DE3227000A1 - Process for the production of a storage-stable product, in particular a product capable of being disposed of in landfill, from filter sludges, sinter sludges or oil separator sludges having iron oxide residues and oil residues contained in the dry matter - Google Patents
Process for the production of a storage-stable product, in particular a product capable of being disposed of in landfill, from filter sludges, sinter sludges or oil separator sludges having iron oxide residues and oil residues contained in the dry matterInfo
- Publication number
- DE3227000A1 DE3227000A1 DE19823227000 DE3227000A DE3227000A1 DE 3227000 A1 DE3227000 A1 DE 3227000A1 DE 19823227000 DE19823227000 DE 19823227000 DE 3227000 A DE3227000 A DE 3227000A DE 3227000 A1 DE3227000 A1 DE 3227000A1
- Authority
- DE
- Germany
- Prior art keywords
- sludges
- sludge
- oil
- filter
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Die Erfindung betrifft ein Verfahren zur HerstellungThe invention relates to a method of manufacture
eines lagerfähigen, insbesondere eines deponiefähigen Erzeugnisses aus Filter-, Sinter-- oder Ölabscheiderschlämmen mit in der Trockenmasse enthaltenen Eisenoxyd- und Ölrückständen gemäß dem Oberbegriff des Anspruches 1.a storable, especially a landfill product from filter, sinter or oil separator sludge with contained in the dry matter Iron oxide and oil residues according to the preamble of claim 1.
Grundlage des erfindungsgemäßen Verfahrens sind Schlämme der eisenverarbeitenden Industrie, insbesondere von Walzwerken. Diese Schlämme fallen entweder bei der Abwasserklärung als Filterrückstand an, der dann einen Wassergehalt von z.B. ca. 20 ffi besitzt. Sinterschlämme liegen in ähnliche Konsistenz vor und haben mit den Filterschlämmen einen relativ großen Anteil an Eisenoxyd, hauptsächlich als sogenannte Hammerschlag gemeinsam, dessen Anteil die Größenordnung von 70-75 % erreichen kann. Diese Schlämme enthalten Öl in Anteilen von z.B. 3 - 7 . Dieser Anteil ist bei Ölabscheiderschlämmen unter Umständen noch höher, deren Trockenmasse mit z.B. 30 - 34 °,S, jedoch im allgemeinen geringer als der Antei der Trockenmasse bei den Filterschlämmen ausfällt, wo er z.B bei 71 % liegen kann. Insbesondere in Walzwerken üblicher Größenordnung fallen sehr erhebliche Mengen solcher Schlämme an, die laufend entfernt werden müssen.The method according to the invention is based on iron-processing sludges Industry, especially of rolling mills. These sludges either fall during wastewater treatment as filter residue, which then has a water content of e.g. approx. 20 ffi. Sintered sludge is of a similar consistency and has a similar consistency with the filter sludge a relatively large proportion of iron oxide, mainly as a so-called hammer blow common, the proportion of which can reach the order of 70-75%. This sludge contain oil in proportions of e.g. 3 - 7. This proportion is in the case of oil separator sludge possibly even higher, their dry matter with e.g. 30 - 34 °, S, but in general less than the proportion of dry matter in the filter sludge where it is e.g. 71%. In particular, fall in rolling mills of the usual size very significant amounts of such sludge that have to be continuously removed.
Im allgemeinen geht man davon aus, daß die bezeichneten Schlämme entsorgt, d.h. vor allem auf geordneten Deponien abgelagert werden müssen. Abgesehen davon, daß sich Schlämme dieser Art wegen ihrer Konsistenz dafür nicht ohne weiteres eignen, stellt ihr Ölanteil das Haupthindernis dar. Dieser findet sich nämlich in dem sogenannten Eluat der Deponie wieder und stellt eine potentielle Gefahr für die Umgebung dar. Deswegen lassen sich diese Schlämme auf geordneten Deponien bislang nicht ablagern.It is generally assumed that the designated sludge is disposed of, i.e. they have to be deposited primarily in orderly landfills. Apart from this, that sludges of this type are not easily suitable for this because of their consistency, their oil content is the main obstacle. This is found in the so-called Eluate from the landfill again and poses a potential danger to the environment. This is why it has so far not been possible to deposit this sludge in controlled landfills.
Die Erfindung hat sich die Aufgabe gestellt, die bezeichneten Filter-, Sinter- oder Ölabscheiderschlämme in ein lagerfähiges, d.h. in ein Erzeugnis umzuwandeln, daß beim Eluieren mit T?(asser keine meßbaren Ölrückstande im Eluat aufweist und daß deswegen ohne Schwierigkeiten deponiert oder anderweitig weiterverarbeitet werden kann.The invention has set itself the task of the designated filter, To convert sinter or oil separator sludge into a storable, i.e. into a product, that when eluting with water does not show any measurable oil residues in the eluate and that therefore can be deposited or otherwise processed without difficulty can.
Die Erfindung löst diese Autgctbe mit den Merkmalen des Anspruches 1. Zweckmäßige Ausfahrungsformen der Erfindung sind in den Unteransprüchen enthalten.The invention solves this problem with the features of the claim 1. Expedient embodiments of the invention are contained in the subclaims.
Es hat sich überraschend herausgestellt, daß ein hydraulisches Bindemittel in verhältnismäßig geringer Menge, jedoch in ausreichender Feinheit, z.B. ein Zement bei Durchmischung mit den anfallenden Schlämmen aus diesen nicht nur eine Masse macht, die sich ausbreiten und trocknen läßt, sondern daß diese Masse, wenn sie aufgebrochen und auf einer Deponie, beispielsweise einer Müllkippe abgelagert ist, ein Eluat aufweist, das keine meßbaren Ölrückstände zeigt. Der Vorteil der Erfindung besteht demnach darin, daß nach dem erfindungsgemäßen Verfahren die erwähnten und umweltfeindlichen Stoffe in eine Masse umgewandelt werden können, die deponiefähig, allgemein gesehen also lagerfähig ist.It has surprisingly been found that a hydraulic binder in a relatively small amount, but in sufficient fineness, e.g. a cement when mixed with the resulting sludge from this not just one mass makes that can spread and dry, but that this mass, if it broken open and deposited in a landfill, for example a garbage dump, has an eluate which shows no measurable oil residues. The advantage of the invention is therefore that according to the method according to the invention, the mentioned and environmentally harmful substances can be converted into a mass that can be landfilled, Generally speaking, it can therefore be stored.
Die Wirtschaftlichkeit des erfindungsgemäßen Verfahrens hängt natürlich von dem Anteil des dabei verwendeten hydraulischen Bindemittels ab, welches den Rohschlämmen zugesetzt werden muß. Dieser Anteil läßt sich gemäß dem Merkmal des Anspruches 2 auf einen wirtschaftlich nennenswerten Teil durch Kalk absenken. Ein solcher Kalkzusatz unterstützt auch die Trocknung der Masse. Diese Trocknung läßt sich z.B. an der Luft ausführen, wenn man nach der Mischung die Schlämme auf Schlammbeeten ablagert, auf denen man nach der Trocknung die Masse z.B. mit Hilfe einer Planierraupe wieder aufbricht, um sie weiter zu verarbeiten. Diese Weiterverarbeitung kann überraschenderweise im Möller erfolgen, so daß das erfindungsgemäße Verfahren sich zum Recycling mindestens des Eisenanteiles der Schlämme eignet, das in den bezeichneten Rückständen in sehr erheblichem Umfang enthalten ist. Außerdem werden durch den Zusatz zum Möller die geordneten Deponien entlastet, die bekanntlich mit achsenden Kosten belastet sind.The economics of the process according to the invention depends of course on the proportion of the hydraulic binder used, which the Must be added to raw sludge. This proportion can be determined according to the feature of the Claim 2 to lower an economically significant part by lime. A such addition of lime also supports the drying of the mass. This drying leaves can be carried out in the air, for example, if the sludge is placed on mud beds after mixing deposited on which after drying the mass e.g. with the help a bulldozer breaks up again in order to process them further. This further processing can surprisingly take place in the Möller, so that the inventive method is suitable for recycling at least the iron content of the sludge that is in the designated residues is contained to a very considerable extent. Also be through the addition of the Möller, the orderly landfills, which are known to be relieved Axial costs are charged.
Es hat sich ferner überraschend herausgestellt, daß die erfindungsgemäß aus den Schlämmen hergestellte Masse erhebliche Mengen an sogenanntem Säureharz aufnehmen kann. Dabei handelt es sich um ein schwarzes Produkt von teerartiger Konsistenz, welches aus polymolekularen Stoffen, Sulfonaten, Schweielsäureestern und Schwefelsäure besteht und bei der Aufbereitung von Altöl mit Schwefel säure anfällt. Offenbar reagiert dieses Säureharz mit dem hydraulischen Bindemittel zu Kalziumsulfat, das zwar grundsätzlich bei der Eisengewinnung unerwünscht ist, dessen Mengen im Möller aber andererseits nicht störend wirken.It has also been found, surprisingly, that the invention Mass produced from the sludge contains considerable amounts of so-called acid resin can accommodate. This is a black product with a tarry consistency, which consists of polymolecular substances, sulfonates, sulfuric acid esters and sulfuric acid exists and is obtained from the processing of waste oil with sulfuric acid. Apparently this acid resin reacts with the hydraulic binder to form calcium sulfate, the Although it is generally undesirable in iron production, its quantities in the Möller but on the other hand not disturbing.
Zum Stand der Technik gehört zwar schon ein Verfahren zur Entsorgung von Säureteer und Säureharz, also von Abfallstoffen der beschriebenen Zusammensetzung und Konsistenz bei dem man diese Stoffe mit ci#enqrz vermischt, das bei der Reinigung von Koksofengasen von Schwefelwasserstoff eine erhebliche Rolle spielt (P 31 39 407.8). Es handelt sich hierbei jedoch ebenso wie bei den sogenannten Luxmassen, d.h. eisenhaltigen Abfällen der Aluminiumindustrie um ein nicht ohne weiteres, sondern häufig eigens zu beschaffendes Material, demgegenüber das erfindungsgemäße Verfahren den Vorteil hat, daß es aus zwei nicht ohne weiteres deponiefähigen Stoffen ein lagerfähiges Erzeugnis schafft.The prior art already includes a method for disposing of acid tar and acid resin, that is, of waste materials of the composition and consistency described, in which these materials are also used mixed ci # enqrz, which plays a significant role in the purification of coke oven gases from hydrogen sulfide (P 31 39 407.8). However, like the so-called lux masses, ie iron-containing waste from the aluminum industry, this is a material that is not readily available, but often specially procured, in contrast to which the method according to the invention has the advantage that it is a storable product made from two materials that cannot be easily dumped creates.
Aus den erfindungsgemäß hergestellten Massen lassen sich jedoch aufgrund des hohen Eisengehaltes der Schlämme Körper erheblicher Festigkeit herstellen, die als Baustoffe und z.B. auch als Ziegel, z.B. für feuerfeste Auskleidungen benutzt werden können. Es ist dann zweckmäßig, gemäß einem weiteren Merkmal der Erfindung entsprechende Mengen an Klärschlämmen zuzusetzen. Diese entstehen bei der Abwasseraufbereitung, und ihre Deponie stößt wegen der schädlichen Inhaltsstoffe, z.B. von Cadmium auf wachsenden Widerstand. Im Rahmen des erfindungsgemäßen Verfahrens macht man vor allem von den in diesen Klärschlämmen enthaltenen faserartigen Bestandteilen, der von Haaren, Häuten oder dergleichen geliefert wird Gebrauch, wodurch die erfindungsgemäß gewonnenen Massen einen verbesserten Zusammenhalt gewinnen und deswegen insbesondere für die bezeichneten Zwecke verwendbar sind.From the masses produced according to the invention, however, can be due to the high iron content of the sludge bodies produce considerable strength, which used as building materials and e.g. also as bricks, e.g. for refractory linings can be. It is then expedient according to a further feature of the invention add appropriate amounts of sewage sludge. These arise during wastewater treatment, and their landfill opens up because of the harmful ingredients, e.g. of cadmium growing resistance. In the context of the method according to the invention, one demonstrates all of the fibrous components contained in these sewage sludge, the of hair, skins or the like is supplied use, whereby the invention gained masses gain an improved cohesion and therefore in particular can be used for the specified purposes.
Es gehört zwar bereits ein Verfahren zur Entsorgung von Klärschlämmen zum nichtvorveröffentlichten Stand der Technik (P 32 02 081.3), bei dem man diese Klärschlämme mit den oben erläuterten Säureharzen und hydraulischen Bindemitteln versetzt und der Mischung auch gegebenenfalls Metalloxyde zusetzt, um den Mischungsprozeß zu beschleunigen und zu begünstigen, sowie die Neutralisation jeder einzelnen Charge zu fördern. Dieses ältere Verfahren zielt jedoch darauf ab, Klärschlämme und Säureharz zu entsorgen und dient nicht der Entsorgung der erfindungsgemäß umgewandelten Filter-, Sinter- oder Ölabscheiderschlämme.There is already a procedure for the disposal of sewage sludge to the prior art not previously published (P 32 02 081.3), in which this Sewage sludge with the acid resins and hydraulic binders explained above added and the mixture also optionally adding metal oxides to the mixing process to accelerate and promote, as well as the neutralization of each individual batch to promote. This older process, however, aims at sewage sludge and acid resin to be disposed of and does not serve to dispose of the filter, Sinter or oil separator sludge.
Im folgenden wird die Erfindung anhand mehrerer praktischer Beispiele näher erläutert: Beispiel 1 Ein Filterschlamm eines Walzwerkes wurde zu folgender Mischung verarbeitet: Filterschlamm 83,0 /Q Hochofenzement 8,:; ,' Kalkhydrat 1,7 % Flugasche 4,1 % Säureharz 2,9 °%O 100,0 % Die Komponenten der Mischung wurden mehrere Minuten intensiv vermischt. Die entstehende Masse wurde ausgebreitet und an der Luft getrocknet. Sie ließ sich später mit einer Planierraupe aufbrechen.In the following the invention is illustrated by means of several practical examples explained in more detail: Example 1 A filter sludge from a rolling mill became the following Mixture processed: filter sludge 83.0 / Q blast furnace cement 8,:; , 'Hydrated lime 1.7 % Fly ash 4.1% Acid resin 2.9 °% O 100.0% The components of the mixture were mixed intensively for several minutes. The resulting mass was spread out and air dried. It was later broken open with a bulldozer.
Beispiel 2 Aus einem Filterschlamm der vorgenannten Art wurde folgende Masse angemischt: Filterschlamm 83,1 Vo Kalk 5,6 %0 Säureharz 11,3 % 100.0 % Die entstehende Masse bilddse einen festen Körper, nachdem sie an der Luft getrocknet worden war. Teile der aufgebrochenen Masse wurden ausgewaschen. Dabei ergaben sich Auswaschungen von weniger als 6 mg/l.Example 2 A filter sludge of the aforementioned type became the following Mixed mass: filter sludge 83.1% lime 5.6% 0 acid resin 11.3% 100.0% die the resulting mass forms a solid body after it has air dried had been. Parts of the broken-up mass were washed out. It resulted Washouts of less than 6 mg / l.
Beispiel 3 Aus einem Filterschlamm der bezeichneten Art wurde folgende Mischung hergestellt: Filterschlamm 94,4 % Kalkhydrat 2,8 9'o Säureharz 100,0 a',# Auch diese Masse konnte nach intensiver Mischung und Ausbreitung an der Luft getrocknet und nachfolgend aufgebrochen werden.Example 3 A filter sludge of the type indicated became the following Mixture made: filter sludge 94.4% hydrated lime 2.8 9'o acid resin 100.0 a ', # This mass could also be dried in the air after intensive mixing and spreading and subsequently broken up.
Beispiel 4 Aus einem Sinterschlamm eines Walzwerkes wurde folgende Mischung hergestellt: Filterschlamm 72,6 % Hochofenzement 21,7 % Kalkhydrat 1,4 % Plugasche 4,5 100,0 % Die so entstandene Masse ließ sich an der Luft trocknen und nachfolgend aufbrechen. Flugasche bedeutet in diesem Beispiel der Rückstand der Elektrofilter der Rauchgasentstaubung eines Kraftwerkes. Offenbar entwickelt die Flugasche puzzozanähnliche Eigenschaften und befördert daher ihrerseits die Bildung einer lufttrockenen Masse.Example 4 The following was obtained from a sintering sludge from a rolling mill Mixture made: filter sludge 72.6% blast furnace cement 21.7% hydrated lime 1.4 % Plug ash 4.5 100.0% The resulting mass could be air-dried and then break open. In this example, fly ash means the residue the electrostatic precipitator for the flue gas dedusting of a power plant. Apparently developed the fly ash has properties similar to pozzozan and therefore promotes the Formation of an air-dry mass.
Beispiel 5 Der Rückstand aus einem Ölabscheider eines Walzwerkes hatte einen Anteil an Trockenmasse von 30 bis 34 %.Example 5 The residue from an oil separator of a rolling mill had a proportion of dry matter of 30 to 34%.
Diese Trockenmasse bestand zu 48,6 % aus Öl, Xestfeststoffe, u.a Sand und Eisenoxyd.This dry matter consisted of 48.6% oil, Xest solids, including sand and iron oxide.
Hieraus wurde eine Mischung folgender Zusammensetzung hergestellt: Ölabscheiderschlsmm 60 bis 65 ffi Klärschlamm 20 bis 25 5'o hydraulisches Bindemittel 9 bis 10 # Kalkhydrat 0 bis 8 % Säureharz 4 bis 7 %.From this a mixture of the following composition was made: Oil separator sludge 60 to 65 ffi sewage sludge 20 to 25 5'o hydraulic binder 9 to 10 # hydrated lime 0 to 8% acid resin 4 to 7%.
Der eingesetzte Klärschlamm hatte eine Trockenmasse von 26,6 #.The sewage sludge used had a dry matter of 26.6 #.
Aus der Mischung wurden Körper geformt, die eine relativ hohe Druckfestigkeit nach 28 Tagen erreichte und einen guten Zusammenhalt zeigten.The mixture was used to form bodies with a relatively high compressive strength reached after 28 days and showed good cohesion.
Die Mischung kann in einem Kollergang vorgenommen werden.Mixing can be done in a pan mill.
Für das Aufbrechen der Masse eignen sich insbesondere Planierraupen, wenn die Masse ausgebreitet ist.Bulldozers are particularly suitable for breaking up the mass, when the mass is spread out.
Die Angaben verstehen sich als Gewichtsprozent.The information is given as percent by weight.
Claims (4)