GB2260988A - Brake pads - Google Patents
Brake pads Download PDFInfo
- Publication number
- GB2260988A GB2260988A GB9222693A GB9222693A GB2260988A GB 2260988 A GB2260988 A GB 2260988A GB 9222693 A GB9222693 A GB 9222693A GB 9222693 A GB9222693 A GB 9222693A GB 2260988 A GB2260988 A GB 2260988A
- Authority
- GB
- United Kingdom
- Prior art keywords
- disc brake
- rubber
- brake pad
- friction material
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Automotive disc brake pads comprising a friction material which contains particulate material, fibre and binder. The binder is substantially all thermoset rubber and makes up only 2 % to 9.5 % by volume of the material.
Description
Improvements in or relating to brake pads
This invention relates to brake pads and particularly brake pads of the kind which are used in disc brakes for automotive applications.
Organic binder materials are in widespread use in the manufacture of brake pads, the common types being phenolic resins or modified phenolic resins with which a proportion of rubber such as SBR or Nitrile rubber is also often used. Many published patent specifications mention organic binder materials of this kind, for example UK Patent No 1,604,828 discloses non-asbestos brake pads which are made from a friction material containing a thermoset binder making up 20% to 45% by volume of the friction material at least half of which is phenol formaldehyde resin. UK
Patent No 1,604,839 discloses a friction material for brake pads which contains a thermoset binder making up 20% to 60% by volume of the friction material at least half of the thermoset binder being phenol formaldehyde resin.
European Patent No 0,184,708 discloses a friction material for automotive uses which contains steel fibres and organic binder, the amount of organic binder being 10% to 35% by volume of the friction material, and all the examples show the use of resin alone at volumes above 20%.
This is typical of the prior art. Binder resin contents expressed as parts by weight or as percentages by weight invariably have a substantial resin content when measured by volume and taking into account material density. Thus in another example, GB-A-2114586 teaches a preferred binder resin content of only 8% by weight, but in volume terms this is as much as 22% by volume when density is taken into account. In some instances, an apparently minimal thermosetting resin content must be considered in the context of a substantial amount of another binder such as rubber, so that the total organic binder content is again relatively high when determined in terms of volume.
We have now found that disc brake pads with advantageous properties may be manufactured using thermosetting resin with or without rubber as a binder, but at very low binder contents when measured by volume.
Thus according to the invention an automotive disc brake pad comprises a friction material containing fibres, particulate materials and an organic binder, wherein the binder comprises thermoset resin with or without a proportion of thermoset rubber and the total binder content is from 2% to 9.5% by volume of the friction material.
It will be understood that in this present context, the organic binder is the sole binder system for the friction material.
In this specification by "automotive" disc brake pad we mean a pad for a disc brake on a road vehicle such as a car, motor cycle, van or truck.
The thermoset resin is preferably a resin of the phenolic or modified phenolic type, although other resins such as epoxy resins may be used.
When rubber is included the rubber used is preferably nitrile rubber, although other rubbers may be used as the whole or part of the rubber in the binder, for example bromobutyl rubber, chlorobutyl rubber.
The other ingredients of the friction material may be selected from the wide range of available fibres, fillers and friction and wear modifiers.
Examples of possible fibres include metal fibres such as steel, mineral fibres such as glass or basalt, and organic fibres such as aramid. The amount of fibre used is not critical but will typically be in the range 0 to 15% by volume.
The balance of the friction material apart from binders and fibres is of particulate materials. The particulate materials used as fillers and friction and wear modifiers may be taken from a vast range of possible options. For example alumina, antimony trisulphide, zirconia, crushed coke, graphite, molybdenum disulphide, powdered metals such as copper, tin, brass, reinforcing fillers such as mica, vermiculite, wollastonite, and other fillers such as barytes, silica, calcium carbonate etc.Owing to the very low volumes of the organic binder used in this invention the particulate materials are used in the larger sizes of the conventional range of eg 300m to 600ism, and finely divided materials (ie particle sizes below 50cm) are to be avoided in order to ensure that there is not too much particle surface area to be wetted out by the binder.
The invention will be described in more detail, by way of example only, in the following Example.
EXAMPLE 1
A friction material was prepared according to the formulation given below in Table 1. The dry ingredients (including the resin) were pre-blended, then intimately mixed with a solution of binder rubber in trichloreothylene. The mix was dried and disintegrated and then charged to a pre-forming die where disc brake pad preforms were moulded under a pressure of 7 tons/in2. Each preform was cured by baking whilst under light pressure in an oven for 2 hours at 2400.
TABLE 1
EXAMPLE NO 1
Ingredient % Vol
Phenolic Resin 6.00
Nitrile Rubber 3.00
Sulphur 4.29
Steel Fibre 3.00
Vermiculite 30.08
Barytes 17.40
Petroleum Coke 17.00
Friction and Wear Modifiers 22.23
Testing
Disc brake pads made according to Example 1 were tested for friction and wear in machine tests against a cast iron brake disc. Fade and recovery behaviour of the material was tested in a severe sequence which consists of a "fade phase" of 20 successive stops from 130kph, followed by a "recovery phase" of 10 successive stops from 50kph. During the stops from high speed the pad temperature (which is constantly monitored) rises to very high levels and (during the stops from slower speeds) the pad temperature gradually falls again. The results of these tests are given below in tabular form in Table II.
TABLE II
EXAMPLE NO 1
Fade Phase
Max. mean coefficient of friction * 0.38
Min. mean coefficient of friction * 0.34
Initial pad temperature oC 200
Peak pad temperature CC 650
Recovery Phase
Max. mean coefficient of friction * 0.39
Min. mean coefficient of friction * 0.34
Final pad temperature "C 175 * In this Table the expression "mean" coefficient of friction is used to refer to the average value of the coefficient of friction during a single stop, because it is normal to see some variation of the coefficient with time during each stop as the pad temperature rapidly rises.
It can be seen from Table II that the brake pads made according to each Example showed excellent resistance to fade and consistency of friction during both phases of the test.
The wear rates of each pad have been found to be less than is usually seen in current commercially available pads.
Claims (7)
1. An automotive disc brake pad which comprises a
friction material containing fibres, particulate
materials and an organic binder, wherein the binder
comprises thermoset resin with or without a proportion
of thermoset rubber and the total binder content is
from 2% to 9.5% by volume of the friction material.
2. A disc brake pad according to claim 1 in which the
thermoset rubber is selected from nitrile rubber,
chlorobutyl rubber and bromobutyl rubber and mixtures
thereof.
3. A disc brake pad according to claim 1 or 2 which
includes a thermoset rubber and wherein said thermoset
resin is a resin of the phenolic or modified phenolic
type.
4. A disc brake pad according to claim 1, 2 or 3 in which
the friction material further contains fibres in an
amount of 0% to 15% by volume.
5. A disc brake pad according to claim 4 in which the
fibres are steel fibres.
6. A disc brake pad according to any preceding claim in
which the friction material includes mica, vermiculite
and/or wollastonite in an amount up to 35% by volume.
7. A disc brake pad substantially as described herein in
any one of the foregoing Examples.