GB1045086A - Magnetic recording medium and method of manufacture - Google Patents
Magnetic recording medium and method of manufactureInfo
- Publication number
- GB1045086A GB1045086A GB30144/63A GB3014463A GB1045086A GB 1045086 A GB1045086 A GB 1045086A GB 30144/63 A GB30144/63 A GB 30144/63A GB 3014463 A GB3014463 A GB 3014463A GB 1045086 A GB1045086 A GB 1045086A
- Authority
- GB
- United Kingdom
- Prior art keywords
- cobalt
- palladium
- chloride
- contacting
- hydrochloric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
A magnetic recording tape is made by contacting a surface of a polyethylene terephthalate film with a hot caustic solution containing alkylene glycol until the surface is hydrolized, sensitizing with stannous chloride, activating with silver nitrate, depositing palladium on the film and then contacting the surface with an electroless plating solution containing cobalt ions and a hypophosphite reducing agent to form a magnetic layer of a cobalt-phosphorus alloy. The sensitizing solution may comprise 70 g./1. stannous chloride 50 ml./1. hydrochloric acid, and 0.5 g./1. of sodium lauryl sulphate. The palladium is deposited from a solution comprising 0.1 g./1. of palladium chloride and 1.0 ml./1. of 35% concentrated hydrochloric acid. The electroless plating solution may comprise (g./1.) cobalt sulphate; 7H2O 28 to 32; ammonium chloride 50 to 100; sodium potassium tartrate 50 to 75; and sodium hypophosphite 20 to 25. The pH is adjusted to 8.7 to 8.9 with ammonium hydroxide. The coated tape may be heated at 70 DEG C for 1 to 60 minutes or may be left at room temperature from a few minutes to a day. The cobalt layer may also contain iron and nickel.
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US21804062A | 1962-08-20 | 1962-08-20 | |
| US288588A US3245826A (en) | 1963-06-12 | 1963-06-12 | Magnetic recording medium and method of manufacture |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB1045086A true GB1045086A (en) | 1966-10-05 |
Family
ID=26912510
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB30144/63A Expired GB1045086A (en) | 1962-08-20 | 1963-07-30 | Magnetic recording medium and method of manufacture |
Country Status (6)
| Country | Link |
|---|---|
| JP (1) | JPS5317533B1 (en) |
| CH (1) | CH460865A (en) |
| DE (1) | DE1521179B2 (en) |
| FR (1) | FR1376605A (en) |
| GB (1) | GB1045086A (en) |
| NL (1) | NL296796A (en) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| WO2003033764A2 (en) * | 2001-10-17 | 2003-04-24 | Atotech Deutschland Gmbh | Metallization of non-conductive surfaces with silver catalyst and electroless metal compositions |
Families Citing this family (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CA1188796A (en) * | 1981-04-14 | 1985-06-11 | Kenji Yazawa | Magnetic recording medium |
-
0
- NL NL296796D patent/NL296796A/xx unknown
-
1963
- 1963-07-30 GB GB30144/63A patent/GB1045086A/en not_active Expired
- 1963-08-15 CH CH1010863A patent/CH460865A/en unknown
- 1963-08-19 DE DE19631521179 patent/DE1521179B2/en active Pending
- 1963-08-20 FR FR945100A patent/FR1376605A/en not_active Expired
- 1963-08-20 JP JP4445263A patent/JPS5317533B1/ja active Pending
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| WO2003033764A2 (en) * | 2001-10-17 | 2003-04-24 | Atotech Deutschland Gmbh | Metallization of non-conductive surfaces with silver catalyst and electroless metal compositions |
| WO2003033764A3 (en) * | 2001-10-17 | 2004-06-24 | Atotech Deutschland Gmbh | Metallization of non-conductive surfaces with silver catalyst and electroless metal compositions |
| CN100338259C (en) * | 2001-10-17 | 2007-09-19 | 阿托特德国有限公司 | Metallization of non-conductive surfaces with silver catalysts and electroless metal compositions |
Also Published As
| Publication number | Publication date |
|---|---|
| FR1376605A (en) | 1964-10-31 |
| JPS5317533B1 (en) | 1978-06-09 |
| CH460865A (en) | 1968-08-15 |
| NL296796A (en) | |
| DE1521179B2 (en) | 1972-08-31 |
| DE1521179A1 (en) | 1969-07-31 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US3245826A (en) | Magnetic recording medium and method of manufacture | |
| GB1004744A (en) | Improvements in and relating to methods of forming copper films on silicous substrate | |
| GB1073006A (en) | Metallising surfaces of plastics articles | |
| GB1339157A (en) | Electroless plating | |
| US3219471A (en) | Process of depositing ferromagnetic compositions | |
| ES375284A1 (en) | Metal plating of thermoplastics | |
| GB1014271A (en) | Deposition of nickel-cobalt alloy on aluminium substrates | |
| GB1397091A (en) | Process and solution for the sensitization of substrates for electroless metal deposition | |
| GB1200931A (en) | Improvements in and relating to magnetic information carriers | |
| GB1045086A (en) | Magnetic recording medium and method of manufacture | |
| GB1194625A (en) | Boron Containing Composite Metallic Films and Plating Baths for their Electroless Deposition | |
| GB965859A (en) | Improvements in and relating to the deposition of palladium | |
| GB1346273A (en) | Metal plating of plastics materials | |
| GB1244101A (en) | Metallising a substrate | |
| GB1080791A (en) | Improvements in or relating to electroless plating solutions | |
| ES313173A1 (en) | Procedure for the protection of aluminum and aluminum alloy objects. (Machine-translation by Google Translate, not legally binding) | |
| GB1201194A (en) | Method of plating substrates | |
| GB953432A (en) | Improvements in or relating to the production of noble-metal layers | |
| US4379184A (en) | Process for forming a reflecting copper coating on a face of a glass substrate | |
| GB992660A (en) | Method for deposition of magnetic film on plastic base | |
| GB1314745A (en) | Electroless plating bath for depositing a nickel alloy layer | |
| GB1518301A (en) | Deposition of copper | |
| GB1266278A (en) | ||
| Mallory | The electroless nickel plating bath | |
| JPS56109843A (en) | Heat ray reflecting glass |