) TITANIUM COMPOSITE HAVING A COIL-SHAPED SKELETAL STRUCTURE ON THE SURFACE THEREOF AND PROCESS FOR PRODUCING THE SAME
US3609856A (en) Brazing carbon bodies to other bodies of temperature resistant materials
US3175937A (en) Method of bonding metals using borosilicate glasses
GB906022A (en) Improvements in or relating to methods of metallising ceramic surfaces
GB1383343A (en) Porous abra 'ble metal
US2820727A (en) Method of metallizing ceramic bodies
US3051592A (en) Ceramic metalizing process
US1335024A (en) Process for preventing distortion of precious metals at temperatures higher than their fusing-points and article produced thereby
US3296017A (en) Method of chemically bonding a metal to a ceramic
US3347704A (en) Method of metal-coating ceramic bodies
US3637435A (en) Metallizing process for glass-free ceramics bodies
GB1108764A (en) Improvements in ceramic bonding
GB1081623A (en) Coated refractory bodies
US2928755A (en) Metal-coated ceramic article and process for producing the same
JPS6442370A (en) Method for joining ceramics and metal
US3926574A (en) Molybdenum based substrate coated with homogeneous molybdenum trialuminide
GB855625A (en) Improvements in the metallising of ceramics
JPS59173272A (en) Manufacture of enameled ware using glaze esp. compounded with far infrared forming element
GB891705A (en) An improved method of forming an adherent layer on a ceramic material
GB625371A (en) Improvements in and relating to ceramic seals and method of making same