DE1936234A1 - Coating chipboard surface finishing plates with - polytetrafluoro ethylene to reduce clogging of meshing of

Info

Publication number: DE1936234A1
Application number: DE19691936234
Authority: DE
Inventors: Hanselmayer Dipl-Ing Richard
Original assignee: WILHELM HOLZHAEUER ATEX
Current assignee: WILHELM HOLZHAEUER ATEX
Priority date: 1968-08-01
Filing date: 1969-07-16
Publication date: 1970-02-05
Also published as: DE6928182U

Abstract

Clogging of mesh on the surface of finishing plates facing chipboards is reduced or prevented by coating the surface with polytetrafluoroethylene.

Description

Satinierbleche zur Herstellung von Holzfaserplatten, Spanplatten und dergl. Satin finishing sheets for the production of fibreboard, chipboard and the like

Die Neuerung bezieht sich auf Satinierbleche zur Herstellung von Holzfaserplatten, Spanplatten oder dergl.The innovation relates to satin-finished sheets for the production of fibreboard, Chipboard or the like.

Solche Satinierbleche verwendet man bei der Fabrikation der besagten Spanplatten, Holzfaserhartplatten oder dergl., um eine glatte Oberflächenausbildung dieser Platten zu erhalten. Zwischen einem solchen Satinierblech und einem Entwässerungssieb oder zwischen äe zwei solchen Satinierblechen läßt man den mit den erforderlichen Zusatzstoffen angemachten Holzfaserwerkstoff unter Druck und Hitze aushärten. Dabei besteht jedoch der Mangel, daß Fasern oder Spanteile an den Satinierblechen haften und relativ schnell zu fest haftender Verkrustung führen, die infolge der dauernden Hitzeeinwirkung verkohlen. Damit ist dann der Zweck dieser Bleche, den herzustellenden Platten eine glatte Oberfläche zu geben, verfehlt.Such satin-finished sheets are used in the manufacture of the aforementioned Chipboard, wood fiber hardboard or the like. To achieve a smooth surface finish to get these plates. Between such a satin sheet and a drainage sieve or between the two such satin-finish sheets, the one with the required ones is left Cure wood fiber material mixed with additives under pressure and heat. Included however, there is a defect that fibers or chips adhere to the satin-finish sheets and lead relatively quickly to firmly adhering encrustation, which as a result of the permanent Charring from exposure to heat. The purpose of these sheets is then the one to be produced Giving plates a smooth surface is a failure.

Um diesen Mangel abzuhelfen, hat man bereits sogenannte Trennmittel eingesetzt, Diese verzögern zwar die genannt« Verkrustungen der Bleche, in gewissen Zeitabständen ist aber trotzdem der zeitraubende und kostspielige Ausbau und die Reinigung der Bleche erforderlich. Außerdem wirkten sich die Trennmittel bei; einer nachträglichen Oberflächenveredlung der hergestellten Platten, wie z.B. bei einer Lackierung, meist sehr störend aus oder machen sie sogar unmöglich.So-called release agents are already available to remedy this deficiency used, These delay the so-called «incrustations of the metal sheets, in certain However, time intervals is still the time consuming and costly Removal and cleaning of the sheets required. The release agents also had an effect at; a subsequent surface refinement of the panels produced, e.g. when painting, usually very annoying or even impossible.

Die Erfindung beseitigt diese Mängel dadurch, dab die batinierbleche mit hitzebeståndigem Kunststoff, insbesondere mit Polytetrafluorätbylen beschichtet sind.The invention eliminates these deficiencies by the fact that the batinierbleche with heat-resistant plastic, especially coated with polytetrafluoroethylene are.

Es hat sich gezeigt, daß an den auf diese Weise beschichteten Satinierplatten keine Fasern oder Spant eile haften und somit keinerlei Verkrustungen auftreten. Uberraschend und nicht vorher sehbar ist hierbei vor allem die gute Trennwirkung zwischen Satinierblecn und Holzwerkstoff, wodurch die Erfindung den bis her geubten Verfahren weit überlegen ist. ebenfalls überraschend ist der Vorteil, daß sich die unter Verwendung der erfindungsgemäß beschichteten Satinierbleche gepreßten Platten anschließend leichter und besser lackieren oder polieren lassen. Mit der Erfindung werden somit neben der guten frennwirkung folgende beachtliche technische Vorteile erzielt: 1. Sehr lange, zeitlich praktisch nicht begrenzte Verwendbarkeit der Bleche.It has been shown that the satin finish plates coated in this way no fibers or ribs adhere and thus no incrustations occur. Above all, the good release effect is surprising and cannot be foreseen in advance between Satinierblecn and wood material, whereby the invention the practiced up to now Procedure is far superior. also surprising is the advantage that the plates pressed using the satinizing sheets coated according to the invention then have it painted or polished more easily and better. With the invention In addition to the good branding effect, the following considerable technical advantages are thus achieved Achieved: 1. Very long, practically unlimited use of the sheets.

2. Wegfall des bisherigen häufigen, aufwendigen Auswechselns der Bleche und Reinigung der Bleche.2. Elimination of the previous frequent, time-consuming replacement of the metal sheets and cleaning the sheets.

3. Einsparung der bisher erforderlichen Trennmittel und Reinigungschemikalien.3. Saving of the previously required release agents and cleaning chemicals.

4. Verbesserung der nachträglichen Veredelung der Oberflächen der erhaltenen Holzfaserplatten o.dgl. Dieser ebenfalls überraschende Vorteil i.t von besonderer Bedeutung.4. Improvement of the subsequent finishing of the surfaces of the obtained fibreboard or the like. This also surprising advantage i.t of special meaning.

Nachfolgend wird ein Ausfütirungsbeispiel der Neuerung anhand der Zeichnung näher erläutert.The following is an example of the innovation based on the Drawing explained in more detail.

Fig. 1 zeigt ein neuerllngsgemäßes Satinierblech im Schnitt nach Linie II-II in Fig. 2 Fig. 2 ist eine Ansicht von unten auf die beschichtete Seite des Bleches nach Fig. 1.1 shows a new satinizing sheet in a section along the line II-II in Figure 2 Figure 2 is a bottom view of the coated side of the Sheet according to Fig. 1.

Fig. 3 zeigt erfindungsgemäße Satinierbleche im Einsatz mit einer gestrichelt schematisch dargestellten Presse.Fig. 3 shows satinizing sheets according to the invention in use with a dashed line schematically shown press.

Das Blech 1 ist auf seiner einen Seite mit einer Schicht Polytetrafluoräthylen 2 versehen. Es weist seitlich Griffansätze 3 zur Erleichterung der Handhabung auf.The sheet 1 is on one side with a layer of polytetrafluoroethylene 2 provided. It has handle lugs 3 on the side to facilitate handling.

Wie in Fig. 3 dargestellt, werden die Formlinge 4 zwischen je zwei heizbaren Griffplatten 5 in der insgesamt mit 6 bezeichneten Griffe behandelt. Zwischen der Oberseite jedes Formlinges und der oberen Heizplatte ist je ein Satinierblech 1 eingesetzt. Dabei ist die Unterseite, jedenfalls die dem Holzwerkstoff bzw. Holzfaserformling zugekehrte Seite des Satìnier bleches gemäß der Neuerung mit-einer Schicht aus Polytetrafluoräthylen 2 beschichtet.As shown in Fig. 3, the moldings 4 are between two heated grip plates 5 treated in the handles designated as a whole by 6. Between the top of each molding and the upper heating plate are each a satin finish 1 used. The underside is here, at least that of the wood-based material or wood fiber molding facing side of the satin sheet according to the innovation with a layer of polytetrafluoroethylene 2 coated.

Hierdurch ergeben sich insbesondere die oben aufgezeigten Vorteile, vor allen Dingen eine uberraschende Trennwirkung bei guter Oberflächenbeschaffenheit.This results in the advantages outlined above in particular, Above all, a surprising release effect with a good surface finish.

Claims

Claim

batining sheet for the production of fibreboard, chipboard or the like., characterized in that the satin-finish sheet with heat-resistant plastic, is coated in particular with polytetrafluoroethylene.