DE2217280A1 - PERFORATED SCREEN IN COLOR TUBES - Google Patents
PERFORATED SCREEN IN COLOR TUBESInfo
- Publication number
- DE2217280A1 DE2217280A1 DE19722217280 DE2217280A DE2217280A1 DE 2217280 A1 DE2217280 A1 DE 2217280A1 DE 19722217280 DE19722217280 DE 19722217280 DE 2217280 A DE2217280 A DE 2217280A DE 2217280 A1 DE2217280 A1 DE 2217280A1
- Authority
- DE
- Germany
- Prior art keywords
- iron
- nickel
- composition
- pinhole
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Metallgesellsuhaft Frankfurt a.LI., den 7.4.72Metallgesellsuhaft Frankfurt a.LI., 7.4.72
AktiengesellschaftCorporation
Prankfurt a.K. Dr.Ml/HtfiPrankfurt a.K. Dr.Ml/Htfi
Reuterweg 14Reuterweg 14
prov.No. 6952 Mprov.No. 6952 M.
Lochblende In Farbbildröhren.Pinhole in color picture tubes.
Die Erfindung betrifft eine Lochblende bzw. Schattenmaske für die Farbbilderzeugung in Farbbildröhren von Farbfernsehempfängern. Insbesondere betrifft dj,e Erfindung eine mit Federhalterung versehene Lochblende aus Blechen aus Eisenwerkstoff. The invention relates to a pinhole or shadow mask for producing color images in color picture tubes of color television receivers. In particular, the invention relates to one with Perforated panel made of sheet metal made of ferrous material with a spring holder.
Me erfindungsgemässe Lochblende ist gekennzeichnet durch einen Werkstoff aus Eisenlegierung mit einer im Temperaturbereich von 20 bis 800G spezifischen thermischen Ausdehnung von 0 bis 2, vorzugsweise 0,6 bis 1,2 χ 10" .0C .Me according to the invention aperture plate is characterized by a material made of iron alloy having a temperature range of 20 to 80 0 G specific thermal expansion from 0 to 2, preferably 0.6 to 1.2 χ 10 "0. C.
Die Farbbildröhre der heutigen Farbfernsehempfänger—Systeme enthält drei Elektronenstrahl-Erzeuger, die' in der Weise ausgerichtet sind., daß ihre Strahlen gemeinsam durch eines der ca. 400.000 Löcher von etwa 0,35 nun Durchmesser einer Lochblende ( Schattenmaske ) hindurch auf eine Dreiergruppe (Tripel) von in den drei Primärfarben Rot, Grün und Blau aufleuchtenden Leuchtstoff-Scheibchen ( Phosphore ) fallen. Diese Leuchtstoff-Scheibchen von etwa 0,43 mm Durchmesser bilden insgesamt den Farbbildschirm. Der Farbbildschirm enthält inThe color picture tube of today's color television receiver systems contains three electron guns which are aligned in such a way that their beams pass through one of the about 400,000 holes of about 0.35 now diameter of a pinhole (Shadow mask) through to a group of three (triples) of in the three primary colors red, green and blue light up fluorescent discs (phosphors) fall. These fluorescent discs form about 0.43 mm in diameter overall the color screen. The color screen contains in
3098^4/05413098 ^ 4/0541
regelmäßiger Anordnung dreimal 400,000 Farbleuchtpunkte. Der Abstand zwischen Schirm und Lochblende beträgt etwa 11,5 nun, während der Abstand der Farbtripel untereinander 0,74 mm beträgt. Die für die drei Jilektronenstrahlen gemeinsame magnetische Ablenkung ist in der Weise ausgeführt, daß die Elektronenstrahlen auch am Bildrand gemeinsam durch das richtige Blendenloch auf die richtigen Leuchtstoff-Scheibchen fallen. Abweichungen erzeugen unerwünschte Farbsäume. Die Deckung der Blendenlöcher mit den Farbtripeln bereitet erhebliche Schwierigkeiten. Der Anteil der Löcher der Schattenmaske an der Gesamtfläche der Lochblende aus üblicherweise Blech aus Eisenwerkstoff beträgt bei den heute üblichen Lochblenden noch nicht einmal 50 "/>. Die Elektronenstrahlen treffen demzufolge auch mit über 50 fo ihrer Intensität auf das Blech der Schattenmaske auf, wodurch diese unvermeidbar und in der Praxis bis auf ca. 80 C erwärmt wird. Diese Erwärmung hat aber eine Ausdehnung des üblicherweise aus einem kohlenstoffarmen Stahl bestehenden Blechs der Lochblende in allen Richtungen zur Folge. Dies führt dazu, daß die Löcher ihrerseits nicht mehr in der richtigen Position bezüglich der Farbtripel sind. Die Folge davon sind Farbverschiebungen und Farbsäurae, die als störend empfunden werden. Um diesen Nachteil von aus üblichen Stahlblechen hergestellten Lochblenden auszugleichen, wird diese üblicherweise an mindestens zwei, vorzugsweise an bis zu vier Regelelementen aus einem Thermobimetall befestigt. Die Regelelemente haben gleichzeitig Federeigenschaften, so daß sich an ihnen die Lochblende in die Halteknöpfe des Schirmglases einhängen läßt. Die an der Lochblende angeschlossenen Thermobimetall-Regelelemente werden ebenfalls durch die Lochblende erwärmt.regular arrangement three times 400,000 colored luminous points. The distance between the screen and the aperture is now about 11.5, while the distance between the color triples is 0.74 mm. The magnetic deflection common to the three electron beams is designed in such a way that the electron beams also fall together at the edge of the image through the correct aperture onto the correct fluorescent disc. Deviations produce undesirable color fringes. The coverage of the diaphragm holes with the color triplets causes considerable difficulties. The proportion of holes is the shadow mask of the total area of the aperture plate from commonly sheet of iron material in the current normal pinhole not even 50 "/>. Making the electron consequently with fo over 50 of their intensity on the plate of the shadow mask, whereby this is unavoidable and in practice is heated up to about 80 C. This heating, however, results in the sheet metal of the perforated diaphragm, which usually consists of a low-carbon steel, expanding in all directions The consequence of this is color shifts and color acidity, which are perceived as annoying. In order to compensate for this disadvantage of apertured diaphragms made from conventional steel sheets, these are usually attached to at least two, preferably to up to four control elements made of a thermal bimetal have spring properties at the same time adhere so that the aperture plate can be hooked into the holding buttons of the screen glass on them. The thermo-bimetal control elements connected to the perforated diaphragm are also heated by the perforated diaphragm.
-3--3-
309844/0541309844/0541
Dadurch biegen sie sieh aus und führen die Lochblende senkrecht zur Mitte der Bildschirmoberflache näher an die leuchtpunkte auf dem Leuchtschirm heran. Hierdurch werden die Blendenlöcher wieder in den vorgesehenen Elektronenstrahlgang gerückt. Es ist verständlich, daß die hohe Präzision der Lochblenden-Herstellung auch eine hohe Präzision in der Punktion der als Federhalterung ausgebildeten Thermobimetall-Regelelemente verlangt und auch die Befestigung dieser Feder- bzw. Regelelemente an der Lochblende mit der größten Genauigkeit erfolgen muß. Die Bewegung der Lochblende in Sichtung zu den Färbtripelpunkten oder von diesen weg, beträgt nämlich im allgemeinen nur etwa 0,08 mm, insgesamt also etwa 0,16 mm im Temperaturbereich von 20 bis 800O.As a result, they bend out and bring the aperture plate perpendicular to the center of the screen surface closer to the luminous dots on the fluorescent screen. As a result, the aperture holes are moved back into the intended electron beam path. It is understandable that the high precision of the aperture diaphragm production also requires high precision in the puncture of the thermobimetallic control elements designed as a spring holder and that these spring or control elements must also be attached to the aperture diaphragm with the greatest accuracy. The movement of the pinhole in sighting the Färbtripelpunkten or away from, namely, is in general only about 0.08 mm, so a total of about 0.16 mm in the temperature range of 20 to 80 0 O.
Der Erfindung liegt die Aufgabe zugrunde, eine Lochblende aus einem Y/erkstoff bereitzustellen, der eine hohe und daher aufwendige Präzision der Regelungstechnik erübrigt, uud die Nachteile der vorbekannten Lochblenden vermeidet.The invention is based on the object of a pinhole to be made from a Y / er material that makes a high and therefore costly precision of the control technology superfluous, uud avoids the disadvantages of the previously known pinhole diaphragms.
Hierzu geht die Erfindung von einer mit Federhalterung versehenen Lochblende aus Eisenwerkstoff für die Farbbilderzeugung in Farbbildröhren von Farbfernsehempfängern aus. Die Erfindung besteht nun darin, daß der Eisenwerkstoff eine Legierung mit im Temperaturbereich von 20° bis 80°G einer spezifischen thermischen Ausdehnung von 0 bis 2, vorzugsweise 0,6 bis 1,2 χ 10" .0C" ist.To this end, the invention is based on a perforated diaphragm made of ferrous material, provided with a spring holder, for generating color images in color picture tubes of color television receivers. The invention consists in that the iron material is an alloy with a specific thermal expansion of 0 to 2, preferably 0.6 to 1.2 χ 10 ". 0 C" in the temperature range from 20 ° to 80 ° G.
Für die Lochblende aus'dem erfindungsgemäß einzusetzenden Werkstoff eignen sich an sich bekannte Eisen/K^ckel-Legierungen oder Sisen/tfickel-Legierungen mit weiteren Legierungselementen wie Kobalt, Chrom, Mangan, Silicium, Wolfram. Für die Lochblende.gemäß der Erfindung geeignete Werkstoffe aus Eisen/Niekel-Legierung,haben im allgemeinen die Zusammensetzung:For the perforated diaphragm to be used according to the invention Material are known iron / K ^ ckel alloys or Sisen / tfickel alloys with others Alloy elements such as cobalt, chromium, manganese, silicon, Tungsten. For the perforated diaphragm according to the invention suitable materials made of iron / Niekel alloy generally have the composition:
30984A/054130984A / 0541
Insbesondere eignen sich Eisen/Nickel-Legierungen der Zusammensetzung:Iron / nickel alloys with the following composition are particularly suitable:
35 bis 37 °/° Nickel35 to 37 ° / ° nickel
0,01 " 0,1 io Kohlenstoff0.01 "0.1 io carbon
0,3 " 0,6 io Mangan0.3 "0.6 io manganese
0 " 0,35 io Silicium0 "0.35 io silicon
Rest EisenRemainder iron
Für die Verwendung von Invar für eine Lochmaske ist folgende Zusammensetzung vorzugsweise geeignet:The following composition is preferably suitable for using Invar for a shadow mask:
Ni =36 io Ni = 36 io
C = 0,01 bis O,O8~7SC = 0.01 to 0.08 ~ 7S
Mn = 0,1 - 0,5 io Mn = 0.1-0.5 io
Pb = 0,04 io maxPb = 0.04 io max
S = 0,05 i° "S = 0.05 i ° "
Si = 0,1 io "Si = 0.1 io "
Rest EisenRemainder iron
WOBEI außer den Elementen Pb und S keine anderen MetalleWHERE besides the elements Pb and S no other metals
in der legierung/sein dürfen, die während der Herstellung enthaltenin the alloy / allowed to be used during manufacture contain
der Röhre oder während des Betriebes der Röhre aus dem Invar herausdampfen können ( Selen, Zink, Antimon, Arsen etc.)the tube or during operation of the tube from the Invar (selenium, zinc, antimony, arsenic etc.)
Formteile aus diesen Legierungen haben bei RaumtemperaturMoldings made from these alloys have at room temperature
-6 ο -1 eine spezifisch thermische Ausdehnung von ca. 1,2 χ 10 .C-6 ο -1 a specific thermal expansion of approx. 1.2 χ 10 .C
309844/0541309844/0541
-5--5-
Weiterhin ist gemäß der Erfindung als Y/erkstoff für die · Lochblende eine Eisen/tlickel-Legiorung der ZusammensetzungFurthermore, according to the invention, as Y / er material for the Pinhole an iron / tickel alloy composition
30 bis 31 cß> Hi ekel 4 bis 8 $,30 to 31 c ß> Hi disgust 4 to 8 $,
vorzugsweise 5 bis 7 $ Kobalt Rest Eisen,preferably 5 to 7 $ cobalt remainder iron,
geeignet. Formteile aus diesen Legierungen besitzen im Temperaturbereich von 20 bis 800G eine spezifischesuitable. Molded parts made from these alloys have a specific temperature range from 20 to 80 ° C.
—6 ο -1 thermische Ausdehnung von ca. 0,6 χ 10 . G—6 ο -1 thermal expansion of approx. 0.6 χ 10. G
Des weiteren eignen sich als Werkstoff für die Lochblende gemäss der Erfindung Eisen/Hickel-Legierungen der Zusammensetzung Furthermore, iron / Hickel alloys of the composition are suitable as material for the perforated diaphragm according to the invention
J i'J J i ' J
Formteile aus diesen.Legierungen sind rostfrei und besitzen im Temperaturbereich von 20 bis 800G eineMolded parts from these alloys are rust-free and have a temperature range from 20 to 80 0 G
spezifische thermische Ausdehnung τοιί "Jireniger als sa0 10-6 ο -1specific thermal expansion τοιί "Jireniger than sa 0 10 -6 ο -1
\j\ j
Die als Werkstoff erfindungsgemäß zur Herstellung von Lochblenden einzusetsenden Eisen/licfcel-Legierungen werden,wie bekannt,auch als Werkstoff zur Herstellung der passiven Komponente von Thermobinietallen verwendet.The iron / licfcel alloys to be used as a material according to the invention for the production of perforated diaphragms are, as is known, also used as a material for the production of the passive component of thermobinietals is used.
309844/0541309844/0541
Die Herstellung der erfindungsgemäßen Lochblenden aus Blechen aus praktisch ausdehnungsfreien Eisen/Nickel- -; Legierungen erfolgt in an sich bekannter V/eise. Vormaterial aus den gemäß der Erfindung einzusetzenden Eisen/ Nickel-Legierungen wird auf die erforderliche Dicken- und Breitenabmessung ( Blechstärke ca. 150/u) in an sich bekannter Weise gewalzt und das gewalzte und gereinigte Blech mittels des Foto-Ätzverfahrens mit den erforderlichen Löchern zur Herstellung der Schattenmaske versehen.The production of the apertured diaphragms according to the invention from sheet metal made of practically expansion-free iron / nickel -; Alloys are made in a manner known per se. Raw material from the iron / nickel alloys to be used according to the invention is rolled to the required thickness and width dimensions (sheet thickness approx. 150 / u) in a known manner and the rolled and cleaned sheet metal with the necessary holes by means of the photo-etching process Manufacture of the shadow mask provided.
Die erfindungsgemässe Lochblende aus Werkstoff aus Eisen/ Nickel-Legierungen kann zweckmässig noch einer Oberflächenbehandlung unterzogen werden um die Wärmeabgabe des Materials zu verbessern. Obwohl nämlich die Erwärmung der Lochblende ( die Elektronenstrahlen tragen mit etwa 30 Watt zu dieser Erwärmung bei ) aus dem erfindungsgemässen Werkstoff aufgrund des geringen Ausdehnungskoeffizienten der einzusetzenden i'isen/Niekel-Legierungen ohne nennenswerten Einfluss auf die Bildqualität ist, wird vorteilhafter Weise die 7/ärmeabstrahlung der Lochblende durch eine Oberflächenbehandlung verbessert. Derartige Oberflächenbehandlungen zwecks Schwärzung der Oberfläche können in bekannter Weise durch, oxidative Behandlung "bei erhöhter Temperatur vorgenommen werden, beispielsweise durch Erwärmen in Luft bei 400 bis 7000C. Ferner kann die Schwarzfärbung durch elektrölytische Oxidation herbeigeführt werden, wie auch des weiteren in bekannter Weise Schwarzfärben oder Brünieren auf chemischem Wege durch z.B. Behandlung der Lochblenden aus nichtrostenden Stählen mix z.B. Chromschwefelsäure.The perforated diaphragm according to the invention made of material made of iron / nickel alloys can expediently also be subjected to a surface treatment in order to improve the heat dissipation of the material. Although the heating of the pinhole diaphragm (the electron beams contribute about 30 watts to this heating) from the material according to the invention has no significant influence on the image quality due to the low expansion coefficient of the iron / Niekel alloys to be used, the 7 / Heat radiation of the pinhole is improved by a surface treatment. Such surface treatments for the purpose of blackening the surface can in a known manner by, "are made at an elevated temperature oxidative treatment, for example by heating in air at 400 to 700 0 C. Further, the black coloring are brought about by elektrölytische oxidation, as well as further in a known manner Black dyeing or burnishing by chemical means, for example by treating the pinhole diaphragms made of stainless steels mix, for example, chromosulfuric acid.
Die herkömmlichen Lochblenden sind in aller Regel mit Federhalterungen ausgestattet. Diese Federhalterungen werden in den Halteknöpfen des Schirmglases eingehängt. Bei vorbekannten Lochblenden müssen zusätzlich Bimetallstreifen vorgesehen werden, um die Ausdehnung des Werkstoffs zu kompensieren. Nach einer weiteren AusgestaltungThe conventional pinhole diaphragms are usually equipped with spring holders. These spring retainers are hung in the holding buttons of the screen glass. In the case of previously known perforated diaphragms, bimetal strips must also be used be provided to compensate for the expansion of the material. According to another embodiment
309844/0541 _7_309844/0541 _ 7 _
der Erfindung wird die äusserst geringe \7armeausdehnung der erfindungsgemässen Lochblende unter Erübrigung von Bimetallfedern durch Federhalmngen aus metallischem Werkstoff bewirkt, der eine spezifische thermische Längenausdehnung von 10 bis 28, vorzugsweise 12 bis 20 χ 10~6.°0 "1 aufweist.of the invention is effected extremely low \ 7armeausdehnung of the inventive perforated diaphragm under Erübrigung of bimetallic by Federhalmngen made of metallic material having a specific linear thermal expansion of 10 to 28, preferably 12 to 20 χ 10 ~. 6 ° 0 '1.
Während z.B. bei Lochblenden aus herkömmlichem unlegiertem Stahl mit einem Ausdehnungskoeffizienten von 12x 10" -.0C , die Lochblende bei einer angenommenen Temperaturdifferenz von 600C um insgesamt etwa 0,16 rom ( bei einer 63 cm-Bildröhre) in Richtung auf den Leuchtschirm hinbewegt werden muß, ist bei einer erfindungsgemäßen Lochblende aus Eisen/Nickel-Legierung, für die z.B. ein Ausdehnungskoeffizient vonWhile, for example, with aperture diaphragms made of conventional unalloyed steel with a coefficient of expansion of 12 x 10 "-. 0 C, the aperture diaphragm with an assumed temperature difference of 60 0 C by a total of about 0.16 rom (with a 63 cm picture tube) in the direction of the luminescent screen must be moved, is in a perforated diaphragm according to the invention made of iron / nickel alloy, for example, a coefficient of expansion of
-6 ο -1
1,2 χ 10 . C zugrunde gelegt wird, eine Verschiebung von nur 0,016 mm in Richtung Leuchtschirm erforderlich.
Zur Bewerkstelligung dieser geringen Verschiebung genügt es, daß die zur Halterung verwendeten Federelemente eine aktive
Länge von 22 mm aufweisen, wenn sie aus unlegiertem Stahl hergestellt sind. Sie können auch eine aktive Länge
von 10 mm aufweisen, wenn sie aus einer Manganlegierung der Zusammensetzung-6 ο -1
1.2 χ 10. C is taken as a basis, a shift of only 0.016 mm in the direction of the luminescent screen is necessary. In order to achieve this slight displacement, it is sufficient that the spring elements used for mounting have an active length of 22 mm if they are made of unalloyed steel. They can also have an active length of 10 mm if they are made from a manganese alloy of the composition
74 °/o Mn74 per cent
16 /» Hi16 / »Hi
10 io Cu10 io Cu
mit einem Ausdehnungskoeffizienten von 28 χ 10~ .0C" hergestellt sind. Unter dem Begriff "Aktive Länge " ist diejenige Länge zu verstehen, die ausschlaggebend für die thermische Ausdehnung ist. Nach der weiteren Ausgestaltung der Erfindung können nun auch sämtliche zwischen den genannten Längen von 22 und 10 mm liegenden Längen der Federelemente, die durch die verschiedensten Konstruktionen erforderlich werden, eingestellt werden. Hierzu werden gemäß der weiteren Ausgestaltung der Erfindung für die Pederhalterung als metallische Werkstoffe legierte Stähle derwith an expansion coefficient of 28 χ 10 ~. 0 C. "The term" active length "is to be understood as the length that is decisive for thermal expansion For this purpose, according to the further embodiment of the invention, alloyed steels are used as metallic materials for the pedal holder
3098ΛΑ/05413098ΛΑ / 0541
-8--8th-
-8-Zusammensetzung -8 composition
18 $, Chrom 8 $> Nickel $ 18, chrome $ 8> nickel
bis 0,12 c/o Kohlenstoff bis 2 i» Mangan bis 1 io Silicium Rest Eisen,up to 0.12 c / o carbon up to 2 % manganese up to 1 % silicon, remainder iron,
vorgesehen, deren Ausdehnungskoeffizient 15 bisprovided, whose coefficient of expansion is 15 to
-6 ο -1-6 ο -1
16 χ 10 .0 beträgt. Ferner legierte Stähle der Zusammensetzung 16 χ 10 .0. Also alloy steels of the composition
22 io Nickel 3 io Chrom bisO,12^ Kohlenstoff " 2 io Mangan22 io nickel 3 io chromium bisO, 12 ^ carbon "2 io manganese
11 1 io Silicium Rest Eisen, 11 1 io silicon remainder iron,
-6 ο -T die einen Ausdehnungskoeffizienten von etwa 18 χ 10 besitzen. Schließlich werden für die Federhalterungen als metallischer Werkstoff legierte Stähle der Zusammensetzung-6 ο -T which has a coefficient of expansion of about 18 χ 10 own. Finally, alloy steels of the composition are used as the metallic material for the spring holders
mit einem Ausdehnungskoeffizienten von 18 bis 20 χ 10"" . C" verwendet.with an expansion coefficient of 18 to 20 χ 10 "". C " used.
In jedem Falle sind jedoch die Ausdehnungskoeffizienten des Werkstoffs der Federhalterung auf den Ausdehnungskoeffizienten des erfindungsgemäss zu verwendenden Werkstoffs für die Lochblende abzustimmen.In any case, however, the expansion coefficients of the material of the spring holder are related to the expansion coefficient to match the material to be used according to the invention for the perforated diaphragm.
—9— 309844/0541 -9- 309844/0541
Die erfindungsgemässe Lochblende weist eine Reihe, von Vorteilen auf. Da die Aufwärmung der lochblende während des Betriebes der Farbbildröhre praktisch keine Ausdehnung bzw. Verschiebung der Löcher des Blendenblechs bewirkt, entfallen zusätzliche Regeleinrichtungen mit Iherraobiinetall-Regelelementen. Die erfindungsgemässen Lochblendenbleche haben den Vorteil, daß eine solche Lochblende sich partiell und örtlich auf verschiedener Temperatur befinden kann, ohne daß dadurch ,die Lage der einzelnen Löcher zueinander und in Bezug auf die leuchtpunkte auf dem Leuchtschirm verändert wird. Die erfindungsgemässe Lochblende aus Bisen/JTickel-Legierungen hat neben der geringen thermischen Ausdehnung im Bereich von 20 bis 800C ebenfalls den Vorteil der ferromagnetischen Eigenschaften wie die unlegierten-Stähle.The perforated diaphragm according to the invention has a number of advantages. Since the heating of the perforated screen during operation of the color picture tube practically does not cause any expansion or displacement of the holes in the screen plate, additional control devices with Herraobiinetall control elements are not required. The perforated plates according to the invention have the advantage that such a perforated plate can be partially and locally at different temperatures without changing the position of the individual holes in relation to one another and in relation to the luminous points on the luminescent screen. Has the inventive perforated diaphragm from Bisen / JTickel alloys in addition to low thermal expansion in the range of 20 to 80 0 C also has the advantage of the ferromagnetic properties as the non-alloyed steels.
Sie ist daher zur magnetischen Absehirmung der Röhre bestens geeignet. Obwohl die Sättigungsmagnetisierung von den erfindungsgemäss zu verwendenden Eisen/Nickel-Legierungen mit etwa 12 bis 13 kG niedriger ist im Vergleich zu unlegiertem Stahl mit 21,5 kG, ist die Maximalpermeabilität der Eisen/ Nickel-Legierungen ( /u max 6000 - 16 000 G . Oe" ) deutlich höher als di-a von unlegiertem Stahl ( Ai max 7000-8000 G. Oe" ) und die Korzitivfeidstärke mit Ηί»0,2 Oe deutlich niedriger als die von unlegiertem Stahl mit H 0,5 bis 1,5 Oe. Schließlich besitzen auch die erfindungsgeinäß einzusetzendenIt is therefore ideally suited for magnetic shielding of the tube. Although the saturation magnetization of the iron / nickel alloys to be used according to the invention is lower with about 12 to 13 kG compared to unalloyed steel with 21.5 kG, the maximum permeability of the iron / nickel alloys is (/ u max 6000 - 16,000 G . Oe ") significantly higher than di-a of unalloyed steel ( Ai max 7000-8000 G. Oe") and the corcitive field strength of Ηί »0.2 Oe is significantly lower than that of unalloyed steel with H 0.5 to 1.5 Oe. Finally, those to be used according to the invention also have
Werkstoffe für die Lochblende mit 45-80 kp/ram eine höhere Festigkeit als der Werkstoff unlegierter Stahl mitMaterials for the perforated diaphragm with 45-80 kp / ram a higher one Strength than the material unalloyed steel with
30 - 40 kp/mm für herkömmliche Lochblenden.30 - 40 kp / mm for conventional pinhole diaphragms.
-10--10-
309844/0541309844/0541
Claims (8)
O /οQ of
O / ο