ES2587443B2 - Procedure for obtaining dry cement and cement mortar and lime for construction, made with slate residues - Google Patents
Procedure for obtaining dry cement and cement mortar and lime for construction, made with slate residues Download PDFInfo
- Publication number
- ES2587443B2 ES2587443B2 ES201500280A ES201500280A ES2587443B2 ES 2587443 B2 ES2587443 B2 ES 2587443B2 ES 201500280 A ES201500280 A ES 201500280A ES 201500280 A ES201500280 A ES 201500280A ES 2587443 B2 ES2587443 B2 ES 2587443B2
- Authority
- ES
- Spain
- Prior art keywords
- mortar
- une
- cement
- procedure
- slate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
La presente invención se basa en la obtención de morteros secos empleando para ello arenas provenientes exclusivamente de residuos de la industria extractiva de la pizarra.#Para la obtención de morteros de calidad y que no presenten problemáticas derivadas de la composición mineral de la pizarra, se emplean cementos específicos así como aditivos en polvo y cales.#La invención protege, además de los morteros, el método de obtención de las arenas a partir de los residuos de pizarra, así como el procedimiento de fabricación de los diferentes morteros en función de sus usos y la utilización de los aditivos necesarios para obtenerlos.The present invention is based on obtaining dry mortars using sands exclusively from waste from the slate extractive industry. # To obtain quality mortars and that do not present problems derived from the mineral composition of the slate, they use specific cements as well as powder additives and limes. # The invention protects, in addition to mortars, the method of obtaining sands from slate residues, as well as the manufacturing process of the different mortars based on their uses and use of the additives necessary to obtain them.
Description
Procedimiento de obtención de mortero seco de cemento y cemento y cal para la construcción, realizado con residuos de pizarra. Procedure for obtaining dry cement and cement mortar and lime for construction, made with slate residues.
5 5
OBJETO DE LA INVENCIÓN: OBJECT OF THE INVENTION:
La presente invención se refiere a la fabricación de morteros sustituyendo la arena por residuo procedente de la industria extractiva de la pizarra. The present invention relates to the manufacture of mortars by replacing sand with waste from the slate extractive industry.
Mediante la utilización de cementos específicos y aditivos orgánicos en polvo se consiguen morteros con buenas propiedades para su uso en el sector de la construcción 10 y se evitan los problemas que los residuos de pizarra presentan, derivados de la forma de las partículas del árido generado y de las interacciones químicas de estos residuos con ciertos componentes presentes en los conglomerantes. By using specific cements and organic powder additives, mortars with good properties for use in the construction sector 10 are achieved and the problems that slate residues present, derived from the shape of the aggregate aggregate particles and of the chemical interactions of these residues with certain components present in the binders.
La industria extractiva de la pizarra genera una importante cantidad de residuos. La mayor parte de éstos se depositan en vertederos próximos a las zonas de extracción generando graves daños medioambientales. Resulta necesario establecer procedimientos de reciclado y reutilización que permitan eliminar la mayor cantidad 20 posible de residuos de manera que se puedan recuperar los entornos naturales gravemente dañados por este tipo de prácticas. The slate extractive industry generates a significant amount of waste. Most of these are deposited in landfills near the extraction areas causing serious environmental damage. It is necessary to establish recycling and reuse procedures to eliminate as much waste as possible so that natural environments severely damaged by these types of practices can be recovered.
El éxito para la reutilización de este tipo de residuos depende, en gran medida, de encontrar usos rentables y con alto consumo de los mismos. La presente invención reúne 25 ambas cualidades y redunda en un importante avance hacia la mejora medioambiental y la sostenibilidad de la industria extractiva de la pizarra. The success for the reuse of this type of waste depends, to a large extent, on finding cost-effective and high-consumption uses thereof. The present invention combines both qualities and results in an important advance towards the environmental improvement and sustainability of the slate extractive industry.
La pizarra se ha utilizado anteriormente como parte del árido en la fabricación de hormigones, principalmente, mostrando siempre importantes problemas de durabilidad 30 debido a los procesos de reactividad que sufre frente a los álcalis de los cementos. En la presente invención se da solución a estos problemas asegurando una mayor y mejor durabilidad del producto. Slate has previously been used as part of the aggregate in the manufacture of concrete, mainly, always showing significant durability problems 30 due to the reactivity processes that it suffers from cement alkalis. In the present invention, these problems are solved by ensuring greater and better product durability.
El mortero objeto de la invención se componen de cemento puzolánico y de pizarra triturada y clasificada como árido. La relación entre la cantidad de cemento y árido de 5 pizarra varía en función del tipo y características del mortero a fabricar y el uso que se va a hacer de él. El tipo de cemento a utilizar será un CEM IV que dependerá de la accesibilidad de los cementos en la zona de fabricación de los morteros. The mortar object of the invention consists of pozzolanic cement and crushed slate and classified as aggregate. The relationship between the amount of cement and aggregate of 5 slate varies depending on the type and characteristics of the mortar to be manufactured and the use that will be made of it. The type of cement to be used will be a CEM IV that will depend on the accessibility of the cements in the mortar manufacturing zone.
El objeto de la invención es la obtención de morteros sustituyendo la arena por residuo de 10 pizarra, procedente de la industria, de tamaños de partícula entre 0 y 2 mm. Las dosificaciones pueden incluir diferentes aditivos, en función de sus características, y se amasan con diferentes cantidades de agua para asegurar relaciones agua/cemento que aporten una consistencia y trabajabilidad adecuadas para su posterior puesta en obra. The object of the invention is to obtain mortars by replacing the sand with residue of 10 slate, from the industry, of particle sizes between 0 and 2 mm. Dosages may include different additives, depending on their characteristics, and are kneaded with different amounts of water to ensure water / cement ratios that provide adequate consistency and workability for later commissioning.
15 fifteen
La granulometría de los áridos de pizarra puede ser variada y también dependerá del uso al que el mortero esté destinado. Una posibilidad es seleccionar curvas granulométricas que entren dentro del uso de las arenas para hormigón, especificado en la EHE-08, o del uso de la antigua Norma Básica de la Edificación NBE FL-90, para morteros empleados en fábrica de ladrillo o, incluso, que entren en ambos usos granulométricos. 20 The granulometry of slate aggregates can be varied and will also depend on the use to which the mortar is intended. One possibility is to select granulometric curves that fall within the use of concrete sands, specified in EHE-08, or the use of the old Basic Building Standard NBE FL-90, for mortars used in brickwork or even , that enter both granulometric uses. twenty
Con las dosificaciones optimizadas se generan morteros que, tanto en estado fresco como en estado endurecido, cumplen con todas las especificaciones y normas aplicables y alcanzan unos estándares de calidad a la altura de los morteros que se comercializan en la actualidad. 25 With optimized dosages, mortars are generated that, both fresh and hardened, comply with all applicable specifications and standards and reach quality standards at the height of mortars that are currently marketed. 25
En primer lugar, se procede a establecer una granulometría para los áridos a partir de las pizarras debidamente procesadas. El procesado de las pizarras conlleva el machacado 30 de los grandes trozos de roca inicial, de los que se parte, y el tamizado para la separación de los distintos tamaños de grano necesarios para recomponer la granulometría seleccionada. First, we proceed to establish a granulometry for aggregates from properly processed slates. The processing of the slates entails crushing 30 of the large pieces of initial rock, from which it is split, and sieving for the separation of the different grain sizes necessary to recompose the selected granulometry.
A continuación se pesan la cantidad de la arena, preparada anteriormente, y la de cemento tipo CEM IV, en las cantidades establecidas en la dosificación. A este material se le une el o los aditivos sólidos debidamente pesados. El conjunto se mezcla hasta obtener un material granular homogéneo. El mortero seco queda, así, preparado para su 5 amasado. Next, the amount of the sand, prepared previously, and the cement type CEM IV, are weighed in the amounts established in the dosage. To this material is added the solid or additives duly heavy. The whole is mixed until a homogeneous granular material is obtained. The dried mortar is thus prepared for its kneading.
Por último, se añade la cantidad de agua tal que proporcione la consistencia adecuada del mortero fresco, según UNE-EN 1015-3: 2000, y se realiza el amasado del conjunto según UNE-EN 1015-2:1998, respetando estrictamente los tiempos de amasado. Finally, the amount of water is added such that it provides the adequate consistency of the fresh mortar, according to UNE-EN 1015-3: 2000, and the mixing of the set according to UNE-EN 1015-2: 1998 is carried out, strictly respecting the times Kneading
10 10
Entre las ventajas de la invención está la obtención de morteros libres de desarrollar reactividades álcali-árido, mediante el uso de cemento tipo IV. Esto posibilita un adecuado comportamiento durante su vida útil y una mayor durabilidad. Among the advantages of the invention is the obtaining of mortars free of developing alkali-arid reactivities, through the use of type IV cement. This enables adequate behavior during its useful life and greater durability.
El uso de aditivos permite mejoras en la trabajabilidad y puesta en obra de los morteros. 15 En especial los aditivos aireantes, que disminuyen de forma importante el rozamiento entre las partículas con forma de laja que presentan las pizarras y que dificultan la movilidad de la masa. Los aireantes también disminuyen de forma importante la densidad del conjunto. Por ambos motivos los morteros con estos aditivos mejoran en gran medida su movilidad. 20 The use of additives allows improvements in the workability and commissioning of mortars. 15 Especially the aerated additives, which significantly reduce friction between the slab-shaped particles that the boards have and that hinder mass mobility. The aerators also significantly decrease the density of the whole. For both reasons the mortars with these additives greatly improve their mobility. twenty
Otra ventaja es la utilización de cales aéreas e hidráulicas en pequeños porcentajes respecto al cemento, con el propósito de añadir plasticidad a los morteros resultantes, mejorando también su trabajabilidad. Another advantage is the use of air and hydraulic limes in small percentages with respect to cement, with the purpose of adding plasticity to the resulting mortars, also improving their workability.
25 25
A continuación se procede a la descripción de varios ejemplos ilustrativos de dosificaciones de morteros realizados con pizarra, en las que se describen los principales parámetros a tener en cuenta para la caracterización de un mortero. Next, several illustrative examples of mortar dosages made with slate are described, in which the main parameters to be taken into account for the characterization of a mortar are described.
Como se puede observar, las características de los morteros varían de forma importante 30 en función del tipo de mortero que se quiere conseguir y los componentes que incluye, con los que se consigue modificar, de forma deliberada, dichas características. As can be seen, the characteristics of the mortars vary significantly depending on the type of mortar that is to be achieved and the components that it includes, with which it is possible to modify these characteristics deliberately.
Ejemplo 1 Example 1
A) Proceso de fabricación: A) Manufacturing process:
Se mezclan, en peso, 4 partes de árido de pizarra con 1 parte de cemento CEM IV/B (V) 32,5N. Se introduce la mezcla en la amasadora y se añade la cantidad de agua necesaria 5 para proporcionar una consistencia normal en el mortero. En este caso la cantidad de agua requerida ha sido tal que la relación agua/cemento (A/C) es 0,81. Se amasa durante 90 segundos, según estipula la norma UNE-EN 1015-2:1998. 4 parts of slate aggregate are mixed by weight with 1 part of CEM IV / B (V) 32.5N cement. The mixture is introduced into the kneader and the amount of water needed 5 is added to provide a normal consistency in the mortar. In this case the amount of water required has been such that the water / cement ratio (A / C) is 0.81. It is kneaded for 90 seconds, as stipulated by UNE-EN 1015-2: 1998.
B) Propiedades del mortero fresco: B) Properties of fresh mortar:
En la siguiente tabla se incluyen los valores representativos de las propiedades del 10 mortero fresco. The following table includes representative values of the properties of fresh mortar.
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- Trabajabilidad Workability
- UNE-EN 1015-9: 2000 min 52 UNE-EN 1015-9: 2000 min 52
- Retención de agua Water retention
- UNE 33-816-93 % 85 UNE 33-816-93% 85
- Densidad aparente Apparent density
- UNE-EN 1015-6: 1999 kg/m3 2.230 UNE-EN 1015-6: 1999 kg / m3 2,230
- Contenido en aire Air content
- UNE-EN 1015-7: 1999 % 3,8 UNE-EN 1015-7: 1999% 3.8
C) Propiedades del mortero endurecido: C) Properties of hardened mortar:
Las propiedades del mortero endurecido se incluyen a continuación. 15 The properties of the hardened mortar are included below. fifteen
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- R. flexión R. flexion
- UNE-EN 1015-11: 2000 MPa 4,4 UNE-EN 1015-11: 2000 MPa 4.4
- R. compresión R. compression
- 20,1 20.1
- Coeficiente de permeabilidad Coefficient of permeability
- UNE-EN 1015-19: 1999 18 UNE-EN 1015-19: 1999 18
- Coef. de absorción por capilaridad Coef of absorption by capillarity
- UNE-EN 1015-18 Kg/m2 min1/2 0,9 UNE-EN 1015-18 Kg / m2 min1 / 2 0.9
D) Ensayos de durabilidad del mortero: D) Mortar durability tests:
Se ha realizado el ensayo de reactividad álcali-sílice y álcali-silicato por el método acelerado en probetas de mortero (UNE 146508: 1999 EX), adaptándolo al mortero diseñado. No se observa ningún tipo de reactividad en el mortero. 5 The alkali silica and alkali silicate reactivity test has been carried out by the accelerated method in mortar specimens (UNE 146508: 1999 EX), adapting it to the designed mortar. No reactivity is observed in the mortar. 5
Ante la no existencia de normativa específica para este material, se ha realizado el ensayo de heladicidad, tomando como referencia la norma UNE 67028:1997 EX de ladrillos cerámicos, sobre probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado. Finalizado el ensayo no se observan defectos reseñables en las probetas de mortero ni disminución en las resistencias mecánicas. 10 In the absence of specific regulations for this material, the ice cream test has been carried out, taking as reference the standard UNE 67028: 1997 EX of ceramic bricks, on prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured. At the end of the test, there are no notable defects in the mortar specimens or a decrease in mechanical resistance. 10
Se ha realizado el ensayo de resistencia a la cristalización de sales adaptando el método descrito en la norma UNE-EN 12370: 1999, de piedra natural, a probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado. El resultado del ensayo es una ligera perdida superficial de material en las probetas no registrándose pérdida de resistencias mecánicas. 15 The salt crystallization resistance test has been carried out adapting the method described in the UNE-EN 12370: 1999 standard, of natural stone, to prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured. The result of the test is a slight surface loss of material in the specimens with no loss of mechanical resistance. fifteen
Ejemplo 2: Example 2:
A) Proceso de fabricación: A) Manufacturing process:
Se mezclan, en peso, 6 partes de árido de pizarra con 1 parte de cemento CEM IV/B (V) 32,5N. Se introduce la mezcla en la amasadora y se añade la cantidad de agua necesaria 20 para proporcionar una consistencia normal en el mortero. En este caso la cantidad de agua requerida ha sido tal que la relación agua/cemento (A/C) es 1,11. Se amasa durante 90 segundos, según estipula la norma UNE-EN 1015-2:1998. 6 parts of slate aggregate are mixed by weight with 1 part of CEM IV / B (V) 32.5N cement. The mixture is introduced into the kneader and the amount of water necessary 20 is added to provide a normal consistency in the mortar. In this case the amount of water required has been such that the water / cement ratio (A / C) is 1.11. It is kneaded for 90 seconds, as stipulated by UNE-EN 1015-2: 1998.
B) Propiedades del mortero fresco: B) Properties of fresh mortar:
En la siguiente tabla se incluyen los valores representativos de las propiedades del 25 mortero fresco. The following table includes representative values of the properties of fresh mortar.
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- Trabajabilidad Workability
- UNE-EN 1015-9: 2000 min 72 UNE-EN 1015-9: 2000 min 72
- Retención de agua Water retention
- UNE 33-816-93 % 86 UNE 33-816-93% 86
- Densidad aparente Apparent density
- UNE-EN 1015-6: 1999 kg/m3 2210 UNE-EN 1015-6: 1999 kg / m3 2210
- Contenido en aire Air content
- UNE-EN 1015-7: 1999 % 4,0 UNE-EN 1015-7: 1999% 4.0
C) Propiedades del mortero endurecido: C) Properties of hardened mortar:
Las propiedades del mortero endurecido se incluyen a continuación. The properties of the hardened mortar are included below.
5 5
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- R. flexión R. flexion
- UNE-EN 1015-11: 2000 MPa 3,1 UNE-EN 1015-11: 2000 MPa 3.1
- R. compresión R. compression
- 9,9 9.9
- Coeficiente de permeabilidad Coefficient of permeability
- UNE-EN 1015-19: 1999 15 UNE-EN 1015-19: 1999 15
- Coef. de absorción por capilaridad Coef of absorption by capillarity
- UNE-EN 1015-18 Kg/m2 min1/2 0,8 UNE-EN 1015-18 Kg / m2 min1 / 2 0.8
D) Ensayos de durabilidad del mortero: D) Mortar durability tests:
Reactividad álcali-sílice y álcali-silicato por el método acelerado en probetas de mortero (UNE 146508: 1999 EX), adaptado al mortero diseñado. No se observa ningún tipo de reactividad en el mortero. 10 Alkali-silica and alkali-silicate reactivity by the accelerated method in mortar specimens (UNE 146508: 1999 EX), adapted to the designed mortar. No reactivity is observed in the mortar. 10
Ensayo de heladicidad, tomando como referencia la norma UNE 67028:1997 EX, sobre probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado: No se observan defectos reseñables en las probetas de mortero ni disminución en las resistencias mecánicas. Ice cream test, taking as reference the UNE 67028: 1997 EX standard, on prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured: No notable defects are observed in the mortar specimens or decrease in mechanical strengths.
Resistencia a la cristalización de sales (UNE-EN 12370: 1999) sobre probetas 15 prismáticas de 40 x 40 x 1600 mm del mortero fabricado: Ligera pérdida superficial de material en las probetas no registrándose pérdida de resistencias mecánicas. Resistance to crystallization of salts (UNE-EN 12370: 1999) on prismatic specimens 15 of 40 x 40 x 1600 mm of the mortar manufactured: Slight surface loss of material in the specimens not registering loss of mechanical resistance.
20 twenty
Ejemplo 3: Example 3:
A) proceso de fabricación: A) manufacturing process:
Se mezclan, en peso, 6 partes de árido de pizarra y 1 parte de cemento CEM IV/B (V) 32,5N. Se añade una cantidad de 1,25 % en peso de cemento de un plastificante-aireante 5 en polvo y se mezcla hasta homogeneidad. Se introduce la mezcla en la amasadora y se añade una cantidad de agua adecuada para proporcionar una consistencia normal en el mortero. En este caso la cantidad de agua requerida ha sido tal que la relación agua/cemento (A/C) es 1,03. Se amasa durante 90 segundos, según estipula la norma UNE-EN 1015-2:1998. 10 6 parts of slate aggregate and 1 part of CEM IV / B (V) 32.5N cement are mixed by weight. An amount of 1.25% by weight of cement of a plasticizer-aerating powder 5 is added and mixed until homogeneous. The mixture is introduced into the kneader and an adequate amount of water is added to provide a normal consistency in the mortar. In this case the amount of water required has been such that the water / cement ratio (A / C) is 1.03. It is kneaded for 90 seconds, as stipulated by UNE-EN 1015-2: 1998. 10
B) Propiedades del mortero fresco: B) Properties of fresh mortar:
En la siguiente tabla se incluyen los valores representativos de las propiedades del mortero fresco. The following table includes representative values of the properties of the fresh mortar.
15 fifteen
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- Trabajabilidad Workability
- UNE-EN 1015-9: 2000 min 208 UNE-EN 1015-9: 2000 min 208
- Retención de agua Water retention
- UNE 33-816-93 % 86 UNE 33-816-93% 86
- Densidad aparente Apparent density
- UNE-EN 1015-6: 1999 kg/m3 2070 UNE-EN 1015-6: 1999 kg / m3 2070
- Contenido en aire Air content
- UNE-EN 1015-7: 1999 % 11,8 UNE-EN 1015-7: 1999% 11.8
La inclusión del plastificante-aireante disminuye la densidad aparente aumentando el contenido de aire en la masa y el tiempo de trabajabilidad de esta. The inclusion of the plasticizer-aerator decreases the apparent density by increasing the air content in the mass and the working time of this.
C) Propiedades del mortero endurecido: 20 C) Properties of hardened mortar: 20
Las propiedades del mortero endurecido se incluyen a continuación. The properties of the hardened mortar are included below.
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- R. flexión R. flexion
- UNE-EN 1015-11: 2000 MPa 3,2 UNE-EN 1015-11: 2000 MPa 3.2
- R. compresión R. compression
- 9,3 9.3
- Coeficiente de permeabilidad Coefficient of permeability
- UNE-EN 1015-19: 1999 9 UNE-EN 1015-19: 1999 9
- Coef. de absorción por capilaridad Coef of absorption by capillarity
- UNE-EN 1015-18 Kg/m2 min1/2 0,19 UNE-EN 1015-18 Kg / m2 min1 / 2 0.19
El efecto del aditivo aireante hace que el coeficiente de absorción de agua disminuya de forma importante, al igual que la permeabilidad y las resistencias mecánicas. The effect of the aerating additive causes the water absorption coefficient to decrease significantly, as does the permeability and mechanical strengths.
D) Ensayos de durabilidad del mortero: 5 D) Mortar durability tests: 5
Reactividad álcali-sílice y álcali-silicato por el método acelerado en probetas de mortero (UNE 146508: 1999 EX), adaptado al mortero diseñado. No se observa ningún tipo de reactividad en el mortero. Alkali-silica and alkali-silicate reactivity by the accelerated method in mortar specimens (UNE 146508: 1999 EX), adapted to the designed mortar. No reactivity is observed in the mortar.
Ensayo de heladicidad, tomando como referencia la norma UNE 67028:1997 EX, sobre probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado: No se observan 10 defectos reseñables en las probetas de mortero ni disminución en las resistencias mecánicas. Ice cream test, taking as reference the UNE 67028: 1997 EX standard, on prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured: There are no 10 notable defects in the mortar specimens or decrease in mechanical strengths.
Resistencia a la cristalización de sales (UNE-EN 12370: 1999) sobre probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado: Ligera pérdida superficial de material en las probetas no registrándose pérdida de resistencias mecánicas. 15 Resistance to crystallization of salts (UNE-EN 12370: 1999) on prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured: Slight surface loss of material in the specimens not registering loss of mechanical resistance. fifteen
Ejemplo 4: Example 4:
A) proceso de fabricación: A) manufacturing process:
Se mezclan, en peso, 6 partes de árido de pizarra y 1 parte de cemento CEM IV/B (V) 32,5N. Se añade una cantidad de 1,25 % en peso de cemento de un plastificante-aireante 20 en polvo y cal aérea, del tipo CL90-S, en una cantidad del 15 % en peso de cemento y se mezclan hasta homogeneidad. Se introduce la mezcla en la amasadora y se añade una cantidad de agua adecuada para proporcionar una consistencia normal en el mortero. En este caso la cantidad de agua requerida ha sido tal que la relación agua/cemento (A/C) es 1,08. Se amasa durante 90 segundos, según estipula la norma UNE-EN 1015-2:1998. 6 parts of slate aggregate and 1 part of CEM IV / B (V) 32.5N cement are mixed by weight. An amount of 1.25% by weight of cement of a plasticizer-aerating 20 powder and air lime, of the CL90-S type, in an amount of 15% by weight of cement is added and mixed until homogeneous. The mixture is introduced into the kneader and an adequate amount of water is added to provide a normal consistency in the mortar. In this case the amount of water required has been such that the water / cement ratio (A / C) is 1.08. It is kneaded for 90 seconds, as stipulated by UNE-EN 1015-2: 1998.
B) Propiedades del mortero fresco: 5 B) Properties of fresh mortar: 5
En la siguiente tabla se incluyen los valores representativos de las propiedades del mortero fresco. The following table includes representative values of the properties of the fresh mortar.
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- Trabajabilidad Workability
- UNE-EN 1015-9: 2000 min 253 UNE-EN 1015-9: 2000 min 253
- Retención de agua Water retention
- UNE 33-816-93 % 90 UNE 33-816-93% 90
- Densidad aparente Apparent density
- UNE-EN 1015-6: 1999 kg/m3 2100 UNE-EN 1015-6: 1999 kg / m3 2100
- Contenido en aire Air content
- UNE-EN 1015-7: 1999 % 12,0 UNE-EN 1015-7: 1999% 12.0
La adición de cal aumenta el tiempo de trabajabilidad así como la retención de agua 10 aportando untuosidad al mortero fresco. The addition of lime increases the workability time as well as the retention of water 10 providing smoothness to the fresh mortar.
C) Propiedades del mortero endurecido: C) Properties of hardened mortar:
Las propiedades del mortero endurecido se incluyen a continuación. The properties of the hardened mortar are included below.
15 fifteen
- PROPIEDAD PROPERTY
- NORMA UNIDAD VALOR VALUE UNIT STANDARD
- R. flexión R. flexion
- UNE-EN 1015-11: 2000 MPa 2,5 UNE-EN 1015-11: 2000 MPa 2.5
- R. compresión R. compression
- 9,4 9.4
- Coeficiente de permeabilidad Coefficient of permeability
- UNE-EN 1015-19: 1999 10 UNE-EN 1015-19: 1999 10
- Coef. de absorción por capilaridad Coef of absorption by capillarity
- UNE-EN 1015-18 Kg/m2 min1/2 0,19 UNE-EN 1015-18 Kg / m2 min1 / 2 0.19
Los resultados del mortero endurecido no se ven apreciablemente afectados por la inclusión de la cal. The results of the hardened mortar are not significantly affected by the inclusion of lime.
D) Ensayos de durabilidad del mortero: 5 D) Mortar durability tests: 5
Reactividad álcali-sílice y álcali-silicato por el método acelerado en probetas de mortero (UNE 146508: 1999 EX), adaptado al mortero diseñado. No se observa ningún tipo de reactividad en el mortero. Alkali-silica and alkali-silicate reactivity by the accelerated method in mortar specimens (UNE 146508: 1999 EX), adapted to the designed mortar. No reactivity is observed in the mortar.
Ensayo de heladicidad, tomando como referencia la norma UNE 67028:1997 EX, sobre probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado: Se observa ligera 10 pérdida superficial de material en las probetas de mortero sin disminución en las resistencias mecánicas. Ice cream test, taking the UNE 67028: 1997 EX standard as a reference, on prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured: There is a slight loss of surface material in the mortar specimens without a decrease in mechanical strengths.
Resistencia a la cristalización de sales (UNE-EN 12370: 1999) sobre probetas prismáticas de 40 x 40 x 1600 mm del mortero fabricado: Ligera pérdida superficial de material en las probetas no registrándose pérdida de resistencias mecánicas. 15 Resistance to crystallization of salts (UNE-EN 12370: 1999) on prismatic specimens of 40 x 40 x 1600 mm of the mortar manufactured: Slight surface loss of material in the specimens not registering loss of mechanical resistance. fifteen
Claims (8)