DE2026553A1

DE2026553A1 - V-belt - with increased form stability at high - working temps

Info

Publication number: DE2026553A1
Application number: DE19702026553
Authority: DE
Inventors: Willfned Dipl Chem Dr rer nat 3000 Hannover Eckelmann
Original assignee: Continental Gummi Werke AG 3000 Hannover
Priority date: 1970-05-30
Filing date: 1970-05-30
Publication date: 1971-12-16

Abstract

The belt consists of rubber, or rubber-like synthetics, with a longitudinal tensile cord, and at least one transverse intermediate layer of a relatively hard rubber - or synthetic mixture which at the max. working temp. has a hardness of at least 75 degrees. Shore A, and pref. 85-95 degrees Shore A. Pref., the mixture contains thermoplastic or duromer components, which do not soften at the working temp. It also contains precondensates and/or prepolymers which harden to duromers at the vulcanisation temp. esp. P-F condensate. The V-belt has high form stability, transverse rigidity, and good flexibility in the running direction.

Description

Keilriemen Die Erfindung bezieht si.ch auf Keilriemen aus Gummi oder gummielastischen Kunststoffen mit mindestens einem in Längsrichtung durchlaufenden Zugstrang und mindestens einer über die gesamte oder nahezu die gesamte Querschnittsbreite parallel zu den ungleichen Seiten des Keilriemenquerschnittes sich erstreckenden Zwischenschicht aus einer vergleichsweise hart eingestellten Gummi- oder Kunststoffmischung. V-belts The invention relates to V-belts made of rubber or si.ch. rubber-elastic plastics with at least one continuous in the longitudinal direction Tensile cord and at least one over the entire or almost the entire cross-sectional width extending parallel to the unequal sides of the V-belt cross-section Intermediate layer made of a comparatively hard rubber or plastic mixture.

Im Gegensatz zu Flachriemen unterliegen Keilriemen beim Umlauf um die Riemenabschnitte in den Keilnuten, in die sie unter der Wirkung der übertragenen Zugkräfte eingezogen werden, einer Flankenpressung, die sie in Querrichtung durchzubiegen sucht. In contrast to flat belts, V-belts are subject to rotation the belt sections in the keyways into which they are transferred under the action of Tensile forces are drawn in, a flank pressure that they bend in the transverse direction seeks.

Die Gefahr solcher auf die Lebensdauer der Keilriemen sich ungünstig auswirkender Verformungen besteht in besonderem Maße bei Riemen mit im Verhältnis zur Breite niedriger Querschnittshöhe, wie sie beispielsweise als sogenannte Breitkeilriemen für Regelgetriebe mit axial verschiebbaren Keilscheibenpaaren Verwendung finden. Es ist bekannt, die Keilriemen durch Einlagerung von quer zur Laufrichtung ausgerichteten Faserschichten, versteifend wirkenden Geweben oder im Vergleich zu dem umgebenden elastomeren Riemenwerkstoff hart eingestellten Zwischenschichten gegen unerwünschte Formänderungen zu stabilisieren. The risk of such on the life of the V-belt is unfavorable deformations that have an effect are particularly evident in belts with in proportion to the width of low cross-sectional height, such as so-called wide V-belts for variable speed gearboxes with axially displaceable pairs of wedge disks. It is known to fasten the V-belts by storing them transversely to the running direction Fiber layers, stiffening fabrics or compared to the surrounding ones elastomeric belt material hard adjusted intermediate layers against undesired To stabilize changes in shape.

Bei der Anbringung derartiger Stabilisierungsschichten war man darauf bedacht, diese Schichten in oder in der Nähe der neutralen Zone des Keilriemens anzubringen, weil sich m anderen Falle Zerstörungserscheinungen innerhalb dieser Schichten bemerkbar machten. The application of such stabilization layers was a concern careful to place these layers in or near the neutral zone of the V-belt to be attached because in the other case there are signs of destruction within this Making layers noticeable.

Andererseits konnten derartige Stabilisierungsschichten die Auf gabe nur teilweise lösen, da bei steigender Temperatur innerhalb des Keilriemens die Härte dieser Schichten abnahm und sie damit unwirksam wurden. On the other hand, such stabilization layers could do the job loosen only partially, as the temperature inside the V-belt increases The hardness of these layers decreased and they became ineffective.

Die Erfindung hat sich die Aufgabe gestellt, die geschilderten wach teile zu vermeiden und die E'ormbeständigkeit der Keilriemen auch bei höheren, während des Keilriemenlaufes auftretenden remperaturen. zu gewährleisten.The invention has set itself the task of awake the described parts to avoid and the E'ormbindigkeit of the V-belt even at higher, while the temperatures occurring during the V-belt run. to ensure.

Die Erfindung sieht bei Keilriemen der eingangs genannten Gattung vor, daß innerhalb des Keilriemenkörpers, vorzugsweise parallel zu den ungleichen Seiten des Keilriemens wenigstens eine Schicht aus Mischungen auf der Grundlage von Gummi oder gummiähnlichen Kunst-.The invention provides for V-belts of the type mentioned at the beginning before that within the V-belt body, preferably parallel to the unequal Sides of the V-belt at least one layer of mixtures on the basis of rubber or rubber-like art.

stoffen angeordnet ist, die bei der maximalen Beanspruchungstempe ratur des Keilriemene eine Härte von mehr als 60, vorzugsweise mehr als 90° Shore A aufweist.materials is arranged at the maximum stress temperature Temperature of the V-belt has a hardness of more than 60, preferably more than 90 ° Shore A.

Die Erfindung geht von der überraschenden Erkenntnis aus, daß eine oder mehrere innerhalb des Keilriemenquerschnittes angeordnete quersteife Schichten hoher Härte während des Keilriemenlaufes dann nicht zerstört werden oder gar auf die Hüllechichten des Keilriemens zerstörend wirken, auch wenn sie nicht in der neutralen Zone angeordnet sind, wenn ihre Härte durch die auftretenden Temperaturen nicht über ein Mindestmaß hinaus verringert wird0 Diese Erscheinung kann damit erklärt werden, daß Relativbewegungen zwischen harten und weichen Schichten während des Laufes nicht auftreten, wenn die Elastizitätsmoduli, die im wesentlichen auch von der Härte abhängig sind, der aneinander angrenzenden Schichten eine ausreichend große Differenz aufweisen.The invention is based on the surprising finding that a or several transversely rigid layers arranged within the V-belt cross-section high hardness during the V-belt run are then not destroyed or even on the envelope layers of the V-belt have a destructive effect, even if they are not in the neutral zone are arranged when their hardness due to the temperatures occurring is not reduced beyond a minimum0 This phenomenon can thus be explained that relative movements between hard and soft layers during the Running does not occur when the moduli of elasticity, which are also essentially of the hardness of the adjacent layers are sufficient have a large difference.

Treten im Keilriemen Beanspruchungstemperaturen auf, die unter etwa 60° C liegen, so können zur Erzielung der gewünschten Härte thermoplastische Polymere mit Erweichungspunkten oberhalb 60° C, wie.z. B.If stress temperatures occur in the V-belt that are below approx 60 ° C, thermoplastic polymers can be used to achieve the desired hardness with softening points above 60 ° C, such as B.

Polystyrol und/oder hochstyrolhaltige Butadien-Styrol»Mischpolymerisate mit Styrolanteilen oberhalb 35 %, vorzugsweise oberhalb 70 % verwendet werden.Polystyrene and / or high styrene butadiene-styrene copolymers can be used with styrene contents above 35%, preferably above 70%.

Mischungen auf die-ser Grundlage weisen auch bei Temperaturen um 60° noch keinen nennenswerten Härteabfall auf, während sie allerdings im Bereich oberhalb 80° bereits Härteverluste um mehr als 25° der Shore-Härte-Skala A erkennen lassen und deswegen in diesen Temperaturbereichen weniger geeignet sind.Mixtures on this basis also show at temperatures around 60 ° still no noticeable drop in hardness, while it does, however, in the area above 80 ° already show a hardness loss of more than 25 ° on the Shore hardness scale A. and are therefore less suitable in these temperature ranges.

Es wurde gefunden, daß über einen weiten Temperaturbereich eine ausreichende Härte dann erzielt werden kann, wenn der Kautschu.kmischung vorzugsweise noch in der flüssigen Phase vorliegende, härtbare duromere ilarze, vorzugsweise Phenolharze zugemischt werden, die bei der Vulkanisation des Keilriemens irreversibel erhärten und den versteifenden Schichten eine Härtekonstanz bis etwa 150° C verleihen. Der an derartigen Kautschukmischungen gemessene Verlust des Elastizitätsmoduls im Temperaturbereich zwischen 0 und 5200 beträgt annähernd 15 bis 20 °, aie absoluten Werte des Elastizitätsmoduls liegen innerhalb dieses Bereiches auf etwa dem Drei- bis Vierfachen des Elastizitätsmoduls herkömmlicher Kautschukmischungen Die Erfindung schafft eine Keilriemenkonstruktion, die sich bei hoher Formbeständigkeit und Quersteifigkeit durch gute Biegsamkeit in Laufrichtung auszeichnet, besonders dann, wenn die Zwischenschichten mit in UmfangsrIchtung aufeinanderfolgenden Wellungen ausgebildet werden.It has been found that a sufficient temperature range over a wide temperature range Hardness can then be achieved if the rubber mixture is preferably still in curable thermoset resins, preferably phenolic resins, present in the liquid phase are added, which harden irreversibly during the vulcanization of the V-belt and give the stiffening layers a hardness constancy of up to about 150 ° C. Of the Loss of the modulus of elasticity measured on such rubber compounds in the temperature range between 0 and 5200 is approximately 15 to 20 °, the absolute values of the modulus of elasticity lie within this range to about three to four times the modulus of elasticity conventional rubber compounds The invention creates a V-belt construction, which is characterized by good flexibility with high dimensional stability and transverse rigidity in the running direction, especially when the intermediate layers with in the circumferential direction successive corrugations are formed.

Die quersteifen Zwischenschichten können an beliebiger Stelle innerhalb des Keilriemenkörpers angeordnet werden. Ihre Lage relativ zum Zugstrang ist für das Zustandekommen der vorteilhaften Wirkungen ebenfalls ohne Bedeutung. Sie können beispielsweise in der Nähe des Zugatranges angeordnet sein, sie können aber auch, ohne vom Grundgedanken der Erfindung abzuweichen, beispielsweise in cder in der Nähe der Keilriemenschmalseite angeordnet sein.The transversely stiff intermediate layers can be placed anywhere within of the V-belt body are arranged. Their location relative to the tension cord is for the occurrence of the beneficial effects is also irrelevant. You can be arranged, for example, near the access range, but they can also without deviating from the basic idea of the invention, for example in cder in Be arranged near the V-belt narrow side.

Die Erfindung ist nicht an die Verwendung eines Unmantelungsgewebes gebunden, sondern ist sowohl für ummantelte wie auch für sogenannte flankenoffene Keilriemen gleich gut zu verwirklichen. Es bestehen auch keine irgendwie gearteten Einschränkungen hinsichtlich des übrigen Riemenaufbaues, sei es im Zusammenha-ng mit der Form und Dimensionierung des Riemenquerschnittes und der Einformung oder Binarbeitung von Quernuten am Innenumfang oder in der Konstruktion und Zuordnung der einzelnen Aufbaukomponenten zueinander.The invention is not limited to the use of a jacketed fabric tied, but is for both sheathed and so-called open-flanked Realize V-belts equally well. There are also none of any kind Restrictions regarding the rest of the belt structure, be it in context with the shape and dimensioning of the belt cross-section and the indentation or Processing of transverse grooves on the inner circumference or in the design and assignment of the individual structural components to each other.

Der Mischungsaufbau der erfindungsgemäßen quersteifen Verstärkungsschichten ist nicht an die Verwendung eines bestimmten Polymers gebunden. Neben Naturkautschuk können auch andere Polymere wie z. B.The mixture structure of the transversely rigid reinforcement layers according to the invention is not tied to the use of a specific polymer. In addition to natural rubber can also use other polymers such. B.

Chlor-Butadien-Kautschuk, Butadien-Acrylnitril-Copolymerisate oder ähnliche Polymere bzw. deren Verschnitte verwendet werden.Chlorine-butadiene rubber, butadiene-acrylonitrile copolymers or similar polymers or their blends are used.

Sollen Kautschukmischungen mit einer Formbeständigkeit hinsichtlich der Quersteifigkeit bei 120 bis 140° C verwendet werden, so wird man bevorzugt Mischungen etwa folgenden Aufbaues verwenden: Gewichtsteile Naturkautschuk 100,-Alterungsschutzmittel 1,-Klebrigmacher 1,-Stearinsäure 3,5 Zinkoxid 5,-RuB 70,-Härtbares Phenolformaldehydharz 50,-Schwefel 2,7 beschleuniger 0,7 233,9 Eine Kautschukmischung dieses Aufbaues weist die folgenden physikalischen Eigenschaftswerte auf (Heizung 40' : 1340 C): Festigkeit nach DIN 53504 135 kp/cm2 Dehnung nach DIN 53504 160 % Härte Shore A nach DIN 53505 bei Raumtemperatur 95 bei 100 C 93 E-Modul nach DIN 53513 bei 230 C 1200 kp/cm2 bei 1000 C 1100 kp/cm Dämpfung (%) bei 230 C DIN 53513 23 bei 1000 C 18 Für Beanspruchungstemperaturen bis etwa 600 C kann eine Kautschukmischung etwa folgenden Aufbaues verwendet werden (40' : 134 C): Gewichtsteile Naturkautschuk 70,-Styrol/Butadion-Kautschuk (60% Styrol) 30,-Alterungsschutzmittel 1,-Klebrigmacher 1,-Stearinsäure 3,5 Zinkoxid 5,-Ruß 70 Weichmacher 7,-Schwefel 2,7 Beschleuniger 0,7 190,9 Eine Kautschukmischung dieses Aufbaues weist die folgenden physikalischen Eigenschaftswerte auf (Heizung 40 : 1340 C): Festigkeit nach DIN 53504 145 kp/cm2 Dehnung nach DIN 53504 200 % Härte Shore A nach DIN 53505 bei Raumtemperatur 95 bei 1000 C 73 E-Modul nach DIN 53513 bei 200 q 1200 kp/cm2 bei 1000 G 100 kp/cm2 Dämpfung (%) bei 200 C DIN 53513 19 bei 1000 C 35 Zur Verdeutlichung der Erfindung sind in der Zeichnung verschiedene Ausführungsbeispiele für den konstruktiven Aufbau der erfindungsgemäßen Keilriemen dargestellt. Es zeigen: Fig. 1 - 4 Teilstücke erfindungagemäßer Keilriemen in perspektivischer Ansicht, Fig. 5 - 6 zwei Gestaltungsmöglichkeiten der für die erfindungsgemäßen Keilriemen geeig- in perspektivischer Ansicht.If rubber mixtures with dimensional stability in terms of transverse rigidity at 120 to 140 ° C are to be used, mixtures of about the following structure will preferably be used: parts by weight of natural rubber 100, anti-aging agent 1, tackifier 1, stearic acid 3.5, zinc oxide 5, -RuB 70 , -Hardenable phenol-formaldehyde resin 50, -Sulfur 2.7 accelerator 0.7 233.9 A rubber mixture of this structure has the following physical property values (heating 40 ': 1340 C): strength according to DIN 53504 135 kp / cm2 elongation according to DIN 53504 160 % Shore A hardness according to DIN 53505 at room temperature 95 at 100 C 93 E-module according to DIN 53513 at 230 C 1200 kp / cm2 at 1000 C 1100 kp / cm Damping (%) at 230 C DIN 53513 23 at 1000 C 18 For exposure temperatures Up to about 600 C, a rubber mixture of the following structure can be used (40 ': 134 C): Parts by weight of natural rubber 70, -styrene / butadione rubber (60% styrene) 30, -age inhibitor 1, -tackifier 1, -steari acid 3.5 zinc oxide 5 carbon black 70 plasticizer 7 sulfur 2.7 accelerator 0.7 190.9 A rubber mixture of this structure has the following physical property values (heating 40: 1340 C): strength according to DIN 53504 145 kp / cm2 elongation according to DIN 53504 200% Shore A hardness according to DIN 53505 at room temperature 95 at 1000 C 73 E-module according to DIN 53513 at 200 q 1200 kp / cm2 at 1000 G 100 kp / cm2 damping (%) at 200 C DIN 53513 19 at 1000 C 35 To illustrate the invention, various exemplary embodiments for the structural design of the V-belts according to the invention are shown in the drawing. 1 to 4 parts of the V-belts according to the invention in perspective view, FIGS. in perspective view.

Es sei darauf hingewiesen, daß die Erfindung keineswegs an die Verwendung von Wellungen oder dgl., wie in Fig. 5 und 6 dargestellt, gebunden ist, vielmehr können Schichten des erfindungsgemäßen Aufbaues auch ungewellt verwendet werden, insbesondere dann, wenn sie in der Nähe der neutralen Zone des Keilriemens angeordnet sind, wie dies für die Schichten 1 der Fig. 1 und 2 dargestellt ist.It should be noted that the invention is in no way intended to be used of corrugations or the like. As shown in Fig. 5 and 6, is bound, rather layers of the structure according to the invention can also be used without corrugation, especially if they are located near the neutral zone of the V-belt are as shown for layers 1 of FIGS.

Der in Fig. 1 dargestellte Keilriemen besteht in seinem Grundkörper 2 aus einer vulkanisierten Kautschukmischung auf der Grundlage von Natur- und/oder Synthesekautschuken in vergleichsweise weicher Härte einstellung mit trapezförmigem Querschnitt, in dessen neutraler Biegezone eine erfindungsgemäß aufgebaute, durch einen Gehalt an während der Vulkanisation erhärtenden Phenolharzen hart eingestellte Schicht 1 angeordnet ist1 in die eine Vielzahl berührungsfrei nebeneinander in Längsrichtung endlos durchlaufender mono- oder multiphiler Kunststoffäden 3 als Zugträger eingebuttet sind. Die Härte des für den Grundkörper verwendeten Gummis liegt bei Raumtemperatur bei etwa 70° Shore 1, die Kautschukmischung für die Zwischenschicht 1 entspricht in ihrem Mischungs- und Eigenschaftsaufbau der entsprechenden eingangs näher beschriebenen Kautschukmischung.The V-belt shown in Fig. 1 consists in its base body 2 from a vulcanized rubber mixture based on natural and / or Synthetic rubbers with a comparatively soft hardness setting with a trapezoidal one Cross-section, in the neutral bending zone of which a constructed according to the invention, through hard set a content of phenolic resins hardening during vulcanization Layer 1 is arranged1 in which a plurality of contact-free side by side in the longitudinal direction endlessly running monophile or multiple plastic threads 3 embedded as tension members are. The hardness of the rubber used for the base body is room temperature at about 70 ° Shore 1, which corresponds to the rubber mixture for the intermediate layer 1 in their mix and property structure of the corresponding initially described in more detail Rubber compound.

In dem Ausführungsbeispiel nach Fig. 2 sind mehrere quersteife Zwischenschichten,1, 4 in den Grundkörper 2 derart eingebettet, daß die offenen Flanken der quersteifen Schichten; 1, 4 von der Gummimischung des Grundkörpers abgedeckt sin*. Einer solchen Ausführungsform wird besonders dann der Vorzug gegeben werden, wenn die: Zwischenschichten t, 4 mi Rücksicht auf die Einstellung der gewünschten Quersteifigkeit Stoffe enthalten, die unter den Betriebseinflüssen, sei es durch Quellung, wie dies beispeilsweise bei Berührung mi Schmierölen und dgl. geschehen kann, sei es durch andere korrodierende Einflüsse, beeinträchtigt werden könnten. Zu einer derartigen Ausführungsform wirdPman dann greifen, wenn die zur den Grundkörper verwendete Gummimischung gegen diese äußeren Einflüsse beständiger ist oder beständiger gestaltet werden kann-als dies für die Art der Zwischenschicht der Fall ist.In the embodiment according to FIG. 2, several transversely rigid intermediate layers, 1, 4 embedded in the base body 2 in such a way that the open flanks of the transverse stiffeners Layers; 1, 4 covered by the rubber compound of the base body are *. One such Embodiment is particularly preferred when: the intermediate layers t, 4 mi contain substances in consideration of the setting of the desired transverse stiffness, those under the operational influences, be it due to swelling, as is the case for example can happen on contact with lubricating oils and the like, be it by other corrosive ones Influences that could be impaired. One such embodiment becomes Pman then grab when the rubber compound used for the base body against this external influences is or can be made more permanent than this for the type of interlayer is the case.

Durch die zusätzlich angebrachten quersteifen Zwischenschichten 4 in der ähe der ungleichen Seiten des Keilriemens wird die Quersteifig keit über den gesamten Riemenquerschnitt verbessert.Due to the additionally attached transversely stiff intermediate layers 4 near the unequal sides of the V-belt, the transverse stiffness is over the entire belt cross-section improved.

In besonders vorteilhafter Ausführungsform der Erfindung werden die Zwischenschichten 4 als Wellbänder gemäß Fig. 6 ausgebildet. Der gesamte Keilquerschnitt des fertig aufgebauten Riemens ist ton einem ihn umschließenden Unmantelungsgewebe 8 in an sich bekannter Weise umgeben.In a particularly advantageous embodiment of the invention, the Intermediate layers 4 designed as corrugated tapes according to FIG. 6. The entire cross-section of the wedge the fully assembled belt is toned in a non-sheathing fabric that surrounds it 8 surrounded in a manner known per se.

Der in Fig. 3 gezeichnete Keilriemen besteht in seinem Grundkörper 5 aus einem unter Verwendung von natürlichen oder auf synthetischem Wege hergestellten Polymeren aufgebauten vulkanisierten Gummi in vergleichsweise weicher Härteeinstellung mit trapezförmigem Querschnitt und enthält als zugkraftübertragende Elemente in dem Bereich seiner neutralen Biegezone eine Vielzahl berührungsfrei nebeneinander in Langsrichtullg endlos durchlaufender Drahtseile 6. In die Querschnittsteile ober- und unterhalb der Drahtseile 6 sind in Form gewellter Bänder aus einer erfindungsgemäßen Gummimischung hergestellte Zwischenschichten 7 mit haftender Bindung zu dem Füllgummi des Grundkörpers 5 eingebettet. Die Zwischenschichten erstrecken sich beide jeweils über die gesamte Breite des Keilquerschnitts und treten mit den Seitenflächen der Keilnuten in den nicht gezeichneten Riemenscheiben in unmittelbare Berührung, so daß der Grundkörper 5 selbst von der Flankenpressung entlastet ist. Der wellenförmige Verlauf der Seitenkanten beider Zwischenschichten zeichnet sich an den freiliegenden Riemenflanken ab, wie dies in der Zeichnung zum Ausdruck gebracht ist.The V-belt shown in Fig. 3 consists in its base body 5 from a manufactured using natural or synthetic means Vulcanized rubber made up of polymers with a comparatively soft hardness setting with a trapezoidal cross-section and contains in In the area of its neutral bending zone, a large number of them contact-free next to one another in the longitudinal direction of endless wire ropes 6. In the cross-sectional parts above and below the wire ropes 6 are in the form of corrugated tapes made of an inventive Intermediate layers 7 produced by a rubber mixture with an adhesive bond to the filling rubber of the base body 5 embedded. The intermediate layers both extend, respectively over the entire width of the wedge cross-section and connect with the side surfaces of the Keyways in the pulleys (not shown) in direct contact, so that the base body 5 itself is relieved of the flank pressure. The wavy one The course of the side edges of both intermediate layers can be seen on the exposed ones Belt flanks off, as shown in the drawing.

In dem Ausführungsbeispiel gemäß Fig. 4 sind die das Zugband bildenden Drahtseile 6 in dem der längeren Parallelseite zugeordneten Randbereich untergebracht, während der übrige Teil des Reilquerschnittes drei in angemessenen Abständen übereinander angeordnete Zwischenschichten 7 erfindungsgemäßen Aufbaues aufweist. Die Zwischenschiehten können ebenfalls als Wellenbänder gemäß der Darstellung in Fig. 3 ausgebildet sein.In the exemplary embodiment according to FIG. 4, those forming the tension band are Wire ropes 6 housed in the edge area assigned to the longer parallel side, while the remaining part of the reed cross-section three at appropriate intervals one above the other having arranged intermediate layers 7 structure according to the invention. The in between can also be designed as wavebands as shown in FIG. 3.

Andere Gestaltungsmöglic}keiten sind in Fig. 5 bis 6 angedeutet: Im einen Falle als Bänder einseitig wechselnder Schichtdicke oder im anderen Falle mit symmetrisch nach Art einer Perlschnur aufeinanderfolgenden Verdickungen. Der fertig aufgebaute Riemen ist von einem den gesamten Keilquerschnitt umschließenden Ummantelungsgewebe 8 umgeben.Other design possibilities are indicated in FIGS. 5 to 6: Im a Fall as bands of one-sided changing layer thickness or in the other case with symmetrical successive thickenings like a string of pearls. The finished one The belt is made of a sheathing fabric that surrounds the entire cross-section of the wedge 8 surrounded.

Claims

Patent claims:

1. V-belts made of rubber or rubber-like plastics with a in the longitudinal direction continuous tensile cord and at least one transversely to the belt extending intermediate layer made of a comparatively hard set rubber or plastic mixture, characterized in that the rubber or plastic mixture the intermediate layers (7) have a Shore hardness at the maximum stress temperature of at least 75 Shore A, preferably 85 to 950 Shore A.

2. V-belt according to claim 1, characterized in that the rubber mixture Thermoplastic or thermosetting materials that do not soften at the exposure temperature Contains ingredients.

3. V-belt according to Claims 1 and 2, characterized in that for exposure temperatures up to about 600 C the rubber mixture polystyrene or high styrene copolymers of butadiene and styrene with a styrene content of more than 35%, preferably more than 70 ffi.

4. V-belt according to Claims 1 and 2, characterized in that the rubber mixture preferably at the vulcanization temperature to form thermosets Contains hardening precondensates and / or prepolymers.

5. V-belt according to claim 4, characterized in that the rubber mixture Phenol-formaldehyde condensates that preferably harden at vulcanization temperature contains.

6. V-belt according to Claims 4 and 5, characterized in that Liquid precondensates hardening the rubber mixture to form duromers in a proportion between 30 and 70, preferably 50 percent by weight, based on the polymer content the mixture, contains,

7. V-belt according to one or more of the Claims 1 to 6, characterized in that the intermediate layers (1, 4) in the Filler rubber (2) are embedded.

8. V-belt according to one or more of claims 1 to 6, characterized characterized in that the intermediate layers (1, 7) extend over the entire cross-sectional width extend.

9. V-belt according to claim 7 or 8, characterized in that The tension cord (3) of the V-belt is embedded in one of the intermediate layers (1) is.

10. V-belt according to claim 9, characterized in that the tension cord (3) in an intermediate layer lying in or near the neutral zone (1) is embedded.

11. V-belt according to one or more of the preceding claims, characterized in that at least one of the two surfaces of each intermediate layer (1, 4, 7) over the circumferential length changing distance from the unequal sides of the Has V-belt cross-section.

12. V-belt according to claim 11, characterized in that the with essentially constant layer thickness intermediate layers in Have successive corrugations in the circumferential direction.

13. V-belt according to claims 11 and 12, characterized in that that the intermediate layers are formed with a thickness that changes in the circumferential direction are.

14. V-belt according to claims 11 and 12, characterized in that that the intermediate layers have a different surface with respect to the stretched continuous surface have surface formed with corrugations following one another in the longitudinal direction.

15. V-belt according to claims 11 to 13, characterized in that that the intermediate layers follow one another in the longitudinal direction in the manner of a string of pearls mutually offset cross-sectional thickenings are formed.