DE2335549C3 - Method of manufacturing a cosmetic stick - Google Patents
Method of manufacturing a cosmetic stickInfo
- Publication number
- DE2335549C3 DE2335549C3 DE19732335549 DE2335549A DE2335549C3 DE 2335549 C3 DE2335549 C3 DE 2335549C3 DE 19732335549 DE19732335549 DE 19732335549 DE 2335549 A DE2335549 A DE 2335549A DE 2335549 C3 DE2335549 C3 DE 2335549C3
- Authority
- DE
- Germany
- Prior art keywords
- water
- cosmetic
- weight
- gel
- lipstick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung betrifft ein Verfahren zur Herstellung eines kosmetischen Stiftes auf Basis einer Wasser-in-Öl-Emulsion, bei dem man 1 bis 50 Gew.-% Wasser, I bis 10 Gew.-% mindestens einer Polyhydroxyverbindung, I bis 5 Gew.-% mindestens einer nichtionogenen, oberflächenaktiven Verbindung und mindestens 20 Gew.-% einer kosmetischen Grundlage sowie gegebencnfalls übliche Farbmittel miteinander vermischt und die Mischung verf'ormt.The invention relates to a method of manufacture a cosmetic stick based on a water-in-oil emulsion, in which 1 to 50 wt .-% water, I to 10% by weight of at least one polyhydroxy compound, I to 5% by weight of at least one nonionic, surface-active compound and at least 20% by weight of a cosmetic base and optionally Usual colorants mixed together and the mixture deformed.
Die üblichen bekannten kosmetischen Stifte, z. B. Lippenstifte, Lippenpomadestifte und Grundierungsstifte, enthalten bekanntlich als Hauptkomponente eine öllösliche Komponente, z. B. ein oder mehrere vegetabilische, tierische oder mineralische Öle, Fette und Wachse und/oder höhere Carbonsäureester sowie geringere Mengen einer färbenden Komponente, und zwar eines Farbstoffes und/oder eines Pigmentes, einen DuftstolT und/oder ein Antioxidationsmittel. Aus der DT-AS 12 46 168 ist es ferner bekannt, als Grundlage für pharmazeutische und kosmetische Stiftmassen Mischungen aus Polyglykolestem von Fettsäuren mit 12 bis 22 Kohlenstoffatomen und Polyglykolestem von Wachssäuren zu verwenden. Die Herstellung von Stiften aus diesen Mischungen erfolgt durch Aufschmelzen der Mischungen, Zusatz von üblichen Zusatzstoffen, insbesondere sauer reagierenden Wirkstoffen und Duftstoffen sowie Vergießen der erhaltenen Massen.The usual known cosmetic sticks, e.g. B. Lipsticks, lip balm sticks and primer pencils, are known to contain an oil-soluble component as the main component, e.g. B. one or more vegetable, animal or mineral oils, fats and waxes and / or higher carboxylic acid esters as well as lower ones Amounts of a coloring component, namely a dye and / or a pigment, one Fragrance stole and / or an antioxidant. From the DT-AS 12 46 168 it is also known as a basis for pharmaceutical and cosmetic stick compounds Mixtures of polyglycol esters of fatty acids having 12 to 22 carbon atoms and polyglycol esters of To use wax acids. The production of sticks from these mixtures is done by melting the mixtures, addition of customary additives, in particular active ingredients with an acidic reaction and fragrances and potting of the obtained masses.
Nachteilig an den üblichen bekannten Stift-Grundlagen ist, daß sie mehr oder weniger stark hydrophob sind, weshalb es schwierig ist, sie mit Wasser zu vermischen. Andererseits sind jedoch Stifte erwünscht, die Wasser enthalten, um die Verträglichkeit der Stifte mit der menschlichen Haut zu verbessern.The disadvantage of the conventionally known pencil bases is that they are more or less strongly hydrophobic which is why it is difficult to mix them with water. On the other hand, however, pens are desirable, which contain water to improve the compatibility of the pencils with human skin.
Aus der US-PS 35 36 816 sind in jüngsterZcit Wasserin-ÖI-Emulsionen für die Herstellung kosmetischer Lotions und Cremes bekanntgeworden. Hs hat sich 6s jedoch gezeigt, daß die üblichen Wasser-in-Öl-Emulsionen vielerlei Nachteile haben, wenn der Versuch unternommen wird, sie zur Herstellung kosmetischer Stifte zu verwenden. Diese Nachteile bestehen beispielsweise darin, daß leicht eine Verfärbung durch nicht gleichförmiges Vermischen der farbbildenden Komponenten erfolgt, daß die Stifte leicht weich werden, daß sie leicht zerbrechen, daß die öligen Komponenten ausgeschieden werden und daß die Verformung der zur Herstellung der Stifte verwendeten Formmassen schwierig ist Aufgrund dieser Nachteile sind bisher noch keine kosmetischen Stifte auf der Grundlage von Wasser-in-Öl-Emulsionen bekanntgeworden. From US-PS 35 36 816 are most recently water-in-oil emulsions became known for the production of cosmetic lotions and creams. Hs has 6s however, the conventional water-in-oil emulsions have been shown to have many disadvantages when attempted is being undertaken to use them in the manufacture of cosmetic pencils. These disadvantages exist, for example in that discoloration is easy due to non-uniform mixing of the color-forming ones Components happens that the sticks are easily soft, that they break easily, that the oily Components are excreted and that the deformation of the pins used to manufacture Molding compounds is difficult. Because of these disadvantages, there are still no cosmetic sticks on the The basis of water-in-oil emulsions has become known.
Es ist ferner allgemein bekannt, z. B. aus E. Sa"ga ri n, »Cosmetics, Science and Technology«, Verlag Iiiterscience Publishers, Inc. New York, 1957, Seite 164, zur Herstellung von kosmetischen Präparaten als Feuchthaltemittel höhere Alkohole wie Mannit, Sorbit und Glukose zu verwenden.It is also well known, e.g. B. from E. Sa "ga ri n, "Cosmetics, Science and Technology", Verlag Iiiterscience Publishers, Inc. New York, 1957, page 164, for the manufacture of cosmetic preparations as Humectants use higher alcohols like mannitol, sorbitol, and glucose.
Aufgabe der Erfindung war es, ein Verfahren zur Herstellung eines kosmetischen Stiftes auf Basis einer Wasser-in-Öl-Emulsion anzugeben, der gegenüber vergleichbaren bekannten Stiften verbesserte Feuchthalte- und Ausbreiteigenschaften sowie glänzendmachende Eigenschaften aufweist und sich durch eine hervorragende Stabilität auszeichnetThe object of the invention was to provide a method for producing a cosmetic stick based on a Water-in-oil emulsion to indicate the opposite of comparable known pens improved moisturizing and spreading properties as well as glossing Has properties and is characterized by excellent stability
Der Erfindung lag die Erkenntnis zugrunde, daß man zu kosmetischen Stiften der geschilderten Eigenschaften dann gelangt, wenn man aus bestimmten Ausgangsverbindungen ein Gel herstellt und dieses mit der kosmetischen Grundlage vermischtThe invention was based on the knowledge that cosmetic sticks with the properties described can be obtained then comes when a gel is made from certain starting compounds and this mixed with the cosmetic base
Gegenstand der Erfindung ist somit ein Verfahren zur Herstellung eines kosmetischen Stiftes auf Basis einer Wasser-in-Öl-Emulsion, bei dem man 1 bis 50 Gew.-% Wasser, 1 bis 10 Gew.-% mindestens einer Polyhydroxyverbindung, 1 bis 5 Gew.-% mindestens einer nichtionogenen, oberflächenaktiven Verbindung und mindestens 20 Gew.-% einer kosmetischen Grundlage sowie gegebenenfalls übliche Farbmittel miteinander vermischt und die Mischung verformt, und das dadurch gekennzeichnet ist, daß man zunächst durch Vermischen mindestens einer aus Glyzerin, Mannitol, Dulcitol und/oder einem Kohlehydrat bestehende Polyhydroxyverbindung und mindestens einer aus einem Ölsäureester oder Oleyläther eines mehrwertigen Alkohols bestehenden nichtionogenen, oberflächenaktiven Verbindung ein Gel herstellt, das Gel mit der kosmetischen Grundlage vermischt und danach mit Hilfe des Gels das Wasser in der Mischung emulgiert.The invention thus relates to a method for producing a cosmetic stick based on a water-in-oil emulsion, in which 1 to 50% by weight of water, 1 to 10% by weight of at least one Polyhydroxy compound, 1 to 5% by weight of at least one nonionic, surface-active compound and at least 20% by weight of a cosmetic base and optionally customary colorants with one another mixed and deformed the mixture, and which is characterized in that one first by mixing at least one of glycerin, mannitol, dulcitol and / or a carbohydrate existing polyhydroxy compound and at least one of an oleic acid ester or oleyl ether a nonionic, surface-active compound consisting of a polyhydric alcohol is a gel produces, the gel mixed with the cosmetic base and then with the help of the gel the water emulsified in the mixture.
Zur Herstellung eines kosmetischen Stiftes werden somit ein Gel mit 1 bis 10, vorzugsweise 5 bis 7 Gew.-"/,, mindestens einer Polyhydroxyverbindung aus Glyzerin, Mannitol, Dulcitol und/oder einem Kohlehydrat sowie 1 bis 5, vorzugsweise 2 bis 3 Gew.-% mindestens einer nichtionogenen, oberflächenaktiven Verbindung verwendet.To produce a cosmetic stick, a gel with 1 to 10, preferably 5 to 7 wt .- "/" at least one polyhydroxy compound made from glycerine, mannitol, dulcitol and / or a Carbohydrate and 1 to 5, preferably 2 to 3 wt .-% of at least one nonionic, surface-active Connection used.
Ein nach dem Verfahren der Erfindung hergestellter kosmetischer Stift ist demzufolge aufgebaut aus einer Wasser-in-Öl-Emulsion mit 1 bis 50Gew.-% Wasser, einem Gel mit einem Gehalt an 1 bis 10 Gew.-% mindestens einer Polyhydroxyverbindung, bestehend aus Glyzerin, Mannitol, Dulcitol oder einem Kohlehydrat und 1 bis 5 Gew.-% mindestens einer nichtionogenen, oberflächenaktiven Verbindung, bestehend aus einem Ölsäureester eines mehrwertigen Alkohols oder einem Oleyläther eines mehrwertigen Alkohols sowie mindestens 20Gcw.-% mindestens einer kosmetischen Grundlage.A cosmetic stick produced according to the method of the invention is accordingly composed of a Water-in-oil emulsion with 1 to 50% by weight of water, a gel with a content of 1 to 10% by weight at least one polyhydroxy compound consisting of glycerine, mannitol, dulcitol or a carbohydrate and 1 to 5% by weight of at least one nonionic, surface-active compound from an oleic acid ester of a polyhydric alcohol or an oleyl ether of a polyhydric alcohol and at least 20% by weight of at least one cosmetic Basis.
Als Kohlehydrate können z. B. D-Lävulosc, Maltose,As carbohydrates, for. B. D-Lävulosc, maltose,
Sucrose, Lactose, Raffinose, Stärke, Pentosen, ζ. Β. D-Ribose, D-Xylose und L-Arabinose sowie Hexosen, z. B. D-GIucose, D-Mannose und D-Galactose verwendet werden. Diese Kohlehydrate können in Wasser gelöst und mit nichtionogenen, oberflächenaktiven Verbindung gelatinisiert werden.Sucrose, lactose, raffinose, starch, pentoses, ζ. Β. D-ribose, D-xylose and L-arabinose and hexoses, e.g. B. D-glucose, D-mannose and D-galactose are used will. These carbohydrates can be dissolved in water and mixed with nonionic, surface-active substances Compound are gelatinized.
Die beschriebenen Polyhydroxyverbindungen stellen wichtige Bestandteile der kosmetischen Stifte dar. Wird zur Herstellung des kosmetischen Stiftes anstelle der angegebenen Polyhydroxyverbindungen Sorbitol verwendet, so läßt sich keine gleichförmige Verteilung eines zur Einfärbung verwendeten Pigmentes erreichen, und die Haltbarkeit des Stiftes ist gering.The polyhydroxy compounds described are important components of cosmetic sticks. Will for the production of the cosmetic stick used instead of the specified polyhydroxy compounds sorbitol, so no uniform distribution of a pigment used for coloring can be achieved, and the durability of the pen is poor.
Vorzugsweise werden zur Herstellung der kosmetischen Stifte 2 bis 3 Gew.-% einer nichtionogenen, oberflächenaktiven Verbindung verwendetPreferably, 2 to 3% by weight of a nonionic, surface active compound used
Die zur Herstellung der erfindungsgemäßen Stifte verwendeten oberflächenaktiven Verbindungen können aus Ölsäureestern mehrbasischer oder mehrwertiger Alkohole und Oleyläthern mehrbasischer oder mehrwertiger Alkohole bestehen. Typische Ölsäureester sind beispielsweise Glyzerinmonoolea^Glyzerindioleat, Sorbilolmonooleat, Sorbilolsesquioleat, Sorbitoltrioleat, Propylenglykolmonooleat, Propylenglykoldioleat, Äthylenglykolmonooleat, Äthylenglykoldioleat und Ölsäureester von Polyäthylenglykolen. Typische nichtionogene, oberflächenaktive Oleyläther sind beispielsweise Dioleyläther von Polyäthylenglykolen. The surface-active compounds used to produce the sticks according to the invention can from oleic acid esters of polybasic or polyhydric alcohols and oleyl ethers of polybasic or polyhydric alcohols exist. Typical oleic acid esters are, for example, glycerine monoolea ^ glycerine dioleate, Sorbilol monooleate, sorbilol sesquioleate, sorbitol trioleate, propylene glycol monooleate, propylene glycol dioleate, Ethylene glycol monooleate, ethylene glycol dioleate and oleic acid esters of polyethylene glycols. Typical nonionic, surface-active oleyl ethers are, for example, dioleyl ethers of polyethylene glycols.
Bei Durchführung des Verfahrens der Erfindung wird die oder werden die Polyhydroxyverbindungen mit der nichtionogenen, oberflächenaktiven Verbindung unter Bildung eines Gels vermischt, das für eine wirksame und stabile Emulgierung des Wassers in der kosmetischen Grundlage sorgt.In carrying out the method of the invention, the polyhydroxy compound or compounds will be used mixed with the nonionic surfactant compound to form a gel which is suitable for a ensures effective and stable emulsification of the water in the cosmetic base.
Die kosmetische Grundlage kann beispielsweise aus flüssigen Paraffinen, Squalan, Rizinusöl, Olivenöl, Avocadoöl, Camelliaöl, Baumwollsaatöl, Mandelöl, Kakaobutter, Sesamöl, Japanwachs, Bienenwachs, Lanolin, Carnaubawachs, Candelillawachs, Paraffinwachs, festem Paraffin, Vaseline, mikrokristallinem Wachs und höheren Fettsäureestern bestehen. Ein zur Herstellung eines kosmetischen Stiftes geeignetes Paraffin hat vorzugsweise eine Viskosität entsprechend 50 bis 365 Saybolt-Sekunden bei 37,8 C. Die höheren Kohlenwasserstoffe, z. B. flüssige Paraffine und Squalan können gegebenenfalls mit etwa 20% vegetabilischem Öl, z.B. Rizinusöl, Olivenöl, Camelliaöl und/ oder höheren Fettsäureestern, ζ. B. Butylstearat und Isopropylmyristat sowie Lanolin vermischt werden. Ein zur Durchführung des Verfahrens nach der Erfindung geeignetes festes Paraffin weist vorzugsweise einen Schmelzpunkt von etwa 60 bis 88 C auf und besteht aus Paraffin-Kohlenwasserstoffen mit 20 oder mehr Kohlenstoffatomen und einem Gehalt von 30 bis 80Gew.-% geradkettiger Kohlenwasserstoffe.The cosmetic base can, for example, consist of liquid paraffins, squalane, castor oil, olive oil, Avocado oil, camellia oil, cottonseed oil, almond oil, cocoa butter, sesame oil, Japan wax, beeswax, lanolin, Carnauba wax, candelilla wax, paraffin wax, solid paraffin, petroleum jelly, microcrystalline Wax and higher fatty acid esters are made. One suitable for making a cosmetic stick Paraffin preferably has a viscosity corresponding to 50 to 365 Saybolt seconds at 37.8 ° C. The higher Hydrocarbons, e.g. B. liquid paraffins and squalane can optionally with about 20% vegetable Oil, e.g. castor oil, olive oil, camellia oil and / or higher fatty acid esters, ζ. B. butyl stearate and Isopropyl myristate and lanolin are mixed together. One for carrying out the method according to the invention suitable solid paraffin preferably has a melting point of about 60 to 88 ° C and consists of paraffin hydrocarbons with 20 or more carbon atoms and a content of 30 up to 80% by weight of straight-chain hydrocarbons.
Der Gehalt eines nach dem Verfahren der Erfindung hergestellten Stiftes an kosmetischer Grundlage oder kosmetischer Grundsubstanz in der Wasscr-in-ÖI-Emulsion liegt bei mindestens 20Gew.-%. Liegt der Gehalt an kosmetischer Grundlage bei weniger als 20Gew.-%, so ist die erhaltene Wasser-in-ÖI-Emulsion instabil.The cosmetic base or the content of a stick made by the method of the invention cosmetic base substance in the water-in-oil emulsion is at least 20% by weight. Is the If the cosmetic base content is less than 20% by weight, this is the water-in-oil emulsion obtained unstable.
Zum Einfärben der kosmetischen Stifte können die üblichen bekannten organischen färbenden Komponenten verwendet werden sowie ferner übliche bekannte anorganische larbende Komponenten, z. B. Titandioxid, Zinkweiß, Talkum, Kaolin, Eisenoxide und Ruß.The customary known organic coloring components can be used to color the cosmetic sticks are used as well as customary known inorganic coloring components such. B. Titanium dioxide, zinc white, talc, kaolin, iron oxides and soot.
Des weiteren kann die Herstellung der kosmetischen Stifte unter Verwendung von einem oder mehreren üblichen Additiven erfolgen, z. B. unter Verwendung eines Duftstoffes, eines Antioxidationsmittels, einer ultraviolette Strahlung absorbierenden Verbindung und/oder eines Germizides.Furthermore, the cosmetic sticks can be manufactured using one or more usual additives take place, z. B. using a fragrance, an antioxidant, a ultraviolet radiation absorbing compound and / or a germicide.
Vorzugsweise wird zur Durchführung des Verfahrens der Erfindung ein mikrobiologisch gereinigtes, deionisiertes Wasser verwendetPreferably, a microbiologically cleaned, deionized one is used to carry out the method of the invention Water used
Im einzelnen läßt sich das Verfahren der Erfindung beispielsweise wie folgt durchführen:In detail, the method of the invention can be carried out, for example, as follows:
Eine wäßrige Lösung von 1 bis 10 Gew.-Teilen, vorzugsweise 5 bis 7 Gew.-Teilen einer oder mehrerer der angegebenen Polyhydroxyverbindungen wird mit 1 bis 5 Gew.-Teilen, vorzugsweise 2 bis 3 Gew.-Teilen eines oder mehrerer nichtkinogener, oberflächenaktiver Verbindungen unter Bildung eines Gels vermischt. Das Gel wird dann mil einer vorbestimmten Menge einer kosmetischen Grundlage bei einer Temperatur von 50 bis 6O0C unter Rühren vermischt Daraufhin wird in die zunächst hergestellte Grundlagen-Gelmischung unter Rühren Wasser eingemischt, wobei das Wasser gleichförmig in die kosmetische Grundlage einerpulgiert wird. Die der Grundlagen-Gelmischung zugesetzte Wassermenge liegt bei 1 bis 50, vorzugsweise 10 bis 20Gew.-%. Ein Zusatz von mehr als 50Gew.-% Wasser führt zu einer starken Verdunstung und zu einer zu geringen Festigkeit des herzustellenden kosmetischen Stiftes. Weniger als 1 Gew.-% Wasser reicht nicht aus, um Stifte der beschriebenen Eigenschaften herstellen zu können.An aqueous solution of 1 to 10 parts by weight, preferably 5 to 7 parts by weight, of one or more of the specified polyhydroxy compounds becomes more surface-active with 1 to 5 parts by weight, preferably 2 to 3 parts by weight, of one or more non-kinogenic Compounds mixed to form a gel. The gel is then mil of a predetermined amount of a cosmetic base at a temperature from 50 to 6O 0 C, with stirring, mixed then blended in the initially prepared foundations-gel mixture with stirring the water, the water being uniformly einerpulgiert in the cosmetic base. The amount of water added to the base gel mixture is 1 to 50, preferably 10 to 20% by weight. An addition of more than 50% by weight of water leads to strong evaporation and to insufficient strength of the cosmetic stick to be produced. Less than 1% by weight of water is insufficient to produce sticks with the properties described.
Des weiteren hat sich gezeigt, daß die Verwendung von weniger als 1 Gew.-% einer nichtionogenen, oberflächenaktiven Verbindung unzureichend ist, um ein homogenes Gel zu erhalten, wohingegen mehr als 5 Gew.-% nichtionogene Verbindung zu einer starken Reizung der menschlichen Haut führen können, ferner zu Verfärbungen der farbbildenden Komponenten und zur Ausbildung von zahlreichen kleinen Löchern im Stift. Wird die Polyhydroxyverbindung in einer Menge von weniger als 1 % verwendet, so wird eine nicht gleichförmige Emulgierung des Wassers bewirkt. Die Verwendung von mehr als 10 Gew.-% Polyhydroxyver-It has also been shown that the use of less than 1% by weight of a nonionic, surface-active Compound is insufficient to obtain a homogeneous gel, whereas more than 5 wt .-% nonionic compound can lead to severe irritation of the human skin, moreover to discoloration of the color-forming components and to the formation of numerous small holes in the Pen. If the polyhydroxy compound is used in an amount less than 1%, one will not be used causes uniform emulsification of the water. The use of more than 10 wt .-% polyhydroxy
45. bindung ist vom kommerziellen Standpunkt aus gesehen nachteilig. 45 . retention is disadvantageous from a commercial standpoint.
Bei der Herstellung der bekannten üblichen Kosmetika wird zur Einemulgierung des Wassers in das hydrophobe kosmetische Grundlagenmaterial oder die kosmetische Base eine relativ große Menge von oberflächenaktiver Verbindung verwendet. Es hat sich jedoch gezeigt, daß die Verwendung solch großer Mengen an oberflächenaktiver Verbindung die Eigenschaften der hergestellten kosmetischen Stifte stark nach-In the manufacture of the known, customary cosmetics, the water is emulsified into the hydrophobic cosmetic base material or the cosmetic base a relatively large amount of surface-active Connection used. However, it has been found that the use of such large amounts on the surface-active compound, the properties of the cosmetic sticks produced are greatly improved.
5<i teilig beeinflußt, und zwar deshalb, weil eine relativ starke Reizung der menschlichen Haut bewirkt wird, da derartige Stifte eine hohe Toxizilät aufweisen, weil eine Verfärbung der Farbkomponenten erfolgen kann, weil das hydrophile-lipophile Gleichgewicht schwierig5 <i partly influenced, namely because a relative severe irritation of the human skin is caused because such pens have a high toxicity because discoloration of the color components can occur because the hydrophilic-lipophilic balance is difficult
(,o zu steuern ist und weil des weiteren in dem kosmetischen Stift aufgrund von Bläschen, die bei der I lerstellung des kosmetischen Produktes gebildet werden, zahlreiche kleine Löcher auftreten können. Als besonders schwierig hat es sich erwiesen, eine ober- (, o is to be controlled and because, furthermore, numerous small holes can occur in the cosmetic stick due to bubbles which are formed during the production of the cosmetic product. It has proven to be particularly difficult to
h5 flüchenaktive Verbindung auszuwählen, welche ein geeignetes hydrophiles-lipophiles Gleichgewicht für eine Vereinigung mit dem Wasser und der kosmetischen Grundlage aufweist.h 5 surface-active compound, which has a suitable hydrophilic-lipophilic balance for a union with the water and the cosmetic base.
Beim Verfahren nach der Erfindung wird das Wasser gleichförmig durch Verwendung einer vergleichsweise geringen Menge, nämlich 1 bis 5 Gew.-% einer nichtionogenen, oberflächenaktiven Verbindung emulgiert. Dies ist möglich, weil die oberflächenaktive Verbindung zunächst mit der Polyhydroxyverbindung oder den Polyhydroxyverbindungen vermischt wird, die hoch hydrophil sind und mit der nichtionogenen Verbindung zu einem Gel verarbeitet werden. Das Gel bewirkt dann eine gleichförmige Emulgierung des Wassers in der hydrophilen kosmetischen Grundlage.In the method of the invention, the water becomes uniform by using a comparator small amount, namely 1 to 5 wt .-% of a nonionic, surface-active compound emulsified. This is possible because the surface-active compound initially interacts with the polyhydroxy compound or the polyhydroxy compounds which are highly hydrophilic and with the nonionic compound processed into a gel. The gel then causes a uniform emulsification of the Water in the hydrophilic cosmetic base.
Nach dem Verfahren der Erfindung herstellbare kosmetische Stifte zeichnen sich insbesondere durch folgende Vorteile aus:Cosmetic sticks which can be produced by the method of the invention are distinguished in particular by the following advantages:
1. Sie lassen sich leicht auf der menschlichen Haut verteilen.1. They can be easily spread on human skin.
2. Sie führen zu einer ausgezeichneten Befeuchtung der menschlichen Haut2. They lead to an excellent moisturizing of the human skin
3. Sie verleihen der menschlichen Haut einen schönen Glanz.3. They give the human skin a beautiful look Shine.
4. Aufgrund des geringen Gehaltes an oberflächenaktiver Verbindung erfolgt keine Reizung der menschlichen Haut.4. Due to the low content of surface-active compound, there is no irritation of the human skin.
5. Selbst bei langer Lagerung blühen die Zusätze nicht oder höchstens sehr wenig aus.5. Even when stored for a long time, the additives do not or at most very little bloom.
6. Die Hautstellen, auf denen ein Teil des Stiftes aufgetragen wurde, fühlen sich weich an.6. The skin on which part of the pen has been applied is soft to the touch.
7. Die Stifte weisen eine ausgezeichnete Festigkeil auf.7. The pens have an excellent fastener wedge on.
8. Die zur Herstellung der Stifte verwendeten Stoffe sind ausgezeichnet mit in Wasser löslichen, nicht toxischen färbenden Komponenten und anderen Additiven verträglich.8. The materials used to make the pencils are excellent with those that are not soluble in water toxic coloring components and other additives compatible.
Die folgenden Beispiele sollen die Erfindung näher veranschaulichen. Sämtliche Prozentangaben in den Beispielen beziehen sich auf Gewichtsteile und Gewichtsprozent. The following examples are intended to illustrate the invention in more detail. All percentages in the Examples relate to parts by weight and percent by weight.
(Herstellung eines Lippenstiftes)
(A) Kosmetische Grundlage (Ölteile) Gew.-Teile(Making a lipstick)
(A) Cosmetic base (oil parts) parts by weight
Flüssiges ParaffinLiquid paraffin
Festes ParaffinSolid paraffin
CandelillawachsCandelilla wax
TiO2 TiO 2
Roter FarbstoffRed dye
Butyl-p-hydroxybenzoatButyl p-hydroxybenzoate
52,84
15,0
5,0
5,70
1,30
0,0552.84
15.0
5.0
5.70
1.30
0.05
Die angegebenen Bestandteile wurden unter Rühren gleichförmig bei 80' C miteinander vermischt.The indicated ingredients were uniformly mixed with one another at 80 ° C. with stirring.
(B) Gel (Emulgiermittel) Gaw.-Teile (B) Gel (emulsifier) Gaw. Parts
Glyzerinmonooleat 3,0Glycerol monooleate 3.0
60%ige wäßrige Lösung von 2,060% aqueous solution of 2.0
D-LävuloseD-levulosis
(C) Wäßrige Komponente (C) Aqueous component
Deionisiertes Wasser 100Deionized water 100
Propylenglykol 5,0Propylene glycol 5.0
Roter Farbstoff 0,01Red dye 0.01
Die Komponenten wurden unter Rühren bei 35 C unter Bildung eines Gels miteinander vermischt. Daraufhin wurde das Gel (S) unter Rühren bei 70 C in die kosmetische Grundlage (A) eingemischt, worauf die Mischung (C) aus deionisiertem Wasser, Propylenglykol und Farbstoff unter Rühren in die erhaltene Mischung einemulgiert wurde. Die erhaltene Mischung wurde dann einer Vakuumbehandlung unterworfen, um in der Masse enthaltene Bläschen zu eliminieren, worauf die Masse in eine Lippenstiftform gegeben wurde. Auf diese Weise wurden rosafarbene Lippenstifte mit gutem Glanz erhalten.The components were mixed together with stirring at 35 ° C. to form a gel. The gel (S) was then mixed into the cosmetic base (A) with stirring at 70.degree. C., whereupon the mixture (C) of deionized water, propylene glycol and dye was emulsified into the mixture obtained with stirring. The obtained mixture was then subjected to a vacuum treatment to eliminate bubbles contained in the mass, and the mass was then placed in a lipstick mold. In this way, pink lipsticks with good gloss were obtained.
■ο Zu Vergleichszwecken wurde in entsprechender Weise ein Lippenstift hergestellt, zu dessen Herstellung jedoch anstelle von D-Lävulose Sorbitol verwendet wurde. Dieser Lippenstift zeichnete sich durch eine ungleichförmige Verteilung des TiO2 aus. Das heißt, das Titandioxid war in den äußeren Teilen des Lippenstiftes stärker verteilt als im Mittelteil des Lippenstiftes.■ ο For comparison purposes, a lipstick was produced in a similar manner, but instead of D-levulose sorbitol was used for its production. This lipstick was distinguished by a non-uniform distribution of the TiO 2 . That is, the titanium dioxide was more widely distributed in the outer parts of the lipstick than in the central part of the lipstick.
Der erfindungsgemäße Lippenstift wurde einem Stabilitätstest unterworfen, bei dem der Lippenstift in eine geschlossene Kammer gebracht wurde, in der die Temperatur in Intervalien von jeweils 72 Stunden von 0 auf 38 C und dann wiederum von 38 C auf 0 C verändert wurde. Nach einer Testdauer von 3 Monaten wurde keine Veränderung bei dem Lippenstift festgestellt. The lipstick according to the invention was subjected to a stability test in which the lipstick in a closed chamber was placed in which the temperature at intervals of 72 hours from 0 to 38 C and then again changed from 38 C to 0 C. would. After a test duration of 3 months, no change was found in the lipstick.
Zu Vergleichszwecken wurden zwei Lippenstifte des Standes der Technik (a) und (b) dem gleichen Stabilitätstesl unterworfen. Die zu Vergleichszwecken getesteten Lippenstifte (a) und (b) hatten die in der folgenden Tabelle angegebene Zusammensetzung.For comparison purposes, two lipsticks of the prior art (a) and (b) were subjected to the same stability test. The lipsticks (a) and (b) tested for comparison purposes had the composition given in the table below.
Lippenstift-BestandteileLipstick ingredients
(a) Ib)(a) Ib)
Gew.-Teile Gew.-TeileParts by weight Parts by weight
CandelillawachsCandelilla wax
BienenwachsBeeswax
Festes ParaffinSolid paraffin
Lanolinlanolin
IsopropylmyristatIsopropyl myristate
Rizinusölcastor oil
CamelliaölCamellia oil
EosinEosin
TiO2 TiO 2
Roter FarbstoffRed dye
Nach Durchführung des Stabilitätstestes über einen Zeitraum von einer Woche wurden auf der Oberfläche der Lippenstifte viele kleine Tröpfchen festgestellt Hieraus ergibt sich, daß sich nüssige Komponenten von den anderen Komponenten von der Lippenstiftmischung ausgeschieden hatten und ausblühten. Die beschriebenen Lippenstiftmassen wurde des weiteren Theologischen Messungen un«er Verwendung eines Ferranti-Shirley-Konus- und -Platten-Viskosimeters unterworfen. Die Messungen erfolgten nach der von S. S. Davis, E. Shotton und B. Warburton in der Zeitschrift J. Pharm. Pharmacol 20, 157S-167S (1968) beschriebenen Methode unter Verwendung eines Konus (Model S) bei 24 C und einer maximalen Rotationsgeschwindigkeit von 100 Umdrehungen pro Minute des Konus 10 Sekunden lang.After the stability test had been carried out over a period of one week, The lipsticks noticed a lot of tiny droplets. This results in nutty components excreted from the other components of the lipstick mixture and bloomed. The lipstick compounds described were also used in theological measurements a Ferranti-Shirley cone and plate viscometer. The measurements were made after by S. S. Davis, E. Shotton and B. Warburton in J. Pharm. Pharmacol 20, 157S-167S (1968) using a cone (Model S) at 24 C and a maximum Rotation speed of 100 revolutions per minute of the cone for 10 seconds.
Die Ergebnisse der durchgeführten Messungen sind in der Zeichnung dargestellt.The results of the measurements carried out are shown in the drawing.
(>s !n der Zeichnung veranschaulicht Kurve 1 die Beziehung zwischen der Scherkraft und der Schergeschwindigkeit der Lippenstiftmasse des Verfahrens der Erfindung, Kurve 2 die Beziehung zwischen der Scher-(> In the drawing, curve 1 illustrates the relationship between the shear force and the shear rate the lipstick mass of the method of the invention, curve 2 the relationship between the shear
kraft und der Schcrgcschwindigkcit der bekannten Lippenstiftmasse (a) und die Kurve 3 die Beziehung im Falle der bekannten Lippenstiftmasse (b). Wie sich aus der Zeichnung eindeutig ergibt, ist die Fließspannung im Zugbereich im Falle der Lippenstiftmasse des Verfahrens der Erfindung geringer als im !■"alle der bekannten Lippenstiftmassen (a) und (b). Hieraus ergibt sich, daß die Lippenstiftmasse des Verfahrens nach der Erfindung beträchtlich weicher ist als die Massen der bekannten Lippenstifte (a) und (h) und bei geringer Belastung gleichförmig gerührt werden können, und zwar auch dann, wenn die Rotationsgeschwindigkeit des Konus erhöht wird.force and the shear speed of the known lipstick compound (a) and curve 3 shows the relationship in the case of the known lipstick compound (b). As can be clearly seen from the drawing, the flow stress in the tensile area in the case of the lipstick compound of the method of the invention is lower than in all of the known lipstick compounds (a) and (b) Invention is considerably softer than the masses of the known lipsticks (a) and (h) and can be stirred uniformly with a low load, even if the speed of rotation of the cone is increased.
Der nach dem Verfahren der Erfindung hergestellte Lippenstift wies insbesondere folgende Vorteile auf:The lipstick produced according to the method of the invention had the following advantages in particular:
1. Er erwies sich Lippen gegenüber ais butterweich und zeichnete sich durch eine ausgezeichnete Lippenverträglichkeit aus.1. It turned out to be as soft as butter in relation to lips and was characterized by an excellent quality Lip tolerance.
2. Er wies ausgezeichnete Ausbreiteigenschaften auf und ließ sich ausgezeichnet glatt auf Lippen auftragen. 2. It had excellent spreading properties and was extremely smooth on lips.
3. Die Lippen ließen sich ausgezeichnet befeuchten und vor einem Aufspringen schützen. Dabei wiesen die mit dem Stift eingefärbten Lippen ein gefälliges Aussehen auf.3. The lips could be moistened excellently and protected from cracking. Included the lips colored with the pencil had a pleasing appearance.
4. Die Lippenstiftmasse zeichnete sich durch eine sehr vorteilhafte Verträglichkeit gegenüber anorganischen Pigmenten, z. B. Titandioxid, Zinkweiß und Eisenoxid aus und in der Lippenstiftmasse ließen sich die färberischen Komponenten ausgezeichnet gleichförmig verteilen.4. The lipstick mass was characterized by a very advantageous compatibility with inorganic pigments, e.g. B. titanium dioxide, zinc white and iron oxide from and in the lipstick mass the coloring components Distribute evenly.
5. Der Lippenstift war ausgezeichnet haltbar und bruchfest.5. The lipstick was extremely durable and break-resistant.
6. Die Lippenstiftmasse ließ sich durch die verschiedensten wasserlöslichen Farbstoffe und anderen hautverträglichen färbenden Komponenten einfärben. 6. The lipstick mass could be through various water-soluble dyes and others Color skin-friendly coloring components.
Demgegenüber wiesen die beiden Lippenstifte (a) und (b) des Standes der Technik in allen Punkten ungünstigere Eigenschaften auf.In contrast, the two lipsticks (a) and (b) of the prior art had less favorable properties in all points.
Beispiel 2
(Herstellung einer Lippenpomade)Example 2
(Making a lip balm)
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die folgenden Komponenten (A), (B) und (C) miteinander vermischt:According to the method described in Example 1, the following components (A), (B) and (C) were mixed with one another:
12,0
3,0
2,0
5,0
0,2
0,0566.75
12.0
3.0
2.0
5.0
0.2
0.05
5,02.0
5.0
Festes Paraffin
Japanwachs
Lanolin
Mikrokristallines Wachs
Antioxidationsmittel
Butyl-p-hydroxybenzoatLiquid paraffin
Solid paraffin
Japan wax
lanolin
Microcrystalline wax
Antioxidants
Butyl p-hydroxybenzoate
1,0
1,02.0
1.0
1.0
50%ige wäßrige Lösung von
D-GlucoseSorbitol sesquioleate
50% aqueous solution of
D-glucose
Propylenglykol
Gelber FarbstoffDeionized water
Propylene glycol
Yellow dye
(B)(B)
(C)(C)
Die einzelnen Komponenten wurden nach dem in Beispiel 1 beschriebenen Verfahren miteinander vermischt, worauf sie zu Hautpflegestiften verformt wurden. The individual components were mixed with one another according to the method described in Example 1, whereupon they were shaped into skin care sticks.
B e i s ρ i e 1 4 (Herstellung eines Grundierungsstiftes)B e i s ρ i e 1 4 (making a primer pen)
Nach dem in Beispiel 1 beschriebenen VerfahrenFollowing the procedure described in Example 1
wurden die folgenden Komponenten (A), (B) undwere the following components (A), (B) and
(C) miteinander vermischt und zu Stiften verformt: (C) mixed together and deformed into pins:
(A) Kosmetische Grundlage (A) Cosmetic base
Flüssiges Paraffin
Festes Paraffin
Mikrokristallines Wachs Butyl-p-hydroxybenzoatLiquid paraffin
Solid paraffin
Microcrystalline wax butyl p-hydroxybenzoate
(A) Kosmetische Grundlage Gew.-Teile (A) Cosmetic base parts by weight
Flüssiges Paraffin 46,94Liquid paraffin 46.94
Festes Paraffin 15,0
Mikrokristalliner Wachs 5,0Solid paraffin 15.0
Microcrystalline wax 5.0
Vaseline 5,0Vaseline 5.0
Butyl-p-hydroxybenzoat 0,05Butyl p-hydroxybenzoate 0.05
(B) Gel (B) gel
Sorbitolmonooleat 3,0Sorbitol monooleate 3.0
Glyzerin 5,0Glycerin 5.0
(C) Deionisiertes Wasser 15,0 (C) Deionized water 15.0
1,3-Butylenglykol 5,01,3-butylene glycol 5.0
Gelber Farbstoff 0,01Yellow dye 0.01
Die erhaltene Masse wurde dann unter Herstellung von Lippenpomadenstiften verformLThe resulting mass was then shaped to produce lip balm sticks
(B) Gel (B) gel
Propy 1 engly kol monool eat GlyzerinPropy 1 engly kol monool eat glycerin
SorbitolmonolauratSorbitol monolaurate
(C) Deionisiertes Wasser
Propylenglykol (C) Deionized water
Propylene glycol
Zinkweiß und Eisenoxid (Verhältnis 4 : 6)Zinc white and iron oxide (ratio 4: 6)
Gew.-TeileParts by weight
24,93 14,024.93 14.0
3,03.0
0,070.07
2,0 5,0 1,02.0 5.0 1.0
25,0 5,025.0 5.0
20,0 Beispiel 5 (Herstellung eines Lippenstiftes)20.0 Example 5 (production of a lipstick)
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die im folgenden angegebenden Komponenten (A), (B) und (C) miteinander vermischt und daraufhin zu Lippenstiften verformt:According to the method described in Example 1, the components (A), (B) and (C) given below were mixed with one another and then shaped into lipsticks:
(A)(A)
Beispiel 8
(Herstellung eines Lippenstiftes)Example 8
(Making a lipstick)
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die folgenden Komponenten (A). (B) und CCV miteinander vermischt, worauf die erhaltene Wasser-in-Öl-Emulsion zu Lippenstiften verformt wurde.Following the procedure described in Example 1, the following components (A) were obtained. (B) and CCV mixed together, whereupon the resulting water-in-oil emulsion was shaped into lipsticks.
Beispiel 6
(Herstellung eines Giundierungsstiftes)Example 6
(Manufacture of a foundation pen)
isis
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die im folgenden angegebenen Komponenten (A), (B) und (C) miteinander vermischt und 20 verformt:According to the method described in Example 1, the components (A), (B) and (C) given below were mixed with one another and shaped:
2525th
4040
Beispiel 7
(Herstellung eines kosmetischen Stiftes)Example 7
(Making a cosmetic pen)
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die folgenden angegebenen Komponenten (A), (B) und (C) miteinander vermischt, worauf die erhaltene Wasser-in-Öl-Emulsion zu einem kosmetischen Stift verformt wurde.According to the method described in Example 1, the following specified components (A), (B) and (C) were mixed with one another, whereupon the water-in-oil emulsion obtained was shaped into a cosmetic stick.
Beispiel 9
(Herstellung eines Lippenstiftes)Example 9
(Making a lipstick)
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die im folgenden angegebenen Komponenten (A), (B) und (C) miteinander vermischt, worauf die erhaltenen Wasser-in-Öl-Emulsion zu Lippenstiften verformt wurde.According to the method described in Example 1, the components (A), (B) and (C) indicated below were mixed with one another, whereupon the resulting water-in-oil emulsion was shaped into lipsticks.
(A)(A)
4545
5555
6060
65 (Herstellung eines kosmetischen Stiftes) 65 (making a cosmetic pen)
Nach dem in Beispiel 1 beschriebenen Verfahren wurden die im folgenden aufgeführten Komponenten (A), (B) und (C) miteinander vermischt, woraufFollowing the procedure described in Example 1, the following components (A), (B) and (C) were mixed together, whereupon
die erhaltene Wasser-in-ÖI-Emulsion unter Erzeugung eines kosmetischen Stiftes verformt wurde.the resulting water-in-oil emulsion to form a cosmetic stick has been deformed.
Der erhaltene kosmetische Stift wurde einem Schimmel-Kulturtest unterworfen, bei dem der Stift bei 25 C und einer Luftfeuchtigkeit von 80% über zwei Wochen lang aufbewahrt wurde. Es wurde kein Schimmel auf dem Stift festgestellt.The obtained cosmetic stick was subjected to a mold culture test in which the stick was 25 C and a humidity of 80% for two weeks. There was no mold noted on the pen.
Zu Vergleichszwecken wurde ein weiterer Stift unter Verwendung von Sorbitol anstelle von Glyzerin hergestellt. Der erhaltene Stift wurde dem gleichen Test unterworfen. Nach einer Inkubationszeit von zwei Wochen wurde auf dem Stift Schimmel festgestellt.For comparison purposes, another stick was made using sorbitol instead of glycerin manufactured. The stick obtained was subjected to the same test. After an incubation period of two For weeks, mold was found on the pen.
Beispiel 11
(Vergleichsbeispiel)Example 11
(Comparative example)
einer vergleichsweise kurzen Zeitspanne aus dem Stift aus. Des weiteren trennen sich bei längerer Lagerung des Stiftes die übrigen Komponenten, so daß der Stift nach längerer Lagerung ein unschönes Aussehen aufweist und auf seiner Oberfläche leicht Wassertröpfchen auftreten.from the pen in a comparatively short period of time. Furthermore, separate with longer Storage of the pen, the remaining components, so that the pen after a long period of storage an ugly Has appearance and water droplets easily appear on its surface.
Λ) Herstellung eines Lippenstiftes nach dem Verfahren der Erfindung unter Verwendung eines GelsΛ) Making a lipstick by the process of the invention using a gel
Es wurde ein Lippenstift ausgehend von den folgenden Komponenten hergestellt:A lipstick was made from the following components:
(a) Kosmetische Grundlage
Flüssiges Paraffin (a) Cosmetic base
Liquid paraffin
CeresinCeresin
CandelillawachsCandelilla wax
TiO2 TiO 2
Roter Farbstoff
Butyl-p-hydroxybenzoatRed dye
Butyl p-hydroxybenzoate
ParfümPerfume
Dies Beispiel zeigt die besondere Bedeutung des bei Durchführung des Verfahrens der Erfindung zunächst hergestellten Gels.This example shows the particular importance of the first step when carrying out the method of the invention manufactured gels.
Aufgrund der ausgezeichneten Emulgiereigenschaften des Gels läßt sich Wasser unter Ausbildung sehr feiner Wasserteilchen von einem Durchmesser von 1 Mikron oder darunter emulgieren. Die Wasserteilchen lassen sich gleichförmig in der kosmetischen Grundlage verteilen, wobei die emulgierten Wasserteilchen stabil bleiben, d.h. ein nach dem Verfahren der Erfindung hergestellter Stift läßt sich über längere Zeiträume hinweg aufbewahren, ohne daß seine Stabilität verlorengeht. Des weiteren behält der Stift seine äußere glatte Oberfläche auch über längere Zeiträume hinweg bei. Dies bedeutet, daß auch nach längerer Lagerung des Stiftes keine Ausscheidungen auftreten und sich auf der Oberfläche des Stiftes keine Wassertröpfchen bilden.Because of the excellent emulsifying properties of the gel, water can be very emulsified with formation Emulsify fine water particles 1 micron or less in diameter. The water particles can be evenly distributed in the cosmetic base, with the emulsified water particles remain stable, i.e. a stick made according to the method of the invention can be used for long periods Store for periods of time without losing its stability. Furthermore, the Pin its smooth outer surface even over long periods of time. This means that even after If the pen is stored for a longer period of time, no excretions occur and there are no deposits on the surface of the pen Form water droplets.
Werden demgegenüber die zur Durchführung des Verfahrens der Erfindung verwendeten Polyhydroxyverbindungen und die angegebenen, nichtionogenen, oberflächenaktiven Verbindungen getrennt voneinander ohne Gelbildung mit der kosmetischen Grundlage und Wasser vermischt, d.h. nach dem bisher üblicherweise praktizierten Verfahren, so wird das Wasser unter Bildung von vergleichsweise großen Wasserteilchen emulgiert, und zwar Wasseneilchen, die einen Durchmesser von größer als 3 Mikron aufweisen. Diese Wasserteilchen scheiden sich leicht innerhalb Gew.-TeileIn contrast, the polyhydroxy compounds used to carry out the process of the invention and the specified, nonionic, surface-active compounds separately from one another mixed with the cosmetic base and water without gel formation, i.e. according to the previous one Usually practiced processes, the water is formed with the formation of comparatively large water particles emulsified, namely, hydrails, the greater than 3 microns in diameter. These water particles easily separate within Parts by weight
56,8456.84
19,019.0
1,01.0
5,705.70
1,301.30
0,050.05
0,10.1
Die angegebenen Komponenten wurden miteinanderThe specified components were with each other
bei 80 C unter Verrühren vermischt. Auf diese Weise wurde ein gleichförmiges Grundmaterial hergestellt.mixed at 80 C with stirring. In this way a uniform base material was produced.
(b) Gel-Emulgiermittel Gew.-Teile (b) Gel emulsifier parts by weight
Glyzerinmonooleat 3,0Glycerol monooleate 3.0
70%ige wäßrige Lösung von
Maltose 2,070% aqueous solution of
Maltose 2.0
Bei der Herstellung des Gels wurde die Maltoselösung tropfenweise in das Glyzerinmonooleat bei Raumtemperatur eingerührt. Nach beendeter Zugabc der Maltoselösung wurde die Mischung noch weitere IO Minuten lang gerührt. Auf diese Weise wurde ein Gel erhalten.When making the gel, the maltose solution was used Stirred drop by drop into the glycerol monooleate at room temperature. After the addition is complete Maltose solution, the mixture was stirred for a further 10 minutes. In this way a Gel received.
(c) Wasser-Anteil (c) water content
Deionisiertes Wasser
Propylenglykol
Roter FarbstoffDeionized water
Propylene glycol
Red dye
Gew. -TeileParts by weight
10.0
1,0
0,0110.0
1.0
0.01
Das Propylenglykol und der Farbstoff wurden in dem deionisierten Wasser gelöst.The propylene glycol and dye were dissolved in the deionized water.
Das Gel (b) wurde tropfenweise in die kosmetische Grundlage (a) bei 70 C eingerührt. Daraufhin wurde der Wasseranteil (c) tropfenweise in die Mischung aus dem Gel (b) und der kosmetischen Grundlage (a) unter Rühren bei 70' C in einem Homogenesierapparat eingerührt. Nach beendetem Mischen wurde die Mischung noch 10 Minuten lang bei 70 C gerührt. Auf diese Weise wurde eine gleichförmige Emulsion erhalten. The gel (b) was stirred into the cosmetic base (a) at 70 ° C. drop by drop. The water portion (c) was then added dropwise into the mixture of the gel (b) and the cosmetic base (a) while stirring at 70 ° C. in a homogenizer. When the mixing was complete, the mixture was stirred at 70 ° C. for a further 10 minutes. In this way a uniform emulsion was obtained.
Die erhaltene Emulsion wurde dann einer Vakuumbehandlung unterworfen, wodurch Bläschen in der Emulsion eliminiert wurden. Anschließend wurde die Emulsion bei 70"C filtriertThe resulting emulsion was then subjected to a vacuum treatment, whereby bubbles in the Emulsion were eliminated. The emulsion was then filtered at 70.degree
Ein Teil der filtrierten Emulsion wurde zu drei Lippenstiften verarbeitet, indem die Emulsion in drei Lippenstift-Formen gegossen und hierin auf Raumtemperatur abkühlen gelassen wurde.A portion of the filtered emulsion was made into three lipsticks by dividing the emulsion into three Lipstick molds were poured and allowed to cool to room temperature therein.
B) Herstellung von Vergleichs-LippenstiftenB) Manufacture of comparative lipsticks
Das unter A) beschriebene Verfahren wurde wiederholt mit der Ausnahme jedoch, daß kein Gel her-The procedure described under A) was repeated with the exception, however, that no gel was produced.
gestellt wurde. Diesmal wurde vielmehr das Glyzerinmonooleat in die kosmetische Grundlage eingemischt. Die wäßrige Maltoselösung wurde mit dem Wasseranteil vermischt, worauf diese Mischung mit der kosmetischen Grundlage vermischt wurde. Auf diese Weise wurde eine Vergleichsemulsion hergestellt. Ein Anteil der filtrierten Vergieichsemulsion wurde in der beschriebenen Weise zu Lippenstiften verarbeitet.was asked. Rather, this time the glycerine monooleate was mixed into the cosmetic base. The aqueous maltose solution was mixed with the water portion, whereupon this mixture with the cosmetic Basis has been mixed. In this way a comparative emulsion was prepared. A Part of the filtered comparative emulsion was processed into lipsticks in the manner described.
(a) Für mikroskopische Beobachtungen wurden von den Lippenstiften kleine Abschnitte abgetrennt. Diese Abschnitte wurden bei 4001'acher Vergrößerung betrachtet. (a) Small sections were cut from the lipsticks for microscopic observation. These sections were viewed at 4001 magnification.
Es ergab sich, daß im Falle des nach dem Verfahren der Erfindung hergestellten Lippenstiftes die emulgierten Wasserteilchen eine Teilchengröße von unter 1 μ haben, wohingegen die emulgierten Wasserteilchen des Vergleichs-Lippenstiftes einen Durchmesser von über 3 μ hatten.It was found that in the case of the lipstick produced by the method of the invention emulsified water particles have a particle size of less than 1 μ, whereas the emulsified water particles of the comparison lipstick had a diameter of over 3 μ.
(b) Ein nach dem Verfahren der Erfindung hergestellter Lippenstift mit einem Gewicht von 3,9 g wurde einem beschleunigten Trockentest unterworfen, bei dem der Lippenstift in einen geschlossenen Behältergebracht wurde, der Phosphorpentoxid als Trocknungsmittel enthielt. Der Stift wurde bei einem verminderten Druck von etwa 5.0 mm Hg bei Raumtemperatur 90 Tage lang getrocknet. Danach wies der Lippenstift ein Gewicht von 3,87 g auf. Es trat somit ein Gewichtsverlust von lediglich etwa 0,8%, bezogen auf das ursprüngliche Gewicht des Lippenstiftes, auf. Der gleiche Test wurde mit dem Vergleichs-Lippenstifl durchgeführt. Auch dieser Lippenstift wies zunächst, d.h. zu Beginn des Testes, ein Gewicht von 3,9 g auf. Nach Beendigung des Testes hatte der Stift ein Gewicht von 3,63 g. Dies entspricht einem Gewichtsverlust von etwa 7%, bezogen auf das Gewicht des ursprünglichen Stiftes. (b) A lipstick made by the method of the invention weighing 3.9 g was subjected to an accelerated drying test in which the lipstick was placed in a closed container containing phosphorus pentoxide as a drying agent. The stick was dried under a reduced pressure of about 5.0 mm Hg at room temperature for 90 days. The lipstick then weighed 3.87 g. There was thus a weight loss of only about 0.8%, based on the original weight of the lipstick. The same test was carried out on the comparative lipstick. This lipstick, too, initially, ie at the beginning of the test, had a weight of 3.9 g. At the end of the test, the stick weighed 3.63 g. This corresponds to a weight loss of about 7% based on the weight of the original pencil.
ίο Aus den erhaltenen Ergebnissen ergibt sich, daß die Bindung des Wassers in dem nach dem Verfahren der Erfindung hergestellten Lippenstift viel stärker war als bei dem Vergleichsstift. Hieraus ergibt sich die beträchtlich bessere Bindung und Emulgierung der Wasserteilchen in dem erfindungsgemäß hergestellten Stift.ίο From the results obtained it can be seen that the binding of the water in the lipstick made by the method of the invention is much stronger was than with the comparison pen. This results in the considerably better binding and emulsification of the Water particles in the stick made according to the invention.
(c) Verwendung der Lippenstifte (c) Using the lipsticks
Mit den in der beschriebenen Weise hergestellten Lippenstiften wurden Versuche mit 10 Versuchspersonen (Frauen) durchgeführt. Ermittelt wurden das Gefühl auf den Lippen, Ausbreiteigenschaften sowie hautweichmachende Eigenschaften.Tests with 10 test persons were carried out with the lipsticks produced in the manner described (Women) performed. The feeling on the lips, spreading properties as well as were determined skin softening properties.
In allen Fällen wurden die nach dem Verfahren der Erfindung hergestellten Stifte weit positiver beurteilt als die Vergleichsstifte.In all cases, the pencils made by the method of the invention were rated far more positively than the comparison pins.
Claims (1)