DE502532C

DE502532C - Process for the production of silver-plated metal objects such as tableware

Info

Publication number: DE502532C
Application number: DEW81239D
Authority: DE
Original assignee: M H Wilkens & Soehne A G
Current assignee: M H Wilkens & Soehne A G
Priority date: 1928-12-12
Filing date: 1928-12-12
Publication date: 1931-11-07

Description

Verfahren zur Herstellung von versilberten rdetallgegenständen, beispielsweise Tafelgeräten Die Erfindung bezieht sich auf ein Verfahren zur Herstellung von versilberten Metallgegenständen, beispielsweise Tafelgeräten, Besteckteilen o. dgl., bei denen mehrfache Silberschichten, die durch Glühen verbunden werden, angewandt werden.Process for the production of silver-plated metal objects, for example Tableware The invention relates to a method for the production of silver-plated Metal objects, such as table utensils, cutlery or the like. Where multiple layers of silver joined by annealing are applied.

Es ist schon vorgeschlagen, den elektrolytischen Niederschlag auf einer Unterlage durch Anwendung eines hohen Druckes unter gleichzeitiger Erwärmung bis zur Glühhitze zusammenzuschweißen. Andererseits hat man schon eine Legierung auf ein Grundmetall niedergeschlagen und den Niederschlag bei hoher Temperatur in reduzierendem Gase geglüht.It has already been suggested that the electrolytic precipitate be applied a pad by applying a high pressure while heating at the same time to be welded together to the point of glowing heat. On the other hand, you already have an alloy deposited on a base metal and the precipitate at high temperature in annealed with reducing gases.

Die vorliegende Erfindung besteht demgegenüber darin, daß auf einem brandeiförmigen bzw. Einzelhalbfabrikat aus Neusilber eine bzw. nacheinander mehrere Feinsilberschichten durch galvanische oder Spritzverfahren aufgebracht werden, diese in bekannter Weise mechanisch durch Walren, Pressen, Hämmern o. dgl. bearbeitet und danach geglüht werden.The present invention, on the other hand, is that on one brand egg-shaped or single semi-finished product made of nickel silver one or several successively Fine silver layers are applied by galvanic or spraying processes, these Machined mechanically in a known manner by rolling, pressing, hammering or the like and then annealed.

Durch ein solches Verfahren wird nicht beabsichtigt, eine feine Silberoberfläche, sondern eine Anreicherung der Unterlage mit Silber zu erzielen. Die aufgebrachten Silberschichten wandern in die Oberflächenkristalle der Unterlage, gehen also eine Diffusion mit der Unterlage ein. Dadurch wird insbesondere erreicht, daß eine Unterlage geschaffen wir=d, die eine besonders günstige Verbindung mit der endgültigen Versilberungsschicht gewährleistet.Such a process is not intended to produce a fine silver surface, but to achieve an enrichment of the base with silver. The angry Silver layers migrate into the surface crystals of the base, so they go one Diffusion with the substrate. This achieves in particular that a base we created = d, which is a particularly favorable connection with the final silver-plating layer guaranteed.

Durch die Erfindung wird ferner erreicht, daß auch an solchen Stellen des Metallgegenstandes, wo bisher keinerlei Verstärkung der Silberauflage möglich war, nach Abnutzung der äußeren Plattierung (Galvanisierung) die Abgrenzung gegen die Farbe des Unterlagemetalls allmählich verläuft, so daß unangenehm auffallende Flecken auf dem Metallgegenstand nach Möglichkeit gemildert werden.The invention also ensures that in such places of the metal object, where previously no reinforcement of the silver coating was possible was the demarcation against after the outer plating (electroplating) was worn down the color of the base metal gradually runs out, making it uncomfortably noticeable Any stains on the metal object should be reduced if possible.

Vorteilhaft ist ferner, daß die Aufbringung der Feinsilberschichten dem fortschreitenden Herstellungsverfahren des Metallgegenstandes angepaßt ist, so daß ein besonderer Arbeitsgang für die Anreicherung der Unterlage mit Silber nicht erforderlich wird, sondern die Herstellung des Metallgegenstandes wie üblich erfolgen kann.It is also advantageous that the application of the fine silver layers is adapted to the progressive manufacturing process of the metal object, so that a special operation for the enrichment of the base with silver is not required, but the production of the metal object as usual can be done.

Die Erfindung läßt sich in verschiedener Weise ausführen. Ein Ausführungsbeispiel ist das -Folgende.The invention can be carried out in various ways. An embodiment is the following.

Nach der Erfindung wird zunächst das Brandei, also eine Unterlage aus Nichteisenmetall, und zwar beispielsweise Neusilber;, entsprechend ausgestanzt. Dann erfolgt, gegebenenfalls nach üblicher Bearbeitung, wie Beizen o. dgl., das Aufbringen der ersten Silberauflage durch Plattierung, Galvanisierung oder Spritzverfahren. Nunmehr wird das Brandei mechanisch in kaltem Zustande bearbeitet, beispielsweise gewalzt, gepreßt oder gehämmert, so daß die Silberschicht zur innigen Anlage an die Unterlage gebracht wird. Hierauf wird geglüht. Dadurch wird eine Diffusion der aufgebrachten Silberschicht in die Oberflächenkristalle der Unterlage bewirkt; Nunmehr wird eine zweite Silberauflage in gleicher Weise aufgebracht und der weiteren mechanischen Kaltbearbeitung unterzogen und dann wieder geglüht. In gleicher Weise können dann noch hintereinander weitere Silberauflagen aufgebracht werden, je nachdem, wie weit eine Anreicherung der Unterlage mit Silber gewünscht wird. Erst dann wird kalt geprägt, der Metallgegenstand, beispielsweise Löffel, abgegratet und geglüht.According to the invention, the first thing is the brand egg, i.e. a base made of non-ferrous metal, for example nickel silver; punched out accordingly. Then, if necessary after customary processing, such as pickling or the like Application of the first silver layer by plating, electroplating or spraying. Now the fire egg is mechanically processed in the cold state, for example rolled, pressed or hammered so that the silver layer becomes intimate System is brought to the document. This is followed by annealing. This creates a diffusion the applied silver layer in the surface crystals of the substrate; Now a second silver layer is applied in the same way and the other subjected to mechanical cold working and then annealed again. In the same way further silver plating can then be applied one after the other, depending on how far an enrichment of the base with silver is desired. Only then will cold embossed, the metal object, for example a spoon, trimmed and annealed.

Es ist zweckmäßig, die Aufbringung der Feinsilberschichten dem fortschreitenden Arbeitsverfahren des Metallgegenstandes anzupassen. Beispielsweise kann also zunächst die brandeiförmige Unterlage, wie oben erwähnt, galvanisiert, gepreßt und geglüht werden; beim jeweiligen Pressen kann dann zugleich die Form des Gegenstandes zweckentsprechend verändert werden.It is useful to apply the fine silver layers to the progressive Adapt the working process of the metal object. For example, so initially the brand egg-shaped base, as mentioned above, galvanized, pressed and annealed will; during the respective pressing, the shape of the object can then also be adapted to the purpose to be changed.

Nach dem Vorprägen wird nun zunächst nochmals eine Silberschicht ohne nachträgliche Ausglühung aufgebracht und erst nunmehr der Gegenstand fertig geprägt, gesäubert und abgegratet. Erst nachdem der Gegenstand so weit hergestellt ist, erfolgt eine Endversilberung in üblicher Weise durch Galvanisierung o. dgl., worauf ein Nachprägen im polierten Gesenk vorgenommen wird.After the pre-embossing, there is now another layer of silver without Subsequent annealing applied and only now the object is fully embossed, cleaned and trimmed. Only after the item has been manufactured so far takes place a final silver plating in the usual way by electroplating o. The like., whereupon a Reprinting is made in the polished die.

Um das Verfahren noch leichter durchführen zu können und in seiner Wirkung zu erhöhen, ist es zweckmäßig, als Unterlage eine schwachsilberhaltige Metallegierung zu verwenden. Dadurch wird die Anreicherung der Unterlage mit Silber begünstigt.In order to be able to carry out the procedure even more easily and in his To increase the effect, it is advisable to use a metal alloy containing weak silver as a base to use. This promotes the enrichment of the base with silver.

Der in dieser Weise hergestellte Metallgegenstand, wie insbesondere Tafelbestecke, Besteckteile o. dgl., besitzt dann die Eigenschaft einer außerordentlich starken und gut verfestigten Versilberung. Es ist eine Verstärkung der Versilberung auch an allen Stellen des Gebrauchsgegenstandes erzielt, während alle bisherigen, nachträglich angewandten Verfahren zur Aufbringung einer Verstärkung der Silberauflage, besonders an den Aufliegestellen, nur eine teilweise Verstärkung der Silberauflage erreichen konnten.The metal object produced in this way, such as in particular Table cutlery, pieces of cutlery o. The like. Then has the property of an extraordinary strong and well solidified silver plating. It is a reinforcement of the silver plating also achieved at all points of the commodity, while all previous, subsequently applied process to apply a reinforcement to the silver layer, especially at the resting points, only a partial reinforcement of the silver plating could achieve.

Ein solcher Gebrauchsgegenstand besitzt also eine außerordentlich hohe Lebensdauer infolge der Verstärkung an seiner ganzen Oberfläche. Die äußerste Silberschicht läuft nur ganz allmählich in das Unterlagemetall über; die sich nach diesem Verfahren auch ohne Schwierigkeiten an sämtlichen Tafelbesteck- o. dgl. Geräten anbringen läßt.Such a commodity therefore has an extraordinary one long service life due to the reinforcement on its entire surface. The extreme The silver layer only gradually overflows into the underlying metal; which are after this method without difficulty on all table cutlery or similar devices can be attached.

Es wird eine außerordentlich günstige Ver-Bindung der endgültigen Versilberungsschicht mit der Unterlage erreicht.It becomes an extraordinarily favorable bond of the final Silver plating achieved with the backing.

Claims

PATENT CLAIMS: i. Process for the production of silver-plated metal objects, for example table utensils, cutlery or the like, in which multiple layers of silver, which are connected to the substrate by annealing are used, characterized in that, that on a brand egg-shaped or single semi-finished product made of non-ferrous metal, for example Nickel silver, one or several layers of fine silver one after the other through galvanic or spray processes are applied, these mechanically in a known manner Rolling, pressing, hammering or the like. Machined and then annealed.

2. Procedure according to claim i, characterized in that the application of the fine silver layers is adapted to the progressive manufacturing process of the metal object.

3. The method according to claim i and 2,. characterized in that the finished embossed and the item provided with the final silver plating was re-embossed in the polished die will.