DE4211248A1 - Agent for barrier for preparing subsurface for coating - comprises organic binder of water-soluble cellulose ether powder - Google Patents
Agent for barrier for preparing subsurface for coating - comprises organic binder of water-soluble cellulose ether powderInfo
- Publication number
- DE4211248A1 DE4211248A1 DE4211248A DE4211248A DE4211248A1 DE 4211248 A1 DE4211248 A1 DE 4211248A1 DE 4211248 A DE4211248 A DE 4211248A DE 4211248 A DE4211248 A DE 4211248A DE 4211248 A1 DE4211248 A1 DE 4211248A1
- Authority
- DE
- Germany
- Prior art keywords
- water
- composition
- vinyl acetate
- cellulose
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die Erfindung bezieht sich auf ein Mittel zum Herstellen einer zur Vorbereitung eines zu verputzenden Untergrundes die nenden Aufbrennsperre, das eine Zusammensetzung auf der Basis eines organischen Bindemittels aufweist.The invention relates to a means for manufacturing one to prepare a surface to be plastered The burning lock, which is a composition based of an organic binder.
Derartige Aufbrennsperren dienen der Vorbereitung des zu verputzenden Untergrundes, beispielsweise Wänden oder Decken von Bauwerken im Innen- oder Außenbereich. Durch die Vor bereitung wird das Wassersaugverhalten des zu verputzenden Un tergrundes günstig beeinflußt, so daß eine dauerhafte und feste Haftung des Putzmörtels auf dem zu verputzenden Untergrund er reicht wird.Such baffles are used to prepare the plastering surface, for example walls or ceilings of buildings indoors or outdoors. By the front preparation is the water suction behavior of the Un to be plastered tergrundes favorably influenced, so that a permanent and solid Adhesion of the plastering mortar to the surface to be plastered is enough.
Bei bisher bekannten Aufbrennsperren der eingangs ge nannten Art liegt das die Basis bildende organische Bindemittel in flüssiger Form vor. Zum Transport dieser Flüssigerzeugnisse vom Hersteller zum Verbraucher sind daher geeignete Behälter, insbesondere Kunststoff- oder Metalleimer erforderlich. Abge sehen von dem wegen des Flüssigkeitsgehalts hohen Trans portgewicht bereitet die Entsorgung der nach dem Gebrauch noch mit Reststoffen belegten Eimer große Schwierigkeiten. Ferner ist bei diesen Flüssigerzeugnissen in der Regel ein Konser vierungsmittel erforderlich. Da die Flüssigerzeugnisse frost empfindlich sind, müssen bei der Lagerung und dem Transport überzeugende Gegenmaßnahmen ergriffen werden. Schließlich be steht auch ein erheblicher Nachteil der Flüssigerzeugnisse darin, daß sie in der Regel nicht vollständig lösungsmittelfrei hergestellt werden können. Diese Lösungsmittelgehalte sind vor allem bei der Anwendung in Innenräumen und ganz allgemein im Hinblick auf die Umweltverträglichkeit des Mittels nach teilhaft.In previously known burnout locks of the beginning named type is the organic binder that forms the basis in liquid form. For the transport of these liquid products Suitable containers from manufacturer to consumer are therefore especially plastic or metal buckets required. Abge see from the high trans due to the liquid content portweight still prepares the disposal after use Buckets covered with residues are very difficult. Further is usually a consumer for these liquid products funds required. Because the liquid products frost sensitive during storage and transportation convincing countermeasures are taken. Finally be there is also a significant disadvantage of liquid products in that they are usually not completely solvent-free can be produced. These solvent levels are present especially when used indoors and in general in With regard to the environmental compatibility of the product partial.
Der Erfindung liegt die Aufgabe zugrunde, ein Mittel der eingangs genannten Art zu schaffen, dessen Handhabung bei der Lagerung und dem Transport erleichtert ist und das darüber hinaus eine besonders hohe Umweltverträglichkeit aufweist.The invention has for its object a means of to create the type mentioned, its handling in the Storage and transportation is facilitated and that also has a particularly high level of environmental compatibility.
Erfindungsgemäß wird diese Aufgabe dadurch gelöst, daß die Zusammensetzung als ein mit Wasser anzumachendes Trocken pulver ausgebildet ist, bei dem das Bindemittel durch ein wasserlösliches Celluloseether-Pulver gebildet ist.According to the invention, this object is achieved in that the composition as a dry to be made with water is formed powder, in which the binder by a water-soluble cellulose ether powder is formed.
Das erfindungsgemäße Mittel ist also ein reines Trocken pulver, dem das Anmachwasser erst zum Zeitpunkt und am Ort der Verarbeitung zugegeben wird. Da es völlig lösungsmittelfrei ge halten werden kann, ist es geruchsarm. Dies ist besonders bei der Anwendung in Innenräumen von Vorteil. Auch bedarf das Trockenpulver keines Konservierungsmittels. Die Lagerung und der Transport kann in Papiersäcken erfolgen, deren Entsorgung erheblich einfacher ist als bei Gebinden, insbesondere Kunst stoff- und Blecheimern, für Flüssigprodukte. Sollte das Trocken pulver, beispielsweise bei Unfällen, unbeabsichtigt verschüttet werden, kann es mechanisch aufgenommen werden, ohne daß nen nenswerte Grundwasserverunreinigungen zu besorgen sind. Schließlich braucht beim Transport des als Trockenpulver aus gebildeten Mittels vom Hersteller zum Verbraucher - im Un terschied zu den herkömmlichen Flüssigprodukten - nicht das Anmachwasser mittransportiert zu werden, was eine erhebliche Gewichts- und Volumeneinsparung bedeutet. Somit erweist sich das erfindungsgemäße Mittel in vieler Hinsicht als besonders umweltverträglich. Letzteres ergibt sich insbesondere auch aus der hinsichtlich des Umweltschutzes äußerst unbedenklichen Natur des Bindemittels, nämlich Celluloseether.The agent according to the invention is therefore a pure dry powder, to which the mixing water only at the time and at the place of Processing is added. Since it is completely solvent-free can be kept, it is low odor. This is particularly the case with indoor use is an advantage. That also needs Dry powder no preservative. The storage and the transport can take place in paper bags, their disposal is considerably easier than with containers, especially art fabric and metal buckets, for liquid products. Should the dry powder, e.g. accidentally spilled be, it can be mechanically recorded without NEN noteworthy groundwater pollution. Finally, when transporting the dry powder educated means from the manufacturer to the consumer - in the Un different from conventional liquid products - not that Mixing water to be transported, which is a considerable Weight and volume saving means. So it turns out the agent according to the invention as special in many respects environmentally friendly. The latter also results in particular from the extremely harmless in terms of environmental protection Nature of the binder, namely cellulose ether.
Für den Verarbeiter des Mittels ergibt sich zunächst der Vorteil einer vereinfachten Lagerhaltung, da das Mittel - im Gegensatz zu wasserhaltigen Erzeugnissen - nicht frostem pfindlich ist. Auch können beim Verarbeiter die anwendungs technischen Eigenschaften durch unterschiedliche Wasserzugabe Mengen in größerem Masse variiert werden. Das Anmachen mit Wasser kann in bedarfsgerechten Mengen erfolgen. Angebrochene Packungen sind bei sachgerechter Lagerung lange gebrauchsfähig.For the processor of the agent, this initially results in Advantage of simplified storage, since the agent - in Contrary to water-based products - not frostem is sensitive. Also at the processor the application technical properties due to different water addition Quantities can be varied to a greater extent. Starting with Water can be used in quantities appropriate to the needs. Dawn If properly stored, packs can be used for a long time.
Durch den Wegfall der Konservierungsmittel und des Lösungsmittels vermindert sich auch die Anzahl der zur Her stellung erforderlichen Ausgangsstoffe. Die Zusammensetzungen können auf herkömmlichen Mischeinrichtungen hergestellt werden, ohne daß besondere Geräte für die Mischung flüssiger Be standteile benötigt werden.By eliminating the preservatives and the The number of solvents also decreases position necessary starting materials. The compositions can be produced on conventional mixing devices, without special equipment for mixing liquid be components are needed.
In einer bevorzugten Ausführungsform des erfin dungsgemäßen Mittels ist vorgesehen, daß das Celluloseether- Pulver mindestens einen der folgenden Bestandteile enthält: Methyl-hydroxy-ethylen-Cellulose, Ethylen-hydroxy-ethyl-Cellu lose oder Natrium-Carboxymethyl-Cellulose. Es hat sich gezeigt, daß derartige Celluloseether-Pulver als Bindemittel für die erfindungsgemäßen Aufbrennsperren besonders geeignet sind. In a preferred embodiment of the invent means according to the invention provides that the cellulose ether Powder contains at least one of the following: Methyl-hydroxy-ethylene-cellulose, ethylene-hydroxy-ethyl-cellu loose or sodium carboxymethyl cellulose. It has shown, that such cellulose ether powder as a binder for the Burn-up barriers according to the invention are particularly suitable.
Vorzugsweise ist bei dem erfindungsgemäßen Mittel vor gesehen, daß die Zusammensetzung ein zur Anquellverzögerung dienendes Zusatzmittel enthält. Durch die Anquellverzögerung werden die Verarbeitungseigenschaften des mit Wasser ange machten Mittels verbessert.Preferably, the agent according to the invention seen that the composition is one for swelling delay serving additive contains. Due to the swell delay the processing properties of the with water made means improved.
Zur Erzielung oder Verbesserung bestimmter technischer Eigenschaften des zur Verarbeitung mit Wasser angemachten Mittels sind in der Zusammensetzung des erfindungsgemäßen Mittels auch noch weitere Zusatzmittel zweckmäßig.To achieve or improve certain technical Properties of the water-treated Agents are in the composition of the invention Also useful with other additives.
In diesem Zusammenhang ist in einer Ausführungsform des erfindungsgemäßen Mittels vorgesehen, daß die Zusammensetzung ein in Wasser dispergierbares, pulverförmiges Zusatzmittel enthält.In this context, in one embodiment of the means provided according to the invention that the composition a water-dispersible, powdery additive contains.
Ein derartiges, in Wasser dispergierbares, pulver förmiges Zusatzmittel, also ein Dispersionspulver, bewirkt eine stärkere Herabsetzung des Saugverhaltens des zu verputzenden Untergrundes und eine Verbesserung der Haftung des Putzes am Untergrund.Such a water-dispersible powder shaped additive, i.e. a dispersion powder, causes a greater reduction in the suction behavior of the plastered Surface and an improvement in the adhesion of the plaster to Underground.
Für das als Dispersionspulver vorgesehene Zusatzmittel kommen zweckmäßig die folgenden Stoffe sowohl allein oder als kombinierte Bestandteile in Betracht: homopolymeres Vinyl acetat, Vinylacetat/Ethylen-Copolymerisat, Vinylacetat/Vinyl ester-Copolymerisat, Vinylacetat/Ethylen-Copolymerisat mit ei nem Acrylsäurederivat oder Vinylacetat/Vinylversatat-Copoly merisat.For the additive intended as a dispersion powder the following substances are useful both alone or as combined components into consideration: homopolymeric vinyl acetate, vinyl acetate / ethylene copolymer, vinyl acetate / vinyl ester copolymer, vinyl acetate / ethylene copolymer with egg nem acrylic acid derivative or vinyl acetate / vinyl versatate copoly merisat.
In einer weiteren Ausführungsform des erfindungsgemäßen Mittels ist vorgesehen, daß die Zusammensetzung ein als Ent schäumer dienendes Zusatzmittel enthält. Der Entschäumer hat die Aufgabe, eine Schaumbildung beim Anmischen des Mittels mit dem Anmachwasser zu unterdrücken. Außerdem soll dadurch er reicht werden, daß der von dem angemachten Mittel auf dem zu verputzenden Untergrund gebildete Beschichtungsfilm blasenfrei ist.In a further embodiment of the invention It is provided that the composition is a Ent contains foaming additive. The defoamer has the task of foaming when mixing the agent with to suppress the mixing water. In addition, it should be enough that the of the chosen agent on the plastering coating film formed without bubbles is.
In dieser Hinsicht zweckmäßige Ausführungsformen des erfindungsgemäßen Mittels zeichnen sich dadurch aus, daß das als Entschäumer dienende Zusatzmittel mindestens einen der folgenden Bestandteile enthält: eine Mischung eines alkoxi lierten Fettalkohols mit einem Fettsäureester eines Poly etherols, eine Kombination von flüssigen Kohlenwasserstoffen, Polyglykol und einer Trägersubstanz, oder eine Kombination von flüssigen Kohlenwasserstoffen, Fettderivaten, Silikonen und einer Trägersubstanz.In this regard, appropriate embodiments of the Agents according to the invention are characterized in that the at least one of the additives used as defoamers contains the following ingredients: a mixture of an alkoxi gated fatty alcohol with a fatty acid ester of a poly etherols, a combination of liquid hydrocarbons, Polyglycol and a carrier, or a combination of liquid hydrocarbons, fat derivatives, silicones and a carrier.
Ein weiterer Gedanke der Erfindung liegt darin, bei dem erfindungsgemäßen Mittel eine nach dem Anmachen des Trockenpulvers mit Wasser einen alkalischen PH-Wert ergebende Einstellung der Zusammensetzung vorzusehen. Aus anwendungs technischer Sicht ist dies aus folgenden Gründen sinnvoll: Der Celluloseether verdickt sehr viel besser. Ferner ist die Ver träglichkeit zwischen der die Putzgrundierung bildenden Auf brennsperre und dem darunterliegenden Putzgrund einerseits sowie auch dem darüber aufzubringenden Putz andererseits sehr viel besser.Another idea of the invention is that agents according to the invention after switching on the Dry powder with water giving an alkaline pH Provision of composition should be provided. From application From a technical point of view, this makes sense for the following reasons: The Cellulose ether thickens much better. Furthermore, the Ver inertness between the plaster primer fire barrier and the underlying plaster base on the one hand as well as the plaster to be applied on the other hand much better.
In zweckmäßigen Ausführungsformen der Erfindung kann der gewünschte hohe PH-Wert dadurch erreicht werden, daß die Zu sammensetzung mindestens einen der folgenden Bestandteile ent hält: Kalkhydrat, Zement, Wasserglas. Darüber hinaus sind auch andere pulverförmige Stoffe denkbar, die nach dem Anmachen mit dem Wasserhydroxid Ionen freisetzen.In expedient embodiments of the invention, the Desired high pH value can be achieved in that the Zu composition contains at least one of the following ingredients holds: hydrated lime, cement, water glass. Beyond that too other powdery substances conceivable, which after having been turned on Release ions from the water hydroxide.
Die Erfindung erstreckt sich auch auf den Gedanken, das erfindungsgemäße Mittel derart zusammenzustellen, daß die Zu sammensetzung einen als wasserlösliche Trägersubstanz dienenden Zuschlagstoff enthält. Dadurch ist eine optimale Verteilung des Bindemittels und der Zusatzstoffe erreicht, was ein ver bessertes Auflösen in Wasser bewirkt.The invention also extends to the idea that to assemble funds according to the invention such that the zu composition serving as a water-soluble carrier substance Contains aggregate. This ensures an optimal distribution of the Binder and additives achieved what a ver better dissolution in water.
Als Trägersubstanz kommen vorzugsweise folgende Stoffe allein oder als Bestandteile der Trägersubstanz in Betracht: Magnesiumsulfat, Natriumgluconat, Natriumsalicylat oder Natrium bicarbonat.The following substances are preferably used as the carrier substance alone or as components of the carrier into consideration: Magnesium sulfate, sodium gluconate, sodium salicylate or sodium bicarbonate.
In etwa sind bevorzugt die Gehalte der einzelnen Be
standteile in der Zusammensetzung des erfindungsgemäßen Mittels
derart bemessen, daß die Zusammensetzung bezogen auf ihre
gebrauchsfertige Anmischung mit Wasser, folgende Gehalte auf
weist:
0,3 bis 1,0 Gew.-% Bindemittel
0,5 bis 1,0 Gew.-% Zusatzmittel
0 bis 9 Gew.-% Zuschlagstoff
89 bis 99 Gew.-% Wasser.The contents of the individual constituents in the composition of the agent according to the invention are preferably measured in such a way that the composition, based on its ready-to-use mixture with water, has the following contents:
0.3 to 1.0 wt .-% binder
0.5 to 1.0% by weight of additives
0 to 9 wt% aggregate
89 to 99% by weight of water.
Nachstehend sind zwei Beispiele für die Zusammensetzung des erfindungsgemäßen Mittels angegeben, wobei das erste Aus führungsbeispiel eine dispersionspulverfreie Aufbrennsperre und das zweite Ausführungsbeispiel eine ein Dispersionspulver ent haltende Aufbrennsperre darstellt.Below are two examples of the composition of the agent according to the invention, the first off example of a powder-free barrier and the second embodiment ent a dispersion powder ent holding fire barrier.
Celluloseether 10,0 Gew.-%
Entschäumer 0,5 Gew.-%
Calciumhydroxid 2,5 Gew.-%
Natriumbicarbonat 87,0 Gew.-%.
Cellulose ether 10.0% by weight
Defoamer 0.5% by weight
Calcium hydroxide 2.5% by weight
Sodium bicarbonate 87.0% by weight.
Celluloseether 8,0 Gew.-%
Entschäumer 0,5 Gew.-%
Dispersionspulver 2,5 Gew.-%
Calciumhydroxid 2,5 Gew.-%
Natriumbicarbonat 86,5 Gew.-%.Cellulose ether 8.0% by weight
Defoamer 0.5% by weight
Dispersion powder 2.5% by weight
Calcium hydroxide 2.5% by weight
Sodium bicarbonate 86.5% by weight.
Claims (12)
0,3 bis 1,0 Gew.-% Bindemittel
0,5 bis 1,0 Gew.-% Zusatzmittel
0 bis 9 Gew.-% Zuschlagstoff
89 bis 99 Gew.-% Wasser.12. Composition according to claim 10 or 11, characterized in that the composition has the following contents, based on its ready-to-use mixture with water:
0.3 to 1.0 wt .-% binder
0.5 to 1.0% by weight of additives
0 to 9 wt% aggregate
89 to 99% by weight of water.