DE19907212C2 - Stainless steel sink and process for its manufacture - Google Patents
Stainless steel sink and process for its manufactureInfo
- Publication number
- DE19907212C2 DE19907212C2 DE19907212A DE19907212A DE19907212C2 DE 19907212 C2 DE19907212 C2 DE 19907212C2 DE 19907212 A DE19907212 A DE 19907212A DE 19907212 A DE19907212 A DE 19907212A DE 19907212 C2 DE19907212 C2 DE 19907212C2
- Authority
- DE
- Germany
- Prior art keywords
- stainless steel
- sink
- hard chrome
- chrome plating
- steel sink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Revoked
Description
Die Erfindung betrifft eine Edelstahlspüle mit einem Spülbecken und einem um das Spülbecken umlaufenden Rand, welcher mit einem Beckenboden des Spülbeckens über eine umlaufende Seitenwand verbunden ist. Die Erfindung betrifft weiterhin ein Verfahren zur Herstellung einer Edelstahlspüle.The invention relates to a stainless steel sink with a sink and a rim running around the sink, which with a Basin floor of the sink over a circumferential side wall connected is. The invention further relates to a method for the production of a stainless steel sink.
Edelstahlspülen sind vielfältig und zur hohen Zufriedenheit der Nutzer im Einsatz, da sie nicht nur über lange Zeit ihr gutes Aussehen behalten, sondern darüber hinaus auch extremen Bean spruchungen standhalten.Stainless steel sinks are varied and to the high satisfaction of Users in action, as they do their good not only for a long time Keep appearance, but also extreme bean withstand spells.
Die eingangs beschriebenen Edelstahlspülen sind beispielsweise aus der DE 44 25 764 C1 bekannt.The stainless steel sinks described at the beginning are, for example known from DE 44 25 764 C1.
In der DE 42 02 517 A1 wird empfohlen, Einbauspülen an den im Gebrauch stark beanspruchten Stellen mit einer Oberflächen struktur von geraden, parallel zueinander verlaufenden Riefen zu versehen.In DE 42 02 517 A1 it is recommended that built-in sinks on the in Use heavily used areas with a surface structure of straight, parallel grooves to provide.
Als nachteilig wird bei den Edelstahlspülen empfunden, daß diese nicht ausreichend schmutzabweisend sind und insbesondere durch die Bildung von Kalkflecken einen Teil ihrer ansonsten gegebenen Reinigungsfreundlichkeit einbüßen.A disadvantage of stainless steel sinks is that these are not sufficiently dirt-repellent and in particular due to the formation of limescale, part of their otherwise loss given the ease of cleaning.
Aufgabe der vorliegenden Erfindung ist es, eine Edelstahlspüle derart weiterzubilden, daß sie eine schmutzabweisende Oberflä che aufweist, die leichter zu reinigen ist. The object of the present invention is a stainless steel sink to develop such that they have a dirt-repellent surface surface that is easier to clean.
Diese Aufgabe wird bei der eingangs beschriebenen Edelstahlspü le erfindungsgemäß dadurch gelöst, daß die Edelstahlspüle auf ihrer Sichtseite eine schmutzabweisende Beschichtung in Form einer Hartverchromung aufweist.This task is the stainless steel sink described at the beginning le solved according to the invention in that the stainless steel sink a dirt-repellent coating in shape on its visible side hard chrome plating.
Die Hartverchromung von Edelstahl ist in der Literatur vielfäl tig beschrieben, und um nur ein Beispiel für die Vielzahl der geeigneten Hartverchromungsverfahren zu geben, wird auf das US- Patent Nr. 4,664,759 verwiesen.The hard chrome plating of stainless steel is diverse in the literature and just to give an example of the multitude of suitable hard chrome plating process is based on the US Patent No. 4,664,759.
Ebenfalls geeignete Verfahren sind z. B. aus Met. Finish. 1975, 43 unter dem Titel "Chromium Plating", Autor: Arthur Logozzo, und der dort zitierten Literatur bekannt.Suitable methods are e.g. B. from Met. Finish. 1975, 43 under the title "Chromium Plating", author: Arthur Logozzo, and the literature cited there.
Mit diesen Verfahren lassen sich exzellent an der Edelstahl oberfläche anhaftende Hartverchromungsschichten ausbilden, die auch im vorliegenden Fall geeignet sind.With these processes, the stainless steel can be excellently Form adhering hard chrome plating layers that are also suitable in the present case.
Überraschenderweise hat sich herausgestellt, daß Edelstahlspü len mit einer Hartverchromung auf ihrer Sichtseite besonders schmutzabweisend sind, d. h. die Sichtseite läßt sich wesent lich einfacher reinigen, insbesondere auch dann, wenn sich auf der Oberfläche durch Antrocknen von Wasserresten Kalkflecken gebildet haben.Surprisingly, it has been found that stainless steel rinsing len with hard chrome plating on their visible side are dirt-repellent, d. H. the visible side can be essential Lich easier to clean, especially when it is on limescale spots on the surface by drying water residues have formed.
Bei einer besonders bevorzugten erfindungsgemäßen Edelstahlspü le ist die Hartverchromung kalkabweisend ausgebildet, was eine besonders glatte Oberfläche der Hartverchromungsbeschichtung voraussetzt. Solche Oberflächen sind z. B. mit dem Verfahren gemäß dem oben zitierten US-Patent erhältlich.In a particularly preferred stainless steel sink according to the invention The hard chrome plating is lime-repellent, which is a particularly smooth surface of the hard chrome plating assumes. Such surfaces are e.g. B. with the method available in accordance with the U.S. patent cited above.
Besonders bevorzugte Edelstahlspülen weisen eine Hartverchro mung auf, die aufgrund ihrer glatten Oberfläche sehr leicht me chanisch gereinigt werden kann, ohne daß dabei abrasive Reini gungsmittel zum Einsatz kommen müssen. Somit lassen sich bei solchen Spülen auch Kalkflecken durch Abwischen entfernen, die sonst entweder nur durch abrasive oder chemisch kalklösende Reinigungsmittel entfernbar waren. Die Reinigung und Erhaltung der Spüle in ihrem ursprünglichen Aussehen ist dadurch sehr stark vereinfacht. Particularly preferred stainless steel sinks have a hard chrome due to its smooth surface can be cleaned mechanically without abrasive cleaning agents must be used. Thus, at such sinks also remove lime stains by wiping the otherwise either only by abrasive or chemical limescale remover Detergents were removable. Cleaning and conservation the sink in its original appearance is very nice greatly simplified.
Da die Hartverchromung der Sichtseite gleichzeitig einen zu sätzlichen Kratzschutz für die Edelstahlspüle bedeutet, wird die Hartverchromung bevorzugt im Bereich des Beckenbodens ge genüber beispielsweise den Bereichen des umlaufenden Randes um mindestens 20% dicker gewählt.Since the hard chrome plating on the visible side also closes one means additional scratch protection for the stainless steel sink hard chrome plating is preferred in the area of the pelvic floor compared to, for example, the areas of the peripheral edge chosen at least 20% thicker.
Die neben dem Beckenboden besonders kratzgefährdeten weiteren Oberflächenbereiche im Bereich der umlaufenden Seitenwand wer den bei einer weiter bevorzugten Ausführungsform ebenfalls mit einer um mindestens 20% größeren Dicke ausgeführt.The other ones particularly prone to scratching next to the pelvic floor Surface areas in the area of the peripheral side wall which also in a further preferred embodiment a thickness that is at least 20% greater.
Schließlich betrifft die Erfindung auch Edelstahlspülen, welche eine an das Spülbecken angeformte Abtropffläche aufweisen, wo bei dann der umlaufende Rand sowohl um das Spülbecken als auch um die angeformte Abtropffläche umläuft. Bevorzugte Edelstahl spülen weisen auch auf der Abtropffläche eine um mindestens 20% größere Dicke der Hartverchromung auf als in den Bereichen des umlaufenden Randes.Finally, the invention also relates to stainless steel sinks, which have a drainer molded onto the sink where then the peripheral edge around both the sink and around the molded drainer. Preferred stainless steel Rinses also have at least one drainer on the drainer Hard chrome plating 20% thicker than in the areas of the peripheral edge.
Die höhere Schichtdicke der Hartverchromung in den ausgewählten Oberflächenbereichen der Edelstahlspüle läßt sich relativ ein fach dadurch bewirken, daß bei dem elektrolytischen Verchro mungsschritt die Elektroden so gestaltet werden, daß in den Be reichen, die eine höhere Schichtdicke verlangen, die Stromdich te während der Elektrolyse höher ausfällt. Dies kann beispiels weise durch die Wahl eines geringeren Abstandes der Elektrode zu diesen Oberflächenbereichen geschehen.The higher layer thickness of the hard chrome plating in the selected Surface areas of the stainless steel sink can be relatively fold cause that in the electrolytic Verchro mung step the electrodes are designed so that in the loading range, which require a higher layer thickness, the current density higher during electrolysis. For example by choosing a smaller distance between the electrodes to happen to these surface areas.
Die Erfindung betrifft ferner ein Verfahren zur Herstellung der erfindungsgemäßen Spülen wie Anspruch 7 definiert.The invention further relates to a method for producing the sinks according to the invention as defined in claim 7.
Bei der Herstellung der erfindungsgemäßen Edelstahlspüle wird üblicherweise so vorgegangen, daß aus einem Edelstahlblech die Spüle durch Tiefziehen geformt, die Oberfläche der Sichtseite gebürstet und dann hartverchromt wird. In the manufacture of the stainless steel sink according to the invention usually proceeded so that the stainless steel sheet Sink formed by deep drawing, the surface of the visible side is brushed and then chrome-plated.
Alternativ kann die den Randbereich der Spüle und, falls vor handen, die Abtropffläche beinhaltende Abdeckung durch Tiefziehen oder Prägen geformt und je nach Spülentyp mit einem oder mehreren in einem getrennten Schritt tiefgezogenen Becken ver schweißt werden. Nach einer Bearbeitung der Sichtseite durch Bürsten wird diese dann hartverchromt.Alternatively, the edge area of the sink and, if in front cover the drainer by deep drawing or shaped and with one or depending on the type of sink several deep-drawn basins in a separate step be welded. After processing the visible side Brushing is then hard chrome-plated.
Bei einer weiter bevorzugten Ausführungsform der erfindungsge mäßen Edelstahlspüle weist die Sichtseite der Edelstahlspüle eine elektro-polierte Oberfläche auf, wobei die Politur (gege benenfalls alternativ zu dem Bürsten) vor der Hartverchromung durchgeführt wird.In a further preferred embodiment of the fiction The stainless steel sink shows the visible side of the stainless steel sink an electro-polished surface, the polish (against alternatively to brushing if necessary) before hard chrome plating is carried out.
Wird hingegen die Edelstahlspüle in gebürstetem Zustand, in dem ein sogenanntes Bürstbild an der Sichtseite erkennbar bleibt, hartverchromt, so bildet sich regelmäßig dieses Bürstbild auch bei der Hartverchromungsschicht ab.However, the stainless steel sink is in a brushed state, in which a so-called brush image remains visible on the visible side, hard chrome-plated, this brush pattern also forms regularly with the hard chrome plating layer.
Die Elektro-Politur der Sichtseite vor der Hartverchromung wird deshalb bei besonders bevorzugten Ausführungsformen so ausge führt, daß die hartverchromte Sichtseite der Spüle im wesentli chen bürstbildfrei ist.The electro-polish on the visible side before the hard chrome plating therefore in particularly preferred embodiments so out leads that the hard chromed visible side of the sink essentially chen is free of brushing.
Schließlich lassen sich mit der Hartverchromung noch optische Effekte an der Sichtseite erzielen, wobei die Hartverchromung vorzugsweise so durchgeführt wird, daß die Sichtseite einen hellblau bis stahlblau erscheinenden Schimmer aufweist.Finally, hard chrome plating can be used to create optical ones Achieve effects on the visible side, with the hard chrome plating is preferably carried out so that the visible side one light blue to steel blue shimmer.
Diese und weitere Vorteile der vorliegenden Erfindung werden im folgenden anhand der Zeichnung noch näher erläutert. Es zeigen im einzelnen:These and other advantages of the present invention are disclosed in following explained with reference to the drawing. Show it in detail:
Fig. 1: eine Draufsicht auf eine erfindungsgemäße Edelstahl spüle mit einer Hartverchromung; und Fig. 1: a plan view of a stainless steel sink according to the invention with a hard chrome plating; and
Fig. 2: eine Schnittansicht längs Linie 2-2 in Fig. 1. Fig. 2 is a sectional view taken along line 2-2 of Fig. 1.
Fig. 1 zeigt eine insgesamt mit dem Bezugszeichen 10 versehene Edelstahlspüle mit einem Spülbecken 12, einem Restebecken 14, einer Abtropffläche 16 sowie einem umlaufenden Rand 18. Die Becken 12 und 14 sind jeweils von einer umlaufenden Seitenwand 20 bzw. 22 umgeben und über diese mindestens stellenweise mit dem umlaufenden Rand 18 verbunden. Der umlaufende Rand 18 hat bei der in Fig. 1 gezeigten Edelstahlspüle eine unterschiedli che Breite und beinhaltet in einem Bereich 18a Durchbrüche 23, 24 für dort zu montierende Armaturen. Fig. 1 shows a generally denoted by reference numeral 10 stainless steel sink with a sink 12, a waste basin 14, a draining surface 16 and a peripheral edge 18. The basins 12 and 14 are each surrounded by a circumferential side wall 20 and 22 and at least in places connected to the circumferential edge 18 . The peripheral edge 18 has in the embodiment shown in FIG. 1, a stainless steel sink differing surface width in a range and includes 18 a apertures 23, 24 for there to be mounted faucets.
Gleichfalls eingeformt sind Ablauföffnungen 25, 26 und 27, die der Abtropffläche 16, dem Becken 12 bzw. dem Restebecken 14 zu geordnet sind.Drain openings 25 , 26 and 27 , which are assigned to the draining surface 16 , the basin 12 and the residual basin 14 , are also formed.
Bei der Herstellung der Spüle 10 wurde in einem ersten Schritt aus einem plattenförmigen Edelstahlmaterial durch Tiefziehen die sogenannte Abdeckung geformt, die neben der Abtropffläche 16 den Rand 18 beinhaltet. Die gesondert tiefgezogenen Becken 12 und 14 werden dann in einem zweiten Schritt in die Abdeckung eingeschweißt. Der fertige Spülenkörper wird auf der Sichtseite gebürstet und/oder elektro-poliert und erst dann in einem letz ten Schritt mit einer Beschichtung 28 aus Hartchrom versehen (in der Figur im einzelnen nicht dargestellt).In the manufacture of the sink 10 , the so-called cover was formed from a plate-shaped stainless steel material by deep drawing, which includes the edge 18 in addition to the draining surface 16 . The separately deep-drawn basins 12 and 14 are then welded into the cover in a second step. The finished sink body is brushed on the visible side and / or electro-polished and only then in a last step provided with a coating 28 made of hard chrome (not shown in the figure in detail).
Überraschenderweise zeigt sich, daß trotz der durch das Tief ziehen veränderten Mikrostruktur des Edelstahlmaterials, das insbesondere im Bereich des Beckenbodens von austenitisch in martensitisch wechselt, die Beschichtung schlagfest und gut haftend aufgebracht werden kann.Surprisingly, it turns out that despite the low pull modified microstructure of stainless steel material that especially in the area of the pelvic floor from austenitic in changes martensitic, the coating is impact-resistant and good can be applied by adhesive.
Bevorzugt wird im Bereich des Beckenbodens der Becken 12 und 14 sowie im Bereich der Abtropffläche 16, insbesondere an den Stellen der erhabenen ausgebildeten Bereiche, die Hartverchromung mit einer um mindestens ca. 20% größeren Dicke ausgeführt als in den restlichen Bereichen.Hard chromium plating with a thickness that is at least about 20% greater than in the remaining areas is preferably carried out in the area of the pool bottom of the pools 12 and 14 and in the area of the draining area 16 , in particular at the locations of the raised areas.
Ebenfalls empfehlenswert ist es, auch die Seitenwände 20 und 22 mit einer erhöhten Dicke der Hartverchromung zu beschichten.It is also advisable to coat the side walls 20 and 22 with an increased thickness of the hard chrome plating.
Bei Reinigungstests an den hartverchromten Spülen, verglichen mit den vorher vorhandenen gebürsteten oder elektro-polierten Edelstahlflächen, erweist sich, daß die hartverchromte Sicht seite der Spüle 10 nicht nur erheblich mehr schmutzabweisend ist, sondern auch, daß sich Kalkränder, die sich durch Ein trocknen von Wasserresten ergeben, erheblich leichter abge wischt werden können. In aller Regel lassen sich solche Kalk flecken durch bloßes Abwischen ohne die Verwendung von abra siven Reinigungsmaterialien und insbesondere auch ohne die Verwendung von chemisch anlösenden, sauren Reinigungsmitteln entfernen. Dadurch wird die Pflege der Edelstahlspüle und der Erhalt ihres ursprünglichen Aussehens wesentlich vereinfacht. Dies wirkt sich insbesondere beim intensiven Gebrauch dieser Spülen zeitsparend aus.In cleaning tests on the hard chrome-plated sinks, compared to the previously existing brushed or electro-polished stainless steel surfaces, it turns out that the hard chrome-plated side of the sink 10 is not only significantly more dirt-repellent, but also that there are limescale edges that can dry out Remaining water can be wiped off much more easily. As a rule, such lime stains can be removed by simply wiping them off without the use of abrasive cleaning materials and in particular also without the use of chemically dissolving, acidic cleaning agents. This significantly simplifies the maintenance of the stainless steel sink and the maintenance of its original appearance. This saves time, especially when these sinks are used intensively.
Claims (10)